Perforation ball sealers are used in the oil and gas recovery industries to temporarily plug perforations made in an oil or gas well to divert the flow of treatment fluid from zones in the geological formation exhibiting higher permeabilities to zones exhibiting lower permeabilities.
Early ball sealers were made from permanent materials such as nylon, phenolics and rubber coated metal, requiring mechanical processing for ball sealer removal. Later ball sealers were made from polymers and copolymers of lactic acid esters which are slowly soluble in acidified water, thereby making mechanical removal unnecessary. See, for example, U.S. Pat. No. 4,716,964 to Erbstrosser et al., the disclosure of which is incorporated herein by reference in its entirety. Numerous other slowly water-soluble materials have also been proposed for making ball sealers, examples of which include polyethylene oxides (PEO), naturally occurring polymers such as collagen and chitosan, polyvinyl alcohol polymers (PVOH), ethylene vinyl alcohol copolymers (EVOH), and the like.
To prevent ball sealers from sinking to the bottom of a well before engaging the perforations to be sealed, they preferably should exhibit a density which is similar to, or even less than, the density of the treatment fluid in which they are supplied. See, for example, Gabriel et al., “The Design of Buoyant Ball Sealer Treatments”, SPE 13085) which reports that all ball sealers having a density less than that of their treating fluids can achieve 100% seating efficiency in both fracturing and matrix treatments because they avoid sinking to the bottom of the drill string.
Unfortunately, most of the slowly water-soluble polymers from which ball sealers can be made exhibit densities which are greater than the densities of the aqueous treatment fluids in which these ball sealers will be used.
To address this issue, U.S. 2017/0210976 to FracSolutions Technologies suggests that, where ball sealers with densities as low as 0.9-1.0 g/cc are desired, the ball sealers can be foamed by using chemical or physical blowing agents. However, the crush strengths of most polymer foams are less than the compressive stress normally encountered when most ball sealers are used, especially in hydraulic fracturing operations. As a result, ball sealers made from simple polymer foams cannot be used in these operations, as a practical matter.
In accordance with this invention, perforation ball sealers exhibiting desirably low densities as well as desirably high crush strengths are provided by forming the ball sealer form a polymer foam core and a shell surrounding the core formed from a solid or essentially solid polymer.
Thus, this invention provides a perforation ball sealer for use in temporarily plugging perforations in an oil or gas well, the perforation ball sealer comprising a polymer foam core made from a first slowly polymer and a shell surrounding the core formed from a solid or essentially solid second polymer, wherein both the first and second polymers are slowly water-soluble, and further wherein the ball sealer exhibits a density of 1.1 g/cc or less and a crush strength of 1,000 psi (˜69 dyne/cm) or more when dry.
In addition, this invention also provides a method for temporarily plugging perforations in an oil or gas well comprising introducing into the well an aqueous treatment fluid containing a mass of the above ball sealers.
This invention may be more readily understood by reference to the following drawings wherein:
Physical Form and Properties
The inventive ball sealer has a conventional physical form and size. That is to say, it is a sphere having a diameter normally used in the oil and gas industry, which typically range from as much as 5 inches to as little as ½ inch. Normally, the inventive ball sealers will have diameters of ⅝ inch to 1½ inch, more typically ⅞ inch to 1¼ inch. Specific examples of typical diameters include ⅝ inch, ¾ inch, ⅞ inch, 1 inch, 1⅛ inch, 1¼ inch, and 1½ inch.
As indicated above, rather than having a solid, homogenous structure, the inventive ball sealer takes the form of a polymer foam core and a shell surrounding the core formed from a solid or essentially solid polymer. As a result, the density of the inventive ball sealer as a whole can be reduced to a desirably low level by virtue of its foam core, while the crush strength of the inventive ball sealer as a whole can be maintained at a desirably high level by virtue of its outer shell.
