1. Field of the Invention
The present invention relates to covering materials, such as for example the laminar covering materials that can be used in the building and furnishing sectors, in particular for the construction of floorings.
2. Description of the Related Art
The wide variety of covering materials of this type currently available fall into three basic categories.
One category that perhaps dates furthest back in time corresponds to the covering material commonly referred to as linoleum. The corresponding production technique basically envisages adding to linseed oil filling materials, such as wood flour and cork flour, mineral fillers, pigments and other additives so as to obtain a so-called linoleum paste. This paste then undergoes rolling in order to form sheets, which in turn undergo a so-called “curing” step, which lasts some dozens of days and is basically aimed at achieving a consolidation of the sheet of linoleum sufficient to enable its further handling and treatment (for example, so as to enable winding thereof into rolls for subsequent laying).
Notwithstanding its long existence over time, this category occupies only quite a modest share of the market both on account of the disadvantages linked to the intrinsic lengthiness of the process of curing and because, in the steps subsequent to laying of the flooring, linoleum tends to release into the environment an intense and characteristic odor linked to the presence of linseed oil.
A very substantial slice of the market of coatings and floorings is represented by synthetic plastic materials. One of the most widely used materials for making these coatings, which is able to present a contained cost, is represented by polyvinyl chloride (PVC). Irrespective of any other consideration, these floorings, and in particular PVC-based ones, tend to be viewed with less favor on account of the substances (for example, compounds of chlorine and plasticizing agents) that can be released by the coating, also on account of their disagreeable smell.
In the course of the last few years, rubber-based floorings have met with particular favor. These floorings are able to combine excellent characteristics of use (for example, as regards resistance to mechanical stresses, to aggressive chemical agents, and to burns) and as regards the possibility of obtaining coatings and floorings that are particularly pleasant from the aesthetic standpoint (for example, with general marbled effects or effects of dispersion of granules of different colors). Examples of this prior art are provided by EP-A-0 968 804 and EP-A-1 020 282.
Over the years there has been no lack of attempts to merge the characteristic elements of the various techniques of production considered previously. For example, in EP-A-0 385 053 there are described coatings of linoleum with the addition of rubber, the main purpose being to enable exploitation of the process of vulcanizing of the rubber in order to make available a coating of linoleum that can be handled and transferred to the site of laying in far shorter times than those characteristically required for curing linoleum floorings of a traditional type.
Even though the solutions described in the known art, have proven to be satisfactory and advantageous to use, there still exists the possibility of achieving further improvements above all as regards the possibility of further improving the mechanical characteristics of the covering material, the resistance to external stresses (particularly as regards the stresses due to treading), and the possibility of widening even more the choice of the chromatic ranges for making the coating.
In one embodiment, the present invention provides a covering material which can be used, for example, as flooring and is able to combine the majority of the qualities of the covering materials of a traditional type, without at the same time sharing their drawbacks.
In particular, the present invention describes a covering material having the characteristics referred to specifically in the ensuing claims. The claims form an integral part of the disclosure of the invention provided herein.
The covering material described in what follows is able to offer, as regards the characteristics of resistance to the environment (mechanical stresses and attack by chemical agents, resistance to burns, etc.), altogether equivalent characteristics, and at least in some cases decidedly superior ones, both as compared to coatings made of plastic material and as compared to coatings made of rubber (and consequently, from this standpoint, a performance amply superior to that of coatings made of linoleum).
As regards the aesthetic characteristics, the method described herein enables production of covering materials with chromatic features chosen within a practically infinite range, with a very wide range of choices as regards “marble” or “granite” effects. Alongside this, results are obtained that, at least on the basis of the experiments so far conducted by the present applicant, are in many cases qualitatively superior to the results that can commonly be achieved in the case of coatings made of plastic material and rubber material.
The invention will now be described, purely by way of non-limiting example, with reference to the annexed plate of drawings, in which:
U.S. Patent Publication No. 2005/0065236, in the name of Mondo, S.p.A., the assignee of the instant application, describes a laminar covering material comprising a polyolefin matrix having a first coloring and a phase of particulate elastomer material dispersed in said polyolefin matrix, the particulate phase comprising particles of at least one second coloring that contrasts with the first coloring. In a preferred way, the elastomer material is vulcanized elastomer material, and the aforesaid phase of elastomer material comprises particles of elastomer material with at least two different colorings that contrast with the coloring of the polyolefin matrix.
In a particularly preferred way, the material described in said prior document envisages that the particles of the phase of elastomer material will present, at least in a proportion that usually constitutes a substantial part of the phase of elastomer material, dimensions between 100 μm and 500 μm. The polyolefin is preferentially chosen in the group consisting of polyethylene, polypropylene and mixtures thereof, whilst the elastomer is chosen in the group consisting of natural rubber (NR), SBR, EPM, EPDM, IR, BR, CR and NBR, as well as mixtures thereof.
