Patent Application
20230019574
The present invention relates to a curing accelerator for an oxidative polymerization type unsaturated resin having a high curing accelerating ability, and to a printing ink and a coating material each including the curing accelerator.
In a field using an oxidative polymerization type resin as a structural component, such as a printing ink and a coating material, a drier is added as a curing accelerator for drying the resin. As the drier used in the ink or the coating material, a metal salt of a heavy metal such as cobalt, manganese, lead, iron, or zinc and various carboxylic acids (hereinafter, may be abbreviated as “metal soap”) is generally used.
Particularly, a cobalt metal soap has excellent drying performance, however, in a case where a large amount thereof is used for obtaining higher drying performance, surface drying of an ink or a coating film may extremely rapidly proceed, and thus, the cobalt metal soap may be a reason of wrinkles or shrinkage. Therefore, as a method of obtaining high drying performance while preventing such wrinkles or shrinkage, a curing accelerator containing both of a cobalt metal soap and bipyridyl has been proposed (for example, see PTL 1). This curing accelerator prevented wrinkles or shrinkage and had high drying performance.
However, cobalt compounds are listed up in Group 2B of “Possibly carcinogenic to humans” in the carcinogenicity risk list by the International Agency for Research on Cancer, and accordingly, carcinogenicity of the cobalt compounds is concerned. In addition, metal cobalt is a rare metal and supplying thereof is unstable, and accordingly, the price of the cobalt metal soap is high. Therefore, a curing accelerator having high drying performance in which no cobalt soap is used or a decreased amount of the cobalt metal soap is used is required.
PTL 1: JP-A-06-172689
A problem to be solved the present invention is to provide a curing accelerator for an oxidative polymerization type unsaturated resin having curing performance equal to or higher than excellent curing performance of cobalt metal soap, having high solubility in organic solvents, being usable outdoors, and having excellent versatility, without using the cobalt metal soap which may affect a human body, or by using a small amount thereof compared to that in the related art, and a printing ink and a coating material using the same.
As a result of intensive studies, the present inventors have found that by adding an imidazole compound to a curing accelerator for an oxidative polymerization type unsaturated resin containing a metal salt, a metal complex or the like, a curing accelerator for an oxidative polymerization type unsaturated resin having a very high curing accelerating ability can be obtained regardless of the central metal of the metal salt or metal complex, and thus the present invention has been completed.
That is, the present invention provides a curing accelerator for an oxidative polymerization type unsaturated resin, which includes a metal salt (A) and an imidazole compound (B) .
The present invention also provides a curing accelerator for an oxidative polymerization type unsaturated resin, which includes a metal complex (D) and an imidazole compound (B).
Further, the present invention provides a printing ink and a coating material each including the curing accelerator for an oxidative polymerization type unsaturated resin and an oxidative polymerization type unsaturated resin.
According to the present invention, a curing accelerator for an oxidative polymerization type unsaturated resin having a very high curing accelerating ability can be provided regardless of the central metal of the metal salt or metal complex, and the curing accelerator can be suitably used as a curing accelerator for an oxidative polymerization drying type printing ink or coating material represented by an ink for lithographic printing.
The curing accelerator for an oxidative polymerization type unsaturated resin of the present invention includes a metal salt (A) or a metal complex (D) and an imidazole compound (B) .
As the metal salt (A), a variety of metal salts used as a central metal source for a curing accelerator for an oxidative polymerization type unsaturated resin or a metal complex for a curing accelerator for an oxidative polymerization type unsaturated resin can be widely used. Examples of the metal salt (A) include a metal salt represented by the following general formula (A-1).
In the formula, the central metal expressed by M is manganese, iron, cobalt, bismuth, zirconium, barium, calcium, strontium, nickel, copper, zinc, cerium, or vanadium, and X is F-, Cl-, Br, I-, PF6-, SbF6-, AsF6-, BF4-, B(C6F5)4-, ClO4- , ClO3-, CO2-, ClO-, H2PO4-, H2PO3-, H2PO2-, HCO3-, NO3-, NO2-, (RCO)2CH- (wherein R is a hydrocarbon group having 1 to 22 carbon atoms), RCOO- (wherein R is a hydrocarbon group having 1 to 22 carbon atoms), O2-, S2-, SO42-, SO32-, or CO32-. n is an integer of 1 or more. These compounds may be used alone or in combination of two or more kinds thereof.
