Curable polyester polyols and their use in thermosetting soft feel coating formulations

Abstract

A soft feel curable polyester composition comprising the residues of a 2,2,4,4-tetraalkylcyclobutane-1,3-diol, a C2-C20 diol other than 2,2,4,4-tetraalkylcyclobutane-1,3-diol, a C2-C20 polyol, an alicyclic diacid and an acyclic aliphatic diacid, wherein said curable polyester contains at least 90 mole percent of aliphatic diacid residues, based on the total moles of diacid residues, and wherein said curable polyester has a hydroxyl number of about 100 to about 250 mgKOH/g, an acid number of 0 to about 30 mgKOH/g, and a number average molecular weight of about 500 to about 10,000 g/mole, a soft segment polyol, an isocyanate crosslinker and a solvent or a solvent mixture.

Description

BACKGROUND OF THE INVENTION

This invention relates to soft feel coatings and in particular to curable polyester polyols for use in thermosetting soft feel coatings.

FIELD OF THE INVENTION

Soft feel coatings are commonly applied to plastic parts to improve comfort and aesthetic value and are also widely used in automotive interior parts as well as consumer electronics. A soft touch coating can impart a range of touch sensations, for example, a velvety feel, a silky feel, or a rubbery feel, to an otherwise hard substrate. In addition to its unique tactile touch property, the coating must function consistently over the desired service time demanded in the market where daily interaction between the users and the coated surfaces occur. Apart from robust adhesion to the coated surface, the coating must perform well when exposed to common chemicals, such as human sweat, cosmetics, sun screens and food items.

Many chemicals, including those found in sunscreen lotions and insect repellants, can further soften soft feel coatings, and will migrate through the coating and into the underlying plastic, causing adhesion loss of the coating to the plastic substrate and, in some instances, damage to the underlying plastic substrate.

There is a fine balance between soft touch and chemical resistance. An increase in cross link density and film hardness typically would improve chemical resistance including sunscreen resistance, but can impact the soft touch feeling of the coating, thereby decreasing the comfort and aesthetic value of the soft feel coating.

This invention relates to a thermosetting soft feel coating composition comprised of at least a branched polyester polyol, a soft segment polyol and a cross linker. The superior chemical resistance of these polyesters provides improved sunscreen lotion resistance in soft feel coating formulations while maintaining the desired comfort and aesthetic value of the soft feel coatings.

SUMMARY OF THE INVENTION

This invention relates to soft feel coatings and in particular to curable polyester polyols for use in thermosetting soft feel coatings In certain embodiments, the present invention is directed to a coating composition comprising:

• • A) a cureable aliphatic polyester composition comprising the residues of:
    • a) 2,2,4,4-tetraalkylcyclobutane-1,3-diol represented by the structure

• • wherein R₁, R₂, R₃, and R₄ each independently are C₁ to C₈ alkyls;
    • b) a C₂-C₂₀ diol other than 2,2,4,4-tetraalkylcyclobutane-1,3-diol;
    • c) a C₂-C₂₀ polyol;
    • d) an alicyclic diacid; and
    • e) an acyclic aliphatic diacid; and wherein said curable polyester contains at least 90 mole percent of aliphatic diacid residues, based on the total moles of diacid residues, and wherein said curable polyester has a hydroxyl number of about 100 to about 250 mgKOH/g, an acid number of 0 to about 30 mgKOH/g, and a number average molecular weight of about 500 to about 10,000 g/mole:
  • B) a soft segment polyol;
  • C) an isocyanate crosslinker; and
  • D) a solvent.

DESCRIPTION OF THE INVENTION

For purposes of the following detailed description, while attempts have been made to be precise, the numerical values and ranges described herein should be considered to be approximations (even when not qualified by the term “about”). These values and ranges may vary from their stated numbers depending upon the desired properties sought to be obtained by the present invention as well as the variations resulting from the standard deviation found in the measuring techniques. Moreover, it is to be understood that any numerical range recited herein is intended to include all sub-ranges that are subsumed therein. For example a range of 10 to 70 is intended to include all sub ranges between 10 and 70 and including the recited minimum value of 10 and the maximum value of 70, that is having a minimum value equal to or greater than 10 and a maximum value equal to or less than 70. Also, a range associated with chemical substituent groups such as, for example, “C₁ to C₅ diols”, is intended to specifically include and disclose C₁, C₂, C₃, C₄ and C₅ diols.

As used in the specification and the appended claims, the singular forms “a,” “an” and “the” include their plural referents unless the context clearly dictates otherwise. For example, a reference to a “polyester,” a “dicarboxylic acid”, a “residue” is synonymous with “at least one” or “one or more” polyesters, dicarboxylic acids, or residues and is thus intended to refer to both a single or plurality of polyesters, dicarboxylic acids, or residues. In addition, references to a composition “comprising”, “containing”, “having” or “including” “an” ingredient or “a” polyester is intended to include other ingredients or other polyesters, respectively, in addition to the specifically identified ingredient or residue. Accordingly, the terms “containing”, “having” or “including” are intended to be synonymous and may be used interchangeably with the term “comprising”, meaning that at least the named compound, element, particle, or method step, etc., is present in the composition or article or method, but does not exclude the presence of other compounds, catalysts, materials, particles, method steps, etc., even if the other such compounds, material, particles, method steps, etc., have the same function as what is named, unless expressly excluded in the claims.

