Patent Grant
11749441
The present disclosure relates to a core component made of a sintered body of an inorganic powder, a method of manufacturing the core component, and an inductor.
Conventionally, when winding a conductive wire, for example, a conductive wire covered with an insulating material such as polyurethane or polyester, around a winding portion of a core component such as a ferrite core, the conductive wire is mounted in a state of being aligned with the winding portion by fixing the end of the conductive wire to any one of the flange portion provided at both ends of the winding portion, and feeding the conductive wire from one end to the other end of the winding portion while bringing adjacent conductive wires into contact with each other.
A core component to which such a conductive wire is mounted is required to have high density. Japanese Patent Application Laid-Open No. 2003-257725 proposes a ferrite powder capable of producing granules having a high powder bulk density and in which cracks are less likely to occur during molding.
Recently, as shown in Japanese Patent Application Laid-Open No. 2017-204596, the miniaturization of electronic devices such as portable terminals is progressing, and the demand for miniaturization of core components mounted on such electronic devices is also increasing. The publication discloses that the conductive wire which is wound around the winding portion is also thinned, and the diameter thereof is as thin as about 20 μm.
The core component of the present disclosure is made of a sintered body of an inorganic powder, in which the core component includes a columnar winding portion having a first axial end and a second axial end and a flange portion integrally formed with the columnar winding portion at both axial ends of the columnar winding portion, and a gap C, between adjacent voids in a surface layer portion of the columnar winding portion, is 6 to 12 μm and is represented by the following Formula,
C=L−R Formula:
where, L is the average value of the distance between the centers of gravity between adjacent voids, and R is the average value of the equivalent circle diameters of the voids.
The method of manufacturing the core component according to the present disclosure includes filling and pressure molding an inorganic powder between an upper punch and a lower punch to form a pressure-molded compact, wherein each of the upper punch and lower punch has an arc-shaped pressing surface for molding the columnar winding portion and the flange portion; and sintering the pressure-molded compact to form a sintered body, in which the arc-shaped pressing surface of the upper punch and the arc-shaped pressing surface of the lower punch at least at a portion forming the columnar winding portion, and wherein a molding pressure at a time of the pressure molding is 98 Mpa or more.
The inductor of the present disclosure includes the core component and a conductive wire wound around the columnar winding portion of the core component.
Hereinafter, core components according to an embodiment of the present disclosure will be described. As shown in
As shown in
C=L−R Formula:
where, L is the average value of the distance between the centers of gravity between adjacent voids, and R is the average value of equivalent circle diameters of the voids.
At this time, it is more preferable that the voids present in the surface layer portion 21 have a larger gap C between adjacent voids than the voids present in an inside 22. Specifically, it is preferable that the difference between the gap CS1 value between the voids in the surface layer portion 21 and the gap CS2 value between the voids in the inside 22, is 1 μm or more, wherein the gap CS1 value and the gap CS2 value are obtained from the above formula.
Here, the surface layer portion 21 is a region having a depth of 0.22 mm or less from the surface of the columnar winding portion 2 toward the axial center, where a gap C between the voids is in a range of 6 to 12 μm. The inside 22 refers to a region excluding the surface layer portion 21.
As described above, since the void distribution at least in the surface layer portion 21 of the columnar winding portion 2 is sparse, so that the particle shedding generated from the inside and the outline of the voids is reduced, and when the conductive wire is wound around the columnar winding portion 2, it is not likely to cause damage to the conductive wire such as disconnection.
As in the columnar winding portion 2, as shown in
Here, the surface layer portion 31 refers to a region having a depth of 0.22 mm or less from the surface of the flange portion 3 toward the axial center. The inside 32 refers to a region excluding the surface layer portion 31.
The average value of the distance between the centers of gravity between the voids and the average value of the equivalent circle diameters of the voids can be determined by the following method.
First, the portion where the size and distribution of the voids are observed on average is selected among the mirror surface of each of the surface layer portion 21 and 31 and the inside 22 and 32 obtained by polishing them using diamond abrasive grains having an average particle diameter of 1 μm (this mirror surface is the cross section perpendicular to the axial direction of the columnar winding portion 2 and the flange portion 3). For example, the range in which the area is 3.84×10−2 mm2 (lateral length is 0.226 mm, longitudinal length is 0.170 mm) is photographed with a scanning electron microscope at a magnification of 500 to obtain an observation image. Then, for this observation image, the average value of the distances between the centers of gravity of the voids can be determined by the distance-between-centroid method of dispersion measurement using the image analysis software “A-Zou Kun (ver 2.52)” (registered trademark, manufactured by Asahi Kasei Engineering Corporation, in the following description, the description of the image analysis software “A-Zou Kun” refers to the image analysis software manufactured by Asahi Kasei Engineering Corporation).
In addition, the average value of the equivalent circle diameters of the voids can be determined by performing analysis using the same observation image as the above-described observation image by means of the particle analysis using the image analysis software “A-Zou Kun”.
