Claims
- 1. A process for reducing or preventing the corrosion of ferrous alloys in contact with corrosive liquids or gases which process comprises contacting the surface of said ferrous metal alloy with a corrosive inhibiting amount of a corrosion inhibitor composition comprising the reaction product of
- (I) the product resulting from reacting at a temperature of from about 0.degree. C. to about 150.degree. C.
- (A) at least one aliphatic .alpha.,.beta.-monoethylenically unsaturated aldehyde having from about 3 to about 6 carbon atoms; and
- (B) at least one organic polyamine represented by the formula ##STR4## wherein R is a divalent saturated C.sub.2 to C.sub.4 aliphatic hydrocarbon group; each R.sup.1 and R.sup.2 is independently hydrogen or a saturated alkyl amino or alkyloxy group containing from 2 to about 4 carbon atoms or when taken together, R.sup.1 and R.sup.2 form a bridging alkylene radical containing from 2 to about 4 carbon atoms such that R, R.sup.1 and R.sup.2 and two nitrogen atoms form a heterocyclic ring containing 4 carbon atoms; x has a value from 1 to about 8; and components (A) and (B) are employed in a mole ratio of (A) to (B) of from about 1:1 to abaout 1:6, and wherein
- said reaction product of components (A) and (B) is thermally treated at a temperature of at least about 180.degree. C. for a time sufficient to render the resultant thermally treated product with a stability temperature at least 25.degree. C. above the stability temperature of the untreated product; and
- (II) (A) at least one saturated or unsaturated, cyclic or acyclic aliphatic mono- or polycarboxylic acid having from about 2 to about 54 carbon atoms; or
- (B) at least one saturated or unsaturated, cyclic or acyclic aliphatic mono- or polyalkyl halide having from about 2 to about 50 carbon atoms; or
- (C) a combination of (II-A) and (II-B);
- wherein components (I) and (II) are employed in quantities which provide from about 0.4 to about 1 equivalent of carboxyl or halide groups from component (II) for each theoretically active amino hydrogen atom contained in component (I).
- 2. A process of claim 1 wherein
- (a) said thermal treatment is conducted at a temperature of from about 190.degree. C. to about 350.degree. C. for from about 10 minutes to about 48 hours;
- (b) component (II-A) has from about 12 to about 36 carbon atoms; and
- (c) components (I) and (II) are employed in quantities which provide from about 0.55 to about 0.85 equivalent of carboxyl or halide groups from oomponent (II) for each theoretically active amino hydrogen atom contained in component (I).
- 3. A process of claim 2 wherein;
- (a) component (II-A) has from about 16 to about 20 carbon atoms; and
- (b) components (I) and (II) are employed in quantities which provide from about 0.65 to about 0.75 equivalent of carboxyl or halide groups from component (II) for each theoretically active amino hydrogen atom contained in component (I).
- 4. A process of claim 3 wherein
- (a) component (I) (A) is acrolein, crotonaldehyde, or combination thereof;
- (b) component (I) (B) is ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, hexaethyleneheptamine or any combination thereof; and
- (c) component (II) is tall oil fatty acid, dimerized tall oil fatty acid, trimerized tall oil fatty acid or any combination thereof.
- 5. A process of claim 2 wherein the reaction product of components (I-A) and (I-B) is an oligomer having an amine hydrogen equivalent weight of from about 50 to about 80.
- 6. A process of claim 3 wherein the reaction product of components (I-A) and (I-B) is an oligomer having an amine hydrogen equivalent weight of from about 50 to about 80.
- 7. A process of claim 4 wherein the reaction product of components (I-A) and (I-B) is an oligomer having an amine hydrogen equivalent weight of from about 50 to about 80.
- 8. A process of claim 1 wherein said corrosion inhibitor composition is employed in an amount of from about 5 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment or piping, either above ground or down hole.
- 9. A process of claim 8 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 50 to about 1000 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 10,000 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 10. A process of claim 9 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 100 to about 200 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 40,000 to about 60,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 11. A process of claim 10 wherein said corrosion inhibitor is dissolved or dispersed in a carrier liquid which in turn is dissolved or dispersed in said corrosive liquid or gas.
- 12. A process of claim 2 wherein said corrosion inhibitor composition is employed in an amount of from about 5 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 13. A process of claim 12 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 50 to about 1000 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 10,000 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 14. A process of claim 13 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 100 to about 200 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 40,000 to about 60,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 15. A process of claim 14 wherein said corrosion inhibitor is dissolved or dispersed in a carrier liquid which in turn is dissolved or dispersed in said corrosive liquid or gas.
- 16. A process of claim 3 wherein said corrosion inhibitor composition is employed in an amount of from about 5 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 17. A process of claim 16 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 50 to about 1000 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 10,000 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 18. A process of claim 17 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 100 to about 200 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 40,000 to about 60,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 19. A process of claim 18 wherein said corrosion inhibitor is dissolved or dispersed in a carrier liquid which in turn is dissolved or dispersed in said corrosive liquid or gas.
- 20. A process of claim 4 wherein said corrosion inhibitor composition is employed in an amount of from about 5 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 21. A process of claim 20 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 50 to about 1000 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 10,000 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 22. A process of claim 21 wherein when the prooess is a continuous treatment, the amount of corrosion inhibitor is from about 100 to about 200 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 40,000 to about 60,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 23. A process of claim 22 wherein said corrosion inhibitor is dissolved or dispersed in a carrier liquid which in turn is dissolved or dispersed in said corrosive liquid or gas.
- 24. A process of claim 5 wherein said corrosion inhibitor composition is employed in an amount of from about 5 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 25. A process of claim 24 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 50 to about 1000 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 10,000 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 26. A process of claim 25 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 100 to about 200 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 40,000 to about 60,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 27. A process of claim 26 wherein said corrosion inhibitor is dissolved or dispersed in a carrier liquid which in turn is dissolved or dispersed in said corrosive liquid or gas.
- 28. A process of claim 6 wherein said corrosion inhibitor composition is employed in an amount of from about 5 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 29. A process of claim 28 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 50 to about 1000 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 10,000 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 30. A process of claim 29 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 100 to about 200 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 40,000 to about 60,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 31. A process of claim 30 wherein said corrosion inhibitor is dissolved or dispersed in a carrier liquid which in turn is dissolved or dispersed in said corrosive liquid or gas.
- 32. A process of claim 7 wherein said corrosion inhibitor composition is employed in an amount of from about 5 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 33. A process of claim 32 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 50 to about 1000 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 10,000 to about 100,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 34. A process of claim 33 wherein when the process is a continuous treatment, the amount of corrosion inhibitor is from about 100 to about 200 and when the process is a batch treatment, then the amount of corrosion inhibitor is from about 40,000 to about 60,000 parts per million parts by weight based upon the weight of the corrosive liquid or gas in contact with said ferrous metal alloy and said ferrous metal alloy is in the configuration of brine, oil or gas well production equipment and piping either above ground or down hole.
- 35. A process of claim 34 wherein said corrosion inhibitor is dissolved or dispersesd in a carrier liquid which in turn is dissolved or dispersed in said corrosive liquid or gas.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of application Ser. No. 691,329, Jan. 14, 1985 now abandoned.
US Referenced Citations (10)