Corrosion inhibitors

Abstract

A method of treating an aqueous system to inhibit the corrosion of metals in contact therewith and/or inhibit the deposition of scale therefrom comprising adding to the aqueous system a minor proportion of a compound of the formula: ##STR1## wherein n is 0 or 1 and when n is O, R.sub.3 and R.sub.4 are the same or different and each is hydrogen, an alkyl group having from 1 to 4 carbon atoms, a benzyl, allyl, --CH.sub.2 PO.sub.3 H.sub.2 -- or --CHCOOH.CH.sub.2 COOH group or a group of formula ##STR2## wherein R.sub.5 is hydrogen, a methyl, --CH.sub.2 COOH or --CH.sub.2 CH.sub.2 COOH group and Z is a group --COOH or --PO.sub.3 H.sub.2, with the proviso that when Z is a PO.sub.3 H.sub.2 group then R.sub.5 is hydrogen or methyl, and when n is 1, R.sub.1 and R.sub.2 are the same or different and each is hydrogen, or a methyl or phenyl residue and R.sub.3 is hydrogen and R.sub.4 is hydrogen, an alkyl group having from 1 to 4 carbon atoms or a --CH.sub.2 CH.sub.2 COOH group, or R.sub.3 and R.sub.4 together may form a methylene group .dbd.CH.sub.2.

Description

The present invention relates to the use of phosphonocarboxylic acids as corrosion inhibitors and/or scale control agents in aqueous systems.

Traditionally chromates, dichromates, nitrites, benzoates, silicates, polyphosphates etc. have been used to combat corrosion. However, each of these inhibitors suffers from at least one serious disadvantage. Chromates and dichromates are toxic and disposal of them to water courses presents severe ecological problems. Inorganic nitrites require high dose levels to function effectively and they are also subject to bacterial decomposition. This necessitates the use of an expensive organic biocide since chlorine cannot be used as it reacts with nitrite. Benzoates and silicates also require high dose levels and silicates, furthermore, tend to coat metal surfaces with a hydrated silica gel which is often very difficult to remove.

Polyphosphates are effective as relatively low dosage rates but suffer from hydrolysis to phosphate especially at high temperature and at pHs below 7 . The phosphate ions liberated on a hydrolysis are not effective as corrosion inhibitors, give rise to sludge problems due to the precipitation of calcium orthophosphate and serve as nutrient for biological growth unless chlorine or another biocide is used.

In an attempt to overcome the problems associated with polyphosphate hydrolysis, corrosion inhibitor systems based on the more hydrolytically stable organic phosphonates have been developed. Examples of acid phosphonates include hydroxy- and amino-diphosphonic acids, e.g. those described in German Patent Specification No. 2,225,645.

According to the present invention, there is provided a method of treating an aqueous system to inhibit the corrosion of metals in contact therewith and/or inhibit the deposition of scale therefrom comprising adding to the aqueous system a minor proportion of a compound of the formula: ##STR3## wherein n is 0 or 1 and when n is 0, R.sub.3 and R.sub.4 are the same or different and each is hydrogen, an alkyl group having from 1 to 4 carbon atoms, a benzyl, allyl, --CH.sub.2 PO.sub.3 H.sub.2 --or --CHCOOH.CH.sub.2 COOH group or a group of formula ##STR4## wherein R.sub.5 is hydrogen, a methyl, --CH.sub.2 COOH or --CH.sub.2 CH.sub.2 COOH group and Z is a group --COOH or --PO.sub.3 H.sub.2, with the proviso that when Z is a PO.sub.3 H.sub.2 group then R.sub.5 is hydrogen or methyl, and when n is 1, R.sub.1 and R.sub.2 are the same or different and each is hydrogen, or a methyl or phenyl residue and R.sub.3 is hydrogen and R.sub.4 is hydrogen, an alkyl group having from 1 to 4 carbon atoms or a --CH.sub.2 CH.sub.2 COOH group, or R.sub.3 and R.sub.4 together may form a methylene group .dbd.CH.sub.2.

The compounds of formula I may be employed in the method of the invention as the free acids or as watersoluble salts or partial esters.

As examples of water-soluble salts of the compounds of formula I there may be mentioned alkali metal salts e.g. the sodium and potassium salts, ammonium salts, as well as salts of amines e.g. mono-, di- or triethanolamines.