As the setting conditions of the distance-between-centroid method and the particle analysis, for example, a threshold value which is an index indicating light and dark of an image may be 83, lightness may be dark, a small figure removing area may be 0.2 μm2 and a noise removing filter may be present. In the above measurement, the threshold value is 83, but the threshold value may be adjusted according to the brightness of the observation image. The lightness is dark, the method of binarization is manual, and the small figure removing area is 0.2 μm2 and a noise removing filter is present. The threshold value may be manually adjusted so that a marker whose size changes according to the threshold value in the observation image matches the shape of the voids.
In the core component 1 of the present embodiment, as shown in
Therefore, since the surface layer portion 21 of the columnar winding portion 2 is dense, the strength of the columnar winding portion 2 is improved, the resistance to deformation is improved, and the particle shedding is also suppressed.
The area occupancy of voids can be determined by a method called the particle analysis using the image analysis software “A-Zou Kun” using the same observation image as the observation image described above. The setting conditions for the particle analysis may be the same as the setting conditions described above.
The area occupancy of voids of the flange portion 3 may have the same relationship as that of the columnar winding portion 2. That is, as shown in
The columnar winding portion 2 has a cutting level difference (Rδc) of the surface roughness curve of 0.2 μm or more and 2 μm or less. The cutting level difference (Rδc) represents the difference between the cutting level at a 25% loading length rate in the surface roughness curve and the cutting level at a 75% loading length rate in the roughness curve. The cutting level difference (Rδc) is a parameter that represents both the axial direction and the radial direction.
Similarly, the cutting level difference (Rδc) of the roughness curve on the surface of the flange portion 3 is preferably 0.2 μm or more and 2 μm or less.
When the cutting level difference (Rδc) is 0.2 μm or more, an appropriate anchor effect can be given to the conductive wire. Therefore, the slip of the conductive wire is appropriately suppressed, the winding installation becomes easy, and the winding of the conductive wire to the columnar winding portion 2 can be performed with high accuracy, so that the occurrence of winding deviation or the like can be prevented. On the other hand, the cutting level difference (Rδc) is 2 μm or less, so that it is possible to suppress the variation in the intervals between the wound conductive wires and the height difference between the adjacent conductive wires.
Moreover, it is preferable that the root mean square height (Rq) in a roughness curve be 0.07 μm or more and 2.5 μm or less.
When the root mean square height (Rq) is 0.07 μm or more, an appropriate anchor effect can be given to the conductive wire, which facilitates the mounting. On the other hand, when the conductive wire is wound with a root mean square height (Rq) of 2.5 μm or less, the risk of disconnection can be reduced.
The columnar winding portion 2 is pressure-molded at a high pressure by a lower punch 5 and an upper punch 6 as described later, so that the surface layer portion 21 of the columnar winding portion 2 is denser than a surface layer portion 31′ of an inner portion of the flange portion 3 shown in
The cutting level difference Rδc and the root mean square height (Rq) of the roughness curve are in accordance with JIS B 0601: 2001, and can be measured by a ultra-depth color 3D shape measuring microscopes (for example, VK-9500 manufactured by Keyence Corporation). The measurement conditions are as follows; measurement mode: color ultra depth, gain: 953, measurement resolution in the height direction (pitch): 0.05 μm, magnification: 400 times, cutoff value λs: 2.5 μm, cutoff value λc: 0.08 mm. Here, it is sufficient that the measurement range per one location is 580 μm to 700 μm×280 μm to 380 μm when the columnar winding portion 2 is to be measured, and 70 μm to 170 μm×500 μm to 550 μm when the flange portion 3 is to be measured.
As shown in
Specifically, the radius of curvature of the corner portion 20 is 40 μm or less, preferably 10 to 30 μm. This can prevent offset of the conductive wire.
Next, a method of manufacturing the core component 1 by press molding will be described based on
As shown in
Therefore, a stepped portion 7 is formed on both sides in a state where the pressing surfaces 50a and 50b of the lower punch 5 and the pressing surfaces 60a and 60b of the upper punch 6 overlap with each other.
In the present embodiment, at least the radius of curvature of the pressing surface 50b of the lower punch 5 and the radius of curvature of the pressing surface 60b of the upper punch 6 may be different from each other at a portion where the columnar winding portion 2 is to be formed.
In molding, first, the lower punch 5 is fixed in the die 4 as shown in
The molding pressure at the time of pressure molding is 98 MPa or more, preferably 196 to 490 MPa. Since such a high pressure can be used for pressure molding, the resulting compact has a dense and closely packed surface, in particular, on the surface portion, and as described above, the void distribution at least in the surface layer portion 21 of the columnar winding portion 2 can be made sparse, and the gap C between adjacent voids can be made to 6 to 12 μm.
For the same reason, the area occupancy of voids of the surface layer portion 21 of the columnar winding portion 2 described above can be made smaller than that of the inside 22 of the columnar winding portion.
In addition, the compact has a dense and closely packed surface, in particular, on the surface portion, so that the cutting level difference (Rδc) of the roughness curve of the surface of the columnar winding portion 2 can be 0.2 to 2 μm.
