Patent Application
20050037224
The present invention relates to curved surfaces, particularly reflectors such as concave mirror elements for use in astronomical telescopes, solar energy concentrators etc., and to methods of forming such surfaces. Besides optical reflectors, the invention is also applicable to curved electromagnetic radiation reflectors for a variety of purposes, such as microwave reflectors for use in telecommunications, and to non-reflective surfaces where an accurately formed curved surface is required.
Conventional curved mirror elements for astronomical telescopes are typically formed by machining solid glass or aluminium. This is expensive and the resulting mirror elements are relatively heavy. Conventional mirrors for very large telescopes (e.g. of the order of 7 m diameter, such as are required for gamma ray astronomy) have to be assembled as an array of segments, because it would be impractical to form such large mirrors in a single piece using conventional techniques. It is desirable that such mirrors should be lightweight, inexpensive and robust. Conventional mirrors are unsatisfactory in all of these respects.
There have been previous proposals for the manufacture of mirrors/reflectors using composite materials and the like, as exemplified by U.S. Pat. No. 5,564,066, however none of these has been satisfactory in practice, for a number of reasons.
In accordance with a first aspect of the invention, there is provided a method of forming a rigid body with a curved surface, comprising:
The vacuum source may be deactivated once any bonding agent used to bond the base member to the planar member has been cured.
The method preferably further includes bonding at least one peripheral casing member to a peripheral surface of the base member and at least one generally planar casing member to a rear surface of the base member. Preferably, this is done while the base member is in situ on the mould, and most preferably while the vacuum source is operating.
The rigid body formed by the method is typically circular in plan, but may have other shapes such as part-circular segments, or geometric (polygonal) shapes, e.g. hexagonal, octagonal etc, or triangular segments of polygonal shapes, etc.
The curved surface is typically at least partially concave, or may be at least partially convex. This includes surfaces having hybrid or irregular shapes that may include both concave and convex facets.
The base member is preferably formed from a rigid, low density material, preferably a honeycomb material and most preferably an aluminium or aluminium alloy honeycomb material.
The rigid body formed by the method may be a reflector.
The flexible planar member is preferably a reflective member, which preferably comprises a thin metallic sheet, more preferably a thin aluminium or aluminium alloy sheet, and most preferably an anodised and coated aluminium sheet.
The casing members are preferably also formed from aluminium or aluminium alloy.
In accordance with a second aspect of the invention, there is provided a rigid body having a curved surface, comprising a generally planar, flexible member that is vacuum formed to a required curvature and bonded to a surface of a structurally rigid base member.
The preferred features and characteristics of the rigid body are as defined above in relation to the first aspect of the invention.
Embodiments of the invention will now be described with particular reference to curved reflectors, by way of example only, with reference to the accompanying drawings, in which:
Referring now to the drawings, a circular curved reflector 10 comprises a base member 12, a reflective member 14, a peripheral (annular, ring-shaped) casing member 16 and a planar casing member 18. The base member 12 has a generally planar rear surface, a front surface (adjacent the reflective member 14), and an annular peripheral surface. The front surface of the base member may be shaped to conform approximately to the required curvature of the reflective surface (particularly where the curvature is relatively large) or may be substantially planar (particularly where the curvature is relatively small)
The reflective member 14 comprises a thin, flexible sheet of reflective material that is bonded to the front surface of the base member 12. The required curvature of the reflective member 14 is obtained by vacuum forming the reflective member 14 to a mould 20, prior to bonding the front surface of the base member 12 thereto, as shall be described in more detail below.
The casing members 16, 18 are bonded to the other outer surfaces of the base member 12 (and to the periphery of the reflective member 14 in the case of the annular casing member 16).
In order for the reflector to exhibit good thermal stability, it is preferable for all of its components to be formed from the same or similar materials, or from materials having similar thermal properties. It is also desirable for the weight of the reflector to be minimised. For this reason, aluminium or aluminium alloy is the preferred material for the base member 12, reflective member 14 and casing members 16 and 18, and the components are bonded together using an epoxy material having similar thermal properties to aluminium, as is well known, for example, in the aerospace industry.
