Patent Application
20210403755
Corrosion is a major cause of failures to the metallic structures, such as bridges, railways, pipelines, and others; the failures of these infrastructures can cause catastrophic accidents that result in huge loss of economy and threatening lives of people. Khatoon et al., ACS Appl. Mater. Interfaces, 11(2):2374-2385, 2018. To address this issue, polymer-based coatings are the most widely used protective films for corrosion control and mitigation of the metallic substrate in civil, mechanical, and aerospace engineering. Wang et al., Compos. Part B Eng., 176(1):107103, 2019.
Among these coatings, epoxy resins are the most widely used protective films as they have good barrier performance, mechanical properties, and low cost. Dittanet et al., Int. J. Adhes. Adhes., 78:74-82, 2017; Ma et al., Bioresources, 12(2):2912-2929, 2017. However, despite many efforts devoted to improving the performance of epoxy-based composites, high-performance multifunctional coatings still face considerable challenges. For example, the hydrophilic surface of the epoxy attracts and absorbs water and other liquids, which reduces the barrier property against corrosive elements. In addition, the performance of the epoxy coatings is significantly degraded due to micropores and cracks generated by shrinkage during the curing process. Wang et al., Nanomaterials, 9(10):1476, 2019. The existing micropores/cracks lead to a reduced barrier property, which reduces the diffusion pathway and allows corrosive media to penetrate the coating film to initiate corrosion damages. Zhang et al., J. Polym. Res., 25(5):130, 2018. Moreover, the micro-cracks weaken the mechanical properties of the coatings, and they can easily become large defects during the service life of the coating, which dramatically compromises the damage tolerance and long-term performance of the coating. Wang et al., Compos. Part B Eng., p. 107103, 2019.
Inclusion of nanoparticles as nanofillers is one of the most promising approaches that enables synthesizing high-performance nanocomposite coatings with excellent corrosion resistance and mechanical strength. Nanofillers, such as carbon nanotubes (CNT), graphene nanoplatelet (GNP), or nanosilica (NS), have led to dramatic improvements of coating performance in terms of their tribological, mechanical, and electrochemical properties. Shen et al., Prog. Org. Coat., 90:139-146, 2016; Jeon et al., J. Ind. Eng. Chem., 19(3):849-853, 2013; Cui et al., Mater. Des., 49:279-284, 2013; Xie et al., Mater. Sci. Eng. R Rep., 49(4):89-112, 2005; Potts et al., Polymer, 52(1):5-25, 2011; Liu et al., J. Mater. Sci. Technol., 32(5):425-431, 2016; Wan et al., Compos. Sci. Technol., 82:60-68, 2013; Liu et al., Compos. Part B Eng., 42(8):2170-2175, 2011; Kang et al., Appl. Surf. Sci., 258(17):6384-6390, 2012; Conradi et al., Appl. Surf. Sci., 292:432-437, 2014; Yue et al., Carbon, 78:268-278, 2014; Nuruddin et al., Polym. Polym. Compos., 25(4):273, 2017; Xiang et al., Mater. Lett., 209:551-554, 2017; Porwal et al., Ceram. Int., 40:12067-12074, 2014; Pourhashem et al., Surf. Coat. Technol., 311:282-294, 2017.
However, there are some limitations in utilizing single nanofiller composites as high-performance materials. Yue et al., Carbon, 78:268-278, 2014; Nuruddin et al., Polym. Polym. Compos., 25(4):273, 2017; Xiang et al., Mater. Lett., 209:551-554, 2017; Kumar et al., Ultrason. Sonochem., 41:37-46, 2018; Hosur et al., J. Reinf. Plast. Compos., 36(9):667-684, 2017.
First, a single filler system can enhance some properties of a composite but may also have a negative impact on other performance aspects. Second, due to the strong van der Walls forces between the particles, severe agglomeration was often observed in nanocomposites having a low content of nanofillers. Therefore, the dispersion level of the particles plays a vital role in the performance of the nanofiller reinforced composite. Pourhashem et al., Surf. Coat. Technol., 311:282-294, 201; Di et al., J. Taiwan Inst. Chem. Eng., 64:244-251, 2016. For example, the addition of carbon nanotubes (CNT) increases the mechanical strength, such as abrasion and tensile strength, of composites but has a negative effect on corrosion barrier performance. Cui et al., Mater. Des., 49:279-284, 2013; Shen et al., Prog. Org. Coat., 90:139-146, 2016; Jeon et al., J. Ind. Eng. Chem., 19(3); 849-853, 2013. With well-dispersed graphene (GNP) nanoplatelets, improved corrosion resistance can be observed in the nanocomposites. However, the mechanical properties, such as wear resistance, and tensile strength, can barely be improved or even reduced by the presence of GNP particles. Potts et al., Polymer, 52(1):5-25, 2011; Liu et al., J. Mater. Sci. Technol., 32(5):425-431, 201; Wan et al., Compos. Sci. Technol., 82:60-68, 2013. The incorporation of nano-silica (NS) particles can slightly enhance both the corrosion resistance and elasticity, but decrease the mechanical strength and Young's modulus of the polymer. Kang et al., Appl. Surf. Sci., 258(17):6384-6390, 2012; Conradi et al., Appl. Surf. Sci., 292:432-437, 2014; Liu, et al., Compos. Part B Eng., 42(8):2170-2175, 2011. Clearly, single nanofiller provided significant improvements in coating properties in certain areas, but may not cover multiple functionalities, as expected for metallic structures, that may suffer from high wear loss and/or fouling, as well as high corrosion.
To address the limitations of single filler reinforced composite, surface treatments and/or hybrid nanofiller systems were introduced by researchers, as these approaches can effectively solve the drawbacks of the single fillers. Pourhashem et al., Surf. Coat. Technol., 311:282-294, 2017; Hosur et al., J. Reinf. Plast. Compos., 36(9):667-684, 2017; Xiang et al., Mater. Lett., 209:551-554, 2017. For example, a commonly used approach to overcome the drawbacks of a single filler system is surface treatment of nanofillers. Ramezanzadeh et al. developed polyaniline-cerium oxide coated graphene oxide (GO) nanofillers to enhance the corrosion protection of an epoxy resin. Ramezanzadeh et al., Corros. Sci., 137:111-126, 2018. The modified graphene oxide nanosheets had better dispersion and stronger barrier performance enhancement, compared with raw GO particles. Sari et al. successfully used polyester-amide hyperbranched polymer (HBP) to modify nanoclay particles, and the modified particles had improved dispersion in an epoxy resin, resulting in improved corrosion resistance compared with unmodified nanoclay. Sari et al., Corros. Sci., 92:162-172, 2015. However, these techniques are generally either time-consuming or require an extensive amount of chemicals or energy. Rider et al., Carbon, 94:971-981, 2015; Cha et al., Compos. Part B Eng., 129:169-179, 2017; Kim et al., Carbon Lett. Carbon Lett, 16(1):34-40, 2015.
Indeed, surface treatments generally only increase the level of reinforcement in a single filler system, without providing additional positive enhancements into the coating. For example, the addition of CNT provided improved tensile properties, but, due to the severe agglomeration, material degradation was observed once the content of CNT reached a critical value. With the surface treatment, the tensile strength was further increased by the modified CNT. Cui et al., Mater. Des., 49:279-284, 2013; Lee et al., Compos. Part Appl. Sci. Manuf., 69:132-138, 2015; Liu et al., Compos. Sci. Technol., 167:331-338, 2018. However, no other enhanced properties were reported in these studies, such as corrosion resistance, water-repellency, properties which are also critical for a protective coating. The above observations revealed the limitation of using a surface-treated single filler system to fabricate multifunctional high-performance coatings.
Besides surface treatment, hybrid nanofiller materials have been used to explore the synergistic effect of the nanofillers, thus, developing multifunctional coatings based on hybrid nanofiller composites. Yue et al., Carbon, 78:268-278, 2014; Nuruddin et al., Polym. Polym. Compos., 25(4):273, 2017; Xiang et al., Mater. Lett., 209:551-554, 2017. The strategy of using a hybrid filler system, in which nanofillers with different geometric shapes are integrated, has been proven to be an effective method to fabricate nanocomposites that overcome the limitations of the single filler system. Nuruddin et al., Polym. Polym. Compos., 25(4):273, 2017. The presence of another nanofiller has led to a better dispersion level of the nanoparticles. Yue et al., Carbon, 78:268-278, 2014; Nuruddin et al., Polym. Polym. Compos., 25(4):273, 2017; Kumar et al., Ultrason. Sonochem., 41:37-46, 2018. The hybrid filler system could form a more robust nanoparticle network with better dispersion and superior improvements compared with a polymer containing a single filler; in addition, with suitable mixture design, the reinforcements of each single filler can be integrated in the hybrid nanofiller system. To conclude, better mechanical, electrical, and barrier properties of composites were observed in these nanocomposites due to the superior dispersion of the nanoparticles. Yue et al., Carbon, 78:268-278, 2014; Nuruddin et al., Polym. Polym. Compos., 25(4):273, 2017.
