Curable composition having high tack and green strength

Information

  • Patent Grant
  • 4740424
  • Patent Number
    4,740,424
  • Date Filed
    Tuesday, May 27, 1986
    38 years ago
  • Date Issued
    Tuesday, April 26, 1988
    36 years ago
Abstract
Curable compositions useful as adhesives, coatings and sealants, comprising a mixture of (a) isocyanate-functional prepolymer derived from (i) polyisocyanate and (ii) active hydrogen-containing low molecular weight polymer selected from the group consisting of polytetramethylene oxide polyols, polycarbonate polyols, and polysulfide polythiols, and (b) halogenated resin compatible with said prepolymer, said resin containing about 50 to about 70 weight percent halogen.
Description

TECHNICAL FIELD
This invention relates to curable compositions for use as adhesives, coatings and sealants. This invention also relates to articles having a layer of such curable compositions thereon, and to a method for bonding, coating or sealing such articles using such compositions.
BACKGROUND OF THE INVENTION
U.S. Pat. Nos. 4,217,254, 4,256,615 and 4,340,682 describe adhesive compositions containing mixtures of isocyanate-terminated ricinoleate prepolymer and chlorinated rubber or chlorinated polyvinyl chloride. These compositions are said to have high green strength. The reexamination file for the '682 patent (Reexamination No. 90/000,780, requested May 13, 1985) contains several affidavits, patents and published patent applications relating to polyurethane adhesive compositions containing chlorinated rubber or chlorinated polyvinyl chloride. Among such references is German OLS No. 26 44 639, which mentions, but does not exemplify, adhesives made from polyisocyanates made by mixing various diisocyanates with various glycols or polyether glycols including "tetramethylene glycol". These polyisocyanates are said to be combined with various polyalkylene polyether polyols said to be made by the reaction of "alkylene oxides" (including "butylene oxide") with "suitable starter molecules" such as water or alcohols. Although not specified in the OLS, "butylene oxide" presumably refers to 1,2-butylene oxide, a compound that can react with water in an anionic polymerization. 1,4-Butylene oxide (tetrahydrofuran) does not react with water under such conditions.
U.S. Pat. No. 3,947,403 (McCready) describes adhesives said to have improved Scott brittle points and "good uncured tack or cohesive strength", made from a solvent solution of a polyurethane prepolymer and polyvinylidene chloride. The polyurethane prepolymer is said preferably to be isocyanate-functional. At column 4, lines 36-44 it is said that the adhesive can be made in a "one shot" method using, inter alia, "polytetramethylene ether glycol or triol".
SUMMARY OF THE INVENTION
Adhesives made from many of the glycols and polyalkylene ether polyols recited in the OLS are not compatible with chlorinated rubber or chlorinated polyvinyl chloride. Incompatibility is manifested by phase separation.
The present invention provides curable adhesive, coating and sealant compositions that are compatible and have high tack and high green strength. The compositions of the invention are not disclosed in the above-mentioned references. The compositions of the invention can be one-part moisture-curable or two-part self-curable compositions.
The one-part moisture-curable compositions of the invention comprise a mixture of (a) isocyanate-functional prepolymer derived from (i) polyisocyanate and (ii) active hydrogen-containing low molecular weight polymer selected from the group consisting of polytetramethylene oxide polyols, polycarbonate polyols, and polysulfide polythiols, and (b) halogenated (e.g., chlorinated) resin compatible with said prepolymer, said resin containing about 58 to about 70 weight percent halogen.
The two-part compositions of the invention comprise the above-described isocyanate-functional prepolymer in a first part, isocyanate-reactive material (e.g., water, polyol, polythiol, or polyamine) in a second part and the above-described halogenated resin in said first or said second part, the two parts being intended to be mixed together prior to use.
The present invention also provides articles having thereon a layer or layers of the above-described compositions, and a method for adhering, coating or sealing such articles by applying a layer or layers of such compositions thereto.
DETAILED DESCRIPTION
For brevity, the active hydrogen-containing low molecular weight polymer will hereafter sometimes be referred to as the "active hydrogen polymer". As used herein, an isocyanate-functional prepolymer "derived from" the above-mentioned polyisocyanate and active hydrogen polymer will include prepolymers actually prepared by a reaction between such polyisocyanate and such active hydrogen polymer, and will also be construed to include prepolymers that have not actually been prepared by such a reaction, but have chemical structures that render the prepolymers capable of being prepared from such a reaction if desired. The isocyanate-functional prepolymers are most conveniently prepared by reactions between one or more polyisocyanates and one or more active hydrogen polymers, employing an excess of polyisocyanate to insure that the reaction product contains residual isocyanate groups.
