Crosslinked binder polymers for electrostatographic toners and toners formed therefrom

Abstract

A binder polymer composition for electrostatographic toners comprises a carboxysubstituted precursor polymer crosslinked by reaction with an N,N,N′N′-tetrakis(2-hydroxyalkyl) bisamide compound of the structure 1

Description

FIELD OF THE INVENTION

[0002] The present invention relates to electrostatographic toners and, in particular, to crosslinked binder polymers useful for preparing toner particles.

BACKGROUND OF THE INVENTION

[0003] Crosslinked polymeric materials have long been known as useful binders for electrostatographic toners. Various types of crosslinked polymers, including vinyl, styryl, and acrylic resins, as well as condensation polymers such as polyesters are disclosed in U.S. Pat. No. 3,938,992 and in Reissue Patent No. 31,072.

[0004] Other references describing toners formed from crosslinked polyesters include the following, the disclosures of which are incorporated herein by reference:

[0005] U.S. Pat. No. 5,276,127, which describes a crosslinked polyester derived from at least one member selected from the group consisting of tribasic and tetrabasic acid components and trihydric and tetrahydric alcohol components and an aromatic or alicyclic diol component in which at least one of the hydroxyl groups is a secondary group.

[0006] U.S. Pat. No. 5,486,444, which describes a process for preparing a crosslinked polyester by first forming a polyhydroxy functional polyester resin precursor, which is then reacted with a dianhydride or diepoxy functional crosslinking component.

[0007] U.S. Pat. No. 5,789,527, which describes a polyester resin formed by linking crosslinked low-molecular weight polyesters through a dicarboxylic linking agent.

[0008] In addition to their usefulness for the production of toners, crosslinked polyesters have found extensive use in various other applications, for example, the production of thermosetting powder coating compositions. Such compositions are disclosed in, for example, U.S. Pat. No. 5,373,084, which describes the preparation of semicrystalline polyester plasticizers from crosslinkable resins and a variety of crosslinking agents. Among the types of crosslinking agents disclosed in this reference are hydroxyalkylamides, epoxy materials, glycouril compounds, and unblocked or blocked isocyanates.

[0009] Commercial polyester crosslinking chemistries frequently involve materials that are toxic or malodorous and, in addition, require in their preparation catalysts that may adversely affect the triboelectric performance of the toner particles. Furthermore, catalyzed processes often require an intimate knowledge of the materials and processes used by suppliers in the preparation of toner ingredient precursors. It would be highly desirable to have the ability to prepare crosslinked polyester toner binders using non-toxic, odorless, low cost ingredients under relatively mild conditions that do not require catalysts.

SUMMARY OF THE INVENTION

[0010] The present invention is directed to a binder polymer composition for electrostatographic toners that comprises a carboxysubstituted precursor polymer crosslinked by reaction with an N,N,N′N′-tetrakis(2-hydroxyalkyl) bisamide compound of the structure 2

[0011] wherein R1 is a substituted or unsubstituted alkylene group containing 1 to about 10 carbon atoms and R2 is H or an alkyl group containing 1 to about 6 carbon atoms.

DETAILED DESCRIPTION OF THE INVENTION

[0012] Unless otherwise specifically stated, the terms “substituted” or “substituent” in this specification are used to refer to any group or atom other than hydrogen. Also, the term “group”, when used to refer to a substituent that includes a substitutable hydrogen, encompasses not only the substituent's unsubstituted form but also its form substituted with any substituent or group that does not interfere with formation of the precursor polymer or its subsequent reaction with the crosslinking agent.

