This application claims, under 35 U.S.C. § 119, the priority of Korean Patent Application No. 10-2018-0128694 filed on Oct. 26, 2018 in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference in its entirety.
The present disclosure relates to a cucurbituril-polyethylenimine-silica complex, a method for preparing the same and a carbon dioxide absorbent containing the same. More specifically, it relates to a technology of preparing a cucurbituril-polyethylenimine-silica complex by forming a complex wherein a cucurbituril is bound to polyethylenimine and including the same inside silica, and applying the same as a carbon dioxide absorbent with superior thermal stability and prevented formation of urea.
The global energy demand relies primarily on fossil fuel. Despite the policies to tackle climate change by governments, the use of fossil fuel is expected to increase continuously in the upcoming 10 years. Fossil fuel burning is still the number one cause of carbon dioxide generation, which contributes to global warming. In 2013, the CO2-equivalent concentration was 296 ppmv, which amounts to more than 40% of increase as compared to mid-1800s. The average increase rate in the recent 10 years was 2 ppm/year. For fossil fuel to be used primarily for electric power production, it is necessary to successfully introduce a practical and cost-effective CO2 capture technology in the existing or newly constructed plants.
Carbon capture and sequestration (or storage) (CCS) is a physical process of capturing carbon dioxide artificially from its sources and storing the same before it is released into the atmosphere. CCS prevents CO2 from being released in large scale by separating, liquefying and storing CO2, and is considered the most practical way of reducing greenhouse gas.
The successful development of the CCS technology relies on the successful research, development and application of elementary technologies for capture, compression, transportation, storage, etc. of carbon dioxide. In particular, the CO2 capture technology is actively studied in developed countries including the US, Europe, Japan, etc. because it accounts for about 80% of the total cost of CCS.
While CO2 adsorption using liquid base media such as aqueous amines is widely used and mature, CO2 adsorption using solid media is considered as the CO2 capture technology of the future which is more practical and less costly. Unlike liquid absorbents, solid absorbents are advantageous in that they can be used under a very broad range of temperatures from ambient temperature to 700° C., less wastes are generated during cycles, and the consumed solid absorbents can be processed easily without undue precautionary measures for the environment.
Meanwhile, porous materials wherein pores are regularly distributed in multi-dimensional framework structures can selectively adsorb gas molecules or small organic molecules depending on the steric and chemical environment of the pores and can be used for applications such as catalysts, ion exchange, separation of mixtures, etc. (non-patent document 1).
Cucurbit[6]uril is a cyclic oligomer made of six glycoluril monomers linked by methylene bridges, synthesized from inexpensive glycoluril and formaldehyde. The structure of the compound was elucidated by W. A. Freeman and coauthors (non-patent document 2). Cucurbit[6]uril is a compound with a chemical formula of C36H36N24O12, which has an internal cavity. Cucurbituril analogues and derivatives are synthesized by the methods published in the literatures by K. Kim and coauthors (non-patent document 3) or A. Day and coauthors (non-patent document 4). In addition, a method of adsorbing gaseous or volatile compounds on cucurbituril analogues and derivatives is studied (patent document 1).
The inventors of the present disclosure have prepared a cucurbituril-polyethylenimine-silica complex wherein a cucurbituril is bound to polyethylenimine and including the same inside silica, and have noticed that it can be used as a carbon dioxide absorbent with superior thermal stability and prevented formation of urea.
Patent document 1. U.S. Pat. No. 6,869,466.
Non-patent document 1. Férey, Gérard. Chemical Society Reviews 37.1 (2008): 191-214.
Non-patent document 2. Freeman, W. A., W. L. Mock, and N. Y. Shih. Journal of the American Chemical Society 103.24 (1981): 7367-7368.
Non-patent document 3. Jon, Sang Yong, et al. Journal of the American Chemical Society 125.34 (2003): 10186-10187.
Non-patent document 4. Day, Anthony, et al. The Journal of Organic Chemistry 66.24 (2001): 8094-8100.
The present disclosure is directed to preparing a cucurbituril-polyethylenimine-silica complex wherein a cucurbituril is bound to polyethylenimine and including the same inside silica, and applying the same as a carbon dioxide absorbent with superior thermal stability and prevented formation of urea.
