Patent Application
20170350449
The present invention relates to a brass-based copper alloy for a slide bearing and a slide bearing.
A bearing in which Mn—Si primary crystals are crystallized out on its sliding surface is known (see Patent Literature 1). In Patent Literature 1, particles of the Mn—Si primary crystals are dispersed so as to be elongated in the sliding direction of a counter shaft.
Patent Literature 1: Japanese Patent No. 3718147
However, with the progress of wear, the Mn—Si primary crystals are disrupted and fallen from the bearing, the fallen Mn—Si primary crystals disadvantageously scratch the sliding surface of the bearing. Further, there is the problem that the scratch formed on the sliding surface causes seizure.
The present invention has been made in light of the aforementioned problems, and an object thereof is to provide a copper alloy for a bearing and a slide bearing which can prevent seizure in Mn—Si primary crystals.
In order to attain the aforementioned object, the copper alloy for a slide bearing and the slide bearing according to the present invention contain 25 wt % or more and 48 wt % or less of Zn, 1 wt % or more and 7 wt % or less of Mn, 0.5 wt % or more and 3 wt % or less of Si, and 1 wt % or more and 10 wt % or less of Bi, the balance consisting of inevitable impurities and Cu, and are characterized in that there exist, in a sliding surface on which a counter material slides, Bi particles having a circle equivalent diameter larger than the average circle equivalent diameter of Mn—Si primary crystals and Bi particles having a circle equivalent diameter smaller than the average circle equivalent diameter of the Mn—Si primary crystals.
In the thus-configured copper alloy for a slide bearing, Bi which has been supplied from the Bi particles covers the sliding surface, thereby making it possible to improve the seizure resistance. The Bi particles having a circle equivalent diameter smaller than the average circle equivalent diameter of the Mn—Si primary crystals are dispersed in the sliding surface, thereby making it possible to suppress regions where Bi is present sparsely in the sliding surface and to supply Bi uniformly in the sliding surface. Accordingly, the seizure resistance can be improved. Further, the Bi particles having a circle equivalent diameter larger than the average circle equivalent diameter of the Mn—Si primary crystals are dispersed in the sliding surface, so that, even when the disrupted Mn—Si primary crystals are once fallen from the sliding surface, the Mn—Si primary crystals can be embedded in Bi having a circle equivalent diameter larger than the average circle equivalent diameter of the Mn—Si primary crystals. Thus, it is possible to prevent the disrupted Mn—Si primary crystals from scratching the sliding surface and to prevent the Mn—Si primary crystals from causing seizure.
The incorporation of 25.0 wt % or more of Zn can enhance the strength of the Cu—Zn matrix and suppress sulfurization corrosion caused by the S component in a lubricant oil. In the region where the Mn—Si primary crystals are present sparsely, sulfurization corrosion due to the S component is easily caused by the frictional heat in the Mn—Si primary crystals. However, since the region where the Mn—Si primary crystals are present sparsely can be covered with Bi, the sulfurization corrosion due to the S component can be suppressed. It is noted that 35.0 wt % or more of Zn is incorporated so that the Mn—Si primary crystal particles can grow up to such a size as to obtain more excellent wear resistance. Also, the Zn content is suppressed to 48.0 wt % or less, thereby making it possible to prevent deposition of a large amount of the y phase in a Cu—Zn matrix and embrittlement of the Cu—Zn matrix.
The incorporation of 1.0 wt % or more of Mn and 0.5 wt % or more of Si can lead to deposition of the Mn—Si primary crystal particles in an amount enough to improve the wear resistance. On the other hand, the Mn content is suppressed to 7.0 wt % or less, and the Si content is suppressed to 3.0 wt % or less, thereby making it possible to prevent reduction in toughness due to excessive deposition of the Mn—Si primary crystals. It is noted that the copper alloy of the present invention can contain inevitable impurities.
The copper alloy of the present invention may be configured so that the standard deviation in circle equivalent diameter of the Bi particles in the sliding surface is greater than the standard deviation in circle equivalent diameter of the Mn—Si primary crystals. Thus, even when Bi particles having a small circle equivalent diameter are dispersed, Bi particles having a large circle equivalent diameter can be dispersed at the same time.