[0013] The present invention relates to binder polymers for toners that are produced by the reaction of a crosslinking agent comprising an N,N,N′N′-tetrakis(2-hydroxyalkyl) bisamide compound with a carboxysubstituted precursor polymer, without the need for triboelectrically altering catalysts. Most preferably, the carboxysubstituted precursor polymers are polyesters that are the reaction products of fumaric acid with alkoxylated Bisphenol A, which are crosslinked with a bisamide compound that preferably is N,N,N′,N′-tetrakis(2-hydroxyethyl)succinamide, N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide, N,N,N′,N′-tetrakis(2-hydroxyethyl)sebacamide, or N,N,N′,N′-tetrakis(2-hydroxypropyl)adipamide. The bisamide crosslinking agent is employed in an amount preferably about 0.1 to about 5, more preferably, about 0.5 to about 3 weight percent of the amount of carboxysubstituted precursor polymer.

[0014] Two of the aforementioned N,N,N′N′-tetrakis(2-hydroxyalkyl)alkylenebisamides preferred in the practice of the present invention are available from Ems-Chemie AG, Zurich, Switzerland and are designated by the product names PRIMID® XL-552 and PRIMID® QM-1260. The chemical structures of these materials are as shown below: 3

[0015] Preferred carboxysubstituted precursor polymers for the practice of the present invention are polyesters bearing pendant and/or terminal carboxyl groups, as represented by the following general formula: 4

[0016] wherein R3 is a substituted or unsubstituted alkylene group containing 1 to about 6 carbon atoms or a substituted or unsubstituted arylene group containing 6 to about 16 carbon atoms; R4 is a substituted or an unsubstituted alkylene group containing 1 to about 6 carbon atoms, or a substituted or unsubstituted arylene, alkylenediarylene, or arylenedialkylene group containing 6 to about 20 carbon atoms.

[0017] Representative R3 groups include, for example, 1,2-ethanediyl, 1,2-ethenediyl, 1,4-butanediyl, hexamethylene, 1,4-phenylene, 1,3-phenylene, 4-carboxy-1,3-phenylene, 1,1,3-trimethyl-3-(4-phenylene)-5-yl, 2,6-naphthalenediyl, 5-hydroxy-1,3-phenylene, and 2-chloro-1,4-phenylene groups. Representative R4 groups include, for example, 1,2-ethanediyl, 2,2-dimethyl-1,3-propanediyl, 2-carboxy-2-methyl-1,3-propanediyl, 1,4-butanediyl, 1,4-cyclohexanedimethylene, hexamethylene, 2,2′-oxydiethylene, 4,4′-isopropylidenediphenylene, and 1,4-phenylene groups.

[0018] The carboxysubstituted precursor polyesters may contain more than one R3 and R4 group and may also include the residue of a polyol or polyacid with a functionality greater than 2, thus providing a branched structure.

[0019] A particularly preferred class of carboxysubstituted polyesters are reaction products of fumaric acid, maleic acid, or malcic anhydride with a glycol. Preferably, the glycol is an alkoxylated derivative of Bisphenol A, represented by the following general structure: 5

[0020] wherein R is H or methyl, and x+y has a value 2.0 to 20.0. The glycol may be a mixture containing both primary and secondary hydroxy substituents. Most preferably, the carboxysubstituted polyester is derived from fumaric acid and propoxylated Bisphenol A, where R is methyl and x+y=2.2. This most preferred polyester is a branched polymer resulting from hydro-alkoxy additions across the fumarate double bonds.

[0021] Another preferred group of carboxysubstituted precursor polymers are vinyl polymers, represented by the following structural formula: 6

[0022] wherein X is H or methyl, Y is H, CO2H, CO2R5, or CONHR6, R5 and R6 each independently represents alkyl groups containing 1 to about 3 carbon atoms, Z represents the residue(s) of any copolymerizable monomer(s), m and n are weight percentages whose total is 100, and m has a value from about 0.01 to 100.0. Monomers corresponding to Z can be, for example, olefinic, styrenic, acrylic, and methacrylic monomers, and mixtures thereof.

[0023] A representative carboxysubstituted vinyl polymer is shown below: 7

[0024] Also in accordance with the present invention, a mixture of carboxysubstituted polyesters or a mixture of carboxysubstituted vinyl polymers, or a mixture of one or more carboxysubstituted polyesters with one or more carboxysubstituted vinyl polymers may be employed.

