Patent Grant
11865831
This application claims the benefit of priority under 35 U.S.C. § 119 of European Patent Application No. 21188763.3, entitled CYLINDER SLEEVE HAVING A LOW CARBON DIOXIDE RELEASE, and filed Jul. 30, 2021, the contents of which are relied upon and incorporated herein by reference in their entirety.
The present invention relates to a process for preparing a cylinder sleeve wherein the process particularly comprises a specific tempering step of said cylinder sleeve. Further, the present invention relates to a cylinder sleeve obtainable and/or obtained by said process. Therefore, the present invention also relates to a cylinder sleeve particularly exhibiting a comparatively reduced CO2 release. In addition thereto, the present invention relates to a use of said cylinder sleeve, preferably in a printing process, and more preferably in a flexographic printing process.
In a typical printing process, a printing plate is mounted on a cylinder sleeve. Said printing plate is usually fixed by an adhesive layer which was applied on the cylinder sleeve in advance. Specific embodiments of said adhesive layer allow repeated mounting and de-mounting of a printing plate for repeated use of the cylinder sleeve. To ensure high quality printing, the cylinder sleeve has to meet specific requirements, in particular with respect to a specific total indicated runout and a specifically constant sleeve diameter. Otherwise, defects in printing may occur leading to an inferior printing quality.
US 2006/137551 A1 discloses a composite compensator sleeve designed specifically to compensate for the dimensional difference that exists between a rotational drive carrier and a printing form, wherein said sleeve comprises a tubular nickel-based metal internal base, an external layer of a hard elastomer material, and an intermediate layer of a soft elastomer material placed between the metal internal base and the hard external layer. Further, a flexographic printing process is disclosed therein.
EP 2292441 A1 discloses a method of making a printing blanket including a cast polyurethane layer.
It has been found that inferior printing quality can occur, in particular if a cylinder sleeve having an adhesive layer applied thereon is used over a longer period, and especially when said cylinder sleeve having an adhesive layer applied thereon was repeatedly used. It has been found that blister formation between the adhesive layer and the upper layer of the cylinder sleeve was responsible for said inferior printing quality because such blisters can have a negative impact on the consistent fixation of the printing plate, thereby disadvantageously affecting the quality of the printing.
Said blisters can be formed due to gas released by the cylinder sleeve which cannot permeate through the adhesive layer. Said blister formation can lead to variances of the total indicated runout and of the diameter of the sleeve, respectively, such that a high quality printing process cannot be ensured.
Therefore, the need exists to provide a cylinder sleeve which has a reduced carbon dioxide (CO2) release such that, in particular, blister formation can be significantly reduced or even essentially avoided when an adhesive layer is applied on the cylinder sleeve.
It has surprisingly been found that by subjecting a cylinder sleeve to a specific treatment step, the resulting cylinder sleeve exhibits a significantly reduced CO2 release. Thus, the resulting cylinder sleeve is suitable for ensuring a high quality printing process, in particular for repeated application of a printing plate thereon.
According to an aspect of the disclosure, a cylinder sleeve is provided that includes:
According to another aspect of the disclosure, a process for preparing a cylinder sleeve is provided that includes:
According to a further aspect of the disclosure, a method for preparing a multitude of cylinder sleeves is provided that includes:
Additional features and advantages will be set forth in the detailed description which follows and will be apparent to those skilled in the art from the description, or recognized by practicing the embodiments as described in the following description, together with the claims.
The present invention relates to a cylinder sleeve, comprising:
The physical unit “d” (day) as used throughout the present invention, such as in the context of the carbon dioxide release coefficient RCO2, refers to a period of time of 24 hours.
Preferably, the carbon dioxide release coefficient RCO2 of the cylinder base sleeve according to (a) is in the range of from 0 to 9 ppmv cm−3 d−1, more preferably in the range of from 0 to 8 ppmv cm−3 d−1, more preferably in the range of from 0 to 7 ppmv cm−3 d−1, more preferably in the range of from 0 to 6 ppmv cm−3 d−1, more preferably in the range of from 0 to 5 ppmv cm−3 d−1.