In this regard, the inventive perforation ball sealers are desirably formulated to have an overall density of 1.1 g/cc or less, more desirably 1.05 g/cc or less, 1.0 g/cc or less, 0.95 g/cc or less, 0.90 g/cc or less, 0.8 g/cc or less, 0.7 g/cc or less, or even 0.6 g/cc or less, in order to prevent them from sinking in the treatment fluid in which they are used. In this context, “overall density” means the density of the ball sealer as a whole.
In addition, the inventive perforation ball sealers are also desirably formulated to have a crush strength of at least 1,000 psi (˜69 dyne/cm) when dry in order that they can withstand the compressive stresses that may be encountered downhole. More desirably, they are formulated to have a crush strength of at least 1,100 psi (˜76 dyne/cm), at least 1,250 psi (˜86 dyne/cm), at least 1,500 psi (˜103 dyne/cm), at least 1,750 psi (˜121 dyne/cm), or even at least 2,000 psi (˜138 dyne/cm), when dry. This substantial crush strength is due to the fact that foaming of the inventive ball sealer resides primarily in its central core which, in turn, enables the shell surrounding this core to exhibit a fairly uniform and substantial thickness.
Slowly-Water Soluble Polymers
The inventive perforation balls are made from slowly-water soluble polymers. In the context of this disclosure, this means that the particular polymer or polymers used to make a ball sealer intended for use in a particular application are selected so that they dissolve, depolymerize or otherwise decompose at a useful dissolution rate under the conditions of temperature and pH that will be encountered in that application.
In this regard, oil and gas bearing subterranean formations where ball sealers are used can exhibit widely differing downhole conditions of temperatures and pH. Some exhibit low downhole temperatures, e.g., ˜75° F. to 200° F. (˜24° C. to ˜93° C.). Others exhibit medium downhole temperatures, e.g., ˜150° F. to 250° F. (˜66° C. to ˜121° C.). And still others exhibit high downhole temperatures, e.g., ˜200° F. to 350° F. (˜93° C. to ˜177° C.) and higher.
In addition, depending on the naturally occurring ground water found there as well as the liquids pumped downhole either before or together with the ball sealers, each of these formations can also exhibit widely differing pH conditions. Thus, some formations exhibit alkaline conditions (e.g., pH of 9-11), while others exhibit neutral conditions (e.g., pH of ˜7). Still others exhibit highly acidic conditions (e.g., pH of ˜0 to 1 or even −1 to 0) from being treated with strong acids, e.g., 15% HCl, during acidizing or matrix acidizing.
Potentially, therefore, nine different sets of downhole conditions can be found where ball sealers are present in oil and gas bearing subterranean formations—low, medium or high temperature at alkaline, neutral or the highly acidic pH associated with acidizing treatments.
As appreciated in the ball sealer art, the particular ball sealer used in a particular well is selected so that, under the particular conditions of temperature and pH that will be encountered, it dissolves, depolymerizes or otherwise decomposes in the aqueous fluids it encounters at a useful dissolution rate, i.e., at a rate which is slow enough to allow the treatment process to be completed but fast enough so that it dissolves, depolymerizes or otherwise decomposes promptly after the treatment process is done. Normally, this dissolution rate will be such that the ball sealer effectively loses its ability to seal the perforation in which it is received within a predetermined period of time, e.g., 2 to 24 hours, after being received in its perforation.
In accordance with this invention, therefore, the particular polymer or polymers that are selected to make a ball sealer for use in a particular application are selected so that the ball sealer obtained dissolves, depolymerizes or otherwise decomposes at a useful dissolution rate under the conditions of temperature and pH that are anticipated to be encountered in that application. Preferably, the polymer or polymers are selected so that 35% of the mass of a ball sealer made from this polymer or polymers is lost within 2 to 24 hours, more typically 3-13 hours, of continuous exposure to water maintained at this temperature and pH.
