Copolycarbonates based on bis(4-hydroxyphenyl)biphenyl disulfone

FIELD OF THE INVENTION
This invention relates to polycarbonates and more particularly to copolycarbonates having improved flame retardancy, improved high temperature resistance and good physical properties.
BACKGROUND OF THE INVENTION
Polycarbonates derived from reactions involving organic dihydroxy compounds and carbonic acid derivatives have found extensive commercial application because of their excellent mechanical and physical properties. These thermoplastic polymers are particularly suited for the manufacture of molded articles where impact strength, rigidity, toughness, thermal and dimensional stability as well as excellent electrical properties are required.
Although polycarbonates have some inherent flame resistance being self-extinguishing (V-2 at 1/8" thickness according to UL Subject 94), ever more demanding applications have required improved flame retardance.
Furthermore, it has been found that articles molded from conventional polycarbonates tend to exhibit both low heat deflection and Vicat softening temperature (ASTM D-648-72 and ASTM D-1525-76, respectively).
U.S. Pat. No. 3,269,986 relates to aromatic polycarbonates, the structure of which is characterized by alternating carbonate groups and sulfone-containing organic groups.
In accordance with the present invention, a copolycarbonate is provided having improved flame retardance, mechanical properties at elevated temperature and good physical properties.
SUMMARY OF THE INVENTION
A copolycarbonate of bis(4-hydroxyphenyl)biphenyl disulfone having improved flame retarding properties and improved mechanical properties at elevated temperature is prepared either by the interfacial polycondensation or transesterification processes.
DETAILED DESCRIPTION OF THE INVENTION
The copolycarbonates of the present invention may be prepared by conventional methods of preparation for polycarbonate resins and may have a weight average molecular weight of about 10,000 to 200,000, preferably of about 20,000 to 80,000, and particularly may have a melt flow rate of about 1 to 24 gm/10 min., most particularly about 2-6 gm/10 min., at 300.degree. C. according to ASTM D-1238.
Any process, reactant, catalyst, solvent, reaction condition and the like for the production of the copolycarbonates generally may be used in the context of the present invention. Such are disclosed in German Patent Nos. 926,274 and 1,046,311 and U.S. Pat. Nos. 2,964,794; 2,970,131; 2,991,273; 2,999,835; 2,999,846; 3,028,365; 3,153,008; 3,187,065; 3,215,668; and 3,248,414, all incorporated herein by reference. The preferred processes are interfacial polycondensation and transesterification.
According to the interfacial polycondensation process, copolycarbonates are obtained by reacting the aromatic dihydroxy compounds with an alkali metal hydroxide or alkaline earth metal oxide or hydroxide to form the salt of the hydroxy compounds. The salt mixture is present in an aqueous solution or suspension and is reacted with phosgene, carbonyl bromide, or bischloroformic esters of the aromatic dihydroxy compounds. An organic solvent is provided in the reaction admixture which is a solvent for the polymer but not for the aromatic dihydroxy salts. Thus, chlorinated or non-chlorinated aliphatic or aromatic hydrocarbons are used as the organic solvent which dissolves the condensation product. Suitable solvents include cyclohexane, methylcyclohexane, benzene, toluene, xylene, methylene chloride, chloroform, carbon tetrachloride and chlorobenzene.
In order to limit the molecular weight, one may use monofunctional reactants such as monophenols, for example, the propyl-, isopropyl- and butyl-phenols, especially p-tert-butyl-phenol and phenol itself. In order to accelerate the reaction, catalysts such as tertiary amines, quaternary ammonium, phosphonium or arsonium salts and the like may be used. The reaction temperature should be about -20.degree. C. to +150.degree. C., preferably about 0.degree. C. to 100.degree. C.
According to the polycondensation process in a homogeneous phase, the dissolved reaction components are polycondensed in an inert solvent in the presence of an equivalent amount of a tertiary amine base required for absorption of the generated HCl, such as, e.g., N,N-dimethyl-aniline, N,N-dimethyl-cyclohexylamine or preferably pyridine and the like.
In still another process, a diaryl carbonate can be transesterified with the aromatic dihydroxy compounds to form the polycarbonate resin.
