Damage tolerant composites containing infusible particles

BACKGROUND OF THE INVENTION
This invention relates to damage tolerant structural composites comprising high strength filaments in a crosslinked epoxy resin matrix. This invention, more particularly, relates to improvements in the crosslinked epoxy resin matrix (and methods of achieving such improvements) which provide the structural composites with high post impact compressive strength while maintaining such other desirable attributes of epoxy composites as good high temperature performance and processing characteristics.
Prior Art
Composites comprising high strength filaments in a resin matrix are well known materials; they are being proposed for use in more and more weight sensitive applications such as aircraft structural components. Recently, there has been keen interest in increasing the "damage tolerance" of these composites. A criteria used for quantifying the "damage tolerance" is the measured compressive strength exhibited by the composite, layed-up in certain fashion, after it has received an impact typically in the range of 1,500 inch-pounds per inch thickness of the composite, such criteria referred to herein as post impact compression or post impact compressive strength (both abbreviated as PIC).
Thermoplastics have been proposed as matrix materials to increase damage tolerance of composites. Thermoplastics are extremely tough materials when they are free of fiber or other solid additives, i.e. as neat resins. Thermoplastics, however, require high processing temperatures in providing prepregs (comprised filaments and the resin) and forming the prepregs into composites.
Epoxy resins, on the other hand, are thermosetting resins and may be processed into prepregs at low temperatures. In addition, composites made using epoxy resins traditionally have exhibited good high temperature properties. However, the damage tolerance of composites having a crosslinked epoxy resin matrix has been generally much less than that of the better thermoplastic materials.
One approach proposed for increasing the damage tolerance of composites made from epoxy resins has focused on increasing the toughness of the cured epoxy resin used as the matrix material in the composites. Inclusion of polysulfones to lower cross-link density have been suggested for this purpose. (See, for example U.S. Pat. Nos. 4,608,404; 4,663,401; 4,656,206 and 4,656,207). Another recent effort along these lines is illustrated by the Diamant and Moultan paper entitled "Development of Resins For Damage Tolerant Composites--A Systematic Approach", Pages 422-436, 29th National Sampe Symposium, Apr. 3-5, 1984. Certain rubber polymers are shown in this paper to enhance toughness of cured epoxy resins. The rubber polymer in the cured epoxy resins discussed by Diamant and Moultan is said to be dispersed in particles 0.5-1 microns in size, independent of the molecular weight of the polymer. Included among the rubber polymers examined by Diamant and Moultan for use in epoxy composites are butadiene acrylonitrile rubbers having carboxy functionality, e.g. Hycar 1472.
Use of rubber polymers in epoxy resin composites is also shown in the following U.S. Pat. Nos. 3,837,904; 3,926,903 and 3,926,904. The use of polysulfone resins in combination with rubber polymers has been disclosed in the following U.S. Pat. Nos. 4,187,347; 4,195,113; 4,220,686; 4,222,918 and 4,264,655.
Still another approach in making damage tolerant composites is described in U.S. Pat. No. 4,539,253. The approach in this patent is to make a "discrete, integral resin interleaf layer" of an epoxy resin comprising a "rubbery vinyl addition polymer." The interleaf layer is supported by a fibrous mat or carrier and is introduced between layers (plies) of high strength filament that comprise a different epoxy resin.
Although progress has been achieved in increasing the damage tolerance of epoxy resin composites made using conventional processing temperatures and techniques, damage tolerant composites with good high temperature performance damage and processing characteristics have not been heretofore available.
OBJECTS OF THE INVENTION
It is an object of this invention to provide improvements in the damage tolerance of composites comprising high strength filaments in a crosslinked epoxy resin matrix, such composites also having good high temperature performance and processing characteristics.
It is an object of this invention to provide a prepreg comprising high strength filaments and a crosslinkable epoxy resin composition wherein the prepreg cures into a damage tolerant composite.
It is an object of this invention to provide an epoxy resin composition which may be used in making damage tolerant composites.
It is an object of this invention to provide a method of manufacturing epoxy resin compositions which may be used in making damage tolerant composites.
These and other objects have been accomplished in practice of this invention which is described in the following disclosure.
SUMMARY OF THE INVENTION
This invention relates to the discovery that composites comprising high strength filaments and a tough, phase separated, crosslinked epoxy resin matrix are made exceptionally damage tolerant when infusible particles comprising a rubber polymer and having a median particle size in excess of ten microns are incorporated as part of the epoxy resin composition used in forming the composite.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
The epoxy resin compositions used in making the damage tolerant composites comprise a polyepoxide component, a reactive aromatic oligomer component, a curing agent and a polymer component that becomes incorporated in the infusible particles preferaoly during manufacture of the resin. The epoxy resin composition may be in the form of a film for impregnating bands of high strength filaments, a mass of material that can be rendered molten by heat and spread on bands of high strength filaments or a dissolution product that can impregnate high strength filaments in dipping operations. The epoxy resin compositions, when cured in neat form, have a K.sub.IC (critical stress intensity factor) greater than 1 MPa.sqroot.m.
The polyepoxide component comprises an epoxide compound having a glass transition temperature preferably between -100.degree. and 20.degree. C. and can assist in providing tack to the prepregs made with the resin composition. The polyepoxide component contains on average more than one epoxide group per molecule and preferably at least 2 epoxide groups per molecule. The term epoxide group as used herein refers to the simplest epoxide group which is the three-membered ring, ##STR1## The terms of .alpha.-epoxy (or epoxide), 1,2-epoxy (or epoxide), vicinal epoxy (or epoxide) and oxirane group are also art recognized terms for this epoxide group.
Polyepoxide compounds having between 2 and about 4 epoxide groups per molecule and a glass transition temperature below 5.degree. C. are particularly preferred. Suitable aromatic polyepoxide compounds are resorcinol diglycidyl ether (or 1,3-bis-(2,3-epoxypropoxy)benzene) marketed, for example, by Wilmington Chemical as HELOXY.RTM. 69; diglycidyl ether of bisphenol A (or 2,2-bis[p-(2,3-epoxypropoxy)phenyl]propane); triglycidyl p-aminophenol (or 4-(2,3-epoxypropoxy)-N,N-bis(2,3-epoxypropyl)aniline); diglycidyl ether of bromobisphenol A (or 2,2-bis[4-(2,3-epoxypropoxy)3-bromophenyl]propane; diglycidylether of bisphenol F (or 2,2-bis[p-(2,3-epoxypropoxy)phenyl]methane); triglycidyl ether of meta-aminophenol (or 3-(2,3-epoxypropoxy) N,N-bis(2,3-epoxypropyl)aniline); tetraglycidyl methylene dianiline (or N,N,N',N'-tetra(2,3-epoxypropyl) 4,4'diaminodiphenyl methane), polyglycidyl ethers of phenol-formaldehyde novalcs (e.g. DEN 431,438 of Dow Chemical Company); and polyglycidyl ether of orthocresol-novalac (available from Ciba Geigy or, for example, ECN 1235 or 1273). Combinations of two or more polyepoxide compounds can be used as the polyepoxide component. Preferred combinations include mixtures of diepoxides comprising diglycidyl ether of bisphenol F, resorcinol diglycidyl ether and the triglycidylaminophenols or tetraglycidyl methylene dianiline, and mixtures of the triglycidylaminophenols and the diglycidyl ether of butanediol (or 1,4-bis[2,3-epoxypropoxy]butane) or the diglycidyl ethers of polypropylene glycol, particularly tri- or tetra-(.alpha.-propylene glycol) di-(2,3-epoxypropyl) ether. Particularly preferred are polyepoxide components which comprise aromatic polyepoxide compounds and up to about 50% of one or more aromatic or aliphatic diepoxide compounds, and which have glass transition temperatures between about -100.degree. C. and about 20.degree. C.