Examples of slowly-water soluble polymers that are useful for this purpose are described in the above-mentioned U.S. 2017/0210976 and include polyvinyl alcohol (PVOH), polyglycolic acid (PGA), polytrimethylene terephthalate (PTT), polylactic acid (PLA), polybutylene succinate (PBS), polybutylene adipate terephthalate (PEAT), polybutylene adipate succinate (PBAS), polyvinyl acetate (PVA), polyethylene oxides (PEO), ethylene vinyl alcohol copolymers (EVOH), and naturally occurring polymers such as collagen and chitosan. Blends of these slowly water-soluble polymers can also be used.
Preferred slowly water-soluble polymers are those described in commonly-assigned application Ser. No. 62/396,960, filed Sep. 20, 2016, the disclosure of which is also incorporated herein by reference in its entirety. As described there, certain specific slowly water-soluble polymers each exhibit useful dissolutions rates at widely different conditions of temperature and pH such that certain groups of these polymers containing only a very few members per group, e.g., groups containing only two or three polymers per group, are needed to provide a system of perforation ball sealers which can be used at all nine of the different downhole conditions of temperature and pH—i.e., low, medium or high temperature at alkaline, neutral or the highly acidic pH associated with acidizing treatments.
Examples of these slowly-water soluble polymers include
Examples of specific groups of these slowly-water soluble polymers which, in combination, are useful for multiple different downhole conditions include
Group 1:
Either or both, including blends, of
Either or both, including blends, of
Blends of
Blends of
Additional slowly water-soluble polymers which are useful in this invention, including blends of these polymers, are described below:
MR (“Medium Temperature Range”) Resins
As indicated above, the inventive perforation ball sealer is composed of two different sections, a polymer core and a polymer shell surrounding the core. In accordance with this invention, these different sections can be made from different slowly water-soluble polymers, if desired. However, normally, both sections will be made from the same slowly water-soluble polymer.
Method of Manufacture
The inventive perforation ball sealers can be made by any method which will produce spherical or essentially spherical polymer products have the core and shell structure described above.
Most commonly, they will be made by an injection molding process in which a chemical foaming (blowing) agent and a single polymer or polymer blend which forms both the core and shell of the ball sealer are fed to a plasticizing extruder, i.e., an extruder which heats the polymer to its softening temperature, after which the softened polymer so-formed is injection molded. If a chemical foaming agent is used, as further discussed below, the temperature of the extruder can also be controlled so that decomposition of this foaming agent in the feeding section of the extruder is avoided, while all or essentially all of this chemical foaming agent decomposes to generate foaming gas in the extruder's compression section. Also if desired, the temperature at the nozzle of the extruder can be reduced by a suitable amount to increase back pressure and improve the melt strength of the extrudate. Thereafter, the molten or semi-molten polymer extrudate so formed is fed to a conventional injection molding machine where it foams and is formed into a part with the desired shape.
Processes for injection molding polymer foams are well-known commercially and described in many different publications including Bergen International, Injection Molding Processing Guide, www.bergenintrenational.com/pdfs/Injection_Molding_Processing_Guide, Sep. 3, 2009; Lemaster, Tips and Techniques: How to Mold & Extrude Using Chemical Blowing Agents, Plastics Technology, February 2011, http//www.ptonline.com/articles/hot-to-mold-extrude-using-chemical-blowing-agents.
As well understood in the art, two different types of foaming agents can be used for making injected molded foams, physical foaming agents and chemical foaming agents. Physical foaming agents are gasses such as nitrogen and carbon dioxide that re injected under high pressure directly into the polymer melt. Meanwhile, chemical foaming agents are specific chemicals that decompose when heated to yield gaseous decomposition products dispersed in the polymer melt. Although physical foaming agents can be used to make the inventive ball sealers, chemical blowing agents will normally be used, as they are simpler and easier to use and, in addition, enable more precise control of the amount of foaming and hence the density of the injected molded product ultimately obtained.