U.S. Patent Publication No. 2005/0065236 hence envisages addition of a dispersed phase of particulate material (the so-called “dust”) of vulcanized rubber to a polyolefin matrix (for example polyethylene).
Materials based upon this combination are in themselves well known in the art, as witnessed by documents such as U.S. Pat. Nos. 4,130,535 and 4,311,628. The solutions described in these prior documents aim at obtaining so-called “thermoplastic elastomers”, i.e., materials that can be used for technological applications, for example in the automotive sector. The materials obtained according to these documents of the known art are suitable for applications typical of elastomers, such as rubber (for example, weatherproofing for windows of motor vehicles, production of hoses for the conveyance of fluids even at high temperature and pressure, etc.). For this purpose, these known solutions emphasize the importance linked to the fact that the particles of elastomer (rubber) constitute a finely dispersed phase within the polyolefin matrix, with a grain size typical of particles of elastomer of markedly submillimetric dimensions. For example, in U.S. Pat. No. 4,130,535, typical dimensions of the particles of rubber constituting the dispersed elastomer phase are indicated in the region of 50 μm.
In the specific case, the arrangement described herein is designed to form a coating which can be used, for example, as flooring. In this regard, it will likewise be appreciated that each of the operating steps described in what follows, as well as the equipment that enables its implementation—taken in themselves—is amply known in the art. This fact thus renders it superfluous to provide herein a detailed description of said operating steps and of the corresponding equipment.
In particular, one embodiment provides a coating with an appearance approximately resembling that of a marble with a fine granular structure or, in a perhaps more precise way, approximately resembling the appearance of granite, all this, of course, with practically infinite possibility of varying the chromatic characteristics of the coating.
As may be better appreciated in the diagram of
The layer designated by 101 constitutes the outermost or uppermost layer of the coating, namely, the layer that will be exposed on the outside, thus being visible.
The layer designated by 102 is an intermediate layer, whilst the layer designated by 103 is a bottom layer or backing, namely, the layer used for applying the coating 10.
For example, in the case of a coating 10 made in the form of a flooring, the layer 103 constitutes the bottom or base layer of the flooring, which will be laid on the substrate to be coated (for example a cement course).
The representation with a dashed line in the bottom part of
The layer 120 functions as stabilization layer and typically consists of glass fiber and/or polyester fiber. The choice of setting the layer 120 between the layers 102 and 103 is preferred, but not imperative: for example, the stabilization layer 120 could also be set between the layer 101 and the layer 102.
An important characteristic of the solution described herein is represented by the fact that the layers 101, 102 and 103 have a base of a mixture of polyolefin material and thermoplastic elastomer (TPE) that is substantially of the same nature for all three layers 101, 102, 103.
The polyolefin material in question is typically chosen in the group consisting of polyethylene, polypropylene and/or mixtures and/or copolymers thereof. Preferably, said material is substantially polyethylene, and in a particularly preferred way, low-density polyethylene.
The thermoplastic elastomer is typically chosen in the group made up of TPS, i.e., thermoplastic elastomers of styrenic origin, and mixtures thereof. Preferably, said thermoplastic elastomer of styrenic origin is substantially poly(styrene-butadiene-styrene) (SBS).
Defining the layers in question as having a base of a mixture of polyolefin material/thermoplastic elastomer that is substantially of the same nature for all three layers is equivalent to saying that said mixture is constituted by the same materials (for example, polyethylene and SBS) for all three layers 101, 102 and 103, at the same time envisaging the possibility of differentiating the three layers 101, 102 and 103 in relation, for example, to the quantity of fillers present in the polyolefin/TPE matrix.
In the case in point, the base coloring of all three layers 101, 102 and 103 can be substantially the same. For example, all three layers 101, 102 and 103 can present a basic coloring of green, or red, or blue, as a whole identical for all three layers. The stabilization layer 120, if present, does not usually have a particular chromatic connotation, being typically made up, as has already been said, of glass fiber and/or polyester fiber.
The fact that all three layers 101, 102 and 103 have a base of polyolefin/TPE mixture is bound to favor the intimate adhesion and cohesiveness of the three layers 101, 102 and 103. This latter characteristic confers particular features of stability on the coating 10 as a whole, above all with reference to the possible application as a flooring for sports facilities. In this connection, it will be appreciated that the stabilization layer, if present and independently of where it is set, is chosen with a sufficiently coarse mesh and a sufficiently small mass per unit area (for example 25-50 g/m2) to cause the stabilization layer itself to be in effect incorporated in the polyolefin/TPE matrix of the adjacent layers.
In the currently preferred embodiment of the invention, the layers 102 and 103 differ from one another prevalently on account of the different level of filling present therein (typically mineral filler, such as calcium carbonate or other fillers currently used in the sector of coatings/floorings).
