Claims
- 1. A fluid composition stable under substantially anhydrous conditions and curable to a self-bonding elastic solid in the presence of moisture which comprises:
- (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR10## wherein R and R.sup.1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000;
- (b) from 0.01 to 5.0 parts by weight of a cross-linking silane of the formula:
- R.sub.m.sup.2 Si (OR.sup.3).sub.4-m
- wherein R.sup.2 and R.sup.3 have the values defined for R and R.sup.1 hereinabove and m has a value of 0 to 3 and an average value based on the total amount of silane in the composition of 0 to 1.99; and
- (c) from 0.1 to 10 parts by weight of a silanol reactive organometallic ester compound of a metal other than silicon, said compound being a partially chelated ester of a lower aliphatic alcohol with a .beta.-dicarbonyl compound or a partial hydrolyzate of such compounds which retain at least one hydrocarbonoxy radical or substituted by hydrocarbonoxy radical attached to the metal atom through M--O--C linkages wherein M is the metal, the weight ratio of components (c) to (b) always being at least 0.5 to 1.
- 2. A fluid composition stable under substantially anhydrous conditions and curable to a self-bonding elastic solid in the presence of moisture which comprises:
- (a) 100 parts by weight of a silanol chainstopped polydiorganosiloxane of the formula: ##STR11## wherein R and R.sup.1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000;
- (b) from 0.01 to 5.0 parts by weight of a cross-linking silane of the formula:
- R.sub.m.sup.2 Si (OR.sup.3).sub.4-m
- wherein R.sup.2 and R.sup.3 have the values defined for R and R.sup.1 hereinabove and m has a value of 0 to 3 and an average value based on the total amount of silane in the composition of 0 to 1.99; and
- (c) from 0.1 to 10 parts by weight of a silanol reactive organometallic ester compound of a metal other than silicon, said compound being a partially chelated ester of a lower aliphatic alcohol with a .beta.-dicarbonyl compound or a partial hydrolyzate of such compounds which retain at least one hydrocarbonoxy radical or substituted hydrocarbonoxy radical attached to the metal atom through M--O--C linkages wherein M is the metal, the weight ratio of components (c) to (b) always being at least unity.
- 3. A composition as defined in claim 1 wherein the total of the number of moles of cross-linking silane (b) is less than the total of the number of moles of terminal silanol groups in polydiorganosiloxane component (a).
- 4. A composition as defined in claim 1 wherein the total of the number of moles of silanol reactive ester linkages in organometallic ester compound (c) is equal to or greater than the total of the number of moles of terminal silanol groups in polydiorganosiloxane component (a).
- 5. A composition as defined in claim 3 wherein the total of the number of moles of silanol reactive ester linkages in organometallic ester compound (c) is equal to or greater than the total of the number of moles of terminal silanol groups in polydiorganosiloxane component (a).
- 6. A composition as defined in claim 1 wherein the weight ratio of components (c) to (b) is from 0.5 to 1 to 50 to 1.
- 7. A composition as defined in claim 1 wherein the weight ratio of components (c) to (b) is from 0.5 to 1 to 10 to 1.
- 8. A composition as defined in claim 7 wherein the weight ratio of components (c) to (b) is from 0.5 to 1 to 5 to 1.
- 9. A composition as defined in claim 1 wherein the viscosity of component (a) is within the range of 2,000 to 1,000,000 cps. at 25.degree. C.
- 10. A composition as defined in claim 9 wherein the viscosity of component (a) is within the range of 20,000 to 200,000 cps. at 25.degree. C.
- 11. A composition as defined in claim 1, wherein, in component (a), at least 50% of the total number of R and R.sup.1 groups are alkyl radicals and any remaining groups are aryl radicals.
- 12. A composition as defined in claim 11 wherein the alkyl radicals are methyl radicals and any remaining aryl radicals are phenyl radicals.
- 13. A composition as defined in claim 1 wherein, in component (b), at least 50% of the total number of R.sup.2 and R.sup.3 groups are alkyl radicals and any remaining groups are aryl radicals and m is 1.
- 14. A composition as defined in claim 13 wherein the alkyl radicals are methyl radicals and any remaining aryl radicals are phenyl radicals.
- 15. A composition as defined in claim 1 wherein, in said organometallic ester component (c), the metal M is selected from lead, tin, zirconium, antimony, iron, cadmium, barium, calcium, titanium, bismuth, manganese, zinc, chromium, cobalt, nickel, aluminum, gallium or germanium.
- 16. A composition as defined in claim 15 wherein, in said organometallic ester component (c), the metal M is titanium.