As also well understood in the art, chemical foaming agents can be categorized as either being endothermic or exothermic. Endothermic chemical foaming agents, which typically release carbon dioxide and/or water vapor, absorb energy as they decompose. Calcium carbonate, sodium citrate and citric acid powder are good examples of this type of foaming agent. Exothermic chemical foaming agents, which typically release nitrogen gas, generate energy as they decompose. Various azo compounds and hydrazides are good examples of this type of foaming agent.
In accordance with this invention, both of types of these chemical foaming agents can be used, as can mixtures of physical and chemical foaming agents. However, endothermic chemical blowing agents will normally used, as not only do then enable foaming to be controlled more easily but, in addition, their decomposition products are compatible with most slowly water-soluble polymers.
Normally, the amount of chemical foaming agent used will be about 2-5 wt. %, based on the weight of the slowly water-soluble polymer used. However, amounts as low as 1.5 wt. %, 1.0 wt. %, 0.75 wt. % or even 0.5 wt. % can be used as well as amounts as high as 7.5 wt. %, 10 wt. %, 12 wt. % or even 15 wt. %. If physical rather than chemical foaming agents are used, then comparable amounts of the physical foaming agents will be used, i.e., amounts which generate a comparable amount of foaming gas.
As indicated above, the inventive perforation ball sealers preferably exhibit a density of 1.05 g/cc or less so that they avoid sinking in the aqueous treatment fluids in which they are used. This means that the effect of foaming in accordance with this invention is to reduce the density of the inventive ball sealer obtained as compared with an otherwise identical conventional ball sealer made without foaming by some particular percentage. For example, in the case of an inventive ball sealer which exhibits a density of 1.0 g/cc and which is made from a slowly water-soluble polymer having a density of 1.5 g/cc, the effect of foaming in accordance with this invention is to reduce the density of the inventive ball sealer by 33% [(1.5−1.0)/1.5], meaning that the density of this inventive ball sealer is 67% of its non-foamed conventional counterpart.
In accordance with this invention, foaming is carried out in such a way that the amount of density reduction achieved can be as little as 5% to as much as 67%% relative to the density of the non-foamed conventional counterpart. More typically, the amount of density reduction achieved will be between 10% to 30%, 12% to 25% or even 14% to 22% relative to the density of the non-foamed conventional counterpart. This, in turn, means that the density of the inventive ball sealer can be as little as 33% to as much as 95% of its non-foamed conventional counterpart. More typically, the density of the inventive ball sealer will be 70% to 90%, 75% to 88% or even 78% to 86% of its non-foamed conventional counterpart. Persons of ordinary skill in the injection molding art should have no difficulty in achieving these density reductions by suitable adjustment of the type and amounts of chemical blowing agents used as well as control of extruder temperature and other extruder variables.
In order to more thoroughly describe this invention, the following working examples are provided:
A group of inventive perforation ball sealers was made by injection molding a slowly water-soluble polymer in accordance with the general procedures discussed above. A sample ball sealer so made was then sectioned and photographed, a copy of which is reproduced in
As can be seen from this photograph, the inventive ball sealer exhibited a shell and core structure, with the core being composed of an expanded polymer foam and with the shell exhibiting a relatively uniform thickness.
Another sample of this ball sealer was analyzed for density and crush strength and found to exhibit a density of ˜0.89 g/cc and a crush strength of 19,000 psi in both dry conditions and after having been immersed in 2% KCl for two hours.
Conventional ball sealers made using known water-soluble or biodegradable polymers or polymer blends can have specific gravity ranging from 1.10 to 1.40 g/cc. Compared to this, the histogram of
Another group of buoyant ball sealers made in accordance with this invention was subjected to solubility testing in accordance with the solubility testing procedures described in the above-mentioned commonly-assigned application Ser. No. 62/396,960. For the sake of comparison, a group of conventional comparable ball sealers was also tested.
The inventive ball sealer exhibited essentially the same dissolution profile as the conventional ball sealers, thereby indicating the inventive ball sealers will provide an equivalent performance to their conventional counterparts even though their densities have been significantly reduced.
