Corrosion resistant wire-grid polarizer and method of fabrication

Information

  • Patent Grant
  • 6785050
  • Patent Number
    6,785,050
  • Date Filed
    Thursday, May 9, 2002
    22 years ago
  • Date Issued
    Tuesday, August 31, 2004
    20 years ago
Abstract
A polarizing device, such as a wire-grid polarizer, includes a substantial mono-layer of a corrosion inhibitor without adversely affecting the optical properties of the polarizing device. The polarizing device can include an optical element and a nano-structure, such as an array of a plurality of spaced-apart, elongated elements disposed on a substrate. The corrosion inhibitor is chemically bonded to surfaces of the elements to form the mono-layer. The mono-layer can have a thickness less than 100 Angstroms. A method of forming the substantial mono-layer can include treating the polarizing device with an amino phosphonate, such as a nitrilotris (methylene) triphosphonic acid.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates generally to wire-grid polarizers for physically decoupling two orthogonal porlarizations of visible or near-visible light. More particularly, the present invention relates to a corrosion resistant wire-grid polarizer, and a method for treating such a wire-grid polarizer to resist reactivity.




2. Related Art




Wire-grid polarizers have been developed that are operable in the visible and near-visible spectrum of electromagnetic radiation or light to generally decouple the two orthogonal polarizations of the light. Such wire-grid polarizers can be useful in optical systems such as image projections systems and image display systems.




Concerns exist, however, about the durability or long-term integrity of the wire-grid polarizers. Specifically, it is a concern that the conductive elements may be susceptible to corrosion or deterioration, especially in situations or applications where humidity or moisture and heat are present. It will be appreciated that the extremely small size of the grids may make the grids more susceptible to corrosion, or may exacerbate the results of such corrosion. The corrosion of the grids can reduce or destroy the ability of the grids to decouple the orthogonal polarizations of the light, thus defeating the purpose of the polarizer. In addition, the corrosion of the grids can detrimentally affect or alter the properties of the light, thus frustrating the operation or performance of the optical system.




Simply encapsulating the grids in order to protect the grids raises additional concerns. In addition to decoupling the orthogonal polarizations of light, it also is desirable that the wire-grid polarizer otherwise unalter the light. The material used to encapsulate the grids can create an interface between the material and the elements or the substrate that can alter various properties of the polarizer. Thus, encapsulating the grids might protect the elements, but also might undesirably alter other properties of the polarizer, thus affecting properties of the light, again frustrating the operation or performance of the optical system.




SUMMARY OF THE INVENTION




It has been recognized that it would be advantageous to develop a polarizing device, such as a wire-grid polarizer, that decouples orthogonal polarization of visible and near-visible light, resists corrosion or reactivity, and that otherwise does not undesirably alter the light. In addition, it has been recognized that it would be advantageous to develop a method for fabricating such a wire-grid polarizer, or for treating such a wire-grid polarizer, to resist corrosion or reactivity, without otherwise undesirably altering the light, and which is inexpensive.




The invention provides a corrosion resistant polarizer device, such as a wire grid polarizer, for generally decoupling two orthogonal polarizations of electromagnetic waves within wavelengths within the range of ultraviolet, visible and infra-red, such as visible visible light. The polarizer device can include an optical element with a nano-structure. The optical element can include a transparent substrate having an optical property of transmitting the electromagnetic waves or visible light therethrough. The nano-structure can include an array of spaced-apart, elongated elements disposed on the substrate. The elements can be sized to interact with electromagnetic waves of the electromagnetic waves or visible light to generally transmit electromagnetic waves of one polarization, and generally reflect electromagnetic waves of another polarization. A substantial mono-layer advantageously can be chemically bonded to, or reacted with, the elongated elements, or a native oxide layer on the elements, without substantially adversely effecting the optical property of the transparent substrate to transmit the electromagnetic waves or visible light, and without substantially adversely altering the electromagnetic waves or visible light transmitted through the array of spaced-apart, elongated elements and the transparent substrate. The mono-layer can be formed from a corrosion inhibitor, and can have a thickness less than approximately 100 Angstroms.




In accordance with a more detailed aspect of the present invention, the corrosion inhibitor can include, or the mono-layer can be formed from, an amino phosphonate applied to the elongated elements. The amino phosphonate can include a nitrilotris (methylene) triphosphonic acid, or NTMP. The amino phosphonate and the polarizer device advantageously can be heated together to a temperature greater than approximately 150 degrees Celsius.




A method for resisting corrosion of elements of the polarizer device, or to fabricate the polarizer device, includes the step of chemically bonding a corrosion inhibitor to the elongated elements to form a layer having a thickness less than approximately 100 Angstroms. The layer can be formed on, and chemically bonded to, the elements by applying an amino phosphonate to at least the elongated elements, such as by dipping or soaking the polarizer device in the corrosion inhibitor. The polarizing device can be dipped and soaked in a solution of nitrilotris (methylene) triphosphonic acid (or NTMP). In addition, the polarizer device can be heated at a temperature greater than approximately 150 degrees Celsius.




