Patent Application
20150203629
The invention relates to curable compositions comprising at least one epoxy resin and at least one hardener wherein the hardener is a compound of formula (I) or (II)
where R1 and R2 are each independently selected from the group of substituents having the formula —(CH2)x—NH2 and x is in each case independently 0, 1, 2, 3 or 4, to surfaces comprising such compositions, to methods comprising applying a coating material comprising such compositions and to the use of such compositions as surface protection.
Epoxy resins are prepolymers comprising two or more epoxy groups per molecule. The reaction of these resins with a range of hardeners affords crosslinked polymers. These polymers may be thermosets and may be used in the fields of civil engineering, particularly in industrial floors, sealing systems and concrete maintenance and repair products, fibre composites, potting compositions, paints/varnishes and adhesives for example. An overview of resins and hardeners, including their properties, and the use thereof in the field of civil engineering may be found in H. Schuhmann, “Handbuch Betonschutz durch Beschichtungen” [Handbook of concrete protection using coatings], Expert Verlag 1992, pp. 396-428. The use of resins and hardeners in the field of fibre composites is described in P. K. Mallick, “Fiber-Reinforced Composites, Materials, Manufacturing, and Design”, CRC Press, pp. 60-76.
In addition to epoxy resins, amines and other compounds involved in the crosslinking reaction, industrially relevant compositions of this type typically also comprise nonreactive components as auxiliaries. Although said nonreactive components are not covalently incorporated, it must be assumed that a certain proportion thereof remains in the composition once curing has completed and is continuously released into the environment over a long period of time. Said nonreactive components may therefore contribute to indoor pollution.
Benzyl alcohol is a typical nonreactive component of curable epoxy-containing compositions. Benzyl alcohol is miscible with the reactive components and acts as a diluent, as a viscosity reducer and thus as a flow promoter. Benzyl alcohol also catalyses the curing reaction.
Against the background of the classification of benzyl alcohol as a VOC (volatile organic compound) by the EU decopaint directive there is, however, a need to develop epoxy systems that do not require benzyl alcohol.
The problem addressed by the present invention is accordingly that of developing amine hardeners for epoxy resins to obtain formulations that cure sufficiently at ambient temperatures with very small quantities of benzyl alcohol and preferably without the use of benzyl alcohol.
A further problem addressed by the invention is that of providing a curable epoxy resin-based composition while retaining individual processing-relevant properties or the entirety of the processing-relevant properties such as very low initial viscosity, sufficiently high hardnesses and a high conversion over a period of from one to seven days at room temperature and avoiding any detrimental effects on through-curing compared to comparable compositions comprising benzyl alcohol.
These and further problems are solved by the subject-matter of the present application and in particular also by the subject-matter of the accompanying independent claims, the dependent claims specifying embodiments of the invention.
The problem addressed by the invention is solved in a first aspect by a curable composition comprising at least one epoxy resin and at least one hardener
In a first embodiment of the first aspect, the problem is solved by a composition where x in R1 and R2 is 1.
In a second embodiment of the first aspect, which is also an embodiment of the first embodiment, the problem is solved by a composition wherein the hardener is 5-aminomethyl-2-furfurylamine (HMF diamine).
In a third embodiment of the first aspect, which is also an embodiment of the first to second embodiments, the problem is solved by a composition wherein the epoxy resin is selected from the group comprising epoxy resins based on bisphenol A diglycidyl ether, bisphenol F diglycidyl ether and cycloaliphatic types.
In a fourth embodiment of the first aspect, which is also an embodiment of the first to third embodiments, the problem is solved by a composition wherein the composition comprises less than 20 g of benzyl alcohol per 100 g of the entirety of all hardeners comprised therein.
In a fifth embodiment of the first aspect, which is also an embodiment of the first to fourth embodiments, the problem is solved by a composition wherein the composition comprises less than 4 wt % of benzyl alcohol.
In a sixth embodiment of the first aspect, which is also an embodiment of the first to fifth embodiments, the problem is solved by a composition wherein the composition comprises no benzyl alcohol.
In a seventh embodiment of the first aspect, which is also an embodiment of the first to sixth embodiments, the problem is solved by a composition wherein the stoichiometric ratio of the entirety of all epoxy resins comprised in the composition to the entirety of all hardeners comprised in the composition is from 0.7 to 1.3.
In an eighth embodiment of the first aspect, which is also an embodiment of the first to seventh embodiments, the problem is solved by a composition wherein the stoichiometric ratio of the entirety of all epoxy resins comprised in the composition to the entirety of all hardeners comprised in the composition is from 0.9 to 1.1.
