Cored wire for introducing additives into a molten metal bath

Information

  • Patent Grant
  • 6770366
  • Patent Number
    6,770,366
  • Date Filed
    Friday, March 16, 2001
    23 years ago
  • Date Issued
    Tuesday, August 3, 2004
    19 years ago
Abstract
The invention relates to a cored wire for introducing additives into a molten metal bath comprising a metallic sheath (5) containing an additive (6), which metallic sheath is covered by a wrapping (7) which, being combustible without leaving harmful residues, momentarily retards the propagation of heat to the core of the cored wire, this cored wire being characterized in that on top of this combustible wrapping, a protective metallic casing encloses the assembly thus constituted by the additive, the metallic sheath and the combustible wrapping.
Description




The invention relates to a cored wire for introducing additives into a molten metal bath.




Steels, irons, etc., are materials whose mechanical or other properties particularly depend on the complex composition of the material.




In order to obtain a material having certain properties from a basic composition, the content of certain elements is adjusted to obtain the desired composition.




It has been known for about twenty years to adjust the composition of molten material by introducing a cored wire of predetermined length into it.




This cored wire is constituted by a metallic casing containing the additive that one wishes to introduce into the molten bath.




The quantity of additive per meter being known, it is relatively simple to adjust the composition of the bath.




In the first cored wires produced, the metallic casing was simply folded so as to place the two edges of the formed strip side by side.




An inner sheet was first put in place in order to close the gap that remained between the edges of said strip, but this was not very effective given that this cored wire was subjected to a winding operation on a reel, then an unwinding operation during its utilization.




This solution was quickly replaced by a different closure for the strip.




This method consists of mechanically crimping the two edges of the strip.




More precisely, it consists of rolling the two edges together so that the edges are fastened to one another. This prevents losses of the additive contained in said strip.




This solution, which makes it possible to adjust a composition by introducing a cored wire into the molten material, works very well with most additives.




However, problems arise with certain additives such as calcium, magnesium, selenium, sulfur and others.




In essence, for some of these additives, the heat of the molten metal bath causes the cored wire to explode in an area very close to the surface of the bath.




Other additives vaporize very quickly and close to the surface. This produces a strong surface reactivity, which results in an oxidation and/or renitriding of the bath, splashes of the liquid metal that damage the material, and heavy smoke emanation. Therefore, this introduction operation is much less efficient in the presence of these additives, and the resulting safety conditions are not adapted for industrial utilization.




In an attempt to eliminate this problem, it is known to introduce the cored wire through a tube made of refractory material immersed in the bath. The use of this tube is very difficult and very costly.




It is known to cover this metallic sheath with a wrapping which, being combustible without leaving any harmful residues, momentarily retards the propagation of heat to the core of the cored wire. This combustible wrapping is wound in a helix around the metallic sheath. Unfortunately, the paper wrapping is sometimes observed to deteriorate during handling, i.e., when the wire is wound around the reel or when the wire placed on the reel is unwound in order to be introduced into the bath.




SUMMARY OF THE INVENTION




The subject of the invention is a cored wire comprising a metallic sheath containing an additive and covered by a wrapping


7


which, being combustible without leaving any harmful residues, momentarily retards the propagation of heat to the core of the cored wire.











BRIEF DESCRIPTION OF THE DRAWINGS




The invention will be better understood with the help of the following description given as a non-limiting example, in reference to the attached drawing, which schematically represents:




FIG.


1


: a cross-section of a cored wire according to the invention,




FIG.


2


: a step in the preparation of the cored wire,




FIG.


3


: an installation using a cored wire,




FIG.


4


: a cross-section of a variant of a cored wire.











Referring to the drawing, we see a cored wire


1


designed for the introduction of an additive into a bath


2


of molten material, such as a steel, an iron, or another material.




This molten bath is at a relatively high temperature, and is contained in a ladle


3


.




In order to adjust the composition of the bath of molten material, this cored wire


1


is introduced into the bath at a predetermined speed.




The means of introduction


4


are conventional and will not be described in detail.




Conventionally, this cored wire comprises a metallic sheath


5


containing an additive


6


.




This metallic sheath


5


is closed mechanically, which means that the edges of the strip are attached to one another, for example by rolling.




Advantageously, this metallic sheath is covered by a wrapping


7


which, being combustible without leaving any harmful residues, momentarily retards the propagation of heat to the core of the cored wire.




Harmful residues would include residues that affect the composition of the bath or produce inclusions that modify the behavior of the bath during casting.




Advantageously, the protective wrapping


7


is constituted by at least one layer


7


A of paper rolled around the metallic sheath.




The paper


7


A is a paper for so-called pyrotechnic applications.




This means that it is flame-resistant and has a thermal resistance coefficient higher than that of a sheet of ordinary paper.




This thermal protection is obtained:




either by integrating the flame-retardant constituents into the composition of the paper,




or by combining the paper layer and the adhesive used to attach the superposed strips to one another.




For example, there are known uncoated, wood-free, guaranteed flame-retardant M


1


papers. This requires a material whose the flame propagation is nil, with no falling of burning drops and no flame persistence.




This wrapping has thermal insulation properties while being combustible.




Tests performed with one type of paper showed that:




without a paper layer, the cored wire explodes after one second,




with two layers, the cored wire explodes after one-and-a-half seconds, and




with ten layers, the cored wire explodes after two-and-two-tenths seconds.




Thus, by adjusting the thickness of the wrapping and the speed at which the cored wire is introduced, it is possible to sufficiently retard either the explosion or the vaporization, and it is then easy to introduce the cored wire to a sufficient depth.