Additional features and advantages of the invention will be apparent from the detailed description which follows, taken in conjunction with the accompanying drawings, which together illustrate, by way of example, features of the invention.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a cross-sectional end view of a wire-grid polarizer in accordance with an embodiment of the present invention; and





FIG. 2

is a perspective view of a cross-sectional view of the wire-grid polarizer of FIG.


1


.











DETAILED DESCRIPTION




Reference will now be made to the exemplary embodiments illustrated in the drawings, and specific language will be used herein to describe the same. It will nevertheless be understood that no limitation of the scope of the invention is thereby intended. Alterations and further modifications of the inventive features illustrated herein, and additional applications of the principles of the inventions as illustrated herein, which would occur to one skilled in the relevant art and having possession of this disclosure, are to be considered within the scope of the invention.




As illustrated in

FIGS. 1 and 2

, a polarizing device, indicated generally at


10


, such as a wire-grid polarizer, in accordance with the present invention is shown for generally decoupling two orthogonal polarizations of a beam of electromagnetic waves, indicated generally at


12


. In one aspect the beam


12


of electromagnetic waves can include visible light. The polarizing device


10


or wire-grid polarizer can include an optical element


14


and a nano-structure


16


. As discussed in greater detail below, the polarizing device


10


or the wire-grid polarizer advantageously includes a substantial mono-layer


24


formed from a corrosion inhibitor to resist corrosion, without adversely affecting the optical properties of the optical element


14


, or the polarizing device


10


. Such a polarizing device


10


or wire-grid polarizer may be used in various applications, such as image displays (monitors, flat panel displays, LCDs, etc.), image projectors, optical trains, scientific and medical instruments, etc.




The polarizing device


10


or the optical element


14


can include a substrate


28


. The substrate


28


can be transparent to the electromagnetic waves or visible light so that the electromagnetic waves or light can be transmitted by, or pass through, the substrate. Thus, the optical element


14


or substrate


28


can have an optical property of transmitting the electromagnetic waves or visible light. In one aspect, the optical element


14


or substrate


28


can transmit the electromagnetic waves or light without otherwise altering it, such as, without changing the phase, angle, etc. The substrate


28


can include, or be formed by, a glass material. It will be appreciated that other materials, such as plastics, quartz, etc. can be used.




In addition, the polarizing device


10


or the nano-structure


16


can include an array of a plurality of spaced-apart, elongated elements


32


. The elements


32


can be conductive, or formed of a conductive material, and can be disposed on or supported by a surface of the substrate


28


. It will be appreciated that other structures, materials, or layers can be disposed between the elements


32


and the substrate


28


, including for example, ribs, gaps, grooves, layers, films, etc. In addition, a region can be formed between the elements and the substrate with a low refractive index (or a refractive index lower than a refractive index of the substrate), and a controlled thickness. The low index region separating the elements from the substrate can shift the longest wavelength resonance point to a shorter wavelength, and can reduce the fraction of P polarized electromagnetic waves or light that is reflected from the polarizer.




The elements


32


are relatively long and thin. All or most of the elements


32


can have a length that is generally larger than the wavelength of desired electromagnetic waves or visible light. Thus, the elements


32


have a length of at least approximately 0.7 μm (micrometers or microns) for visible light applications. The typical length, however, may be much larger. The elements


32


can have a thickness or a height t less than the wavelength of the desired electromagnetic waves or light, or less than 0.4 μm (micrometers or microns) for visible light applications. In one aspect, the thickness can be less than 0.2 μm for visible light applications. In addition, the elements


32


are located in generally parallel arrangement with a spacing, pitch, or period P of the elements being smaller than the wavelength of the desired electromagnetic waves or light. Thus, the elements


32


have a pitch P of less than 0.4 μm (micrometers or microns) for visible light applications. In one aspect, the pitch P can be approximately one-half the wavelength of light, or approximately 0.2 μm for visible light applications. The elements


32


also can have a width w less than the period P, or less than 0.4 μm or 0.2 μm for visible light applications. In one aspect, the width can be less than 0.1-0.2 μm for visible light applications. It should be noted that arrays with longer periods (greater than approximately twice the wavelength of light or 1.4 μm) can operate as diffraction gratings, while arrays with shorter periods (less than approximately half the wavelength of light or 0.2 μm) operate as polarizers, while arrays with periods in a transition region (between approximately 0.2 and 1.4 μm) also act as diffraction gratings and are characterized by abrupt changes or anomalies referred to as resonances. Thus, it will be appreciated that the actual size of the elements


32


is quite small, and the array of elements


32


can actually appear as a continuous, reflective surface to the unaided eye. As shown in the figures, however, the array of elements


32


actually creates a very small structure, or nano-structure


16


with a size or scale on the order of 10


−8


meters.