Examples of water-soluble partial esters of the compounds of formula Iare those derived from alcohols containing from 1 to 4 carbon atoms.

Preferred compounds of formula I for use according to the invention are those wherein:

n is 0, R.sub.3 is hydrogen and R.sub.4 has its previous significance n is 1, R.sub.1 and R.sub.3 are hydrogen and either R.sub.2 is hydrogen and R.sub.4 is hydrogen, an alkyl group having from 1 to 4 carbon atoms or --CH.sub.2 CH.sub.2 COOH, or R.sub.2 is methyl and R.sub.4 is hydrogen.

Particularly preferred compounds are those wherein n is 0 and R.sub.3 and R.sub.4 are each hydrogen or n is 1 and R.sub.1, R.sub.2 and R.sub.3 are hydrogen and R.sub.4 is methyl.

Specific examples of corrosion inhibitors of formula I include:

1. 2-phosphonoacetic acid 2. 2-phosphonopropionic acid 3. 2-phosphonohexanoic acid 4. 2-phenyl-2-phosphonopropionic acid 5. 2-phosphonopent-4-enoic acid 6. 2-methyl-2-phosphonopropionic acid 7. 2-butyl-2-phosphonohexanoic acid 8. 2-methyl-2-phosphonohexanoic acid 9. 2-methyl-3-phenyl-2-phosphonopropionic acid 10. 2,3-diphosphonopropionic acid 11. 1-phosphonopropane-1,2,3-tricarboxylic acid 12. 1-phosphonopropane-1,3-dicarboxylic acid 13. 3-methyl-1-phosphonopropane-1,3-dicarboxylic acid 14. 1-phosphonobutane-1,3,4-tricarboxylic acid 15. 1-phosphonopentane-1,3,5-tricarboxylic acid 16. 2,4-diphosphonobutyric acid 17. 2,4-diphosphonopentanoic acid 18. 3-phosphonopentane-1,3,5-tricarboxylic acid 19. 5-phosphonononane-1,3,5,7,9-pentacarboxylic acid 20. 3-phosphonoheptane-1,3-dicarboxylic acid 21. 1-phenyl-2-phosphonobutane-2,4-dicarboxylic acid 22. 3-phosphonopropionic acid 23. 3-phosphonobutanoic acid 24. 2-methyl-3-phosphonobutanoic acid 25. 3-phenyl-3-phosphonopropionic acid 26. 2-methyl-3-phosphonopropionic acid 27. 2-butyl-3-phosphonopropionic acid 28. 1-phosphonobutane-2,4-dicarboxylic acid 29. 2-phosphonomethylacrylic acid

In the Examples, the same numbering is used to designate the various compounds under test.

The phosphonic-carboxylic acids of the invention are mostly known compounds and are prepared by hydrolysis of the corresponding esters or nitriles. These phosphorous containing esters or nitriles are prepared by methods well known in the organo-phosphorus literature, namely:

When n = 1

A. These compounds may be prepared by base-catalysed addition of a dialkylphosphite to an .alpha., .beta.-unsaturated ester or nitrile (see e.g. Houben-Weyl, Methoden der Organischen Chemie, Band XII/1, pp. 465-74)

When n =0

The intermediate esters ##STR5## can be prepared in several ways.

B 1. By a Michaelis-Arbuzov reaction between an .alpha.-halocarboxylic ester or nitrile and a trialkylphosphite e.g. where R.sub.2 = R.sub.3 =H or R.sub.2 =H, R.sub.3 = Me (see e.g. Houben-Weyl, Methoden der Organischen Chemie, Band XII/1, p. 433).

B 2. By alkylation of an intermediate ester ##STR6## e.g. where R.sub.2 = H, R.sub.3 = Bu (see e.g. A.N. Pudovik et al., Zhur.Obshch.Khim, 1957, 27, 2367).

B 3. By base-catalysed addition of an intermediate ester ##STR7## to 1 or 2 moles of an .alpha., .beta.-unsaturated ester or nitrile (see e.g. A.N. Pudovik and N.M.Lebedeva, Zhur.Obshch. Khim. 1955, 25, 1920).

B 4. By a combination of (1) or (2) and (3) above.

The compound ##STR8## may be prepared as described by B.E. Ivanov et. al., Izv.Akad. Nauk. SSSR,Ser.Khim, 1969, 1851-3 The compound ##STR9## may be prepared as described by B.E. Ivanov et al., Izv.Akad. Nauk SSSR, Ser.Khim, 1970, 96-100

The following compounds of formula I are new and were prepared by the known methods outlined above.

