CPVC drain waste and vent fittings

Abstract

A drain, waste and vent (“DWV”) fitting is made from chlorinated polyvinyl chloride.

Description

FIELD OF THE INVENTION

[0002] This invention relates generally to fittings and, more specifically, to drain, waste, and vent fittings used for piping that handles corrosive waste.

BACKGROUND OF THE INVENTION

[0003] Drain, waste, and vent fittings (referred to as “DWV fittings” or “DWV pattern fittings”) have been used for many years to move liquids at low pressures using gravity. DWV fittings are used to move waste liquids and solids out of bathrooms and kitchens and into sanitary sewers. DWV pattern fittings are also used to plumb, as drains for roof and floor, in industrial processes, in institutional settings, and in commercial waste systems.

[0004] DWV fittings for handling non-corrosive waste have been constructed of many materials: clay, iron, copper, ABS plastic, and PVC plastic. DWV fittings are generally of the type having sweeping full bore solids handling design and fall. “Fall” as that term is used in drain systems means to move the material and keep the pipe from filling with solids. Typical fall is about ¼″ per foot, meaning every foot of pipe is ¼″ lower than the last. This fall is typically built into the fittings. For example, in the case of a sanitary tee branch, the sanitary tee branch isn't exactly 90 degrees, so that when pipe is attached to it, the tee branch approaches at a slope of about ¼″ per foot.

[0005] Problems, however, arise when DWV fittings are used in piping systems that handle corrosive waste. As used herein, “corrosive waste” includes waste such as chemical corrosives and/or waste that can reach temperatures of about 210 degrees Fahrenheit. One problem with present DWV fittings used for corrosive wastes is that present fittings are susceptible to the formation of leaks over time. Another problem is that installation of present fittings can be cumbersome and time consuming.

[0006] DWV fittings for handling corrosive waste have typically been constructed of either polyolefin ASTM F1412-01, specifically polypropylene (PP) with a flame retardant added, or polyvinylidene Fluoride ASTM F1673-95. These fittings can require a mechanical joint connection system or a fusion connection system to connect pipe to fittings. The mechanical joining method is time consuming and prone to leaking after time because the plastic moves and the joint loosens. The fusion method is difficult, cumbersome, and requires special equipment. Most fusion systems use metal coils and an electrical device to heat and melt the two surfaces to be joined. These metal coils remain in the middle of the joint and can be corroded away causing a leak-path if they become exposed on the inside. The fusion joining method is not consistently dependable. The fusion joining method varies in consistency based on the quality of power available on the job sites, the skill of the installer, and the required dimensional stability of the parts to be joined. Leaks are not uncommon in corrosive waste systems that use polyolefin DWV fittings and polyvinylidene fluoride DWV fittings.

[0007] Accordingly, there is a need for DWV fittings that avoid the aforementioned problems of difficulty in installation and susceptibility to leaks in the prior art.

DRAWINGS

[0008] FIG. 1 shows a DWV fitting having features of the present invention.

DETAILED DESCRIPTION

[0009] Patterned fittings constructed of CPVC “chlorinated polyvinyl chloride” solve the need for DWV fittings that can handle corrosive waste. CPVC fittings are easily installed, and are not as susceptible to leaks as the fittings in the aforementioned prior art.

[0010] DWV fittings made from CPVC are easily installed, and provide a strong bond with pipes. For example, CPVC like PVC materials, can be solvent cement welded, or joined by chemically dissolving the surface of both pipe and fitting, forcing the two together, then allowing the solvent to leave and, are common installation practices used by those of ordinary skill in the art. Solvent cementing is much easier, requires significantly less skill, and produces a more leak resistant joint than other joining methods. The invention described in this application has these useful benefits over the aforementioned prior art.