In addition, the size and configuration of the array of elements


32


is designed to interact with the electromagnetic waves or visible light to generally transmit electromagnetic waves of one polarization, and generally reflect electromagnetic waves of another polarization. As stated above, a beam


12


can be incident on the polarizer device


10


. The polarizer device


10


can divide the beam


12


into a specularly reflected component


40


, and a non-diffracted, transmitted component


44


. Using the normal definitions for S and P polarization, the wave or light with S polarization has the polarization vector orthogonal to the plane of incidence, and thus parallel to the conductive elements. Conversely, wave or light with P polarization has the polarization vector parallel to the plane of incidence and thus orthogonal to the conductive elements.




In general, the polarizer device


10


can reflect waves or light with its electric field vector parallel to the elements


32


(or the S polarization), and transmit waves or light with its electric field vector perpendicular to the elements (or the P polarization). Ideally, the polarizer device can function as a perfect mirror for one polarization of waves or light, such as the S polarized light, and can be perfectly transparent for the other polarization, such as the P polarized light. In practice, however, even the most reflective metals used as mirrors absorb some fraction of the incident light and reflect only 90% to 95%, and plain glass does not transmit 100% of the incident light due to surface reflections.




As stated above, an important consideration in optics and/or image processing is the controlled and deliberate manipulation of light, without adversely or unintentionally affecting the light or properties thereof. For example, while it can be desirable to polarize (or separate the polarization of) the light with a polarizing device, it is undesirable for the polarizing device to unintentionally alter the light, such as by inadvertently introducing phase shifts, or changing the angle. It is known in the field of optics that the addition of materials to optical elements can create an interface between the optical element and added material that can change the optical properties of the optical element, and thus the light. Therefore, the addition of materials to optical elements is only done with great care.




In the particular case of wire-grid polarizers, it has been found that the addition of thin layers of materials on the wire-grid structure has a deleterious effect on the performance of the device. Such layers will affect both the polarization contrast, or the ability of the polarizer to completely separate the two polarizations, and the efficiency of transmission of the one polarization. These effects can be so significant as to render the polarizer unsuitable for use. These deleterious effects occur because the wire-grid polarizer is a nano-structured device in which the function is dependent on the wavelength of the light. The addition of thin layers of material can change the effective wavelength of the light in relation to the fixed dimensions of the wire-grid, which change would cause a reduction in performance. This effect has been shown by experiment to be measurable even for layers that are only 200-300 Angstroms thick.




It has been discovered that a substantial mono-layer


24


, as described below, can be formed over at least the nano-structure


16


or the elements


32


, as shown in solid lines, to resist corrosion of the elements


32


, and without substantially altering or detrimentally affecting the optical properties of the optical element. (It will be noted that the layer shown in the figures is greatly exaggerated for clarity.) The mono-layer


24


may also be formed over portions of the optical element


14


or the substrate


28


, as shown in dashed lines. As used herein, the term “substantial mono-layer” is used to refer to a layer having a thickness of less than approximately 100 Angstroms. This mono-layer consists of one or more molecular or atomic layers. It is believed that the extreme thinness of the layer


24


contributes to the layer's lack of interference with the optical properties of the optical element


14


or substrate


28


, or lack of interference with the beam


12


of light or the reflected or transmitted beams


40


or


44


.




In addition, the layer


24


advantageously is chemically bonded to, or reacts with, the elements


32


, or to a natural oxide layer


48


on the elements, so that the layer covers exposed surfaces of the elements (the exposed surfaces being those not contacting the substrate). It is believed that the chemical bond of the layer


24


to the elements


32


permits the layer to be extremely thin, and contributes to the layer's ability to resist corrosion. Again, the chemical bond formed only with the elements


32


is believed to be another reason why the layer


24


does not affect the optical properties of the polarizer device


10


.




The layer


24


can be formed from a material including a corrosion inhibitor, as described in greater detail below. Such a corrosion inhibitor can include an amino phosphonate. In particular, the corrosion inhibitor can include a nitrilotris (methylene) triphosphonic acid (or NTMP). Such an NTMP material is presently available from Aldrich Chemical Company as #14,479-7. It has been found that such a corrosion inhibitor chemically reacts with the elements


32


to form a chemical bond between the material and the elements, and to create the layer


24


. In addition, it has been unexpectedly found that the application of these corrosion inhibitors to the polarizer device


10


does not substantially interfere with the optical properties of the polarizer device


10


, optical element


14


, or substrate


28


.




As stated above, the elements can be formed from a conductive material. For example, the elements can include aluminum or silver. Many materials can have a natural or native oxide layer that can provide a limited, but inadequate corrosion resistance. Thus, the surface of the elements can have a native or natural oxide layer that provides a limited, but inadequate corrosion resistance. It has been found that the amino phosphonate, or the nitrilotris (methylene) triphosphonic acid, can be used to form the substantial mono-layer, even on the nano-structure. It is believed that the amino phosphonate, or the NTMP, alters the natural oxide layer by reacting with the material surface, adding the substantial mono-layer over the natural oxide layer. It is also believed that the amino phosphonate, or the NTMP, chemically bonds to the native oxide layer.