The term “curable aliphatic polyester”, as used herein, is synonymous with the term “resin” and is intended to mean a thermosetting surface coating polymer prepared by the polycondensation of one or more acid components and hydroxyl components.

The term “residue”, as used herein in reference to the polymers of the invention, means any organic structure incorporated into a polymer through a polycondensation or ring opening reaction involving the corresponding monomer. It will also be understood by persons having ordinary skill in the art, that the residues associated within the various curable polyesters of the invention can be derived from the parent monomer compound itself or any derivative of the parent compound. For example, the dicarboxylic acid residues referred to in the polymers of the invention may be derived from a dicarboxylic acid or its associated acid halides, esters, salts, anhydrides, or mixtures thereof. Thus, as used herein, the terms “diacid” is intended to include dicarboxylic acids and any derivative of a dicarboxylic acid, including its associated acid halides, esters, half-esters, salts, half-salts, anhydrides, and mixtures thereof, useful in a polycondensation process with a diol to make a curable, aliphatic polyester.

The term “aliphatic” is intended to have its common meaning as would be understood by persons having ordinary skill in the art, that is, acyclic or cyclic, saturated or unsaturated carbon compounds, excluding benzenoid or other aromatic systems. The term “acyclic aliphatic diacid” is intended to mean an open-chain aliphatic dicarboxylic acid compound, its diester derivative, its anhydride, or a combination thereof. The term “alicyclic diacid” is intended to mean a cyclic aliphatic dicarboxylic acid compound, its diester derivative, its anhydride, or a combination thereof. The term “aliphatic polyester”, as used herein, is understood to mean a polyester that contains 90 mole percent or greater aliphatic diacid or diol residues, based on the total moles of diacid or diol residues. Small amounts, such as less than 10 mole %, or less than 9 mole %, or less than 8 mole %, or less than 5 mole %, or less than 3 mole %, or less than 2 mole %, or less than 1 mole % of aromatic dicarboxylic acids residues or aromatic diol residues also may be present in the curable, aliphatic polyester. Desirably, the curable, aliphatic polyester is essentially free, i.e., having less than 1 mole % of aromatic diacid and/or aromatic diol residues.

In one embodiment, this invention provides a curable polyester comprising the residues of:

• • a) 2,2,4,4-tetraalkylcyclobutane-1,3-diol (TACD) in an amount of about 30 to about 90 mole %, based on the total moles of the diols,
  • b) a diol other than TACD in an amount of about 10 to 70 mole % based on the total moles of the diols,
  • c) a polyol in an amount of 5 to 60 mole %, based on the total moles of the diols and polyol,
  • d) an alicyclic diacid in an amount of about 70 to about 100 mole %, based on the total moles of the diacids, and
  • e) an acyclic aliphatic diacid in an amount of about 0 to 30 mole %, based on the total moles of the diacids,

wherein said curable polyester contains at least 90 mole % of aliphatic diacid residues, based on the total moles of diacid residues, and wherein said curable polyester has a hydroxyl number of about 100 to about 250 mgKOH/g, an acid number of 0 to about 30 mgKOH/g, and a number average molecular weight of about 500 to about 10,000 g/mole.

TACD is a diol and can be represented by the general structure:

wherein R₁, R₂, R₃, and R₄ each independently represent an alkyl radical, for example, a lower alkyl radical having 1 to 8 carbon atoms; or 1 to 6 carbon atoms, or 1 to 5 carbon atoms, or 1 to 4 carbon atoms, or 1 to 3 carbon atoms, or 1 to 2 carbon atoms, or 1 carbon atom. The alkyl radicals may be linear, branched, or a combination of linear and branched alkyl radicals. Examples of TACD include 2,2,4,4-tetramethylcyclobutane-1,3-diol (TMCD), 2,2,4,4-tetraethylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-propylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-butylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-pentylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-hexylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-heptylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-octylcyclobutane-1,3-diol, 2,2-dimethyl-4,4-diethylcyclobutane-1,3-diol, 2-ethyl-2,4,4-trimethylcyclobutane-1,3-diol, 2,4-dimethyl-2,4-diethyl-cyclobutane-1,3-diol, 2,4-dimethyl-2,4-di-n-propylcyclobutane-1,3-diol, 2,4-n-dibutyl-2,4-diethylcyclobutane-1,3-diol, 2,4-dimethyl-2,4-diisobutylcyclobutane-1,3-diol, and 2,4-diethyl-2,4-diisoamylcyclobutane-1,3-diol.