[0025] Various addenda may be added to the toner formulation. These addenda include but are not restricted to materials such as colorants (either pigments or dyes), charge control agents, waxes, and low surface energy additives.

[0026] Measurement of the rheological properties of a polymer is useful for determining its suitability as a toner binder polymer, in particular, for forming a toner image that is fixed to a paper receiver using a heated roll. Useful polymers have a viscosity, as measured on a dynamic viscometer at 120° C. and 1 radian/second, of preferably about 20 kpoise to about 200 kpoise, more preferably about 40 kpoise to about 140 kpoise.

[0027] Storage modulus is a measure of the elastic nature of a polymer and provides some indication of the operating range of a heated roll without resulting in offset. Polymers useful for toners should have a storage modulus of preferably at least about 20 kdyne/cm2, more preferably, at least about 35 kdyne/cm2.

[0028] Tan delta, which is the ratio of the loss modulus to the storage modulus, gives an indication of the viscous vs the elastic characteristics of a polymer. For use in toners, polymers preferably should have a tan delta value of less than about 2, more preferably, of less than about 1.

[0029] The following examples are illustrative of the present invention:

EXAMPLE 1

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide at 0.5% Crosslinking Agent Level

[0030] 47.76 g of a propoxylated bisphenol-A fumarate polyester, available as 382ES-HMW from Reichhold Chemicals, Inc., was dry-blended with 0.24 g of N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide (PRIMID® XL-552). The mixture was placed in a laboratory mixer, available from C. W. Brabender, Inc., equipped with sigma blades that had been preheated to 235° C. The mixing speed was set at 150 rpm, and total mixing time was 4 minutes. The rheology of the polyester before and after crosslinking was determined on a dynamic viscometer, available from Rheometrics, Inc., at 120° C. and 1 radian/second:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	59	38	1.22
0.5% PRIMID ® XL-552

EXAMPLE 2

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide at 1% Crosslinking Agent Level

[0031] The same procedure as in Example 1 was used, except that 47.52 g of the propoxylated bisphenol-A fumarate polyester was mixed with 0.48 g of PRIMID® XL-552. The rheology of the polyester before and after crosslinking was:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	115	92	0.74
1% PRIMID ® XL-552

EXAMPLE 3

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide at 3% Crosslinking Agent Level

[0032] The same procedure as in Example 1 was used, except that 46.56 g of the propoxylated bisphenol-A fumarate polyester was mixed with 1.44 g of PRIMID® XL-552. The rheology of the polyester before and after crosslinking was:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	129	127	0.21
3% PRIMID ® XL-552

EXAMPLE 4

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxypropyl)adipamide at 0.5% Crosslinking Agent Level

[0033] The same procedure as Example 1 was used except 47.76 g of the propoxylated bisphenol-A fumarate polyester was mixed with 0.24 g PRIMID® QM-1260. The rheology of the polyester before and after crosslinking was:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	54	31	1.38
0.5% PRIMID ® QM-1260

EXAMPLE 5

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxypropyl)adipamide at 1% Crosslinking Agent Level

[0034] The same procedure as in Example 4 was used, except that 47.52 g of the propoxylated bisphenol-A fumarate polyester was mixed with 0.48 g of PRIMID® QM-1260. The rheology of the polyester after crosslinking was:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	93	74	0.76
1% PRIMID ® QM-1260

EXAMPLE 6

Crosslinking a Carboxysubstituted 2,2-dimethyl-1, 3-propylene Terephthalate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide at 1% Crosslinker Level

[0035] The same procedure as in Example 1 was used, except that 47.52 g of a carboxysubstituted 2,2-dimethyl-1,3-propylene terephthalate polyester, prepared by Ruco Polymers Inc. and designated PE 2073, was mixed with 0.48 g of PRIMID® XL-552. The rheology before and after crosslinking was:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	47	11	4.00
Polyester after crosslinking with	170	137	0.72
1% PRIMID ® XL-552