A method for fabricating the polarizing device


10


described above, and for resisting corrosion of the elements of the wire-grid polarizer, includes chemically bonding the corrosion inhibitor to the elements to form a substantial mono-layer with a thickness less than approximately 100 Angstroms. The substantial mono-layer and/or the chemical bond can be formed by applying the corrosion inhibitor to the elements, and to the polarizing device


10


, in a liquid solution. For example, the polarizing device


10


can be dipped into a solution of the amino phosphonate, or the NTMP. In particular, it has been found that a solution of 0.0002 liters NTMP per liter of distilled water is desirable. For example, NTMP can be added to distilled water in a quantity of 4 drops per liter. In addition, the polarizing device


10


can be soaked in the solution for a period of time. After dipping and soaking the polarizing device


10


in the solution of corrosion inhibitor (amino phosphonate or NTMP), the polarizing device


10


can be rinsed with distilled water. It has been found that dipping and soaking the elements of the polarizing device can form a layer on the elements that is chemically bonded to the elements. It has also been found that the layer is formed completely on all the exposed surfaces (those surfaces not contacting the substrate) to completely surround and bond to the elements.




In addition, the layer on the elements, and the polarizing device, advantageously can be heated or baked. It has unexpectedly and advantageously been found that heating the polarizing device improves the corrosion resistance of the layer. In particular, it has been found that heating the polarizing device to greater than 150 degrees Celsius improves the corrosion resistance of the layer.




As an example, a polarizer device was dipped into a solution of NTMP with a concentration of 10 ml per 25 liter tank (or a concentration of 0.0002 NTMP per liter of distilled water). The temperature of the solution was 80 degrees Celsius. The polarizer device was soaked for 20 minutes, and rinsed for 1 minute. The polarizer device was heated or baked at 200 degrees Celsius for 20 minutes. The polarizer device was then subjected to boiling distilled water (to simulate environmental conditions, and to accelerate corrosion) until failure occurred. The polarizer device thus treated exhibited the greatest corrosion resistance.




Various other polarizer devices were fabricated under various different processing methods. It was found that the heat or bake temperature appears to be the most critical factor, with 200 degrees Celsius being better than 150 degrees Celsius, and with 150 degrees Celsius being better than 100 degrees Celsius. The next most important factor appeared to be dip or soak temperature, with 80 degrees Celsius being better than 70 degrees Celsius, but with 90 degrees Celsius being worse than 80 degrees Celsius. The next most important factor appeared to be dip or soak time, with 20 minutes being better than 15 minutes or 40 minutes.




As discussed above, it is desirable to fabricate a wire-grid polarizer, or to treat a wire-grid polarizer, to resist corrosion or reactivity of the elements, which is optically negligible, and which is inexpensive.




Also as discussed above, a wire-grid polarizer presents unique challenges for corrosion protection due to its configuration as both an optical element and a nano-structure. While traditional corrosion inhibitors may have been applied to traditional materials, there is no expectation that corrosion inhibitors can be successfully utilized with optical elements. In fact, the presumption in optics is often that the addition of such foreign materials to optical elements will adversely affect the optical element, and thus the light. Therefore, such foreign materials are often strictly avoided. For example, the addition of as little as 100 nm of a material which has absorptive properties can seriously affect the transmission properties of an optical component. Since it is well known that materials can age or change properties with exposure to light over extended periods of time, even very thin layers of new or unknown materials are avoided. Thus, the field of optics traditionally limits the substances applied to optics to those traditionally used. For example, it is known to seal the surface of an aluminum mirror with a coating of silicon dioxide. Such a coating is relatively thick, but provides known results. Such a coating, however, detrimentally affects the operation and performance of a wire-grid polarizer.




In addition, there is no expectation that corrosion inhibitors can be successfully utilized with nano-structures. It is desirable to absolutely protect the elements, rather than to just slow corrosion. It will be appreciated that while corrosion to a depth of of 200 nm can be negligible or insignificant in traditional corrosion situations, such corrosion can completely destroy the nano-structure of the wire-grid polarizer, causing catastrophic failure. In fact, corrosion of just 10 nm depth in the wire grid polarizer will have measurable effects on the contrast ratio.




Traditional methods of corrosion protection apply a fairly thick (200 nm-1000 nm) film or protective coating in order to provide the required degree of reliable protection against corrosion. Experiments with thin films (on the order of 100 nm) of polymers and other materials with the goal of protecting the wire-grid have been unsuccessful. In fact, it has been found by experiment that the addition of optical overcoatings of traditional materials such as Magnesium Fluoride to thicknesses of 100 nm do not provide sufficient protection against corrosion of the wire-grid. Coatings of this thickness also cause measurable changes in the optical performance of the polarizer. All these experimental facts lead to the conclusion that protection of the wire-grid polarizer through the use of conventional techniques is not possible.




In addition, the nano-structure of the wire-grid polarizer presents a structure that is different from traditional surfaces by providing numerous, individual elements spaced-apart from one another, as opposed to a continuous surface. Thus, the nano-structure presents both structured surfaces, as opposed to continuous surfaces, and extremely small structures, and it is not tolerant of even a small amount of corrosion.