The diols (b) other than TACD have 2 hydroxyl groups and can be branched or linear, saturated or unsaturated, aliphatic or cycloaliphatic C₂-C₂₀ compounds, the hydroxyl groups being primary, secondary, and/or tertiary. Examples of diols (b) include 2,2-dimethyl-1,3-propanediol (neopentyl glycol), 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4-trimethyl-1,3-pentanediol, hydroxypivalyl hydroxypivalate, 2-methyl-1,3-propanediol, 2-butyl-2-ethyl-1,3-propanediol, 2-ethyl-2-isobutyl-1,3-propanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 2,2,4,4-tetramethyl-1,6-hexanediol, 1,10-decanediol, 1,4-benzenedimethanol, ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, and 2,2-bis(hydroxymethyl)propionic acid (dimethylolpropionic acid).

In some embodiments, the diol (b) is 2,2-dimethyl-1,3-propanediol (neopentyl glycol), 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4-trimethyl-1,3-pentanediol, hydroxypivalyl hydroxypivalate, 2-methyl-1,3-propanediol, 2-butyl-2-ethyl-1,3-propanediol, 1,4-butanediol, and 1,6-hexanediol or mixtures thereof. In other embodiments, at least one of the diols is neopentyl glycol.

In some embodiments, TACD (a) is present in an amount of about 30 to about 90 mole % and the diol (b) in an amount of about 10 to 70 mole %, both based on the total moles of the diols, (a) and (b). In other embodiments, TACD (a) is present in about 40 to about 80 mole % and the diol (b) in about 20 to about 60 mole %.

The polyol (c) having 3 or more hydroxyl groups can be branched or linear, saturated or unsaturated, aliphatic or cycloaliphatic C₂-C₂₀ compounds, the hydroxyl groups being primary, secondary, and/or tertiary. In some embodiments at least two of the hydroxyl groups are primary. In yet other embodiments, the polyols are hydrocarbons and do not contain atoms other than hydrogen, carbon and oxygen. Examples of the polyol include 1,1,1-trimethylolpropane (TMP), 1,1,1-trimethylolethane, glycerin, pentaerythritol, erythritol, threitol, dipentaerythritol, sorbitol, mixtures thereof, and the like. In another embodiment, the polyol is TMP.

In some embodiments, the polyol (c) is present in an amount of about 5 to about 60 mole % based on the total moles of the diols and the polyol, (a), (b), and (c). In other embodiments, the polyol is present in about 10 to about 50 mole % based on the total moles of the diols and the polyol, (a), (b), and (c).

The alicyclic diacid (d) is a cyclic aliphatic dicarboxylic acid compound, its diester derivative, its anhydride, or a combination thereof. Suitable alicyclic diacid compounds include compounds having two carboxylic acid groups, their diester derivatives, and their anhydrides. The dicarboxylic acid compounds are capable of forming ester linkages with diol or polyol compounds. For example, a polyester can be synthesized by using a polyhydroxyl compound and a derivative of a dicarboxylic acid such as, for example, dimethyl ester or other dialkyl esters of the diacid, or diacid chloride or other diacid halides, or acid anhydride.

Suitable alicyclic diacids include, but are not limited to, 1,4-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, hexahydrophthalic anhydride (HHPA), tetrahydrophthalic anhydride, tetrachlorophthalic anhydride, 5-norbornene-2,3-dicarboxylic anhydride, 5-norbornene-2,3-dicarboxylic acid, 2,3-norbornanedicarboxylic acid, 2,3-norbornanedicarboxylic acid anhydride, and mixtures thereof. In some embodiments HHPA is the alicyclic diacid.

The acyclic aliphatic diacid (e) is an open-chain aliphatic dicarboxylic acid compound, its diester derivative, its anhydride, or a combination thereof. Examples of acyclic aliphatic diacids include adipic acid, maleic anhydride, maleic acid, fumaric acid, itaconic anhydride, itaconic acid, citraconic anhydride, citraconic acid, dodecanedioic acid, sebacic acid, azelaic acid, and the like. In some embodiments adipic acid is the aliphatic diacid (e).

In some embodiments, the alicyclic diacid (d) is present in an amount of about 70 to about 100 mole % and the acyclic aliphatic diacid (e) is in an amount of about 0 to about 30 mole %, both based on the total moles of the diacids, (d) and (e). In some embodiments, the alicyclic diacid (d) is above 80% and the acyclic aliphatic diacid (e) is less than 20%, both based on the total moles of the diacids, (d) and (e).

The hydroxyl number of the curable polyester of the present invention may be from about 100 to about 250, from about 120 to about 230, or from about 150 to about 200 mgKOH/g. The acid number may be from 0 to about 30, from about 3 to about 20, from 3 to about 15, or from 5 to about 10 mgKOH/g.

The number average molecular weight (Mn) of the curable polyester of the present invention may be from 500 to 10,000, from 800 to 6,000, or from 1,000 to 3,000 g/mole. The weight average molecular weight (Mw) of the curable polyester of the present invention may be from 1,000 to 10,000, from 1,500 to 6,000, or from 2,000 to 4,000 g/mole. Molecular weights are measured by gel permeation chromatography (GPC) using polystyrene equivalent molecular weight.