[0011] DWV patterned fittings of the present invention are preferably made from CPVC material compounds corresponding to ASTM D1784, Standard Specification for Rigid Ply (Vinyl Chloride) (PVC) Compounds and Chlorinated Poly (Vinyl Chloride) (CPVC) Compounds. The typical physical properties of DWV patterned fittings that were made according to the present invention are:

Property	Test Method	Typical Value
Mechanical Properties @ 73° F.
Specific Gravity	ASTM D 792	1.49
Tensile Strength, psi	ASTM D 638	8010
Tensile Modulus, psi	ASTM D 638	495,000
Flexural Strength	ASTM D 790	13,000
Izod Impact, ¼ in.ft-lb/in.notched	ASTM 256	1.4
Thermal Properties
Heat Deflection Temperature, ° C. at 66 psi	ASTM D 648	101
Thermal Conductivity, BTU/hr/sq ft/° F./in	ASTM C 177	.95
Coefficient of Liner Expansion, in/in/° F.	ASTM D 696	3.4 × 10−5
Flammability
Limiting Oxygen Index	ASTM D 2863	60
UL 94 Rating	UL 94	V-0, 5VB
Flame & Smoke Rating1	CAN/ULC S102.2
Pipe: Flame Spread		0
Smoke Developed		5-30
Fittings: Flame Spread		5-10
Smoke Developed		15-50
Solvent Cement	ASTM F493	Heavy Body; Yellow
		Color

[0012] 1—Based on test of physical product, as opposed to test of material only.

[0013] The DWV fittings of the present invention are inert to most mineral acids, bases, salts, and aliphatic hydrocarbons, and compare favorably to other non-metals in these chemical environments. The general chemical resistance overview of DWV fittings of the present invention are:

	Weak Acids	Excellent	Salts	Excellent
	Strong Acids	Excellent	Aliphatic Solutions	Good
	Weak Bases	Excellent	Halogens	Good-Fair
	Strong Bases	Excellent	Strong Oxidants	Good-Fair

[0014] DWV fittings according to the present invention have been produced according to applicable DWV patterns of ASTM D3311, Standard Specification for Drain, Waste, and Vent (“DWV”) Plastic Fitting Patters, as well as having been produced according to speciality patterns. An example of a fitting according to the present invention is shown in FIG. 1. FIG. 1 shows a lab waste sanitary tee made from CPVC material compounds corresponding to ASTM D1784, Standard Specification for Rigid Ply (Vinyl Chloride) (PVC) Compounds and Chlorinated Poly (Vinyl Chloride) (CPVC) Compounds. Examples of different sizes for lab waste sanitary tee as shown in FIG. 1, include those having the following dimensions in inches for G1 and G2:

SIZE	G1	G2
1½	1¾	1
2	2{fraction (5/16)}	1⅜
3	3{fraction (1/16)}	1¾
4	3{fraction (15/16)}	2¼
6	5	3½
8	6	4½

[0015] One of ordinary skilled in the art will recognize that other DWV fittings in a variety of different sizes, like the above sanitary tee, can be constructed using CPVC. All drainage fittings of the present invention with 90 degree angles, such as sanitary tees and elbows, preferably have socket pitch to maintain about ¼ inch per foot.

[0016] Appropriate DWV fittings of the present invention can be used to transition to piping that is not constructed of CPVC so long as the piping is suitable for corrosive waste. Piping made of CPVC is preferable for use with CPVC DWV fittings. For example, Spears® LabWaste™ CPVC Schedule 40 pipe (manufactured for and sold by Spears Manufacturing Company, 15853 Olden Street, Sylmar, Calif. 91342) which is produced in accordance with dimensional requirements of ASTM F441, Standard Specification for Chlorinated Poly (Vinyl Chloride) (CPV) Plastic Pipe, Schedule 40 and 80, is a suitable CPVC pipe, and has dimensions in inches as follows:

	Pipe Diameter
	1½	2	3	4	6	8
Avg. O.D.	1.900	2.375	3.500	4.500	6.625	8.625
Avg. I.D.	1.592	2.049	3.042	3.998	6.031	7.943
Min. Wall	.145	.154	.216	.237	.280	.322

[0017] The thermal expansion table below is useful for the installation of this CPVC piping with fittings according to the present invention under specified temperatures:

Length
of Run
(L) in	Length Change in Inches (ΔL) for Specified Change in Temperature (ΔT)
feet	20° F.	30° F.	40° F.	50° F.	60° F.	70° F.	80° F.	90° F.	100° F.
10	.08	.12	.16	.20	.24	.29	.33	.37	.41
20	.16	.24	.41	.51	.61	.71	.82	.92	1.02
40	.33	.49	.65	.82	.98	1.14	1.31	1.47	1.63
50	.41	.61	.82	1.02	1.22	1.43	1.63	1.84	2.04
70	.57	.86	1.14	1.43	1.71	2.00	2.28	2.57	2.86
90	.73	1.10	1.47	1.84	2.20	2.57	2.94	3.30	3.67
120	.98	1.47	1.96	2.45	2.94	3.43	3.92	4.41	4.90

[0018] Thermal expansion change in length is calculated from expected change in temperature and given Coefficient of Linear Thermal Expansion of 3.4×10−5 in./in. °F for CPVC as follows:

[0019] ΔL=12 eL (ΔT):

[0020] e=3.4×10−5 in./in. °F

[0021] L=Length of Run in feet

[0022] ΔT=Temperature Change in °F

[0023] An example of using the above thermal expansion chart is shown below: How much will a 50 ft. run Spears® LabWaste™ pipe expand if the expected ambient temperature will range from 45 °F. to 85 °F.?

[0024] ΔL=12 eL (ΔT)

[0025] ΔL=12×0.000034×50×40

[0026] ΔL=0.816 inches

[0027] When solvent cements are used to join DWV fittings to pipes, solvent cements are preferably produced according to ASTM F493, Standard Specification for Solvent Cements for Chlorinated Poly (Vinyl Chloride) (CPVC) Compounds. DWV fittings of the present invention have been easily joined to pipes made of CPVC using Spears® LW-5 One-Step Solvent Cement (manufactured for and sold by Spears Manufacturing Company, 15853 Olden Street, Sylmar, Calif. 91342) that has been specially formulated for corrosive/acid waste applications and manufactured in accordance with ASTM F-493, Standard Specification for Solvent Cements for Chlorinated Poly (Vinyl Chloride) (CPVC) Plastic Pipe and Fittings. When cured, this cement provides a fused joint that maintains the same physical and chemical resistance properties as the CPVC components in the system. Spears® LW-5 is a “one-step” cement and does not require the use of primer. Systems using DWV fittings and pipe made of CPVC can be additionally joined using threaded (NPT) or flanged connections where removal or connection to supplementary equipment is required. Special Compression Couplings can be used for joining to Polypropylene systems.

[0028] Solvent cement joints should be made according to directions on the cement container label. On initial assembly, all joints should be hand-held together without movement for 30 seconds. An initial set time is recommended to provide good handling strength after which the joint will handle normal stresses of installation. Cure time is the recommended waiting period prior to placing the joint into service. Set and cure time are relative to temperature at time of installation. Best results are obtained at temperatures between 400 and 110° F. The following set and cure time recommendations are estimates based on laboratory tests. Due to the many field variables, these times are useful as a general guide only.

Recommended Set & Cure Time
Temperature	Initial Set	Cure
60°-100° F.	30 min.	1 hr.
40°-60° F.	1 hr.	2 hr.
0° F.	2 hr.	4 hr.

[0029]

Average Number of Joints per Quart of LW-5 One-step Cement
	Pipe Diameter
		1½	2	3	4	6	8
	No. of Joints	90	60	40	30	10	5

[0030] Systems using DWV fitting made of CPVC should be properly supported to avoid stress caused by sagging. The following chart shows recommended horizontal support spacing. Pipe can be supported with conventional hangers and brackets. The hangers should not be over tightened to restrict pipe movement or cut into the pipe.