EXAMPLE 7

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide in an Extruder at 0.5% Crosslinker Level

[0036] 9950 g of propoxylated bisphenol-A fumarate polyester (382ES-HMW) was dry-blended with 50 g PRIMID® XL-552 and processed with a twin-screw co-rotating extruder Model ZSK-30, available from Werner & Pfleiderer Corp. Feed rate was 10 kg/hr, screw speed was 300 rpm, and zone temperature setpoints were: zone 1-93° C., zones 2-5-216° C. The polyester before and after crosslinking was measured in the same manner as in Example 1 to obtain the following results:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	46	35	0.87
0.5% PRIMID ® XL-552

EXAMPLE 8

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide in an Extruder at 1% Crosslinker Level

[0037] 9900 g of propoxylated bisphenol-A fumarate polyester (382ES-HMW) was dry-blended with 100 g PRIMID® XL-552 and processed with the Model ZSK-30 twin-screw co-rotating extruder. Feed rate was 10 kg/hr, screw speed was 300 rpm, and zone temperature setpoints were: zone 1-93° C., zones 2-5-216° C. The polyester before and after crosslinking was measured in the same manner as in Example 1, giving the following results:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	81	71	0.55
1% PRIMID ® XL-552

EXAMPLE 9

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxypropyl)adipamide in an Extruder at 0.5% Crosslinker Level

[0038] 9950 g of propoxylated bisphenol-A fumarate polyester (382ES-HMW) was dry-blended with 50 g PRIMID® QM-1260 and processed with the Model ZSK-30 twin-screw co-rotating extruder. Feed rate was 10 kg/hr, screw speed was 300 rpm, and zone temperature setpoints were: zone 1-93° C., zones 2-5-216° C. The polyester before and after crosslinking was measured in the same manner as Example 1 to give the following results:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	46	30	1.18
0.5% PRIMID ® QM-1260

EXAMPLE 10

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxypropyl)adipamide in an Extruder at 1% Crosslinker Level

[0039] 9900 g of propoxylated bisphenol-A fumarate polyester (382ES-HMW) was dry-blended with 100 g PRIMID® QM-1260 and processed with the Model ZSK-30 twin-screw co-rotating extruder. Feed rate was 10 kg/hr, screw speed was 300 rpm, and zone temperature setpoints were: zone 1-93° C., zones 2-5-216° C. The polyester before and after crosslinking was measured in the same manner as in Example 1:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.7	5.00
Polyester after crosslinking with	92	78	0.62
1% PRIMID ® QM-1260

EXAMPLE 11

Preparation of N,N,N′,N′-tetrakis(2-hydroxyethyl)succinamide

[0040] 8

[0041] A mixture of 43.55 g (0.25 mol) of diethyl succinate and 157.71 g (1.50 mol) of diethanolamine was heated under nitrogen in a 140° C. bath for 1.75 hr while collecting the ethanol distillate. The excess diethanolamine was then distilled off at reduced pressure (1.2 mm) while heating in a 190° C. bath. The oily residue was cooled, stirred with acetone, and allowed to stand. The oil crystallized to a white solid, which was collected and dried. The yield of product was 48.27 g (66.0% of theory); mp=89-91° C.

EXAMPLE 12

Preparation of N,N,N−,N′-tetrakis(2-hydroxyethyl)sebacamide

[0042] 9

[0043] A mixture of 57.58 g (0.25 mol) dimethyl sebacate and 157.71 g (1.50 mol) of diethanolamine was heated in a 140° C. bath under nitrogen for 2.5 hrs while collecting the methanol condensate. The reaction mixture was subsequently heated in a 200° C. at reduced pressure (1.5 mm) to distill off excess diethanolamine. The highly viscous oily residue was dissolved in an equal volume of acetone and stirred overnight. The resulting crystalline solid was collected, washed with acetone, and dried. The yield of product was 35.0 g (9.3% of theory); mp=87-98° C.