With respect to the cylindrical polyurethane layers according to (a), it is preferred that each of the said cylindrical polyurethane layers, independently of each other, consist from 75 to 100 weight-%, more preferably from 85 to 100 weight-%, more preferably from 95 to 100 weight-%, of polyurethane.
Further, it is preferred that at least one of the one or more cylindrical polyurethane layers according to (a) further comprises at least one additive, wherein the at least one additive is preferably one or more of a pigment and a conductivity amplifier, more preferably one or more of carbon black and carbon nanotubes.
No particular restriction applies with respect to the thickness of the one or more cylindrical polyurethane layers according to (a). It is preferred that, independently of each other, each of the one or more cylindrical polyurethane layers according to (a) has a thickness in the range of from 25 micrometer to 150 mm, more preferably in the range of from 50 micrometer to 110 mm, more preferably in the range of from 100 micrometer to 100 mm.
Further, it is preferred that, independently of each other, each of the one or more cylindrical polyurethane layers according to (a) has a density in the range of from 0.01 to 2.0 g cm−3, more preferably in the range of from 0.05 to 1.75 g cm−3, more preferably in the range of from 0.1 to 1.5 g cm−3.
No particular restriction applies with respect to the number of cylindrical polyurethane layers according to (a). It is preferred that the cylinder base sleeve according to (a) comprises from 1 to 10, more preferably from 1 to 8, more preferably from 1 to 6, more preferably from 1 to 4, cylindrical polyurethane layers, such as 1 or 2 or 3 or 4 cylindrical polyurethane layers.
The cylinder base sleeve according to (a) may further comprise, in addition to the one or more cylindrical polyurethane layers, one or more further cylindrical layers. It may be preferred that independently of each other, from 0 to 1 weight-%, more preferably from 0 to 0.5 weight-%, more preferably from 0 to 0.2 weight-%, more preferably from 0 to 0.1 weight-% of each of said further cylindrical layers consist of polyurethane, based on the total weight of the respective cylindrical layer.
Further in the case where the cylinder base sleeve according to (a) further comprises one or more further cylindrical layers, in addition to the one or more cylindrical polyurethane layers, it is preferred that said one or more further cylindrical layers comprises one or more of a glass fiber, a carbon fiber, an unsaturated polyester resin, an epoxy resin, a vinyl ester resin, a UV polymerizable resin, more preferably an acrylate-based UV polymerizable resin, wherein said one or more further cylindrical layers preferably comprise, more preferably consist of, a glass fiber reinforced composite comprising one or more of an unsaturated polyester resin, an epoxy resin, a vinyl ester resin, a UV polymerizable resin, preferably an acrylate-based UV polymerizable resin, and a carbon fiber reinforced composite comprising one or more of an unsaturated polyester resin, an epoxy resin, a vinyl ester resin, and a UV polymerizable resin, preferably an acrylate-based UV polymerizable resin.
No particular restriction applies with respect to the number of cylindrical layers of the cylinder base sleeve according to (a). In particular, the cylinder base sleeve according to (a) can further comprise one or more further cylindrical layers in addition to the one or more cylindrical polyurethane layers. It is preferred that the cylinder base sleeve according to (a) consists of from 2 to 10 cylindrical layers, more preferably of from 2 to 8 cylindrical layers, more preferably of from 2 to 6 cylindrical layers.
Thus, particularly considering that the cylinder base sleeve according to (a) may further comprise one or more further cylindrical layers, in addition to the one or more cylindrical polyurethane layers, and that the number of cylindrical layers of the cylinder base sleeve according to (a) may vary, depending on the specific requirements of a cylinder sleeve, different alternatives are possible with respect to a specific arrangement of said cylindrical layers. In particular, the following six embodiments are preferred in this regard.
