Patent Application
20100139451
1. Field of the Invention
The present invention relates to a crankshaft member and manufacturing method thereof, and more particularly to a crankshaft member having high fatigue strength and its method of manufacture.
2. Description of the Background Art
In a reciprocating engine of an automobile or the like, a crankshaft is used to convert the up-and-down motion of a piston into a rotating motion. The crankshaft comprises a journal portion that rotates around a rotating shaft, an arm portion provided at a predetermined interval along the rotating shaft and formed protruding sideways, and a pin portion of the protruding end portion of the arm portion that is connected via a pin to a connecting rod that connects with a piston. The up-and-down motion of the piston rotates the arm portion around the rotating shaft via the connecting rod, and is converted into a rotating motion. The rotating motion can then be extracted from the journal portion.
This crankshaft, comprising such portions, is integrally formed by hot forging the steel rod into the required shape, for example. Subsequently, as required, a normalizing process is carried out, removing residual stress, and surface hardening process such as a soft-nitriding or nitriding process is carried out, improving fatigue strength. During the forging or the surface hardening process, the crankshaft member is likely to bend or warp. Therefore, subsequently, a bending correction process is carried out to correct bending, warping, and the like.
Now, in general, through the bending correction process, any bends or warps is corrected by bending the crankshaft member in the direction opposite the direction of the bend. At this time, particularly on a crankshaft member that has been subjected to a surface hardening process, such as a soft-nitriding or nitriding process, cracks readily occur on the hardened surface as a result of the bending. These cracks may cause damage to the crankshaft.
JP2001-254143A discloses a crankshaft member made of a micro-alloyed steel consisting of a two-phase structure of ferrite and perlite with a decreased perlite grain size, that decreases crack occurrence in the hardened layer during the bending correction process. This document states that crack occurrence can be decreased in the hardened layer by reducing the size of the perlite grain since cracks in the hardened layer grow in units of perlite grains. On the other hand, when the perlite grain size in the two-phase structure of ferrite and perlite is decreased, the ratio of ferrite having a lower hardness than perlite increases relatively. Therefore, when the material is used for a crankshaft, the strength of the overall crankshaft member becomes inadequate. As a result, the hardness of the hardened layer needs to be increased to increase the fatigue strength of the overall crankshaft member, causing the hardened layer to remain susceptible to cracking.
On the other hand, JP2007-197812A discloses a crankshaft steel comprising a two-phase structure of ferrite and perlite, capable of forming a soft-nitride layer that provides high fatigue strength to a crankshaft when used for a crankshaft despite its low level of hardness, by including predetermined amounts of Cu, Ni, and Cr, and a crankshaft member that uses the same. The invention makes it possible to achieve the same level of fatigue strength with a hardened layer having a lower level of hardness, thereby making it possible to further reduce crack occurrence.
As described above, through the bending correction process, any bends or warps is corrected by bending the crankshaft member in the direction opposite the direction of the bend. Therefore, a crankshaft member that makes it possible to perform a bending correction process without imparting excessive strain, i.e., a crankshaft member with superior bending correctability, is preferred. In contrast, such a crankshaft member with superior bending correctability suffers a decrease in fatigue strength, which requires providing a hardened layer having increased hardness by a surface hardening process, such as a soft-nitriding or nitriding process. As a result, cracks readily occur from the hardened layer, making the bending correction process difficult.
In JP2007-197812A as well, the bending correctability of the steel used in a crankshaft member that is not provided with a hardened layer is increased by increasing the ratio of the ferrite phase, resulting in the need to increase the hardness of the hardened layer to provide fatigue strength to the overall crankshaft member.
The present invention was made in view of such circumstances, and it is therefore an object of the present invention to provide a crankshaft member having both high fatigue strength and good bending correctability, that is made of a steel capable of increasing bending correctability without particularly decreasing the fatigue strength of the overall crankshaft member, reducing crack occurrence in the hardened layer, and enabling easy and reliable execution of a bending correction process, and a manufacturing method thereof.
The crankshaft member according to the present invention is a member made of steel consisting essentially of a two-phase structure of ferrite and perlite, wherein the steel includes C, Ni, Mn, and Cr as required elements and Si, Cu, Mo, Ti, V, Nb, Ca, and S as optional elements that may be included, in the amounts of C within the range of 0.20 to 0.50 wt %, Si within the range of 0 to 0.6 wt %, Mn within the range of 0.5 to 1.5 wt %, Cu within the range of 0 to 0.7 wt %, Ni within the range of 0.05 to 1.5 wt %, Cr within the range of 0.05 to 0.45 wt %, and Mo within the range of 0 to 0.5 wt % to satisfy the condition 115≧70 C+8 Si+23 Mn+11 Cu+128 Cr+83 Mo≧50; at least a portion of the surface is provided with a hard nitride layer having an average hardness within the range of 300 to 450 HV; and lamellar spacing of the perlite is 0.3 μm or less.