The reactive aromatic oligomer contains functional groups which are reactive with the polyepoxide component and/or the amine hardener of the composition. In one preferred embodiment the oligomer is epoxy-reactive (i.e. reacts with epoxide groups) and has at least 1.4 epoxy-reactive groups per molecule. In another embodiment the oligomer is epoxy-functional, i.e. it contains epoxide groups. The reactive aromatic oligomer perferably contains divalent aromatic groups such as phenylene, diphenylene or naphthalene groups linked by the same or different divalent non-aromatic linking groups. Exemplary linking groups are oxy(--O--); sulfonyl(--SO.sub.2 --); divalent sulfur (--S--); oxyalkylene or oxyalkyleneoxy(--OR-- or --ORO-- wherein R is lower alkylene preferably with 1-3 carbon atoms); lower alkylene or alkylidene (--R-- or --R(R.sub.1).sub.y wherein R and R.sub.1 are independently lower alkylene and y is 1 or 2); ester groups such as --(R.sub.1).sub.x COO)R.sub.2).sub.y -- wherein R.sub.1 and R.sub.2 are independently lower alkylene preferably with 1 to 3 carbons and x and y are independently zero or 1; and oxaalkylene, i.e. ##STR2## where R.sub.1 and R.sub.2 are independently lower alkylene or a valence bond. The aromatic units can be substituted with non-interfering substituents such as chlorine, lower alkyl, phenyl etc. Generally, at least twenty-five percent of the total number of carbon atoms in the reactive aromatic oligomer will be in aromatic structures, and preferably at least about 50% of the total carbon atoms are in aromatic structures.
The preferred reactive aromatic oligomers are preferably polyethers, polysulfones, polyethersulfones, polyethersulfonepolythioethersulfones and more preferably contain sulfone bridged diphenylene units or ketone bridged diphenylene units. Other types of units which can be present in these preferred oligomers are aromatic or cycloaliphatic units that are not bridged (e.g., naphthalene) or are bridged by groups which are essentially nonpolar, examples of which are alkylidene such as isopropylidene bridges. Particularly preferred reactive oligomers contain sulfone bridge diphenylene units and bisphenol units, a portion of the latter units optionally being replaced by divalent sulfur (--S--) to provide a reactive oligomer of the formula:
NH.sub.2 R"--O--(R--R').sub.m --(R--S).sub.n --R--O--R"NH.sub.2 I
wherein R" is 3,4-phenylene or 4,4'phenylene; R is the residuum of a dihalodiphenylsulfone such as 4,4'dichlorodiphenylsulfone or a dihalogendiphenyl ketone, R' is the residuum of a dihydroxy or dithiol aromatic compound such as bisphenol A, dihydroxy benzene biphenol and quinoline, O is divalent oxygen, S is divalent sulfur and m plus n averages between 8 and 25 and m is preferably at least 2.
The reactive aromatic oligomers preferably have reactive groups that are terminal groups on the oligomer backbone and more preferably are reactive groups at the ends of oligomeric backbones which have little or no branching. The preferred reactive groups of the reactive aromatic oligomer are primary amine(--NH.sub.2), hydroxyl(--OH), carboxyl(--COOA where A is hydrogen or an alkali metal), anhydride, thiol, secondary amine and epoxide groups. Especially preferred are reactive aromatic oligomers having at least about 1.7 reactive groups per molecule and having at least about 70% of the total number of reactive groups present as primary amine, secondary amine, hydroxyl and/or epoxide groups.
The preferred reactive aromatic oligomers are made, for example, by reacting a molar excess of a sulfone such as dichlorodiphenylsulfone with a dihydroxy aromatic compound or compounds such as bisphenol A or 2,7 naphthalenediol so as to yield a chloro-terminated oligomer and then reacting this chloro-terminated oligomer with an alkali metal salt of a hydroxy amine compound such as para or meta aminophenol to provide the reactive groups on the ends of the oligomer. Suitable sulfones for this procedure are meta, and para dichlorodiphenylsulfones. Among the suitable dihydroxy aromatic compounds for use in this procedure are bisphenol A, bisphenol F, naphthalenediols and biphenyl diols. More detailed procedural steps appear in U.S. Ser. No. 823,912 filed Jan. 30, 1986, now abandoned, which is herein incorporated by reference. Other procedures for producing oligomers having reactive end groups are disclosed in U.S. Pat. No. 3,895,064 to Brode and Kawakami and U.S. Pat. No. 3,563,951 to Radlman and Nischk, the latter patent using a procedure which involves forming nitro terminated oligomers and then reducing the nitro groups to amines.
An advantageous route for making the preferred amine terminated aromatic oligomers comprises: (a) dehydrating a dihydroxy aromatic compound or a combination of dihydroxy compounds with an amount of alkali metal hydroxide that provides slightly less than one equivalent of alkali metal for eacn equivalent of hyoroxyl in the dihydroxy compound or combination thereof, the dehydration being in the presence of an organic liquid and an alkali metal carbonate in an amount which is at least equivalent to the hydroxyl excess; (b) reacting a molar excess of dihalogen diphenylsulfone bearing about two replacable halogens per molecule with the dehydrated product of (a) in the presence of an organic solvent and an alkali metal carbonate; (c) dehydrating a phenol bearing epoxy-reactive functionality such as p-aminophenol, m-aminophenol or combinations thereof with alkali metal hydroxide in an amount that provides slightly less than one alkali metal equivalent for each hydroxy equivalent in the aminophenol; and (d) reacting the dehydrated products of (c) with the condensed product of (b). Amine terminated polysulfone oligomers made in this manner have at least about 70% of the end groups amine terminated and contain little or no organic chlorine substituents. Epoxide terminated aromatic oligomers can be prepared by the same route by reacting the condensed product of (d) with an amount of a polyepoxide compound sufficient to provide at least one epoxide per equivalent of active hydrogen of (b) or (d). Preferably an excess of epoxide groups will be present and more preferably the epoxide:hydrogen equivalence ratio will be between about 5:1 and about 30:1. Generally the temperature of the reaction mixture will be maintained at about 50.degree. C. or above to ensure reaction in a reasonable period of time. The preferred temperature range is about 80.degree. to 150.degree. C. Epoxide terminated polysulfone oligomers made in this manner can contain up to 12 epoxide groups depending upon the epoxide functionality of the polyepoxide compound.
The glass transition temperature of the reactive aromatic oligomer preferably ranges between 150.degree. and 230.degree. C. A more preferred range is between 160.degree. and 190.degree. C. The molecular weight (number average) of the reactive aromatic oligomer preferably ranges between 2500 and 5000. Preferably, the reactive aromatic oligomer has a polydispersity (M.sub.w /M.sub.n) of between about 2.0 and 4.0 where M.sub.n is number average molecular weight and M.sub.w is weight average molecular weight.