Furthermore, since the surface shape of the molding die (lower punch 5 and upper punch 6 described later) can be faithfully reflected because of pressure molding with high pressure, the radius of curvature of the corner portion 20 where the columnar winding portion 2 and the flange portion 3 intersect may be less than or equal to the diameter of the conductive wire.
Such high pressure can be applied because, as described above, the pressing surfaces 50a and 50b of the lower punch 5 and the pressing surfaces 60a and 60b of the upper punch 6 have different radiuses of curvature. On the other hand, when the pressing surfaces 50a and 50b of the lower punch 5 and the pressing surfaces 60a and 60b of the upper punch 6 have the same radius of curvature, the compact cannot be taken out of the molding die when pressurized with high pressure. Therefore, since it cannot be pressurized at high pressure but must be pressurized at low pressure, the core component 1 formed by pressure molding has a lot of voids, the strength is inferior, and further, it is easy to generate the particle shedding.
After molding, as shown in
The second lower punch 52 is relatively raised with respect to the die 4 simultaneously with or after the rise of the upper punch 6. As a result, the compact 9 can be pushed up, and the compact 9 can be easily taken out.
After removing the raw material powder adhering to the obtained compact 9 by air blow or the like if necessary, for example, the compact 9 is held at the maximum temperature of 1000 to 1200° C. for 2 to 5 hours in an air atmosphere to obtain the sintered body. Further, the sintered body is subjected to polishing such as barrel polishing, if necessary, to obtain the core component 1.
A stepped portion 10 corresponding to the stepped portion 7 due to the difference in the radiuses of curvature of the pressing surfaces 50a and 50b of the lower punch 5 and the pressing surfaces 60a and 60b of the upper punch 6 is formed on the surface of the compact 9 corresponding to the columnar winding portion 2 and the flange portion 3. If the stepped portion 10 has a problem in winding the conductive wire around the surface of the columnar winding portion 2, it is preferable to remove as much as possible by polishing.
As shown in
In addition, the stepped portion 10 may be largely removed by polishing, and the portion may be processed into a planar shape. In this case, as shown in
The above polishing process may be applied not only to the columnar winding portions 2 and 2′ but also to the flange portion 3 in the same manner. That is, as shown in
The second projection 131 preferably has a curved outer peripheral surface. Furthermore, the outer peripheral surface of the second projection 131 preferably has a radius of curvature smaller than that of the outer peripheral surface of the flange portion. As a result, the residual stress in the first projection 13 is reduced, so that the first projection 13 is less likely to be brittlely fractured, and the occurrence of particle shedding due to the brittle fracture is reduced.
As in the columnar winding portion 2 shown in
The obtained core component 1 is suitably used as an inductor by winding a conductive wire around the columnar winding portions 2 and 2′. The application of the core component 1 of the present disclosure is not limited to the inductor, and may be applied to the case where members having flanges at both ends and a central portion having a columnar shape and a smooth curved surface shape are formed of ceramics or the like. For example, in the case of manufacturing, with a ceramic, a tape guide for guiding a magnetic tape or the like, in which the tape guide has flanges at both ends of a columnar body, the manufacturing can be easily performed by using the core component manufacturing method of the present disclosure.
Hereinafter, the core component of the present disclosure will be described in detail by way of Examples and Comparative Example.
(Example)
The ferrite powder was pressure-molded at 384 MPa using the molding apparatus shown in
(Comparative Example)
Only a central portion of the columnar compact of a ferrite powder was cut and processed to produce a core component having a winding portion and a flange portion at both ends thereof of a sintered body obtained by firing.
(Measurement of the Gap Between Voids)
With respect to the obtained core components, the average value L of the distance between the centers of gravity between voids, the average value R of the equivalent circle diameters of the voids, and the gap C between the voids which is a difference thereof were measured by the above-described measurement method. In order to obtain an average value, the number of measured voids was 360 to 640 in each observation image. The measurement was performed on the surface layer portion and the inside (near the axial center) of the columnar winding portion and the flange portion of the core component. The results are shown in Table 1.
It can be seen from Table 1 that, unlike the core component of the Comparative Example, the core component of Example has an area occupancy of voids in each surface layer portion of the columnar winding portion and the flange portion smaller than that in each of their respective insides, so that it is dense.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-003548 | Jan 2019 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 10074468 | Inagaki et al. | Sep 2018 | B2 |
| 20100028796 | Nakamura | Feb 2010 | A1 |
| 20120274429 | Ogawa | Nov 2012 | A1 |
| 20160071637 | Inagaki | Mar 2016 | A1 |
| 20160293309 | Inagaki | Oct 2016 | A1 |
| 20170330672 | Uchida et al. | Nov 2017 | A1 |
| 20170330676 | Uchida et al. | Nov 2017 | A1 |
| 20220375673 | Ochiai | Nov 2022 | A1 |
| Number | Date | Country |
|---|---|---|
| H05-275256 | Oct 1993 | JP |
| 2003-257725 | Sep 2003 | JP |
| 2011-223025 | Nov 2011 | JP |
| 2016-39236 | Mar 2016 | JP |
| 2017-204596 | Nov 2017 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20200227197 A1 | Jul 2020 | US |