______________________________________Compound of formula I Method of production______________________________________ ##STR10## B (3) ##STR11## B (3) ##STR12## B (2) and (3) ##STR13## B (3) ##STR14## B (3) ##STR15## A______________________________________ ##STR16## may be prepared by alkylation of intermediate ester ##STR17## (B.E. Ivanov et al., Izv. Akad. Nauk.SSSR,Ser.Khim., 1969,889-893) followed by hydrolysis and decarboxylation.

The addition of the compounds of formula I to aqueous systems had been found to inhibit the corrosion of ferrous metals in contact with the aqueous system and/or to inhibit the precipitation of scale-forming salts of calcium, magnesium, barium and strontium from the aqueous systems so treated.

In performing a role as a corrosion inhibitor, the compound of formula I may be used alone or in conjunction with other corrosion inhibitors such as zinc, phosphates, polyphosphates, nitrites e.g. sodium nitrile, sodium chromate, nitrates e.g. sodium nitrate, benzotriazole, bis-benzotriazole or copper-deactivating benzotriazole derivatives, N-acyl sarcozines, triethanolamines, fatty amines, and polycarboxylic acids e.g. polymaleic acid and polyacrylic acid as well as their respective alkali metal salts. The compounds of formula I have been found to be particularly active in inhibiting ferrous metal corrosion when used in conjunction with zinc ions, nitrite ions, phosphate ions, polyphosphate ions and benzotriazoles or derivatives thereof. Normally, the total amount of corrosion inhibitor will be within the range of from 1 to 200 ppm especially from 1 to 100 ppm of the aqueous system.

Combinations of corrosion inhibitors according to the present invention preferably contain from 20 to 97.5%, more preferably from 40 to 90% of the phosphonocarboxylic acid and from 2.5 to 80%, more preferably from 10 to 60% of the other corrosion inhibitor or inhibitors.

In their role as a scale-inhibitor, the compounds of formula I may be used alone or in conjunction with other compounds known to be useful in water treatment.

Dispersing and/or threshold agents may be used, such as for example polymerised acrylic acid and its salts, hydrolysed polyacrylonitrile, polymerised methacrylic acid and its salts, polyacrylamide and co-polymers thereof from acrylic and methacrylic acids, lignin sulphonic acid and its salts, tannin, naphthalene sulphonic acid/formaldehyde condensation products, starch and its derivatives, and cellulose. Specific threshold agents such as for example, hydrolysed polymaleic anhydride and its salts, alkyl phosphonic acids, 1-aminoalkyl, 1,1-diphosphonic acids and their salts and alkali metal phosphates, may also be used.

Precipitating agents such as alkali metal orthophosphates, carbonates and hydroxides, oxygen scavengers such as alkali metal sulphites and hydrazine, sequestering agents such as nitrilotriacetic acid and their salts, ethylene diamine tetraacetic acid and its salts, antifoaming agents such as distearylsebacamide, distearyl adipamide and related products derived from ethylene oxide condensations, in addition to fatty alcohols, such as capryl alcohols and their ethylene oxide condensates may also be used.

In addition to their use in purely aqueous systems, the phosphonocarboxylic acids, alone or in admixture with other corrosion inhibitors, are also useful in systems containing only a proportion of water such as hydraulic fluids and cutting fluids.

The following Examples further illustrate the present invention. Parts and percentages shown therein are by weight unless otherwise stated.

EXAMPLE 1

A mixture of triethylphosphonoacetate (11.2 parts) and diethylvinylphosphonate (8.2 parts) was heated to 40.degree. C and treated with 5 drops of a saturated solution of sodium ethoxide in ethanol. When the exothermic reaction had subsided (maximum temp. 110.degree.) the resulting mixture was heated at 100.degree. for 1 hour, then cooled and dissolved in 100 parts by volume of chloroform. The chloroform solution was washed with water, dried over MgSO.sub.4 and distilled to give 7 parts of the pentaethyl ester of 2,4-diphosphonobutyric acid, boiling at 184.degree.-190.degree./4mm.