The curing agent of the preferred epoxy resin compositions is preferably an amine hardener, more preferaoly an aromatic diamine having a molecular weight below 750 and still more preferabiy is a compound of the formula ##STR3## where R.sub.1, R.sub.2, R.sub.3 and R.sub.4 are independently hydrogen, halogen or an alkyl or alkoxy group with 1 to 12 carbon atoms and X is O, S, SO.sub.2, alkylene, alkylidene, and oxoalkylene and m is 0 or 1, a phenylene diamine or a heterocyclic diamine. A particularly preferred aromatic diamine is 3,3'diaminodiphenylsulfone. Other aromatic diamines include a diaminodiphenyl sulfide; a methylenedianiline such as 4,4'-methylene-dianiline; a diaminodiphenylether; a diaminobenzophenone; benzidine; 4,4'thiodianiline; 4-methoxy-6-m-phenylenediamine; 2,6-diaminopyridine; 2,4-toluenediamine; and dianisidine. Still other aromatic diamines such as the di(aminophenoxy)diphenyl ethers or sulfones can be employed if desired. Alicylic amines such as menthane diamine may also be employed. In some cases aliphatic amines such as secondary alkylamines which are normally fast reacting hardeners can be used alone or in combination with other amine hardeners provided the concentration and/or curing temperature are sufficiently low to permit control of the curing rate. Other fast reacting hardeners which can be employed for making the epoxy resins of the invention are dicyandiamide, boron trifluoride/amine complexes and the like.
The hardener is present in the composition in an amount sufficient to crosslink or cure the composition and preferably is present in an amount which provides (together with the reactive aromatic oligomer) from 0.6 to 1.5 equivalents and more preferably from 0.8 to 1.2 equivalents of active hydrogen atoms per one equivalent of epoxide groups in the composition.
The epoxy resin compositions hereof also contain a rubber polymer. The rubber polymer is insoluble in the polyepoxide compounds used in making the epoxy resin compositions. An amount of this polymer is contained in infusible particles that are dispersed throughout the epoxy resin composition. The rubber polymer preferably is crosslinkable having functionality such as carboxyl groups. Carboxy functional butadiene acrylonitrile polymers are preferred. An example of this latter polymer is Hycar 1472 marketed by B. F. Goodrich. A description of carboxy functional rubber polymers appears in the article "Crosslinking Reactions of Carboxylic Elastomers" by Harold P. Brown in Rubber Chemistry and Technology 36(4), 931-62 (1963). A catalyst is preferably employed with carboxy or other functional polymer. An example of such a catalyst is an aryl phosphonium halide catalyst such as ethyltriphenylphosphonium iodide available from Morton-Thiokol.
The infusible particles have a median particle size (i.e. half are bigger and half are smaller) ranging between 10 and 75 microns. The particles may be evenly distributed in the epoxy resin composition but are segregated according to size during prepreg manufacture, discussed below. As an alternative the particles may be dispensed directly on the prepreg during its manufacture.
The infusibie particles may take a variety of shapes including cylindrical, mostly round and spherical. The particles are infusible insofar as they resist deformation and agglomeration during manufacture of the epoxy resin composition and prepregs thereof. The infusible particles also have a lower modulus than the remainder of the crosslinked epoxy resin matrix.
A preferred route in making epoxy resin compositions of this invention which contain the particles involves forming the infusible particles in situ. By "in situ" is meant forming the particles during manufacture of the epoxy resin composition. The particles formed in this manner are stable and resist deformation, agglomeration and solubilization during manufacture of the epoxy resin composition.
Manufacture of the epoxy resin compositions using the preferred in situ process comprises admixing a portion e.g., between 40 and 60% by weight of the polyepoxide component, together with the reactive oligomer component at elevated temperature, e.g., between 30.degree. and 90.degree. C., to dissolve the oligomer component in the epoxy compounds. A crosslinkable rubber polymer preferably in the form of a solution which has between about 10 and 20% of the polymer and between 90 and 80% of low boiling solvent is added. The solvent is then distilled under vacuum to provide a resin premix having less than 5% by weight solvent, more preferably 3% or less solvent. Then the catalyst and other ingredients such as antioxidant are added. Mixing continues at this temperature permitting continued reaction of the crosslinkable rubber polymer in completing the formation of the infusible particles. Alternatively, a crosslinkable rubber polymer may be dissolved in a portion of the polyepoxide component using a low-boiling solvent, the solvent driven off, and the polyepoxide compound(s) containing the dissolved rubber polymer added at elevated temperature to a mixture of the amine terminated polyarylene polyether sulfone and another portion of the polyepoxide component. The catalyst is added permitting an accelerated completion of the reaction forming the infusible particles, as desired.
In still another procedure, the polyepoxide component and the oligomer component are mixed in a sealed mixer and then the rubber polymer, dissolved in solvent, is added together with or followed by addition of the catalyst and antioxidant as desired. The sealed mixer is maintained at elevated temperature causing the infusible particles of appropriate size to form. The resulting epoxy resin composition may be used to form prepregs using a bath that is agitated to keep the infusible particles dispersed during impregnation of fiber passing through the bath.
The curing agent of the epoxy resin composition is preferably added after formation of the infusible particles. Dispersion of the curing agent in the intermediate epoxy resin composition may be accomplished without deformation of the infusible particles.
Table A below provides the general and preferred ranges, as parts by weight, for the polyepoxide polymer component, reactive aromatic oligomer, hardener and organic polymer present in the thermosetting epoxy resin compositions of this invention:
TABLE A______________________________________ General More Preferred______________________________________Polyepoxide Component 100 100Reactive Oligomer 10 to 200 20 to 60Hardener (curing agent) 15 to 100 20 to 60Organic Polymer.sup.(a) 1 to 15.sup.(b) 4 to 12.sup.(b)______________________________________ .sup.(a) E.g. carboxy functional rubber polymer. .sup.(b) By weight, per hundred parts of the epoxy resin composition.
Other ingredients such as catalyst, antioxidant, processing aids and the like are included in the epoxy resin compositions in minor amounts.
The preferred cured, i.e., crosslinked resins produced from the compositions of this invention have a multiphase morphology comprising glassy phases and a phase i.e. the infusible particle phase, that is more elastic than the glassy phases. The domains of the dispersed discontinuous glassy phase preferably are between aoout 0.05 and 10 microns and more preferably between 0.1 and 5 microns in largest dimension. The domains are generally spherical or ellipsoidal in shape but may take other shapes particularly around the filaments in the matrix. The particles containing rubber polymer are dispersed in the glassy phases and have a size and distribution as previously discussed. The particles containing the rubber polymer are more elastic than the remainder of the crosslinked epoxy resin matrix comprising tne glassy phases.