EXAMPLE 13

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)succinamide at 1% Crosslinking Agent Level

[0044] The same procedure as in Example 1 was used, except that 47.52 g of a propoxylated bisphenol-A fumarate polyester was mixed with 0.48 g of N,N,N′,N′-tetrakis(2-hydroxyethyl)succinamide, prepared as described in Example 11. The rheology of the polyester before and after crosslinking was:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.1	6.24
Polyester after crosslinking with	133	97	0.93
1% N,N,N′,N′-tetrakis-
(2-hydroxyethyl)succinamide

EXAMPLE 14

Crosslinking Propoxylated Bisphenol-A Fumarate Polyester with N,N,N′,N′-tetrakis(2-hydroxyethyl)sebacamide at 1% Crosslinking Agent Level

[0045] The same procedure as in Example 1 was used, except that 47.52 g of a propoxylated bisphenol-A fumarate polyester was mixed with 0.48 g of N,N,N′,N′-tetrakis(2-hydroxyethyl)sebacamide, prepared as described in Example 12. The rheology of the polyester before and after crosslinking was:

	Viscosity	Storage Modulus	Tan
Identification	(kpoise)	(kdyne/cm2)	Delta
Polyester before crosslinking	19	3.1	6.24
Polyester after crosslinking with	126	89	1.00
1% N,N,N′,N′-tetrakis
(2-hydroxyethyl)sebacamide

EXAMPLE 15

Preparation of a Toner

[0046] The crosslinked polymer of Example 8 was used to prepare a toner by melt-blending the following ingredients on a two-roll mill for 15 minutes at 120° C.: 30 grams of the crosslinked polyester of Example 8, 2.4 grams of REGAL® 330 carbon black (from Cabot Corp.), 0.6 gram of VISCOL® 550P polypropylene wax (from Sanyo Corp.), and 0.6 gram of BONTRON® E-84 charge control agent (from Orient Corp.).

[0047] The mixture was pulverized to a particle size of 7-12 microns using a fluid energy mill.

[0048] A developer was prepared by shaking together for 10 minutes 1 gram of toner with 9 grams of a silicone-resin coated carrier. The triboelectric charge for this developer was −22 μc/g.

EXAMPLE 16

Roller-Fusing Evaluation

[0049] The fixing properties of the toner prepared in Example 15 were determined by passing toned sheets through a roller-fuser obtained from a Kodak EK-95 copier. The toner exhibited excellent offset latitude and fusing quality.

[0050] The use of N,N,N′N′-tetra(2-hydroxyalkyl)alkylenebisamides as crosslinking agents in accordance with the present invention offers several significant advantages, including the following:

[0051] the crosslinking agents and crosslinked polyesters derived therefrom emit no objectionable odors either neat or in toners and require no hazard warning labels

[0052] no special storage measures or handling precautions such as special breathing equipment, eye protection or hand protection are required

[0053] the crosslinking reaction is not influenced by catalysts; therefore monitoring of catalyst in the precursor polyester or the introduction of potentially triboelectrically altering catalysts is not required

[0054] the effective equivalent molecular weight is low, which translates to relatively low crosslinking agent levels on a weight basis

[0055] the PRIMID® crosslinking agents are low cost, commercially available materials that are listed on the TSCA inventory

[0056] the PRIMID® crosslinking agents are low melting (˜120° C.) materials, which contributes to the formation of a more homogeneous crosslinked toner binder

[0057] relatively low temperatures are required to effect the crosslinking reaction

[0058] the reactants and crosslinked products are colorless, providing useful als for the preparation of variously colored toners

[0059] The invention has been described in detail with particular reference to certain red embodiments thereof, but it is to be understood that variations and ications can be effected within the spirit and scope of the invention, which is ed by the following claims.

Claims

1. A binder polymer composition for electrostatographic toners comprising: a carboxysubstituted precursor polymer crosslinked by reaction with an N,N,N′N′-tetrakis(2-hydroxyalkyl) bisamide compound having the structure 10wherein R1 is a substituted or unsubstituted alkylene group containing 1 to about 10 carbon atoms and R2 is H or an alkyl group containing 1 to about 6 carbon atoms.