Suitable polyisocyanates include aromatic, aliphatic, and cycloaliphatic polyisocyanates such as 4,4'-diphenylmethane diisocyanate ("MDI"), toluene diisocyanate ("TDI"), xylylene diisocyanate, tetramethylxylene diisocyanate, naphthalene diisocyanate, para-phenylene diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, mixtures thereof, and the like. Polymeric polyisocyanates, biurets, blocked polyisocyanates, and mixtures of polyisocyanates with melting point modifiers can also be used. MDI is a particularly preferred polyisocyanate. Suitable commercially available polyisocyanates include "Isonate" 125M and 143L and the series "PAPI 20" through "PAPI 901" polyisocyanates (all commercially available from the Upjohn Co.), "Multrathane M" and "Mondur" CD, M, MR, MRS, and MRS 10, 509, TDS, TD, TD-80, HX, E-448, E-501, E-512, PF, and MT-40 polyisocyanates (all commercially available from Mobay Chemical Corp.), "Rubinate M" polyisocyanate (commercially available from Rubicon Chemicals, Inc.) and "Elate 160" polyisocyanate (commercially available from Akzo Chemie America).
The active hydrogen polymers contain two or more repeating units derived from tetramethylene oxide (--CH.sub.2 CH.sub.2 CH.sub.2 CH.sub.2 O--), carbonate ##STR1## disulfide (--SS--), or mixtures thereof. Preferably such repeating units occur in blocks of two or more. The active hydrogen polymers preferably have two or more active hydrogen atoms (as determined by the Zerewitinoff method) per polymer unit, and preferably have a number average molecular weight between 162 and about 10,000, more preferably between about 300 and about 3000. Polyols are preferred active hydrogen polymers, and polytetramethylene oxide polyether polyols are particularly preferred. Preferably a mixture of both long- and short-chain active hydrogen polymers is employed to prepare the isocyanate-functional prepolymer. Suitable active hydrogen polymers are formed by polymerizing or copolymerizing active hydrogen-containing monomers (or optional comonomers or copolymers), or by employing ring-opening polymerization reactions, to provide a polymeric product containing active hydrogen atoms. For example, polytetramethylene oxide polyether polyols can be prepared using a conventional ring opening polymerization of tetrahydrofuran. Optional active hydrogen-containing comonomers or copolymers that can be used to form the active hydrogen polymer include ethylene glycol, 1,4-butanediol, 1,6-hexanediol, trimethylol propane, pentaerythritol, 1,4-cyclohexane dimethanol and polyetherpolyols. The optional active hydrogen-containing comonomers or copolymers can also be combined separately with the active hydrogen-containing polymer and polyisocyanate when the isocyanate-functional prepolymer is formed.
Suitable commercially available active hydrogen polymers include "Terathane" 650, 1000, 2000 and 2900 polytetramethylene oxide polyether polyols and "Polymer Te1000" alternating copolymer of tetramethylene oxide and ethylene oxide (all commercially available from E. I. duPont de Nemours & Co.), "Duracarb" 120, 122, 140 and 142 polycarbonate polyols (all commercialy available from PPG Industries, Inc.), and LP-2, LP-3, LP-12, LP-31, LP-32 and LP-33 polysulfide polythiols (all commercially available from Thiokol Corp).
The polyisocyanate and active hydrogen polymer are combined using methods well known to those skilled in the art, to form a prepolymer having residual isocyanate groups. The reaction mixture preferably contains a suitable catalyst, and is conducted under anhydrous conditions. The progress of the reaction can be followed using infrared ("IR") spectroscopy to monitor the size of the NCO peak. For MDI-based prepolymers, a useful procedure is to mix the MDI and a suitable solvent (e.g., 1,2-dichloroethane) at room temperature. Next, the active hydrogen polymer(s) (or mixture thereof with comonomer(s) or copolymer(s)) are added to the MDI solution in four equal portions at 45 minute intervals. The resulting mixture can be mixed overnight at room temperature to ensure completion of the reaction.
The halogenated resin is compatible with the isocyanate-functional prepolymer. As used herein, the term "compatible" refers to a halogenated resin that, when in admixture with the isocyanate-functional prepolymer and an optional solvent of the type described below, forms a single phase liquid solution that persists in such single phase at room temperature for a sufficiently long time period to enable the mixture to be shipped and used in commerce (e.g., one month or more).
Suitable halogenated resins include chlorinated polyisoproprene, postchlorinated polyvinyl chloride (37 CPVC"), copolymers of halogenated monomers and copolymerizable monomers, mixtures thereof, and the like. Chlorinated resins are preferred, and chlorinated polyisoprene resins are most preferred. The halogenated resin contains at least about 58 to about 70 weight percent chlorine, more preferably about 63 to about 70 weight percent chlorine.