According to a first alternative, it is preferred that the cylinder base sleeve according to (a) consists of two (2) cylindrical layers on top of each other, being a first cylindrical layer and a second cylindrical layer, wherein the first cylindrical layer is the innermost layer and the second cylindrical layer is the outermost layer, wherein the first cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined hereinabove, and the second cylindrical layer comprises polyurethane, wherein the second cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove.
According to a second alternative, it is preferred that the cylinder base sleeve according to (a) consists of four (4) cylindrical layers on top of each other, being a first cylindrical layer, wherein the first cylindrical layer is the innermost layer, a second cylindrical layer on the first cylindrical layer, a third cylindrical layer on the second cylindrical layer, and a fourth cylindrical layer on the third cylindrical layer, wherein the first cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, the second cylindrical layer comprises a polyurethane, wherein the second cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a soft foam, the third cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, and the fourth cylindrical layer comprises a polyurethane, wherein the fourth cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove.
According to a third alternative, it is preferred that the cylinder base sleeve according to (a) consists of five (5) cylindrical layers on top of each other, being a first cylindrical layer, wherein the first cylindrical layer is the innermost layer, a second cylindrical layer on the first cylindrical layer, a third cylindrical layer on the second cylindrical layer, a fourth cylindrical layer on the third cylindrical layer, and a fifth cylindrical layer on top of the fourth cylindrical layer, wherein the first cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, the second cylindrical layer comprises a polyurethane, wherein the second cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a soft foam, the third cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, the fourth cylindrical layer comprises polyurethane, wherein the fourth cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a hard foam, and the fifth cylindrical layer comprises a polyurethane, wherein the fifth cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove.
According to a fourth alternative, it is preferred that the cylinder base sleeve according to (a) consists of four (4) cylindrical layers on top of each other, being a first cylindrical layer, wherein the first cylindrical layer is the innermost layer, a second cylindrical layer on the first cylindrical layer, a third cylindrical layer on the second cylindrical layer, and a fourth cylindrical layer on the third cylindrical layer, wherein the first cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, the second cylindrical layer comprises a polyurethane, wherein the second cylindrical layer preferably is a cylindrical polyurethane layer as in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a soft foam, the third cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, and the fourth cylindrical layer comprises a polyurethane, wherein the fourth cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove.
According to a fifth alternative, it is preferred that the cylinder base sleeve according to (a) consists of five (5) cylindrical layers on top of each other, being a first cylindrical layer, wherein the first cylindrical layer is the innermost layer, a second cylindrical layer on the first cylindrical layer, a third cylindrical layer on the second cylindrical layer, a fourth cylindrical layer on the third cylindrical layer, and a fifth cylindrical layer on top of the fourth cylindrical layer, wherein the first cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, the second cylindrical layer comprises a polyurethane, wherein the second cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a soft foam, the third cylindrical layer comprises a polyurethane, wherein the third cylindrical layer is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a hard foam, the fourth cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, and the fifth cylindrical layer comprises a polyurethane, wherein the fifth cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove.
According to a sixth alternative, it is preferred that the cylinder base sleeve according to (a) consists of six (6) cylindrical layers on top of each other, being a first cylindrical layer, wherein the first cylindrical layer is the innermost layer, a second cylindrical layer on the first cylindrical layer, a third cylindrical layer on the second cylindrical layer, a fourth cylindrical layer on the third cylindrical layer, a fifth cylindrical layer on top of the fourth cylindrical layer, and a sixth cylindrical layer on the fifth cylindrical layer, wherein the first cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, the second cylindrical layer comprises a polyurethane, wherein the second cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a soft foam, the third cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, the fourth cylindrical layer comprises a polyurethane, wherein the fourth cylindrical layer is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove, wherein the polyurethane is preferably a hard foam, the fifth cylindrical layer comprises a glass fiber, preferably a glass fiber reinforced composite as defined in one or more of the particular and preferred embodiments hereinabove, and the sixth cylindrical layer comprises a polyurethane, wherein the sixth cylindrical layer preferably is a cylindrical polyurethane layer as defined in one or more of the particular and preferred embodiments hereinabove.
