Patent Application
20100021750
1. Field of Endeavor
The present invention relates to corrosion resistant materials and more particularly to corrosion resistant amorphous materials and methods of forming corrosion resistant amorphous materials.
2. State of Technology
U.S. Pat. No. 6,767,419 for methods of forming hardened surfaces issued Jul. 27, 2004 to Daniel Branagan and assigned to Bechtel BWXT Idaho, LLC, provides the following state of technology information, “Both microcrystalline grain internal structures and metallic glass internal structures can have properties which are desirable in particular applications for steel. In some applications, the amorphous character of metallic glass can provide desired properties. For instance, some glasses can have exceptionally high strength and hardness. In other applications, the particular properties of microcrystalline grain structures are preferred. Frequently, if the properties of a grain structure are preferred, such properties will be improved by decreasing the grain size. For instance, desired properties of microcrystalline grains (i.e., grains having a size on the order of 10−6 meters) can frequently be improved by reducing the grain size to that of nanocrystalline grains (i.e., grains having a size on the order of 10−9 meters). It is generally more problematic to form grains of nanocrystalline grain size than it is to form grains of microcrystalline grain size. Accordingly, it is desirable to develop improved methods for forming nanocrystalline grain size steel materials. Further, as it is frequently desired to have metallic glass structures, it is desirable to develop methods of forming metallic glasses.”
United States Patent Application No. 2003/0051781 for hard metallic materials, hard metallic coatings, methods of processing metallic materials and methods of producing metallic coatings by Daniel J. Branagan published Mar. 20, 2003 provides the following state of technology information, “Both microcrystalline grain internal structures and metallic glass internal structures can have properties which are desirable in particular applications for steel. In some applications, the amorphous character of metallic glass can provide desired properties. For instance, some glasses can have exceptionally high strength and hardness. In other applications, the particular properties of microcrystalline grain structures are preferred. Frequently, if the properties of a grain structure are preferred, such properties will be improved by decreasing the grain size. For instance, desired properties of microcrystalline grains (i.e., grains having a size on the order of 10−6 meters) can frequently be improved by reducing the grain size to that of nanocrystalline grains (i.e., grains having a size on the order of 10−9 meters). It is generally more problematic, and not generally possible utilizing conventional approaches, to form grains of nanocrystalline grain size than it is to form grains of microcrystalline grain size.”
Features and advantages of the present invention will become apparent from the following description. Applicants are providing this description, which includes drawings and examples of specific embodiments, to give a broad representation of the invention. Various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this description and by practice of the invention. The scope of the invention is not intended to be limited to the particular forms disclosed and the invention covers all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the claims.
The present invention provides a method of coating a surface comprising the steps of providing a source of amorphous metal, providing ceramic particles, and applying the amorphous metal and the ceramic particles to the surface by a spray. The amorphous metal is Fe-based, Ni-based, Cu-based, Al-based, or Zr-based amorphous metal. The ceramic particles have a size within the range of nanometers to microns.
In one embodiment of the present invention the amorphous metal includes yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), and carbon (≧4 atomic %). In one embodiment of the present invention the ceramic particles have a size within the range of 5 nanometers to 5 microns. In one embodiment of the present invention the step of applying the amorphous metal and the ceramic particles to the surface by a spray comprises spraying alternating layers to the surface wherein at least one of the alternating layers contains amorphous metal including yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), carbon (≧4 atomic %) and ceramic particles having a size with the range of nanometers to microns.
In another embodiment of the present invention the amorphous metal includes yttrium, chromium, molybdenum, tungsten, boron, and carbon, at any composition where glass formation can occur. In this embodiment of the present invention the ceramic particles have a size within the range of 5 nanometers to 5 microns.
In yet another embodiment of the present invention, a metal-ceramic composite coating consisting of a homogenous mixture of ceramic particles and an amorphous-metal binder, with an appropriate bonding or transition layer is envisioned.
In yet another embodiment of the present invention, a metal-ceramic composite coating consisting of a homogeneous mixture of amorphous metal particles and a soft metal binder, sufficiently soft to enable application with cold spray technology, with an appropriate bonding or transition layer is envisioned.