The fabrication or treatment of the wire-grid polarizer with a corrosion inhibitor, such as NTMP, to form a substantial mono-layer with a thickness less than approximately 100 Angstroms, and that is chemically bonded to, or reacts with, the surface of the elements, produced surprising and unexpected results. The treated wire-grid polarizers exhibited both exceptional optical performance, and exceptional corrosion resistance.




In addition to the above-described amino phosphonate or NTMP corrosion inhibitors, other phosphate based hydration inhibitors may be used, including for example, methyl phosphonic acid (MPA). Silanes can be used, such as 2-(3,4-epoxycyclohexyl)-ethyltrimethoxysilane, or phenyltriethosysilane. Siloxanes can be used, such as Oxyalkylsiloxane. Azole based materials can be used, such as benzotriazole, benzotriazole amine, tolyltriazole, sodium tolyltriazole, or carboxybenzotriazole. Heavy metal materials can be used, such as cromium, molybdneum, or tungsten. For example, the surface can be dipped into a solution of metal-containing compounds, such as Na2MoO4, thus creating a protective monolayer. Organic materials can be used, such as Rodine™ or Alodine™, available from the Henkel Corporation, Madison Heights, Mich. 48071. In addition, n-alkanoate materials can be used.




It is to be understood that the above-referenced arrangements are only illustrative of the application for the principles of the present invention. Numerous modifications and alternative arrangements can be devised without departing from the spirit and scope of the present invention while the present invention has been shown in the drawings and fully described above with particularity and detail in connection with what is presently deemed to be the most practical and preferred embodiments(s) of the invention, it will be apparent to those of ordinary skill in the art that numerous modifications can be made without departing from the principles and concepts of the invention as set forth in the claims.