The layer or layers of the wrapping are advantageously constituted by one or more helical windings of a strip of paper.




These windings are for example crossed.




In a variant of embodiment, an external fixation of these layers is achieved by applying a layer of varnish, which must clearly be free from water or any substances that react violently with the material constituting the bath.




Therefore, a fixative layer is provided for the wrapping, especially when the latter is formed by several strips.




The width of the strip is preferably adapted to the diameter of the wire and to the conditions for utilization, and is for example between five and forty centimeters.




The thickness of the protective wrapping is therefore adapted to the user's needs (temperature of the bath and material to be injected).




Advantageously (FIG.


4


), particularly in certain cases where the injection machine could damage the combustible wrapping, on top of this combustible wrapping


7


, a protective metallic casing


10


encloses the assembly constituted by the additive, the metallic sheath and the combustible wrapping.




Said assembly is therefore covered by a protective metallic casing.




This protective metallic casing


10


prevents the combustible wrapping from being altered during the handling of the cored wire and forms, with the metallic sheath housing the additive and the combustible wrapping, a complex material that retards the melting of the assembly.




Advantageously, this protective metallic casing is constituted by a strip whose edges are crimped to form a tubular element.




This is the method normally used to form the metallic sheath housing the additives.




The shape of the crimp


11


is not illustrated.




This is the method that seems to be simplest to implement and that does not damage the combustible wrapping.




Advantageously, instead of applying the paper sheet in wound form, the paper sheet can be much thicker and can be applied at the same time as the protective metallic casing.




The edges of the thick sheet overlap.



Claims
  • 1. A cored wire for introducing additives into a molten metal bath comprising a wire core (6) having a metallic sheath (5) thereon containing an additive, and a wrapping (7) around said sheath, said wrapping (6) being combustible without leaving harmful residues, said wrapping being made of a material that will momentarily retard propagation of heat to the wire core (6) when introduced into the molten metal bath.
  • 2. The cored wire according to claim 1, wherein wrapping (7) comprises at least one layer (7A) of paper wound around the metallic sheath (5).
  • 3. The cored wire according to claim 2, wherein paper (7A) is a pyrotechnic paper.
  • 4. The cored wire according to claim 3, wherein a protective metallic casing (10) disposed on top of the combustible wrapping encloses the assembly formed by the wire core (6), the metallic sheath (5), containing the additive, and the combustible wrapping (7).
  • 5. The cored wire according to claim 2, wherein the at least one layer comprises at least one helical winding of a strip of paper.
  • 6. The cored wire according to claim 5, wherein the at least one helical winding is arranged in more than one layer.
  • 7. The cored wire according to claim 6, wherein a protective metallic casing (10) disposed on top of the combustible wrapping encloses the assembly formed by the wire core (6), the metallic sheath (5), containing the additive, and the combustible wrapping (7).
  • 8. The cored wire according to claim 5, wherein the at least one layer has a coating of varnish to provide fixation of the layers.
  • 9. The cored wire according to claim 8, wherein a protective metallic casing (10) disposed on top of the combustible wrapping encloses the assembly formed by the wire core (6), the metallic sheath (5), containing the additive, and the combustible wrapping (7).
  • 10. The cored wire according to claim 5, wherein the width of the strip is between five and forty centimeters.
  • 11. The cored wire according to claim 10, wherein a protective metallic casing (10) disposed on top of the combustible wrapping encloses the assembly formed by the wire core (6), the metallic sheath (5), containing the additive, and the combustible wrapping (7).
  • 12. The cored wire according to claim 5, wherein a protective metallic casing (10) disposed on top of the combustible wrapping encloses the assembly formed by the wire core (6), the metallic sheath (5), containing the additive, and the combustible wrapping (7).
  • 13. The cored wire according to claim 2, wherein a protective metallic casing (10) disposed on top of the combustible wrapping encloses the assembly formed by the wire core (6), the metallic sheath (5), containing the additive, and the combustible wrapping (7).
  • 14. The cored wire according to claim 13, wherein the protective metallic casing (10) comprises a sheet whose edges are crimped to form a tubular element.
  • 15. The cored wire according to claim 13, wherein the combustible wrapping (17) is formed by a thick sheet applied at the same time as the protective metallic casing (10).
Priority Claims (1)
Number Date Country Kind
00 08284 Jun 2000 FR
US Referenced Citations (16)
Number Name Date Kind
3921700 Frantzreb, Sr. et al. Nov 1975 A
3991808 Nieman et al. Nov 1976 A
3991810 Nieman Nov 1976 A
4040468 Nieman Aug 1977 A
4163827 Nieman et al. Aug 1979 A
4199351 El Gammal Apr 1980 A
4200456 Fujii Apr 1980 A
4277282 Guthrie et al. Jul 1981 A
4297133 Fujii Oct 1981 A
4652299 Bienvenu et al. Mar 1987 A
4832742 Ototani May 1989 A
5352271 Margaria et al. Oct 1994 A
5376160 Neuer et al. Dec 1994 A
6280497 King et al. Aug 2001 B1
6346135 King et al. Feb 2002 B1
20020025434 Riche et al. Feb 2002 A1
Foreign Referenced Citations (2)
Number Date Country
29 23 236 Dec 1980 DE
0 032 874 Jul 1981 EP
Non-Patent Literature Citations (1)
Entry
Patent Abstracts of Japan, vol. 014, No. 236 (C-0720) May 18, 1990 & JP 02 061006A (Hitachi Cable LTD), Mar. 1, 1990, Abstract.