Patent Application
20110250379
Not Applicable
1. Field of the Invention
The present invention relates to oral prosthetics, and in a particular relates to cross-grain laminates used to increase the strength and workability of oral prosthetics.
2. Description of Prior Art
Mouth guards may be used in sports such as football, soccer, hockey, boxing, and others to protect the teeth of the athlete from impacts that contact sports generate. Such mouth guards are also helpful in preventing concussion. Mouth guards may be mandatory in some states even for “non-contact sports” such as basketball, soccer, and wrestling.
Dental mouth guards have been fabricated from several different plastic materials, and may be manufactured from ethylene vinyl acetate (EVA), urethanes, polycarbonates and other plastics which may have the properties of low toxicity and impact resistance. Dental mouth guards and other oral prosthetics have been made from extruded or injection molded plastic sheets which are heated in a dentist's laboratory or in a commercial dental laboratory and vacuum or pressure formed over a “stone” model of the patient's dentition.
Other prostheses and dental retainers are fabricated from the same or different materials using similar vacuum or pressure forming techniques.
A method for manufacturing a laminate for making a dental prosthetic is provided. The method includes arranging a first plastic sheet with a first grain orientation on a second plastic sheet with a second grain orientation. The first grain orientation and the second grain orientation form an angle greater than 0 degrees and less than 180 degrees. The method also includes fusing the first plastic sheet and the second plastic sheet c.
The fusing operation may include heating the first plastic sheet and the second plastic sheet to between 50 and 80 percent of a lowest melting point of the first plastic sheet and the second plastic sheet, or possibly between 50 and 70 percent of the lowest melting point, or possibly between 50 and 65 percent of the lowest melting point.
The fusing operation may include evacuating air from around the first plastic sheet and the second plastic sheet, and may include applying pressure to sandwich the first plastic sheet and the second plastic sheet.
The first plastic sheet and the second plastic sheet may include ethylene vinyl acetate (EVA), urethane, a polycarbonate or any other appropriate material.
The method may include labeling the laminate to indicate at least one of the first grain and the second grain.
The dental prosthetic made by the laminate may include a dental mouth guard, a dental splint, a retainer and/or another oral prosthetic.
The method may include arranging a third plastic sheet with a third grain orientation on the first plastic sheet or the second plastic sheet. The third grain orientation may form a second angle with the one of the first grain orientation and the second grain orientation corresponding to the first plastic sheet or the second plastic sheet. The second angle may be greater than 0 degrees and less than 180 degrees. The fusing operation may further include fusing the third plastic sheet with the first plastic sheet and/or the second plastic sheet.
The fusing of the third plastic sheet with the first plastic sheet and/or the second plastic sheet may occur at a same time, or at a different time, as the fusing of the first plastic sheet and the second plastic sheet. The angle may be approximately 90 degrees.
A dental prosthetic laminate is provided that includes a first plastic sheet having a first grain orientation, and a second plastic sheet having a second grain orientation fused to the first plastic sheet. The second grain orientation forms an angle with the first grain orientation. The angle is greater than 0 degrees and less than 180 degrees.
The dental prosthetic laminate may include a label on the first plastic sheet or the second plastic sheet indicating the first grain orientation and/or the second grain orientation.
The dental prosthetic laminate may further include a third plastic sheet with a third grain orientation on the first plastic sheet or the second plastic sheet. The third grain orientation may form a second angle with the first grain orientation or the second grain orientation corresponding to the first plastic sheet or the second plastic sheet. The second angle may be greater than 0 degrees and less than 180 degrees. The third plastic sheet may be fused with the first plastic sheet or the second plastic sheet.
A method for manufacturing a dental prosthetic form is provided that includes arranging a first plastic sheet with a first grain orientation on a second plastic sheet with a second grain orientation forming an angle between the first grain orientation and the second grain orientation. The angle is greater than 0 degrees and less than 180 degrees. The method also includes fusing the first plastic sheet and the second plastic sheet together to form a laminate, and forming the laminate into the dental prosthetic.
In the following description, dental prosthetics refers to dental mouth guards, splints, retainers or any other oral prosthetic. Additionally, any description of mouth guards in the following may also apply to other dental or oral prosthetics.
Laminated versions of dental prosthetics have been used, and laminates may provide superior impact resistance. Exemplary embodiments of the instant invention provide for oral prosthetics constructed from cross-grained laminations of extruded plastics.
Mouth guards may be fabricated from ethyl vinyl acetate (EVA). Some mouth guards consist of a single sheet or multiple laminated sheets which are formed over a model of a patient's dentition, and some are pre-formed. Urethane mouth guards may be processed in a similar manner. The urethane polymer may be extruded into a sheet, injection molded into a sheet, or pre-formed.
Mouth guards may be 0.150 inches (approx. 3.8 mm) or 0.160 inches (approx. 4 mm) in thickness. Mouth guards may be single-ply extrusions, or may be injection molded. Mouth guards may also be laminates of two or more layers. The layers may be composed of different materials when the varying properties are considered advantageous for a particular use or a particular patient.
