Claims
- 1. A process for preparing, in aqueous emulsion, a crystallizable, controlled composition interpolymer consisting essentially of (a) from about 88 to about 92 mole percent vinylidene chloride, (b) from about 8 to about 12 mole percent methyl methacrylate, and (c) up to about 3 weight percent, based on the combined weight of (a) and (b), of one or more ethylenically unsaturated comonomers; said interpolymer having a relative viscosity of at least about 1.40 at 25.degree. C. as a 1 percent solution in tetrahydrofuran and being capable of forming substantially haze-free solutions when present in an amount of about 20 percent solids in a solvent mixture consisting of 65 percent by weight tetrahydrofuran and 35 percent by weight toluene as measured in terms of at least 85 percent transmission of the solution, after aging at 25.degree. C. for a period of 24 hours, against a reference of the pure solvent mixture using an ultraviolet spectrophotometer operating at a wavelength of 640 nm said interpolymer having a minimum heat-seal temperature no greater than 115.degree. C., and having a water-vapor transmission rate of no greater than 0.25 g/100 in.sup.2 /24 hours when deposited as a coating from a tetrahydrofuran lacquer solution at a coating weight of 4 grams/meter.sup.2 ; said process comprising the sequential steps of:
- (1) polymerizing a primary monomer mixture consisting essentially of from about 88 to about 92 mole percent vinylidene chloride and from about 8 to about 12 mole percent methyl methacrylate in an aqueous polymerization medium containing an emulsifier, and a polymerization initiator; wherein
- (A) from about 35 to about 45 percent of the primary monomer mixture is added to the aqueous medium at a rate sufficient to continuously provided an excess of unreacted monomer in the aqueous medium, and
- (B) the remainder of the primary monomer mixture is added to the aqueous medium at a rate sufficient to continuously preclude the presence of an excess of unreacted monomer in the aqueous medium, and
- (2) following the addition of substantially all of the primary monomer mixture, adding an end-shot comonomer to the polymerization medium in an amount and under conditions sufficient to control composition drift in the crystallizable interpolymer.
- 2. The process of claim 1 wherein the end-shot comonomer is added in an amount of from about 1 to about 3 weight percent based on the total weight of the primary monomer mixture of step (1).
- 3. The process of claim 2 wherein the primary monomer mixture of step (1) consists essentially of about 90 mole percent vinylidene chloride and about 10 mole percent methyl methacrylate.
- 4. The process of claims 1, 2 or 3 wherein the end-shot comonomer is selected from the group consisting of methyl acrylate, methyl methacrylate, vinyl chloride, methacrylic acid, and vinyl acetate.
CROSS-REFERENCE TO RELATED APPLICATION
This is a continuation of application Ser. No. 126,637, filed Mar. 3, 1980, now abandoned which is a continuation-in-part of application Ser. No. 27,201, filed Apr. 5, 1979, now abandoned which in turn is a continuation-in-part of application Ser. No. 902,313, filed May 3, 1978, now abandoned.
US Referenced Citations (12)
Continuations (1)
|
Number |
Date |
Country |
Parent |
126637 |
Mar 1980 |
|
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
27201 |
Apr 1979 |
|
Parent |
902313 |
May 1978 |
|