It is to be understood that it is possible to combine in a chemically meaningful way in the processes described above both the aromatic dihydroxy compounds and the monohydroxy compounds in the form of alkali metal salts and/or bis-haloformic acid esters, and the amount of phosgene or carbonyl bromide then still required in order to obtain high molecular weight products. Other methods of synthesis in forming the polycarbonates of the invention such as disclosed in U.S. Pat. No. 3,912,688, incorporated herein by reference, may also be used.
The aromatic diphenols useful in the practice of the invention, all characterized in the absence of a sulfone bridging group therefrom include the following compounds: hydroquinone, resorcinol, dihydroxydiphenyls, bis-(hydroxyphenyl)-alkanes, bis-(hydroxyphenyl)-cycloalkanes, bis-(hydroxyphenyl)-sulfides, bis-(hydroxyphenyl)-ethers, bis-(hydroxyphenyl)-ketones, bis-(hydroxyphenyl)-sulfoxides and .alpha.,.alpha.-bis-(hydroxyphenyl)-diisopropylbenzenes, as well as their alkylated and halogenated derivatives. These and further suitable aromatic dihydroxy compounds are described, for example, in U.S. Pat. Nos. 3,028,365; 2,999,835; 3,148,172; 3,271,368; 2,991,273; 3,271,367; 3,280,078; 3,014,891 and 2,999,846 (all incorporated herein by reference), in German Offenlegungsschriften (German Published Specifications) 1,570,703; 2,063,050; 2,063,052; 2,211,956 and 2,211,957, in French Patent Specification 1,561,518 and in the monograph "H. Schnell, Chemistry and Physics of Polycarbonates, Interscience Publishers, New York, 1964".
Preferred aromatic diphenols are those of the formula I ##STR1## in which
R is identical or different and denotes H, C.sub.1 -C.sub.4 -alkyl, Cl or Br, preferably H or C.sub.1 -C.sub.4 -alkyl, and in which
X is a bond, C.sub.1 -C.sub.8 -alkylidene, C.sub.2 -C.sub.8 -alkylidene,
C.sub.5 -C.sub.15 -cycloalkylene, C.sub.5 -C.sub.15 -cycloalkylidene, --S--, --SO--, --CO--, ##STR2##
Examples of these aromatic diphenols are: 4,4'-dihydroxydiphenyl, 2,2-bis-(4-hydroxyphenyl)-propane (bisphenol A), 2,4-bis-(4-hydroxyphenyl)-2-methylbutane, 1,1-bis-(4-hydroxyphenyl)-cyclohexane, .alpha.,.alpha.-bis-(4-hydroxyphenyl)-p-diisopropylbenzene, 2,2-bis-(3-methyl-4-hydroxyphenyl)-propane, 2,2-bis-(3-chloro-4-hydroxyphenyl)-propane, bis-(3,5-dimethyl-4-hydroxyphenyl)-methane, 2,2-bis-(3,5-dimethyl-4-hydroxyphenyl)-propane, bis-(3,5-dimethyl-4-hydroxyphenyl)-sulfoxide, dihydroxy-benzophenone, 2,4-bis-(3,5-dimethyl-4-hydroxyphenyl)-2-methylbutane, 1,1-bis-(3,5-dimethyl-4-hydroxyphenyl)-cyclohexane, .alpha.,.alpha.-bis-(3,5-dimethyl-4-hydroxyphenyl)-p-diisopropyl-benzene, 2,2-bis-(3,5-dichloro-4-hydroxyphenyl)-propane and 2,2-bis-(3,5-dibromo-4-hydroxyphenyl)-propane (tetrabromo bisphenol A).
Examples of particularly preferred aromatic diphenols are: 2,2-bis-(4-hydroxyphenyl)-propane, 2,2-bis-(3,5-dimethyl-4-hydroxyphenyl)-propane, 2,2-bis-(3,5-dichloro-4-hydroxyphenyl)-propane, 2,2-bis-(3,5-dibromo-4-hydroxyphenyl)-propane and 1,1-bis-(4-hydroxyphenyl)-cyclohexane.
The most preferred aromatic diphenol is 2,2bis-(4-hydroxyphenyl)-propane (bisphenol A).