In yet another embodiment of the present invention the step of applying the amorphous metal and the ceramic particles to the surface by a spray comprises spraying alternating layers to the surface wherein at least one of the alternating layers contains amorphous metal including yttrium, chromium, molybdenum, tungsten, boron, and carbon, and ceramic particles having a size with the range of nanometers to microns, as shown in
The present invention also provides a coating comprising a composite material made of amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles. In one embodiment of the present invention the amorphous metal and ceramic particles form a layered metal-ceramic composite material with alternating layers of amorphous metal and ceramic particles. In one embodiment of the present invention the amorphous metal and ceramic particles form a layered metal-ceramic composite material with alternating layers of amorphous metal and ceramic particles and wherein there are interfaces between the layers with sharp changes in composition at the interfaces. In one embodiment of the present invention the amorphous metal and ceramic particles form a layered metal-ceramic composite material with alternating layers of amorphous metal and ceramic particles and wherein there are interfaces between the layers with compositional gradients at the interfaces.
The present invention also provides a coating comprising a composite material made of amorphous metal that contains one or more of the following elements in any range of composition that yields an amorphous metal: yttrium, chromium, molybdenum, tungsten, boron or carbon, and ceramic particles. In one embodiment of the present invention the amorphous metal and ceramic particles form a layered metal-ceramic composite material with alternating layers of amorphous metal and ceramic particles. In one embodiment of the present invention the amorphous metal and ceramic particles form a layered metal-ceramic composite material with alternating layers of amorphous metal and ceramic particles and wherein there are interfaces between the layers with sharp changes in composition at the interfaces. In one embodiment of the present invention the amorphous metal and ceramic particles form a layered metal-ceramic composite material with alternating layers of amorphous metal and ceramic particles and wherein there are interfaces between the layers with compositional gradients at the interfaces.
The invention is susceptible to modifications and alternative forms. Specific embodiments are shown by way of example. It is to be understood that the invention is not limited to the particular forms disclosed. The invention covers all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the claims.
The accompanying drawings, which are incorporated into and constitute a part of the specification, illustrate specific embodiments of the invention and, together with the general description of the invention given above, and the detailed description of the specific embodiments, serve to explain the principles of the invention.
Referring to the drawings, to the following detailed description, and to incorporated materials, detailed information about the invention is provided including the description of specific embodiments. The detailed description serves to explain the principles of the invention. The invention is susceptible to modifications and alternative forms. The invention is not limited to the particular forms disclosed. The invention covers all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the claims.
Referring now to the drawings and in particular to
As illustrated in
As illustrated in
Referring now to
Referring now to
Referring now to
Referring now to
Corrosion costs the nation billions of dollars every year, with an immense quantity of material in various structures undergoing corrosion. For example, in addition to fluid and seawater piping, ballast tanks, and propulsions systems, approximately 345 million square feet of structure aboard naval ships and crafts require costly corrosion control measures. The use of the corrosion resistant amorphous metal-ceramic coating of the present invention to prevent the continuous degradation of this massive surface area would be extremely beneficial.
The corrosion resistant amorphous metal-ceramic coating of the present invention could also be used to coat the entire outer surface of containers for the transportation and long-term storage of high-level radioactive waste (HLW) spent nuclear fuel (SNF), or to protect welds and heat affected zones, thereby preventing exposure to environments that might cause stress corrosion cracking. In the future, it may be possible to substitute such high-performance iron-based materials for more-expensive nickel-based alloys, thereby enabling cost savings in various industrial applications.
The coating is formed by spray or deposition processing as illustrated in
Referring now to
Referring again to the drawings and in particular to
Referring again to the drawings and in particular to
In the system 400, a multi-layer corrosion resistant coating 404 is produced by spray processing. The spray processing forms a multiplicity of layers 401, 402, and 403 of the coating 404. The layers 401, 402, and 403 comprise amorphous metal and ceramic particles. As illustrated in
There are interfaces between the layers 401, 402, and 403. For example, an interface between the layers 401 and 402 gradually transition from the layer 401 that has a composition that is primarily amorphous metal to the layer 402 that has a composition that is amorphous metal and ceramic particles. An interface between the layers 402 and 403 gradually transition from the layer 402 that has a composition that is primarily ceramic particles to the layer 403 that has a composition that is primarily ceramic particles.