The volume of the discontinuous glassy phases preferably constitutes at least about 15%, more usually between 30% and 65% of the total volume of the cured resin. The total volume of the cured resin (Vr) is defined as the volume of the continuous phase(s) (Vc) and the volume of the discontinuous phase(s) (Vd) combined. In determining the volume of the discontinuous phase(s), a micrograph of a microtomed section of the cured resin or composite is made and the area (or an area fraction) of the micrograph occupied by the continuous phase(s) (Ac), discontinuous phase(s) (Ad) and filament or fiber (Af) may be determined visually or instrumentally, using commercial devices such as a digitizer or image analyzer. In certain composites of this invention, the disperse phase may be continuous in certain portions of the composite and vice-versa. The amine functional polyarylene polyether sulfone may exist in either of the glassy phases and has been shown in certain instances as residing as well in the infusible particles comprising a crosslinkable rubber.
The prepregs of this invention are made by combining the epoxy resin compositions and high strength filaments using conventional techniques. For example, the epoxy resin composition can be made into a film on a sheet of release paper in a film process. Film carried by upper and lower release papers are pressed into bands or sheets of high strength filaments in making prepreg by this process. Alternatively, a "hot bead" process may be used wherein the epoxy resin composition is rendered molten and pressed into the bands or sheets of high strength filaments. Still another route is by dispersing the epoxy resin composition in solvent, passing the high strength filaments through a bath containing the solvent and then driving off the solvent to provide the prepreg. In this latter technique, the bath is advantageously agitated to keep the infusible particles dispersed therein.
In all of the aforementioned techniques of making prepreg, the large infusible particles are trapped by the filament tows or bundles thereby providing in a prepreg that has these particles on its surface rather than between filaments in the bundle or tows of filaments. The prepregs may be simply layed on one another in making the damage tolerant components of this invention.

BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 shows a photomicrograph of a damage tolerant composite of the invention. The carbon fiber appears as white streaks (0.degree. , i.e. parallel to the horizontal axis of the micrograph), white ovals (+/-45.degree., i.e. diagonal to the horizontal axis of the micrograph) and white circles (90.degree., i.e. perpendicular to the plane of the micrograph). The crosslinked epoxy resin matrix appears grayish in the micrograph with the particles comprising rubber polymer generally being circular black dots. The damage tolerant composite exhibited a 52.2 Ksi (thousand of pounds per square inch) post impact compressive strength (PIC) at an impact of 1500 inch pounds per inch thickness using the lay-up described in the Examples. (All PIC values of the composites in the drawings were determined at 1500 inch pounds per inch thickness using the procedures of the Examples.)
FIG. 2 shows other micrographs of the damage tolerant composite like that of FIG. 1 [FIGS. 2(a) and 2(b)] together with a crosslinked epoxy resin cured without fiber [FIGS. 2(c) and 2(d)]. The crosslinked epoxy resin of FIGS. 2(c) and 2(d) is made with the same formulation of the composite of FIGS. 1, 2(a) and 2(b). The cured resin of FIGS. 2(a), (b) and (c) has been washed with methylene chloride (CH.sub.2 Cl.sub.2) to improve phase contrast.
FIGS. 3, 4 and 5 respectively show photomicrographs of three damage tolerant composites. The composites were made using the same nominal formulation. The composite of FIGS. 3(a), (b) and (c) had a post impact compressive strength (PIC) of 48.5. The composite of FIG. 4 three separate photomicrographs, views (a), (b) and (c) of FIG. 4 had a post impact compressive (PIC) strength of 43.5. The PIC strength composites of FIG. 5 (shown in three separate photomicrographs, views (a), (b), and (c) of FIG. 5) was 38.3.
FIG. 6 (shown in two separate photomicrographs, views (a) and (b) of FIG. 6) shows a photomicrograph of a cured epoxy resin wherein the formulation includes an oligomer which is different from those of FIGS. 1-5.

This invention has particular applicability to damage tolerant composites which are made from materials commonly referred to as "prepregs." Prepregs comprise resin and high strength filaments which are in the form of filamentary bundles (often called "rovings" or "tows") comprising a multitude of the filaments. Each tow of carbon fiber, for example, typically bundles between about 500 and 20,000 filaments. A plurality of filamentary bundles are aligned or woven together in making a prepreg in sheet form, a preferred form according to this invention. Alternately, the prepreg may be in the form of a single bundle of filaments impregnated with resin. This later prepreg form finds use in processes such as filament winding and pultrusion.
The preferred high strength filaments are carbon fiber filaments made, for example, by carbonizing polyacrylonitrile, rayon or pitch. (Carbon fiber is also called "graphite fiber" by some and the terms "carbon fiber" and "graphite fiber" are interchangeable as used herein.) Examples of preferred high strength filaments are AS-4, IM-6 and IM-7 carbon fiber marketed by Hercules Incorporated. Other high strength filaments preferably having a diameter between 3 and 9 microns can also be employed.
The prepregs hereof comprise epoxy resin composition that permit the prepreg to cure into damage tolerant composites. The epoxy resin compositions when cured without any high strength filaments have a K.sub.IC of greater than 1 MPa.sqroot.m. This high degree of toughness, coupled with the action of the infusible particles provides composites that include the infusible particles and high strength filaments with post impact compression values in excess of 45,000 psi at 1,500 inch pounds per inch thickness of the composite.
FIGS. 1-5 are copies of photomicrographs of sections taken of damage tolerant composites of this invention. As can be seen in viewing these Figures, the distribution of infusible particles (black or darker dots) is such that the larger particles generally reside between the fiber plies whereas the smaller particles tend to be trapped between filaments within the plies. A comparison of the photomicrographs of FIGS. 5 (a composite having a measured post impact compression strength (PIC) of 38) with the photomicrographs of FIGS. 1 and 2(a) and (b) (composites having a measured post impact compressive strength of 52.2 and 54 respectively) shows a relationship between the size of infusible particles in the matrix and high PIC values of the damage tolerant composites.
The damage tolerant composites of FIGS. 1-5 are made using epoxy resin compositions all having the same nominal formulation. The composites having the higher post impact compression values are made from epoxy resin compositions having infusible particles with a higher median particle size; and such larger particles can be seen as generally residing in that portion of the crosslinked epoxy resin matrix between the plies of filaments.
The epoxy resin compositions used in making the composites illustrated in FIGS. 1-5 comprise infusible particles of similar size and shape as appear in FIGS. 1-5. Compare, for example, the infusible particles in the neat resin of FIGS. 2(c) and 2(d) with the infusible particles of the damage tolerant composites in FIGS. 2(a) and 2(b). A number of these particles, preferably more than half, have a dimension that is greater than 10 microns. Composites with highest damage tolerability as measured in post impact compression tests generally comprise infusible particles having a mean dimension at least about 15 microns. More preferably, the median particle size of the infusible particles is between about 25 and 75 microns.
The following Examples illustrate practice of this invention and are not intended as a limitation thereof. All parts and percentages in the Examples are parts and percentages by weight and all temperatures are in degrees centigrade unless otherwise noted.
EXAMPLE 1
The formulation in Table 1 set forth below was used in preparing prepreg made of an epoxy resin composition and tows of carbon fibers using procedures described hereinafter.