The bis(4-hydroxyphenyl)biphenyl disulfones useful in the practice of the present invention are those represented by the structural formula ##STR3## wherein
R.sub.1, R.sub.2, R.sub.3 and R.sub.4 independently are H, C.sub.1 -C.sub.4 -alkyl, Cl or Br, preferably H, and
n.sub.1 to n.sub.4 independently are 0 to 4. Structural units derived from these disulfones are present in the copolycarbonate in an effective amount, based on the total dihydroxy compound content, to improve the flammability properties and the mechanical properties at elevated temperatures of the polycarbonate. Preferably, these disulfones are present in about 0.1 to 60 wt. %, based on the total weight of dihydroxy compounds and, most preferably from about 0.5 to 20 wt. %.
The aromatic copolycarbonates can be branched by the incorporation therein of small amounts, preferably between about 0.05 and 2.0 mol % (relative to diphenols employed), of trifunctional or more than trifunctional compounds, especially compounds with three or more phenolic hydroxyl groups.
Polycarbonates of this type are described, for example, in German Offenlegungsschriften (German Published Specifications), 1,570,533; 1,595,762; 2,116,974 and 2,113,347, British patent specification Nos. 885,442 and 1,079,821 and U.S. Pat. Nos. 3,544,514 and 4,185,009, all incorporated herein by reference.
Some examples of compounds with three or more than three phenolic hydroxyl groups which can be used are phloroglucinol, 4,6-dimethyl-2,4,6-tri-(4-hydroxyphenyl)-heptane, 1,4,5-tri-(4-hydroxyphenyl)-benzene, 1,1,1-tri-(4-hydroxyphenyl)-ethane, tri-(4-hydroxyphenyl)-phenylmethane, 2,2-bis-[4,4-bis-(4-hydroxyphenyl)-cyclohexyl]propane, 2,4-bis-(4-hydroxyphenyl-isopropyl)-phenol, 2,6-bis-(2-hydroxy-5'-methyl-benzyl)-4-methylphenol, 2-(4-hydroxyphenyl)-2-(2,4-dihydroxyphenyl)-propane, hexa(4-(4-hydroxyphenylisopropyl)phenyl)orthoterephthalic acid ester, tetra-(4-hydroxyphenyl)-methane, tetra-(4-(4-hydroxyphenylisopropyl)-phenoxy)-methane and 1,4-bis-((4',4"-dihydroxytriphenyl)-methyl)-benzene. Some of the other trifunctional compounds are 2,4-dihydroxybenzoic acid, trimesic acid, cyanuric chloride, 3,3-bis-(4-hydroxyphenyl)-2-oxo-2,3-dihydroindole and 3,3-bis-(4-hydroxyphenyl)-oxindole.
In a preferred embodiment of the present invention, the copolycarbonate may be intimately blended with small amounts of organic acid salts used alone or in combination with low concentrations of halogen-containing compounds to further improve the flame retardance of the copolycarbonate. Preferably, the acid salts are present in the copolycarbonate in quantities of from about 0.01 to 1% by weight, most preferably from about 0.05 to 0.2% by weight, based on the weight of the copolycarbonate. Additionally, halogen, preferably chlorine or bromine, may be introduced into the copolycarbonate either as a halogen-containing organic compound blended therewith or as a halogen-containing component of the polymeric structure, in which latter case the diols from which the copolycarbonate is produced are halogenated in a known manner. Preferably, the halogen content of the copolycarbonate of this embodiment is from about 0.01 to 7 wt. %, most preferably from about 1 to 3 wt. %, based on the weight of the copolycarbonate.
Suitable organic acid salts which may be used are disclosed in U.S. Pat. No.3,775,367, incorporated herein by reference, and include, for example, sodium and potassium perfluorobutane sulfonate, sodium and potassium perfluoromethylbutane sulfonate, sodium and potassium perfluorooctane sulfonate, sodium and potassium perfluoromethane sulfonate, sodium and potassium perfluoroethane sulfonate, sodium and potassium perfluoropropane sulfonate, sodium and potassium perfluorohexane sulfonate, sodium and potassium perfluoroheptane sulfonate, tetraethylammonium perfluorobutane sulfonate, tetraethylammonium perfluoromethylbutane sulfonate and the like and mixtures thereof. The corresponding chloro- and bromo-organic acid salts may also be used. Such sulfonates or mixtures thereof may be added to the polycarbonate during its preparation or they may be added to the melt of the finished polycarbonate by homogenization using an extruder, for example, or by any other suitable means which will ensure a thorough distribution in the copolycarbonate resin. Some such suitable methods are described, for example, in U.S. Pat. No. 3,509,091, incorporated herein by reference.