The cylinder sleeve according to the present invention comprises an adhesive layer according to (b). It is preferred that the adhesive layer according to (b) comprises a polymer, wherein the polymer is preferably obtainable or obtained by crosslinking one or more compounds having two or more ethylenically unsaturated groups, wherein the one or more compounds having two or more ethylenically unsaturated groups are preferably selected from the group consisting of:
It is preferred that the polymer comprised in the adhesive layer according to (b) comprises a repeating unit comprising a functional group selected from the group consisting of:
In the case where the polymer comprised in the adhesive layer according to (b) comprises a repeating unit comprising a functional group selected from the group consisting of VI., VII., and VIII. as defined hereinabove, it is preferred that the functional group has a weight average molecular weight in the range of from 500 to 10,000 Dalton, more preferably in the range of from 1,000 to 5,000 Dalton.
Further in the case where the polymer comprised in the adhesive layer according to (b) comprises a repeating unit comprising a functional group selected from VI., VII., and VIII. as defined hereinabove, it is preferred that the one or more compounds having two or more ethylenically unsaturated groups are one or more compounds according to formula (I) or according to formula (II) as defined hereinabove, wherein a functional group according to one or more of the particular and preferred embodiments hereinabove is comprised in one of R1 and R2, preferably in R2, wherein said functional group is preferably a hydrogenated polyene, preferably a hydrogenated polybutadiene, and wherein the other one of R1 and R2, preferably R1, is a non-polymeric group having a molecular weight of at most 500 Dalton, preferably less than 500 Dalton, said polymeric group preferably being an aromatic group having from 6 to 20 carbon atoms or an aliphatic group having from 2 to 20 carbon atoms, said aromatic group preferably being toluene diisocyanate (TDI), methylene diphenyl diisocyanate (MDI), butane diisocyanate (BDI), hexamethylene diisocyanate (HDI), trimethyl-hexamethylene diisocyanate (TMDI), lysine ethyl ester diisocyanate (ELDI), lysine methyl ester diisocyanate (MLDI), isophorone diioocyanate (IPDI) or 1,4-cyclohexane diisocyanate (CHDI).
In the case where the adhesive layer according to (b) comprises a polymer, it is preferred that the one or more compounds having two or more ethylenically unsaturated groups further comprise one or more (meth)acrylate compounds, preferably not containing a —NHC(O)O— group, more preferably one or more (meth)acrylate compounds selected from the group consisting of:
The cylinder sleeve according to the present invention comprises according to (b) one or more cylindrical layers, arranged on top of each other. In particular, the following two alternatives are preferred in this regard.
According to a first alterative, it is preferred that the cylinder sleeve comprises, according to (b), one single cylindrical layer applied on the lateral surface of the cylinder base sleeve according to (a), said one single cylindrical layer being the adhesive layer for attaching a printing plate thereto.
According to a second alternative, it is preferred that the cylinder sleeve comprises, according to (b), one or more cylindrical layers, more preferably one or two cylindrical layers, applied between the outermost adhesive layer according to (b) and the lateral surface of the cylinder base sleeve according to (a).
With respect to the second alternative, it is further preferred that at least one of said one or more cylindrical layers, more preferably of said one or two cylindrical layers, is a stabilizing layer, wherein said stabilizing layer more preferably comprises one or more of polyethylene terephthalate (PET), polyvinyl chloride (PVC), polyethylene (PE), polyamide (PA), and polypropylene (PP), more preferably PET, wherein more preferably, from 75 to 100 weight-%, more preferably from 90 to 100 weight-%, more preferably from 95 to 100 weight-%, of the stabilizing layer consist of PET. It is preferred that the stabilizing layer has a thickness in the range of from 2 to 600 micrometer, more preferably in the range of from 5 to 550 micrometer, more preferably in the range of from 10 to 500 micrometer.