The glass transition temperature (Tg) of the curable polyester of the present invention may be from 0° C. to 55° C., from 5° C. to 45° C., or from 10° C. to 40° C.

In another embodiment, this invention provides a thermosetting soft feel coating composition comprising:

• • i. the curable polyester of the present invention,
  • ii. a soft segment polyol that could be polycarbonate diol (PCD), polytetoramethylene glycol (PTMG), polycaprolactone or the mixture of these soft segment polyols,
  • iii. a crosslinker, and
  • iv. an organic solvent.

In some embodiments, the curable polyester (i) is desirable present in an amount from 10 to 50 weight %, or from 15 to 45%; the soft segment polyol (ii) is from 50 to 90 weight %, or from 55 to 85 weight %; and the crosslinker (iii) from 10 to 50 weight %, from 15 to 40 weight, based on the total weight of the polyols (i) and (ii), and crosslinker (iii).

The crosslinker may be an isocyanate isocyanurate type. Suitable isocyanates include, but are not limited to, toluene diisocyanate, isocyanurates of toluene diisocyanate, diphenylmethane 4,4′-diisocyanate, isocyanurates of 4,4′-diisocyanate, methylenebis-4,4′-isocyanatocyclohexane, isophorone diisocyanate, isocyanurates of isophorone diisocyanate, 1,6-hexamethylene diisocyanate, isocyanurates of 1,6-hexamethylene diisocyanate, 1,4-cyclohexane diisocyanate, p-phenylene diisocyanate, and triphenylmethane 4,4′,4″-triisocyanate, tetramethyl xylene diisocyanate, metaxylene diisocyanate, and polyisocyanates. There can also be employed isocyanate terminated adducts of diols and polyols, such as ethylene glycol, 1,4-butylene glycol, trimethylol propane, etc. These are formed by reacting more than one mole of a diisocyanate, such as those mentioned, with one mole of a diol or polyol to form a higher molecular weight isocyanate prepolymer with a functionality of 2 to 3. Examples include those isocyanate crosslinkers under the Desmodur and Mondur trade names from Bayer Material Science. Where isocyanates are used as crosslinkers. In some embodiments, the crosslinkers are aliphatic isocyanates, since they provide outdoor durability and color stability in the cured coating. Examples include 1,6-hexamethylene diisocyanate, 1,4-butylene diisocyanate, methylene bis (4-cyclohexyl isocyanate) and isophorone diisocyanate. Mixtures of isocyanate crosslinkers can also be employed. The example thermosetting soft feel coating formulations provided contain the triisocyanurate of 1,6-hexamethylene diisocyanate as the crosslinker.

Stoichiometric calculations for the polyester resin and isocyanate reaction are known to those skilled in the art and are described in The Chemistry of Polyurethane Coatings, Technical Publication p. 20, by Bayer Material Science, 2005. Theoretically, crosslinking between the polyester resin and isocyanate reaches maximum molecular weight and optimal properties associated with molecular weight when one equivalent of isocyanate (NCO) reacts with one equivalent of hydroxyl (OH), which is when the NCO to OH ratio is 1.0/1.0. It is common practice to use a small excess of isocyanate, about 5-10%, to allow for the likely consumption of isocyanate by moisture from the atmosphere, solvents and pigments. It is sometimes desirable to vary the NCO to OH ratio less than 1.0/1.0 to improve flexibility or greater than 1.0/1.0 for harder, more chemical resistant and more weather resistant coatings.

In another aspect, this invention further provides a curable coating composition further comprising one or more cross-linking catalysts. Useful catalysts may include tertiary amines, such as triethylene diamine, N-methyl morpholine, N-ethyl morpholine, diethyl ethanolamine, 1-methyl-4-dimethylamino ethyl piperazine, 3-methoxy-N-dimethyl propyl amine, N-dimethyl-N′-methyl isopropyl propylene diamine, N,N-diethyl-3-diethyl amino propylamine, N,N-dimethyl benzyl amine, dicyclohexylmethylamine, 2,4,6-tris dimethylaminomethylphenol, N,N-dimethyl cyclohexylamine, triethylamine, tri-n-butylamine, 1,8-diaza-bichloro[5,40]-undecene-7 N-methyl diethanolamine, N,N-dimethyl ethanolamine, N,N-diethyl cyclohexylamine, N,N,N′N′-tetramethyl-ethylene diamine, 1,4-diaza-bicyclo-[2,2,2]-octane N-methyl-N-dimethylaminoethyl-piperazine, bis-(N,N-diethylaminoethyl)-adipate, N,N-diethylbenzylamine, pentamethyldiethylene triamine, N,N,N′,N′-tetramethyl-1,3-butanediamine, 1,2-dimethylimidazole, 2-methylimidazole; tin compounds, such as stannous chloride, dibutyl tin di-2-ethyl hexoate, stannous octoate, dibutyl tin dilaurate, trimethyl tin hydroxide, dimethyl tin dichloride, dibutyl tin diacetate, dibutyl tin oxide, tributyl tin acetate, tetramethyl tin, dimethyl dioctyl tin, tin ethyl hexoate, tin laurate, dibutyl tin maleate, dioctyl tin diacetate; other metal organics, such as zinc octoate, phenyl mercuric propionate, lead octoate, lead naphthenate, and copper naphthenate. In some embidiments the catalyst is dibutyl tin dilaurate (DBTDL). In some embodiments the amount of catalyst will be about 0.01 to 5%, based on the total weight of the resin solids.