When the halogen atoms are to be present as substituents of the polycarbonate polymer itself, halogenated reactants are included in the reaction mixture from which the polycarbonate is being prepared. Thus, a halogenated dihydroxy compound may be included in the reaction mixture in addition to the conventional polycarbonate precursors and, upon the addition of a polycarbonate-forming derivative of carbonic acid under suitable reaction conditions, a copolycarbonate is formed wherein the divalent radicals derived from the halogenated dihydroxy compound and from the conventional polycarbonate precursor are linked together through divalent carbonate radicals.
Examples of halogen-containing dihydric phenol compounds which may be used as additives in order to improve the flame retardance of the copolycarbonates of this invention include 2,2-(3,5,3',5'-tetrachloro-4,4'-dihydroxydiphenyl) propane, 2,2-(3,5,3',5'-tetrabromo-4,4'-dihydroxydiphenyl) propane, (3,3'-dichloro-4,4'-dihydroxydiphenyl)methane, 1,1-bis-(4-hydroxy-2-chlorophenyl)ethane, 5'-chloro-2,4'-dihydroxydiphenyl sulfone, 5'-chloro-2',4-dihydroxydiphenyl sulfone, 3'-chloro-4,4'-dihydroxydiphenyl sulfone, 3'-chloro-2,4'-dihydroxydiphenyl sulfone, 4,4'-dihydroxy-3,3'-dichlorodiphenyl ether, 4,4'-dihydroxy-2,3'-dichlorodiphenyl ether, 4,4'-dihydroxy-3,3'-dichlorodinaphthyl ether, and the like.
Further, any other suitable halogenated polycarbonate may be employed such as, for example, those described in U.S. Pat. Nos. 3,043,800; 2,999,835; 3,028,365; 3,106,545; 3,106,546; 3,119,787; 3,141,863; 3,177,179; 3,186,961; 3,203,980; 3,220,978; 3,232,993; 3,240,756; 3,248,366; 3,251,805, all incorporated herein by reference.
In addition to forming copolycarbonates from the dihydroxy aromatic compounds and halogen-containing dihydroxy aromatic compounds, homopolymeric polycarbonates may also be formed from halogen-containing dihydroxy compounds such as the additives enumerated above.
Where desired, the halogenated organic compound may be introduced into the polycarbonate polymeric composition as a chain terminator, whether or not the remainder of the polymer contains halogen atoms. For example, halogenated phenols having from 1 to 5 halogen groups connected to the phenol nucleus may be incorporated into the polycarbonate resin, the amount employed being dependent on the desired molecular weight as well as the minimum required concentration of halogen atoms in accordance with this invention. Generally, the chain terminating agent may be introduced into the reaction mixture in any suitable manner as described in the processes set forth in the patents mentioned herein.
The copolycarbonates of the present invention may also contain other conventional resin additives such as glass fibers, pigments, dyes, UV stabilizers, thermal stabilizers, mold release agents and fillers. Examples of such suitable additives are discussed in the text Chemistry and Physics of Polycarbonates by Hermann Schnell, Interscience Publishers, New York, 1964 and in the text Polycarbonates by W. F. Christopher and D. W. Fox, Reinhold Publishing Corp. New York, 1962.
Any additives, including the organic acid salts and halogen-containing compounds, may be blended with the copolycarbonate in known mixing devices such as kneaders, single-screw extruders, twin-screw extruders, mills and the like.

The invention will be further illustrated, but is not intended to be limited, by the following examples.
EXAMPLES
EXAMPLE 1
Preparation of a copolycarbonate based on bis(4-hydroxyphenyl)biphenyl disulfone (HBD) by the transesterification polycondensation process.