Among these, the central metal of the metal salt (A) is preferably manganese or iron because of its excellent performance as a curing accelerator. The valence of the central metal of the metal salt (A) is not particularly limited, and in a case where the central metal is manganese, for example, it usually has a valence of 2 to 7. When the central metal is iron, it is usually divalent or trivalent. Further, since the metal salt (A) has excellent solubility in printing ink or coating material, it is preferable that the metal salt (A) is a fatty acid salt of the general formula (A-1) in which X is a RCOO-(wherein R is a hydrocarbon group having 1 to 22 carbon atoms), and it is particularly preferable that the metal salt (A) is an octylate, a neodecanoic acid salt, an isononanoic acid salt, or a naphthenic acid salt.
The curing accelerator for an oxidative polymerization type unsaturated resin of the present invention may contain a ligand compound (C) in combination with the metal salt (A) . As the ligand compound (C), various compounds used as a ligand of a metal complex for a curing accelerator for an oxidative polymerization type unsaturated resin can be widely used. Examples of the ligand compound (C) include amino alcohol compounds, 2,2’-bipyridyl and derivatives thereof, 1,10-phenanthroline and derivatives thereof, N,N’-bissalicylidene 1,2-propanediamine and derivatives thereof, 8-quinolinol and derivatives thereof, picolinic acid and derivatives thereof, pyridinedicarboxylic acid and derivatives thereof, and quinoline-2-carboxylic acid and derivatives thereof. Examples of the derivative of the compound include a compound having one or more substituents such as a hydroxyl group, an amino group, a nitro group, a nitroso group, a sulfo group, a halogen atom, a hydrocarbon group which may have a substituent, a hydrocarbon oxy group which may have a substituent, and a hydrocarbon oxycarbonyl group which may have a substituent on an aromatic nucleus of each compound, and an alkyl ester of a carboxylic acid. For the above-mentioned various substituents, examples of the halogen atom include fluorine, chlorine, bromine, and iodine. The hydrocarbon group in the hydrocarbon group, the hydrocarbon oxy group, and the hydrocarbon oxycarbonyl group may be any one of an aliphatic hydrocarbon group, an alicyclic structure-containing hydrocarbon group, and an aromatic ring-containing hydrocarbon group. The aliphatic hydrocarbon group may have a straight chain or branched structure, and may have an unsaturated group in its structure. Examples of the substituents on the hydrocarbon group, the hydrocarbon oxy group, and the hydrocarbon oxycarbonyl group include a hydroxyl group, an amino group, a nitro group, a nitroso group, a sulfo group, a halogen atom, an alkyl group, and an alkoxy group.
Examples of the metal complex (D) include a metal complex obtained by mixing the metal salt (A) and the ligand compound (C). The type of the metal salt (A), the type of the ligand compound (C), and the combination of the metal salt (A) and the ligand compound (C) are appropriately selected according to the desired curing accelerator performance and the like, and any design may be used without any particular limitation. Among them, the central metal of the metal complex (D) is preferably manganese or iron as in the metal salt (A) for excellent performance of the curing accelerator.
The mixing ratio of the metal salt (A) and the ligand compound (C) is appropriately selected according to the desired curing accelerator performance and the like, and any design may be used without any particular limitation. Among them, the ratio of the ligand compound (C) to 1 mol of the metal atom in the metal salt (A) is preferably in a range of 0.1 to 20 mol, more preferably in a range of 0.2 to 10 mol, and particularly preferably in a range of 0.5 to 5 mol, since it is excellent in the performance as a curing accelerator.
The mixing of the metal salt (A) and the ligand compound (C) is preferably carried out in a solvent capable of dissolving both of them. The solvent is not particularly limited, and examples thereof include a variety of organic solvents widely used in printing inks and coating applications. When the imidazole compound (B) to be described later is capable of dissolving the metal salt (A) and the ligand compound (C), the imidazole compound (B) may be used as a solvent.