The present disclosure provides a cucurbituril-polyethylenimine complex wherein a cucurbituril represented by Chemical Formula 1 is bound to polyethylenimine:
wherein
n is an integer from 4 to 20,
X is O, S or NH, and
each of A1 and A2, which are identical to or different from each other, is independently H, OR, SR, NHR, COOH, O(CH2)aR or O(CH2)aSR, wherein a is an integer from 1 to 5 and R is H, a halogen, C1-C30 alkyl, C2-C30 alkenyl, C2-C30 alkynyl, C2-C30 carbonylalkyl, C3-C30 cycloalkyl, C2-C30 heterocycloalkyl, C6-C30 aryl, C6-C30 aryl C1-C30 alkyl, C2-C30 heteroaryl or C2-C30 heteroaryl C1-C30 alkyl.
The cucurbituril represented by Chemical Formula 1 may be cucurbit[6]uril, wherein n is 6, each of A1 and A2 is independently H, and X is O.
The polyethylenimine may have a molecular weight of 100-50000.
The present disclosure also provides a cucurbituril-polyethylenimine-silica complex containing a silica and the cucurbituril-polyethylenimine complex according to the present disclosure, which is included inside the silica.
The cucurbituril-polyethylenimine-silica complex may have a BET specific surface area of 1-500 m2/g.
The cucurbituril may be cucurbit[6]uril, the polyethylenimine may have a molecular weight of 500-12000, and the cucurbituril-polyethylenimine-silica complex may have a BET specific surface area of 20-60 m2/g.
The present disclosure also provides a carbon dioxide absorbent containing the cucurbituril-polyethylenimine complex according to the present disclosure.
The present disclosure also provides a carbon dioxide absorbent containing the cucurbituril-polyethylenimine-silica complex according to the present disclosure.
The present disclosure also provides a method for preparing a cucurbituril-polyethylenimine complex, which includes a step of mixing and dispersing a cucurbituril represented by Chemical Formula 1, polyethylenimine and a solvent:
wherein
n is an integer from 4 to 20,
X is O, S or NH, and
each of A1 and A2, which are identical to or different from each other, is independently H, OR, SR, NHR, COOH, O(CH2)aR or O(CH2)aSR, wherein a is an integer from 1 to 5 and R is H, a halogen, C1-C30 alkyl, C2-C30 alkenyl, C2-C30 alkynyl, C2-C30 carbonylalkyl, C3-C30 cycloalkyl, C2-C30 heterocycloalkyl, C6-C30 aryl, C6-C30 aryl C1-C30 alkyl, C2-C30 heteroaryl or C2-C30 heteroaryl C1-C30 alkyl.
The solvent may be one or more selected from methanol, ethanol, water, dimethylformamide, diethylformamide, N-methyl-2-pyrrolidone, dimethyl sulfoxide and dimethylacetamide.
The present disclosure also provides a method for preparing a cucurbituril-polyethylenimine-silica complex, which includes
(a) a step of obtaining a dispersion solution containing a cucurbituril-polyethylenimine complex by mixing and dispersing a cucurbituril represented by Chemical Formula 1, polyethylenimine and a solvent, and
(b) a step of further mixing silica in the dispersion solution:
wherein
n is an integer from 4 to 20,
X is O, S or NH, and
each of A1 and A2, which are identical to or different from each other, is independently H, OR, SR, NHR, COOH, O(CH2)aR or O(CH2)aSR, wherein a is an integer from 1 to 5 and R is H, a halogen, C1-C30 alkyl, C2-C30 alkenyl, C2-C30 alkynyl, C2-C30 carbonylalkyl, C3-C30 cycloalkyl, C2-C30 heterocycloalkyl, C6-C30 aryl, C6-C30 aryl C1-C30 alkyl, C2-C30 heteroaryl or C2-C30 heteroaryl C1-C30 alkyl.
The cucurbituril may be cucurbit[6]uril, the polyethylenimine may have a molecular weight of 500-12000, the solvent may be anhydrous methanol, a step of activating the silica at 150-250° C. for 20-30 hours in advance may be further included before the step (b), a weight ratio of the cucurbituril-polyethylenimine complex and the silica may be 1:0.5-1.5, and the cucurbituril-polyethylenimine-silica complex may have a BET specific surface area of 20-60 m2/g.