Further with respect to the second alternative, it is preferred that said one or more cylindrical layers exhibit a carbon dioxide release coefficient RCO2 in the range of from 0 to 1 ppmv cm−3 d−1, RCO2 being defined as the amount of carbon dioxide in ppmv released by said one or more cylindrical layers per day and volume of said one or more cylindrical layers in cm3, RCO2 being determined in an air atmosphere exhibiting a relative humidity in the range of from 25 to 60% at a temperature of the gas atmosphere in the range of from 48 to 52° C. and at a pressure in the range of from 0.95 to 1.15 bar(abs), determined essentially as described in Reference Example 1.
Preferably, the adhesive layer according to (b) exhibits a carbon dioxide release coefficient RCO2 in the range of from 0 to 1 ppmv cm−3 d−1, RCO2 being defined as the amount of carbon dioxide in ppmv released by said one or more cylindrical layers per day and volume of said one or more cylindrical layers in cm3, RCO2 being determined in an air atmosphere exhibiting a relative humidity in the range of from 25 to 60% at a temperature of the gas atmosphere in the range of from 48 to 52° C. and at a pressure in the range of from 0.95 to 1.15 bar(abs), determined essentially as described in Reference Example 1.
With respect to the cylinder base sleeve according to the present invention, it is preferred that it has a side wall thickness in the range of from 0.5 to 200 mm, preferably in the range of from 1 to 100 mm, more preferably in the range of from 1.5 to 75 mm, more preferably in the range of from 2 to 50 mm.
No particular restriction applies with respect to the axial length of the cylinder base sleeve of the present invention. It is preferred that the cylinder sleeve according to the present invention has an axial length in the range of from 50 to 5000 mm, more preferably in the range of from 100 to 4000 mm, more preferably in the range of from 300 to 3000 mm, more preferably in the range of from 400 to 2500 mm.
Preferably, the cylinder base sleeve of the present invention has a total indicated runout of at most 90 micrometer, preferably of at most 50 micrometer, more preferably of at most 40 micrometer, wherein the total indicated runout is determined as described in DIN ISO 2768 T1 c.
Further, it is preferred that the cylinder base sleeve according to the present invention has a surface hardness in the range of from 65 to 95 Shore D, more preferably in the range of from 70 to 85 Shore D, determined as described in DIN 53505.
Further, it is preferred that the cylinder base sleeve according to the present invention has an electric resistance of at most 106 Ohm, determined as described in the Directive 94/9/EC of the European Parliament and the Council of 23 Mar. 1994.
It is preferred that the deviation in the diameter of the cylinder sleeve according to the present invention is at most ±80 micrometer, preferably at most ±60 micrometer, more preferably at most ±40 micrometer. The term “deviation in the diameter” as used in the context of the present invention refers to the result of a statistically relevant number of diameter measurements over the entire axial length of the cylinder sleeve.
It is preferred that on each front end of the cylinder sleeve, an end plate is applied which covers at least the respective end wall surface of the cylinder sleeve.
It is preferred that the cylinder sleeve according to the present invention consists of the base sleeve according to (a) and the one or more cylindrical layers according to (b).
The cylinder sleeve according to the present invention is particularly suitable for application in a printing process, in particular in a flexographic printing process. Thus, it is preferred that the cylinder sleeve further comprises (c) a printing plate being applied onto the outer surface of the adhesive layer according to (b). It is preferred that the cylinder sleeve consists of the base sleeve according to (a), the one or more cylindrical layers according to (b) and the printing plate according to (c). Further, it is preferred that the printing plate has a thickness in the range of from 0.5 to 5.0 mm, more preferably in the range of from 1.0 to 3.0 mm, more preferably in the range of from 1.1 to 2.6 mm. In addition thereto, it is preferred that the cylinder sleeve comprising a printing plate according to (c) has a repeat length in the range of from 50 to 2000 mm, more preferably in the range of from 175 to 1700 mm, more preferably in the range of from 200 to 1650 mm.
Further, the present invention relates to a process for preparing a cylinder sleeve according to any one of the embodiments disclosed herein, optionally according to any one of the embodiments relating to a cylinder sleeve comprising a printing plate, said process comprising:
It is preferred that the air atmosphere according to (ii) has a temperature in the range of from 30 to 55° C., more preferably in the range of from 35 to 50° C.