According to the invention, during a bending correction process capable of imparting a relatively slow strain rate, the bending correction process can be reliably performed on a crankshaft member that is not provided with a hard nitride layer as a result of the two-phase structure of perlite and ferrite, which exists without a decrease in its relative amount, without particularly imparting excessive strain due to ferrite ductility. That is, superior bending correctability is achieved. Further, a predetermined amount of Ni imparts ductility to the perlite grain having the narrow lamellar spacing of 0.3 μm or less in the hard nitride layer under the condition of slow strain rate that may be achieved during such an above-described bending correction process, thereby making it possible to prevent the layer from becoming the origin of a crack.
Therefore, the bending correction process can be easily performed without causing a crack to occur in the hardened layer. On the other hand, when the steel material is used for a crankshaft that is subjected to cyclic stress at a relatively high frequency, the hard nitride layer having an average hardness within the range of 300 to 450 HV imparts high fatigue strength to the overall crankshaft member, and the perlite having a high level of hardness with lamellar spacing of 0.3 μm or less provides high fatigue strength even in the portion that is not provided with a hard nitride layer. That is, the present invention enables to achieve a crankshaft member having high fatigue strength. Further, as an additional advantage, by verifying whether or not the lamellar spacing of the perlite is within a predetermined range, it is possible to assess whether or not the fatigue strength of the product is acceptable, thereby enabling easier control of the manufacturing process and making it possible to reduce manufacturing costs.
Further, in the above-described invention, the hard nitride layer may be imparted by a soft-nitriding process. According to the invention, it is possible to provide a perlite grain having higher ductility to the hard nitride layer, and during the bending correction process, the hard nitride layer cracking can be prevented, thereby enabling easy bending correction. At the same time, higher fatigue strength can be achieved for use as a crankshaft.
Further, in the above-described invention, the optional elements may include S within the range of 0.01 to 0.2 wt %. According to the invention, the predetermined amount of S can increase machinability. That is, the predetermined amount of S enables easy machining during the cutting process and further reduce crack occurrence in the hardened layer during machining.
Further, in the above-described invention, the optional elements may include at least one or more of Ti, V, Nb and Ca, Ti in an amount of 0.1 wt % or less, V in an amount of 0.1 wt % or less by weight, Nb in an amount of 0.1 wt % or less by weight and Ca in an amount of 0.005 wt % or less. According to the invention, it is possible to improve the yield strength and/or machinability of the steel of the crankshaft member without reducing its high fatigue strength or superior bending correctability.
Further, in the above-described invention, unavoidable impurity elements may include P in amounts of 0.035 wt % or less and O in the amounts of 0.01 wt % or less, respectively. According to the invention, it is possible to prevent a reduction in toughness.
Furthermore, the manufacturing method according to the present invention of a crankshaft member such as described above may comprise the steps of hot forging the steel into a predetermined shape at an austenite single-phase region temperature, continuously cooling the steel to obtain a two-phase structure of ferrite and perlite having lamellar spacing of the perlite of 0.3 μm or less, and soft-nitriding at least a portion of the steel to provide a hard nitride layer having an average hardness of the surface thereof within the range of 300 to 450 HV.
According to the invention, it is possible to achieve a crankshaft member having high fatigue strength. Further, by verifying whether or not the lamellar spacing of the perlite is within the predetermined range, it is possible to assess whether or not the fatigue strength of the product is acceptable, thereby enabling easier control of the manufacturing process and making it possible to reduce manufacturing costs.
Further, in the above-described invention, the hot forging may be performed at a temperature of 1050 degrees Celsius or higher. According to the invention, hot forging can be performed while completely dissolving the precipitates, thereby preventing forging cracks and making it possible to obtain a good product.
Further, in the above-described invention, the continuous cooling may be performed at a cooling rate of 0.3 to 20 degrees Celsius per second, particularly the steel being cooled from 800 degrees Celsius to 450 degrees Celsius. According to the invention, it is possible to reliably obtain perlite having a narrow lamellar spacing of 0.3 μm or less in the steel of the above-described component composition.
Prior to obtaining a crankshaft disclosed in the description of the preferred embodiments of the present invention, empirical experiments such as the following were performed. The empirical experiments are described below with reference to accompanying drawings.
Steel comprising the components shown in
The cooled square rods for test pieces 1 to 14 and square rod test pieces 2-1 to 2-6 were machined to 210 mm long test pieces.
The fatigue test was carried out using an Ono-type rotating-bending fatigue test machine, under the test conditions of a test rotation speed of 3,000 rpm, a stress ratio of −1, and room temperature. The fatigue limit was obtained by repeating the test 107 cycles.
The hardness test was carried out using a Vickers hardness tester. The rod test piece 1 was cut at a curved portion 5 shown in
The perlite lamellar spacing was measured from a SEM (scanning electron microscope) image. The test piece used in the hardness test was molded and polished. And then, the polished surface is etched by picral to observe a two-phase structure of ferrite and perlite by SEM.
