Patent Application
20110146777
The disclosure generally pertains to solar cells. More particularly, the disclosure pertains to dye-sensitized and/or nanocrystal-sensitized solar cells.
A wide variety of solar cells have been developed for converting sunlight into electricity. Of the known solar cells, each has certain advantages and disadvantages. There is an ongoing need to provide alternative solar cells as well as alternative methods for manufacturing solar cells.
The disclosure pertains generally to solar cells and, more particularly, to dye-sensitized and/or nanocrystal-sensitized solar cells. Also disclosed are counter electrodes for solar cells including dye-sensitized and/or nanocrystal-sensitized solar cells.
An example counter electrode for a solar cell may include a substrate, a microstructured template disposed on the substrate, and a layer of catalytic material on the microstructured template.
An example solar cell may include a photoelectrode and a counter electrode. The counter electrode may include a microstructured template. A layer of catalytic material may be disposed on the microstructured template. An active layer may be disposed between the photoelectrode and the counter electrode. An example method for manufacturing a solar cell may include providing a substrate, forming a microstructured template on the substrate, disposing a layer of catalytic material on the microstructured template, providing a photoelectrode, and providing an active layer between the catalytic material and the photoelectrode. In some instances, the substrate, microstructured template, catalytic material, active layer and photoelectrode may be coupled together.
The above summary is not intended to describe each and every disclosed embodiment or every implementation of the disclosure. The Description that follows more particularly exemplify the various illustrative embodiments.
The following description should be read with reference to the drawings. The drawings, which are not necessarily to scale, depict selected embodiments and are not intended to limit the scope of the disclosure. The disclosure may be more completely understood in consideration of the following description of various embodiments in connection with the accompanying drawings, in which:
While the disclosure is amenable to various modifications and alternative forms, specifics thereof have been shown by way of example in the drawings and will be described in detail. It should be understood, however, that the intention is not to limit the disclosure to the particular illustrative embodiments described. On the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention.
For the following defined terms, these definitions shall be applied, unless a different definition is given in the claims or elsewhere in this specification.
All numeric values are herein assumed to be modified by the term “about,” whether or not explicitly indicated. The term “about” generally refers to a range of numbers that one of skill in the art would consider equivalent to the recited value (i.e., having the same function or result). In many instances, the terms “about” may include numbers that are rounded to the nearest significant figure.
The recitation of numerical ranges by endpoints includes all numbers within that range (e.g. 1 to 5 includes 1, 1.5, 2, 2.75, 3, 3.80, 4, and 5).
As used in this specification and the appended claims, the singular forms “a”, “an”, and “the” include plural referents unless the content clearly dictates otherwise. As used in this specification and the appended claims, the term “or” is generally employed in its sense including “and/or” unless the content clearly dictates otherwise.
The following description should be read with reference to the drawings. The drawings, which are not necessarily to scale, depict an illustrative embodiments and are not intended to limit the scope of the invention.
A wide variety of solar cells (which also may be known as photovoltaics and/or photovoltaic cells) have been developed for converting sunlight into electricity. Some example solar cells include a layer of crystalline silicon. Second and third generation solar cells often utilize a film of photovoltaic material (e.g., a “thin” film) deposited or otherwise provided on a substrate. These solar cells may be categorized according to the photovoltaic material deposited. For example, inorganic thin-film photovoltaics may include a thin film of amorphous silicon, microcrystalline silicon, CdS, CdTe, Cu2S, copper indium diselenide (CIS), copper indium gallium diselenide (CIGS), etc. Organic thin-film photovoltaics may include a thin film of a polymer or polymers, bulk heterojunctions, ordered heterojunctions, a fullerence, a polymer/fullerence blend, photosynthetic materials, etc. These are only examples.
Another type of solar cell utilizes a photosensitive dye or nanocrystals to generate electricity. The dye in these dye-sensitized solar cells (and/or the nanocrystals in the nanocrystal-sensitized solar cells) absorbs photons and, as a result, inject or otherwise direct electrons to an electron conductor material. An electrolyte solution in the cell typically reduces the dye back to its original electrical state. These dye-sensitized solar cells may be desirable due to their relatively simple construction and lower material costs.