Claims
  • 1. A corrosion resistant wire grid polarizer device, comprising:a) a transparent substrate having an optical property of transmitting electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red; b) an array of spaced-apart, elongated elements, disposed on the substrate, sized to interact with electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red to generally transmit electromagnetic waves of one polarization, and generally reflect electromagnetic waves of another polarization; and c) a substantial mono-layer, chemically bonded to the elongated elements without substantially adversely affecting the optical property of the transparent substrate to transmit the electromagnetic waves, and without substantially adversely altering the electromagnetic waves transmitted through the array of spaced-apart, elongated elements and the transparent substrate, the mono-layer being formed from a corrosion inhibitor and having a thickness less than approximately 100 Angstroms. d) the substantial mono-layer including an amino phosphonate applied to the elongated elements.
  • 2. A device in accordance with claim 1, wherein the elements have a thickness less than approximately 400 nm, a width less than approximately 300 nm, a length greater than approximately 700 nm, and a pitch of less than approximately 400 nm.
  • 3. A device in accordance with claim 1, wherein the amino phosphonate includes a nitrilotris (methylene) triphosphonic acid.
  • 4. A device in accordance with claim 1, wherein the amino phosphonate and the wire grid polarizer device have been heated together to a temperature greater than approximately 150 degrees Celsius.
  • 5. A corrosion resistant wire grid polarizer device for generally decoupling two orthogonal polarizations of electromagnetic waves, the device comprising:a) an optical element formed from a transparent material to transmit electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red; b) a nano-structure, associated with the optical element, including an array of spaced-apart, elongated elements with a thickness on the order of 10−8 m, to interact with the electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red to generally transmit electromagnetic waves of one polarization, and generally reflect electromagnetic waves of another polarization; and c) a corrosion resistant layer, chemically bonded to the nano-structure, having a thickness less than approximately 100 Angstroms, the layer resisting corrosion of the nano-structure without substantially adversely effecting an optical property of the optical element to transmit the electromagnetic waves, and without substantially adversely altering the electromagnetic waves transmitted through the nano-structure and the optical element; and d) the corrosion resistant layer including an amino phosphonate applied to the elongated elements.
  • 6. A device in accordance with claim 5, wherein the elements have a thickness less than approximately 400 nm, a width less than approximately 300 nm, a length greater than approximately 700 nm, and a pitch of less than approximately 400 nm.
  • 7. A device in accordance with claim 5, wherein the amino phosphonate includes a nitrilotris (methylene) triphosphonic acid.
  • 8. A device in accordance with claim 5, wherein the amino phosphonate and the wire grid polarizer device have been heated together to a temperature greater than approximately 150 degrees Celsius.
  • 9. A method for resisting corrosion of elements of a wire grid polarizer, comprising the steps of:a) providing a wire grid polarizer having an array of spaced-apart, elongated elements, disposed on a substrate, sized to interact with electromagnetic waves having a wavelength with the range of ultraviolet, visible and infra-red to generally transmit electromagnetic waves of one polarization, and generally reflect electromagnetic waves of another polarization; b) chemically bonding a corrosion inhibitor to the elongated elements including applying an amino phosphate to at least the elongated elements to form a layer having a thickness less than approximately 100 Angstroms.
  • 10. A method in accordance with claim 9, wherein the step of chemically bonding a corrosion inhibitor to the elongated elements further includes chemically bonding the corrosion inhibitor to all exposed surfaces of the elongated elements.
  • 11. A method in accordance with claim 9, wherein the step of applying the amino phosphonate further includes applying nitrilotris (methylene) triphosphonic acid to at least the elements.
  • 12. A method in accordance with claim 9, further comprising the step of:heating the wire grid polarizer at a temperature greater than approximately 150 degrees Celsius.
  • 13. A method in accordance with claim 9, wherein the step of applying the amino phosphonate further includes applying a liquid with a solution of 0.0002 liters nitrilotris (methylene) triphosphonic acid per liter of distilled water.
  • 14. A method in accordance with claim 9, wherein the step of applying the amino phosphonate corrosion inhibitor includes dipping the wire grid polarizer in the amino phosphonate corrosion inhibitor at a temperature greater than approximately 70 degree Celsius.
  • 15. A method in accordance with claim 14, further comprising the step of:rinsing the wire grid polarizer after the amino phosphonate corrosion inhibitor is applied and before drying.