Recommended Hanger Spacing (feet)
	Pipe Diameter
		1½	2	4	6	8
	Hanger Spacing	6	6	7½	8	9

[0031] The invention is suitable for underground service. Underground installation should be in a smooth, uniform trench bottom that supports the length of the CPVC DWV pipe over its entire length, free of rocks and debris. This subsoil should be stable to provide physical protection of the pipe and fittings. Where large boulders are not removed, the trench should be padded with sand or fine-grain soil. The trench should be wide enough to allow for easy installation, but should be kept as narrow as possible. The trench construction, bedding and backfill shall be in accordance with ASTM Standard D2774 and local codes.

[0032] Snaking the pipe is recommended if thermal expansion or contraction is anticipated. Pipe that is joined during the hottest portion of a summer day will undergo a certain amount of contraction during the cooler night time period. This can place stresses on a newly solvent-cemented joint, possibly causing it to separate or leak. Snaking is also suggested when the trench is backfilled with cool earth before the joints are fully cured. The following is a suggested “Loop Offset” chart: 1

[0033] A larger size pipe as a sleeve should be installed where piping must pass through masonry walls. Only solvent cement connection should be used in underground piping. The pipe should be surrounded with an initial backfill material having a particle size of ½″ or less, free of sharp rock or debris and uniformly compacted in layers. Refer to ASTM D2774, Underground Installation of Thermoplastic Pressure Piping, for additional information on underground installations.

[0034] Preferably, DWV fittings according to the present invention used in a system should be tested with water to ensure its integrity. The testing can be in its entirety or in sections.

[0035] All openings should be closed tight except the highest opening and the system should be filled with water to the point of overflow. A minimum of ten (10) foot (3048 mm) head should be used for entire system or for each section tested. System or section should be set for about 15 minutes or longer before inspection for leaks. Duration of the test shall be per local code.

[0036] CPVC DWV pipe and fitting systems can be used with many kinds of waste, including industrial process waste, corrosive waste, sanitary waste, polyolefin acid waste, iron acid waste and glass acid waste. CPVC DWV pipe and fitting systems are ideal for use in environments which are closely controlled for flame and smoke. CPVC DWV pipe and fitting systems can be connected to polypropylene acid waste systems and to PVDF acid waste systems.

[0037] The CPVC DWV pipe and fitting systems of the invention can be disposed within other pipe and fitting systems to create a “double contained” pipe and fitting system.

[0038] In a typical embodiment, the DWV fitting of the invention consists of chlorinated polyvinyl chloride. In other embodiments of the invention, the DWV fitting consists essentially of chlorinated polyvinyl chloride.

EXAMPLE

[0039] An example of a special drainage system for corrosive chemical or acid waste according to the present invention was manufactured from CPVC Type IV material, ASTM D 1784 Cell Classification 23447. All pipe fittings and solvent cement were supplied together as a system, as Spears® Manufacturing Company, 15853 Olden Street, Sylmar, Calif. 91342. Spears® LabWaste™ CPVC Corrosive Waste Drainage Systems were manufactured to the following applicable portions of ASTM Standards:

Applicable Conformance Standards
		Standard Specification
Conformance Criteria	Applicable Standard	or Practice Title
Product Certification	NSF Standard 14 Special Engineered	Standard14: Plastics Piping
(3rd party approval to criteria	(SE) product certification for	System Components and
specified below)	corrosive waste end use	Related Material,
		NSF-cw S.E. Certified to
		specified conformance
		standards & specifications
Material	D1784, cell class 23447 (CPVC)	D1784: Standard
		Specification for Rigid
		Poly(Vinyl Chloride) (PVC)
		and Chlorinated Poly(Vinyl
		Chloride) (CPVC)
		Compounds
Dimensions and Tolerances - Pipe	ASTM F1412, Section 6.1, Sch 40	F1412: Standard
Dimensions and Tolerances - Fittings	ASTM F1412, Section 6.2	Specification for Polyolefin
Chemical Resistance	ASTM F1412, Section 6.3	Pipe and Fittings for
Adjusted concentrations for CPVC	ASTM 1673, Section 8.3	Corrosive Waste Drainage
Water Absorption	ASTM F1412, Section 6.4	Systems
Mechanical Joint - Transition Fittings	ASTM F1412, Section 6.5	F1673: Standard
Flattening - Pipe	ASTM F1412, Section 6.8	Specification for
Impact Resistance - Pipe & Fittings	ASTM F1412, Section 6.9	Polyvinylidene Fluoride
Workmanship, Finish & Appearance	ASTM F1412, Section 7	(PVDF) Corrosive Waste
Fittings		Drainage Systems
Solvent Cement	F493	F493: Standard Specification
		for Solvent Cements for
		Chlorinated Poly (Vinyl
		Chloride) (CPVC) Plastic
		Pipe and Fittings

[0040] All pipes in the above example were Spears® LabWaste™ CPVC Schedule 40 (manufactured and sold by Spears® Manufacturing Company, 15853 Olden Street, Sylmar, Calif. 91342), and manufactured to applicable requirements of ASTM F1412. All pipes were CAN/ULC S102.2 evaluated for surface burning characteristics for flame spread and smoke development with ratings designated on the pipe marking. All pipe markings were accompanied by a yellow stripe for identification of CPVC chemical waste system. All fittings were CPVC drainage patterns meeting the applicable requirements of ASTM F1412. All fittings were CAN/ULC S102.2 evaluated for surface burning characteristics for flame spread and smoke development with ratings designated on the original package labeling. Joining method for pipe and fittings was done by solvent cement welding. Solvent cement was “one-step” primerless type CPVC cement formulated for resistance to corrosive chemicals and manufactured in accordance with ASTM F493. Spears® LabWaste™ CPVC Corrosive Waste Drainage System was independently tested for chemical resistance and certified to applicable ASTM standards as a Special Engineered (SE) product under NSF Standard 14 by NSF International, Ann Arbor, Mich.

[0041] Having thus described the invention, it should be apparent that numerous structural modifications and adaptations may be resorted to without departing from the scope and fair meaning of the instant invention as set forth hereinabove.

Claims

1. A DWV fitting comprised of chlorinated polyvinyl chloride.

2. A DWV fitting consisting essentially of chlorinated polyvinyl chloride.

3. A DWV fitting consisting of chlorinated polyvinyl chloride.

4. A method for transporting waste comprising the step of transporting the waste in pipes and pipe fittings comprising chlorinated polyvinyl chloride.

5. The method of claim 4 wherein the waste is an industrial process waste.

6. The method of claim 4 wherein the waste is a sanitary waste.

7. The method of claim 4 wherein the waste is an acid waste.

8. The method of claim 4 wherein the pipes and pipe fittings comprising chlorinated polyvinyl chloride are connected to a polypropylene acid waste system.

9. The method of claim 4 wherein the pipes and pipe fittings comprising chlorinated polyvinyl chloride are connected to a PVDF acid waste system.

10. The method of claim 4 wherein the pipes and pipe fittings comprising chlorinated polyvinyl chloride are connected to a glass acid waste system.

11. The method of claim 4 wherein the pipes and pipe fittings comprising chlorinated polyvinyl chloride are connected to a polyolefin acid waste system.

12. The method of claim 4 wherein the pipes and pipe fittings comprising chlorinated polyvinyl chloride are connected to an iron acid waste system.

13. The method of claim 4 wherein the pipes and pipe fittings comprising chlorinated polyvinyl chloride are disposed within other pipes.