Suitable commercially available halogenated resins include "Parlon" S10, S20, S125, and S300 chlorinated polyisoprene resins (Hercules, Inc.), "Alloprene" 5, 10, 20, 40 and 125 chlorinated polyisoprene resins (ICI Americas, Inc.) and "TempRite" 623.times.563, 625.times.563, and 627.times.563 CPVC resins (B. F. Goodrich Co.).
The halogenated resin conveniently is combined with the prepolymer by mixing them neat (in instances where the halogenated resin is compatible without the use of a solvent), or by first dissolving the halogenated resin in one or more suitable solvents, and then combining the resulting solution with any desired adjuvants (e.g., stabilizers or catalysts). Next, the prepolymer is added with stirring to form a uniform mixture. The halogenated resin, prepolymer, and optional solvent preferably are mixed under anhydrous conditions (e.g., a nitrogen atmosphere).
Suitable solvents include acetone, dichloromethane, dichloroethane, methyl ethyl ketone, N-methyl pyrrolidinone, tetrahydrofuran, toluene, xylene, mixtures thereof, and the like. The amount of solvent employed should be sufficient to dissolve the halogenated resin and provide the desired final viscosity for the mixture of halogenated resin and prepolymer.
The amount of prepolymer and halogenated resin in compositions of the invention preferably is an amount sufficient to provide the desired level of handling and bonding performance before and after cure. In general, the prepolymer and halogenated resin can be combined in a weigh ratio between about 1:9 and 9:1, based upon the weight of solids. A preferred weight ratio of prepolymer to halogenated resin is about 1:1 to 9:1.
The compositions of the invention can contain adjuvants of the type customarily employed in adhesives, coatings, and sealants. Suitable adjuvants include extending and reinforcing fillers, pigments, UV stabilizers, UV absorbers, antioxidants, acid scavengers, catalysts, plasticizers, tackifying resins, wetting aids, surfactants, adhesion promoters, dessicants, and the like. The types and amounts of such adjuvants typically are chosen empirically using techniques familiar to those skilled in the art. Compositions of the invention can be put up in packages in accordance with techniques known to those skilled in the art. Suitable packages include, for example, caulking tubes, screw-topped squeezable tubes, cans, drums and the like.
The one-part compositions of the invention are cured by exposure to ambient water, e.g., water vapor or moisture. The two-part compositions of the invention self-cure soon after the two parts are mixed together. In a preferred two-part composition, the prepolymer, halogenated resin, and one or more emulsifying surfactants are combined to form the first part, water is used as the second part, and the two parts are mixed shortly before use under high shear conditions to form a water-based emulsion or dispersion. For both the one-part and two-part compositions of the invention, heat or high humidity will accelerate cure, and low temperatures or low humidity will retard cure. Bonds to damp substrates (e.g., wood) typically cure faster than bonds to dry substrates (e.g., glass).
The compositions of the invention can be employed in any application where a high-performance, high green strength adhesive, coating or sealant is desired. One such use is in the manufacture of adhesively-bonded laminates, where the high green strength of the compositions of the invention permits substrate memory (e.g., warp) to be overcome, thereby simplifying fixturing, reducing fixturing time, and boosting production. The compositions of the invention are also useful where single surface application and moderate curing temperatures are desired. The compositions of the invention can be applied to a variety of articles and substrates, e.g., glasses, metals, plastics, woods, leathers, masonry, textiles and the like. Typical applications include the manufacture of wood-to-wood, wood-to-plastic, and plastic-to-plastic laminates such as plywood, insulated foam panels, and skis. Other applications include building construction (e.g., structural adhesives, panel adhesives, moisture barriers, and glazing sealants), coatings (e.g., deck coatings and roof membranes), and automotive interior assembly.
The following examples are offered to aid understanding of the present invention and are not to be construed as limiting the scope thereof. Unless otherwise indicated, all parts and percentages are by weight. In the examples, several compositions of the invention and comparison compositions we evaluated for green strength and tack using a dead load tensile test and a subjective tack test, and evaluated for bond strength using an overlap shear strength test and a 90.degree. peel test.
The dead load tensile test was performed by brushing a 0.2 to 0.3 mm thick wet film of the composition onto one face of a 25 mm wide by 100 mm long by 3.2 mm thick fiber-reinforced plastic ("FRP") coupon. The wet film was allowed to stand for a specified open time at 24.degree. C. and 50% relative humidity. A second, noncoated coupon was placed perpendicular and in bonding relationship with the first coupon to provide a cross-shaped assembly with a 25 mm by 25 mm bonded area. The cross-shaped assembly was suspended horizontally (from the ends of the upper coupon) between a pair of vertical knife-edge supports. A 500 gram weight was suspended from the bottom coupon, and the assembly was allowed to stand at room temperature. The elapsed time until bond failure (or the absence of failure after 30 minutes) was recorded.
