The invention relates to a crystal laminate structure.
Conventionally, a method in which a dopant is added during crystal growth by the MBE (Molecular Beam Epitaxy) method or the EFG (Edge-defined Film-fed Growth) method (see, e.g., PTLs 1 and 2) and a method in which a dopant is added to a grown β-Ga2O3-based single crystal by ion implantation (see, e.g., PTL 3) are known to dope a β-Ga2O3-based single crystal.
When using the MBE method, however, doping with a concentration of not less than 1×1018 atoms/cm3 is difficult since impurities segregate during epitaxial crystal growth. In addition, a doping profile in a depth direction and distribution uniformity on the wafer surface are not good due to the impurity segregation and repeatability is poor.
Meanwhile, when using the EFG method, since a raw material contains an impurity at a concentration of about 1×1017 atoms/cm3, doping with a lower concentration is not possible.
In case of ion implantation, implantation depth of the impurity ion is limited to about 1 μm. In addition, since the ion beam damages the crystal, vacancy/void-type defects are introduced, causing deterioration of crystallinity.
Therefore, it is one of objects of the invention to provide a crystal laminate structure having a β-Ga2O3-based single crystal film in which a dopant is included throughout the crystal and the concentration of the dopant can be set across a broad range.
To achieve the above-mentioned object, an aspect of the invention provides a crystal laminate structure defined by [1] to [10] below.
[1] A crystal laminate structure, comprising: a Ga2O3-based substrate; and a β-Ga2O3-based single crystal film formed by epitaxial crystal growth on a principal surface of the Ga2O3-based substrate, wherein the β-Ga2O3-based single crystal film comprises Cl and a dopant doped in parallel with the crystal growth at a concentration of not less than 1×1013 atoms/cm3 and not more than 5.0×1020 atoms/cm3.
[2] The crystal laminate structure defined by [1], wherein a concentration of Cl of the β-Ga2O3-based single crystal film is not more than 5×1016 atoms/cm3.
[3] The crystal laminate structure defined by [1] or [2], wherein the dopant comprises Si.
[4] The crystal laminate structure defined by [1] or [2], wherein the dopant concentration is not less than 6.5×1015 atoms/cm3 and not more than 2.1×1020 atoms/cm3.
[5] The crystal laminate structure defined by [1] or [2], wherein a density of a carrier generated by the doping of the dopant is not less than 1×1013 cm−3 and not more than 5.0×1020 cm−3.
[6] The crystal laminate structure defined by [5], wherein a density of a carrier generated by the doping of the dopant is not less than 3.2×1015 cm −3 and not more than 1.8×1018 cm −3.
[7] The crystal laminate structure defined by [1] or [2], wherein the β-Ga2O3-based single crystal film comprises a β-Ga2O3 crystal film.
[8] The crystal laminate structure defined by [1] or [2], wherein the principal surface of the Ga2O3-based substrate has a plane orientation of (001), (010), (−201) or (101).
[9] The crystal laminate structure defined by [3], wherein a source gas of the dopant comprises a SiCl4 gas.
[10] The crystal laminate structure defined by [1] or [2], wherein a thickness of the β-Ga2O3-based single crystal film is not less than 1000 nm.
According to the invention, it is possible to provide a crystal laminate structure having a β-Ga2O3-based single crystal film in which a dopant is included throughout the crystal and the concentration of the dopant can be set across a broad range.
(Configuration of Crystal Laminate Structure)
The Ga2O3-based substrate 10 is a substrate formed of a Ga2O3-based single crystal with a β-crystal structure. The Ga2O3-based single crystal here means a Ga2O3 single crystal or is a Ga2O3 single crystal doped with an element such as Al or In, and may be, e.g., a (GaxAlyIn(1-x-y))2O3 (0<x≤1, 0≤y≤1, 0<x+y≤1) single crystal which is a Ga2O3 single crystal doped with Al and In. The band gap is widened by adding Al and is narrowed by adding In. The Ga2O3-based substrate 10 may also contain a conductive impurity such as Si.
The plane orientation of the principal surface 11 of the Ga2O3-based substrate 10 is, e.g., (001), (010), (−201) or (101).
To form the Ga2O3-based substrate 10, for example, a bulk crystal of a Ga2O3-based single crystal grown by, e.g., a melt-growth technique such as the FZ (Floating Zone) method or the EFG (Edge Defined Film Fed Growth) method is sliced and the surface thereof is then polished.