Hydrolysis of this material by heating at reflux in 75 parts by volume of 18% hydrochloric acid gave, after evaporation, 2,4-diphosphonobutyric acid hydrate as a highly viscous oil, having the following elemental analysis by weight:

Calculated for C.sub.4 H.sub.10 O.sub.8 P.sub.2.H.sub.2 O: C, 18.04%; H, 4.51%; P, 22.30%. Found: C, 17.84%; H, 4.43%; P, 22.73%.

EXAMPLE 2

A mixture of diethylvinyl phosphonate (16.4 parts) and diethylphosphonoacetonitrile (8.9 parts) was heated to 40.degree. and treated with 10 drops of a saturated solution of sodium ethoxide in ethanol. The resulting solution was heated at 100.degree. for 1 hour, cooled and dissolved in 100 parts by volume of chloroform. The chloroform solution was washed with water, dried over MgSO.sub.4 and the chloroform removed by evaporation to give a viscous residual oil (17 parts) comprising mainly of 3-cyano-1,3,5-tris(diethylphosphono) pentane.

Hydrolysis of this material in 100 parts by volume of refluxing 18% hydrochloric acid, followed by evaporation, redissolution in water and elution down an anion exchange column, and final evaporation to dryness, gave a hygroscopic sample of 1,3,5-triphosphonopentane-3 -carboxylic acid, having the following elemental analysis by weight:

Calculated for C.sub.6 H.sub.15 O.sub.11 P.sub.3.H.sub.2 O: C, 19.25%; H, 4.54%; P, 24.87%. Found: C, 19.08%; H, 4.87%; P, 23.64%.

EXAMPLE 3

A mixture of 2,4-dicyanobut-1-ene (21.2 parts) and triethylphosphonoacetate (44 parts) was treated with 10 drops of a saturated solution of sodium ethoxide in ethanol and heated at 100.degree. for 4 hours. The reaction solution was dissolved in chloroform (100 parts by volume) washed with water, dried over MgSO.sub.4 and distilled to give 19 parts of ethyl (2-diethylphosphono-4,6-dicyano)-hexanote boiling at 206.degree.-208.degree./O.lmm.

This material was heated to reflux for 18 hours in 150 parts by volume of 18% hydrochloric acid. After evaporation the residue was treated with 200 parts by volume of acetone and the insoluble NH.sub.4 Cl removed by filtration. Evaporation of the acetone gave 1-phosphonopentane-1,3,5-tricarboxylic acid (monohydrate) as a highly viscous oil having the following elemental analysis by weight

Calculated for C.sub.8 H.sub.13 O.sub.9 P.H.sub.2 O: C, 31.80%; H, 4.97%; P, 10.27%. Found: C, 32.23%; H, 5.25%; P, 10.43%.

EXAMPLE 4

A mixture of 2,4-dicyanobut-1-ene (21.2 parts) and diethylphosphonoacetonitrile was (17.7 parts) treated with 10 drops of saturated sodium ethoxide in ethanol as in Example 3 (above) to give an undistillable 2:1 adduct. This was hydrolysed and isolated as in Example 3 to give a crude sample of 5-phosphonononane-1, 3,5,7,9-pentacarboxylic acid, whose nuclear magnetic resonance spectrum ('H,.sup.31 P) was consistent with the proposed structure.

EXAMPLE 5

A mixture of 2,4-dicyanobut-1-ene (21.2 parts) and diethylphosphite (27.6 parts) was heated to 70.degree. and treated dropwise with a saturated solution of sodium ethoxide in ethanol until the exothermic reaction ceased. The reaction mass was cooled, treated with 2 parts by volume of acetic acid and distilled to give 29 parts of 1-diethylphosphono-2,4-dicyanobutane, boiling at 183.degree.-4.degree./0.2mm and having the following elemental analysis by weight:

Calculated for C.sub.10 H.sub.17 N.sub.2 O.sub.3 P: C, 49.20%; H, 7.02%; P, 11.48%. Found: C, 49.14%; H, 6.98%; P, 11.67%.

This material was hydrolysed and worked up as in Example 3 to give 1-phosphonobutane-2,4-dicarboxylic acid as a hydrate having the following elemental analysis by weight:

Calculated for C.sub.6 H.sub.11 O.sub.7 P.1.5 H.sub.2 O: C, 28.65%; H, 5.58%; P, 12.34%. Found: C, 28.73%; H, 5.20%; P, 12.35%.