It is preferred that the cylinder base sleeve provided according to (i) is subjected to the air atmosphere according to (ii) for a period in the range of from 34 to 528 h, preferably in the range of from 48 to 336 h.
It is preferred that the air atmosphere according to (ii) has a relative humidity in the range of from 15 to 80%, more preferably in the range of from 30 to 80%, more preferably in the range of from 35 to 75%, more preferably in the range of from 40 to 60%.
It is preferred that the cylinder base sleeve provided in (i) is subjected to the air atmosphere according to (ii) at an absolute pressure in the range of from 0.85 to 1.15 bar(abs), preferably in the range of from 0.9 to 1.1 bar(abs).
According to the present invention, the following two alternatives are preferred with respect to the temperature of the air atmosphere according to (ii), in particular in connection with the period of time for subjecting the cylinder sleeve to step (ii), the relative humidity of said air atmosphere and/or the pressure of said air atmosphere.
According to a first alternative, it is preferred to apply a comparatively high temperature, preferably with a comparatively short period of time, and further preferably with a specific relative humidity. In particular, it is preferred that the air atmosphere according to (ii) has a temperature in the range of from 45 to 55° C., more preferably in the range of from 48 to 52° C. Further, it is preferred that the cylinder base sleeve provided according to (i) is subjected to the air atmosphere according to (ii) for a period in the range of from 100 to 350 h, more preferably in the range of from 200 to 300 h, more preferably in the range of from 230 to 250 h. Further, it is preferred that the air atmosphere according to (ii) has a relative humidity in the range of from 35 to 75%, more preferably in the range of from 40 to 60%. In addition thereto, it is preferred that the cylinder base sleeve provided in (i) is subjected to the air atmosphere according to (ii) at an absolute pressure in the range of from 0.85 to 1.15 bar(abs), more preferably in the range of from 0.9 to 1.1 bar(abs).
According to a second alternative, it is preferred to apply a comparatively low temperature, preferably with a comparatively long period of time, and further preferably with a specific relative humidity.
In particular, it is preferred that the air atmosphere according to (ii) has a temperature in the range of from 35 to 45° C., more preferably in the range of from 38 to 42° C. Further, it is preferred that the cylinder base sleeve provided according to (i) is subjected to the air atmosphere according to (ii) for a period in the range of from 375 to 600 h, more preferably in the range of from 400 to 550 h, more preferably in the range of from 450 to 500 h. Further, it is preferred that the air atmosphere according to (ii) has a relative humidity in the range of from 35 to 75%, more preferably in the range of from 40 to 60%. In addition thereto, it is preferred that the cylinder base sleeve provided in (i) is subjected to the air atmosphere according to (ii) at an absolute pressure in the range of from 0.85 to 1.15 bar(abs), more preferably in the range of from 0.9 to 1.1 bar(abs).
According to the present invention, it is preferred that the process for preparing a cylinder sleeve according to any one of the embodiments disclosed herein comprises subjecting the cylinder base sleeve obtained according to (ii) to reconditioning conditions according to (iii). It is preferred that the reconditioning conditions according to (iii) comprise an air atmosphere and a temperature of the air atmosphere in the range of from 15 to 25° C. Further, it is preferred that the cylinder base sleeve obtained according to (ii) is subjected to reconditioning conditions according to (iii) for a period in the range of from for 6 to 72 h, more preferably in the range of from 12 to 36 h, more preferably in the range of from 20 to 28 h.
As disclosed above with respect to a cylinder sleeve according to the present invention, it is preferred that said cylinder sleeve is particularly suitable for application in a printing process, in particular in a flexographic printing process. Thus, it is preferred that the process further comprises (v) applying a printing plate onto the adhesive layer according to (iv).
Furthermore, the present invention relates to a cylinder sleeve, obtainable or obtained by a process according to any one of the embodiments disclosed herein.