Examples of the various organic solvents include hydrocarbon solvents such as toluene, xylene, heptane, hexane, and mineral spirit; alcohol solvents such as methanol, ethanol, propanol, and cyclohexanol; ketone solvents such as methyl ethyl ketone, methyl isobutyl ketone, and cyclohexanone; ether solvents such as propyl ether, methyl cellosolve, cellosolve, butyl cellosolve, and methyl carbitol; alcohol solvents such as methanol, ethanol, propanol, butanol, and benzyl alcohol; vegetable oils and fats such as soybean oil, linseed oil, rapeseed oil, and safflower oil; fatty acid esters represented by R-COOR' (wherein R is an alkyl group having 5 to 11 carbon atoms and R’ is an alkyl group having 1 to 3 carbon atoms); “Spindle Oil No. 1”, “Solvent No. 3”, “Solvent No. 4”, “Solvent No. 5”, “Solvent No. 6”, “Naphtesol H”, and “Alkene 56NT” manufactured by JXTG Nippon Oil & Energy Corporation; “Diadol 13” and “Dialen 168” manufactured by Mitsubishi Chemical Corporation; “F OXOCOL” and “F OXOCOL 180” manufactured by NISSAN CHEMICAL INDUSTRIES, Ltd.; “AF Solvent No. 4”, “AF Solvent No. 5”, “AF Solvent No. 6”, And “AF Solvent No. 7” manufactured by JXTG Nippon Oil & Energy Corporation; D-SOL solvent “Solvent H” manufactured by ISU EXACHEM Co., Ltd.; “N-Paraffin C14-C18” manufactured by ISU EXACHEM Co., Ltd.; “Supersol LA35” and “Supersol LA38” manufactured by Idemitsu Kosan Co., Ltd.; “Exxsol D80”, “Exxsol D110”, “Exxsol D120”, “Exxsol D130”, “Exxsol D160”, “Exxsol D100K”, “Exxsol D120K”, “Exxsol D130K”, “Exxsol D280”, “Exxsol D300”, and “Exxsol D320” manufactured by EXXON Chemical Co., Ltd.; and “Magiesol 40”, “Magiesol 44”, “Magiesol 47”, “Magiesol 52”, and “Magiesol 60” manufactured by Magie Brothers Oil Company. These diluents may be used alone or in combination of two or more kinds thereof.
As described above, in the present invention, it is preferable to use the metal salt (A) or the metal complex (D) in which the central metal is manganese or iron. Further, as described above, a plurality of the metal salts (A) or the metal complexes (D) may be used in combination. When the metal salt (A) or the metal complex (D) in which the central metal is manganese or iron is an essential component, it is preferable to use a metal salt or metal complex in which the central metal is any one of bismuth, zirconium, barium, calcium, and strontium together because the performance as a curing accelerator is further improved. Among these, in a case where the central metal is one or more of bismuth, zirconium, or barium, the addition amount thereof is preferably such that the amount of metal contained in the other metal salt or metal complex is 1 to 100 parts by mass, and more preferably 3 to 40 parts by mass with respect to 1 part by mass of metal in the metal salt or metal complex in which the central metal is manganese or iron. In a case where the central metal is one or more of calcium or strontium, the addition amount thereof is preferably such that the amount of metal contained in the other metal salt or metal complex is 1 to 100 parts by mass with respect to 1 part by mass of metal in the metal salt or metal complex in which the central metal is manganese or iron.
Examples of the imidazole compound (B) include compounds represented by the following structural formula (B-1).
In the formula, R1 is independently any one of hydrogen, a hydroxyl group, an amino group, a nitro group, a nitroso group, a sulfo group, a halogen atom, a hydrocarbon group which may have a substituent, a hydrocarbon oxy group which may have a substituent, and a hydrocarbon oxycarbonyl group which may have a substituent.
The amount of the imidazole compound (B) added is preferably in a range of 0.5 to 100 parts by mass, and more preferably in a range of 1 to 30 parts by mass with respect to the metal salt (A). When the metal salt (A) and the ligand compound (C) are used in combination, the amount of the imidazole compound (B) added is preferably in a range of 0.5 to 50 parts by mass, and more preferably in a range of 1 to 20 parts by mass with respect to the total amount of the metal salt (A) and the ligand compound (C). When the metal complex (D) is used, the amount of the imidazole compound (B) added is preferably in a range of 0.5 to 100 parts by mass, and more preferably in a range of 1 to 30 parts by mass with respect to the metal complex (D).
A curable resin composition of the present invention includes the above-mentioned curing accelerator for an oxidative polymerization type unsaturated resin and an oxidative polymerization type unsaturated resin as essential components, and may contain an organic solvent, various additives, and the like. The oxidative polymerization type unsaturated resin used here may be of any type that has an unsaturated bond in the molecular structure and allows the unsaturated bond to undergo oxidative polymerization with oxygen in the air. Specifically, in a case of being used for the printing ink, a rosin-modified phenolic resin, an unsaturated group-containing polyester resin, an alkyd resin, a petroleum resin, polymerized oil, and the like are used. In addition, in a case of being used for the coating material, an alkyd resin, an unsaturated group-containing urethane resin, an unsaturated group-containing epoxy resin, an unsaturated group-containing polyester resin, polymerized oil, and the like are used. These oxidative polymerization type unsaturated resins may be used alone or in combination of two or more kinds thereof.