The bottom layer 103 in fact usually consists of a polyolefin/TPE matrix containing fillers so as to have a density equal to or greater than 1.6 g/cm3. A density of this type confers on the layer 103 (and on the coating 10 as a whole) characteristics of mechanical stability and firm anchorage. Typically, the thickness of the layer 103 accounts for approximately 40%-60% of the overall thickness of the coating 10. Excluded from said given amount is the height of the formations 103 (if present).
Furthermore, when at the end of the process of fabrication described in greater detail in what follows the bottom or outer face of the bottom layer 103 is subjected to a treatment of grinding, the presence of a high level of filling means that the aforesaid outer face 103a (the bottom one in the representation of
Albeit with a formulation substantially identical to the polyolefin/TPE matrix, the intermediate layer 102 has a lower level of filling than that of the base layer 103; typical values of the density of the intermediate layer 102 are 1.3-1.4 g/cm3. The reasons for this choice will emerge more clearly from what follows.
The thickness of the layer 102 also accounts for approximately 40%-60% of the overall thickness of the coating 10, whilst (as may be seen from the cross section of
The overall aesthetic effect of the coating 10 results from the presence of the top or outermost layer 101. The latter is obtained preferentially starting from granules 104, 106, 108 of a polyolefin/TPE mixture substantially similar to the mixture constituting the matrix of the layers 102 and 103, with the difference represented by the fact that, in the case of the outermost layer 101, said matrix is substantially free from fillers i.e., it contains only a small amount of fillers (for example, on account of the presence of pigmenting fillers) so as to have a density in the region of 1-1.1 g/cm3.
In what follows it will be assumed—purely by way of example—that the layer 101 consists of granules 104, 106 and 108 of three different colorings, such as, for example, dark green, medium green or grayish-green, and light green.
The individual granule can have, instead, a single coloring or different colorings, given for example by the presence, within the granule, of portions having different colorings.
Of course, the fact that the example illustrated herein envisages the use of granules 104, 106, 108 of three different colors must not be interpreted as in any sense limiting the possibility of using granular materials in a smaller number (for example, it is possible to envisage the presence of just one type of granular material) or a larger number (for example, four or more) as compared to the example presented herein.
The typical dimensions of the particles/granules 104, 106, 108 are in a range of from a fraction of a millimeter to some millimeters, if it is also necessary to take into account the fact that said dimensions, as perceived by the observer, usually tend to increase as a result of the process of fabrication described in what follows, which tends to a certain extent to compress/flatten out said granules. The experiments conducted by the present applicant show that also particles of smaller dimensions can achieve a certain effect in the context of the overall chromatic result, creating, in the coating obtained as final result, portions of material having a coloring that is intermediate between the colorings of the various starting components.
From
The fact of making the outermost layer 101 with a particulate material (granules 104, 106 and 108) substantially not containing fillers and hence substantially free from fillers i.e., containing only a small amount of fillers, with the values of density indicated herein, has surprisingly and unexpectedly proven advantageous as regards the possibility of preventing the appearance of directional phenomena upon visual observation of the top layer 101.
The importance of this aspect can be more fully appreciated with reference to the process currently preferred for making the coating 10 schematically represented in
In the left-hand part of
The reference number 110 is a schematic representation of a coupling station, where the strips of the layers 102 and 103 (and 120) are set on top of one another, without for the moment achieving a more intimate connection, so as to cause them to advance in a coordinated way towards a station 112, where there is then carried out, according to a technique of “seeding”, which is widely used in the fabrication of marbled floorings, the operation of depositing the material that is to form the outermost layer 101, namely, the granules 104, 106 and 108.
In a possible variant embodiment of the invention, the layer 101 can also be supplied in the form of a strip or ribbon that is wound off a respective reel and is coupled (juxtaposed) with the strips of the layers 102 and 103 (and 120) in the station 110.
The set of the elements or parts that are to form the coating 10 is then sent on towards equipment for the simultaneous application of heat and pressure, designated as whole by 114.
The use of presses of this type is well known and widely employed in the techniques of fabrication of coatings and floorings made of plastic and rubber material.
Whatever the specific solution of the system used, the simultaneous application of heat and pressure to the set of parts or components described leads to the formation of a coating structure such as the structure indicated as a whole by 10 in
Said coating structure can then be sent on for subsequent processes.
For example, the reference number 116 in
Of course, without prejudice the principle of the invention, the details of fabrication and the embodiments may vary widely with respect to what is described and illustrated herein, without thereby departing from the scope of the present invention.
All of the above U.S. patents, U.S. patent application publications, U.S. patent applications, foreign patents, foreign patent applications and non-patent publications referred to in this specification and/or listed in the Application Data Sheet, are incorporated herein by reference, in their entirety.
| Number | Date | Country | Kind |
|---|---|---|---|
| 04425860.6 | Nov 2004 | EP | regional |