Additional additives that may be included in the composition described herein include UV inhibitors, wetting agents, flow agents, defoamers, flattening agents, rheology control agents, anti-settling, anti-sag agents and slip agents. In some embodiments, the coating compositions described herein may include a flattening agent. Flattening agents are generally small solid particles of material that are insoluble in water and are effective to reduce gloss. Preferably, the flattening agent particles have a size of from about 0.05 to about 10 microns, but may be present in clumps or agglomerates of up to about 50 microns. The flattening agent particles may be inorganic or organic. Examples of suitable inorganic flattening agents include silicates, such as talc, and various forms of silica, such as amorphous, aerogel, diatomaceous, hydrogel and fumed silicas. Examples of suitable organic flattening agents include insoluble urea-formaldehyde resins, polyethylene, polypropylene, cellulosic fibers and polyurethane/polyurea copolymers.

Some examples of UV absorbers and UV light stabilizers are substituted benzophenone, substituted benzotriazoles, hindered amines, and hindered benzoates, available from Cytec Specialty Chemicals as CYASORB® UV, and available from Ciba Specialty Chemicals as TINUVIN®; diethyl-3acetyl-4-hydroxy-benzyl-phosphonate, 4-dodecyloxy-2-hydroxy benzophenone, and resorcinol monobenzoate.

If desired, the coating compositions can comprise other functional materials such as pigments, abrasion resistant particles, anti-oxidants, thixotropic agents and fillers. Examples of pigments include those generally recognized by persons of ordinary skill in the art of surface coatings. For example, the pigment may be a typical organic or inorganic pigment, especially those set forth in the Colour Index, 3rd ed., 2nd Rev., 1982, published by the Society of Dyers and Colourists in association with the American Association of Textile Chemists and Colorists. Other examples of suitable pigments include titanium dioxide, barytes, clay, calcium carbonate, CI Pigment White 6 (titanium dioxide), CI Pigment Red 101 (red iron oxide), CI Pigment Yellow 42, CI Pigment Blue 15,15:1,15:2,15:3,15:4 (copper phthalocyanines); CI Pigment Red 49:1 and CI Pigment Red 57:1. Colorants such as, for example, phthalocyanine blue, molybdate orange, or carbon black also may be added to the coating composition.

In preparing the present coatings, the branched polyester, the soft segment polyols and the crosslinker can be dissolved or dispersed in a single solvent or a mixture of solvents. Any solvent that will enable the formulation to be coated on a substrate may be used, and these will be well known to the person skilled in the art. Suitable organic solvents include glycols, glycol ether alcohols, alcohols, ketones, and aromatics, such as xylene and toluene, acetates, mineral spirits, naphthas and/or mixtures thereof. “Acetates” include the glycol ether acetates. The amount of organic solvent can be up to 85 wt. % based on the weight of the coating composition.

After formulation, the coating composition can be applied to a substrate or article. Thus, a further aspect of the present invention is a shaped or formed article that has been coated with the coating compositions of the present invention. The substrate can be any common substrate such as paper; polymer films such as polyethylene or polypropylene; wood; metals such as aluminum, steel or galvanized sheeting; glass; urethane elastomers; primed (painted) substrates; and the like. The coating composition can be coated onto a substrate using techniques known in the art, for example, by spraying, draw-down, roll-coating, etc., to form a dried coating having a thickness of about 0.1 to about 4 mils (1 mil=25 μm), or 0.5 to 3, or 0.5 to 2, or 0.5 to 1 mils on the substrate. The coating can be cured at ambient (room) temperature or heated to a temperature of about 50° C. to about 230° C., or desirably from 50° C. to 100° C., for a time period that typically ranges about 5 to about 90 minutes and allowed to cool.

This invention can be further illustrated by the following examples, although it will be understood that these examples are included merely for purposes of illustration and are not intended to limit the scope of the invention.

EXAMPLES

The following examples are given to illustrate the invention. It should be understood, however, that the invention is not to be limited to the specific conditions or details described in these examples.

Preparation of the Curable Polyesters of the Present Invention and Also Comparative Polyester Example

Curable polyesters of the present invention and comparative polyester example (Table 1) were prepared using a solvent process to help remove the water of esterification. The resins were prepared in a two-liter reaction kettle equipped with a heating mantle, mechanical stirrer, thermocouple, nitrogen blanket (0.6 scfh), oil-heated partial condenser (103° C.-105° C.), condensate trap, and water-cooled total condenser (15° C.). The condensate trap, kettle top and adapter from the kettle to the column were wrapped in aluminum foil and fiberglass tape to facilitate water removal. Stage 1 raw materials were charged to the reactor. Additional xylene (˜30 g) was used to fill the condensate trap. The temperature was then increased from room temperature to 150° C. over ninety minutes to form a homogenous melt. Agitation (300 rpm) was started and the temperature increased to a maximum of 230° C. over 240 minutes. The Stage 2 TMP was added when half the theoretical condensate was collected. The reaction mixture was held at 230° C.