Recently, many successful studies demonstrated the advantages of utilizing hybrid nanofillers in nanocomposite coatings. For instance, Yue et al. successfully utilized a CNT/GNP hybrid system into the epoxy matrix, and both the mechanical and electrical behaviors were enhanced in the developed nanocomposites. Yue et al., Carbon, 78:268-278, 2014. Nuruddin et al. investigated the effect of graphene nanoplatelets and cellulose nanofibers on the mechanical properties of epoxy polymer composites. Nuruddin et al., Polym. Polym. Compos., 25(4):273, 2017. The hybrid filler system exhibited improved mechanical and thermo-mechanical properties. The combination of 0.1 wt. % GNP and 0.5 wt. % cellulose nanofibers provided the best performance; however, degradation was observed when the filler content exceeded the value above. Xiang et al. studied the tensile, electrical, and barrier properties of three types of binary nanofillers systems, with combinations of CNT, GNP, and carbon black (CB). Xiang et al., Mater. Lett., 209:551-554, 2017. Excellent tensile and barrier property performance were obtained using combinations of CNT/GNP and GNP/CB, respectively. Hosur et al. pointed out that, compared with the single filler reinforced epoxy, the storage modulus and flexural modulus improved using the hybrid nanofillers that contained carbon nanotube and nanoclay. Hosur et al., J. Reinf. Plast. Compos., 36(9):667-684, 2017. Kumar et al. examined the performance of epoxy with CNT/TiO2 nanofiller. Kumar et al., Ultrason. Sonochem., 41:37-46, 2018. Superior improvements in tensile and anti-corrosion properties were obtained with the addition of the hybrid nanofiller, and the presence of TiO2 prevented the re-agglomeration of CNT. Among these hybrid filler systems, the combination of graphene/silica was more desirable as both mechanical and corrosion protection properties were improved by the synergistic effect of hybrid nanofillers. Porwal et al., Ceram. Int., 40:12067-12074, 2014; Pourhashem et al., Surf. Coat. Technol., 311:282-294, 2017.
While a few investigations studied the combination of graphene oxide/SiO2 (Ramezanzadeh et al., Chem. Eng. J., 303:511-528, 2016; Wang et al., Express Polym. Lett., 6(4):299-307, 2012), there is still a lack of research studies on graphene nanoplatelets/SiO2 hybrid filler systems. Yu et al. prepared a hybrid filler system with SiO2 particles on the surface of graphene nanoplatelets. Yu et al., Fibers Polym., 17(3):453-459, 2016. However, due to the different focus of the study, the research was particularly concerned with the tensile properties of the composites. And Pourhashem et al. studied the influence of incorporating SiO2 nanoparticles into graphene oxide (GO) nanosheets to reinforce epoxy resin. Pourhashem et al., Surf Coat. Technol., 311:282-294, 2017. The nanocomposite with SiO2/GO hybrid nanofillers have greater corrosion resistance compared with the one with GO, and improved mechanical properties were also observed. Hybrid filler nanocomposites must still be evaluated for their electrochemical, mechanical, and tribological properties, which are critical in real-world applications, especially anti-corrosion coatings.
As mentioned, the hydrophilic surface of epoxy coatings is a major challenge while protecting the substrate against water and other liquids. Despite the advantages of nanofiller reinforcement, the incorporation of nanofillers can barely improve the hydrophobicity of the coating as the major content of the nanocomposite coating is epoxy, especially when the added nanofillers are hydrophilic, such as nanoclay and cellulose nanofiber. On the other hand, even with nanofillers with a hydrophobic surface, like carbon nanotube and fullerene, the enhancement of water repellency is limited by the low concentration of the nanofiller in the composite (<3 wt. %); and increasing the content of the nanofiller results in material degradation due to severe agglomeration.
Therefore, besides nanofiller reinforcement, high-performance coatings could be further reinforced through surface modification by incorporation of the concept of superamiphiphobicity, as it is capable of self-cleaning or anti-fouling. Chen et al., Adv. Funct. Mater., 25:1035-1041, 2015. Some recent efforts were taken using surface-treated particles to develop the superamphiphobic surface. Li et al., Chem. Eng. J., 246:238-243, 2014; Zhou et al., Adv. Funct. Mater., 23:1664-1670, 2013; He et al., Soft Matter, 7:6435, 2011; Zhou et al., Adv. Funct. Mater., 27:1604261, 2017. Li reported single-step approach to fabricate superamphiphobic SiO2 nanoparticles by imparting perfluorodecyltrichloro group from perfluorodecyltrichlorosilane (FDTS). Li et al., Chem. Eng. J., 246:238-243, 2014. Then the functionalized SiO2 nanoparticle solution was sprayed on a paper surface. Zhou prepared a superamphiphobic surface on a fabric surface by a two-step wet-chemistry method. Zhou et al., Adv. Funct. Mater., 23:1664-1670, 2013. The fabric was applied with a silica sol with tetraethylorthosilicate (TEOS) and FAS in ethanol first, then dipped coating to a PVDF-HFP/dimethylformamide solution. The coated fabric showed a contact angle of 172° and 160° to water and hexadecane, correspondingly. However, these strategies were still unable to ensure durable, reliable treatments in long run. As a result, contact angle of the treated surface could be quickly dropped, if the functionalized particles on the surface were grinded out by mechanical stresses or were exposed to the moist environment to certain periods. Parallel to the treated particles, modification of the epoxy resins is another promising approach to increase the hydrophobicity. Research studies demonstrated the intercalation of polydimethylsiloxane (PDMS) with epoxy and resulted a significant increase in hydrophobicity of the epoxy coating. The PDMS-epoxy coating system has high water contact angle due to the low surface energy that PDMS introduced, with a simple modification process. Ammar et al., Surf. Coat. Technol., 324:536-545, 2017; Zhang et al., Appl. Surf. Sci., 436:405-410, 2018; Yang et al., Appl. Surf Sci., 401:146-155, 2017. The application of using these two approaches to prepare a superamphiphobic coating for metallic substrate is unknown.
The invention is directed to a nanofiller-reinforced PDMS/epoxy coating system with excellent hydrophobicity, anti-corrosion property, mechanical strength, and damage tolerance. The prepared coatings were suitable for varied application methods, including drawdown, air-spray, brush, and dip coating techniques. The invention is also
The invention also relates to a robust self-cleaning nanoparticle-polymer coating, which may be used, for example, in oil/gas pipeline applications, with specific functionality of: 1) high superamphiphobic surface, 2) modified resin, and 3) hybrid nanofiller reinforcement. The hybrid nanofiller reinforcement provides significantly improved mechanical and corrosion protection properties, while the superamphiphobic surface and modified resin provides superior water and oil repellency. The new high-performance coating has a significant advantage over existing coatings since it can be tailored to provide multifunctional protection for extended long-term civil infrastructure performance against corrosion and fouling issues.
The invention relates to a curable coating composition comprising, consisting essentially of, consisting of:
The invention also relates to a cured coating composition comprising, consisting essentially of, or consisting of the curable coating composition of the invention.
The invention further relates to a substrate or an object coated with the curable coating composition of the invention.
The invention also relates to a method for making the curable coating composition of the invention.
The invention further relates to a method for coating the surface of a metal or non-metal substrate comprising, consisting essentially of, or consisting of the steps of:
applying the nanoparticle-polymer composition of the curable coating composition of the invention to at least a part of the surface of the substrate to form a first coated surface, and
curing the first coated surface to form a cured first coated surface,
optionally, applying the superamphiphobic nanoparticles of the curable coating composition of the invention to the cured first coated surface to form a second coated surface, and
curing the second coated surface.
The invention relates to a curable coating composition comprising, consisting essentially of, consisting of:
Nanoparticle-Polymer Composition
The epoxy resin may be selected from the group consisting of bisphenol-based resin, novolac resin, aliphatic resin, halogenated resin, diluent resin, glycidol amine resin, and mixtures thereof. Preferably, the epoxy resin is bisphenol A/epichlorohydrin epoxy resin (e.g., EPON™ 828, available from Hexion, Inc.). The epoxy resin may be present in the nanoparticle-polymer composition in an amount ranging from about 35-65 wt. %, more preferably about 42-59 wt. %, most preferably about 46-54 wt. %, based on the total solid content of the nanoparticle-polymer composition.