- 17. A fluid composition stable under substantially anhydrous conditions and chain-stopped to a self-bonding elastic solid in the presence of moisture which comprises:
- (a) 100 parts by weight of a silanol chainstopped polydiorganosiloxane of the formula: ##STR12## wherein R and R.sup.1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from 10 to 15,000;
- (b) from 0.01 to 5.0 parts by weight of a cross-linking silane of the formula:
- R.sub.m.sup.2 Si (OR.sup.3).sub.4-m
- wherein R.sup.2 and R.sup.3 have the values defined for R and R.sup.1 hereinabove and m has a value of 0 to 3 and an average value based on the total amount of silane in the composition of 0 to 1.99; and
- (c) from 0.1 to 10 parts by weight of a titanium chelate catalyst of the formula: ##STR13## wherein R.sup.4 is hydrogen, or an organic radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl, or carboxyalkyl; R.sup.5 is a radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl; R.sup.6 is selected from same group as R.sup.4 and in addition from halo, cyano, nitro, carboxy ester, or acyl and hydrocarbyl substituted by halo, cyano, nitro, carboxy ester and acyl, the total number of carbon atoms in the R.sup.4 and in the R.sup.6 substituted alkanedioxy radical being not more than about 18; R.sup.7 is selected from hydrogen or an organic radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl, or acyl and, when taken together with R.sup.5 forms together with the carbon atoms to which they are attached a cyclic hydrocarbon substituent of up to about 12 carbon atoms or such a substituent substituted with one or more of a chloro, nitro, acyl, cyano or carboxy ester substituents; X is a radical of up to 20 carbon atoms selected from hydrocarbyl, halohydrocarbyl, cyanoalkyl, alkoxy, haloalkoxy, cyanoalkoxy, amino or ether and polyether groups of the formula -- (C.sub.q H.sub.2q O).sub.v R where q is from 2 to 4, v is from 1 to 20 and R is an organic radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl or cyano lower alkyl, a is 0 or an integer of up to 8 and, when a is 0, the >C--R.sub.2.sup.4 groups are bonded to each other in a cyclic fashion, and R.sup.8 is a radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl or cyano lower alkyl, the weight ratio of components (c) to (b) always being at least 0.5 to 1.
- 18. A fluid composition stable under substantially anhydrous conditions and curable to a self-bonding elastic solid in the presence of moisture which comprises:
- (a) 100 parts by weight of a silanol chain-stopped polydiorganosiloxane of the formula: ##STR14## wherein R and R.sup.1 are each, independently, organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl and n is an average number of from about 10 to 15,000;
- (b) from 0.01 to 5.0 parts by weight of a cross-linking silane of the formula:
- R.sub.m.sup.2 Si (OR.sup.3).sub.4-m
- wherein R.sup.2 and R.sup.3 have the values defined for R and R.sup.1 hereinabove and m has a value of 0 to 3 and an average value based on the total amount of silane in the composition of 0 to 1.99; and
- (c) from 0.1 to 10 parts by weight of a titanium chelate catalyst of the formula: ##STR15## wherein R.sup.4 is hydrogen, or an organic radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl, or carboxyalkyl; R.sup.5 is a radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl; R.sup.6 is selected from same group as R.sup.4 and in addition from halo, cyano, nitro, carboxy ester, or acyl and hydrocarbyl substituted by halo, cyano, nitro, carboxy ester and acyl, the total number of carbon atoms in the R.sup.4 and in the R.sup.6 substituted alkanedioxy radical being not more than about 18; R.sup.7 is selected from hydrogen or an organic radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl, or acyl and, when taken together with R.sup.5 forms together with the carbon atoms to which they are attached a cyclic hydrocarbon substituent of up to about 12 carbon atoms or such a substituent substituted with one or more of a chloro, nitro, acyl, cyano or carboxy ester substituents; X is a radical of up to 20 carbon atoms selected from hydrocarbyl, halohydrocarbyl, cyanoalkyl, alkoxy, haloalkoxy, cyanoalkoxy, amino or ether and polyether groups of the formula --(C.sub.q H.sub.2q O).sub.v R where q is from 2 to 4, v is from 1 to 20 and R is an organic radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl or cyano lower alkyl, a is 0 or an integer of up to 8 and, when a is 0, the >C--R.sub.2.sup.4 groups are bonded to each other in a cyclic fashion, and R.sup.8 is a radical of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl or cyano lower alkyl, the weight ratio of components (c) to (b) always being at least unity.