The acid number (abbreviated “AN”), hydroxyl number (abbreviated “OHN”), number average molecular weight (abbreviated “Mn”), weight average molecular weight (abbreviated “Mw), z-average molecular weight (abbreviated as “Mz”), molecular weight distribution polydispersity index (abbreviated “Mw/Mn”), glass transition temperature (abbreviated “Tg”) and melt viscosity of the polyester resins are shown in Table 1.

Acid number was determined using ASTM method D 1639.

Hydroxyl number was determined by esterifying the resin with excess acetic anhydride in pyridine and then decomposing the unreacted anhydride with water. The resulting acetic acid is then titrated with a standard solution of KOH. The number of milligrams KOH which are equivalent to one gram of resin sample is reported as the hydroxyl number.

Number average molecular weight was determined by gel permeation chromatography (Agilent 1100 Series GPC-SEC system) with a refractive index detector and polystyrene standards.

Residual solvent remaining in the resin from processing can artificially lower the Tg measurement. To obtain a more accurate Tg, a resin sample was first subjected to preconditioning in an oven. About 0.3 g-0.5 g of resin was placed into a sample tin and heated to 150° C. The sample remained in the oven for 14-16 hours (overnight). The sample was then transferred to a differential scanning calorimeter (TA Instruments DSC Q2000 V24.9 Build 121). On the first heating cycle, the sample in the DSC chamber was cooled to −50° C. by liquid nitrogen and then heated from −50° C. to 140° C. at a rate of 20° C./min under nitrogen atmosphere. The sample was then quench cooled to −50° C. For the second heating cycle, the sample was heated under the same conditions as those used in the first heating cycle. The midpoint of the second heating cycle is reported as the Tg of the sample.

TABLE 1
The curable polyesters of the present invention
and a comparative polyester example
	Example	Example	Comparative
Polyester resin	PE 1	PE 2	PE 3
Stage 1
TMCD(a),(b)	510	408.1	750.1
TMP(c)	53	189.8	55.9
HHPA(d)	865.4	915	984.3
Triphenylphosphite	1.83	1.84	1.84
Xylene process solvent	18.29	18.44	18.68
Stage 2
NPG(a),(f)	368.3	147.4	0
TMP	53	189.8	55.8
Fascat 4100 catalyst(g)	1.84	1.84	1.84
Determined Resin
Properties
AN, mg KOH/g resin	4	9	10
OHN, mg KOH/g resin	154	157	130
Mz	5526	7762	4200
Mw	2602	3764	2310
Mn	1190	1561	1100
Mw/Mn	2.19	2.41	2.1
Tg, ° C.	26	36	8
(a)Add 0.25 wt. % glycol excess based on calculated charge weights
(b)2,2,4,4-tetramethyl-1,3-cyclobutanediol
(c)Trimethylolpropane
(d)Hexahydrophthalic anhydride
(e)Adipic acid
(f)2,2-Dimethyl-1,3-propanediol

Thermosetting Soft Feel Coating Preparation and Evaluation:Prepartion of Thermosetting Soft Feel Coatings

Thermosetting soft feel coatings were prepared by mixing the ingredients listed in Table 2. Polyester samples prepared in table 1 were pre-dissolved into butylacetate to form 75% solid solutions. Part A was first prepared by mixing the ingredients in listed order to form a uniform solution. The Part B was added to Part A and mixed to uniform solution before apply.

TABLE 2
Thermosetting monocoat formulation
	Example	Comparative	Comparative
	soft feel	soft feel	soft feel
Ingredients	coating SF 1	coating SF 2	coating SF 3
Part A
Example PE2*1	11.05
Comparative PE3*1		11.40
Desmophen 670 BA*2			10.70
Desmophene C 1200*3	19.15	19.15	20.00
Acemat 3300*4	4.31	4.31	4.31
Baysilone OL-17(10% in	1.29	1.29	1.29
xylene)*5
DBTDL Solution*6	2.15	2.15	2.15
Butyl Acetate	25.50	25.50	25.50
Xylene	25.61	24.98	25.98
EB acetate	3.25	3.25	3.25
Tinuvin 292	0.51	0.51	0.51
Tinuvin 400	0.51	0.51	0.51
Ceramat 258*7	5.39	5.39	5.39
Total	98.73	98.45	99.60
Part B:
Desmodur N3390	10.45	9.66	9.40
Total	109.17	108.10	109.00
NCO/OH	1:1.15	1:1.15	1:1.15
Matt agent/Binder	0.12	0.12	0.12
NV	40.44	40.46	40.40
*1PE2 and PE 3 75% in butyl acetate
*2Desmophen 670 BA Branched PE polyol in BAC, OH content 3.5%
*3Desmophene C 1200 Liner Polycarbonate Polyester; OH content 1.7%
*4Acemat 3300 Silica matt agent Polyether modified polysiloxane from OMG
*5Baysilone OL-17 Borchers GmbH
*6DBTDL Solution 20% dibutyltin dilaurate in methyl propyl ketone
*7Ceramat 258 Oxidized HD polyethylene wax dispersion

Evaluation of Thermosetting Soft Feel Coatings

Plastic substrate Solvay Sequel 1440 which is made of thermoplastic polyolefin, in 4×12 inch size was used. The plastic substrates were pre-coated with a wash primer to improve adhesion. The wash primer was made by dissolving a chlorinated polyolefin CP-730 from Eastman Chemical Company into xylene to form a 15% solids solution. The DFT of the adhesion primer is about 5 microns.