The GNP may have an average specific surface area of about 15-750 m2/g (e.g., 100-700 m2/g, 200-600 m2/g, 300-500 m2/g) and an average thickness of about 1-15 nm (e.g., 2-12 nm, 4-10 nm, 6-8 nm). Preferably, the GNP have a specific surface area of about 500-700 m2/g and an average thickness of about 8-12 nm. Exemplary GNP that may be used are available from Cheap Tubes, Inc. and Sigma-Aldrich (e.g., xGnP M-5 having 5 μm particle size, surface area of 120-150 m2/g; xGnP C-750, having a surface area of 750 m2/g, graphene powder (CAS No. 1034343-98-0)).
The NS may be selected from silicon dioxide nanopowders. The silicon dioxide nanopowders may have a particle size of about 20 nm or less. Preferably, the silicon dioxide nanopowders have a particle size ranging from about 5-20 nm. For example, the silicon dioxide nanopowders may have a particle size ranging from about 10-20 nm. Exemplary NS that may be used are available from Sigma-Aldrich (e.g., CAS No. 7631-86-9).
The ratio of GNP:NS in the hybrid nanofiller may range from 25:75 to 75:25, such as 30:70 to 70:30, 35:65 to 65:35, 40:60 to 60:40, 45:55 to 55:45, 50:50. Preferably, the ratio of GNP:NS is 50:50.
The hybrid nanofiller may be present in the nanoparticle-polymer composition in an amount ranging from about 0.1-10 wt. %, more preferably about 0.5-5 wt. %, most preferably about 1-2.5 wt. %, based on the total solid content of the nanoparticle-polymer composition. For example, the hybrid nanofiller may be present in the nanoparticle-polymer composition in an amount of about 1 wt. %.
The hybrid nanofiller may have a particle size ranging from about 40-600 nm (e.g., 50-500 nm, 60-400 nm, 70-300 nm, 80-200 nm, 90-100 nm), preferably 70-120 nm.
The PDMS may have a molecular weight ranging from about 400
The PDMS may be, for example, a hydroxy-terminated PDMS or a monocarbinol-terminated PDMS.
The PDMS is present in amount ranging from about 4-18 wt. % (e.g., 5-16 wt. %, 6-14 wt. %, 7-12 wt. %, 8-10 wt. %), based on the total solid content of the nanoparticle-polymer composition. Preferably, the PDMS is present in amount ranging from about 7-13 wt. %, based on the total solid content of the nanoparticle-polymer composition.
The silane coupling agent may be at least one aminosilane, such as 3-aminopropyltriethoxysilane (APTES), (3-aminopropyl)-diethoxy-methylsilane (APDEMS), (3-aminopropyl)-dimethyl-ethoxysilane (APDMES), and (3-aminopropyl)-trimethoxysilane (APTMS). Preferably, the silane coupling agent is APTES.
The silane coupling agent is present in amount ranging from about 1-6 wt. %, more preferably about 2-4 wt. %, based on the total solid content of the nanoparticle-polymer composition.
The nanoparticle-polymer composition may also not contain a solvent.
Superamphiphobic Nanoparticles
The superamphiphobic nanoparticles may comprise, consist essentially of, or consist of the reaction product of the silicon dioxide nanoparticles and the FDTS, FDDTS, or mixtures thereof.
The silicon dioxide nanoparticles may be the same or different as the nano-silica (NS) used in the nanoparticle-polymer composition.
Optional Solvents, Curing Agents, and Catalysts
The nanoparticle-polymer composition and/or the superamphiphobic nanoparticles can be prepared in the presence of at least one optional solvent, at least one curing agent, and/or at least one optional catalyst. The type and amount of solvent, curing agent, and catalyst used to prepare the nanoparticle-polymer composition and the superamphiphobic nanoparticles may be the same or different. The solvent, curing agent, and catalyst may be used during any step of the synthesis of the curable coating compositions of the invention.
The solvent that may be used in the invention includes, but is not limited to, hexane, ethanol, toluene, xylenes, n-butyl acetate (nBA), t-butyl acetate (TBA), acetone, methyl ethyl ketone (MEK), methyl n-amyl ketone (MAK), N-methyl pyrrolidone (NMP), ethyl 3-ethoxyproprionate (EEP), and mixtures thereof. The amount of solvent used may vary. For example, the solvent may be present in an amount of about 30%, preferably about 20%, and more preferably about 15% or less. A mixture of two or more solvents may be used. In the case of the use of a mixture of solvents, the amount of solvents used may be calculated such that the final curable coating composition has a target of about 70%, preferably about 80%, and more preferably about 85%, solid in 50/50 w/w solvent blend of the solvent mixture. One or more solvents may be used to solubilize the curable coating compositions. The curable coating compositions of the invention may also contain no solvent.
The curing agent that may be used in the invention can be, for example, aliphatic amines, cycloaliphatic amines, anhydrides, anhydrides, polyamides, or mixtures thereof. Preferably, the curing agent is a polyamide and/or a polyamine (e.g., EPIKURE™ Curing Agent 3175 and EPIKURE™ Curing Agent 3164 from Hexion, Inc.). The curing agent may be present in an amount ranging from about 19-38 wt. % (e.g., 24-36 wt. %, 26-34 wt. %, 29-32 wt. %), based on the total solid content of the curable coating composition.
The catalyst that may be used in the invention can be organometallic complexes, organic bases, or mixtures thereof. Examples of organometallic compounds include, but are not limited to, dibutyl tin dilaurate, dibutyl tin diacetate, dimethyl-dineodacanoate tin (DMDN-Sn), di-n-butyl bis(2-ethylenehexanoate) (DBBE-Sn), tin (II) oleate, tetrakis(acetoxydibutyl tinoxy)silane (TKAS), bismuth carboxylate, and compounds of zirconium and aluminum, such as, but not limited to, K-Kat® 4205, K-Kat® 5218, and K-Kat® XC-6212. Examples of organic base catalysts includes, but is not limited to, 1,4-diazabicyclo[2.2.2]octane, which is sold under the DABCO® trade name by Air Products. The amount of catalyst used may vary. For example, the catalyst may be present in an amount ranging from about 0.04-0.13 wt. %, preferably about 0.06-0.08 wt. %, and more preferably about 0.07 wt. %, based on the total solid content of the curable coating composition.
Pigments, Additives, Solvents, and Fillers
Pigments and other additives known in the art to control coating rheology and surface properties can also be incorporated in the curable coating composition of the invention. For example, a curable coating composition of the invention may further contain coating additives. Such coating additives include, but are not limited to, one or more leveling, rheology, and flow control agents such as silicones, fluorocarbons, or cellulosics; extenders; reactive coalescing aids such as those described in U.S. Pat. No. 5,349,026, incorporated herein by reference; plasticizers; flatting agents; pigment wetting and dispersing agents and surfactants; ultraviolet (UV) absorbers; UV light stabilizers; tinting pigments; colorants; defoaming and antifoaming agents; anti-settling, anti-sag and bodying agents; anti-skinning agents; anti-flooding and anti-floating agents; biocides, fungicides and mildewcides; corrosion inhibitors; thickening agents; or coalescing agents. Specific examples of such additives can be found in Raw Materials Index, published by the National Paint & Coatings Association, 1500 Rhode Island Avenue, N.W., Washington, D.C. 20005. Further examples of such additives may be found in U.S. Pat. No. 5,371,148, incorporated herein by reference.
Examples of flatting agents that may be used in the coatings of the invention include, but are not limited to, synthetic silica, available from the Davison Chemical Division of W. R. Grace & Company as SYLOID®; polypropylene, available from Hercules Inc., as HERCOFLAT®; synthetic silicate, available from J. M. Huber Corporation, as ZEOLEX®.
Examples of viscosity, suspension, and flow control agents that may be used in the curable coating compositions of the invention include, but are not limited to, polyaminoamide phosphate, high molecular weight carboxylic acid salts of polyamine amides, and alkylene amine salts of an unsaturated fatty acid, all available from BYK Chemie U.S.A. as ANTI TERRA®. Further examples include, but are not limited to, polysiloxane copolymers, polyacrylate solution, cellulose esters, hydroxyethyl cellulose, hydroxypropyl cellulose, polyamide wax, polyolefin wax, hydroxypropyl methyl cellulose, polyethylene oxide, and the like.