According to the present disclosure, a cucurbituril-polyethylenimine-silica complex may be prepared by forming a complex wherein a cucurbituril is bound to polyethylenimine and including the same inside silica, and it may be used as a carbon dioxide absorbent with superior thermal stability and prevented formation of urea.
Hereinafter, various aspects and exemplary embodiments of the present disclosure are described in more detail.
The present disclosure relates to a cucurbituril-polyethylenimine complex wherein a cucurbituril represented by Chemical Formula 1 is bound to polyethylenimine:
wherein
n is an integer from 4 to 20,
X is O, S or NH, and
each of A1 and A2, which are identical to or different from each other, is independently H, OR, SR, NHR, COOH, O(CH2)aR or O(CH2)aSR, wherein a is an integer from 1 to 5 and R is H, a halogen, C1-C30 alkyl, C2-C30 alkenyl, C2-C30 alkynyl, C2-C30 carbonylalkyl, C3-C30 cycloalkyl, C2-C30 heterocycloalkyl, C6-C30 aryl, C6-C30 aryl C1-C30 alkyl, C2-C30 heteroaryl or C2-C30 heteroaryl C1-C30 alkyl.
The cucurbituril-polyethylenimine complex according to the present disclosure has remarkably improved thermal stability because the cucurbituril and polyethylenimine are linked with each other. In addition, the formation of urea can be prevented through passivation of the primary amine of the polyethylenimine and remarkably superior carbon dioxide adsorption performance can be provided.
The cucurbituril represented by Chemical Formula 1 may be cucurbit[6]uril wherein n is 6, each of A1 and A2 is independently H, and X is O.
The polyethylenimine may have a molecular weight of 100-50000, specifically 300-30000, more specifically 500-12000.
The present disclosure also provides a cucurbituril-polyethylenimine-silica complex containing a silica and the cucurbituril-polyethylenimine complex according to the present disclosure, which is included inside the silica.
The cucurbituril-polyethylenimine-silica complex may have a BET specific surface area of 1-500 m2/g, specifically 10-300 m2/g, more specifically 20-60 m2/g.
The cucurbituril may be cucurbit[6]uril, the polyethylenimine may have a molecular weight of 500-12000, and the cucurbituril-polyethylenimine-silica complex may have a BET specific surface area of 20-60 m2/g. Remarkably superior carbon dioxide adsorption performance and thermal stability are achieved when the above-described conditions are satisfied.
The present disclosure also provides a carbon dioxide absorbent containing the cucurbituril-polyethylenimine complex according to the present disclosure.
The present disclosure also provides a carbon dioxide absorbent containing the cucurbituril-polyethylenimine-silica complex according to the present disclosure.
The present disclosure also provides a method for preparing a cucurbituril-polyethylenimine complex, which includes a step of mixing and dispersing a cucurbituril represented by Chemical Formula 1, polyethylenimine and a solvent:
wherein
n is an integer from 4 to 20,
X is O, S or NH, and
each of A1 and A2, which are identical to or different from each other, is independently H, OR, SR, NHR, COOH, O(CH2)aR or O(CH2)aSR, wherein a is an integer from 1 to 5 and R is H, a halogen, C1-C30 alkyl, C2-C30 alkenyl, C2-C30 alkynyl, C2-C30 carbonylalkyl, C3-C30 cycloalkyl, C2-C30 heterocycloalkyl, C6-C30 aryl, C6-C30 aryl C1-C30 alkyl, C2-C30 heteroaryl or C2-C30 heteroaryl C1-C30 alkyl.
The polyethylenimine may have a molecular weight of 100-50000, specifically 300-30000, more specifically 500-12000.
The solvent may be one or more selected from methanol, ethanol, water, dimethylformamide, diethylformamide, N-methyl-2-pyrrolidone, dimethyl sulfoxide and dimethylacetamide, although not being limited thereto. Specifically, anhydrous methanol may be used.