The viscosity of the soft feel coatings were adjusted to 25 seconds measured by a number 4 Ford cup using aromatic 100 solvent. Coatings were spray-applied to pre-primered plastic substrates using a gravity fed Devilbiss gun. Target Dry Film Thickness (DFT) was 30 microns. A fifteen minute flash time was allowed and coatings were baked at 80° C. for 30 minutes. Cured panels were aged for 5 to 7 days at ambient temperature ahead of property testing.

Soft touch performance is critical to the comfort and aesthetic value of soft feel coatings, however, there is no test method developed for this test other than relying on tangible recognition of a human's hand comparing a test panel with a standard panel. For the sunscreen resistance testing, the test method described below was used.

• • A pencil hardness test per ASTM D3363 was conducted on the coated substrate panels and initial hardness was recorded.
  • The sunscreen lotion used was Neutrogena® Ultra Sheer® Dry-Touch sunscreen (SPF 45) available from Johnson and Johnson Corporation.
  • 0.5 grams of Neutrogena sunscreen was evenly applied to 40×40 mm squares of coated substrate.
  • The panels were heated in an oven at 55 degree C. for 4 hours.
  • The Neutrogena cream was wiped off of the panels, and the panels were washed with water and dried at ambient conditions.
  • A second pencil hardness test was conducted on the panels and the result was recorded.
  • A visual assessment of the panels was done to determine if there was any change of color, gloss and appearance of the coating.
  • A 2 mm cross cut adhesion test using ASTM D3359 was performed.

Table 3 below shows the key test results of the soft feel coatings prepared in Table 2.

TABLE 3
Sunscreen resistance test results
	Example	Comparative	Comparative
	soft feel	soft feel	soft feel
Test items	coating SF 1	coating SF 2	coating SF 3
Soft touch performance	Good	Good	Good
Pencil hardness initial	HB*	HB	HB
Pencil hardness after	2B	3B	3B
sunscreen test
Pencil hardness rank drop	2	3	3
Cross hatch adhesion after	Pass	Pass	Pass
test
Visual examination:
Color changes	No	No	No
Gloss changes	No	No	No
Film appearance changes	No	Slightly	Slightly
		swelled	swelled
*Hardness order is 2H > H > HB > B > 2B > 3B

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.

Claims

1. A curable coating composition comprising: A) a curable aliphatic polyester composition comprising the residues of: i. a hydroxyl component, said hydroxyl component comprising the residues of: a) from 30 to about 90 mole %, based on the total moles of a) and b) of 2,2,4,4-tetraalkylcyclobutane-1,3-diol represented by the structure

2. The composition of claim 1 wherein said C1 to C8 alkyls on said 2,2,4,4-tetraalkylcyclobutane-1,3-diol are linear, branched, or a combination of linear and branched alkyls.

3. The composition of claim 1 wherein said 2,2,4,4-tetraalkylcyclobutane-1,3-diol is 2,2,4,4-tetramethylcyclobutane-1,3-diol (TMCD), 2,2,4,4-tetraethylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-propylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-butylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-pentylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-hexylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-heptylcyclobutane-1,3-diol, 2,2,4,4-tetra-n-octylcyclobutane-1,3-diol, 2,2-dimethyl-4,4-diethylcyclobutane-1,3-diol, 2-ethyl-2,4,4-trimethylcyclobutane-1,3-diol, 2,4-dimethyl-2,4-diethyl-cyclobutane-1,3-diol, 2,4-dimethyl-2,4-di-n-propylcyclobutane-1,3-diol, 2,4-n-dibutyl-2,4-diethylcyclobutane-1,3-diol, 2,4-dimethyl-2,4-diisobutylcyclobutane-1,3-diol, 2,4-diethyl-2,4-diisoamylcyclobutane-1,3-diol or mixtures thereof.

4. The composition of claim 1 wherein the alkyl portion of said b) C2-C20 diol is branched or linear, saturated or unsaturated, aliphatic or cycloaliphatic and the hydroxyl group of said b) C2-C20 diol is primary, secondary or tertiary.

5. The composition of claim 1 wherein said b) C2-C20 diol is 2,2-dimethyl-1,3-propanediol, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, 1,4-cyclohexanedimethanol, 2,2,4-trimethyl-1,3-pentanediol, hydroxypivalyl hydroxypivalate, 2-methyl-1,3-propanediol, 2-butyl-2-ethyl-1,3-propanediol, 1,4-butanediol, and 1,6-hexanediol or mixtures thereof.