Solvents may also be added to the curable coating compositions of the invention to reduce the viscosity, some of which may also be used in the synthesis of the nanoparticle-polymer composition and/or the superamphiphobic nanoparticles, as discussed above. For example, hydrocarbon, ester, ketone, ether, ether-ester, alcohol, or ether-alcohol type solvents may be used individually or in mixtures. Examples of solvents that can be added to the curable coating compositions of the invention include, but are not limited to benzene, toluene, xylene, aromatic 100, aromatic 150, acetone, methylethyl ketone, methyl amyl ketone, butyl acetate, t-butyl acetate, tetrahydrofuran, diethyl ether, ethylethoxy propionate, isopropanol, butanol, butoxyethanol, and so on. Alternatively, the solvent system may include water or be water-based (>50% water in the solvent system).
Fillers may also be added to the curable coating compositions of the invention, including, but not limited to, calcium carbonate such as calcite, dolomite, talc, mica, feldspar, barium sulfate, kaolin, nephelin, silica, perlite, magnesium oxide, and quartz flour, etc. Fillers (and pigments) may also be added in the form of nanotubes or fibers, thus, apart from the before-mentioned examples of fillers, the curable coating composition may also comprise fibers, e.g., those generally and specifically described in WO 00/77102, incorporated herein by reference.
The invention also relates to a method for making the curable coating composition of the invention.
The invention also relates to a cured coating composition comprising, consisting essentially of, or consisting of the curable coating composition of the invention. The curable coating compositions of the invention may be cured at ambient or elevated (e.g., about 80° C.) temperatures.
The invention further relates to a metal or non-metal substrate or an object coated with the curable coating composition of the invention. Preferably, the object is a metal substrate (e.g., a steel oil pipe or a steel gas pipe).
The invention also relates to a method for coating the surface of a substrate (e.g., a steel oil pipe or a steel gas pipe) comprising, consisting essentially of, or consisting of the steps of:
applying the nanoparticle-polymer composition of the curable coating composition of the invention to at least a part of the surface of the substrate to form a first coated surface,
curing the first coated surface to form a cured first coated surface,
optionally, applying the superamphiphobic nanoparticles of the curable coating composition of the invention to the cured first coated surface to form a second coated surface, and
curing the second coated surface.
The curable coating composition of the invention is typically applied to at least a part of the surface of a substrate. The term “applying” is used in its normal meaning within the paint industry. Thus, “applying” is conducted by means of any conventional means, e.g., by brush, by roller, by spraying (e.g., convention air-atomized spray, airless spray, HVLP), by dipping, by drawdown, etc. The commercially most interesting way of “applying” the curable coating composition of the invention is by spraying. Hence, the coating composition is preferably sprayable. Spraying is effected by means of conventional spraying equipment known to the person skilled in the art. The coating is typically applied in a dry film thickness of about 50-600 μm, such as about 50-500 μm (e.g., 75-400 μm, 20-150 μm, 30-100 μm).
The term “at least a part of the surface of a substrate” refers to the fact that the curable coating composition of the invention may be applied to any fraction of the surface (or, for that matter, the entire surface). For many applications, the curable coating composition is at least applied to the part of the substrate where the surface may encounter water.
The term “substrate” means a solid material onto which the curable coating composition is applied. The substrate typically comprises a metal such as steel, iron, aluminum, or glass- or carbon-fiber composite, but also includes wood, plastic, and glass. The substrate may be a metal substrate, in particular a steel substrate. The metal substrate may be coated with an anticorrosive coating such as an anticorrosive epoxy-based coating, e.g., cured epoxy-based coating, or a shop-primer, e.g., a zinc-rich shop-primer. The substrate may also be a glass-fiber reinforced polyester substrate, optionally coated with an epoxy primer coating. The substrate may be at least a part of the outermost surface of a marine structure.
The term “surface” is used in its normal sense, and refers to the exterior boundary of an object. Particular examples of such surfaces are the surface of marine structures, such as vessels (including, but not limited to, boats, yachts, motorboats, motor launches, ocean liners, tugboats, tankers, container ships and other cargo ships, submarines, and naval vessels of all types), pipes, shore and off-shore machinery, constructions and objects of all types such as piers, pilings, bridge substructures, water-power installations and structures, underwater oil well structures, nets, and other aquatic culture installations, and buoys, etc.
The surface of the substrate may be the “native” surface (e.g., the steel surface). However, the substrate is typically coated, e.g., with an anticorrosive coating, so that the surface of the substrate is constituted by such a coating. When present, the anticorrosive coating is typically applied in a total dry film thickness of 20-200 μm, such as 50-150 μm, e.g., 80-125 μm. Alternatively, the substrate may carry a paint coat, e.g., a worn-out fouling release paint coat, or similar. One advantage of the curable coating compositions described herein is that they can be applied directly onto the primed surface without a tie-coat. However, the curable coating compositions described herein can also be applied onto a tie-coat if desired.
The method of the invention may result in the substrate having improved mechanical protection properties, corrosion protection properties, water repellency, and/or oil repellency.
Materials
All chemicals and nanofiller were purchased commercially and used as received without any purifications. The silicon dioxide nanopowders were purchased from Sigma-Aldrich Inc., USA; with a particle size of 10-20 nm and a surface area of 175-225 m2/g. Graphene nanoplatelets with an average specific surface area of 500-700 m2/g and an average thickness of 8-12 nm were used as one type of nanofiller and were purchased from Cheap Tubes Inc., USA. EPON™ Resin 828 resin and EPIKURE™ Curing Agent 3175 were obtained from Hexion Inc., USA, and were used as the epoxy resin and curing agent, respectively. EPON™ Resin 828 is a bisphenol A/epichlorohydrin derived liquid epoxy resin and can provide good mechanical, adhesive, dielectric and chemical resistance properties when crosslinked with appropriate curing agents. EPIKURE™ Curing Agent 3175 was used as the curing agent of EPON™ Resin 828.
Hydroxy-terminated poly(dimethylsiloxane) (PDMS, 0.97 g/mL at 25° C.), 3-aminopropyltriethoxysilane (APTES, 0.97 g/mL at 25° C.), dibutyl tin dilaurate (DBTDL, 1.066 g/mL at 25° C.), hexadecane, hexane, and ethanol were purchased from Sigma-Aldrich (USA). 1H,1H,2H,2H-Perfluorodecyltrichlorosilane (FDTS, 1.540 g/mL at 25° C.) was obtained from Alfa Aesar (USA). S-36 steel Q-panels with a surface roughness of 0.5˜1.14 μm were used as metallic substrates for the developed coatings (0-Lab, USA).
As illustrated in
1.2.1 Electrochemical Corrosion Resistance Test
Electrochemical impedance spectroscopy (EIS) test was used to characterize the anticorrosion barrier performance of the coatings. The main applications of EIS test are coating performance evaluation, electrochemical mechanisms and rate analysis, and barrier performance. Gamry Reference 600 Spectroscopy was used to measure the impedance vs. frequency curve, and the obtained curves were used to study the corrosion resistance of the test coatings. During the test, a 3-cm diameter O-ring glass tube with silicon joint was clamped on the test panel. A saturated calomel electrode reference electrode was used for the reference electrode; thus, a platinum mesh was employed as the counter electrode and steel panel was worked as the working electrode. In order to confirm the longer-term corrosion resistance performance, salt spary tests was applied as accelerated durability test. The samples were exposed to a salt fog atmosphere in a Q-Lab Corporation Q-Fog CCT chamber with ASTM B117 specifications. The impedance curves were measured after 100 and 500 hours exposure to evaluate their overall long-term performance. As shown in
1.2.2 Abrasion Resistance Test
Taber Abraser method was applied to examine the wear resistance of the nanocomposites by the selected abrading wheels and applied loads. With the applied load and the rotation of sample, a circular abrasion mark with an area approximately 30 cm2 will be formed by the abrading wheel. The abrasion resistance is calculated as the mass loss in a specified number of abrasion cycles with the selected loads. Each specimen was tested for a total of 1000 cycles, 1000 g of the load was used during the test, and the rotational speed is 72 rpm with two CS-10 abrading wheels.
1.2.3 Coupon Tension Test
The determination of the tensile properties of CNT reinforced polymer coating was done by the coupon tensile test (ASTM D638). The test was performed by Shimadzu's EZ-X tester (with a testing speed of 1 mm/min). The hardened coupon specimens were clamped at two ends by the grips during the test. Tensile strength was applied to elongate the specimens during the test until the specimens were broke in the narrow cross-sectional test section. Maximum tensile strength and Young's modulus were determined for each specimen.
1.2.4 Water Contact Angle Test
Contact angle test (ASTM D7334) was employed to determine the water-repellency properties indirectly as the obtained results indicate the ability of a liquid to maintain contact with the coated surface. Images were captured by the camera and processed by a computer to calculate the angle between the drop and the substrate.
