The present invention is directed to parts used in an outdoor or other corrosive environment and, more particularly, to an aluminum alloy part used in a corrosive environment.
Many parts used in an outdoor or other corrosive environment are manufactured from aluminum alloys. Such parts often are used in airplanes, automobiles, bicycles and fishing equipment. While aluminum alloys achieve strengths comparatively higher than steel through the use of a heat treatment, aluminum alloys also have relatively inferior corrosion resistance. Consequently, a surface treatment known as an alumite process normally is applied to aluminum alloy parts as a means to improve corrosion resistance.
Unfortunately, the alumite process itself creates some problems as shown in FIGS. 1(A)-1(C). As shown in
Japanese Laid-Open Patent Publication No. 1994-192888 discloses a method intended to improve the corrosion resistance of an aluminum alloy part by increasing the thickness of an alumite layer and by electrodepositing a cation resin onto the aluminum alloy part after the alumite process. While increasing the thickness of the alumite layer may improve corrosion resistance, it becomes more difficult to maintain a high-quality metallic luster of the aluminum alloy part. On the other hand, if the alumite process is not applied to the aluminum alloy part, then good corrosion resistance of the aluminum alloy part is lost.
The present invention is directed to various features of an aluminum alloy part and methods for manufacturing such a part. In one embodiment, a corrosion resistant part is provided for use in a corrosive environment. The part comprises an aluminum alloy part main body, an alumite layer disposed on the part main body, and a corrosion resistant layer disposed on the alumite layer. The part main body has a normal portion and a flawed portion. Thus, the alumite layer comprises a normal portion alumite layer formed on the normal portion and a flawed portion alumite layer formed on the flawed portion, and the corrosion resistant layer comprises a normal portion corrosion resistant layer formed on the normal portion and a flawed portion corrosion resistant layer formed on the flawed portion. The normal portion alumite layer has a thickness between approximately 0.5 microns and approximately 5.0 microns. The corrosion resistant layer is formed from an ionic resin and has a thickness less than or equal to approximately 5 microns.
Additional inventive features will become apparent from the description below, and such features alone or in combination with the above features may form the basis of further inventions as recited in the claims and their equivalents.
In Step S2, part main body 10 is subjected to an alumite process. Conventional alumite processes are performed using superimposed direct and alternating electrical currents. In this embodiment, however, direct electrical current is used, and the process is performed within sulfuric acid. More specifically, the alumite process is performed by immersing part main body 10 in sulfuric acid and applying a direct current with a current density between approximately 0.1 A/cm2 and approximately 6 A/cm2, preferably between approximately 0.5 A/cm2 and approximately 3 A/cm2, to produce the structure shown in
The alumite process also forms an alumite layer 20 on part main body 10. Alumite layer 20 comprises a normal portion alumite layer 21, disposed on flat normal portions 12 of part main body 10, and a flawed portion alumite layer 22 disposed on flawed portion 11 of part main body 10. In this embodiment, a thickness t1 of normal portion alumite layer 21 is controlled to be from approximately 0.5 microns and approximately 5 microns, preferably 2.0 microns, such that the metallic luster of aluminum alloy part 100 is not lost. The thickness of flawed portion alumite layer 22 is approximately 1.0 micron.
Alumite layer 20 has properties closely resembling an insulator. However, because of the different thicknesses of normal portion alumite layer 21 and flawed portion alumite layer 22, the electrical resistances of the two layers will differ. More specifically, an electrical resistance of normal portion alumite layer 21 will be greater than an electrical resistance of flawed portion alumite layer 22, so flawed portion alumite layer 22 will have good conductivity relative to normal portion alumite layer 21.
In Step S3, part main body 10 is subjected to a sealing process to improve corrosion resistance. In this embodiment, the sealing process is performed for a period of between approximately 1 minute and approximately 60 minutes, preferably approximately 10 minutes, in an acetic acid nickel solution at a temperature between approximately 80° C. and approximately 100° C., preferably 90° C. Although the sealing process produces a hydration reaction in one portion of the oxidation coating, comparatively stable hydrates can easily be obtained by these conditions. The differences in the conductivity of normal portion alumite layer 21 and the flawed portion alumite layer 22 still remain after this sealing process.
In Step S4, part main body 10 is subjected to an ionic resin electrodeposition process. More specifically, a voltage of between approximately 15 volts and approximately 70 volts, preferably between approximately 30 volts and approximately 50 volts, is applied with part main body 10 immersed within an aqueous solution to precipitate anion resin or cation resin. Preferably, a resin with high light permeability and excellent corrosion resistance is used for this purpose. This produces a corrosion resistant layer 30 comprising an anionic resin or cationic resin that restores the surface of the flawed portion 11 to the normal portion as shown in
As noted above, the conductivity of normal portion alumite layer 21 is less than flawed portion alumite layer 22, even after applying the sealing process in Step S3. Therefore, ionic resin with even higher light permeability and excellent corrosion resistance precipitates more readily through selective conduction onto flawed portion alumite layer 22 than onto normal portion alumite layer 21. This results in a corrosion resistant layer 30 comprising a normal portion corrosion resistant layer 31, disposed on normal portion alumite layer 21, and a flawed portion corrosion resistant layer 32 that is preferentially precipitated onto flawed portion alumite layer 22. A thickness t2 of normal portion corrosion resistant layer 31 is controlled to be 5 microns or less, preferably 0.7 microns, to control the appearance of the film coating (e.g., reduce muddiness, roughness, cloudiness, etc.). As a result of the foregoing process steps, corrosion resistance is improved while maintaining high-quality metallic luster of the aluminum alloy.
In Step S5, aluminum alloy part 100 is subjected to a high temperature bonding and drying process to strengthen the combination of materials coated on the surface of aluminum alloy part 100. More specifically, it is possible to change the organic compound of the ionic resin to a macromolecular organic compound. A double combination or triple combination portion with a molecular structure can be opened and a molecular bridging action brought into play to further improve corrosion. Applying the bonding and drying process in this manner makes it possible to additionally improve the corrosion resistance while maintaining high-quality metallic luster of the aluminum alloy.
While the above is a description of various embodiments of inventive features, further modifications may be employed without departing from the spirit and scope of the present invention. For example, the size, shape, location or orientation of the various components may be changed as desired. Components that are shown directly connected or contacting each other may have intermediate structures disposed between them. The functions of one element may be performed by two, and vice versa. The structures and functions of one embodiment may be adopted in another embodiment. It is not necessary for all advantages to be present in a particular embodiment at the same time. Every feature that is unique from the prior art, alone or in combination with other features, also should be considered a separate description of further inventions by the applicant, including the structural and/or functional concepts embodied by such feature(s). Thus, the scope of the invention should not be limited by the specific structures disclosed or the apparent initial focus or emphasis on a particular structure or feature.