EXAMPLE 6

Diethyl diethylphosphonomethylmalonate (31 parts) was added dropwise to a stirred solution of sodium (2.3 parts) in ethanol (250 parts by volume). After 15 mins the solution was treated n-butylbromide (15.3 parts). The mixture was stirred at 25.degree. for 30 mins and heated to reflux for a further 2 hours. After removal of the ethanol by evaporation the residual oil was taken up in chloroform (200 parts by volume), washed with water, dried over MgSO.sub.4 and distilled to give diethyl diethylphosphomomethylbutylmalonate (7.9 parts) boiling at 128.degree.-130.degree./0.1mm.

Hydrolysis of this material in refluxing 18% hydrochloric acid (100 parts by volume) gave after evaporation 3,4 parts of 2-phosphonomethylhexanoic acid hydrate, as a viscous oil having the following elemental analysis by weight:

Calculated for C.sub.7 H.sub.15 O.sub.5 P.H.sub.2 O: C, 36.84%; H, 7.46%; P, 13.60%. Found: C, 35.50%; H, 6.93%; P, 13.90%.

The nuclear magnetic resonance spectrum ('H,.sup.31 P) was consistent with the proposed structure.

EXAMPLES 7 to 38

Evaluation of Corrosion Inhibition by the Aerated Solution Bottle Test

To carry out the Aerated Solution Bottle Test, a standard corrosive water is made up from:

20 g. CaSO.sub.4 2H.sub.2 O

15 g. MgSO.sub.4 7H.sub.2 O

4.6 g. NaHCO.sub.3

7.7 g. CaCl.sub.2 6H.sub.2 O

45 gallons Distilled water

Mild steel coupons, 5 cms. .times. 2.5 cms are scrubbed with pumice, immersed for one minute in hydrochloric acid and then rinsed, dried and weighed.

The desired proportion of additive combination is dissolved in 100 ml. of standard corrosive water. A steel coupon is suspended in the solution, and the whole is stored in a bottle in a thermostat at 40.degree. C. During the storage period, air is passed into the solution at 500 ml/minute, the passage of the air being screened from the steel coupon; any water losses by evaporation are replaced as they occur with distilled water from a constant head apparatus.

After 48 hours, the steel coupon is removed, scrubbed with pumice, immersed for one minute in hydrochloric acid inhibited with 1% by weight of hexamine and then rinsed, dried and reweighed. A certain loss in weight will have occured.

A blank test i.e. immersion of a mild steel specimen in the test water in the absence of any potential corrosion inhibitor, is carried out with each series of tests. The corrosion rates are calculated in milligrams of weight loss/sq. decimeter/day (m.d.d.) but for convenience the results are shown as percentage protection, which is defined as follows: ##EQU1## The results obtained using individual corrosion inhibitors according to the invention are given in Table I.

TABLE I______________________________________Aerated Solution BottleTest for individual corrosion inhibitorsof formula IExample Corrosion Inhibitor under test % Protection______________________________________7 Compound No. 11 728 Compound No. 10 9810 Compound No. 26 9411 Compound No. 23 8312 Compound No. 3 80______________________________________

The results obtained in the Aerated Solution Bottle Test using mixtures of corrosion inhibitors consisting of a compound of formula I with zinc, nitrite and phosphate ions are shown in Table 2.

Table 2__________________________________________________________________________Aerated Solution Bottle Testresults using corrosion inhibitors of formula Iwith zinc, nitrite and phosphate ions. % Protection 50 ppm 50 ppm 50 ppm compound compound compound Blank corrosion +50 ppm +50 ppm +50 ppmExample Compound Rate (mdd) Zn++ NO.sub.2 HPO.sub.4 2--__________________________________________________________________________13 1 93 92 85 8614 2 78 49 -- 8915 3 83 92 95 8416 4 63 92 84 8317 10 92 87 68 9118 11 115 83 61 1519 15 83 100 90 9520 16 70 79 93 7921 18 100 99 29 022 19 109 89 87 4223 21 73 99 97 8224 22 92 100 99 3025 23 94 94 -- 3426 25 63 84 0 4627 26 83 96 96 2528 27 82 98 -- 1229 28 73 100 100 8430 29 103 95 93 83__________________________________________________________________________

The results obtained, using various combinations of corrosion inhibitors according to the invention, are set out below in Table 3.