Further, the copper alloy of the present invention may be configured so that the number of the Bi particles having a circle equivalent diameter, in the sliding surface circle, that is smaller than the average circle equivalent diameter of the Mn—Si primary crystals, is 70% or more and 90% or less of the total number of the Bi particles. Thus, the number of the Bi particles having a circle equivalent diameter smaller than the average circle equivalent diameter of the Mn—Si primary crystals is controlled, thereby making it possible to attain both of the embeddability of the Mn—Si primary crystals due to the Bi particles having a large circle equivalent diameter and the uniformity in supply of Bi due to the Bi particles having a small circle equivalent diameter.
An embodiment of the present invention will now be described in the following order.
(1) Configuration of radial bearing
(2) Method for producing radial bearing
(3) Experimental results
(4) Other embodiments
Hereinafter, a copper alloy for a slide bearing which constitutes the radial bearing 1 will be described. The copper alloy for a slide bearing contains 40.0 wt % of Zn, 4.0 wt % of Mn, 1.3 wt % of Si and 3.4 wt % of Bi, the balance consisting of Cu and inevitable impurities. The inevitable impurities include Mg, Ni, Ti, B, Pb, Cr and the like, and are impurities mixed during refining or scrapping. The entire content of the inevitable impurities is 1.0 wt % or less. The masses of the respective elements in the copper alloy for a slide bearing were measured by using an ICP emission spectrophotometer (ICPS-8100 manufactured by Shimadzu Corporation).
The image of the photomicrograph of the sliding surface shown in
Further, the degree of circularity was measured for the respective images of the Bi particles 3 by means of the aforementioned image analyzing device. Among all the images of the Bi particles 3, the number proportion of the Bi particles 3 having a degree of circularity of 0.7 or more was 97%. The degree of circularity is a value obtained by dividing the length of the circumference of the circle having an area which is equal to that of the image of the Bi particle 3 (=circle equivalent diameter×π) by the length of the contour of the image of the Bi particle 3. The degree of circularity is 1 when the image of the Bi particle 3 is circular, and decreases as the shape of the image of the Bi particle 3 deviates from the circular shape.
In order to evaluate the seizure resistance of the copper alloy for a slide bearing constituting the radial bearing 1, a seizure test was conducted.
Frictional force is generated between the counter material A and the test pieces T, and the beam parts E rotate horizontally by the frictional force. Therefore, frictional force which horizontally rotates the beam parts E is applied to the load cell Y, and the magnitude of the load measured by the load cell Y means the magnitude of the frictional force between the test pieces T and the counter material A. Therefore, when the load applied to the load cell Y had arrived at a predetermined threshold value or more, it was determined that the frictional force between the test pieces T and the counter material A was abnormally large so that seizure occurred.
The magnitude of the static load applied between the test pieces T by the hydraulic cylinder W was gradually increased (2 MPa/5 min.) to measure the seizure load as the static load when seizure occurred between the test pieces T and the counter material A. Further, the seizure surface pressure was measured by dividing the seizure load by the contact area between the test pieces T and the counter material A.
When measured in the above manner, the seizure surface pressure of the copper alloy for a slide bearing constituting the radial bearing 1 of this embodiment was 26 MPa, which is a favorable result. It is meant that the greater the seizure surface pressure is, the higher the seizure resistance is.
Also, the standard deviation in circle equivalent diameter of the Bi particles 3 is greater than the standard deviation in circle equivalent diameter of the Mn—Si primary crystals 4, and the Bi particles 3 are distributed on a larger circle equivalent diameter side more broadly than the Mn—Si primary crystals 4. So, the possibility that the Mn—Si primary crystals 4 can be embedded can be enhanced. Further, the present invention is configured so that 78.6% of the total number of the Bi particles 3 have a circle equivalent diameter smaller than the average circle equivalent diameter of the Mn—Si primary crystals 4, thereby making it possible to attain both of the embeddability of the Mn—Si primary crystals due to the Bi particles having a large circle equivalent diameter and the uniformity in supply of Bi due to the Bi particles having a small circle equivalent diameter.
Further, since the number proportion of the Bi particles 3 having a large degree of circularity is high, the disrupted Mn—Si primary crystals 4 can be surely embedded.