1.2.5 Nanocomposite Characterization
The particle size distribution of the nanofillers was investigated by dynamic light scattering (DLS) with a submicron particle sizer (Nicomp 380). Furthermore, JEM-2100 high-resolution analytical TEM instrument was used to examine the morphologies and microstructures of single and hybrid nanofillers. The nanofiller were dispersed into ethanol with a proper weight ratio before TEM observation. The size and shape of nanofillers were studied by the obtained TEM images. The nanoparticle structure of the nanofiller were analyzed by Powder X-Ray Diffraction (XRD) patterns which was recorded by a Bruker AXS' D8 Discover multipurpose X-Ray Diffractometer. The obtained results were used to characterize the nanofiller and also determine the degree of exfoliation.
FTIR analysis was conducted to the neat epoxy and nanocomposites to study reaction mechanism of epoxy resin and the nanofillers. FTIR spectra of neat epoxy, single filler, and hybrid filler composite were obtained by a Thermo Scientific Nicolet 8700 spectrometer.
The micrographs were obtained by a field emission scanning electron microscope (FE-SEM), with a JSM-7600F Schottky at 2 KV. Visual assessment of the prepared samples was able to be performed with this advanced electron microscopy technique. The obtained images from the fractured surface of samples were used to study the dispersion and agglomeration of the different nanofillers. Meanwhile, the SEM images of the abraded sample were used to investigate the relation between surface morphology and water repellency. Surface roughness analysis was performed with an atomic force microscopy, carried out on a Nanoscope IIIa system. Both 2-D and 3-D images were collected in “tapping-mode”. By scanning the surface of the coating with a sample-probe, the height changes were recorded, and three-dimensional images will be formed in the process. The obtained data can also be used to analyze the surface roughness of the tested samples.
This section presents the evaluation of the “hybrid effect” on mechanical, electrical, and tribological properties in epoxy nanocomposites. The exemplified hybrid nanofiller composites were combinations of CNT and GNP, CNT and NS, GNP and NS. For each type of filler, the concentration of the nanofiller was fixed at 1 wt. % with five different mix ratios: 0:1, 25:75, 50:50, 75:25, and 1:0.
1.3.1 Characterization of GNP/NS Nanohybrids
Transmission electron microscopy (TEM) images of GNP, NS and GNP/NS hybrid nanofillers was displayed in
As shown in
1.3.2 X-ray Powder Diffraction (XRD)
The XRD patterns were conducted to demonstrate the degree exfoliation of various fillers. Wan et al., Compos. Sci. Technol., 82:60-68, 2013. GNP exhibited as crystalline solids with a sharp peak at 26.5°, corresponding highly-ordered nanoparticle structure with an interlay spacing of 3.4 nm, as shown in
Apart from that, it was clear that the hybrid filler showed two weak diffraction peaks at 26.5° and 19.5° (
1.3.3 Particle Size Analysis
To get more information on the synergistic effect of hybrid nanofillers, the particle size distributions of single and hybrid fillers were measured by a dynamic light scattering (DLS) analyzer. Particle size distributions of GNP, NS, and the hybrid filler were illustrated in
1.3.4 Fourier-Transform Infrared Spectroscopy (FTIR)
FTIR analysis was conducted on neat epoxy, single filler/epoxy, and hybrid filler/epoxy nanocomposites to understand the possible chemical reaction between polymer and nanofillers. The characteristic peaks (
The peak for the N—H deformation around 1507 cm−1 represented the primary amine of hardener used for epoxy resin. It was clear to observe that the intensity of this peak in all the nanofiller/epoxy composites was decreased compared with neat epoxy, this may probably because some amino groups did not take parts in ring-opening polymerization reaction due to the agglomeration of nanoparticles. However, the intensity of hybrid filler composites was significantly stronger than both 1% G-Epoxy and 1% S-Epoxy at this peak, indicated agglomeration was dramatically reduced in the hybrid filler group, especially 1% GS-Epoxy (50:50). Nuruddin et a1., Polym. Polym. Compos., 25(4):273, 2017; Gonzalez et al., “Applications of FTIR on epoxy resins-identification, monitoring the curing process, phase separation and water uptake,” in Infrared Spectroscopy-Materials Science, Engineering and Technology, InTech, 2012.
1.3.5 EIS Spectra Analysis
EIS measurement of the specimens were performed to characterize the corrosion resistance of the nanocomposite coatings during exposure.
Initially, the collected data indicated that the neat epoxy coating was incapable to behave as an intact coating for corrosion protection, as a clear bend of was observed in phase angle curve in the tested frequency region. Compared with the neat epoxy, the phase angle remained close to 90 degrees in all the tested frequency, which reflected that the coating films behaved as an intact layer to protect the substrates. Moreover, all the nanofiller/epoxy groups exhibited higher impedance, suggesting that the protective coatings have excellent corrosion barrier performance. Obviously, the hybrid filler groups displayed stronger corrosion resistance reinforcement than the single filler groups, as the increase in |Z|0.01 Hz values and phase angle. The values of |Z|0.01 Hz for the GS-Epoxy coatings were around 7{circumflex over ( )}10, higher than the neat epoxy coating by 1 order. Overall, it turned out that model A in
After 100 hours of exposure,
After 500 hours of exposure, 1% GS-Epoxy (50:50) showed its extraordinary anti-corrosion performance, regardless of exposure time. It was clear to observe that high impedance value has been maintained during exposure, as the impedance value was over 1010 Ω/cm2 for both 100 hours and 500 hours. All the coatings with nanofillers exhibited improved barrier properties as expected, hence, model C was applied to neat epoxy at this stage. However, compared to the coatings with single fillers, no significant improvement was observed in the other coatings with hybrid filler, thus, the impedance value of 1% GS-Epoxy (25:75) and 1% GS-Epoxy (75:25) were close to the 1% S-Epoxy specimen. In summary, the 1% GS-Epoxy (50:50) sample remained in model A during the whole exposure, while 1% G-Epoxy, 1% GS-Epoxy (25:75) and 1% GS-Epoxy (75:25) were in model B with Warburg elements.
1.3.6 Coating Damage Indices
Evaluation of the degradation process on the coating-substrate interface was conducted by coating damage indices. As identified in
The damage index I, DI1, was determined by the reduction of Zmod values at low frequencies (0.01 Hz) during coating degradation process, as shown in equation below:
where, Zintact coating and Zdamage coating are impedance value at intact and damaged stages, respectively.
In addition, the damage index II, DI2, was identified the coating degradation at all tested frequency range:
where, the region below the impendence curve could be separated into the capacitive (A2) and resistive region (A1) by the breakpoint frequency values where phase angle reaches −45°. Ammar et al., Surf Coat. Technol., 324:536-545, 2017. Compared with a perfect intact coating, an extra area (A3) could be determined above the resistive region (A1) for the damaged coating. As electrolyte solution penetrated the coating system, which initiated coating damage and corrosion reaction occurred at the coating-substrate interface, let to a decrease in the capacitive region and increase in the resistive region. Ramezanzadeh et al., Corros. Sci., 103:283-304, 2016.
On the other hand, the incorporation of nanofillers results in enhancing the barrier properties as the capacitive region has remained relatively large compared with neat epoxy coating. As illustrated in
The results of coating damage indices were illustrated in
1.3.7 Water Absorption
Researchers have studied the mechanism of polymer-based coating based on EIS measurements (Philippe et al., J. Electrochem. Soc., 150(4):B111-B119, 2003; Lacombre et al., Electrochimica Acta, 231:162-170, 2017), and the penetration of water into the coating is expected to increase the coating capacitance due to the dielectric constant of water is higher than typical polymers (Brasher et al., J. Appl. Chem., 4(2):62-72, 1954). The model that employed for quantifying the water uptake was employed by Brasher and Kingsbury, and presented in the equation:
where Φ is the water content volume percentage; Ct and C0 are the capacitance for before and after the test, respectively; εw is the dielectric constant of water at the working temperature (equal 78.5 at 25° C., and 75 at 35° C.). Brasher et al., J. Appl. Chem., 4(2):62-72, 1954.
The calculated water absorptions were shown in
1.3.8 Effects of Nanofiller on the Occurrence of Blistering and Localized Corrosion
The anti-corrosion performance of the coating films was also investigated by visual assessment after exposure, as displayed in
1.3.9 Abrasion Resistance Test
Coatings with strong abrasion resistance can protect the substrate from damage by friction, and extent the service life of the structure. The abrasion resistance of the tested coatings was characterized by the Taber abraser test and wear mass loss was measured during the test. Less mass loss after the test indicates the coating has better abrasion resistance.