Table 3__________________________________________________________________________Aerated Solution Bottle Test Resultsfor various combinations of corrosion inhibitorsof formula I with zinc, phosphate, nitrite orpolyphosphate ions.__________________________________________________________________________Example Compound 1 (ppm) Zinc (ppm) % Protection__________________________________________________________________________31 100 0 87 80 20 97 60 40 94 40 60 91 20 80 52 0 100 0 Blank corrosion rate 88 mdd__________________________________________________________________________Example Compound 1 (ppm) Phosphate (ppm) % Protection__________________________________________________________________________32 100 0 88 80 20 93 60 40 90 40 60 70 20 80 69 0 100 24 Blank corrosion rate 120 mdd__________________________________________________________________________Example Compound 3 (ppm) Zinc (ppm) % Protection__________________________________________________________________________33 100 0 98 80 20 90 60 40 92 40 60 96 20 80 64 0 100 0 Blank corrosion rate 73 mdd__________________________________________________________________________Example Compound 3 (ppm) Nitrite (ppm) % Protection__________________________________________________________________________34 100 0 87 80 20 93 60 40 94 40 60 100 2 80 93 0 100 0 Blank corrosion rate 109 mdd__________________________________________________________________________Example Compound 10 (ppm) Phosphate (ppm) % Protection__________________________________________________________________________35 50 0 61 40 10 54 30 20 95 20 30 85 10 40 74 0 50 26 Blank corrosion rate 97 mdd__________________________________________________________________________Example Compound 28 (ppm) Zinc (ppm) % Protection__________________________________________________________________________36 100 0 19 80 20 100 60 40 97 40 60 99 20 80 3 0 100 0 Blank corrosion rate 73 mdd__________________________________________________________________________Example Compound 28 (ppm) Nitrite (ppm) % Protection__________________________________________________________________________37 100 0 19 80 20 94 60 40 79 40 60 91 20 80 94 0 100 21 Blank corrosion rate 109 mdd__________________________________________________________________________ PolyphosphateExample Compound 29 (ppm) (ppm) % Protection__________________________________________________________________________38 50 0 41 40 10 76 30 20 72 20 30 61 10 40 41 0 50 0 Blank corrosion rate 64 mdd__________________________________________________________________________

EXAMPLES 39 to 43

Evaluation of Corrosion Inhibition by the Laboratory Heat Exchanger Rig Test

Some laboratory tests were carried out using a Laboratory Heat Exchanger Rig, a form of laboratory testing intended to similate practical use conditions more closely than does the Aerated Solution Bottle Test described in Examples 1-27.

In this rig, corrosive water is aerated and circulated over a number of metal coupons, and is heated by being passed through a heated steel heat exchanger tube. After a suitable test period, the metal coupons and the heat exchanger tube are examined, and their state assessed.

In detail, the rig consists of a closed water circuit, made up of the following items in order,

20 liter reservoir

1 liter reservoir

flow meter

coupon chamber

heat exchanger

cooling condenser

Corrosive water in the 20 liter reservoir is aerated with compressed air introduced through a sintered disc at about 5 liters per minute, and is then pumped to the 1 liter reservoir. From this reservoir it is pumped through the flow meter to the glass coupon chamber in which are a number of rectangular metal coupons each 2.5 by 5.0 cms. mounted on a perspex jig. The water then flows through the heat exchanger which is made up of a 5/8 inch internal diameter steel tube with copper end pieces around which is wound a 960 watt heater coil; from the heat exchanger the water flows through the cooling condenser back to the 20 liter reservoir.

A flow rate in the circuit of about 1.0 gallon per minute provides a velocity of about 1.5 feet per second and a Reynolds number of 8500 in the heat exchanger. The heater coil gives the heat exchanger tube a skin temperature of about 60.degree. C. and the water leaves at about 45.degree. C., a difference across the heat transfer surface of some 15.degree. C. The cooling condenser is so operated as to cool the water to about 40.degree. C. before it begins a fresh circuit.

Metal coupons are scrubbed with pumice and then immersed in acid as follows:

______________________________________metal acid______________________________________mild steel Conc. HCl diluted 1:1 with water at room temperature for 1 minutescopper "brass "aluminum 5% phosphoric acid/2% chromic acid, at 75.degree. C. for 5 minutes______________________________________ After such immersion, the coupons are rinsed with water, dried and weighed; they are then mounted on a perspex jig, care being taken to ensure that none of the coupons touch each other, and that they are insulated from the bolt holding the jig together. The heat exchanger tube is cleaned with pumice dipped in conc. hydrochloric acid diluted 1:1 with water, and then rinsed in water and dried.