The β-Ga2O3-based single crystal film 12 is formed of a Ga2O3-based single crystal with a β-crystal structure in the same manner as the Ga2O3-based substrate 10. The β-Ga2O3-based single crystal film 12 also contains a dopant such as Li, Na, K, Rb, Cs, Be, Mg, Ca, Sr, Ba, Sc, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, Hg, B, Al, In, Tl, C, Si, Ge, Sn, Pb, N, P, As, Sb, Bi, S, Se or Te, etc., which is doped during crystal growth.
A concentration of the dopant contained in the β-Ga2O3-based single crystal film 12 is not less than 1×1013 atoms/cm3 and not more than 5×1020 atoms/cm3, preferably, not less than 6.5×1015 atoms/cm3 and not more than 2.1×1020 atoms/cm3.
A density of carrier generated by the doping of the dopant is, e.g., not less than 3.2×1015 cm−3 and not more than 1.8×1018 cm−3.
The β-Ga2O3-based single crystal film 12 also contains Cl at a concentration of not more than 5×1016 atoms/cm3. This results from that the β-Ga2O3-based single crystal film 12 is formed by the HVPE method using Cl-containing gas. Generally, Cl-containing gas is not used to form aβ-Ga2O3-based single crystal film when using a method other than the HVPE method, and the β-Ga2O3-based single crystal film does not contain Cl, or at least does not contain 1×1016 cm −3 or more of Cl.
Meanwhile, the β-Ga2O3-based single crystal film 12 is formed by the HYPE (Halide Vapor Phase Epitaxy) method with a high crystal growth rate, and thus can be formed thick, e.g., can have a thickness of not less than 1000 nm. In general, a growth rate of the β-Ga2O3-based single crystal film by industrial HVPE is 200 μm/h, and in this case, a film of up to 1000 μm in thickness can be grown in a realistic production time. In other words, it is possible to form the β-Ga2O3-based single crystal film 12 having a thickness of not less than 1000 nm and not more than 1000 μm. In this regard, use of the MBE method is not realistic in actual production since a crystal growth rate of the β-Ga2O3-based single crystal film is about 120 nm/h and it requires not less than 8 hours to form a film of not less than 1000 nm in thickness.
Additionally, a buffer layer may be provided between the Ga2O3-based substrate 10 and the β-Ga2O3-based single crystal film 12 to prevent carrier compensation in the β-Ga2O3-based single crystal film 12 due to impurity diffusion from the Ga2O3-based substrate 10.
(Structure of Vapor Phase Deposition System)
A structure of a vapor phase deposition system used for growing the β-Ga2O3-based single crystal film 12 in the present embodiment will be described below as an example.
The growth rate when using the HVPE method is higher than that in the MBE method, etc. In addition, in-plane distribution of film thickness is highly uniform and it is possible to grow a large-diameter film. Therefore, it is suitable for mass production of crystal.
The reaction chamber 20 has a source reaction region R1 in which a reaction container 26 containing a Ga source is placed and a gallium source gas is produced, and a crystal growth region R2 in which the Ga2O3-based substrate 10 is placed and the β-Ga2O3-based single crystal film 12 is grown thereon. The reaction chamber 20 is formed of, e.g., quartz glass.
Here, the reaction container 26 is formed of, e.g., quartz glass and the Ga source contained in the reaction container 26 is metal gallium.
The first heating means 27 and the second heating means 28 are capable of respectively heating the source reaction region R1 and the crystal growth region R2 of the reaction chamber 20. The first heating means 27 and the second heating means 28 are, e.g., resistive heaters or radiation heaters.
The first gas introducing port 21 is a port for introducing a Cl-containing gas (Cl2 gas or HCl gas) into the source reaction region R1 of the reaction chamber 20 using an inert carrier gas (N2 gas, Ar gas or He gas). The second gas introducing port 22 is a port for introducing an oxygen-containing gas (O2 gas or H2O gas, etc.) as an oxygen source gas into the crystal growth region R2 of the reaction chamber 20 using an inert carrier gas (N2 gas, Ar gas or He gas). The third gas introducing port 23 is a port for introducing an inert carrier gas (N2 gas, Ar gas or He gas) into the crystal growth region R2 of the reaction chamber 20. The fourth gas introducing port 24 is a port for introducing a source gas of dopant to be added to the β-Ga2O3-based single crystal film 12, such as Si (e.g., silicon tetrachloride, etc.), into the crystal growth region R2 of the reaction chamber 20 using an inert carrier gas (N2 gas, Ar gas or He gas).