TABLE 1______________________________________Ingredient Parts by Weight______________________________________Digylcidyl Ether of Bisphenol-F.sup.1 13.12Triglycidyl p-amino phenol.sup.2 13.12Amine functional polyarylene 13.65polyether sulfone.sup.33,3'-Bis(aminophenyl)sulfone.sup.4 12.86Carboxy-functional butadiene acrylonitrile 2.09polymer.sup.5Ethyltriphenylphosphonium iodide.sup.6 0.0368Polymerized 1,2-dihydro-2,2,4-trimethyl 0.1052quinoline.sup.7______________________________________ .sup.1 Epicion 830, a product of Dainippon Ink and Chemicals, Inc. having an epoxy equivalent of about 180, viscosity of about 3000 cps (at 25.degree. C.) and specific gravity of about 1.18 (at 25.degree. C.). .sup.2 MY 0510, a product of Ciba Geigy, said to be a reaction product of three molar parts of epichlorohydrin and one molar part of paminophenol, and have an epoxy equivalent of about 99. .sup.3 A product made by reacting a molar excess of dichlorodiphenylsulfone with the potassium double salt of BisphenolA followed by reaction with the potassium salt of aminophenol. Product has molecular weight (number average) between about 3500 and 5500 and between about 85-95% of the end groups are amine groups with the remainder of the end groups comprising hydroxyl groups. Procedures for making this polyether sulfone are described in detail in the examples of USSN 823,912 filed on January 30, 1986 in the name of Jabloner and Nguyen which are hereby incorporated herein by reference. .sup.4 Air milled from Sumitomo Chemical, Alva Chemical or Aceto Chemical companies. .sup.5 Hycar 1472, a product of B. F. Goodrich, said to be nitrile rubber made from butadiene and acrylonitrile, in the form of a rubber crumb. .sup.6 Catalyst sold by MortonThiokol. .sup.7 Agerite Resin D sold by R. T. Vanderbilt, antioxidant.
PART A--PREPARATION OF EPOXY RESIN COMPOSITION
Composition
1. Formation of Rubber Solution
The carboxy-functional butadiene acrylonitrile polymer in the form of a crumb is added to methylethylketone at a weight ratio of 15 parts crumb to eighty five parts methylethylketone. The mixture is stirred to form a homogeneous solution which is called "Rubber Solution" in this Example.
2. Formation of Epoxy Resin Composition
A Meyer's vacuum mixer having a five gallon capacity is used in the preparation of the epoxy resin composition. The mixer is equipped with a thermometer and fast and slow mixing blades; it is heated by oil circulation and can be evacuated by a vacuum pump using a solvent trap.
The vacuum mixer is cleaned with solvent and then first set to have a temperature between 60.degree. C. and 100.degree. C. to drive off the cleaning solvent. The triglycidyl p-aminophenol epoxy resin (13.12 parts) and diglycidyl ether of Bisphenol F epoxy resin (2.62 parts) are added together and mixed in the vacuum mixer while heated to about 60.degree. C. To these preheated, mixed epoxy resins is added the amine functional polyarylene polyether sulfone (13.65 parts) in particulate form. Methylethylketone (6.658 parts) is used to wash the polysulfone ether powder from the sides of the mixer during the mixing operation. The lid on the mixer is then closed and the temperature of the mixture increased to about 60.degree. C. The high speed mixer blades are set at about 1400 RPM. After the temperature of about 60.degree. C. is reached and the amine functional polyarylene polyether sulfone is dissolved, the mixer is opened and the Rubber Solution (13.91 parts) added. The mixer is closed and the temperature set for about 120.degree. C. The mixer blades are set at low speed and mixing continued until the reflux temperature (80.degree.) is reached. The vacuum pump is then started. The vacuum in the mixer is maintained at a level no higher than 13-15 centimeters Hg up to a temperature of 85.degree. C. (Should the resin foam up, the vacuum is released slowly until foaming decreases to a position below the top of the mixing blades at a pressure of about 13 centimeters Hg.)
Table 2, set forth below, shows the relationship between temperature and maximum vacuum that can be employed in heating the resin mixture:
TABLE 2______________________________________Resin Temperature (.degree.C.) Vacuum (cm)______________________________________Up to 85 13-1585 22.988 30.591 35.5 93.5 45.7102 +/- 3 50.8______________________________________
When the temperature of the resin mixture reaches 102+/-3.degree. C., the vacuum is released and the ethyltriphenyl phosphonium radicle catalyst (0.0368 parts) and polymerized 1,2-dihydro-2,2,4trimethyl quinoline antioxidant (0.1052 parts) are added to the mixer.
With the mixer closed, mixing is continued at low speeds for about 50 minutes at 105.degree./-3.degree. C. After the mixing has continued for 5 minutes, vacuum is applied and maintained at about 51-52 centimeters Hg for 30 minutes. After this 30 minute period, a full vacuum is applied for the remainder of the 50+/-5 minute mixing period. The vacuum is released and the temperature is set for about 70.degree. C. A sample of the resin mixture is then taken through a port in the mixer and the sample heated to drive off the solvent. If the heating reveals that the sample had more than 3% volatiles by weight, the vacuum and heating is again applied to the resin mixture in the vacuum mixer. If there is less than a 3% weight difference between the sample of the resin mixture and its heated (i.e. devolatilized) product, then the remainder of the diglycidyl ether of Bisphenol F (10.5 parts) is added to the vacuum mixer. Mixing is continued while the resin mixture is cooled. When the mixture reaches 98.degree. C., the 3,3'-bis(aminophenol)sulfone (12.86 parts) is added through a port in the mixer. After the powdery 3,3-bis(aminophenol) sulfone is fully dispersed, the mixer is raised and the walls scraped down. The temperature is set to 77.degree. C., the mixer closed with mixing continued at full vacuum for about 15 minutes. The mixer is opened and the contents are poured into small containers which are stored at 0.degree. C. for further processing of the epoxy resin composition thereof into prepreg.
Part B--Preparation of Prepreg Using The Epoxy Resin Composition of Part A
The frozen epoxy resin composition of Part A is slowly brought to a temperature of about 50.degree. C. The warmed epoxy resin composition comprises the uncured epoxy resin composition and distinct particles which contain the butadiene acrylonitrile polymer. The warmed epoxy resin composition containing the infusible particles is spread on a sheet of release paper. The sheet of release paper having the film of the epoxy resin composition is rolled up and stored at about 10.degree. C. or below for further processing.
Tows of carbon fiber (IM-7 carbon fiber.sup.8 available from Hercules Incorporated, Magna, Utah) are formed into a band. Two different bands are prepared. The first band has an areal weight (i.e. weight per unit area) of about 145 grams per square meter and the second band has an areal weight of about 190 grams per square meter. The first band is impregnated with the epoxy resin composition of this Example by passing it between a pair of rollers which press the band and upper and lower filmed epoxy resin composition parts together as they pass between the rollers. The rollers are kept about 75.degree. C. and the resultant prepreg is between about 33 and 37% by weight resin. Similarly, the second band is made into prepreg by pressing the second band of carbon fiber and a further amount of the filmed resin together between rollers kept at a temperature above 75.degree. C. The resultant prepreg made from the 190 gm per square centimeters areal weight carbon fiber is between about 33 and 37% by weight resin.
Approximately 12,000 filaments per tow. Filament physical characteristics include filament diameter 5 microns; round cross section. The modulus of the carbon fiber is about 44 million psi and the tensile strength about 750 thousand psi, these modulus and strength values measured using tow tests.