Referring again to the drawings and in particular to
The corrosion resistant amorphous metal-ceramic coating 504 is produced by spray processing to form a composite material on a structure 507. The spray processing forms alternating layers of the coating 504 and the alternate layers comprise amorphous metal and ceramic particles. As illustrated in
There are interfaces between the layers 501, 502, and 503. For example, an interface 505 between the layers 501 and 502 gradually transition from the layer 501 that has a composition that is primarily amorphous metal to the layer 502 that has a composition that is primarily ceramic particles. An interface 506 between the layers 502 and 503 gradually transition from the layer 502 that has a composition that is primarily ceramic particles to the layer 503 that has a composition that is primarily amorphous metal.
The alternate layers 501, 502, and 503 provide a coating that is a composite material. The at least one of the layers 501, 502, or 503 is a corrosion resistant amorphous metal-ceramic coating made of amorphous metal and ceramic particles. The composite material has the composition of an iron-based amorphous metal, and is made of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), carbon (≧4 atomic %) and ceramic p articles 5 nanometers to 5 microns.
In another embodiment of this invention, alternate layers 501, 502, and 503 provide a coating that is a composite material. The at least one of the layers 501, 502, or 503 is a corrosion resistant amorphous metal-ceramic coating made of amorphous metal and ceramic particles. The composite material has the composition of amorphous metal made of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, carbon, and ceramic particles 5 nanometers to 5 microns.
A spray processing forms alternating layers of amorphous metal and ceramic particles. There are interfaces 505 and 506 between the layers 501, 502, and 503. The interfaces 505 and 506 between the layers gradually transition from a composition that is primarily amorphous metal to a composition that is primarily ceramic particles.
Referring now to
As illustrated in
The system 600 provides the corrosion resistant coating 601.
As illustrated in
As illustrated in
As illustrated in
As illustrated in
As illustrated in
Corrosion costs the nation billions of dollars every year. There is an immense quantity of material in various structures undergoing corrosion. For example, approximately 345 million square feet of structure aboard naval ships and crafts require costly corrosion control measures. In addition, fluid and seawater piping, ballast tanks, and propulsions systems require costly corrosion control measures. The use of advanced corrosion-resistant materials to prevent the continuous degradation of this massive surface area would be extremely beneficial.
Man-made materials with unusually long service lives are needed for the construction of containers and associated structures for the long-term storage or disposal of spent nuclear fuel (SNF) and high-level waste (HLW) in underground repositories. Man has never designed and constructed any structure or system with the service life required by a SNF and HLW repository. Such systems will be required to contain these radioactive materials for a period as short as 10,000 years, and possibly as long as 300,000 years. The most robust engineering materials known are challenged by such long times. Thus, the ongoing investigation of newer, more advanced materials would be extremely beneficial.
The present invention provides a system for forming a coating comprising the steps of spray processing to form a composite material made of an iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. In another embodiment of the coating the amorphous metal includes the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %). The spray processing is thermal spray processing or cold spray processing.
The present invention also provides a system for forming a coating comprising the steps of spray processing to form a composite material made of amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. In another embodiment of the coating the iron-based amorphous metal includes the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon (no ceramic particles included). The spray processing is thermal spray processing or cold spray processing.
In different embodiments, the spray processing forms alternating layers of amorphous metal and ceramic particles wherein there are interfaces between the layers. In one embodiment the interfaces between the layers gradually transition from a composition that is primarily amorphous metal to a composition that is primarily ceramic particles. In another embodiment the interfaces between the layers that gradually transition from a composition that is primarily ceramic to a composition that is primarily amorphous metal.
There are many uses for the corrosion resistant amorphous metal-ceramic coating of the present invention. For example, the coating has application on ships; oil, gas, and water drilling equipment; earth moving equipment; tunnel-boring machinery; pump impellers and shafts; containers for shipment, storage and disposal of spent nuclear fuel; pressurized water and boiling water nuclear reactors; breeder reactors with liquid metal coolant; metal-ceramic armor; projectiles; gun barrels; tank loader trays; rail guns; non-magnetic hulls; hatches; seals; propellers; rudders; planes; and any other use where corrosion resistance is needed.
The use of the corrosion resistant amorphous metal-ceramic coating of the present invention to prevent the continuous degradation of fluid and seawater contact areas of surfaces including piping, ballast tanks, and propulsions systems, aboard naval ships and crafts would be extremely beneficial. The corrosion resistant amorphous metal-ceramic coating of the present invention can also be used to coat the outer surface of containers for the transportation and long-term storage of high-level radioactive waste (HLW) spent nuclear fuel (SNF), or to protect welds and heat affected zones, thereby preventing exposure to environments that might cause stress corrosion cracking.