  • 16. A method in accordance with claim 9, wherein the step of chemically bonding a corrosion inhibitor to the elongated elements further including the step of:altering a natural oxide layer formed on the elongated elements.
  • 17. A corrosion resistant wire grid polarizer device, comprising:a) a transparent substrate having an optical property of transmitting electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red; b) an array of spaced-apart, elongated elements, disposed on the substrate, sized to interact with electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red to generally transmit electromagnetic waves of one polarization, and generally reflect electromagnetic waves of another polarization; and c) a substantial mono-layer including an amino phosphonate, disposed over the elongated elements without substantially adversely affecting the optical property of the transparent substrate to transmit the electromagnetic waves, and without substantially adversely altering the electromagnetic waves transmitted through the array of spaced-apart, elongated elements and the transparent substrate.
  • 18. A device in accordance with claim 17, wherein the mono-layer has a thickness less than approximately 100 Angstroms.
  • 19. A device in accordance with claim 17, wherein the amino phosphonate includes a nitrilotris (methylene) triphosphonic acid.
  • 20. A device in accordance with claim 17, wherein the amino phosphonate and the wire grid polarizer device have been heated together to a temperature greater than approximately 150 degrees Celsius.
  • 21. A corrosion resistant wire grid polarizer device, comprising:a) a transparent substrate having an optical property of transmitting electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red; b) an array of spaced-apart, elongated elements, disposed on the substrate, sized to interact with electromagnetic waves having a wavelength within the range of ultraviolet, visible and infra-red to generally transmit electromagnetic waves of one polarization, and generally reflect electromagnetic waves of another polarization; c) a natural oxide layer, disposed on the elongated elements; and d) a substantial mono-layer formed from an amino phosphonate, disposed over the natural oxide layer and the elongated elements without substantially adversely affecting the optical property of the transparent substrate to transmit the electromagnetic waves, and without substantially adversely altering the electromagnetic waves transmitted through the array of spaced-apart, elongated elements and the transparent substrate.
  • 22. A device in accordance with claim 21, wherein the mono-layer has a thickness less than approximately 100 Angstroms.
  • 23. A device in accordance with claim 21, wherein the amino phosphonate includes a nitrilotris (methylene) triphosphonic acid.
  • 24. A device in accordance with claim 21, wherein the amino phosphonate and the wire grid polarizer device have been heated together to a temperature greater than approximately 150 degrees Celsius.
US Referenced Citations (120)
Number Name Date Kind
2224214 Brown Dec 1940 A
2287598 Brown Jun 1942 A
2403731 MacNeille Jul 1946 A
2748659 Geffcken et al. Jun 1956 A
2887566 Marks May 1959 A
3046839 Bird et al. Jun 1962 A
3436143 Garren Apr 1969 A
3479168 Bird et al. Nov 1969 A
3536373 Bird et al. Oct 1970 A
3566099 Makas Feb 1971 A
3627431 Komamiski Dec 1971 A
3631288 Rogers Dec 1971 A
3731986 Fergason May 1973 A
3857627 Harsch Dec 1974 A
3857628 Strong Dec 1974 A
3876285 Schwarzmüller Apr 1975 A
3912369 Kashnow Oct 1975 A
3969545 Slocum Jul 1976 A
4009933 Firester Mar 1977 A
4025164 Doriguzzi et al. May 1977 A
4025688 Nagy et al. May 1977 A
4049944 Garvin et al. Sep 1977 A
4073571 Grinberg et al. Feb 1978 A
4104598 Abrams Aug 1978 A
4181756 Fergason Jan 1980 A
4220705 Sugibuchi et al. Sep 1980 A
4221464 Pedinoff et al. Sep 1980 A
4268127 Oshima et al. May 1981 A
4289381 Garvin et al. Sep 1981 A
4294119 Soldner Oct 1981 A
4308079 Venables et al. Dec 1981 A
4456515 Krueger et al. Jun 1984 A
4466704 Schuler et al. Aug 1984 A
4492432 Kaufmann et al. Jan 1985 A
4512638 Sriram et al. Apr 1985 A
4514479 Ferrante Apr 1985 A
4515441 Wentz May 1985 A
4560599 Regen Dec 1985 A
4679910 Efron et al. Jul 1987 A
4688897 Grinberg et al. Aug 1987 A
4711530 Nakanowatari et al. Dec 1987 A
4743092 Pistor May 1988 A
4743093 Oinen May 1988 A
4759611 Downey, Jr. Jul 1988 A
4759612 Nakatsuka et al. Jul 1988 A
4799776 Yamazaki et al. Jan 1989 A
4818076 Heppke et al. Apr 1989 A
4840757 Blenkhorn Jun 1989 A
4865670 Marks Sep 1989 A
4895769 Land et al. Jan 1990 A
4913529 Goldenberg et al. Apr 1990 A
4946231 Pistor Aug 1990 A
4966438 Mouchart et al. Oct 1990 A
4991937 Urino Feb 1991 A
5029988 Urino Jul 1991 A
5061050 Ogura Oct 1991 A
5087985 Kitaura et al. Feb 1992 A
5113285 Franklin et al. May 1992 A
5122887 Mathewson Jun 1992 A
5122907 Slocum Jun 1992 A
5139340 Okumura Aug 1992 A
5157526 Kondo et al. Oct 1992 A
5177635 Keilmann Jan 1993 A
5204765 Mitsui et al. Apr 1993 A
5216539 Boher et al. Jun 1993 A
5225920 Kasazumi et al. Jul 1993 A
5235443 Barnik et al. Aug 1993 A
5235449 Imazeki et al. Aug 1993 A
5239322 Takanashi et al. Aug 1993 A
5245471 Iwatsuka et al. Sep 1993 A
5279689 Shvartsman Jan 1994 A
5295009 Barnik et al. Mar 1994 A
5305143 Taga et al. Apr 1994 A
5325218 Willett et al. Jun 1994 A
5333072 Willett Jul 1994 A
5349192 Mackay Sep 1994 A
5357370 Miyatake et al. Oct 1994 A
5383053 Hegg et al. Jan 1995 A
5422756 Weber Jun 1995 A
5436761 Kamon Jul 1995 A
5466319 Zager et al. Nov 1995 A
5485499 Pew et al. Jan 1996 A
5486935 Kalmanash Jan 1996 A