Further, the present invention relates to a cylinder sleeve, obtainable or obtained by a process according to any one of the embodiments disclosed herein, wherein the process comprises (v) applying a printing plate onto the adhesive layer according to (iv).
Further, the present invention relates to a cylinder sleeve, preferably the cylinder sleeve according to any one of the embodiments disclosed herein, for use in a printing process, preferably for use in a flexographic printing process.
Further, the present invention relates to a cylinder sleeve, preferably the cylinder sleeve according to any one of the embodiments disclosed herein, wherein the cylinder sleeve comprises a printing plate, for use in a printing process, preferably for use in a flexographic printing process.
Yet further, the present invention relates to a use of a cylinder sleeve according to any one of the embodiment disclosed herein in a printing process, preferably in a flexographic printing process.
Yet further, the present invention relates to a use of a cylinder sleeve according to any one of the embodiments disclosed herein, wherein the cylinder sleeve comprises a printing plate, in a printing process, preferably in a flexographic printing process.
Yet further, the present invention relates to a printing process, preferably a flexographic printing process, wherein a cylinder sleeve according to any one of the embodiments disclosed herein is employed.
Yet further, the present invention relates to a printing process, preferably a flexographic printing process, wherein a cylinder sleeve according to any one of the embodiments disclosed herein, and comprising a printing plate, is employed.
Yet further, the present invention relates to a use of a process according to any one of the embodiments disclosed herein for preparing a multitude of cylinder sleeves, wherein each cylinder sleeve comprises:
Yet further, the present invention relates to a method for preparing a multitude of cylinder sleeves, wherein each cylinder sleeve of this multitude comprises:
Yet further, the present invention relates to a multitude of cylinder sleeves, obtainable or obtained by the method disclosed above.
Yet further, the present invention relates to a use of the method disclosed above for ensuring a consistently high indicated runout quality of a multitude of cylinder base sleeves.
In the context of the present invention, the term “cylinder” refers to a circular cylinder.
In the context of the present invention, the term “total indicated runout” (TIR) refers to the maximum difference in the lengths of the radius of a cylinder base sleeve along the entire surface of said sleeve during rotation.
In the context of the present invention, the term “repeat length” refers to the circumference of a cylinder sleeve containing the base sleeve as defined in feature (a), the one or more cylindrical layers as defined in feature (b), and a printing plate as defined in feature (c).
The unit bar(abs) refers to an absolute pressure wherein 1 bar equals 105 Pa.
The present invention is further illustrated by the following set of embodiments and combinations of embodiments resulting from the dependencies and back-references as indicated. In particular, it is noted that in each instance where a range of embodiments is mentioned, for example in the context of a term such as “The cylinder sleeve of any one of embodiments 1 to 5”, every embodiment in this range is meant to be explicitly disclosed for the skilled person, i.e., the wording of this term is to be understood by the skilled person as being synonymous to “The cylinder sleeve of any one of embodiments 1, 2, 3, 4 and 5”. Further, it is explicitly noted that the following set of embodiments is not the set of claims determining the extent of protection, but represents a suitably structured part of the description directed to general and preferred aspects of the present invention.
The present invention is further illustrated by the following Reference Examples, Comparative Examples and Examples.
A cylinder sleeve was cut in pieces to obtain a cylindrical piece having an axial length of 25 cm.
A container having a volume of 10.7 liter was equipped with a carbon dioxide measuring probe connected to a measurement device. The measuring probe (testo CO2 sensor connected to a testo 440 climate measuring gauge) allowed to detect the temperature of the air atmosphere, the absolute pressure, the relative humidity and the CO2 release of the above-mentioned cylindrical piece within the container. A high bleeched cellulose tissue (ZW-hochgebleicht; Papierfabrik Sundern GmbH, Germany) having a size of 20 cm×20 cm and a weight of about 0.8 g was soaked with 0.35±0.02 g of water and put into the container. A sample cylindrical piece was put into the container. The container was then closed and heated in a pre-heated oven to a temperature of 50° C. for evaporating the water. The water was evaporated within 1.5 h to provide a relative humidity in the container in the range of from 25 to 60%.