(Growth of β-Ga2O3-Based Single Crystal Film)
To grow the β-Ga2O3-based single crystal film 12, it is possible to use a technique of growing β-Ga2O3-based single crystal film disclosed in Japanese Patent Application No. 2014-088589. A process of growing the β-Ga2O3-based single crystal film 12 in the present embodiment will be described below as an example.
Firstly, the source reaction region R1 of the reaction chamber 20 is heated by the first heating means 27 and an atmosphere temperature in the source reaction region R1 is then maintained at a predetermined temperature.
Next, in the source reaction region R1, a Cl-containing gas introduced through the first gas introducing port 21 using a carrier gas is reacted with the metal gallium in the reaction container 26 at the above-mentioned atmosphere temperature, thereby producing a gallium chloride gas.
The atmosphere temperature in the source reaction region R1 here is preferably a temperature at which GaCl gas has the highest partial pressure among component gases of the gallium chloride gas produced by the reaction of the metal gallium in the reaction container 26 with the Cl-containing gas. The gallium chloride gas here contains GaCl gas, GaCl2 gas, GaCl3 gas and (GaCl3)2 gas, etc.
The temperature at which a driving force for growth of Ga2O3 crystal is maintained is the highest with the GaCl gas among the gases contained in the gallium chloride gas. Growth at a high temperature is effective to obtain a high-quality Ga2O3 crystal with high purity. Therefore, for growing the β-Ga2O3-based single crystal film 12, it is preferable to produce a gallium chloride gas in which a partial pressure of GaCl gas having a high driving force for growth at a high temperature is high.
It is possible to increase a partial pressure ratio of the GaCl gas in the gallium chloride gas by reacting the metal gallium with the Cl-containing gas at an atmosphere temperature of about not less than 300° C. Therefore, it is preferable that the metal gallium in the reaction container 26 be reacted with the Cl-containing gas in a state that the atmosphere temperature in the source reaction region R1 is maintained at not less than 300° C. by using the first heating means 27.
At the atmosphere temperature of, e.g., 850° C., the partial pressure ratio of the GaCl gas is predominantly high (the equilibrium partial pressure of the GaCl gas is four orders of magnitude greater than the GaCl2 gas and is eight orders of magnitude greater than the GaCl3 gas) and the gases other than GaCl gas hardly contribute to the growth of Ga2O3 crystal.
Meanwhile, considering the lifetime of the first heating means 27 and heat resistance of the reaction chamber 20 formed of quartz glass, etc., it is preferable that the metal gallium in the reaction container 26 be reacted with the Cl-containing gas in a state that the atmosphere temperature in the source reaction region R1 is maintained at not more than 1000° C.
In addition, if hydrogen is contained in an atmosphere for growing the β-Ga2O3-based single crystal film 12, surface flatness and a driving force for growth of the β-Ga2O3-based single crystal film 12 decrease. Therefore, it is preferable that a Cl2 gas not containing hydrogen be used as the Cl-containing gas.
Next, in the crystal growth region R2, the gallium chloride gas produced in the source reaction region R1 is mixed with the oxygen-containing gas introduced through the second gas introducing port 22 and the dopant source gas such as Si introduced through the fourth gas introducing port 24, the Ga2O3-based substrate 10 is then exposed to the mixed gas, and the β-Ga2O3-based single crystal film 12 containing the dopant is thereby epitaxially grown on the Ga2O3-based substrate 10. At this time, in a furnace housing the reaction chamber 20, pressure in the crystal growth region R2 is maintained at, e.g., 1 atm.
The dopant source gas used here is preferably a chloride-based gas to prevent other unintentional impurities from being mixed. For example, when Si, Ge, Sn or Pb (Group 14 element) is selected from the dopants listed above and is used as a dopant, a chloride-based gas such as SiCl4, GeCl4, SnCl4 or PbCl2, respectively, is used. Here, the chloride-based gas is not limited to a compound of an element with only chlorine, and may be, e.g., a silane-based gas such as SiHCl3.
The dopant such as Si is doped during growth of a β-Ga2O3-based single crystal.