In the present embodiment, the radial bearing 1 is produced by carrying out the following steps: (a) melting, (b) continuous casting, (c) cutting and (d) mechanical processing in turn. Hereinafter, the respective steps will be explained.
a. Melting
Firstly, raw materials were weighed and provided so as to enable the formation of a copper alloy for a slide bearing containing 40.0 wt % of Zn, 4.0 wt % of Mn, 1.3 wt % of Si and 3.4 wt % of Bi, the balance consisting of Cu and inevitable impurities. In the present embodiment, a Cu ingot, a Zn ingot, a Cu—Mn ingot and a Cu—Si ingot, respectively, were weighed and provided. The raw materials should be provided in masses according to the target mechanical properties of the radial bearing 1. The target mechanical properties of the radial bearing 1 are determined, for example, according to the mechanical properties of the counter shaft 2. Next, the provided raw materials are heated up to 1200° C. by a high-frequency induction furnace. Thus, the respective ingots melt. Thereafter, bubbles of Ar gas are dispersed and jetted to remove hydrogen gas and inclusions.
b. Continuous Casting
Next, the molten materials for the copper alloy for a slide bearing were injected into a mold, and the copper alloy for a slide bearing is continuously pulled out through an opening of the mold in the casting direction and cooled, as it is, to room temperature, thereby forming a continuously cast bar of the copper alloy for a slide bearing. For example, casting is carried out at 1060° C. by means of a mold formed of carbon, and the copper alloy for a slide bearing is pulled out at a pulling-out speed of 90 mm/min, thereby forming a continuously cast bar. It is considered that, in the solidification process in continuous casting from the molten state, the Mn—Si primary crystals 4 are crystallized out first; that the Cu—Zn matrix 5 is crystallized out next; and that a eutectic of Mn—Si and Cu—Zn is solidified at the end. It is noted that the diameter of the continuously cast bar of the copper alloy for a slide bearing is made larger by the machining quantity in the mechanical processing than the outer diameter of the radial bearing 1.
c. Cutting
Then, the continuously cast bar of the copper alloy for a slide bearing is cut for each thickness of the radial bearing 1 (thickness in the length direction of the counter shaft 2).
d. Mechanical Processing
Finally, the continuously cast bar of the copper alloy for a slide bearing after cutting is subjected to machine work or press work, thereby completing the radial bearing 1. Here, machine work is carried out so as to form a through hole having an inner diameter which is larger by a predetermined quantity than the outer diameter of the counter shaft 2 and so that the outer diameter size of the radial bearing 1 coincides with a designed value.
Table 1 indicates the experimental results of Examples 1 to 3. It is noted that Example 1 is identical with the first embodiment. Examples 1 to 3 were produced by a production method almost similar to that of First Embodiment. However, in Example 3, the average circle equivalent diameters of the Mn—Si primary crystals 4 and Bi particles 3 were made smaller than those of Examples 1 and 2 by increasing the pulling-out speed (solidification speed) as compared with those in Examples 1 and 2. It is noted that the average circle equivalent diameters of the Mn—Si primary crystals 4 and Bi particles 3 can be made smaller as the solidification speed is higher, but that the solidification speed can also be made higher by increasing the flow rate of cooling water for a mold in continuous casting.
As indicated in Table 1, in all of Examples 1 to 3, there exist, in the sliding surface, the Bi particles 3 having a circle equivalent diameter larger than the average circle equivalent diameter of Mn—Si primary crystals 4 and the Bi particles 3 having a circle equivalent diameter smaller than the average circle equivalent diameter of the Mn—Si primary crystals 4. Therefore, the disrupted Mn—Si primary crystals 4 could be embedded in the Bi particles 3 having a large degree of circularity, and good seizure surface pressure could be obtained also in the sliding surface in all of Examples 1 to 3. Also, it has been found that, as the number proportion of the Bi particles 3 having a large degree of circularity is higher, good seizure surface pressure can be obtained and the disrupted Mn—Si primary crystals 4 can be embedded efficiently, as indicated in Table 1. The average circle equivalent diameter of the Bi particles 3 (large Bi particles+small Bi particles) is increased, and, at the same time, the number proportion of the Bi particles 3 having a large degree of circularity is increased, thereby making it possible to synergistically improve the embeddability of foreign matter such as the Mn—Si primary crystals 4 in the Bi particles 3 and to drastically improve the seizure surface pressure.
The above embodiment has illustrated an example of the radial bearing 1 formed of the copper alloy of the present invention, but other sliding members may be formed of the copper alloy of the present invention. For example, gear bushes for transmission, piston pin bushes and boss bushes may be formed of the copper alloy of the present invention. Also, the copper alloy for a slide bearing of the present invention may be produced by any other production method than continuous casting.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2015-001419 | Jan 2015 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2015/081472 | 11/9/2015 | WO | 00 |