Applicants have conducted studies and analysis of systems of the present invention. Examples of systems incorporating the present invention are provided below.
Example 1 is a specific example of a system incorporating the present invention. The system provides a corrosion resistant amorphous metal-ceramic coating. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles were used to form the coating.
In Example 1a at least one layer of the coating is formed by the Flame Spray Process (FSP) that uses a combustion flame and characterized by relatively low gas and particle velocities. The at least one layer of the coating produced by the Flame Spray Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Flame Spray Process is used for the deposition of at least one layer of the coating with desired degrees of residual porosity and crystallinity. The at least one layer of the coating produced by the Flame Spray Process has bond strengths of about 4,000 pounds per square inch, porosities of approximately 5 percent (5%), and micro-hardness of 85 HRB.
In Example 1b at least one layer of the coating is formed by the Flame Spray Process (FSP) that uses a combustion flame and characterized by relatively low gas and particle velocities. The at least one layer of the coating produced by the Flame Spray Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Flame Spray Process is used for the deposition of at least one layer of the coating with desired degrees of residual porosity and crystallinity. The at least one layer of the coating produced by the Flame Spray Process has bond strengths of about 4,000 pounds per square inch, porosities of approximately 5 percent (5%), and micro-hardness of 85 HRB.
Example 2 is another specific example of a system incorporating the present invention. The system provides at least one layer of a corrosion resistant amorphous metal-ceramic coating. The at least one layer of the corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles are used to form the coating.
In Example 2a the at least one layer of the coating is formed by the Wire Arc Process (WAP) that uses an electrical discharge instead of a combustion flame, and is more energetic than FSP. The at least one layer of the coating produced by the Wire Arc Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Wire Arc Process is used for the deposition of the at least one layer of the coating with desired degrees of residual porosity and crystallinity. The coating produced by the Wire Arc Process has bond strengths of about 5,800 pounds per square inch, porosities of approximately two percent (2%), and micro-hardness of 55 HRC.
In Example 2a the at least one layer of the coating is formed by the Wire Arc Process (WAP) that uses an electrical discharge instead of a combustion flame, and is more energetic than FSP. The at least one layer of the coating produced by the Wire Arc Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in any range of composition: yttrium; chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Wire Arc Process is used for the deposition of the at least one layer of the coating with desired degrees of residual porosity and crystallinity. The coating produced by the Wire Arc Process has bond strengths of about 5,800 pounds per square inch, porosities of approximately two percent (2%), and micro-hardness of 55 HRC.
Example 3 is another specific example of a system incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles are used to form the coating.
In Example 3 the coating is formed by the Plasma Spray Process (PSP) that involves the use of an electric arc with inert gas to create a plasma. Flame temperatures as high as 30,000° C. can be achieved.
The coating produced by the Plasma Spray Process is a composite material made of iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity. The coating produced by the Plasma Spray Process has bond strengths of about 8,000 pounds per square inch, porosities of approximately three percent (3%), and micro-hardness of 90 HRB.
The coating produced by the Plasma Spray Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity. The coating produced by the Plasma Spray Process has bond strengths of about 8,000 pounds per square inch, porosities of approximately three percent (3%), and micro-hardness of 90 HRB.
Example 4 is another specific example of a system incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles are used to form the coating.
In Example 4 the coating is formed by the Laser Assisted Plasma Spray Process (LAPSP). The Laser Assisted Plasma Spray Process was developed by Faunhoffer Institute and involves the direct interaction of a high-intensity laser beam with spray particles and the substrate. This process produces metallic coatings with virtually theoretical density and with metallurgical bonding. In regard to the distribution of energy released during the process, ninety to ninety-five percent (90-95%) of the energy is transferred from the plasma torch to the spray powder and used to melt the powder, while five to ten percent (5-10%) of the energy is consumed by the laser and ultimately used to fuse the spray particles and to melt the substrate.
The coating produced by the Plasma Spray Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Laser Assisted Plasma Spray Process (LA PSP) is used for the deposition of the coating with desired degrees of residual porosity and crystallinity.