If hydrogen is contained in an atmosphere for growing the β-Ga2O3-based single crystal film 12, surface flatness and a driving force for growth of the β-Ga2O3-based single crystal film 12 decrease. Therefore, it is preferable that an O2 gas not containing hydrogen be used as the oxygen-containing gas.
Meanwhile, the smaller the equilibrium partial pressure of the GaCl gas, the more the GaCl gas is consumed for growth of Ga2O3 crystal and the Ga2O3 crystal grows efficiently. For example, the equilibrium partial pressure of the GaCl gas sharply falls when a ratio of the supplied partial pressure of the O2 gas to the supplied partial pressure of the GaCl gas (the O2/GaCl supplied partial pressure ratio) is not less than 0.5. Therefore, to efficiently grow the β-Ga2O3-based single crystal film 12, the β-Ga2O3-based single crystal film 12 is preferably grown in a state that the O2/GaCl supplied partial pressure ratio in the crystal growth region R2 is not less than 0.5.
In
Meanwhile, a growth temperature of not less than 900° C. is required to grow the β-Ga2O3-based single crystal film 12. A single crystal may not be obtained at less than 900° C.
(Evaluation of β-Ga2O3-Based Single Crystal Film)
Plural β-Ga2O3-based single crystal films 12 were formed under different growth conditions, and Si concentration and carrier density thereof were measured. The results are shown in Tables 1 to 3 below.
Samples a1 and a2 shown in Table 1 are the crystal laminate structures 1 each having the β-Ga2O3-based single crystal film 12 formed under the condition that a partial pressure of the GaCl gas supplied as a Ga source gas, P0GaCl, was fixed to 2×10−4 atm. Meanwhile, samples b1 to b12 shown in Table 2 are the crystal laminate structures 1 each having the β-Ga2O3-based single crystal film 12 formed under the condition that P0GaCl was fixed to 5×10−4 atm, and samples c1 to c9 shown in Table 3 are the crystal laminate structures 1 each having the β-Ga2O3-based single crystal film 12 formed under the condition that P0GaCl was fixed to 1×10−3 atm.
In the samples a1, a2, b1 to b12 and c1 to c9, a 7 μm-thick Si-containing β-Ga2O3 single crystal film was formed as the β-Ga2O3-based single crystal film 12 on a β-Ga2O3 substrate having a (001)-oriented principal surface used as the Ga2O3-based substrate 10.
“RSi” in Tables 1 to 3 is a physical quantity expressed by P0SiCl4/(P0GaCl+P0SiCl4). P0SiCl4 here is a partial pressure of the SiCl4 gas supplied as a Si source gas during growth of the β-Ga2O3-based single crystal film 12. The value of P0GaCl for forming the β-Ga2O3-based single crystal film 12 is not specifically limited as long as pressure in the crystal growth region R2 of the vapor phase deposition system 2 (e.g., 1 atm) is maintained.
“Si concentration” in Tables 1 to 3 is a concentration of Si as a dopant in the β-Ga2O3-based single crystal film 12 (in a region at a depth of 2 to 6 μm from the surface) obtained by SIMS (Secondary Ion Mass Spectrometry). The background level of the Si concentration measured by SIMS differs depending on the measurement conditions. The Si concentration of the samples b2 and b3 was measured under the condition that the background level was about 3.0×1015 atoms/cm3, the Si concentration of the other samples was measured under the condition that the background level was about 3.0×1016 atoms/cm3, and Si at a concentration of not more than the background level is not detectable in each sample.
“Nd-Na” in Tables 1 to 3 is a difference between a donor concentration Nd and an acceptor concentration Na, i.e., a carrier concentration, obtained by ECV (Electrochemical Capacitance-Voltage) measurement.
From Tables 2 and 3, it is understood that the carrier density obtained by ECV measurement substantially coincides with the Si concentration obtained by SIMS measurement. From Table 4 which is described later, it is understood that the carrier density obtained by Hall measurement also substantially coincides with the Si concentration obtained by SIMS measurement.
In
In
FIG.5 shows that the relation between RSi and the carrier density of the β-Ga2O3-based single crystal film 12 is a substantially linear relation.