The mass loss of the neat epoxy film was 114 mg, improvement on abrasion resistance was observed in all the tested nanofiller/epoxy samples. The maximum improvement of abrasion resistance was obtained in 1% GS-Epoxy (50:50), which the weight of mass loss was decreased by 44%. For the composites containing hybrid nanofiller with a ratio of 25:75 and 75:25, the mass loss was generally higher than single filler groups (1% G-Epoxy and 1% S-Epoxy). The generalizability of research work suggested that abrasion resistance is dependent on the cohesion or strength of the coatings, and the ability to transfer the applied load during the abrasion process. Fan et al., Prog. Org. Coat., 86:125-133, 2015; Daniels et al., J. Colloid Interface Sci., 205(1):191-200, 1998. Without nanofillers, the neat epoxy coating film contains micro-pores, which leads a weaker abrasion resistance. This suggestion was confirmed by the SEM images of the abraded surface for the neat epoxy film, therefore, a porous surface with air entrapped voids was detected in the
1.3.10 Coupon Tensile Test
The tensile properties of hybrid nanofiller reinforced epoxy was characterized by the coupon tensile test (ASTM D638). To evaluate the influence of varied mix ratios in the hybrid nanofillers,
The results in
The overall results suggested that the addition of NS would increase the strength and strain of the epoxy resin, however, a reduction of stiffness was observed which revealed a weaker ability to resists deformation. No significant impact on the test results was observed in GNP/composites, indicating the tensile properties of the epoxy resin was not improved by the addition of GNP. Evidently, it can be claimed that there exists a critical ratio between GNP and NS which the strength, strain, and stiffness of the composites could be improved, thus, at this stage the ratio was 50:50.
1.3.11 Characterization of Robust Hydrophobic Surface
The application of hydrophobic surface was often limited by its durability due to its mechanical instability. The function is easy to be impaired after rigorous physical damages that caused by abrasion and scratching. Nine et al., ACS Appl. Mater. Interfaces, 7(51):28482-28493, 2015. Abrasion with sandpaper was applied to the coating film, and the contact angle was measured on the abraded surfaces in order to evaluate the robustness of the nanocomposites. Different grit sandpapers were applied on the coating surface of all the tested samples. Sandpapers with medium, mild, and fine grade abrasive grades were empolyed in order to create varied mechanical damges.
Strong evidence revealed that the coating films were robust enough to maintain the hydrophobic properties after abrasion. A schematic of the contact angles of the tested coating films was illustrated in
Furthermore, AFM and SEM techniques were used to investigate the micromorphology of the tested samples. Similar to the natural leaf, such as lotus leaf, island-like spots were obtained on the surfaces leads to the enhanced hydrophobicity of the nanocomposite coatings. In addition, the water repellency was also contributed by the exposed hydrophobic nanoparticles. Hydrophobic nanotexture was obtained, and this finding was verified by using advanced microscopy technologies.
FESEM images were applied to examine the morphology of the abraded surfaces.
AFM test was performed to examine the morphology of the abraded surfaces by illustrating 3-dimensional images.
Overall, the coating compositions of the invention with GNP/NS hybrid-filler reinforced nanocomposites have robust anti-corrosion and hydrophobic properties. The test results demonstrate synergistic effects of the hybrid fillers, in particular a remarkable enhancement in abrasion resistance, mechanical strength, barrier properties, corrosion protection performance, and water-repellency. The combination of GNP/NS in a ratio of 50:50 exhibited highest improvements on corrosion and mechanical performance, most likely due to the presence of GNP, which improved the dispersion of NS, and the NS enhanced the exfoliation degree of GNP. Thus, the GNP/NS epoxy coating compositions of the invention may be used as high-performance protection coatings.
The fabrication process of the nanoparticle-polymer composites coating was illustrated in
2.2.1 Characterization
The characterization of nanofillers and nanocomposites was carried out by several techniques, which include scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-Ray Diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). The TEM images of nanofillers were collected by JEOL JEM-2100 high-resolution analytical transmission electron microscopy, and the images were used to examine the microstructure of the hybrid nanofiller virtually. The XRD patterns were conducted to demonstrate the intercalation and degree of exfoliation of the nanofillers, and the results were collected by Bruker AXS' D8 Discover multipurpose X-Ray Diffractometer. FTIR analysis was conducted to study the reaction mechanism of epoxy and polydimethylsiloxane. A Thermo Scientific Nicolet 8700 spectrometer obtained FTIR spectra of neat epoxy and PDMS/epoxy composite. The surface micrographs of nanocomposite in this study were recorded by JSM-7600F Schottky field-emission scanning electron microscope (FE-SEM); thus, SEM images of fracture and abraded surface were utilized to analyze the fracture toughness and wear resistance for the composites, respectively.
2.2.2 Corrosion Resistance
The corrosion resistance of the developed nanoparticle-polymer coatings was evaluated by the electrochemical impedance spectroscopy (EIS) test. The test was utilized a three-electrode cell setup, which consisting of a reference electrode (saturated calomel electrode), a counter electrode (platinum mesh), and a working electrode (test panel). A 30-mm diameter O-ring glass tube was clamped on the coated panels and filled with 1.0% NaCl solution; hence, the tested area was exposed to a conductive electrolyte solution during the test. The EIS measurement was herein carried out by a Gamry equipment (Reference 600 potentio/Galvanostat/ZRA), and test frequency range of 100 kHz to 10 mHz. The collected data were converted into Bode plots with impedance and phase angle curves.
To examine the long-term corrosion barrier properties of the developed coating systems, the salt spray exposure (ASTM B117) was carried out as an accelerated durability test. The specimens were exposed to salt fog spray (5.0% NaCl solution) with evaluated temperature (35° C.) while kept in a 0-Fog CCT chamber, and EIS measurements were conducted before, 24, 100, and 200 hr after the exposure.
The obtained EIS data were fitted into an equivalent electrical circuit (EEC) model to describe the coating degradation process caused by corrosion impacts. As described in
In order to determine the degree of coating degradation over expose time, the coating damage index was employed as it can effectively describe the corrosion protection of a coating. The formulation was modified from early work from researchers (Ammar et al., Surf. Coat. Technol., 324:536-545, 2017; Ramezanzadeh et al., Corros. Sci., 103:283-304, 2016), and as shown below:
where, the combination of (A1+A2) is the area under the impedance curved for a damaged coating, and the (A1+A2+A3) denotes the area for an ideally perfect coating film (
2.2.3 Abrasion Resistance
Wear resistance of the prepared coatings was evaluated by Taber abraser test by following ASTM D 4060. The coating samples were abraded by two CS-10 abrading wheels, with a rotation speed of 72 rpm and an applied load of 1000 g. Each specimen was subjected to 1000 abrasion cycles, and the weight at 100, 500, and 1000 cycles was recorded. Both total mass loss and wear index was employed to evaluate the abrasion resistance of the composites:
Mass loss (mg)=Mintact−Mabraded (5)
where, Mintact refers to the initial weight before coating, and Mabraded is the remaining mass after abrasion.
In this case, both the total mass loss and mass loss rate of specimens were used to characterize the wear resistance of coatings.
2.2.4 Tensile Properties
To understand the damage tolerance of the coatings of the invention, a coupon tensile test was employed to characterize the tensile properties of each composite. The test was carried out by using a Shimadzu's EZ-X tester in accordance with ASTM D638 standard. The testing speed was controlled as 1 mm/min until failure; thus, tensile strength, elongation at break, and Young's modulus were calculated for each specimen.
2.2.5 Contact Angle
The hydrophobicity of the nanoparticle-polymer coatings was characterized by water contact angle test, by following ASTM D7334. Water droplet was gently deposited on the coating surface and images were captured by a camera, then the water contact angle (WCA) was calculated by a computer based on the obtained images.
2.3.1 X-Ray Diffraction (XRD) of Hybrid Nanofillers
The XRD patterns of GNP, NS, and GNP/NS hybrid nanofillers were presented in
Supporting this, the TEM micrograph was presented to show the morphology of the GNP/SiO2 hybrid nanofillers. It is well known that the NS and GNP nanoparticles could be defined as zero, and two-dimensional materials, respectively.
2.3.2 Fourier Transform Infrared Spectroscopy (FTIR) Spectra
FTIR spectra was utilized to study the chemical structure of neat epoxy and PDMS modified epoxy system, which investigated the chemical reaction between neat chemicals. As shown in
2.3.3 Corrosion Barrier Performance of the New Developed Nanocomposite Coating
Corrosion barrier performance plays a vital role in coating's overall performance, and electrochemical impedance spectroscopy (EIS) measurement was utilized then the results were displayed using Bode plots. In order to determine the long-term performance of prepared coating systems, the coated samples were exposed to salt fog spray (5.0% NaCl solution) under-evaluated temperature (35° C.), and EIS measurement was conducted periodically.