- 19. A composition as defined in claim 17 wherein said component (c) is of the formula: ##STR16##
- 20. A composition as defined in claim 17 wherein, in component (b), R.sup.2 and R.sup.3 are alkyl and, in component (c), R.sup.4 and R.sup.6 are hydrogen and R.sup.5 is alkyl.
- 21. A composition as defined in claim 17 wherein, in component (b), R.sup.2 and R.sup.3 are methyl, and, in component (c) R.sup.5 is methyl, X is --OC.sub.15 H.sub.31, and a is 1.
- 22. A composition as defined in claim 21 wherein, in component (c), R.sup.4 and R.sup.6 are each hydrogen.
- 23. A composition as defined in claim 20 wherein, in component (b), R.sup.2 and R.sup.3 are methyl and, in component (c), R.sup.5 and X are methyl and R.sup.4 and R.sup.6 are hydrogen.
- 24. A composition as defined in claim 17 wherein component (a) is ##STR17## wherein n is from about 300 to about 5,260; component (b) is (CH.sub.3)Si(OCH.sub.3).sub.3 ; and component (c) is ##STR18##
- 25. A composition as defined in claim 17 wherein component (a) is ##STR19## wherein n is from about 370 to about 1,350; component (b) is
- CH.sub.3 Si(OCH.sub.3).sub.3 ;
- and
- component (c) is ##STR20##
- 26. A composition as defined in claim 17 wherein, in component (c), a is 0 or 1 and R.sup.4 and R.sup.6 are hydrogen or methyl.
- 27. A composition as defined in claim 1 wherein from about 10 to about 100 parts by weight of a filler per 100 parts of the silanol chain-stopped polydiorganosiloxane is also included.
- 28. A composition as defined in claim 27 wherein said filler is calcium carbonate or a mixture of fumed silica and calcium carbonate.
- 29. A composition as defined in claim 1 wherein from 0.2 to 2 parts of an adhesion promoter per 100 parts of the silanol chain-stopped polydiorganosiloxane is also included.
- 30. A composition as defined in claim 29 wherein said adhesion promoter is of the formula: ##STR21## wherein G is the same as R.sup.10, hereinafter defined, a (R.sup.11 O).sub.3-b -- R.sub.b.sup.10 --Si--R.sup.9 radical, styryl, vinyl, allyl, chloroallyl or cyclohexenyl; R.sup.9 is a divalent radical selected from alkylenearylene, alkylene, cycloxyene and halosubstituted such divalent radicals; R.sup.10 is a radical of up to 8 carbon atoms selected from hydrocarbyl or halohydrocarbyl, and R.sup.11 is a radical of the type defined for R.sup.10 and also cyano lower alkyl; and b is 0 to 3.
- 31. A composition as defined in claim 29 wherein said adhesion promoter is 1,3,5-tris-trimethoxysilylpropylisocyanurate.
- 32. A composition as defined in claim 29 wherein said adhesion promoter is bis-1,3-trimethoxysilylpropylisocyanurate.
- 33. A composition as defined in claim 1 wherein from about 0.3 to about 20 parts by weight of a polydiorganosiloxane viscosity depressant per 100 parts of the silanol chain-stopped polydiorganosiloxane component (a) is also included.
- 34. A composition as defined in claim 33 wherein said viscosity depressant is of the formula: ##STR22## wherein R.sup.12 and R.sup.13 are each organic radicals of up to 8 carbon atoms selected from hydrocarbyl, halohydrocarbyl and cyano lower alkyl, R.sup.14 and R.sup.15 are, independently, hydrogen or radicals as defined for R.sup.12 and R.sup.13 and x has a value of from 2 to 46.
- 35. A composition as defined in claim 34 wherein at least 50% of the total number of R.sup.12 and R.sup.13 groups are alkyl radicals and any remaining such groups are aryl radicals.
- 36. A composition as defined in claim 35 wherein the alkyl radicals are methyl radicals and any remaining aryl radicals are phenyl radicals.
- 37. A composition as defined in claim 34 wherein in the viscosity depressant, R.sup.14 and R.sup.15 are hydrogen or methyl, R.sup.12 and R.sup.13 are methyl or methyl and phenyl in a ratio of about 70:30, and x is an integer of from 3 to 50.
- 38. A method of preparing a rubbery material which comprises preparing a composition in accordance with claim 1 under substantially anhydrous conditions and thereafter exposing the composition to moisture until it cures to a rubbery material.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of application Ser. No. 417,787, filed Nov. 21, 1973, now abandoned.
US Referenced Citations (19)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
417787 |
Nov 1973 |
|