A 500 ml 3-neck flask was charged with 80 g BPA (0.351 moles), 20 g HBD (0.0429 moles) and 92.7 g diphenyl carbonate (0.433 mole, 10% XS). The flask, equipped with an N.sub.2 capillary bleed tube, a distillation head and a mechanical stirrer, was evacuated and flushed with nitrogen three times. The reaction mixture in the presence of a catalytic amount of anhydrous zinc acetate was heated to 220.degree. C. at 300 mm Hg, and as phenol began to distill off, the temperature was gradually increased (300.degree. C.) and pressure decreased (0.65 mm Hg) over three hours. After an additional two hours at 300.degree. C. and 0.65 mm Hg, the molten polymer was scooped out of the flask to give 104 g of 20 wt. % HBD-BPA copolymer having a relative viscosity, measured in a 0.377 wt. % solution in CH.sub.2 Cl.sub.2, 1.308 and a glass transition temperature of 167.8.degree. C.
EXAMPLE 2
Preparation of a copolycarbonate based on bis(4-hydroxyphenyl)biphenyl disulfone (HBD) by the interfacial polycondensation process.
A copolycarbonate having a melt index of 3.4 g/10 min. was prepared by reacting a mixture of the disodium salts of 2,2-bis(4-hydroxyphenyl)-propane (bisphenol A) and bis(4-hydroxyphenyl)biphenyl disulfone with phosgene in accordance with the interfacial polycondensation synthesis hereinbefore discussed. 2.5 wt. % of bis(4-hydroxyphenyl)biphenyl disulfone and 97.5 wt. % of bisphenol A, based on the total weight of the dihydroxy compounds, was used, 2.4 mol percent, based on total bisphenol, of 4 t-butyl phenol was used as a chain stopper. The resulting, highly transparent copolycarbonate was then pelletized and 1/8" thick standard samples were molded for evaluation of physical properties. The properties measured are reported in Table 1.
EXAMPLES 3-15
Copolycarbonate based on bis(4-hydroxyphenyl)biphenyl disulfone prepared in accordance with the procedure outlined in Example 2.
The properties of these resins are summarized in Table 1. Table 2 reports the properties of flame retardant compositions based on these resins wherein blended are organic acid salts or organic acid salts with halogen-containing compounds.
EXAMPLES 16-18
Industrial scale production runs of the copolycarbonates of the invention were carried out yielding resins having the properties summarized in Table 3. The preparation of a copolycarbonate resin containing 5% HBD (Example 18) was carried out as follows:
An aqueous solution of bisphenol A was prepared by simultaneously charging into a suitable mixing vessel 17.24 kg of bisphenol A, 0.91 kg HBD, 90.3 kg of water, 12.3 kg of 50% aqueous sodium hydroxide, and 0.20 kg of phenol. 33.9 kg/h of this solution was continuously phosgenated with 2.46 kg/h of phosgene in 43.1 kg/h of 1:1 methylene chloride:monochlorobenzene solvent. 2.3 kg/h of 25% aqueous caustic was added to maintain the proper pH for the interfacial reaction. The phosgenated solution was then mixed with 0.72 kg/h of 25% aqueous sodium hydroxide and 0.025 kg/h of triethylamine to catalyze the polycondensation reaction. The average time to complete the reaction was 45 minutes. The organic phase was separated from the aqueous phase and the organic phase containing the high molecular weight copolycarbonate was washed with aqueous sodium hydroxide solution, dilute phosphoric acid solution and water. The polymer solution was concentrated by evaporation of the solvent and the polymer recovered by passing the concentrated solution through a devolatilizing extruder. The polymer prepared in this fashion had a relative viscosity of 1.277 (0.37% in methylene chloride).
The temperature of the reaction was 25.degree. C.-30.degree. C. Examples 16 and 17 containing 0.5% and 1% HBD respectively were carried out in a similar fashion.
EXAMPLES 19-27
Copolycarbonates based on HBD were prepared by transesterification following the procedure outlined in Example 1 above. Table 4 reports some of the properties of these resins.