Generally, researchers suggested that the impedance value at low frequency (0.01 Hz) represented the coating barrier properties; thus, the higher Zmod0.01 Hz in the impedance curve, the better corrosion protective property that the coating has. Moreover, the phase angle curve reflects the intactness of a coating system, and a value of 0° and 90° represents the coating has low and high degrees of intactness, correspondingly. Overall, a perfect coating film has a straight line with a slope of −1 in impedance curve and phase angle values are close to 90° in wide frequencies; in this case, the coating can prevent electrolyte media to penetrate into the coating-substrate interface and initiate corrosion reaction.
At the fresh stage, the neat epoxy coating exhibited good corrosion protection performance for the substrate. However, according to the impedance plot, an apparent bend was obtained in the low frequencies, while the phase angle reduced to 17° in the corresponded frequency region. In addition, the EIS data was well-fitted to the Model B with the Warburg model at this stage (Table 2). These observations revealed that the neat epoxy could not behave as an intact barrier film against corrosive electrodes. This was further confirmed by the EIS measurements after exposure, the impedance values were significantly reduced as the exposure time elapsed. Meanwhile, the frequency that has a low phase angle was shifted to the higher frequency region, indicating the micropores and cracks in the coating film was developed. These observations revealed that the neat epoxy was damaged while exposing to the salt spray, which made it not suitable to provide long-term protection for the metallic substrate.
On the other hand, as clearly illustrated in
The prepared PDMS modified epoxy coating with 1% GNP/NS demonstrated high impedance value at the low-frequency region, and the phase angle was around 90° in both high and low-frequency regions. The long-term performance of the GS-PDEP coatings showed a good agreement with the EIS results at the fresh stage. As clearly illustrated in
On the other hand, the index values for PDMS/epoxy and GNP/epoxy composites were both around 100% before exposure, suggesting that they were behaved as an intact film to protect the substrate, and high index values were maintained at 24 and 100 hr exposure for both coatings. However, degradation was observed in the GS-EP sample after 200 hr, indicating the elongated diffusion pathway attributed by nanofillers could dramatically improve the corrosion resistance in the short-run, but the coating was still weak in durability for a long-term test due to the hydrophilic epoxy resin. Conversely, the PDMS/epoxy coating (PDEP) showed its extraordinary anti-corrosion performance, regardless of exposure time in salt spray, this suggesting that the increased hydrophobicity could effectively prevent the penetration of corrosive media and resulted in improved durability against corrosive environment. Particularly, the combination of PDMS and nanofiller reinforcement exhibited the highest index value regardless of the testing duration, as the GS-PDEP coating maintained an index value of 100% at all times. This phenomenon confirmed that the combination of resin modification and nanofiller reinforcement had outperformed the coating with the single enhancements.
2.3.4 Abrasion Resistance of the New Developed Nanocomposite Coating
The abrasion resistance plays a vital role in quantifying the damage tolerance of a protective coating, and the anti-abrasion performance was herein evaluated by using the Taber abraser method (ASTM D 4060). The total wear mass loss and the wear index were employed to characterize the abrasion resistance of the developed coating systems, and less mass loss and wear index indicates better abrasion resistance.
As displayed in
The SEM images of the worn surface were employed to demonstrate the feature of the specimens with enhanced abrasion resistance. The neat epoxy and GS-PDEP composites were selected as a representative in
2.3.5 Tensile Behavior of the New Developed Nanocomposite Coating
The tensile properties of the protective coating could assist in evaluating their tolerance against mechanical damage for real-world application, and
strain at failure
and Young's modulus
of the composites, where P is the ultimate load, A is the cross-sectional area, Lo and ΔL are initial length and change in length, respectively.
The ultimate strain is the elongation at the point of failure when the coating is subjected to deformation. Improvement was observed in all the modified composites; thus, the addition of PDMS and hybrid nanofiller led to an increase in ultimate strain, as shown in
The Young's modulus of the GS-PDEP nanocomposites exhibited an identical trend with the tensile strength and strain (
The SEM image of fracture surfaces for the neat epoxy and GS-PDEP specimens was selected as presented in
2.3.6 Contact Angle Measurement of the New Developed Nanocomposite Coating
The water contact angle (WCA) test was utilized to characterize the water-repellency of the developed coatings. The contact angle of the neat epoxy was 51°, indicating the surface was hydrophilic that easy to attract and absorb water in a moist environment; thus, it resulted corrosion reaction to the metallic substrate and eventually shortened the service life. The addition of GNP/NS hybrid nanofiller showed a reduced water repellency and the WCA decreased to 26°. With the content of PDMS in the epoxy resin, the WCA of the coating increased to 110°, as presented in
To study the stability of the water repellency against various damages, the water contact angle was measured after the developed GS-PDEP nanocomposite coating subjected to salt fog spray and abrasion test. As shown in
The mechanical stability of the GS-PDEP coating was investigated after the abrasion test, and the coating surface was subjected to two CS-10 abrasive rollers with a pressure of 122.6 KPa applied on each roller, which is a typical test method to evaluate heavy-duty protective coatings.
In summary, GNP/NS loaded PDMS/epoxy nanocomposite was synthesized via a facile solvent-free fabrication method, and the obtained coating was suitable for various application methods. The developed coating has a dramatic improvement in anti-corrosion performance, and the coating displayed long-term resistance when they were exposed to accelerated weathering environments. The results of the coupon tensile test confirmed that the inclusion of GNP/NS nanofiller in the polymer resin could improve the strength, strain, Young's modulus, as they are critical mechanical properties for engineering applications. The developed coating also displayed a reduced mass loss after abrasion, indicating a dramatically enhanced wear resistance. SEM images were utilized to examine the surfaces after tensile and abrasion tests virtually. Significantly rougher fracture surfaces with compacted cleavages were observed in the developed coating, as compared to the neat epoxy; indicating the composite has higher energy absorption and fracture resistance. After abrasion, the decreased amount and size of micro-cracks were observed in the developed coating; this observation indicated the coating has stronger toughness when subjected to the abrasion forces, which was consistent with the results of mass loss. The increased contact angle suggested that the coating has excellent hydrophobicity. Moreover, the surface was robust enough as the hydrophobicity has remained even after mechanically damaged or exposed to an accelerated weathering environment. Such a robust multifunctional corrosion protection coating with remarkable durable hydrophobicity is useful in applications in civil infrastructures.
As shown in
The nanofiller/epoxy mixture was stirred while PDMS (7.5 g), APTES (2.13 g), and DBTDL (0.075 g) were added during the mixing. To allow the PDMS to react with epoxy, the mixture was stirred under a speed of 800 rpm at 80° C. for 20 min. The addition of EPIIKURE™ Curing Agent 3175 (36.35 g) was mixed into the as-prepared mixture and stirred for 10 min, and the nanocomposites were ready to cast on metallic substrates.
SiO2 NPs (2 g) and FDTS (3 g) were added into a flask with 160 ml hexane and refluxed for 3 hours to allow the FDTS modify the surface of SiO2. The prepared solution was then dried and grounded, and the obtained white fine powders were the fluorinated SiO2 NPs.
3.3 Coating Treatment
The prepared nanofiller composite coatings were coated on a steel substrate with an 8 mils drawdown bar. The coated substrates were then air-dried for 3 hours and the fluorinated SiO2 NPs were applied to the coating surface by a natural fiber brush; and the brush-coating was repeated around 8˜10 times to achieve a uniform layer of NPs. After that, the specimens were left at room temperature for a few days to allow completely dry and ready for characterization.
FTIR measurements were carried out with a Nicolet 8700 spectrometer to characterize the PDMS modifier epoxy resin and fluorinated SiO2 NPs. The particle size of the hybrid nanofillers was determined by dynamic light scattering (DLS) method with a submicron particle sizer (Nicomp 380). Furthermore, a Bruker AXS' D8 Discover multipurpose X-Ray Diffractometer was employed to study the structure of the nanofillers, and the morphologies were characterized by TEM images using a JEM-2100 high-resolution analytical TEM instrument. Micrographs of coating top surface and fractured cross-sectional surface were taken by a field emission scanning electron microscope (FE-SEM), with a JSM-7600F Schottky.