The present disclosure also provides a method for preparing a cucurbituril-polyethylenimine-silica complex, which includes (a) a step of obtaining a dispersion solution containing a cucurbituril-polyethylenimine complex by mixing and dispersing a cucurbituril represented by Chemical Formula 1, polyethylenimine and a solvent, and (b) a step of further mixing silica in the dispersion solution:
wherein
n is an integer from 4 to 20,
X is O, S or NH, and
each of A1 and A2, which are identical to or different from each other, is independently H, OR, SR, NHR, COOH, O(CH2)aR or O(CH2)aSR, wherein a is an integer from 1 to 5 and R is H, a halogen, C1-C30 alkyl, C2-C30 alkenyl, C2-C30 alkynyl, C2-C30 carbonylalkyl, C3-C30 cycloalkyl, C2-C30 heterocycloalkyl, C6-C30 aryl, C6-C30 aryl C1-C30 alkyl, C2-C30 heteroaryl or C2-C30 heteroaryl C1-C30 alkyl.
The cucurbituril represented by Chemical Formula 1 may be cucurbit[6]uril wherein n is 6, each of A1 and A2 is independently H, and X is O.
The polyethylenimine may have a molecular weight of 100-50000, specifically 300-30000, more specifically 500-12000.
The solvent may be one or more selected from methanol, ethanol, water, dimethylformamide, diethylformamide, N-methyl-2-pyrrolidone, dimethyl sulfoxide and dimethylacetamide, although not being limited thereto. Specifically, anhydrous methanol may be used.
The cucurbituril-polyethylenimine-silica complex may have a BET specific surface area of 1-500 m2/g, specifically 10-300 m2/g, more specifically 20-60 m2/g.
Specifically, a dispersion solution wherein the cucurbituril-polyethylenimine complex has been formed may be obtained through the step (a).
Then, a cucurbituril-polyethylenimine-silica complex wherein the formed cucurbituril-polyethylenimine complex is included inside the silica may be formed through the step (b).
A step of activating the silica at 50-500° C., specifically 70-300° C., more specifically 150-250° C., for 1-100 hours, specifically 10-50 hours, more specifically 20-30 hours, in advance may be further included before the step (b). Through this activation of the silica in advance, water inside the silica may be removed completely.
Although not stated explicitly in the following examples or comparative example, the cucurbituril-polyethylenimine-silica complexes prepared by varying the molecular weight of polyethylenimine, the solvent, the activation of the silica before the step (b), the weight ratio of the cucurbituril-polyethylenimine complex and the silica and the BET specific surface area of the cucurbituril-polyethylenimine-silica complex were investigated by transmission electron microscopy (TEM) after 3000 cycles of carbon dioxide adsorption.
As a result, when all the conditions that (i) the cucurbituril is cucurbit[6]uril, (ii) the polyethylenimine has a molecular weight of 500-12000, (iii) the solvent is anhydrous methanol, (iv) a step of activating the silica at 150-250° C. for 20-30 hours in advance is further included before the step (b), (v) the weight ratio of the cucurbituril-polyethylenimine complex and the silica is 1:0.5-1.5 and (vi) the cucurbituril-polyethylenimine-silica complex has a BET specific surface area of 20-60 m2/g were satisfied, no aggregation of the cucurbituril-polyethylenimine-silica complex even after the 3000 cycles occurred and the cucurbituril-polyethylenimine complex included inside the silica of the complex was not lost at all, unlike under other conditions. When any one of the above conditions was not satisfied, significant aggregation of the cucurbituril-polyethylenimine-silica complex occurred after the 3000 cycles and the cucurbituril-polyethylenimine complex included inside the silica of the complex was significantly lost.
Hereinafter, the preparation examples and examples according to the present disclosure are described in detail referring to the attached drawings.
A cucurbituril-PEI complex (CB[6]-PEI) (0.2 g) was obtained by adding PEI with a molecular weight of 0.6 KDa, 1.2 KDa, 1.8 KDa or 10 KDa and cucurbit[6]uril to a beaker containing anhydrous methanol (1.6 g) and then dispersing the same by stirring. Examples 1-4 correspond to the molecular weight of the PEI, 0.6 KDa, 1.2 KDa, 1.8 KDa and 10 KDa, respectively (see
A cucurbituril-PEI-silica complex wherein the CB[6]-PEI of each of Examples 1-4 was included inside silica was synthesized. First, 100 g of silica (Aldrich 381276, SA=175-225 m2/g) was activated in advance at 200° C. for 1 day to obtain 1 g of activated silica. 0.2 g of the activated silica was added to the dispersion solution of CB[6]-PEI (0.2 g) each of Examples 1-4 and then stirred further for 30 minutes. Then, a cucurbituril-PEI-silica complex (CB[6]-PEI@Silica) was synthesized by drying the final product at 70° C. for 16 hours under dynamic vacuum. Examples 5-8 correspond to the molecular weight of the PEI, 0.6 KDa, 1.2 KDa, 1.8 KDa and 10 KDa, respectively (BET SA; Example 5: 89 m2/g, Example 6: 88 m2/g, Example 7: 39 m2/g, Example 8: 49 m2/g).