TABLE 1__________________________________________________________________________ Properties of BPA.sup.1 /HBD.sup.2 CopolycarbonatesExample No. 2 3 4 5 6 7 8 (Control).sup.12__________________________________________________________________________HBD (wt %) 2.5 2.5 2.5 5.0 5.0 5.0 0Melt Index (g/10 min).sup.3 3.4 4.1 11.4 5.1 4.8 2.9 3.1Sulfur (wt %) 0.31 0.30 0.27 0.57 0.56 0.61 --UL-94.sup.4 3.2 mm (time,s) V-0 (3.0) V-1 (4.7) V-2 (8.7) V-2 (12.6) V-0 (3.4) V-1 (6.3) V-2 1.6 mm (time,s) V-2 V-2 (3.9) V-2 (7.1) V-2 (3.8) V-2 (3.8) V-2 (16.6) Fail V-2Oxygen Index (%).sup.5 28.5 26.5 27.0 25.0 26.3 25.0 24.2Notched Izod Impact.sup.6 3.2 mm (J/m) 791 834 728 764 763 760 822 6.4 mm (J/m) 152 160 128 137 145 154 164Critical Thickness (mm).sup.11 5.4 5.7 4.4 4.7 5.0 5.0 5.6Heat Distortion Temp. (.degree.C.).sup.7 at 1.82 MPa 140 138.1 137.9 137.3 139.4 141.2 134.0 at 0.46 MPa -- 138.4 140.6 137.0 136.3 140.3 135.8Vicat Softening Temperature (.degree.C.).sup.8 -- 159 157 158 159 162 155Ultimate Strength (MPa).sup.9 61.4 -- 61.4 62.7 67.6 60.7 67.6Strength Failure (MPa).sup.9 53.1 -- 56.5 62.1 67.6 60.7 69.6Elongation Yield (%).sup.9 8 -- 8 8 6 8 8Elongation Failure (%).sup.9 15-95 -- 95 105 125 75 105Flexural Strength (MPa).sup.10 79.3 -- 91.0 92.0 -- -- --Ultimate Strength (MPa).sup.10 79.3 -- 96.5 97.6 -- -- --Instron Melt Stability(300.degree. C.) Kpas 5 min. 700 682 260 420 530 810 35 min. 720 840 280 460 550 700 65 min. 720 874 300 430 580 760__________________________________________________________________________ .sup.1 BPA is bisphenol A .sup.2 HBD is bis(4hydroxyphenyl)biphenyl disulfone .sup.3 ASTM D1238; at 300.degree. C. and 1200 g. load .sup.4 Underwriters Laboratories, Inc. 94: Standard for tests for flammability of plastic materials for parts in devices and appliances; th numbers in parentheses denote burning time in seconds. .sup.5 ASTM D2863 .sup.6 ASTM D256 .sup.7 ASTM D648/72 .sup.8 ASTM D1525/76 .sup.9 ASTM D638 .sup.10 ASTM D790 .sup.11 Mobay method: the thickness at which a transition from ductile to brittle performance upon impact occurs .sup.12 Merlon M50 polycarbonate from Mobay Chemical Corporation
TABLE 2______________________________________Example No. 9 10 11 12 13 14 15______________________________________Wt. % HBD.sup.1 2.5 2.5 2.5 2.5 2.5 2.5 2.5Melt Index 3.4 4.1 4.1 4.1 11.4 11.4 3.4(gm/10 min).sup.2Added Organic.sup.3 0.1 0.05 0.075 0.1 0.075 0.1 0.1Acid Salt,wt. %Added -- -- -- -- -- -- 1.00Halogen.sup.4Flammability.sup.5Rating, UL-94 1.6 mm (sec.) V-0 V-2 V-0 V-0 V-2 V-2 V-0 (2.4) (3.4) (3.4) (3.4) (2.3) 3.2 mm (sec.) V-0 V-0 V-0 V-0 V-0 V-0 V-0 (2.1) (1.2) (1.1) (0.9) (0.8)Oxygen Index.sup.6 29.3 27.6 28.0 28.7 27.1 28.2 31.2Critical -- -- -- -- -- -- 4.7Thickness (mm)______________________________________ .sup.1 HBDbis(4-hydroxyphenyl)biphenyl disulfone .sup.2 Per ASTM D1238 at 300.degree. C. .sup.3 Potassium perfluorobutane sulfonate .sup.4 Bromine .sup.5 The number in parenthesis denotes burn time .sup.6 ASTM D2863