From the actual measurement data shown in
However, when trying to dope Si at a concentration of less than about 1×1013 atoms/cm3, it is difficult to accurately control the partial pressure of the doping gas and it is thus difficult to control the Si concentration. Meanwhile, the upper limit of the Si concentration at which crystal quality of the β-Ga2O3-based single crystal film 12 can be maintained by solid solubility of Si in β-Ga2O3-based single crystal is about 5.0×1020 atoms/cm3. Thus, it is preferable to control the Si concentration in the range of not less than 1×1013 atoms/cm3 and not more than 5.0×1020 atoms/cm3.
Meanwhile, from the actual measurement data shown in
In an undoped β-Ga2O3-based single crystal film grown by the HVPE method, carriers with a density of not more than 1×1013 cm −3 remains as disclosed in Japanese Patent Application No. 2014-088589, and it is difficult to control the carrier concentration to be lower than 1×1013 cm−3. In addition, the upper limit of the Si concentration at which crystal quality of the β-Ga2O3-based single crystal film 12 can be maintained is about 5.0×1020 atoms/cm3 as described above. Therefore, for the carrier concentration which substantially coincides with the Si concentration, the upper limit at which crystal quality of the β-Ga2O3-based single crystal film 12 can be maintained is considered to be about 5.0×1020 cm−3. Thus, it is preferable to control the carrier density of the Ga2O3-based single crystal film in the range of not less than 1×1013 cm−3 and not more than 5.0×1020 cm −3.
Sn is a dopant contained in the Ga2O3-based substrate 10 of the sample c4. From the SIMS profile of Sn in
According to
Plural β-Ga2O3 single crystal films were formed under different growth conditions, and carrier density, resistivity and electron mobility thereof were measured. The results are shown in Table 4 below. These values were obtained by Hall measurement using the Van del Pauw method. In the Hall measurement, a DC magnetic field of 0.57 T and an electric current of 0.1 mA were applied at room temperature (25° C.). Table 4 also shows the Si concentration in the β-Ga2O3-based single crystal film (in a region at a depth of 2 to 6 μm from the surface) measured by SIMS.
The samples d1 to d4 to be subjected to Hall measurement were made as follows. Firstly, a β-Ga2O3 single crystal film was epitaxially grown on a highly Fe-doped β-Ga2O3 substrate having a (001)-oriented principal surface. At this time, SiCl4 gas supply was started in the middle of the growth of the β-Ga2O3 single crystal film so that a 2 μm-thick undoped β-Ga2O3 single crystal film and an 8 μm-thick Si-doped β-Ga2O3 single crystal film were formed. The undoped β-Ga2O3 single crystal film has a function of preventing diffusion of Fe from the β-Ga2O3 substrate and thus preventing carrier compensation in the Si-doped β-Ga2O3 single crystal film.
The β-Ga2O3 single crystal film here was formed under the condition that P0GaCl was fixed to 1×10−3 atm.
Next, for surface flattening, the surface of the Si-doped β-Ga2O3 single crystal film was polished 2 μm by CMP (Chemical Mechanical Polishing). Next, circular In electrodes having a diameter of 1 mm were formed at four corners on the surface of the Si-doped β-Ga2O3 single crystal film and were then annealed in a N2 atmosphere at 900° C. for 90 seconds, thereby forming ohmic electrodes.
In the samples d1 to d4 to be subjected to Hall measurement, the β-Ga2O3 substrate corresponds to the Ga2O3-based substrate 10 and the Si-doped β-Ga2O3 single crystal film corresponds to the β-Ga2O3-based single crystal film 12.
Although the β-Ga2O3 substrate having a (001)-oriented principal surface was used as the Ga2O3-based substrate 10 in the samples a1, a2, b1 to b12, c1 to c9 and d1 to d4 as described above, similar evaluation results are obtained also when a β-Ga2O3 substrate having a (−201)-, (101)- or (010)-oriented, principal surface is used. In addition, similar evaluation results are obtained also when another β-Ga2O3-based substrate is used instead of the β-Ga2O3 substrate or when another β-Ga2O3-based single crystal film is formed instead of the β-Ga2O3 single crystal film.
(Effects of the Embodiment)
In the embodiment, by adding a dopant while growing a β-Ga2O3-based single crystal using the HVPE method, it is possible to control the dopant concentration of the β-Ga2O3-based single crystal in a wider range than when using the MBE method or the EFG method. In addition, unlike when using ion implantation, problems such as limitation of dopant implantation depth or deterioration of crystallinity due to ion beam do not occur.
Although the embodiment of the invention has been described, the invention is not intended to be limited to the embodiment, and the various kinds of modifications can be implemented without departing from the gist of the invention.