For determining carbon dioxide release of the cylindrical piece in the container, the container was airtight sealed and then placed in an oven for keeping the temperature of the gas atmosphere in the container at 50° C. over a measuring period of 24 h. The conditions in the container comprised a gas atmosphere having a temperature of 50° C., a relative humidity in the range of from 25 to 60% and a pressure of 1 bar(abs).
Based on the measurement results, the carbon dioxide release coefficient RCO2 for the sample cylinder sleeve was calculated in ppmv cm−3 d−1.
For the determination of blister/bubble formation, a sample cylinder sleeve was checked every 24 h. Especially when looked against the backlight, blister/bubble formation can be determined.
Various cylinder sleeves were subjected to the treatment stage according to step (ii) of the present invention in a climate chamber; specific cylinder sleeves are listed in Table 1 below. According to a first alternative, a given cylinder sleeve was stored for 120 h in a climate chamber in an air atmosphere having a relative humidity of 50% and a temperature of 40° C.; subsequently, the sleeve was subjected to a higher temperature of 50° C. which was maintained for 48 h. According to a second alternative, a given cylinder sleeve was stored for 96 h in a climate chamber in an air atmosphere having a relative humidity of 50% and a temperature of 50° C.
In Table 1 hereinunder, these cylinder sleeves are described in detail. In Table 2, in columns 1 and 2, these cylinder sleeves are referred to again. In columns 3 to 5 of Table 2, the treatment conditions according to step (ii) of the present invention are described. In columns 6 and 7 of Table 2, the reconditioning conditions are given. In the last column of Table 2, the respective carbon dioxide release coefficients are listed.
1) n.d.: not determined
1) After 15 h and 20 min a RCO2 value of 6.47 ppmv cm−3 d−1 was determined. Based on a linear extrapolation, said value corresponds to a RCO2 value of 10 ppmv cm−3 d−1 after 24 h.
For comparative purposes, an adhesive layer and a foam tape with a thickness of 1.5 mm, were applied on thick-walled cylinder base sleeves #5 and #6, and medium walled cylinder base sleeves #7 and #8, each containing several layers of polyurethane, according to Table 1 above, wherein these base sleeves were not subjected to the step (ii) according to the invention. Further, the same type of adhesive layer and foam tape were applied on cylinder base sleeves #5 and #6, and medium walled cylinder base sleeves #7 and #8 which had been subjected to step (ii) according to the present invention, in particular to a temperature of 50° C. for 14 d at a relative humidity of 50%. The respectively obtained cylinder sleeves were then stored in a climate chamber in an air atmosphere having a relative humidity of 50% and a temperature of 40° C. for a duration as indicated in Table 3; during the storage, the cylinder sleeve were checked on a daily basis, as described in Reference Example 2, with respect to the formation of bubbles under the adhesive layer. Subsequently, the sleeves were optionally subjected to a higher temperature of 50° C. which was maintained for 48 h or 96 h as indicated for medium walled cylinder base sleeve #8. The cylinder sleeves were checked again with respect to the formation of bubbles, again as described in Reference Example 2. The results are described in Table 3 below.
As can be seen in the above, it was found that a cylinder sleeve, after being subjected to the inventive treatment exhibits a significantly reduced CO2 release. Further, it can be seen that a cylinder sleeve which was subjected to the specific inventive treatment does not show blister formation.
While exemplary embodiments and examples have been set forth for illustrative purposes, the foregoing description is not intended in any way to limit the scope of the disclosure and the appended claims. Accordingly, variations can be made to the embodiments and examples above without departing from the principles of the disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 21188763 | Jul 2021 | EP | regional |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20060137551 | Piolat | Jun 2006 | A1 |
| 20100098934 | Stearns | Apr 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 2292441 | Mar 2011 | EP |
| Entry |
|---|
| European Patent Office, Extended European Search Report, dated Dec. 16, 2022, 4 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20230052373 A1 | Feb 2023 | US |