Photoelectrode 12 and/or counter electrode 16 may be made from a number of different materials including polymers, glass, and/or transparent materials. For example, photoelectrode 12 and/or counter electrode 16 may include polyethylene terephthalate, polyimide, low-iron glass, fluorine-doped tin oxide, indium tin oxide, Al-doped zinc oxide, any other suitable conductive inorganic element(s) or compound(s), conductive polymer(s), and other electrically conductive materials, combinations thereof, or any other suitable material or material combination. In some embodiments, counter electrode 16 may include a substrate and/or the counter electrode may be referred to as being a substrate, for example, to which materials including catalytic and/or electrically conductive materials may be coupled to so as to define the counter electrode 16.
In some embodiments, a layer of material 18, for example a layer of electron conductor material, may be disposed on photoelectrode 12, although this is not required in all embodiments. Layer 18 may be formed of any suitable material or material combination. In some cases, layer 18 may be an n-type electron conductor. The layer 18 may be metallic, such as TiO2 or ZnO. In some cases, layer 18 may be an electrically conducting polymer, such as a polymer that has been doped to be electrically conducting or to improve its electrical conductivity.
Active layer 14 may include an electrolyte. In these embodiments, active layer 14 may also include a photosensitive dye 20 that may be disposed, for example, adjacent layer 18 when layer 18 is provided or adjacent layer 12 when layer 18 is not provided. Photosensitive dye 20 may be any suitable material. For example, photosensitive dye 20 may include triscarboxy-ruthenium terpyridine [Ru(4,4′,4″-(COOH)3-terpy)(NCS)3], a ruthenium-polypyridine dye, other ruthenium complex materials, 1-ethyl-3 methylimidazolium tetrocyanoborate [EMIB(CN)4], copper-diselenium [Cu(In,GA)Se2], and the like, or any other suitable materials. In general, photosensitive dye 20 may be configured to release or otherwise inject electrons onto, for example, layer 18 upon absorption of a photon. In other embodiments, one or more alternative or additional semiconductor materials may be utilized in cell 10 in order to generate electrons and/or holes.
Photosensitive dye 20 may bond or otherwise tend to accumulate on or above layer 18. It can be appreciated that the amount of photosensitive dye 20 present in cell, or more particularly the density of the photosensitive dye 20 adjacent the surface of layer 18 in the illustrative embodiment, may impact the overall efficiency of cell 10. In order to increase the amount of photosensitive dye 20 present on layer 18 and available for electron transfer to layer 18, it may be desirable for the overall effective surface area of the photosensitive dye 20 to be increase. To this end, in some cases, layer 18 may be formed or otherwise include a structured pattern or array of, for example, nanoparticles, nanopillars, nanowires, or the like that results in an increased surface area. Alternatively, layer 18 may be a generally porous layer with an overall increase in surface area relative to a planar layer. Such configurations may increase the surface area of layer 18 such that the effectiveness of the photosensitive dye 20 may be increased along and/or adjacent layer 18, if desired.
In some illustrative embodiments, where active layer 14 includes an electrolyte, active layer 14 may include redox couple that includes, for example, iodide (I−) and triiodide (I3−). Other redox couples are contemplated. In general, and in the illustrative embodiment, active layer 14 may be configured to provide electrons to photosensitive dye 20 after photosensitive dye 20 has injected or otherwise passed an electron to layer 18. For example, iodide may oxidized to triiodide so as to contribute an electron to photosensitive dye 20. In turn, the triiodide may recover an electron from counter electrode 16, thus reducing triiodide to iodide. In some cases, the reduction of triiodide may be improved by providing a catalyst or a catalytic material on counter electrode 16. For example, counter electrode 16 may include platinum, gold, combinations thereof, and the like, and/or any other suitable material or materials that may catalyze a desirable reaction such as the reduction of triiodide.