The curable resin composition of the present invention may be produced by any method. Specifically, the curable resin composition may be produced by a method of mixing all components for the composition at a time or by a method that includes mixing some of them in advance and then mixing the other components into the mixture. Examples include a method in which the metal salt (A) or the metal complex (D) and the imidazole compound (B) are mixed in advance to prepare a curing accelerator for an oxidative polymerization type unsaturated resin, which is mixed with an oxidative polymerization type unsaturated resin and other components; and a method in which the metal salt (A) or the metal complex (D), the imidazole compound (B), and an oxidative polymerization type unsaturated resin are mixed together. Also, examples include a method in which the metal salt (A) and the ligand compound (C) and the imidazole compound (B) are mixed in advance to prepare a curing accelerator for an oxidative polymerization type unsaturated resin, which is mixed with an oxidative polymerization type unsaturated resin and other components; a method in which after the metal salt (A) and the ligand compound (C) are mixed in advance, the imidazole compound (B) and an oxidative polymerization type unsaturated resin and other components are mixed; and a method in which the metal salt (A), the ligand compound (C), the imidazole compound (B), an oxidative polymerization type unsaturated resin, and the other components are mixed together.
A case of using the curing accelerator for an oxidative polymerization type unsaturated resin of the present invention for the printing ink will be described. The printing ink includes a pigment or a dye, a gelling agent, a surface modifier, a drying inhibitor, vegetable oil, various organic solvents, and the like, in addition to the curing accelerator for an oxidative polymerization type unsaturated resin and the oxidative polymerization type unsaturated resin. A mixing ratio of each component or the kind of mixtures is suitably adjusted depending on a printing system. The curing accelerator for an oxidative polymerization type unsaturated resin of the present invention can also be suitably used in a printing ink of any system such as a lithographic offset ink, a waterless lithographic ink, and a letterpress ink.
The amount of the curing accelerator for an oxidative polymerization type unsaturated resin mixed in the printing ink is preferably in a range of 0.001 to 5 parts by mass in 100 parts by mass of the printing ink, from viewpoints of realizing an ink which has a short drying time and skinning of which hardly occurs.
For the pigment, organic pigments for a printing ink disclosed in “Organic Pigment Handbook (writer: Isao Hashimoto, Publisher: Color Office, 2006, the first edition)” is used, for example, and a soluble azo pigment, an insoluble azo pigment, a condensed azo pigment, a metal phthalocyanine pigment, a metal-free phthalocyanine pigment, a quinacridone pigment, a perylene pigment, perinone pigment, an isoindolinone pigment, an isoindoline pigment, a dioxazine pigment, a thioindigo pigment, an anthraquinone-based pigment, a quinophthalone pigment, a metal complex pigment, a diketopyrrolopyrrole pigment, a carbon black pigment, and other polycyclic pigments can be used. In the present invention, inorganic pigments can also be used, and for example, inorganic extender pigments such as carbonate lime powder, precipitated calcium carbonate, gypsum, clay (China Clay), silica powder, diatomaceous earth, talc, kaolin, alumina white, barium sulfate, aluminum stearate, magnesium carbonate, baryte powder, and polishing powder, silicone, or glass beads are used, in addition to inorganic colored pigments such as titanium oxide, graphite, and zinc flower. The amount of these pigments mixed depends on the kinds of the desired printing ink, and is normally preferably in a range of 5 to 55 parts by mass in 100 parts by mass of the printing ink.
The gelling agent is used for adjusting viscoelasticity for the printing ink, and examples thereof include an organoaluminum compound, an organic titanate compound, an organozinc compound, and an organo-calcium compound. The gelling agents may be used alone or in combination of two or more kinds thereof. Among these, the organoaluminum compound is preferable, and examples of the organoaluminum compound include aluminum alcoholate and aluminum chelate compounds. In addition, examples of the aluminum chelate compound include aluminum diisopropoxide monoethyl acetoacetate, aluminum di-n-butoxide monomethyl acetoacetate, aluminum di-n-butoxide monoethyl acetoacetate, aluminum di-i-butoxide monomethyl acetoacetate, aluminum di-sec-butoxide monoethyl acetoacetate, aluminum tris (acetylacetonate), aluminum tris(ethyl acetoacetonate), and aluminum mono-acetylacetonate bis(ethyl acetoacetonate). The amount of the gelling agent added depends on the kinds of the desired printing ink, and is normally in a range of 0.1 to 5 parts by mass in 100 parts by mass of the printing ink.