The base member 12 preferably comprises a rigid aluminium honeycomb material, such as is used for structural members in aircraft. The size of the honeycomb cells should be sufficiently small to avoid the formation of significant flats in the reflective surface when the reflective member is bonded thereto. The reflective member 14 preferably comprises a thin sheet of anodised aluminium, most preferably anodised and coated aluminium (e.g. coated with TiO2 or quartz after anodization). The thickness of the reflective member is determined by the requirement for it to be deformed by a vacuum to conform to the surface of the mould 20 and the need to avoid the formation of flats, which depends on the size of the base member honeycomb cells. The required precision of the reflector surface in turn depends on its intended application. That is, the thickness of the reflective sheet and the honeycomb cell size are interdependent, and depend in turn on the required precision of the reflector surface. For a high precision surface for use in astronomical telescope mirrors, the reflective member might suitably be of the order of 0.8 mm in thickness when used with a base member having a honeycomb cell size of the order of 0.25 inch (6.35 mm). Generally, the thickness of the reflective member is likely to be in the range 0.5 to 2 mm. An example of a suitable aluminium honeycomb material is 3003 aluminium, cell size 0.25 inch (6.35 mm), foil gauge 0.0015 inch (0.038 mm), nominal density 3.4 lb/ft3 (54.5 kg/m3), with a thickness of 25 mm (dependent on the size of the reflector).
The combination of the reflective member 14 and the base member 12 exhibits good rigidity. The casing members 16 and 18 are provided primarily to aid structural integrity and to protect the base member honeycomb against the ingress of moisture etc., to facilitate the attachment of other mechanical fittings thereto and to protect users against contact with the sharp edges of the honeycomb material. The casing ring 16 might suitably be of the order of 2 mm thick, with a depth corresponding to the thickness of the bonded base. The back casing plate 18 might suitably be of the order of 2 mm thick.
The reflector is assembled as follows.
A mould 20 is formed, by any of a variety of known techniques, having a precision curved surface complementary to the required reflector surface. At least one vacuum port 22 extends through the mould 20 to communicate with the curved surface, and is connected to a vacuum source (not shown). The reflective member 14 is laid on top of the mould 20 and is sealed thereto by a seal member 24, such as an O-ring. The curvature of the mould 20 is exaggerated in
The vacuum source is operated to evacuate the space between the mould 20 and the reflective member 14, causing the reflective member 14 to deform and conform closely to the curved surface of the mould.
The surface of the mould 20 may be provided with one or more grooves (not shown) to assist in the rapid and uniform evacuation of air from between the mould 20 and the reflective member 14. The dimensions of such grooves is selected to be sufficiently small to avoid any undesirable deformation of the reflective member 14. It will be understood that the desired deformation of the reflective member 14 to conform to the surface of the mould 20 may comprise plastic and/or elastic deformation, depending on the material of the reflective member 14 and/or the degree of curvature.
While the vacuum is maintained, the front surface of the base member 12 is bonded to the reverse surface of the reflective member 14. Once the bonding agent has cured, the vacuum may be removed. If necessary, the front surface of the honeycomb base member 12 may be preformed (e.g. by crushing) to conform approximately to the required shape of the reflective surface. If the required curvature is small, the front surface of the base member 12 may be substantially planar, and the thickness of the bonding agent may vary to match the curvature of the reflective member 14.
The reflective member 14 as initially applied to the mould is slightly oversized in relation to the base member 12 and may subsequently be trimmed.
The casing members 16 and 18 are preferably bonded to the base member 12 and reflective member 14 while in situ on the mould and while the vacuum source is operating. Preferably, pressure is applied at least to the rear surface of the assembly while the bonding agent is curing to ensure good contact between the base member the bonding agent and the reflective member.
Aluminium or aluminium alloy is the preferred material for all of the components, but other materials, such as carbon fibre, could be used depending on the intended application of the reflector.
The surface of the mould 20 may be formed to sufficient precision that no post-processing of the reflector surface is necessary. If required, final polishing and/or coating of the reflector surface may be performed.
Improvements and modifications may be incorporated without departing from the scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0130141.5 | Dec 2001 | GB | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/GB02/05697 | 12/16/2002 | WO |