The subjective tack test was performed by placing a fingertip against a film of the composition after the film had been permitted to stand (at 24.degree. C. and 50% relative humidity) until it became tacky. Tack was evaluated on a scale of "0" to "5", with a rating of zero being assigned to films with no tack and a rating of five being assigned to films with tack equivalent to the bond that forms between surfaces coated with a neoprene contact adhesive.
The overlap shear strength test was performed by applying a 0.2 to 0.3 mm thick wet film of the composition to a 25 mm wide by 100 mm long by 15.9 mm thick wooden or 3.2 mm thick plastic coupon. After a specified open time at a specified temperature and 50% relatively humidity, one end of a second, noncoated coupon was overlapped with one end of the first coupon to provide a 25 mm.times.25 mm (in some cases 12.5 mm by 25 mm) bonded area. The assembly was allowed to cure for 7 days at 24.degree. C. and 50% relative humidity, then pulled apart using an "Instron" or a "Thwing-Albert" tensile tester operated at a crosshead separation rate of 5 mm/min.
The 90.degree. peel strength test was performed by applying a 0.2 to 0.3 mm thick wet film of the composition to a 25 mm wide by 254 mm long by 3.2 mm thick FRP coupon. After a specified open time at a specified temperature and 50% relative humidity, a 25 mm wide by 254 mm long by 1 mm thick ABS coupon was laminated onto the coated face of the FRP coupon. The resulting assembly was passed through a nip roller, allowed to cure at 24.degree. C. and 50% relative humidity for 7 days, then pulled apart at a peel angle of 90.degree. using an Instron tensile tester operated at a crosshead separation rate of 51 mm/min.
Prepolymer Examples 1 through 20
In a series of runs, a polyisocyanate, a mixture of short- and long-chain active hydrogen polymers and a solvent were combined to form a series of isocyanate-functional prepolymers. Set out below in Table I are the Prepolymer Example No., type and amount (expressed in terms of NCO equivalents) of polyisocyanate, type and amount (expressed in terms of OH equivalents) of active hydrogen-containing material, solvent, and percent solids obtained. The compositions of Prepolymer Example Nos. 12, 13, 14, and 15 contained 0.14, 0.14, 0.33, and 0.33 weight percent respectively of "Epon 828" epoxide (commercially available from Shell Chemical Co.) as a stabilizer.
TABLE I______________________________________ Poly-Prepolymer isocyanate Active hydrogenExample A- polymer Sol- %No. Type mount Type Amount vent Solids______________________________________ 1 TDI 3.25 eq T1000 1 eq toluene 90-93 BD 0.26 eq TMP 0.26 eq 2 MDI 3.25 eq T1000 1 eq toluene 90-94 BD 0.26 eq TMP 0.26 eq 3 TDI 3.25 eq T2000 1 eq toluene 90-92 BD 0.26 eq TMP 0.26 eq 4 MDI 3.25 eq T2000 1 eq toluene 90-92 BD 0.26 eq TMP 0.26 eq 5 MDI 3.25 eq T1000 1 eq DCM 80 BD 0.26 eq TMP 0.26 eq 6 MDI 3.25 eq T1000 0.8 eq DCM 80 PCP0230 0.2 eq BD 0.26 eq TMP 0.26 eq 7 MDI 3.25 eq T1000 0.6 eq DCM 80 PCP0230 0.4 eq BD 0.26 eq TMP 0.26 eq 8 MDI 3.25 eq T1000 0.4 eq DCM 80 PCP0230 0.6 eq BD 0.26 eq TMP 0.26 eq 9 MDI 3.25 eq T1000 0.2 eq DCM 80 PCP0230 0.8 eq BD 0.26 eq TMP 0.26 eq10 MDI 3.25 eq T1000 1 eq THF 80 BD 0.26 eq TMP 0.26 eq11 MDI 3.25 eq T1000 1 eq DCE 80 BD 0.26 eq TMP 0.26 eq12 MDI 3.25 eq T1000 1 eq DCE 67 BD 0.26 eq TMP 0.26 eq13 MDI 3.25 eq D122 1 eq DCE 67 BD 0.26 eq TMP 0.26 eq14 MDI 3.25 eq LP3 