The coating produced by the Plasma Spray Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Laser Assisted Plasma Spray Process (LAPSP) is used for the deposition of the coating with desired degrees of residual porosity and crystallinity.
Example 5 is another specific example of a system incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles are used to form the coating.
In Example 5 the coating is formed by the Water Stabilized Plasma Spray Process (WSPSP). The Water Stabilized Plasma Spray Process was recently developed by Caterpillar and provides the capability of spraying at extremely high rates, approaching 200 pounds per hour. This process has already been used for coating large components, such as the Caterpillar Model 3500 Diesel Engine block.
The coating produced by the Water Stabilized Plasma Spray Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (1.4 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity.
The coating produced by the Water Stabilized Plasma Spray Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity.
Example 6 is another specific example of a system incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles are used to form the coating.
In Example 6 the coating is formed by the High Velocity Oxy Fuel (HVOF) Process. The High Velocity Oxy Fuel Process involves a combustion flame, and is characterized by gas and particle velocities that are three to four times the speed of sound (mach 3 to 4).
The coating produced by the High Velocity Oxy Fuel Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity. The coat produced by the High Velocity Oxy Fuel Process has bond strengths of about 8,600 pounds per square inch, porosities of less than one percent (≦1%), and micro-hardness of 68 HRC.
The coating produced by the High Velocity Oxy Fuel Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity. The coat produced by the High Velocity Oxy Fuel Process has bond strengths of about 8,600 pounds per square inch, porosities of less than one percent (<1%), and micro-hardness of 68 HRC.
Example 7 is another specific example of a system incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles are used to form the coating.
In Example 7 the coating is formed by the Detonation Gun Process (DGP). The Detonation Gun Process was developed in Russia, and is based upon the discontinuous detonation of an oxygen-fuel mixture. Very high gas and particle velocities are achieved with this novel process, velocities approaching four to five times the speed of sound (mach 4-5).
The coating produced by the Detonation Gun Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity. The coating produced by the Detonation Gun Process has exceptional bond strengths, in excess of 10,000 pounds per square inch, porosities of less than one-half of one percent (<0.5%), and micro-hardness of 68 HRC.
The coating produced by the Detonation Gun Process is a composite material made of an iron-based amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity. The coating produced by the Detonation Gun Process has exceptional bond strengths, in excess of 10,000 pounds per square inch, porosities of less than one-half of one percent (<0.5%), and micro-hardness of 68 HRC.
Example 8 is another specific example of systems incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. Amorphous metal and ceramic particles are used to form the coating.
In the other Examples 8 the coating is formed by processes including HP HVOF, LA PSP, WS PSP, and DGP, and promise the advantages of fully dense coatings, improved bonding to substrates, and high rates of deposition. High-density infrared fusing with high-intensity lamps, a process developed by ORNL, may be used for postdeposition porosity and bonding control, provided that amorphous metals with sufficiently low critical cooling rates (CCRs) can be found.
The coating produced by the other Examples 8 is a composite material made of amorphous metal that contains one or more of the following elements in the specified range of composition: yttrium (≧1 atomic %), chromium (14 to 18 atomic %), molybdenum (≧7 atomic %), tungsten (≧1 atomic %), boron (≦5 atomic %), or carbon (≧4 atomic %) and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity.
The coating produced by the other Examples 8 is a composite material made of amorphous metal that contains one or more of the following elements in any range of composition: yttrium, chromium, molybdenum, tungsten, boron, or carbon and ceramic particles in the range of nanometers to microns. The Water Stabilized Plasma Spray Process is used for the deposition of the coating with desired degrees of residual porosity and crystallinity.
In other embodiments, the spray processing includes spray processing additional ingredients for the purpose of enhancing lubricity. For example, in one embodiment the spray processing includes spray processing graphite for the purpose of enhancing lubricity. In another embodiment, the spray processing includes spray processing fluorinated polymers for the purpose of enhancing lubricity.