2. The binder polymer composition of claim 1 wherein said N,N,N′N′-tetrakis(2-hydroxyalkyl) bisamide compound is selected from the group consisting of N,N,N′,N′-tetrakis(2-hydroxyethyl)succinamide, N,N,N′,N′-tetrakis(2-hydroxyethyl)adipamide, N,N,N′,N′-tetrakis(2-hydroxyethyl)sebacamide, and N,N,N′,N′-tetrakis(2-hydroxypropyl)adipamide.

3. The binder polymer composition of claim 1 wherein said carboxysubstituted precursor polymer comprises a polyester having the structure

4. The binder polymer composition of claim 3 wherein R3 is selected from the group consisting of 1,2-ethanediyl, 1,2-ethenediyl, 1,4-butanediyl, hexamethylene, 1,4-phenylene, 1,3-phenylene, 4-carboxy-1,3-phenylene, 1,1,3-trimethyl-3-(4-phenylene)-5-yl, 2,6-naphthalenediyl, 5-hydroxy-1,3-phenylene, 2-chloro-1,4-phenylene, and mixtures thereof.

5. The binder polymer composition of claim 3 wherein R4 is selected from the group consisting of 1,2-ethanediyl, 2,2-dimethyl-1,3-propanediyl, 2-carboxy-2-methyl-1,4-butanediyl, 1,4-cyclohexanedimethylene, hexamethylene, 2,2′-oxydiethylene, 4,4′-isopropylidenediphenylene, 1,4-phenylene, and mixtures thereof.

6. The binder polymer composition of claim 3 wherein R4 in said polyester is an alkoxylated Bisphenol A residue, said polyester being formed from a glycol having the structure

7. The binder polymer composition of claim 6 wherein R is CH3, and x+y=2.2.

8. The binder polymer composition of claim 1 wherein said carboxysubstituted precursor polymer comprises a vinyl polymer having the structure

9. The binder polymer composition of claim 8 wherein said copolymerizable monomers are selected from the group of olefinic, styrenic, acrylic, and methacrylic monomers, and mixtures thereof.

10. The binder polymer composition of claim 8 wherein said vinyl polymer has the formula

11. The binder polymer composition of claim 1 wherein said carboxysubstituted precursor polymer is selected from a mixture of carboxysubstituted polyesters, a mixture of carboxysubstituted vinyl polymers, or a mixture of one or more carboxysubstituted polyesters with one or more carboxysubstituted vinyl polymers.

12. The binder polymer composition of claim 1 wherein said carboxysubstituted precursor polymer comprises a 2,2-dimethyl-1,3-propylene terephthalate polyester.

13. The binder polymer composition of claim 1 comprising said bisamide compound in an amount about 0.1 to about 5 weight percent of the amount of said carboxysubstituted precursor polymer.

14. The binder polymer composition of claim 13 comprising said bisamide compound in an amount about 0.5 to about 3 weight percent of the amount of said carboxysubstituted precursor polymer.

15. The binder polymer composition of claim 1 having a viscosity, as measured on a dynamic viscometer at 120° C. and 1 radian/second, of about 20 kpoise to about 200 kpoise.

16. The binder polymer composition of claim 15 having a viscosity, as measured on a dynamic viscometer at 120° C. and 1 radian/second, of about 40 kpoise to about 140 kpoise.

17. The binder polymer composition of claim 1 having a storage modulus of at least about 20 kdyne/cm2.

18. The binder polymer composition of claim 17 having a storage us of at least about 35 kdyne/cm2.

19. The binder polymer composition of claim 1 having a tan delta of less than about 2.

20. The binder polymer composition of claim 19 having a tan value of less than about 1.

21. A toner composition comprising the binder polymer sition of claim 1.

22. A toner composition of claim 21 further comprising addenda ted from the group consisting of pigments, dyes, charge control agents, waxes, urface energy additives, and combinations thereof.