1 eq DCE 67 BD 0.26 eq TMP 0.26 eq15 MDI 3.25 eq C1000 1 eq DCE 67 BD 0.26 eq TMP 0.26 eq16 TDI 3.25 eq PPG1025 1 eq toluene 93 BD 0.26 eq TMP 0.26 eq17 MDI 3.25 eq PPG1025 1 eq toluene 94 BD 0.26 eq TMP 0.26 eq18 MDI 2.16 eq BD 1 eq 50:50 54 THF: MEK19 MDI 2.16 eq T1000 0.66 eq toluene 67 BD 0.17 eq TMP 0.17 eq20 MDI 3.25 eq T1000 1 eq -- 100 BD 0.26 eq TMP 0.26 eq______________________________________ Key to entries in table: TDI = Mixture of 2,4 and 2,6toluene diisocyanate. MDI = 4,4Diphenylmethane diisocyanate. T1000 = "Terathane 1000", a 1000 M.W. poly(tetramethylene oxide) diol (commercially available from E. I. duPont de Nemours & Co.). T2000 = "Terathane 2000", a 2000 M.W. poly(tetramethylene oxide) diol (commercially available from E. I. duPont de Nemours & Co.). BD = 1,4Butanediol. TMP = Trimethylolpropane. PCP0230 = "Niax PCP 0230", a 1260 M.W. poly(epsiloncaprolactone) diol (commercially available from Union Carbide Corp.). DCM = Dichloromethane. DCE = 1,2Dichloroethane. D122 = "Duracarb 122", a linear aliphatic polycarbonate polyol (commercially availble from PPG Industries, Inc.). LP3 = "LP3" polysulfide polythiol (commercially available from Thiokol Corp.). C1000 = "Carbowax 1000", a 1000 M.W. poly(ethylene oxide) diol (commercially available from Union Carbide Corp.). PPG1025 = "PPG 1025", a 1000 M.W. poly(propylene oxide) diol (commerciall available from Union Carbide Corp.). THF = Tetrahydrofuran. MEK = methyl ethyl ketone.





EXAMPLES 1 THROUGH 23 AND COMPARISON EXAMPLES 1 THROUGH 16
In a series of runs, an isocyanate-functional prepolymer, a halogenated resin, and one or more solvents were combined to form uniform mixtures and evaluated for compatibility. Set out below in Table II are the Example number or Comparison Example ("C.E.") number, type of prepolymer (identified by "P.E." number, an abbreviation for "Prepolymer Example"), weight percent of prepolymer (based on a comparison of prepolymer solids weight to the total mixture weight), type and weight percent of halogenated resin (similarly expressed), type of solvent, weight percent of solvent (based on a comparison of the solvent weight to the total mixture weight), and an indication of whether or not the halogenated resin was compatible with the prepolymer. The compositions of Examples 12, 14-16, 18, 20, and Comparison Examples 1, 3-5 and 10 each contained 0.016 weight % dibutyltin dialurate. The composition of Example 13 contained 0.47 weight % each of dilaurylthiodipropionate and tributylphosphite, 0.11 weight % 2,6-di-t-butyl-4-methyl phenol, and 0.02 weight % dibutyltin dilaurate. The compositions of Example 19 and Comparison Example 9 each contained 0.027 weight % dibutyltin dialurate. The composition of Example 21 contained 0.07 weight % "ERL 4221" epoxide (commercially available from Union Carbide Corp.), 0.05 weight % "FC-430" fluorosurfactant (commercially available from 3M), 0.04 weight % each of "Irganox 1010" hindered phenol (commercially available from Ciba-Geigy Corp.) and "Weston 619" diphosphite (commercially available from Borg-Warner Corp.), and 0.03 weight % dibutyltin dilaurate. The compositions of Examples 22 and 23 and Comparison Examples 15 and 16 each contained 0.032 weight % dibutyltin dilaurate. The compositions of Comparison Examples 2 and 13 each contained 0.013 weight % dibutyltin dilaurate. The composition of Comparison Example 14 contained 0.02 weight % dibutyltin dilaurate.