The surface modifier is added in order to improve abrasion resistance, blocking preventing properties, sliding properties, scratch preventing properties, and other properties of an ink coating film, and examples thereof include natural wax such as carnauba wax, wood wax, lanolin, montan wax, paraffin wax, or microcrystalline wax; and synthesis wax such as Fischer-Tropsch wax, polyethylene wax, polypropylene wax, polytetrafluoroethylene wax, polyamide wax, or a silicone compound. The amount of the surface modifier mixed depends on the kinds of the desired printing ink, and is normally preferably in a range of 0.1 to 7.0 parts by mass in 100 parts by mass of the printing ink.
The drying inhibitor is added in order to improve storage stability of the printing ink and prevent skinning, and examples thereof include hydroquinone, methoquinone, and tert-butyl hydroquinone. The amount of the drying inhibitor mixed depends on the kinds of the desired printing ink, and is normally in a range of 0.01 to 5 parts by mass in 100 parts by mass of the printing ink.
Examples of the vegetable oil include monoester of the vegetable oil fatty acid such as linseed oil fatty acid methyl ester, soybean oil fatty acid methyl ester, linseed oil fatty acid ethyl ester, soybean oil fatty acid ethyl ester, linseed oil fatty acid propyl ester, soybean oil fatty acid propyl ester, linseed oil fatty acid butyl ester, or soybean oil fatty acid butyl ester, in addition to vegetable oil such as linseed oil, tung oil, rice oil, safflower oil, soybean oil, tall oil, rapeseed oil, palm oil, castor oil, or coconut oil and fat, and recycled vegetable oil obtained by being subjected to a recycling treatment after using these vegetable oils for food processing. These may be used alone or in combination of two or more kinds thereof. Among these, the vegetable oil including an unsaturated bond in a molecule such as linseed oil, tung oil, or soybean oil is preferable, from a viewpoint of producing a printing ink having excellent drying properties, and soybean oil or recycled oil thereof is more preferable, from a viewpoint of small environmental loads.
Examples of the organic solvent include “Spindle Oil No. 1”, “Solvent No. 3”, “Solvent No. 4”, “Solvent No. 5”, “Solvent No. 6”, “Naphtesol H”, and “Alkene 56NT” manufactured by JXTG Nippon Oil & Energy Corporation; “Diadol 13” and “Dialen 168” manufactured by Mitsubishi Chemical Corporation; “F OXOCOL” and “F OXOCOL 180” manufactured by NISSAN CHEMICAL INDUSTRIES, Ltd.; “AF Solvent No. 4”, “AF Solvent No. 5”, “AF Solvent No. 6”, And “AF Solvent No. 7” manufactured by JXTG Nippon Oil & Energy Corporation; D-SOL solvent “Solvent H” manufactured by ISU EXACHEM Co., Ltd.; “N-Paraffin C14-C18” manufactured by ISU EXACHEM Co., Ltd.; “Supersol LA35” and “Supersol LA38” manufactured by Idemitsu Kosan Co., Ltd.; “Exxsol D80”, “Exxsol D110”, “Exxsol D120”, “Exxsol D130”, “Exxsol D160”, “Exxsol D100K”, “Exxsol D120K”, “Exxsol D130K”, “Exxsol D280”, “Exxsol D300”, and “Exxsol D320” manufactured by EXXON Chemical Co., Ltd.; and “Magiesol 40”, “Magiesol 44”, “Magiesol 47”, “Magiesol 52”, and “Magiesol 60” manufactured by Magie Brothers Oil Company.
The amount of the vegetable oil or the organic solvent added depends on the kinds of the desired printing ink, and is normally in a range of 20 to 80 parts by mass in 100 parts by mass of the printing ink.
As a method of preparing the printing ink, for example, a method of milling a mixture of the oxidative polymerization type unsaturated resin, the pigment, the vegetable oil, the organic solvent, and various additives by an ink mill such as three-roll ink mill is used. The curing accelerator for an oxidative polymerization type unsaturated resin of the present invention may be added at the time of the milling or may be added after the milling.