After adding PEI with a molecular weight of 1.8 KDa to a beaker containing anhydrous methanol (1.6 g) and then dispersing the same by stirring, 0.2 g of the silica activated in advance in Example 5 was added and the mixture was stirred further for 30 minutes. Then, a PEI@Silica complex wherein the PEI was included inside the silica was synthesized by drying the final product at 70° C. for 16 hours under dynamic vacuum.
In order to elucidate the supramolecular structure of the cucurbituril-PEI complexes synthesized in Examples 1-4, a small amount of the cucurbit[6]uril-PEI complex was dissolved in D2O and 1D and 2D nuclear magnetic resonance (1H-NMR) spectra were obtained. Solid NMR spectra were obtained to investigate the CO2 adsorption amount and regeneration performance of the cucurbit[6]uril-PEI@Silica complex. Thermogravimetric analysis (TGA) data were obtained while heating from 25° C. to 800° C. at a rate of 10° C./min under nitrogen atmosphere. Carbon dioxide adsorption isotherms were measured through a volumetric method after regenerating the sample at 110° C. under vacuum. Carbon dioxide adsorption amount and repeated adsorption-regeneration cycles depending on temperature were measured via a weight method of magnetic suspension balance.
Referring to
And, referring to
Referring to
The amount of the cucurbit[6]uril-PEI complex included in the silica can be seen from
The CO2 adsorption amount depending on the cucurbit[6]uril-PEI complexes can be confirmed from
Referring to
Referring to
Referring to
Referring to
Referring to
Referring to
According to the present disclosure, a cucurbituril-polyethylenimine-silica complex may be prepared by forming a complex wherein a cucurbituril is bound to polyethylenimine and including the same inside silica, and it may be used as a carbon dioxide absorbent with superior thermal stability and prevented formation of urea.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2018-0128694 | Oct 2018 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6869466 | Day et al. | Mar 2005 | B2 |
| Number | Date | Country |
|---|---|---|
| 1020110006073 | Jan 2011 | KR |
| Entry |
|---|
| Carmen Stoffelen and Jurriaan Huskens, “Size-tunable supramolecular nanoparticles mediated by ternary cucurbit[8]uril host-guest interactions”, Chem. Commun., 2013, 49, 6740-6742. (Year: 2013). |
| Li et al., “An eco-friendly in situ activatable antibiotic via cucurbit[8]uril-mediated supramolecular crosslinking of branch polyethylenimine”, Chem. Commun. , 2017, 53, 5870-5873. (Year: 2017). |
| Midhun Mohan et al., “Surface modification induced enhanced CO2 sorption in cucurbit[6]uril, an organic porous material,” Phys. Chem. Chem. Phys., 2017, pp. 25564-25573, vol. 19. |
| Anthony Day et al., “Controlling Factors in the Synthesis of Cucurbituril and Its Homologues”, J. Org. Chem., 2001, pp. 8094-8100, vol. 66, No. 24, American Chemical Society. |
| Gerard Ferey, “Hybrid porous solids: past, present, future,” Chemical Society Reviews, 2007, pp. 191-214, vol. 37, The Royal Society of Chemistry. |
| Sang Yong Jon et al., “Facile Synthesis of Cucurbit[n]uril Derivatives via Direct Functionalization: Expanding Utilization of Cucurbit[n]uril”, J. Am. Chem. Soc., 2003, pp. 10186-10187, American Chemical Society. |
| W. A. Freeman et al., “Cucurbituril”, J. Am. Chem. Soc., 1981, pp. 7367-7368, American Chemical Society. |
| Number | Date | Country | |
|---|---|---|---|
| 20200129957 A1 | Apr 2020 | US |