In an alternate procedure (hot bead) the epoxy resin is heated to about 75.degree. C. and spread on a sheet of release paper. The tows of carbon fiber are then pressed into the molten resin carried on the release paper in making the prepreg. The resultant prepreg has between about 33 and 37% by weight resin.
The prepreg, prepared as above, is made into rolls of prepreg in which the prepreg in each of the rolls is separated by a sheet of release paper.
Part C--Testing
1. Analysis of Infusible Particles
Particles
Twenty five grams of epoxy resin compositions prepared using the procedures of Part A of this Example 1 were placed in a two hundred fifty milliliter beaker and mixed with 100 milliliters of tetrahydrofuran (THF) until the resin composition in which the infusible particles were dispersed was dissolved. The dissolution product was then filtered through pre-weighed Whatman #41 filter paper. The beaker and stir bar were rinsed with the THF until the filter paper was white. The filter paper was allowed to air dry and then placed in an oven at 75.degree. C. The filter paper was cooled to room temperature in a desicator and weighed. This procedure was repeated using different batches of the epoxy resin composition. The particles on the filter paper are found using these procedures to weigh in a range between 2 and 6% by weight of the respective epoxy resin compositions.
2. Determination of Post Impact Compressive Strength and Size of Infusible Rubber Particles
A series of composite test panels are made from prepregs prepared following the foregoing procedures. The prepregs were layed up and cured and the cured composite panel tested to determine the post impact compression test values. The panels tested were 10 centimeters wide and 15 centimeters long. The panels were thirty two plies thick, each ply containing carbon fiber filaments extending in a single direction. The panels were quasi-isotropic according to the following scheme: (+45.degree./90.degree./-45.degree./0.degree.).sub.4s. (The 4S in the lay-up means the lay-up had a total of thirty two (32) plies layed up as follows: a set of four plies was layed at the recited angles four times (i.e. sixteen plies in all) starting each time with a +45.degree. ply followed by laying a set of four plies four times in reverse order (i.e. sixteen plies in all) starting each time with a 0.degree. ply. The lay-up was cured at 177.degree. C. for two hours. The cured panels were impacted with an impact energy of 1,500 inch--lbs/inch thickness while suspended over a 3.times.5 inch opening. The compressive strength of the impacted panels was determined using the test procedure of NASA publication 1092, modified as above. Portions of the impacted panels were examined microscopically for phase separation in the epoxy thermoset matrix. Also, the size of the rubbery particles in sections of the impacted samples were measured and counted. Table 3, below, shows the results of the post impact compression (PIC) test together with the results of the particle size measurements.
As can be seen from Table 3, the size and distribution of the rubber particles have a correlation with the post impact compression (PIC) test results; the larger particle distributions generally give higher post impact compression results. Also as is seen from Table 3, the cured laminates having high PIC values exhibit a "phase separation." By "phase separation" is meant that there exists distinct epoxy phases in addition to the rubbery particulate phase.
TABLE 3__________________________________________________________________________MICROSCOPIC EXAMINATION Crosslinked Infusible Epoxy Matrix RubberPIC Phase Particle Phase Particle SizePanel No. (ksi) Description Description Small (.mu.) Large (.mu.) Mean (.mu.)__________________________________________________________________________39652 43.5 N.P.* Spherical 2.5 15.037009 54 S.P.** Spherical 10 5839668 38.3 N.P. Spherical 1.25 1039669 42.6 N.P. Spherical 1.25 1039558 48.5 S.P. Speherical 4 2539718 39 S.P.**** Irregular 1.25 1039737 41.5 N.P. Irregular 0.6 7.539735 43.4 N.P. Irregular 0.6 7.5 5.639713 41.5 N.P. Roundish*** 1.25 7.539865 45.7 S.P. Spherical 2.5 5539867 51.3 S.P. Spherical 5 3539868 46.8 S.P. Irregular 2.5 2039869 46.7 S.P. Irregular 1.25 2539870 49.4 S.P. Roundish 1.25 1539875 52.1 S.P. Spherical 5 4539876 52.2 S.P. Spherical 10 52.5 24.739877 51.5 S.P. Spherical 7.5 6540034-1 43.0 S.P. Irregular 1.0 55 12.240034-3 52.9 S.P. Irregular 2.5 72.5 17.240023-1 50.5 S.P. Spherical 5.0 77.5 16.540024-1 50.5 S.P. Roundish 2.5 50 20.340028-2 52.5 S.P. Roundish 5.0 45 15.440028-3 42.7 S.P. Roundish 2.5 52.5 14.940029-1 50.4 S.P. Roundish 5.0 35 13.4__________________________________________________________________________ *N.P. means a distinct phase separation not detected. (Not epoxy composites of this invention.) **S.P. means phase separation detected. ***Roundish differs from spherical in that Roundish has a greater number of particles which were not entirely circular but elliptical or oblong like. ****This panel had a different layup than the rest of the panels, it contains only 24 plys.
EXAMPLE 2
Part A
This example describes a laboratory preparation of an epoxy resin composition of this invention which does not require solvent removal after addition of the polyarylene polyether sulfone. An initial step in this preparation was forming a solution of carboxy-functional butadiene acrylonitrile polymer.sup.1 and methylethylketone at 20% by weight of the polymer. Four hundred parts of this solution were mixed with 500 parts of dicylcidyl ether of Bisphenol F.sup.2 at room temperature. The mixture was stripped of methylethylketone until its volatile content was below 2% by weight. Another step in this procedure began with heating 500 parts of triglycidyl aminophenol.sup.3 to 60.degree. C. in a separate vessel. Then, 520 parts of amine functional polyarylene polyether sulfone.sup.4 were added slowly to the triglycidyl aminophenol with mixing and the temperature increased to 107.degree. C. Mixing continued until the polyether sulfone dissolved. Five hundred eighty parts of the mixture of carboxy functional butadiene nitrile polymer and diglycidyl ether of Bisphenol F (less than 2% by weight volatiles) were heated to 100.degree. C. in an oven and added at 110.degree. C. to the solution of triglycidyl aminophenol and polyether sulfone to provide a reaction mixture that is held at about 107.degree. C. for forty-five minutes. Antioxidant.sup.5 (4 parts) and catalyst.sup.6 (1.4 parts) were then added to the reaction mixture. The temperature of the reaction mixture was then cooled to 80.degree. C. and 490 parts of 3,3'diaminodiphenylsulfone.sup.7 added and dispersed into the mixture.
Part B
A prepreg was made from the epoxy resin composition prepared as shown above in Part A. The high strength filaments used in preparing this prepreg were tows of IM-7 carbon fiber.sup.8 of Hercules Incorporated. The prepreg had a fiber volume of 55%. The prepreg was made into panels using the lay-up procedures of Example 1. The panels were tested also using the procedures of Example 1 and determined to have the following compressive strengths at 1500 inch pounds per inch thickness impacts: 50.6 thousand pounds per square inch; 52.9 thousand pounds per square inch and 51.1 thousand pounds per square inch. Also, neat resin samples were examined microscopically and found to have spherical particles compring the butadiene acrylonitrile polymer ranging in size between 2.4 microns and 81.4 microns, which were generally spherical in shape. The median size of the particles was judged to be much greater than 10 microns.