In a ninth embodiment of the first aspect, which is also an embodiment of the first to eighth embodiments, the problem is solved by a composition wherein the composition comprises at least one further hardener comprising at least two or more primary and/or secondary amine groups, preferably a hardener selected from the group of hardeners comprising methylenedianiline, N-aminoethylpiperazine, isophoronediamine, m-phenylenebis(methylamine), trimethylhexamethylenediamine, polyoxyalkyleneamines, polyaminoamides and reaction products of amines with acrylonitrile and Mannich bases.
In a tenth embodiment of the first aspect, which is also an embodiment of the first to ninth embodiments, the problem is solved by a composition further comprising at least one reaction accelerant, preferably selected from the group consisting of organic acids and tertiary amines.
In an eleventh embodiment of the first aspect, which is also an embodiment of the first to tenth embodiments, the problem is solved by a composition further comprising at least one reactive diluent, preferably selected from the group consisting of mono- and polyfunctional epoxy compounds liquid at room temperature.
In a twelfth embodiment of the first aspect, which is also an embodiment of the first to eleventh embodiments, the problem is solved by a composition according to any of claims 1 to 13 further comprising pigments, fillers and/or additives.
In a second aspect, the problem addressed by the invention is solved by a surface preferably comprising metal, mineral substrate, plastic, paint/varnish, polymer concrete, adhesive, fibre composite, potting composition or impregnation and coated with the composition according to the invention.
In a third aspect, the problem addressed by the invention is solved by a method of coating a surface comprising applying to the surface the coating material comprising the composition according to the first aspect or an embodiment thereof.
In a first embodiment of the third aspect, the problem is solved by a method wherein the surface is a surface comprising metal, mineral substrate, plastic, paint/varnish, polymer concrete, adhesive, fibre composite, potting composition or an impregnation.
In a fourth aspect, the problem addressed by the invention is solved by the use of the composition according to the first aspect or an embodiment thereof as surface protection on metal, mineral substrate, plastic, paint/varnish, polymer concrete, adhesive, fibre composite, potting composition or as an impregnation.
In a fifth aspect, the problem addressed by the invention is solved by a composition obtainable by curing the curable composition according to the first aspect or an embodiment of the first aspect.
The invention is based on the surprising discovery that curable compositions without benzyl alcohol according to the invention exhibit processing-relevant properties which are equivalent to or even improved over comparable prior art compositions comprising benzyl alcohol.
It is first of all essential for the curable composition of the invention, comprising at least one epoxide, to comprise at least one hardener, said hardener being a compound of formula (I) or (II),
where R1 and R2 are each independently selected from the group of substitutents having the formula —(CH2)x—NH2 and x is in each case independently 0, 1, 2, 3 or 4. In one preferred embodiment, R1 is at position 1 of the ring, i.e., it is covalently bonded to a carbon atom which is comprised in the five-membered ring and which itself is covalently bonded to the ring system oxygen atom by a C—O single bond. In one particularly preferred embodiment, R1 is at position 1 of the ring and R2 is at position 2, 3 or preferably at either of positions 3 and 4. In one preferred embodiment, the composition comprises, in addition to this hardener, at least one further hardener which may be a further compound of formula (I) or (II) or else preferably at least one hardener other than a hardener according to formula (I) or (II).
Useful other hardeners include all hardeners described in the prior art as useful for curable compositions comprising at least one epoxide, in particular amine-containing hardeners bearing at least two or more primary and/or secondary amino groups, for example diethylenetriamine, triethylenetetramine, methylenedianiline, bis(aminocyclohexyl)methane, 3,3′-dimethyl-4,4′-diaminodicyclohexylmethane, tricyclododecanediamine, norbornanediamine, N-aminoethylpiperazine, isophoronediamine, m-phenylenebis(methylamine), 1,3- and/or 1,4-bis(aminomethyl)cyclohexane, trimethylhexamethylenediamine, polyoxyalkyleneamines, polyaminoamides and reaction products of amines with acrylonitrile and Mannich bases.
One preferred embodiment comprises using as hardener a mixture of at least two hardeners including at least one hardener according to formula (I) or (II). Here, the proportion of hardener according to formula (I) or (II) in the mixture of at least two hardeners is, in order of increasing preference, at least 10, 20, 30, 40, 50, 60, 70, 80, 90 or 95 wt %.
DE102010030991.5 describes one preparative organic synthesis route to compounds of formula (I) and (II). These compounds are also obtainable biotechnologically by oxidation of corresponding cyclic alcohols by suitable oxidases followed by transamination by transaminases. A useful method is described in EP11170011.8 for example.