3.4.1 Corrosion Protection Test
To evaluate the corrosion protection performance of the prepared coatings, electrochemical impedance spectroscopy (EIS) measurement was performed by the Gamry Reference 600 instrument. In a typical process, a 30-mm diameter O-ring glass tube was clamped to the test panels and filled with 1.0% NaCl solution, so the tested area was immersed by the conductive solution. Three electrode system was employed during the test: a saturated calomel electrode, a platinum mesh, and the test panel were worked as the reference electrode, counter electrode, and working electrode, respectively. Both DC potential and small superimposed AC excitation were applied to the working electrode during the test, and the data of current and potential of the electrochemical cell were collected, then converted into impedance vs. frequency curve.
3.4.2 Water Adhesion Test
The adhesion of water to the coating surface was evaluated by applying a water droplet ascending and descending from the coating surface. Constant speed of 0.5 mm/sec was applied to control the movement of water droplets. To make sure the droplet was sable on the coating, the droplet was squeezed against surface, and then rested for 15 sec before the descending process. The water droplet would completely detached from the surface and suspended on the tip during the descending process if it is a superhydrophobic surface with excellent water repellency; otherwise, the water would elongated into a cone shape during the descending process and detached from the tip in the final step.
3.4.3 Durability Test
The long-term performance of the coating under a corrosive environment was evaluated using accelerated durability test. The coated samples were left in a Q-Fog CCT chamber and exposed to salt spray with 5% NaCl solution, under an evaluated temperature (35° C.). The contact angle, water adhesion, and corrosion protection were evaluated after exposure. The accelerated weathering test was also utilized to examine the stability of the amphiphobicity of the developed coating. The specimens were exposed to artificial accelerated weathering cycles that carried out by a QUV accelerated weathering tester, each cycle includes 4 h of UV-light irradiation (60° C., UV intensity of 0.71 W m−2) and 4 h of water condensation (50° C.). Contact angles, sliding angles and water adhesion were examined after the exposure.
3.4.4 Mechanical Strength Test
The tensile properties of the developed coating were determined by the coupon tensile test (ASTM D638), with a Shimadzu's EZ-X tester. The coupon specimens were clamped at both ends by the grip, and tensile strength was applied to elongate the specimens until the narrow cross-sectional test section was broke. The elongation speed was control to 1 mm/min, and real-time recorded stress vs. strain was used to determine the tensile strength, ultimate strain and Young's modulus for each specimen.
3.4.5 Durability and Reliability During Salt Fog Exposure
As the civil infrastructures are generally exposed to a moist or corrosive environment, the salt fog exposure was applied to examine the durability of the developed coatings as well, which corrosion resistance and hydrophobicity of the specimens were evaluated after exposure.
3.4.6 Corrosion Barrier Performance: EIS
The corrosion barrier property plays a vital role in the overall performance of a protective coating. To evaluate the long-term corrosion protection provided by the coating, coating was exposed to a corrosive environment with salt fog spray and elevated temperature for 500 hours, and electrochemical impedance spectroscopy (EIS) measurement was performed during the exposure.
The bode plots are generally represented by impedance and phase angle curves to study the performance of coatings. The impedance value in the low-frequency region (0.01 Hz) reflects the coating protective property of coating, and researchers suggested that an effective coating should have a maximum impedance value higher than 106 Ωcm2. The phase angle curve represented the intactness of coating system, which a value 0° and 90° indicated that coating has poor and superior degrees of intactness, respectively. For an intact coating film against corrosion, as the electrolyte media could not penetrate the coating system, a straight line with a slope of −1 could be obtained in impendence curve and the phase-angle values reached up mostly approached 90° in a wide frequency region. Analysis of the ratio changes between resistive and capacitive regions during exposure can be utilized to understand the coating delamination process. The anti-corrosion performance is associated with the capacitive and resistive behavior of coatings; a purely capacitive behavior corresponds to a perfect barrier property; if the capacitive behavior is low, the electrode can pass the film like a resistor, and the resistive behavior is attributed to the coating performance. The region below the impendence curve could be split into the capacitive and resistive region by the breakpoint frequency values where phase angle reaches −45°. Therefore, the ratio changes between capacitive and resistive region is attributed by the coating damage and delamination. A decrease in capacitive region while an increase in resistive region revealed that the coating is damaged, and the corrosion protection performance is reduced.
3.5.1 X-Ray Diffraction (XRD) of Nanoparticle-Polymer Composite
The nano-silica particles have uniformly attached and hanged on the surface of graphene nanoplatelets during the dispersion procedure, as confirmed by transmission electron microscope (TEM) image shown in
3.5.2 FTIR of Superamphiphobic Surface
The superamphiphobic surface were synthesized by modifying SiO2 nanoparticles with 1H,1H-2H,2H perfluorodecyltrichlorosilane (PDTS) and hexadecane. When the coating surface was covered with a dense layer of modified SiO2 surface, as presented in
3.5.3 Corrosion Barrier Performance: EIS
The impedance values at 0.01 Hz were summarized in
3.5.4 Superamphiphobicity of Coating Upon Corrosive Environment and Accelerated Weathering Treatment
The application of the hydrophobic surface was often limited by its poor durability. The stability of the amphiphobic surface on the developed coating was further examined by measuring the CA and SA after salt fog spray. The results strongly suggested the coating film was robust enough to maintain the superhydrophobic properties under the accelerated corrosive environment. The CA values have slightly deceased after 24 hours exposure and then displayed no obvious change after that. A water contact angle (CA) values around 152˜155° were obtained in both 24, 100, 200 and 500 hours. In addition, the SA values were increased a little after 24 hours exposure and retained less than 10° even after 500 hours. Meanwhile, similar tendency was also observed with oil droplets (hexadecane), the CA of hexadecane remained in a range of 143˜150° with the exposure time, while the SA was still low. These results indicated that the superior water and oil repellency of the developed coating was survived after exposing to the severe environment.
Besides exposing to corrosive environment, the weather condition that includes UV irradiation and water condensation is another challenge to superamphiphobic coatings, which may result severe coating degradation and reduce the hydrophobicity. To evaluate the stability of the developed coating under UV-light and water-condensation cycles, accelerated weathering treatment was performed to the specimens, while the CA and SA was measured after exposure as well. The results revealed the developed coating could resist attacks attributed by UV-irradiation and water-condensation. Similar to the results from salt spray, slightly decreased CA and increased SA were observed at the beginning of exposure then remained unchanged during the test. As shown in
3.5.5 Water Droplet Adhesion from the Coating Surface
The coating surface was categorized as hydrophilic (contact angle <45°), hydrophobic (contact angle >90°), and in-between (45°<contact angle <90°) if water was used as the test liquid. Moreover, it is worth to mention that the adhesion of water to the contact surface is also a primary factor that contributed to the water repellency of coatings. Yin et al., Appl. Surf. Sci., 258:4063-4068, 2012; Xue et al., Sci. Technol. Adv. Mater., 9:035008, 2008; Das et al., ACS Appl. Mater. Interfaces, 9:21496-21502, 2017; Dong et al., ACS Appl. Mater. Interfaces, 9:1941-1952, 2017; Wang et al., ACS Appl. Mater. Interfaces, 7:743-755, 2014. Higher water adhesion indicates the water is more difficult to detach from the surface, which increase the wettability of the coating.
Excellent water repellency was observed in 1% GS-PDEP (10:90) MS coating, as it was found that the water droplet was easily detached from the surface and suspending on the tip, as presented in
The results from the water adhesion showed a strong agreement with the contact angle test. As the exposure time elapsed, no significant increase in water adhesion was observed, indicating the surface remained undamaged under the severe environment. As presented in
3.5.6 Tension Properties
In the SEM images of the fracture surface (
A self-cleaning superamphiphobic coating with excellent corrosion protection properties and mechanical strength was synthesized by integrating the hybrid nanofiller reinforcement with surface modification. The simple fabrication method and easy application process showed its potential toward large scale commercial applications. The use of GNP/NS hybrid nanofiller provided a reinforcement on corrosion barriers performance and also a significant improvement on mechanical properties was obtained in the proposed coating. A superamphiphobic coating was fabricated which consisted the fluorinated particles and PDMS modified epoxy resin; hence, the contact angle of water and hexadecane was increased to around 168° and 150°, respectively. The obtained results during accelerated corrosion test revealed the proposed coating was durable, as its excellent corrosion resistance and hydrophobicity remained undamaged after exposure. This nanofiller-epoxy coating is well-suited as a multifunctional protective coating for metallic infrastructures.
This application claims priority to U.S. Provisional Application No. 63/045,426, filed Jun. 29, 2020, which is incoporated herein by reference.
This invention was made with government support under grant DTPH56-16-H-CAAP03 awarded by the U.S. Department of Transportation, Pipeline and Hazardous Materials Safety Administration (USDOT PHMSA). The U.S. government has certain rights in the invention.