TABLE II__________________________________________________________________________ HalogenatedEx. Prepolymer resin Solvent(s)No. Type Weight % Type Weight % Type Weight % Compatible__________________________________________________________________________ 1 P.E.1 63 S300 8 Toluene 29 yes 2 P.E.2 64 S300 8 Toluene 28 yes 3 P.E.3 62 S300 8 Toluene 30 yes 4 P.E.4 63 S300 8 Toluene 29 yes 5 P.E.5 45 S300 5 DCM 27 yes MEK 23 6 P.E.6 45 S300 5 DCM 30 yes MEK 20 7 P.E.7 45 S300 5 DCM 30 yes MEK 20 8 P.E.8 45 S300 5 DCM 30 yes MEK 20 9 P.E.9 45 S300 5 DCM 30 yes MEK 2010 P.E.10 45 S300 5 THF 50 yes11 P.E.11 45 S300 5 DCE 30 yes MEK 2012 P.E.12 27 S300 12 DCE 13 yes MEK 4713 P.E.12 27 S300 12 DCE 13 yes MEK 4714 P.E.12 27 TR623 3 DCE 13 yes THF 5715 P.E.12 35 TR625 4 DCE 17 yes THF 4316 P.E.12 35 TR627 4 DCE 17 yes THF 4317 P.E.12 28 A40 12 MEK 60 yes18 P.E.13 27 S300 12 DCE 13 yes MEK 4719 P.E.14 45 S300 5 DCE 50 yes20 P.E.14 27 S300 12 DCE 61 yes21 P.E.19 27 S300 12 Toluene 13 yes MEK 4722 P.E.20 28 S300 12 THF 60 yes23 P.E.20 28 TR627 12 THF 60 yesC.E.1 P.E.12 24 NAC 11 DCE 12 no MEK 53C.E.2 P.E.12 22 NAC 10 DCE 11 no THF 57C.E.3 P.E.12 27 H20 12 DCE 14 no MEK 47C.E.4 P.E.12 27 H20 12 DCE 14 no THF 47C.E.5 P.E.12 27 VMCH 12 DCE 14 NTGS MEK 47C.E.6 P.E.12 18 G121 2 DCE 9 no THF 71C.E.7 P.E.12 16 G121 4 DCE 8 no THF 72C.E.8 P.E.12 14 G121 6 DCE 7 NTGS THF 73C.E.9 P.E.15 49 S300 5 DCE 24 no MEK 22C.E.10 P.E.15 27 S300 12 DCE 14 no MEK 47C.E.11 P.E.16 63 S300 8 Toluene 29 noC.E.12 P.E.17 63 S300 8 Toluene 29 noC.E.13 P.E.18 18 S300 2 MEK 16 NTGS THF 64C.E.14 P.E.20 18 G121 8 THF 75 NTGSC.E.15 P.E.20 28 SF310 12 THF 60 noC.E.16 P.E.20 28 SF310 12 THF 12 no MEK 48__________________________________________________________________________ Key to entries in table: S300 = "Parlon" S300 chlorinated polyisoprene (commercially available fro Hercules, Inc.). DCM = Dichloromethane. DCE = 1,2Dichloroethane. MEK = Methyl ethyl ketone. THF = Tetrahydrofuran. TR 623 = "TempRite" 623 .times. 653 CPVC resin (commercially available from the B. F. Goodrich Co.). TR 625 = "TempRite" 625 .times. 653 CPVC resin (commercially available from the B. F. Goodrich Co.). TR 627 = "TempRite" 627 .times. 653 CPVC resin (commercially available from the B. F. Goodrich Co.). A40 = "Alloprene" 40 chlorinated polyisoprene resin (commercially available from ICI, America, Inc.). NAC = "Neoprene" AC polychlorobutadiene, containing 39.2 weight % chlorin (commercially available from E. I. Dupont de Nemours & Co.). H20 = "Hypalon" 20 chlorosulfonated polyethylene, containing 27 to 31% chlorine (commercially available from E. I. DuPont de Nemours & Co.). VMCH = "Vinylite" VMCH 86/14 vinyl chloride/vinyl acetate copolymer, containing 46.4 weight % chlorine (commercially available from Union Carbide Corp.). G121 = "Geon" 121 polyvinyl chloride resin, containing 56.8% chlorine (commercially available from the B. F. Goodrich Co.). SF310 = "Saran" F310, believed to be a copolymer of vinylidene chloride with acrylonitrile or methacrylaonitrile, and believed to contain about 56.7 weight % chlorine (commercially available from Dow Chemical Co.). NTGS = Mixture appeared to be compatible, but no improvement in tack or green strength was noted.
These examples illustrate formation of compatible mixtures from a variety of isocyanate-functional prepolymers and halogenated resins. For each Example a film of the isocyanate-functional prepolymer alone had no tack, whereas a film of the compatible mixture was tacky within a few minutes after coating. Tackiness generally reached a maximum value within about 20 to 30 minutes at room temperature, then diminished as the film cured. These mixtures contained halogenated resins whose halogen content was between about 58 and about 70 weight percent.
For each Comparison Example, the mixture was incompatible, or compatible but non-tacky and lacking in green strength. These mixtures contained halogenated resins whose halogen content was less than about 58 weight percent (Comparison Examples 1-8 and 14-16), or were prepared from prepolymers derived from polyethylene oxide diol (Comparison Examples 9 and 10), polypropylene oxide diol (Comparison Examples 11 and 12) or 1,4-butanediol (Comparison Example 13).
EXAMPLE 21
Dead load tensile test
The compositions of Example Nos. 11 through 23 were evaluated using the above-described dead load tensile test. The compositions of Example Nos. 19 and 20 did not pass the test when a 500 g weight was used but did have enhanced green strength and would have passed using a smaller weight. Set out in Table III below for the compositions of Examples 11 through 18 and 21 through 23 are the open time and the time to failure.
