Crystalline adduct of bisphenol A and bisphenol TMC

Information

  • Patent Grant
  • 5756860
  • Patent Number
    5,756,860
  • Date Filed
    Friday, August 2, 1996
    28 years ago
  • Date Issued
    Tuesday, May 26, 1998
    26 years ago
Abstract
The invention relates to the preparation of a transparent crystalline adduct consisting of bisphenol A (75 parts) and bisphenol TMC (25 parts), which has a melting point of 144.degree. C. which is below the melting points of the pure starting compounds bisphenol A (157.degree. C.) and bisphenol TMC (208.degree. C.).
Description

The invention relates to the preparation of a transparent, crystalline adduct consisting of bisphenol A (75 parts) and bisphenol TMC (1,1-bis-(4-hydroxyphenyl)-3,3,5-trimethylcyclohexane) (25 parts) which has a melting point of 144.degree. C. which is below the melting points of the pure starting components bisphenol A (157.degree. C.) and bisphenol TMC (208.degree. C.).
Technical, energetic and processing advantages are produced by the use of this type of crystalline adduct during the preparation of transparent and thermally stable polymers which are resistant to high temperature, such as polycarbonates.
Bisphenol A (BPA) is prepared by reacting phenol and acetone under acid conditions in the presence of optionally modified ion exchange resins (e.g. DE-A 3 727 641, corresponding to US-A 4,912,263).
Isolation is performed essentially via a graduated crystallisation procedure for bisphenol A/phenol adducts followed by filtration and removal of excess phenol. Bisphenol A prepared in this way is suitable, without any further purification, as a monomer for preparing highly transparent polymers such as, for instance, polycarbonates.
Bisphenol TMC is prepared by reacting 3,3,5-trimethyl-cyclohexanone and is used as a mixture with bisphenol A as an additional component for preparing transparent polycarbonates which are resistant to high temperature.
It has now been found that a mixture of 75 parts of high purity bisphenol A and 25 parts of high purity bisphenol TMC form a crystalline adduct from the melt, which has a sharp melting point at 144.degree. C.
This melting point is below the melting point of bisphenol A (157.degree. C.) and well below that of bisphenol TMC (208.degree. C.).
The invention provides a crystalline adduct consisting of 75 parts by wt. of bisphenol A and 25 parts by wt. of bisphenol TMC with a melting point of 144.degree. C., characterised in that a mixture of 90 to 60 parts by wt. of bisphenol A and 10 to 40 parts by wt. of bisphenol TMC is heated to a temperature of 150 to 160.degree. C. and then cooled to a temperature <140.degree. C.
The adduct prepared in accordance with the invention can be used to prepare high purity, transparent polymers which are resistant to high temperature such as, for instance, specific types of polycarbonate.
This adduct is used, for instance, to prepare high purity, transparent and thermally stable melts from bisphenol A and bisphenol TMC at temperatures <200.degree. C. and can be stored as raw material and processed at this temperature.
The adduct prepared in accordance with the invention can be used to prepare high purity bisphenol TMC. This can be achieved by distillation and/or by crystallisation.
Mixed crystals of bisphenol A and phenol (60 parts of BPA: 40 parts of phenol) are known and are used as a process purification step in the process for preparing bisphenol A.





EXAMPLE
75 parts of bisphenol A and 25 parts of bisphenol TMC were mixed, melted at 160.degree. C. and then allowed to solidify again. The melting point of the mixture was found to be 144.degree. C.
DSC measurements were performed on mixtures of bisphenol A and bisphenol TMC (Table 1). A clear, sharp melting point was determined at 144.degree. C.
TABLE 1______________________________________GC analysisp,p-BPA BP-TMC DSC analysis Melting range% % .degree.C. .degree.C. .degree.C.______________________________________0.00 100 205.9 203 2105.00 95.0 202.4 182 20610.0 90.0 198.0 170 20515.0 85.0 196.3 140 20220.0 80.0 191.7 155 20025.0 75.0 188.5 150 19830.0 70.0 184.5 145 19335.0 65.0 181.5 135 19540.0 60.0 177.2 150 19545.0 55.0 173.2 133 18350.0 50.0 169.3 130 18055.0 45.0 159.3 128 18060.0 40.0 141.6 115 17065.0 35.0 142.8 115 16570.0 30.0 142.4 115 16575.0 25.0 144.4 115 16580.0 20.0 140.2 120 15585.0 15.0 145.5 125 15590.0 10.0 152.3 125 16095.0 5.0 154.8 130 165100 0.00 157.1 145 165______________________________________
Claims
  • 1. A process for preparing a crystalline adduct of 75 parts by wt. of bisphenol A and 25 parts by wt. of bisphenol TMC with a melting point of 144.degree. C., characterised in that a mixture of 90 to 60 parts by wt. of bisphenol A and 10 to 40 parts by wt. of bisphenol TMC is heated to a temperature of 150.degree. to 160.degree. C. and then cooled to a temperature<140.degree. C.
  • 2. A crystalline adduct of 75 parts by wt. of bisphenol A and 25 parts by wt. of bisphenol TMC with a melting pint of 144.degree. C., prepared in accordance with claim 1.
Priority Claims (1)
Number Date Country Kind
195 29 857.8 Aug 1995 DEX
US Referenced Citations (4)
Number Name Date Kind
4034039 Sun Jul 1977
4912263 Rudolph et al. Mar 1990
5336812 Salek et al. Aug 1994
5368827 Moriya et al. Nov 1994
Foreign Referenced Citations (3)
Number Date Country
1 168 445 May 1960 DEX
27 19 997 Dec 1977 DEX
3727641 Mar 1989 DEX