5486949 Schrenk et al. Jan 1996 A
5490003 Van Sprang Feb 1996 A
5506704 Broer et al. Apr 1996 A
5508830 Imoto et al. Apr 1996 A
5513023 Fritz et al. Apr 1996 A
5513035 Miyatake et al. Apr 1996 A
5517356 Araujo et al. May 1996 A
5557343 Yamagishi Sep 1996 A
5559634 Weber Sep 1996 A
5570215 Omae et al. Oct 1996 A
5574580 Ansley Nov 1996 A
5579138 Sannohe et al. Nov 1996 A
5594561 Blanchard Jan 1997 A
5609939 Petersen et al. Mar 1997 A
5612820 Schrenk et al. Mar 1997 A
5619356 Kozo et al. Apr 1997 A
5626408 Heynderickx et al. May 1997 A
5658060 Dove Aug 1997 A
5686979 Weber et al. Nov 1997 A
5731246 Bakeman et al. Mar 1998 A
5748368 Tamada et al. May 1998 A
5748369 Yokota May 1998 A
5798819 Hattori et al. Aug 1998 A
5826960 Gotoh et al. Oct 1998 A
5833360 Knox et al. Nov 1998 A
5838403 Jannson et al. Nov 1998 A
5841494 Hall Nov 1998 A
5986730 Hansen et al. Nov 1999 A
5991075 Katsuragawa et al. Nov 1999 A
6081376 Hansen et al. Jun 2000 A
6082861 Dove et al. Jul 2000 A
6108131 Hansen et al. Aug 2000 A
6122103 Perkins et al. Sep 2000 A
6234634 Hansen et al. May 2001 B1
20020191286 Gale et al. Dec 2002 A1
20030117708 Kane Jun 2003 A1
20030180024 Edlinger et al. Sep 2003 A1
Foreign Referenced Citations (24)
Number Date Country
416157 Jul 1925 DE
296391 Feb 1950 DE
3707984 Mar 1987 DE
0317910 Nov 1987 EP
0336334 Apr 1988 EP
0349144 Jun 1988 EP
0349309 Jun 1988 EP
0357946 Aug 1988 EP
407830 Jul 1989 EP
0407830 Jul 1989 EP
416157 Sep 1989 EP
0488544 Nov 1990 EP
0507445 Mar 1991 EP
0518111 May 1991 EP
0588937 Jun 1991 EP
0521591 Jul 1991 EP
0543061 Nov 1991 EP
0606940 Jan 1993 EP
0634674 Jun 1993 EP
0670506 Sep 1993 EP
0744634 May 1995 EP
0084502 Aug 1989 JP
10073722 Mar 1998 JP
1781659 Oct 1990 SU
Non-Patent Literature Citations (31)
Entry
U.S. patent application Ser. No. 60/356,284.*
Lloyd Wiliiam Taylor Manual of Advanced Undergraduate Experiments in Physics, p. 302 (1959).
Flanders, “Application of ≈100 Å linewidth structures fabricated by shadowing techniques”, J. Vac. Sci. Technol., 19(4), Nov./Dec. 1981.
Kuta and van Driel, “Coupled-wave analysis of lamcllar metal transmission gratings for the visible and the infrared,” J. Opt. Soc. Am. A/vol. 12, No. 5/May 1995.
Lockbihler and Depine, “Diffraction from highly conducting wire gratings of arbitrary cross-section,” Jornal of Modern Optics, 1993, vol. 40, No. 7, pp. 1273-1298.
Novak et al., “Far infrared polarizing grids for use at cryogenic temperatures,” Applied Optics, Aug. 15, 1989/ vol. 28, No. 15, pp. 3425-3427.
Auton and Hutley, “Grid Polarizers for Use in the Near Infrared,” Infrared Physics, 1972, vol. 12, pp. 95-100.
Stenkamp et al, “Grid polarizer for the visible spectral region,” SPIE vol. 2213 pp. 288-296.
Handbook of Optics, 1978, pp. 10-68—10-77.
Hand of Optics vol. II, 2nd Edition, pp. 3.32-3.35.
Glytsis and Gayloard, “High-spatial-frequency binary and multilevel stairstep gratings: polarization-selective mirrors and broadband antireflection surfaces,” Applied Optics Aug. 1, 1992 vol. 31, No. 22 pp. 4459-4470.
Auton, “Infrared Transmission Polarizers by Photolithography, ” Applied Optics Jun. 1967 vol. 6, No. 6, pp. 1023-1027.
Haggans et al., “Lamellar gratings as polarization components for specularly reflected beams,” Journal of Modern Optics, 1993, vol. 40, No. 4, pp. 675-686.
Nordin et al., “Micropolarizer array for infrared imaging polarimetry”, J. Op. Soc. Am. A. vol. 16 No. 5/May 1999.
Lavin, “Specular Reflection”, Monographs on App. Opt. No. 2.
Maystre & Dainty, Modern Analysis of Scattering Phenomena Proceeding from International Workshop held at Domaine deTournon, Aix en Provence, France Sep. 5-8, 1990.
Bird and Parrish, Jr., “The Wire Grid as a Near-Infrared Polarizer,” J. Op. Soc. Am. vol. 50 No. 9 (1960).
Optics 9th Edition, pp. 338-339 (1980).
Whitebourn and Douglas, “Phase shifts in transmission line models of thin periodic metal grids,” Applied Optics Aug. 15, 1989 vol. 28, No. 15, pp. 3511-3515.
Enger and Case, “Optical elements with ultrahigh spatial-frequency surface corrugations,” Applied Optics Oct. 15, 1983, vol. 22, No. 20 pp. 3220-3228.
Knop, “Reflection Grating Polarizer for the Infrared,” Optics Communication vol. 26, No. 3, Sep. 1978.
Hass and O'Hara, “Sheet Infrared Transmission Polarizers,” Applied Optics Aug. 1965, vol. 4, No. 8, pp. 1027-1031.
Flanders, “Submicron periodicity gratins as artificial anisotropic dielectrics,” Appl. Phys. Lett. 42 (6), Mar. 15, 1983, pp. 492-494.
Li Li and J.A. Dobrowski, “Visible broadband, wide-angle, thin-film multilayer polarizing beam splitter,” Applied Optics May 1, 1996, vol. 35, No. 13, pp. 2221-2224.
Sonek et al., “Ultraviolet grating polarizers,” J. Vac. Sci. Technol., 19(4), Nov./Dec. 1981, pp. 921-923.
N.M. Ceglio, Invited Review “Revolution in X-Ray Optics”, J. X-Ray Science & Tech. 1, 7-78 (1989).
Dainty, et al., “Measurements of light scattering by characterized random rough surface”, Waves in Random Media 3 (1991)/
DeSanto & Wombell, “Rough surgace scattering”, Waves in Random Media 1 (1991).
Moshier, Davis & Ahearn, “The Corrosion and Passivity of Aluminum Exposed to Dilute Sodium Sulfate Solutions”, Corrosion Science vol. 27, No. 8, pp 785-801, 1987.
Zanzucchi & Thomas III, “Corrosion Inhibitors for Aluminum Films”, Journal of the Electrochemical Society, vol. 135, No. 6, Jun. 1988.
Scandurra, Curro, Frisina, & Pignataro; “Corrosion Inhibition of Al Metal in Microelectronic Devices Assembled in Plastic Packages”, Journal of The Electrochemical Society, 148 (8) B289-B292 (2001).