TABLE III______________________________________Composition Time toof Example Open time, min. failure, min.______________________________________11 2 4 3 4 4 50% N.F.12 2 N.F.13 2 N.F.14 3 N.F.15 2 50% N.F. 3 75% N.F.16 2 N.F.17 3 50% N.F.18 3 N.F.21 2 N.F.22 3 N.F.23 3 75% N.F.______________________________________ Key to entries in table: N.F. = No failure within 30 minutes. 50% N.F. signifies that half of the samples did not fail within 30 minutes, and 75% N.F. signifies that threefourths of the samples did not fail within 30 minutes.
In each instance, exclusion of the halogenated resin resulted in immediate failure of the dead load tensile test at the same open time. This example illustrates the very useful improvement in green strength that is provided in this invention.
EXAMPLE 22
Subjective tack test and overlap shear test
The compositions of Examples 1 through 12 and 18 were evaluated using the above-described subjective tack test and overlap shear strength test. Set out below in Table IV are the composition employed, test substrates, open time and temperature, subjective tack test result, and overlap shear strength test result for each composition.
TABLE IV______________________________________ Sub- jec- OverlapComposi- tive sheartion of Open Open tack strength,Ex. No. Substrate Time Temp test kg/cm.sup.2(1)______________________________________1 maple/maple 20 min. 24.degree. C. 1 55.2.sup.(2)2 maple/maple 20 min. 24.degree. C. 2 143.8.sup.(2)3 maple/maple 20 min. 24.degree. C. 1 49.6.sup.(2)4 maple/maple 20 min. 24.degree. C. 2 59.3.sup.(2)5 maple/maple 20 min. 24.degree. C. 3 64.5 PVC/PVC 20 min. 24.degree. C. 3 57.16 maple/maple 20 min. 24.degree. C. 3 53.4 PVC/PVC 20 min. 24.degree. C. 3 62.47 maple/maple 20 min. 24.degree. C. 3 56.0 PVC/PVC 20 min. 24.degree. C. 3 59.68 maple/maple 20 min. 24.degree. C. 3 62.3 PVC/PVC 20 min. 24.degree. C. 3 62.19 maple/maple 20 min. 24.degree. C. 3 63.9 PVC/PVC 20 min. 24.degree. C. 3 64.010 pine/PVC 1 min. 71.degree. C. 3 --11 ABS/FRP .sup.(3) .sup.(3) 3 --12 oak/oak 3 min. 24.degree. C. -- 85.8(-40.degree. C.) oak/oak 3 min. 24.degree. C. -- 81.6 oak/oak 3 min. 24.degree. C. -- 45.0(82.degree. C.) FRP/FRP 3 min. 24.degree. C. -- 158.2(-40.degree. C.) FRP/FRP 3 min. 24.degree. C. -- 99.8 FRP/FRP 3 min. 24.degree. C. -- 59.1(82.degree. C.)18 FRP/FRP 3 min. 24.degree. C. -- 39.4(82.degree. C.)______________________________________ Key to entries in table: PVC = Polyvinyl chloride. ABS = Acrylonitrilebutadiene-styrene plastic. FRP = Fiberreinforced plastic (a styrene molding compound containing glas fibers). Footnotes for entries in table: .sup.(1) 25 mm .times. 25 mm bond evaluated at 24.degree. C., unless otherwise indicated. .sup.(2) 25 mm wide bond, overlapped 12.5 mm. .sup.(3) open time and temperature were two minutes at room temperature, followed by one minute at 71.degree. C., followed by one minute at room temperature.
For each of the above compositions, a subjective tack test score of zero was obtained when the halogenated resin was excluded. This example shows that tack was enhanced by addition of halogenated resin. Several of the compositions had excellent shear strength at room elevated temperatures.
EXAMPLE 23
90.degree. Peel Strength test
The composition of Example 10 was evaluated using a one minute open time at 72.degree. C. and the above-described 90.degree. peel strength test. At temperatures of -29.degree. C., 24.degree. C. and 82.degree. C. the composition exhibited 90.degree. peel strength values of 1.25, 0.18 and 1.25 kg/cm, respectively.
Various modifications and alterations of this invention will be apparent to those skilled in the art without departing from the scope and spirit of this invention, and the latter should not be restricted to that set forth herein for illustrative purposes.