In order to further improve the reduction of triiodide, counter electrode 16 may include a microstructured template 24 as shown in
As indicated above, microstructured template 24 may have a structural configuration that allows the surface area thereof to be increased and available as a substrate for a catalytic material. For example, microstructured template 24 may have a three dimensional structure such as illustrated in
A layer of material 28, for example catalytic material, may be disposed on microstructured template 24 as illustrated in
The microstructured template 24 may be formed in a number of different ways. For example, forming microstructured template 24 may include disposing one or more layers of material 30 on a substrate (which may also be referred to as disposing the material 30 on counter electrode 16) as illustrated in
Another layer of material 32, for example a layer of conductive material, may be disposed on the polystyrene microspheres 30 as illustrated in
The step of disposing conductive material 32 on the polystyrene microspheres 30 may vary, for example, depending on the composition of material 32. For example, an Al-doped zinc oxide polycrystalline film (e.g., in an illustrative embodiment that utilizes Al-doped zinc oxide for material 32) may be prepared for a sol-gel dip coating process in a 0.5M zinc acetate in isopropanol solution stabilized by diethanolamine and doped with aluminum nitrate ethanol solutions. The aluminum content in the sol may be about 1% or so. The resultant crystalline ZnO thin films may be annealed at about 500° C. (which may be suitable to remove the sacrificial polystyrene microspheres 30) for about 1 hour. The heat may be sufficient to remove the polystyrene microspheres 30. Alternatively, or in addition, a solvent such a THF may be used to remove the polystyrene microspheres 30 if desired.
When layer 32 includes CuS, for example, a mesoporous film may be formed via a chemical bath deposition method. For example, a 0.5M solution of copper(II) chloride, 3.7M triethanolamine, 7.6M ammonia in 1M sodium hydroxide, 1M thiourea, and deionized water. The substrate (e.g., counter electrode 16) may be immersed (e.g., vertically) into this solution and heated at about 30° C. for about 4 hours. The substrate may be washed with deionized water and moved to the vacuum oven at about 40° C. for about 40 minutes, and then annealed at about 160° C. for about 10 minutes.
Disposing layer 28 of catalytic material on microstructured template 24 may be done using any suitable technique. For example, disposing layer 28 on microstructured template 24 may include disposing a layer of H6PtCl6, HAuCl4, or both (e.g., as a solution or solutions in isopropanol) on microstructured template 24. Such a step may occur over a period of time, for example about 10 seconds. Template 24 may then be heated (e.g., at about 380-450° C. or so), which may dispose activated platinum and/or gold on template 24 and, thus, counter electrode 16. In other embodiments, a thermal decomposition method may be used to add the layer of catalytic material.
As shown in
Other embodiments may include coating a precursor or moldable material on counter electrode 16 and performing a nano-imprinting process to form a microstructured template 24. The moldable material may be disposed on counter electrode 16 in a manner analogous to how the polystyrene microspheres 30 are disposed on counter electrode 16. A pre-formed nanostructured template (e.g., a stainless steel stamp with arrays of nano-pillars formed thereon) may be pressed against the moldable material. This may form microstructured template 24. Subsequently, material 32 may be disposed on the nanostructured material so as fill in or otherwise coat the structure of the nanopillars. If desired, the moldable material may be removed using heat, a solvent, or any other suitable methodology, if desired. A catalytic material 28 may be disposed on material 32.
The method for producing cell 10, thus, may include providing counter electrode 16 (which may be prepared as disclosed above and may have a microstructured template 24 coupled thereto), and disposing layer 28 of catalytic material on microstructured template 24. The method may also include providing a photoelectrode 12 (which may have layer 18 coupled thereto). Cell 10 may be assembled by attaching or joining electrodes 12/16 with active layer 14.
The disclosure should not be considered limited to the particular examples described above, but rather should be understood to cover all aspects of the invention as set out in the attached claims. Various modifications, equivalent processes, as well as numerous structures to which the invention can be applicable will be readily apparent to those of skill in the art upon review of the instant specification.
This application is related to U.S. patent application Ser. No. 12/502,782, filed Jul. 14, 2009 and entitled “QUANTUM DOT SOLAR CELL” and to U.S. patent application Ser. No. 12/468,755, filed May 19, 2009 and entitled “SOLAR CELL WITH ENHANCED EFFICIENCY”, the entire disclosures of which are incorporated herein by reference.