1, 2, 3, 4, 5 , 6, 7 and 8--See Example 1 for source and fuller description.
EXAMPLE 3
This Example illustrates use of epoxy resin compositions in making single tows of carbon fiber impregnated with resin. The carbon fiber used in making the tow-preg was IM-7 carbon fiber available from Hercules Incorporated. Tows of this carbon fiber have approximately 12,000 filaments and no twist. The cross sectional area of the tow is about 0.25 millimeter with each filament having a diameter of 5 microns and a smooth, round cross-section.
An epoxy resin composition prepared according to the procedures of Example is admixed with three levels of methylethylketone as shown in Table 4. The resin solutions were placed in resin coating baths which were agitated during passage of tows of the IM-7 carbon fiber through the bath. The tows were passed through the bath under a roller fixed in the bath and then out of the bath to an "S-bar" apparatus. The tow passed over a first bar and then under a second bar in traveling an S-shaped path. This path permitted wiping both sides of the tow-preg and was judged to give a uniform distribution of the particles of rubber polymer.
A stirring motor was used for take up of the tow-preg. A tow speed of about 4 feet per minutes was used. The pulley was high enough that a four-foot length of wet tow-prep could pull and cut off. This section was dried in air for about 10 minutes at room temperature and then in an oven at 93.degree. C. for five minutes. This crying was determined to reduce volatiles to less than 3% by weight.
Volatiles content was determined by weighing a length of tow, drying it at 350.degree. F. (133.degree. C.) for 15 minutes and reweighing. Resin content was determined by extracting a weighed length of tow with tetrahydrofuran (THF), drying the extracted tow and reweighing. Insoluble rubber content was determined by filtering the THF extract through a weighed filter paper, drying and reweighing the filter paper. Distribution of rubber particles on the tow was determined by visual examination.
The following Table 4 provides information for three preparations of tow-preg prepared and tested as discussed above.
TABLE 4______________________________________ Resin Concen- Volatiles Resin RubberDes. tration Content (S.D.) Content (S.D.) Content______________________________________9493-12-1 50% 3.0% (0.1) 46.3% (1.05) 3.3%9493-12-2 35% 3.1% (0.5) 34.4% (1.12) 3.2%9493-12-3 30% 3.2% (0.6) 32.1% (1.34) 2.8%______________________________________
EXAMPLE 4
Part A--Concentrate Preparation
A concentrate of particles comprising rubber polymer in an epoxy resin admixture is made as follows: Ten parts of diglycidyl ether of Bisphenol F (Epicon 830 from Dainippon Ink and Chemicals) and 10 parts triglycidyl p-aminophenol (CG 0510 from Ciba Geigy) were heated to 70.degree. C. Twenty parts of amine functional polyarylene polyether sulfone were added to the epoxy resins and a slurry was formed. The slurry was heated to 105.degree. C. and held for 40 minutes whereby the amine functional polyarylene polyether sulfone was dissolved. The product was then cooled to about 75.degree. C. and fifteen parts of methyl ethyl ketone added. Then eight parts of carboxy functional butadiene acrylonitrile (Hycar 1472, B. F. Goodrich) rubber was added as a 15% by weight solution in methylethylketone. The mixture was heated to about 107.degree. C. while removing the methlethylketone and held at about 107.degree. C. for fifteen minutes. The resultant epoxy resin concentrate was cooled to room temperature.
Part B--Resin Formulation From Concentrate
An initial step in formulating an epoxy resin composition of this invention from the concentrate of Part A, above, was forming a slurry of the triglycidyl p-aminophenol (40 parts), diglycidylether of Bisphenol F (40 parts) and amine functional polyarylene polyether (32 parts). The slurry was heated to 105.degree. C. and held at that temperature for 40 minutes to dissolve the polyether sulfone and form a resin solution. The concentrate (48 parts) at room temperature was combined with the resin solution held at 105.degree. C. Then this combination was cooled to 70.degree. C. and antioxidant (0.4 parts, Agerite Resin D, polymerized 1,2-dihydro-2,2,4-trimethyl quinoline, from R. T. Vanderbilt), catalyst (0.14 parts ethyltriphenyl phosphonium iodide from Morton-Thiokol and 3,3'-bis(aminophenyl) sulfone (49 parts, available from Example 1) were added and mixing continued for ten minutes to provide the epoxy resin composition.
EXAMPLE 5
In this example, a number of uncured epoxy resin compositions and cured epoxy resin compositions were analyzed relative particle size (Table 5) and viscosity (Table 6). The epoxy resin compositions were made generally according to the procedures of Example 1. The results reported in Table 5 were gathered by making a photomicrograph of the uncured resin composition and then using an image analyzer with a computerized "mouse" to determine particle size from the photomicrograph. The image analyzer was set to establish particle size within 10 micron increments.
TABLE 5______________________________________PARTICLE SIZE ANALYSISUNCURED (NEAT) RESIN 10 Mean Range (mi- 90-100Lot N.sup.1 (microns) (microns) crons).sup.3 (microns).sup.4______________________________________S005A 51 51.7 10-90S005B 66 46.8 10-100 1S005C 55 39.2 10-100 1S005D 55 48.9 10-90S005E 74 47.8 10-90S005F 65 47.2 1-100 2 1S005G 40 67.0 20-100 4S005H 45 41.9 1-100 4 3S005I 29 42.6 1-100 2S005J 47 46.7 1-100 1 2S005K 78 36.0 1-100 4 2S005L 124 33.2 1-100 10 5S005M 99 35.7 10-90S005N 76 38.5 10-705005O 77 38.1 1-80 3S005P 70 34.9 1-100 4 1S005S 97 33.2 1-90 3S005T 88 38.0 10-70S005U 66 36.7 1-90 4S005X 118 28.8 1-90 6S005Q 104 36.4 .sup. N.D..sup.2 N.D. N.D.S005R 74 39.2 N.D. N.D. N.D.S005G 89 44.3 10-100 1S005W 136 29.2 1-80 6S005X 78 37.4 1-80 1S005Y 109 35.2 1-80 5S005Z 175 24.6 1-80 22S005AA 119 34.9 1-100 17 2S005AB 42 58.9 1-100 5 1S005AC 49 47.2 1-100 7 1S005AD 35 63.5 1-80 1S005AE 59 48.6 1-100 9 1S005AF 50 42.5 1-100 10 1S005AG 61 51.3 1-100 7 2S005AJ 63 45.9 N.D. N.D. N.D.S005AI 40 50.6 1-80 1S005AK 75 36.6 1-60 7S005AL 117 31.3 1-70 16S005-S006 102 32.7 1-70 14Average 2997 38.7 171 30 (6.20%) (1.09%)______________________________________ .sup.1 N means number of particles counted. .sup.2 N.D. means not determined. .sup.3 Number in 10 micron range. .sup.4 Number in 90-100 micron range.