A case of using the curing accelerator for an oxidative polymerization type unsaturated resin of the present invention for the coating material will be described. The coating material includes a pigment, a pigment dispersing agent, a drying inhibitor, a surface modifier, an ultraviolet absorber, a defoaming agent, a thickener, an anti-settling agent, vegetable oil, or various organic solvents, in addition to the curing accelerator for an oxidative polymerization type unsaturated resin and the oxidative polymerization type unsaturated resin. A mixing ratio of each component or the kinds of mixtures is suitably adjusted depending on the purpose or the desired performance of the coating material.
The amount of the curing accelerator for an oxidative polymerization type unsaturated resin mixed in the coating material is preferably in a range of 0.001 to 5 parts by mass in 100 parts by mass of the coating material, from viewpoints of realizing a coating material which has a short drying time and of which skinning hardly occurs.
As described above, examples of the oxidative polymerization type unsaturated resin used for the coating material include an alkyd resin, an unsaturated group-containing urethane resin, and an unsaturated group-containing epoxy resin. The alkyd resin having particularly high versatility among these is a kind of polyester resin in which a polybasic acid compound, a polyhydric alcohol compound, and an oil fatty acid are main raw material components.
As the polybasic acid compound, for example, dibasic acids such as phthalic anhydride, isophthalic acid, terephthalic acid, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, succinic acid, fumaric acid, adipic acid, sebacic acid, and maleic anhydride; and lower alkyl esterified material of these acids are mainly used. In addition, tri- or higher valent polybasic acids such as trimellitic anhydride, methylcyclohexene tricarboxylic acid, or pyromellitic anhydride; sulfophthalic acid, sulfoisophthalic acid, and ammonium salt, sodium salt, or lower alkyl esterified material of these acids can be used, if necessary. Further, as an acid component, a monobasic acid such as benzoic acid, crotonic acid, or p-tert-butylbenzoic acid can be used in combination in order to adjust a molecular weight or the like.
Examples of the polyhydric alcohol compound include dihydric alcohol such as ethylene glycol, diethylene glycol, propylene glycol, 1,4-butanediol, neopentyl glycol, 3-methylpentanediol, 1,4-hexanediol, and 1,6-hexanediol. In addition, a tri- or higher polyhydric alcohol such as glycerin, trimethylolethane, trimethylolpropane, or pentaerythritol; a polyhydric alcohol including a polyoxyethylene group; or the like can be used in combination therewith, if necessary. These polyhydric alcohols can be used alone or in combination of two or more kinds thereof. In addition, a part of the acid component and the alcohol component can also be substituted with an oxy acid component such as dimethylolpropionic acid, oxypivalic acid, or paraoxybenzoic acid; lower alkyl ester of these acids; or lactones such as ε-caprolactone.
Examples of the oil fatty acid include a coconut oil fatty acid, a soybean oil fatty acid, a linseed oil fatty acid, a safflower oil fatty acid, a tall oil fatty acid, a dehydrated castor oil fatty acid, and a tung oil fatty acid.
In addition, an epoxy-modified alkyd resin prepared by using an epoxy compound for a part of the raw materials, or a vinyl-modified alkyd resin obtained by graft polymerization with a vinyl monomer such as styrene or (meth) acrylic acid ester can also be used. Further, a polyester resin (hereinafter, abbreviated as “recycled PES”) produced using, as a main raw material, terephthalic acid recycled from polyethylene terephthalate collected for recycling of resources (for example, PET bottles), polyethylene terephthalate as industrial waste, waste generated in a case of manufacturing polyester products (films, fiber, car components, electronic components, and the like) such as polyethylene terephthalate or polybutylene terephthalate prepared by using terephthalic acid as a main raw material, or the like, can be used. A recycled PES-modified alkyd resin obtained by dissolving this recycled PES in a mixture of the alcohol component and the polybasic acid component, and allowing depolymerization and esterification can be also used.
Examples of the pigment include an inorganic pigment such as a titanium dioxide, an iron oxide, a cadmium sulfide, a calcium carbonate, a barium carbonate, a barium sulfate, clay, talc, chrome yellow, or carbon black; and an organic pigment such as an azo-based organic pigment, a diazo-based organic pigment, a condensed azo-based organic pigment, a thioindigo-based organic pigment, an indanthrone-based organic pigment, a quinacridone-based organic pigment, an anthraquinone-based organic pigment, a benzimidazolone-based organic pigment, a perylene-based organic pigment, a perinone-based organic pigment, a phthalocyanine-based organic pigment, a halogenated phthalocyanine-based organic pigment, an anthrapyridine-based organic pigment, or a dioxazine-based organic pigment. These may be used alone or in combination of two or more kinds thereof. The amount of these pigments mixed depends on the purpose or the desired performance of the coating material, and is normally preferably in a range of 20 to 70 parts by mass in 100 parts by mass of the coating material.