TABLE 3______________________________________Example No. 16 17 18______________________________________Wt. % HBD 0.5 1 5Solution RV.sup.1 1.335 1.324 --Pellet RV.sup.1 1.320 1.326 1.271Melt Index 3.8 3.8 7.61/8" Notched Izod (J/m) 929.8 851.3 764.51/4" Notched Izod (J/m) 151.8 150.3 109.8Critical thickness (inch) .218 .147Heat Distortion temperature 142 139.61.82 MPa, .degree.C.Glass transition temperature .degree.C. 151.0 150.4Sulfur content wt. %, actual .04 .12 --Sulfur content wt. %, theoretical .06 .12 --Flexural PropertiesInitial flex. (MPa) 2256 2254 2280Flex strength (MPa) 53.8 83 53.6Ult. Flex Strength (MPa) 86.0 91 85.5Tensile PropertiesYield (MPa) 60.1 59.86 --Ult. (MPa) 60.1 60.29 --Failure (MPa) 52.6 57.04 --Ultimate elongation % 87 88 --UL-94 flammability rating1/16" (avg. burn time sec.) Fails V-2 Fail V-2 (4.5)1/8" 80% V-0 V-1 (5.6) V-0 (1.7) 20% V-1Hydrolyzable Cl.sup.- 0 -- 176Inorganic Cl (ppm) 0 10 461______________________________________ .sup.1 Relative viscosity measured on a 0.377 wt % solution in CH.sub.2 Cl.sub.2
TABLE 4______________________________________HBD-BPA COPOLYCARBONATESBY TRANSESTERIFICATIONExample No. Wt. % HBD RV.sup.1 Tg.sup.2 M.sub.w.sup.3 M.sub.n.sup.4______________________________________Control.sup.5 0 1.289 146.4 36,600 13,80019 .5 1.292 146.5 32,300 13,30020 15 1.256 160.3 28,000 12,60021 15 1.264 160.3 32,600 14,20022 20 1.308 167.8 39,600 16,60023 25 1.247 169.4 29,600 13,00024 30 1.476 182.3 65,200 23,80025 30 1.324 181.026 40 1.264 187.027 50 1.231 201.5______________________________________ .sup.1 Relative viscosity measured on a 0.377 wt % solution in CH.sub.2 Cl.sub.2 .sup.2 Glass transition temperature determined at 20.degree. C./min. unde 20 cc/min. N.sub.2 purge .sup.3 Weight average molecular weight, relative values based on calibration for BPA polycarbonates .sup.4 Number average molecular weight, relative values based on calibration for BPA polycarbonates .sup.5 Merlon 40, polycarbonate resin by Mobay Chemical Corporation prepared by transesterification
EXAMPLE 28
A copolymer of bisphenol A and HBD containing 0.1% HBD was prepared and tested. The properties of this copolycarbonate are listed below:
______________________________________Glass transition temperature, .degree.C. 147.8Flammability rating UL-941/8 (burn time, sec) V-2 (13.9)1/16 (burn time, sec) V-2 (14.9)HDT, .degree.C. @ 1.82 MPa 140Impact strength, Izod-notched, ft. lbs/in.1/8" 17.381/4" 2.73Critical thickness, mils 206Tensile yield strength, MPa 59.1Tensile failure strength, MPa 66.4Ultimate elongation, % 110-120Flexural strength, MPa 54.1Flexural modulus, GPa 2.28Haze, % 1.8______________________________________
Although the invention has been described in detail in the foregoing for the purpose of illustration, it is to be understood that such detail is solely for that purpose and that variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention as it may be limited by the claims.

Number	Name	Date
2964794	Peilstocker et al.	Dec 1960
2970131	Moyer et al.	Jan 1961
3028365	Schnell et al.	Apr 1962
3153008	Fox	Oct 1964
3269986	Goldberg	Aug 1966
3775367	Nouvertne	Nov 1973
3836490	Bockmann et al.	Sep 1974
3912688	Schiller et al.	Oct 1975
4303776	Baron et al.	Dec 1981
4306055	Baron et al.	Dec 1981

Copolycarbonates based on bis(4-hydroxyphenyl)biphenyl disulfone

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

US Referenced Citations (10)