The bending correction test was carried out by a 3-points bending test. A test piece is mounted on two supports having a span W of 182 mm, as schematically shown in
First, test pieces 1 to 14 made of steel comprising the components shown in
The F value can be empirically defined as F=70 C+8 Si+23 MN+11 Cu+128 Cr+83 Mo related to the amounts of C, Si, Mn, Cu, Cr, and Mo, and these are listed in
Further, using the values of
Next, test pieces 2-1 to 2-6 in the same composition were cooled at various cooling rates V to observe the metal structure. These results are shown in
The cooling rate V (degrees Celsius per second) are plotted on a horizontal axis and the lamellar spacing λ (μm) of the perlite structure are plotted on a vertical axis for the test pieces 2-1 to 2-5 as shown in
In the above description, the guidelines for obtaining the range of each component indicated in
The C amount is preferably 0.2 to 0.5 wt % to improve the strength of the steel, more preferably 0.3 to 0.5 wt % to relatively increase the perlite amount.
Ni improves the ductility of perlite in the nitride layer and improves bending correctability. On the other hand, when Ni is added excessively, machinability decreases. Therefore, the Ni amount is preferably 0.05 to 1.0 wt %, more preferably 0.10 to 1.0 wt %.
Mn improves the yield strength of the steel, and produces an Mn sulfide when combined with S, thereby making it possible to improve machinability. Therefore, the amount included is preferably 0.5 to 1.5 wt %.
Cr increases the strength and toughness of the steel, making it possible to improve fatigue strength. Therefore, the amount is preferably 0.05 to 0.45 wt %, more preferably 0.06 to 0.3 wt % to ensure that the hardness of the nitride layer does not increase excessively, causing a decrease in bending correctability.
Si, Cu, Mo, Ti, V, Nb, Ca, S, and the like may be optionally included based on the purpose of element addition.
Si improves fatigue strength and functions as a deoxidizing agent during steel making. On the other hand, when Si is added excessively, bending correctability deteriorates. Therefore, the amount is preferably 0.6 wt % or less, more preferably 0.05 to 0.4 wt % from the viewpoint of stabilizing control in the soft-nitriding or nitriding process.
Cu improves the yield strength of steel, making it possible to increase strength. On the other hand, when Cu is added excessively, hot workability deteriorates. Therefore, the amount is preferably 0.5 wt % or less, more preferably 0.1 to 0.5 wt % from the viewpoint of fatigue strength improvement.
Mo can improve the strength of the steel, but deteriorates machinability when added excessively. Therefore, the amount is preferably 0.3 wt % or less.
Ti forms a fine oxide and acts as the nucleus of the above-described Mn sulfide. On the other hand, when added in excess, Ti excessively increases the hardness of the nitride layer. Therefore, to prevent deterioration of bending correctability, the amount is preferably 0.05 wt % or less by weight.
V can improve yield strength, but excessively increases the hardness of the nitride layer when added in excess. Therefore, to prevent deterioration of bending correctability, the amount is preferably 0.03 wt % or less.
Nb can improve yield strength, but excessively increases the hardness of the nitride layer when added in excess. Therefore, to prevent deterioration of bending correctability, the amount is preferably 0.03 wt % or less.
Ca can improve machinability, but produces CaS and conversely deteriorates machinability when added excessively. Therefore, the amount is preferably 0.005 wt % or less.
S produces Mn sulfide as described above, making it possible to improve machinability. When added excessively, however, cracks may readily occur as a result of hot forging. Therefore, the amount is preferably 0.01 to 0.15 wt %.
Note that the impurities that may be unavoidably included during manufacturing are preferably restricted as follows. That is, when the amount of P exceeds 0.035 wt %, toughness may deteriorate. Therefore, the amount is preferably 0.035 wt % or less. Similarly, the amount of O is preferably 0.01 wt % or less.
From the empirical experiments such as described above, a crankshaft member 10 as shown in
Such crankshaft 10 were manufactured using steel having compositions shown in test pieces 1 to 10 of
According to the embodiment, it was confirmed that it is possible to improve bending correctability while lessening crack occurrence in the hardened layer and easily and reliably executing bending correction, without decreasing the fatigue strength of the overall crankshaft member 10, in particular. It was also confirmed that such crankshaft member 10 achieves high fatigue strength.
Thus the present inventors arrived at the present invention upon focusing on the differences between the mechanical conditions imparted to the crankshaft member during bending correction and the mechanical conditions during use as a crankshaft. That is, while the former makes it possible to demand ductility in the crankshaft member in response to the strain that may be imparted at a relatively slow rate since the deformation rate may be arbitrarily changed, the latter demands deformation resistance in the crankshaft member in response to the high-frequency varying stress during actual use.
While the above has described representative embodiments of the present invention and modifications based thereon, the present invention is not limited thereto and suitable modifications can be made by those skilled in the art. It will be apparent to those skilled in the art that various modifications can be made in the present invention without departing from the spirit or scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-313698 | Dec 2008 | JP | national |