The drying inhibitor is added in order to improve storage stability of the coating material and prevent skinning, and examples thereof include hydroquinone, methoquinone, and tert-butyl hydroquinone. The amount of the drying inhibitor mixed depends on the purpose or the desired performance of the coating material, and is normally in a range of 0.01 to 5 parts by mass in 100 parts by mass of the coating material.
Examples of the organic solvent include “Spindle Oil No. 1”, “Solvent No. 3”, “Solvent No. 4”, “Solvent No. 5”, “Solvent No. 6”, “Naphtesol H”, and “Alkene 56NT” manufactured by JXTG Nippon Oil & Energy Corporation; “Diadol 13” and “Dialen 168” manufactured by Mitsubishi Chemical Corporation; “F OXOCOL” and “F OXOCOL 180” manufactured by NISSAN CHEMICAL INDUSTRIES, Ltd.; “AF Solvent No. 4”, “AF Solvent No. 5”, “AF Solvent No. 6”, And “AF Solvent No. 7” manufactured by JXTG Nippon Oil & Energy Corporation; D-SOL solvent “Solvent H” manufactured by ISU EXACHEM Co., Ltd.; “N-Paraffin C14-C18” manufactured by ISU EXACHEM Co., Ltd.; “Supersol LA35” and “Supersol LA38” manufactured by Idemitsu Kosan Co., Ltd.; “Exxsol D80”, “Exxsol D110”, “Exxsol D120”, “Exxsol D130”, “Exxsol D160”, “Exxsol D100K”, “Exxsol D120K”, “Exxsol D130K”, “Exxsol D280”, “Exxsol D300”, and “Exxsol D320” manufactured by EXXON Chemical Co., Ltd.; and “Magiesol 40”, “Magiesol 44”, “Magiesol 47”, “Magiesol 52”, and “Magiesol 60” manufactured by Magie Brothers Oil Company, in addition to a hydrocarbon-based solvent such as toluene, xylene, heptane, hexane, or mineral spirit, an alcohol-based solvent such as methanol, ethanol, propanol, or cyclohexanol, a ketone-based solvent such as methyl ethyl ketone, methyl isobutyl ketone, or cyclohexanone, and an ether-based solvent such as propyl ether, methyl cellosolve, cellosolve, butyl cellosolve, or methyl carbitol. The amount of the organic solvent added depends on the purpose or the desired performance of the coating material, and is normally in a range of 20 to 80 parts by mass in 100 parts by mass of the coating material.
As a method of preparing the coating material, for example, a method of mixing a mixture of the oxidative polymerization type unsaturated resin, the pigment, the organic solvent, and various additives by various mixers such as a paint shaker is used. The curing accelerator for an oxidative polymerization type unsaturated resin of the present invention may be added at the time of this mixing or after the mixing.
The coating material of the present invention can be applied on a material to be coated, dried and cured by usual methods to obtain a coating film. Here, as a base material (material to be coated) capable of being coated with the coating material of the present invention, steel or the like is used, for example. In addition, as drying conditions (curing conditions) after the coating, room-temperature drying is used. Further, the coating material of the present invention is particularly useful as a coating material for thick coating, because the coating material of the present invention can exhibit excellent curing properties, even in a case of a thick coating film. Specifically, a film thickness of the cured coating film can be in a range of 1 to 500 µm. Accordingly, the coating material of the invention is useful as coating materials for building.
Hereinafter, the present invention will be described more specifically with reference to specific examples. In the examples, “part” and “%” are based on mass, unless otherwise noted.