The rig is assembled, and cleaned thoroughly by circulating conc. hydrochloric acid diluted 1:1 with water, then flushing with tap water for about half an hour (about 30 gallons in all) and draining. The necessary quantity of additives to produce the desired concentrations is put into one of the reservoirs and the rig is filled with 22 litres of a standardised corrosive test water, which is characterised as follows:

______________________________________Phenol Alkalinity : 0Total Alkalinity : 20Temp. Hardness : 20 as p.p.m. of CaCO.sub.3Perm. Hardness : 0Total Hardness : 20Chloride : 15 p.p.m.Total Dissolved Solids : 70 p.p.m.______________________________________ The pump is primed and started, and the heater switched on.

The concentration of inhibitor and the water level in the rig are checked daily.

After approximately ten days, the heat exchanger tube is removed, sectioned and examined. The test coupons are removed and the mild steel, brass and copper coupons are cleaned as before except that the acid is inhibited with 1% hexamine, rinsed, dried and reweighed. The aluminium specimens are scrubbed, dried and re-weighed.

The results observed enable an assessment to be made of the anti-corrosive action of the inhibitor under test.

Using this test procedure the following results were obtained as shown in Table 4, following.

Table 4__________________________________________________________________________Laboratory Heat Exchanger Rig TestsInitial level Length Corrosion Rates (mdd) of corrosion of Test Mild Cast Alum- Sol- Cop-Ex. inhibitor (Days) steel iron inium der per Brass__________________________________________________________________________-- None 17 142.5 89.1 2.0 5.0 1.9 1.6 Compound 1 40ppm +Zinc 10ppm39 13 2.7 7.2 1.2 3.2 0 0.1 + Benzotri- zole 2ppm Compound 1 30ppm + Zinc 10ppm + Polyphos-40 8 15.9 52.0 1.1 5.5 1.2 1.5 phate 10ppm + Benzotri- azole 2ppm Compound 26 40ppm + Zinc 10ppm41 13 5.0 46.2 0.9 3.5 0.1 0.1 + Benzotri- azole 2ppm Compound 28 75ppm + Zinc 25ppm42 10 24.4 37.7 1.5 4.4 0 0.3 + Benzotri- azole 2ppm Compound 29 24ppm + Zinc 24ppm + Polyphos-43 11 2.6 1.4 0.1 0 0.2 0.2 phate 10ppm + Benzotri- azole 2ppm__________________________________________________________________________

EXAMPLES 44 AND 45

Evaluation of Anti-Scaling Activity

A mild steel heater sheath into which was inserted a 1 KW Firerod cartridge heater was immersed in a solution containing Mg.sup.2+ ions and HCO.sub.3.sup.- ions. 2 Liters of a solution containing 6.5 g/l. Mg (NO.sub.3).sub.2.6H.sub.2 O and 2 liters of a solution containing 4.0 g/l. NaHCO.sub.3 were prepared. The additive to be evaluated was added to the magnesium nitrate solution, the additive concentration being calculated on the total 4 liters of solution. 1 Liter of each solution was mixed in a beaker and the heater sheath immersed in the solution. As the solution evaporated the remaining 2 liters of mixed solutions were added at such a rate that a constant volume of 2 liters was maintained in the test solution. After 5 hrs., 2 liters of the solution had evaporated, giving a concentration factor of 2. The heater sheath was removed from the solution and allowed to dry. The weight of scale formed on the sheath was recorded and the thickness of the scale deposit around the central part of the sheath measured using an Elcometer. The magnesium content of the final solution was determined by titration.

The results obtained using two individual compounds of formula I in this test are set out in Table 5. When the test is operated in the absence of additive the final solution is cloudy due to precipitated magnesium hydroxide, hence the result shown in Table 5 for the blank is not a true indication of the result.

Table 5______________________________________High Temperature Scale Test Results Wt. Scale ppm M.sub.g.sup.2+ of Thick- in Conc. Scale ness final TypeEx. Compound ppm. gm. thou. solution of Scale______________________________________44 Compound 10 0.725 3-5 357.3 V. hard No. 16 non-uni- form45 Compound 10 0.64 4-5 345.3 V.hard No. 11 non-uni- form-- Control -- 2.1 20 150 --______________________________________

EXAMPLES 46 TO 49

Evaluation of Corrosion Inhibition in Aqueous Hydraulic Systems

The following method is a modification of the Institute of Petroleum's Test Method IP 287/74.