Example 3 was repeated, except that a different slowly water-soluble polymer, designated as “HR”, was used. In addition, only two solubility tests were done using two different aqueous test fluids, one containing 2% KCl at 175° F., the other containing NaOH to pH 11 also at 175° F.
Examination showed that these inventive buoyant ball sealers also exhibit dissolution profiles which are essentially the same as their conventional non-foamed counterparts.
Although only a few embodiments of this invention have been disclosed above, it should be appreciated that many modifications can be made without departing from the spirit and scope of this invention. All such modifications are intended to be included within the scope of this invention, which is to be limited only by the following claims.
This application is based on and claims priority to Provisional Application Ser. No. 62/587,996, filed Nov. 17, 2017, the entire disclosure of which is incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
2803306 | Hower | Aug 1957 | A |
3724549 | Dill | Apr 1973 | A |
3797575 | Dill et al. | Mar 1974 | A |
3872923 | Knight et al. | Mar 1975 | A |
3954629 | Scheffel et al. | May 1976 | A |
4005753 | Scheffel et al. | Feb 1977 | A |
4102401 | Erbstoesser | Jul 1978 | A |
4527628 | Dill et al. | Jul 1985 | A |
4716964 | Erbstoesser et al. | Jan 1988 | A |
5356149 | Kane | Oct 1994 | A |
5824746 | Harris | Oct 1998 | A |
5852114 | Loomis et al. | Dec 1998 | A |
6367548 | Purvis et al. | Apr 2002 | B1 |
6380138 | Ischy et al. | Apr 2002 | B1 |
9303474 | Shindgikar | Apr 2016 | B2 |
9914872 | Wehunt | Mar 2018 | B2 |
20010044477 | Soane | Nov 2001 | A1 |
20060175059 | Sinclair et al. | Aug 2006 | A1 |
20070169935 | Akbar et al. | Jul 2007 | A1 |
20090255674 | Boney et al. | Oct 2009 | A1 |
20120285695 | Lafferty et al. | Nov 2012 | A1 |
20140345785 | Wang et al. | Nov 2014 | A1 |
20140345878 | Murphree | Nov 2014 | A1 |
20160281454 | Zhu et al. | Sep 2016 | A1 |
20170210976 | Okamoto et al. | Jul 2017 | A1 |
20180346800 | Fu et al. | Dec 2018 | A1 |
Number | Date | Country |
---|---|---|
2884041 | Jun 2015 | EP |
2025485 | Jan 1980 | GB |
2012174065 | Dec 2012 | WO |
2013101702 | Jul 2013 | WO |
2014074326 | May 2014 | WO |
Entry |
---|
Search Report and Written Opinion for International Application No. PCT/US2017/052204 dated Dec. 18, 2017. |
Injection Molding Processing Guide, www.bergenintrenational.com/pdfs/Injection_Molding_Processing_Guide, Sep. 3, 2009; Lemaster, Tips and Techniques: How to Mold & Extrude Using Chemical Blowing Agents, Plastics Technology, Feb. 2011, http//www.ptonline.com/articles/hot-to-mold-extrude-using-chemical-blowing-agents. |
Gabriel et al., “The Design of Buoyant Ball Sealer Treatments”, SPE 13085; 1984; Society of Petroleum Engineers of AIME. |
Foamazol Chemical Foaming Agents, Injection Molding Processing Guide, Bergen International, 2008; 7 pages. |
Office Action for U.S. Appl. No. 15/708,957 dated Sep. 5, 2019. |
Search Report for Denmark Application No. PA 2019 70233 dated Oct. 4, 2019. |
Examination Report for Denmark Application No. PA 2019 70233 dated May 12, 2020. |
Number | Date | Country | |
---|---|---|---|
20190153296 A1 | May 2019 | US |
Number | Date | Country | |
---|---|---|---|
62587996 | Nov 2017 | US |