Claims
  • 1. A curable composition comprising a mixture of:
  • (a) isocyanate-functional prepolymer derived from:
  • (i) polyisocyanate, and
  • (ii) active hydrogen-containing low molecular weight polymer selected from the group consisting of polytetramethylene oxide polyols, polycarbonate polyols, and polysulfide polythiols, and
  • (b) halogenated resin compatible with said prepolymer and dissolved in said prepolymer to form a single phase liquid solution, said resin containing about 58 to about 70 weight percent halogen.
  • 2. A composition according to claim 1, wherein said polyisocyanate comprises 4,4'-diphenylmethane diisocyanate.
  • 3. A comparison according to claim 1, wherein said polymer comprises polytetramethylene oxide polyol.
  • 4. A composition according to claim 3, wherein said polymer contains repeating units derived from tetramethylene oxide, said repeating units occurring in blocks of two or more.
  • 5. A composition according to claim 1, wherein said polymer comprises polycarbonate polyol.
  • 6. A composition according to claim 1, wherein said polymer comprises polysulfide polythiol.
  • 7. A composition according to claim 1, wherein said polymer has a number average molecular weight between 162 and about 10,000.
  • 8. A composition according to claim 1, wherein said polymer has a number average molecular weight between about 300 and about 3000.
  • 9. A composition according to claim 1, wherein said halogen is chlorine.
  • 10. A composition according to claim 9, wherein said resin contains about 63 to about 70 weight percent chlorine.
  • 11. A composition according to claim 9, wherein said resin comprises chlorinated polyisoprene.
  • 12. A composition according to claim 9, wherein said resin comprises postchlorinated polyvinyl chloride.
  • 13. A composition according to claim 1, further comprising solvent.
  • 14. A composition according to claim 13, wherein said prepolymer and said resin are mixed in a weight ratio between about 1:9 and 9:1.
  • 15. A composition according to claim 14, wherein said ratio is between about 1:1 and 1:9.
  • 16. A composition according to claim 1, wherein said mixture is a one-part moisture-curable composition.
  • 17. An article comprising a substrate having thereon a layer or layers of a composition comprising a mixture of:
  • (a) isocyanate-functional prepolymer derived from:
  • (i) polyisocyanate, and
  • (ii) active hydrogen-containing low molecular weight polymer selected from the group consisting of polytetramethylene oxide polyols, polycarbonate polyols, and polysulfide polythiols, and
  • (b) halogenated resin compatible with said prepolymer and dissolved in said prepolymer to form a single phase liquid solution, said resin containing about 58 to about 70 weight percent halogen.
  • 18. A method for adhering, coating or sealing an article, comprising the step of applying thereto a layer or layers of a composition comprising a mixture of:
  • (a) isocyanate-functional prepolymer derived from:
  • (i) polyisocyanate, and
  • (ii) active hydrogen-containing low molecular weight polymer selected from the group consisting of polytetramethylene oxide polyols, polycarbonate polyols, and polysulfide polythiols, and
  • (b) halogenated resin compatible with said prepolymer and dissolved in said prepolymer to form a single phase liquid solution, said resin containing about 58 to about 70 weight percent halogen.
CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part of copending application Ser. No. 762,042, filed Aug. 2, 1985, now abandoned.

US Referenced Citations (26)
Number Name Date Kind
3315380 Mack, III et al. Apr 1967
3337481 Singelyn et al. Aug 1967
3357939 Reischl et al. Dec 1967
3381056 Beer Apr 1968
3444266 Reischl et al. May 1969
3574149 Harrington Apr 1971
3594449 Binder Jul 1971
3637359 Molloy et al. Jan 1972
3645933 Flint Feb 1972
3714077 Cobbledick et al. Jan 1973
3718611 Maxey et al. Feb 1973
3792000 Conger et al. Feb 1974
3810851 Norman et al. May 1974
3876571 Cobbledick et al. Apr 1975
3882191 Balatoni et al. May 1975
3917742 Harlan Nov 1975
3929928 Wolf, Jr. et al. Dec 1975
3931062 Cobbledick Jan 1976
3947403 McCready Mar 1976
3970716 Evers et al. Jul 1976
3981762 Davis et al. Sep 1976
4162276 Rim et al. Jul 1979
4173691 Treadwell Nov 1979
4217254 Legue Aug 1980
4256615 Legue Mar 1981
4340682 Legue Jul 1982
Foreign Referenced Citations (2)
Number Date Country
2644639 Apr 1978 DEX
1552992 Sep 1979 GBX
Non-Patent Literature Citations (2)
Entry
"Compatibility of Parlon.RTM. Chlorinated Rubber with Hydrocarbon Resins, Alkyds, Reactive Urethanes, and Other Types of Resins", technical publication of Hercules, Inc. (1981).
"TempRite.TM. CPVC", technical publication of the B. F. Goodrich Company (1982).
Continuation in Parts (1)
Number Date Country
Parent 762042 Aug 1985