A multi-laminated mouthguard may be fabricated using heat and vacuum pressure. EVA dental plastic may be formed with positive pressure at about 90 psi, or at 12 psi for vacuum pressure. A multi-laminated mouthguard with an interoclussal (i.e., the vertical distance between the occluding surfaces of the upper and lower teeth when the mandible is in the resting position) thickness of between 3 to 5 millimeters may reduce a rate of concussion received by a blow to the mandible. Vacuum-forming a single sheet of EVA may cause the material to lose approximately 50 percent of its original thickness as it softens and droops.
An EVA-based co-polymer may provide high shock-absorption and be laminated to itself using vacuum pressure. Laminating may be performed in different forming cycles. An exemplary method according to the present innovation may allow fabrication of a mouthguard with increased thickness using a vacuum-form machine, which typically costs less than pressure laminating machines. To determine the final thickness of a multi-layer mouthguard, a rule of thumb may be to calculate the thinning of the material in processing at 50 percent. For instance, to fabricate a mouthguard with a final thickness of 3 to 3.5 millimeters, a total of two layers that have a combined thickness equaling 6 or more millimeters may be used. In particular, a first layer of 3-millimeter sheet followed by another 3-millimeter sheet may be used, or a first layer of 4 millimeter followed by a 2-millimeter sheet may be used.
In an exemplary embodiment of the present invention, the plastic sheets are oriented prior to lamination so that the grains of the several sheets are at right angles, or alternatively, at another specified angle other than 0 degrees. The cross-grain structure may increase impact strength and may allow for thinner appliances which may be more comfortable for the user. An exemplary embodiment of the present invention provides for laminating two or more layers, the grain of which are at a 90 degree angle to a layer below and/or above. This structure provides the unexpected benefit of imparting additional strength to the finished product. This is called an orthotropic orientation.
While there may be no general grain in injection molded sheets, there typically is a grain in an extruded product. The grain may be difficult to see so it may be beneficial that a dentist or dental technician using this invention either have an indicator on each sheet or purchase a prelaminated product in which the manufacturer has exercised control to make sure the grain angle and orientation are correct. In addition, exemplary embodiments provide that single sheets, which may be intended to be laminated in the dental office or dental lab, may include a directional indicator of the grain which will allow the lab technician to identify the sheet orientation.
An unexpected benefit is that the orthotropic material resists the tendency to become thin when vacuum-formed over a stone model. Normal mouth guard materials and laminates tend to thin out in areas where the material is stretched. In particular the grinding surfaces of teeth, areas of high vertical gradient, the occlusal surfaces and the palatal areas may be thinner than the balance of the mouth guard. Experiments have shown minimal thinning of orthotropic material. For example, when using a material in an exemplary embodiment having a thickness of 0.160 inches prior to forming, most of the mouth guard retains a thickness of at least 0.145 inches after forming. The orthotropic material may stabilize the internal stresses that normally cause the material to thin during the heating and/or vacuum or pressure forming process.
An orthotropic mouth guard made according to the present application may provide the additional unexpected benefit of producing little or no smoke in the process of vacuum or pressure forming. This contrasts with medium to large amounts of smoke generated when forming conventional mouth guard materials.
In exemplary embodiments, laminate sheets may be formed to make a “jigsaw” pattern such that the sheets may have differing grain angles at various points in order to achieve beneficial results, and/or different strengths or deformability in specific directions, and/or in response to specific stressors.
An exemplary method for manufacturing the orthotropic materials may include the following steps. First, materials are “laid” up in a cross-grained orientation and “release paper” is placed between layers which are not to be bonded. The release paper may contain a slightly raised design to give a particular look (e.g., sandstone) and/or a grain direction indicator. The sheets are stacked and surrounded by a vacuum bag and placed in an industrial autoclave, for example the Econoclave (made by ASC Process Systems of Sylmar, Calif.). A layer of glass is placed on top of the stacks to evenly distribute pressure.
Second, the bag is evacuated and heat is applied. The temperature may preferably be 50-80%, more preferably 50-70% and most preferably 50-65%, of the lowest melting point of any of the components.
Third, the pressure in the chamber is increased to about 100 Lbs/sq. in. for a defined period of time depending on the materials used. In some cases, this time period may be approximately 1 hour.
Fourth, the temperature and pressure are reduced and the autoclave is brought down to standard temperature and pressure (STP) and opened. The bag is opened and the orthotropic laminates are removed.
In alternative exemplary embodiments, a third (or more) sheet of EVA may be fused or laminated in a separate processing cycle over the first layer. Alternatively, the third or more layer may be fused simultaneously with the first and second layers.
Alternatively, rather than being orthogonal, first grain 110 and second grain 210 may be oriented at another angle between zero and 180 degrees.
While only a limited number of preferred embodiments of the present invention have been disclosed for purposes of illustration, it is obvious that many modifications and variations could be made thereto. It is intended to cover all of those modifications and variations which fall within the scope of the present invention, as defined by the following claims.
This application claims the benefit of U.S. Provisional Application No. 61/342,113 filed Apr. 12, 2010, and this application also claims the benefit of U.S. Provisional Application No. 61/399,523 filed Jul. 14, 2010, both of which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 61342113 | Apr 2010 | US | |
| 61399523 | Jul 2010 | US |