In accordance with the invention, useful epoxy resins include all epoxy resins curable with amines. The epoxy resins include, for example, polyepoxides based on bisphenol A diglycidyl ether, bisphenol F diglycidyl ether or cycloaliphatic types, for example 3,4-epoxycyclohexylepoxymethane or 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate.
The curable composition according to the invention preferably comprises an epoxy resin selected from the group comprising epoxy resins based on bisphenol A diglycidyl ether, epoxy resins based on bisphenol F diglycidyl ether and cycloaliphatic types, for example 3,4-epoxycyclohexylepoxyethane or 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate, particular preference being given to bisphenol A-based epoxy resins and to bisphenol F-based epoxy resins. Such compounds are commercially available.
It is essential for carrying out the teaching according to the invention to adhere to a certain ratio of the entirety of the epoxy resins to the entirety of the hardeners. In a preferred embodiment, the ratio is a stoichiometric ratio. In a more preferred embodiment, the stoichiometric ratio of the entirety of the epoxy resins in the composition to the entirety of the hardeners in the composition is from 1:0.7 to 1:1.3, yet more preferably from 1:0.9 to 1:1.1 and most preferably 1:1.
Prior art curable compositions comprising epoxy resin and amine hardeners generally comprise a modifier, usually benzyl alcohol. Modifiers such as benzyl alcohol can be used to adjust the binder properties such as through-curing, flow and the resin-hardener mixture ratio. One particular advantage of the teaching according to the invention is that the quantity of benzyl alcohol employed as modifier may be reduced or the modifier, preferably the benzyl alcohol, may be omitted completely without sacrificing the entirety of the processing-relevant properties. In one preferred embodiment, the composition comprises, in order of increasing preference, less than 20 g, 15 g, 10 g, 5 g or 1 g of benzyl alcohol per 100 g of the entirety of all hardeners comprised therein. In a further preferred embodiment, the composition comprises, in order of increasing preference less than 10, 8, 6, 4, 3, 2, 1 or 0.5 wt % of benzyl alcohol. In a most preferred embodiment, the quantity of benzyl alcohol in the composition according to the invention is undetectable.
In one preferred embodiment, the curable composition according to the invention comprises at least one reactive diluent. In one preferred embodiment, the term “reactive diluent” as used herein is to be understood as meaning a low-viscosity epoxy-containing compound which is compatible with epoxy resin and hardener and which provides optimal dilution. The reactive diluent is preferably selected from the group of mono- bi- or polyfunctional epoxy compounds liquid at room temperature, for example butyl glycidyl ether, phenyl glycidyl ether, glycidyl ether of versatic acid, C12-C14 glycidyl ethers, C13-C15 glycidyl ethers, p-tert-butylphenyl glycidyl ether, 1,6-hexane diglycidyl ether, 1,4-butane diglycidyl ether, neopentyl glycol diglycidyl ether, glycerol triglycidyl ether, pentaerythritol polyglycidyl ether, trimethylolpropane triglycidyl ether and cresyl glycidyl ether.
In a further preferred embodiment, the curable composition according to the invention comprises at least one reaction accelerant, preferably selected from the group consisting of organic acids and tertiary amines, for example salicylic acid, aminoethylpiperazine, tris(N,N-dimethylaminomethyl)phenol.
In a further preferred embodiment, the curable composition according to the invention comprises at least one solvent, for example xylene or isopropanol.
In a further preferred embodiment, the curable composition according to the invention comprises pigments, fillers and/or additives.
The present invention is more particularly described by the following figures and non-limiting examples from which further features, embodiments, aspects and advantages of the present invention may be discerned.
The example which follows shows results compared to isophoronediamine (IPD) which is an amine regarded as industry standard, for example for epoxy resin-based industrial flooring. All components were thoroughly commixed with one another for processing and testing.
The IPD-based formulation requires benzyl alcohol to achieve a sufficient conversion.
Using HMF diamine makes it possible to achieve conversions after 7 days of about 85% without using modifiers such as benzyl alcohol. This is within a range usually acceptable in practice.
Compared to the IPD-based formulation without benzyl alcohol, the HMF diamine-based curable epoxy-based composition has a distinctly lower viscosity and is more reactive.
Using HMF diamine as hardener in place of IPD achieves good through-curing (heat deflection temperatures, Shore hardnesses) even without using benzyl alcohol.
Coatings having good surface qualities are obtainable.
| Number | Date | Country | Kind |
|---|---|---|---|
| EP12183423 | Sep 2012 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP13/67386 | 8/21/2013 | WO | 00 |