6. The composition of claim 1 wherein the alkyl portion of said c) C2-C20 polyol is branched or linear, saturated or unsaturated, aliphatic or cycloaliphatic and having three or more hydroxyl groups and wherein the hydroxyl groups are primary, secondary, and/or tertiary.

7. The composition of claim 1 wherein said c) C2-C20 polyol has at least two primary hydroxyl groups.

8. The composition of claim 1 wherein said alicyclic diacid is a cyclic aliphatic dicarboxylic acid or diester derivative of a cyclic aliphatic dicarboxylic acid, or an anhydride derivative of a cyclic aliphatic dicarboxylic acid, or a combination thereof.

9. The composition of claim 1 wherein said alicyclic diacid is, 1-4-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, hexahydrophthalic anhydride (HHPA), tetrahydrophthalic anhydride, tetrachlorophthalic anhydride, 5-norbornene-2,3-dicarboxylic anhydride, 5-norbornene-2,3-dicarboxylic acid, 2,3-norbornanedicarboxylic acid, 2,3-norbornanedicarboxylic acid anhydride, and mixtures thereof.

10. The composition of claim 1 wherein said acyclic aliphatic diacid is an open-chain aliphatic dicarboxylic acid compound, or a diester derivative of aliphatic dicarboxylic acid compound, or an anhydride derivative of aliphatic dicarboxylic acid compound, or a combination thereof.

11. The composition of claim 1 wherein said acyclic aliphatic diacids is adipic acid, maleic anhydride, maleic acid, fumaric acid, itaconic anhydride, itaconic acid, citraconic anhydride, citraconic acid, dodecanedioic acid, sebacic acid, azelaic acid.

12. The coating composition of claim 1 wherein said crosslinker is toluene diisocyanate, isocyanurates of toluene diisocyanate, diphenylmethane 4,4′-diisocyanate, isocyanurates of 4,4′-diisocyanate, methylenebis-4,4′-isocyanatocyclohexane, isophorone diisocyanate, isocyanurates of isophorone diisocyanate, 1,6-hexamethylene diisocyanate, isocyanurates of 1,6-hexamethylene diisocyanate, 1,4-cyclohexane diisocyanate, p-phenylene diisocyanate, and triphenylmethane 4,4′,4″-triisocyanate, tetramethyl xylene diisocyanate, metaxylene diisocyanate, polyisocyanates and isocyanateterminated adducts of diols and polyols and mixtures thereof.

13. The coating composition of claim 1 further comprising one or more cross-linking catalysts present in the amount of about 0.01 to 5 weight percent based on the total weight of the resin solids in said coating composition.

14. The coating composition of claim 13 wherein said cross-linking catalyst is a tertiary amine, a tin compound or an organo-metallic compound or a mixture thereof.

15. The coating composition of claim 13 wherein said cross-linking catalyst is triethylene diamine, N-methyl morpholine, N-ethyl morpholine, diethyl ethanolamine, 1-methyl-4-dimethylamino ethyl piperazine, 3-methoxy-N-dimethyl propyl amine, N-dimethyl-N′-methyl isopropyl propylene diamine, N,N-diethyl-3-diethyl amino propylamine, N,N-dimethyl benzyl amine, dicyclohexylmethylamine, 2,4,6-tris dimethylaminomethylphenol, N,N-dimethyl cyclohexylamine, triethylamine, tri-n-butylamine, I,8-diaza-bichloro[5,40]-undecene-7 N-methyl diethanolamine, N,N-dimethyl ethanolamine, N,N-diethyl cyclohexylamine, N,N,N′N′-tetramethyl-ethylene diamine, I,4-diaza-bicyclo-[2,2,2]-octane N-methyl-N-dimethylaminoethyl-piperazine, bis-(N,N-diethylaminoethyl)-adipate, N,N-diethylbenzylamine, pentamethyldiethylene triamine, N,N,N′,N′-tetramethyl-I,3-butanediamine, 1,2-dimethylimidazole, 2-methylimidazole, stannous chloride, dibutyl tin di-2-ethyl hexoate, stannous octoate, dibutyl tin dilaurate, trimethyl tin hydroxide, dimethyl tin dichloride, dibutyl tin diacetate, dibutyl tin oxide, tributyl tin acetate, tetramethyl tin, dimethyl dioctyl tin, tin ethyl hexoate, tin laurate, dibutyl tin maleate, dioctyl tin diacetate; zinc octoate, phenyl mercuric propionate, lead octoate, lead naphthenate, and copper naphthenate or a mixture thereof.

16. The coating composition of claim 1 wherein said solvent is a ketone, an aromatic compound, an acetate, mineral spirits, a naphtha or mixtures thereof.

17. The coating composition of claim 1 further comprising a UV inhibitor, a wetting agent, a flow agent, a defoamer, a flattening agent, a rheology control agent, an anti-settling agent, an anti-sag agents or slip agents or a combination thereof.