In addition, the invention according to claims is not to be limited to the embodiment described above. Further, it should be noted that all combinations of the features described in the embodiment are not necessary to solve the problem of the invention.
Provided is a crystal laminate structure having a β-Ga2O3-based single crystal film in which a dopant is included throughout the crystal and the concentration of the dopant can be set across a broad range.
Number | Date | Country | Kind |
---|---|---|---|
2015-058518 | Mar 2015 | JP | national |
The present application is a continuation application filed under 35 USC § 120 claiming priority to co-pending application U.S. Ser. No. 15/559,167, filed Sep. 18, 2017, which claims priority as a national stage filing under 35 USC § 371 of PCT/JP2016/054620 filed Feb. 17, 2016, the entire contents of each of which are incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
8421190 | Okahisa et al. | Apr 2013 | B2 |
8822263 | Koukitu et al. | Sep 2014 | B2 |
9437689 | Sasaki et al. | Sep 2016 | B2 |
9461124 | Sasaki et al. | Oct 2016 | B2 |
10249767 | Sasaki et al. | Apr 2019 | B2 |
20030186475 | Ueda et al. | Oct 2003 | A1 |
20070012943 | Okahisa et al. | Jan 2007 | A1 |
20090127664 | Okahisa et al. | May 2009 | A1 |
20100006836 | Koukitu et al. | Jan 2010 | A1 |
20110018003 | Okahisa et al. | Jan 2011 | A1 |
20140217405 | Sasaki et al. | Aug 2014 | A1 |
20140217469 | Sasaki et al. | Aug 2014 | A1 |
20140217554 | Sasaki | Aug 2014 | A1 |
20160265137 | Goto et al. | Sep 2016 | A1 |
20160300953 | Sasaki et al. | Oct 2016 | A1 |
20160365418 | Sasaki et al. | Dec 2016 | A1 |
20180350967 | Sasaki et al. | Dec 2018 | A1 |
20200102667 | Goto | Apr 2020 | A1 |
Number | Date | Country |
---|---|---|
103765593 | Apr 2014 | CN |
103782392 | May 2014 | CN |
2 063 458 | May 2009 | EP |
3 054 037 | Aug 2016 | EP |
2001-253794 | Sep 2001 | JP |
2003-017420 | Jan 2003 | JP |
2006-193348 | Jul 2006 | JP |
2009-126723 | Jun 2009 | JP |
2010-232623 | Oct 2010 | JP |
2013-056803 | Mar 2013 | JP |
2013-058637 | Mar 2013 | JP |
2013-082587 | May 2013 | JP |
WO 2013035842 | Mar 2013 | WO |
WO 2013035845 | Mar 2013 | WO |
Entry |
---|
International Search Report dated Apr. 12, 2016 issued in PCT/JP2016/054620. |
Japanese Office Action dated Jul. 11, 2017 issued in JP 2015-058518. |
Murakami, Hisashi et al., “Homoepitaxial growth of Beta-Ga2O3 layers by halide vapor phase epitaxy”, Applied Physics Express (Dec. 11, 2014), vol. 8, No. 1, 015503. |
Sasaki, Kohei et al., “Device-Quality Beta-Ga2O3 Epitaxial Films Fabricated by Ozone Molecular Beam Epitaxy”, Applied Physics Express (Feb. 28, 2012), vol. 5, No. 3, 035502. |
International Preliminary Report on Patentability dated Oct. 5, 2017 issued in PCT/JP2016/054620. |
Official Action dated Jan. 9, 2018 received from the Japanese Patent Office in related JP 2015-058518 together with English language translation. |
Gogova, D. et al., “Structural properties of Si-doped β-Ga2O3 layers grown by MOVPE”, Journal of Crystal Growth, vol. 401, Sep. 1, 2014, pp. 665-669. |
Extended Supplementary European Search Report dated Oct. 16, 2018 in European Patent Application No. 16 76 8238.4. |
Chinese Office Action dated Jul. 18, 2019 in Chinese Patent Application No. 201680016988.8. |
Holgate, S. A., “Understanding Solid State Physics”, 2010, p. 253, CRC Presss, Taylor and Francis Group, NY. |
Number | Date | Country | |
---|---|---|---|
20200102667 A1 | Apr 2020 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 15559167 | US | |
Child | 16702186 | US |