Compositions (1) to (4) were prepared by mixing various metal salts and ligand compounds according to proportions shown in Table 1. Details of each component used in Table 1 are as follows. Manganese neodecanoate solution: “Mn-NEODECOATE 6.5%” manufactured by DIC Corporation, benzyl alcohol solution having a manganese content of 6.5% by massIron octylate solution: “Fe-OCTOATE 6%” manufactured by DIC Corporation, benzyl alcohol solution having an iron content of 6% by mass 8-Quinolinol: “8-Quinolinol” manufactured by Tokyo Chemical Industry Co., Ltd. N,N’-Bissalicylidene-1,2-propanediamine: “N,N’-Bis(2-hydroxybenzylidene)-1,2-propanediamine” manufactured by Tokyo Chemical Industry Co., Ltd. 2-[[(2-Dimethylamino)ethyl]methylamino]ethanol: “2-[[(2-Dimethylamino)ethyl]methylamino]ethanol” manufactured by Tokyo Chemical Industry Co., Ltd. 1-Methylimidazole: “1-Methylimidazole” manufactured by Tokyo Chemical Industry Co., Ltd.
Components were mixed according to proportions shown in the following Table 2, and coating materials (1) to (5), (1'), and (2') were prepared. The resulting coating materials were evaluated for curing properties in the following manner. The results are shown in Table 2. The base coating material was prepared in the following manner. Details of each component used in Table 2 are as follows. Anti-skinning agent: “Methyl ethyl ketoxime” manufactured by Ube Industries, Ltd. Manganese neodecanoate solution: “Mn-NEODECOATE 6.5%” manufactured by DIC Corporation, benzyl alcohol solution having a manganese content of 6.5% by mass Cobalt octylate solution: “DICNATE210SB” manufactured by DIC Corporation, soybean oil solution having a cobalt content of 10% by mass. 1-Methylimidazole: “1-Methylimidazole” manufactured by Tokyo Chemical Industry Co., Ltd. Zirconium soap: “12% Zr-OCTOATE” manufactured by DIC Corporation, mineral spirit solution having a zirconium content of 12% by mass
100 parts by mass of Titanium white pigment (“Ti-Pure R-960” manufactured by Chemours Co., Ltd.), 40 parts by mass of calcium carbonate (“NS#100” manufactured by Nitto Funka Kogyo K.K.), 240 parts by mass of alkyd resin (“Alukidir P-470-70” manufactured by DIC Corporation) and 20 parts by mass of mineral spirit (“Mineral Spirit A” manufactured by JXTG Nippon Oil & Energy Co., Ltd.) were kneaded with a paint shaker to obtain a base coating material.
The test was carried out in a constant temperature and humidity chamber (23±2° C., 50±5% RH). The previously obtained coating material was applied to a glass plate with an applicator of 76 µm. After the application, the time until the coating material was completely dried and a scratch applied by a needle of a drying time recorder (“Model No. 404” manufactured by Taiyu Kizai Co., Ltd.) was not observed was measured.
Components were mixed according to proportions shown in the following Table 3, and printing inks (1) to (3) were prepared. The resulting printing inks were evaluated for curing properties in the following manner. The results are shown in Table 3. The base ink was prepared in the following manner.
100 parts by mass of a rosin-modified phenolic resin (“BECKACITE F-7310” manufactured by DIC Corporation) and 100 parts by mass of soybean oil (“Soybean Salad Oil (S)” manufactured by The Nisshin Oillio Group, Ltd.) were heated at 210° C. for 1 hour, and 47.5 parts by mass of an organic solvent (“AF Solvent No. 6” manufactured by JXTG Nippon Oil & Energy Co., Ltd.) and 2.5 parts by mass of an aluminum chelate (“Chelope (S)” manufactured by Hope Chemical Co., Ltd.) were added thereto, and the mixture was heated at 150° C. for 1 hour to prepare a varnish for printing ink. 100 parts by mass of the previously obtained varnish for printing ink, 20 parts by mass of a phthalocyanine blue pigment (“FASTOGEN BLUE TGR-L” manufactured by DIC Corporation), 25 parts by mass of soybean oil (“Soybean Salad Oil (S)” manufactured by The Nisshin Oillio Group, Ltd.), and 25 parts by mass of an organic solvent (“AF Solvent No. 6” manufactured by JXTG Nippon Oil & Energy Co., Ltd.) were kneaded in a three-roll mill to obtain a base ink.
The test was carried out in a constant temperature and humidity chamber (23±2° C., 50±5% RH). The previously obtained printing ink was applied to a glass plate with an applicator of 38 µm. After the application, the time until the ink was completely dried and a scratch applied by a needle of a drying time recorder (“Model No. 404” manufactured by Taiyu Kizai Co., Ltd.) was not observed was measured.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017-113409 | Jun 2017 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16614880 | Nov 2019 | US |
| Child | 17955678 | US |