1.0%, 0.5% and 0.25% weight/volume solutions of various compounds of formula I were prepared in deionised water and neutralized to pH 8.0 with triethanolamine.

Cast iron chips were prepared, sieved, washed and dried in accordance with the IP 287 procedure and placed on a filter paper contained in a petri dish in order to cover a 35 mm square. 2 ml. of the solution under test were pipetted over the chips to wet them uniformly and the dish was covered with a lid. After two hours the chips were washed from the filter paper which was then dried with warm air. If corrosion of the cast iron chips occurs, brown spots develop on the filter paper to an extent which is dependent upon the degree of corrosion. A visual assessment of the total area of these spots is made with the aid of a graticule and the result is expressed as a percentage of the total surface area. Diffuse staining is ignored.

The results obtained are set out in the following Table 6.

Table 6______________________________________Modified IPTM 287/74 Results Compound of Concentration of Area covered byEx. formula I Compound I (%) rust (%)______________________________________-- -- -- 4046 Compound No. 1 1.00 0 0.50 0 0.25 1047 Compound No. 12 1.00 0 0.50 0 0.25 1048 Compound No. 29 1.00 3 0.50 5 0.25 1549 Compound No. 26 1.00 0-1 0.50 5 0.25 15______________________________________

Claims

1. A method of treating an aqueous system to inhibit the corrosion of metals in contact therewith and to inhibit the deposition of scale therefrom which comprises

adding to the aqueous system a minor proportion of a compound of the formula ##STR18## wherein n is 0 or 1, and when n is 0, R.sub.3 and R.sub.4 are each hydrogen; or when n is 1, R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are each hydrogen; or when n is 1, R.sub.1, R.sub.2 and R.sub.3 are hydrogen, and R.sub.4 is methyl.

2. A method as claimed in claim 1 wherein the water-soluble salt of the compound of formula I is an alkali metal salt, an ammonium salt or an amine salt.

3. A method as claimed in claim 1 wherein the water-soluble partial ester of the compound of formula I is derived from an alcohol having from 1 to 4 carbon atoms.

4. A method as claimed in claim 1 wherein n is 0 and R.sub.3 and R.sub.4 are each hydrogen.

5. A method as claimed in claim 1 wherein the compound of formula I is used in conjunction with other corrosion inhibitors.

6. A method as claimed in claim 5 wherein the other corrosion inhibitors are zinc, phosphates, polyphosphates, nitrites, sodium chromate, nitrates, benzotriazole, bis-benzotriazole or copper-deactivating benzotriazole derivatives, N-acyl sarcosines, triethanolamines, fatty amines or polycarboxylic acids.

7. A method as claimed in claim 6 wherein the other corrosion inhibitors are zinc ions, nitrite ions, phosphate or polyphosphate ions or benzotriazoles or derivatives thereof.

8. A method as claimed in claim 7 wherein the corrosion inhibitor of formula I is such that n is 0 and R.sub.3 and R.sub.4 are each hydrogen and the other corrosion inhibitors are zinc and benzotriazole.

9. A method as claimed in claim 7, wherein the corrosion inhibitor of formula I is such that n is 1 and R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are each hydrogen and the other corrosion inhibitors are zinc and benzotriazole.

10. A method as claimed in claim 7 wherein the corrosion inhibitor of formula I is such that n is 1, R.sub.1, R.sub.2 and R.sub.3 hydrogen and R.sub.4 is methyl and the other corrosion inhibitors are zinc and benzotriazole.

11. A method as claimed in claim 1 wherein the total amount of corrosion inhibitor is within the range of from 1 to 200 ppm.

12. A method as claimed in claim 11 wherein the total amount of corrosion inhibitor is within the range of from 1 to 100 ppm.

13. A method as claimed in claim 5 wherein the corrosion inhibitor mixture contains 20 to 97.5% of the compound of formula I and 2.5 to 80% of the other corrosion inhibitor or inhibitors.

14. A method as claimed in claim 13 wherein the corrosion inhibitor mixture contains 40 to 90% of the compound of formula I and from 10 to 60% of the other corrosion inhibitor or inhibitors.