Patent Application
20060019120
The present invention relates to a coated cutting tool insert with a sharp cutting edge particularly useful for machining of non-ferrous materials such as titanium, aluminium, brass, bronze, plastics etc.
For the machining of metals, cutting tool inserts of cemented carbide having a rake face and clearance faces intersecting to form a cutting edge are used. The cutting edge should be sharp to provide low cutting forces and low energy consumption. However, cemented carbide is a brittle material and for that reason, a sharp cutting edge is generally not strong enough. If it breaks, the cutting forces increase and the surface finish of the machined material will be poor. In order to strengthen the edge it can be rounded to a radius of generally 10-50 μm, or provided with a chamfer or a land. The exact design of the edge depends on the material to be machined and is a compromise between acceptable cutting forces and strength of the edge. Some workpiece materials such as aluminium, etc., require a very sharp edge with minimal edge rounding. An excessively rounded edge can in such materials represent a worn edge and can affect the subsequent wear development. For the machining of such materials, uncoated cemented carbide inserts are generally used. If a coating is applied, the edge will be less sharp. In addition, coated cutting edges require a certain amount of rounding to ensure a satisfactory application of a coating. It is however, a desire to be able to use coated inserts also for the machining of materials requiring sharp cutting edges.
Published U.S. Patent Application 2002/0187370 disclose the grinding of certain amounts of the rake face and flank side of a blade-edge ridge to achieve a surface roughness of 0.2 μm or less over a reference length of 5 μm. It is stated that surface reforming by means of microblasting and ion-beam radiation may also be applied but only grinding and lapping are exemplified.
It is therefore an object of the present invention to provide a method of making coated cemented carbide cutting inserts with a sharp edge.
In one aspect of the invention, there is provided a cutting tool insert for metal machining comprising a substrate, a coating comprising at least one wear resistant layer on the substrate, said insert further comprising clearance faces and rake faces intersecting to form cutting edges, wherein the cutting edge has essentially no edge radius, the coating has been removed by grinding on the clearance face from at least close to the cutting edge and the coating on the rake face has a surface roughness of less than about 0.3 μm over a measured length of 0.25 mm.
In another aspect of the invention, there is provided a method of making a cutting tool insert for metal machining comprising providing a coated cutting tool insert having a coating comprising at least one wear resistant layer and a substrate, said insert further comprising clearance faces and rake faces intersecting to form cutting edges, subjecting at least the rake face of said insert to a blasting operation to obtain a smooth surface with a surface roughness (Ra) of less than about 0.3 μm over a measured length of 0.25 mm and subjecting the insert to a peripheral grinding operation with a fine grinding wheel to obtain a cutting edge with essentially no edge radius.
In order to obtain a sharp cutting edge, the coated inserts have to be ground on the clearance face after the coating operation. Initial tests indicated that such a method seemed not to be possible because the grinding operation led to damages to the coating in the edge line and an insufficiently sharp edge. It has, however, surprisingly been found that if the coating is subjected to a final blasting operation at least on the rake face in a surface roughness (Ra) of less than about 0.3 μm over a measured length of 0.25 mm before grinding then the coating remains almost unaffected by the grinding operation resulting in an extremely sharp edge.
In a preferred embodiment, the outermost layer is an alumina layer, preferably an α-alumina layer, with a thickness of from about 1 to about 10 μm, preferably from about 3 to about 6 μm
In a further preferred embodiment, there is an inner layer of Ti(C,N) between the alumina layer and the substrate with a thickness of from about 1 to about 10 μm, preferably from about 4 to about 7 μm, with columnar grains.
The present invention also relates to a method of making a coated cutting tool insert with extremely sharp edge by
The invention is additionally illustrated in connection with the following Examples which are to be considered as illustrative of the present invention. It should be understood, however, that the invention is not limited to the specific details of the Examples.
Cemented carbide inserts of style N-123L-0800-AM with a composition of 6% Co and as balance WC were coated with a 0.5 μm equiaxed TiCN-layer followed by a 5 μm thick TiCN layer with columnar grains by using MTCVD-technique (process temperature 850° C.). In subsequent process steps during the same coating cycle, a 1 μm thick layer with equiaxed grains of TiCxNyOz (approx. x=0.6, y=0.2 and z=0.2) was deposited followed by a 4 μm thick layer of α-Al2O3 deposited. After coating, the inserts were smoothed by wet blasting to a surface roughness of 0.2 μm over a measured length of 0.25 mm. Finally, the inserts were subjected to a peripheral grinding operation by a diamond disk with 25 μm grain size to obtain a sharp cutting edge.
Example 1 was repeated without the blasting operation and with a coating of a 0.5 μm equiaxed TiC0.05N0.95-layer followed by a 2.6 μm thick TiC0.54N0.46-layer, with columnar grains by using MTCVD-technique (temperature 850-885° C. and CH3CN as the carbon/nitrogen source). In subsequent steps during the same coating cycle, a 1.3 μm thick layer of κ-Al2O3 was deposited using a temperature 970° C. and a concentration of H2S dopant of 0.4%. A 0.5 μm layer of TiN was deposited on top according to known CVD-technique.
Example 1 was repeated without the final blasting operation. An appearance of the coating of the edge line similar to that of