In other embodiments, the spray processing includes dispersing the ceramic particles in the amorphous metal in situ through controlled thermally-driven internal oxidation or precipitation reaction. In other embodiments, the spray processing includes dispersing the ceramic particles in the amorphous metal in situ through controlled thermally-driven internal oxidation or precipitation reaction by heating from a thermal spray process. In other embodiments, the spray processing includes dispersing the ceramic particles in the amorphous metal in situ through controlled thermally-driven internal oxidation or precipitation reaction by heating from a high-intensity lamp. In other embodiments, the spray processing includes dispersing the ceramic particles in the amorphous metal in situ through controlled thermally-driven internal oxidation or precipitation reaction by heating from a laser. In other embodiments, the spray processing includes dispersing the ceramic particles in the amorphous metal in situ through controlled thermally-driven internal oxidation or precipitation reaction by heating from electrical resistance heating. In other embodiments, the spray processing includes dispersing the ceramic particles in the amorphous metal in situ through controlled thermally-driven internal oxidation or precipitation reaction by heating from a localized induction heating. In other embodiments, the spray processing includes dispersing the ceramic particles in the amorphous metal in situ through controlled thermally-driven internal oxidation or precipitation reaction by heating from a localized exothermic chemical reaction.
The system of forming a coating of the present invention includes the steps of using particle-size optimization to ensure that the amorphous metal particles are small enough to ensure that a critical cooling rate is achieved throughout the amorphous metal enabling the achievement of a fully dense metal-ceramic composite coating. For example, the present invention includes the steps of using particle-size optimization using small enough amorphous metal powder in a mixed metal-ceramic feed to ensure that the critical cooling rate is achieved throughout the amorphous metal, even in cases where the critical cooling rate may be relatively high (≧1000 K per second).
The system of forming a coating of the present invention includes the steps of post-spray high-density infrared fusing to achieve lower porosity and higher density, thereby enhancing corrosion resistance and damage tolerance of the coating. The system of forming a coating of the present invention includes the steps of post-spray high-density infrared fusing to achieve enhanced metallurgical bonding and to control damage tolerance through controlled devitrification of the amorphous metal.
In other embodiments, the system of forming a coating of the present invention utilizes ceramic particles having diameters in the range of nanometers to microns are used in the step of spray processing. For example, the system of forming a coating of the present invention utilizes ceramic particles having diameters in the range of five nanometers to five microns are used in the step of spray processing.
In other embodiments the system of forming a coating of the present invention, the ceramic particles used in the step of spray processing are produced by reverse micelle synthesis.
Example 9 is another specific example of a system incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The coating produced is a composite material. The composite material has the composition shown in Table 1. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles. In other embodiments, the amorphous metal is Fe-based, Ni-based, Cu-based, Al-based, or Zr-based amorphous metal.
Example 10 is another specific example of a system incorporating the present invention as illustrated by the system. The system provides a corrosion resistant amorphous metal-ceramic coating. The coating produced is a composite material. The composite material has the composition shown in Table 2. The corrosion resistant amorphous metal-ceramic coating is produced by spray processing to form a composite material made of amorphous metal and ceramic particles.
In different embodiments of a system incorporating the present invention the spray processing forms alternating layers of amorphous metal and ceramic particles. There are interfaces between the layers. In one embodiment the interfaces between the layers gradually transition from a composition that is primarily amorphous metal to a composition that is primarily ceramic particles. In another embodiment the interfaces between the layers that gradually transition from a composition that is primarily ceramic to a composition that is primarily amorphous metal.
While the invention may be susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and have been described in detail herein. However, it should be understood that the invention is not intended to be limited to the particular forms disclosed. Rather, the invention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the following appended claims.
This application is a Divisional of application Ser. No. 11/595,676 filed Nov. 9, 2006 and titled “Corrosion Resistant Amorphous Metals and Methods of Forming Corrosion Resistant Amorphous Metals” which claims benefit of U.S. Provisional Patent Application No. 60/736,792 filed Nov. 14, 2005 and titled “Corrosion Resistant Amorphous Metal and Ceramic Particle System” and co-pending application Ser. No. 12/571,535 filed Oct. 1, 2009 and titled “Corrosion Resistant Amorphous Metals and Methods of Forming Corrosion Resistant Amorphous Metals, and is incorporated herein by this reference.
The United States Government has rights in this invention pursuant to Contract No. DE-AC52-07NA27344 between the United States Department of Energy and Lawrence Livermore National Security, LLC for the operation of Lawrence Livermore National Laboratory.
| Number | Date | Country | |
|---|---|---|---|
| 60736792 | Nov 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11595676 | Nov 2006 | US |
| Child | 12572419 | US |