Table 6 shows melt flow rhelogy on eleven batches of resin compositions made according to Example 1. Table 7 shows the initial viscosity at 60.degree. C. for these samples, the minimum viscosity, the temperature at which the minimum viscosity occurs, the dynamic gel temperature (DGT) and heating rate. All scans reported in Table 6 were run at similar conditions of 50 mm diameter parallel plates, 0.5 mm gap, 10 radians/second frequency, 50% strain and cure mode. The temperatures at which minimum viscosity and DGT occur are fairly constant while the viscosities are scattered but not out of line with other resin systems. The DGT for the epoxy resin compositions was determined to be about 156.degree. C. when heating at 0.851.degree. C./minute; 176.degree. C. when heating at 1.857.degree. C./minute; 186.degree. C. when heating at 2.897.degree. C./minute and 199.degree. C. when heating at 4.273.degree. C./minute.
TABLE 6______________________________________RESIN VISCOSITY MinimumInitial 60.degree. C. Viscosity Heating n* n* Temp. DGT Rate (poise) (poise) (.degree.C.) (.degree.C.) (.degree.C./min)Resin 4505 21.1 137 174 1.921______________________________________SX005C 3510 15.1 142 175 1.937SX005F 3215 13.3 137 174 1.889SX005G 3605 11.6 144 176 1.729SX005I 4955 33.7 135 175 1.765SX005K 7585 22.8 145 173 1.691SX005M 6965 20.0 143 176 1.857SX005P 4670 10.0 143 176 1.933SX005S 6780 20.0 149 177 2.035SX006A 5565 16.4 143 175 1.828SX006C 6035 22.6 141 174 1.917X(n = 11) 5217 18.8 142 175 1.864 1493 6.6 4 1 0.103Cv (%) 28.62 35.27 2.86 0.68 5.51______________________________________
Table 7 shows the glass transitions of thirteen coupons made from an epoxy resin composition prepared as in Example 1. The existence of more than one glass transition temperature in these samples as shown in Table 7 indicates the presence of more than one crosslinked epoxy phase.
TABLE 7______________________________________COMPOSITE Tg T.DELTA.G' T.DELTA.G' T.DELTA.G'Panel No. Lot No. (.degree.C.) #1(.degree.C.) #2(.degree.C.)______________________________________40025 3-8318 161 181 20340026 3-8319 162 181 20240027 3-8322 164 181 20340030 3-8321 161 181 20240033 3-8323 164 181 20740034 3-8323 160 180 19740087 3-8342 154 173 19540118 3-8349 159 181 19340137 3-8353 160 181 20340220 3912-2 161 185 19940328 3-8390 135 158 17840337 3-8391 160 180 20040341 3-8395 160 178 201.sup.--X(n = 13) 159 179 199 8 7 7Cv (%) 4.72 3.76 3.65______________________________________
EXAMPLE 6
In this Example, particle sizes of uncured epoxy resin compositions (prepared according to Example 1) compositions are compared with the particle size and post impact compression values obtained from prepregs layed-up and cured using the procedures of Example 1.
The uncured epoxy resin compositions were analyzed as follows: A one half gram (approximate) sample was taken from each batch of the epoxy resin compositions and placed on a glass slide. The slides were then each heated on a hot plate having a temperature setting of 118.degree. C. The resin sample was then smeared into a thin film across the slide and allowed to further heat at 118.degree. C. for five (5) minutes. The sample slide was then cooled and examined on a polarizing microscope equipped with a transmitting light source and a Polaroid camera. A photomicrograph was taken of the sample at a magnification of 156.times..
The photomicrograph was visually examined and those samples having at least about 75% of the particles which were round and non-agglomerated were selected for further processing.
The photomicrographs were then further evaluated on an image analyzer set at 10 micron steps. A computerized "mouse" was used in measuring the long axis of each particle. When all particles in the sample were measured, the computer was used to generate a histogram and print out the number of particles counted, the median particle size, the range and the standard deviation.
The size of the particles in the cured composites were determined similarly. The particles measured in the cured composites were those in the boundary (essentially fiber fill) of resin between the plies of cured resin. The lay-up was the same as in Example 1 except for sample D shown in Table 8 below. Sample D had the lay-up [45/O/-45/90].sub.3S which gives a 24 ply laminate. As can be seen from Table 8 the particles remain about the same size during processing of the epoxy resin compositions into cured composites.
TABLE 8______________________________________Composite Neat ResinMedian Median PostParticle Particle ImpactDiameter Diameter Compression Resin(Microns) (Microns) (PIC) Lot Nos.______________________________________A 31 33 50.5 XS005 LB 34.2 36 50.0 XS005 KC 35.3 36 52.5 XS005 MD 39.9 36 48.5 XS005 ME 30.8 29 54.4 XS005 VF 37.9 35 50.6 XS005 AAG 36.8 35 50.0 XS005 YH 41.4 47 52.8 XS005 ACI 41.1 42 54.1 XS005 AFJ 32.8 31 51.7 XS005 AL______________________________________
EXAMPLE 7
In this Example, epoxy resin compositions are made on a larger than laboratory scale using the procedures of Example 2, except for the following. The dissolution product of amine functional polyether sulfone and triglycidyl aminophenol was cooled to 90.degree. C. and the mixture of carboxy functional butadiene nitrile polymer and diglycidyl ether of Bisphenol F was added at 55.degree. C. thereto.
A series of prepregs were made from these epoxy resin compositions. The prepregs were made by first making a film of the resin. The highest temperature used in making the film was about 70.degree. C. The prepregs were made by pressing either 145 grams per meter areal weight IM-7 carbon fiber or 90 grams per meter areal weight IM-7carbon fiber into the film. The resulting prepregs were about 35% (Grade 145) or 42% (Grade 190) by weight resin. Portions of the prepreg on each spool were layed up, cured and tested according to the procedures of Example 1. The particle size in the boundary resin layer (between plies) in the cured laminate was determined to the extent of determining dimensions of the largest and smallest particles thereof. In addition, the shape of the particles in each cured sample was judged visually. The results of this testing are shown below in Table 9A. These results show that more dense layers of fiber (i.e. areal weight 190 grams power centimeter) can be used to filter particles from the epoxy resin compositions. This filtration causes these larger particles to lie on the surface of the prepreg and thereafter reside in the boundary resin layer that is between plies (layers) of filaments. Presence of these larger particles between plies of filaments provides, as can be seen from the results in Table 9A, greater post impact compressive strength to the resulting composites.
TABLE 9______________________________________GRADE 190.sup.1 PARTICLE SIZE PIC SMALL- LARG-SPOOL (KSI) PARTICLE SHAPE EST EST______________________________________1 48.5 SPHERICAL 4 253 46.8 IRREGULAR 2.5 204 46.7 IRREGULAR 1.25 255 49.4 IRREGULAR 1.25 156 45.7 ROUND 2.5 557 51.3 ROUND 5 35______________________________________GRADE 145.sup.2 PARTICLE SIZE.sup.3 PIC SMALL- LARG-RUN # (KSI) PARTICLE SHAPE EST EST______________________________________3-8522 38.3 SMALL SPHERICAL 1.25 103-8210 42.6 SMALL SPHERICAL 1.25 103-8230 41.1 SMALL SPHERICAL 1.25 7.53-8232 43.4 NOT SPHERICAL 0.6 7.53-8237 41.5 NOT SPHERICAL 1.25 10______________________________________ .sup.1 IM7 carbon fiber having an areal weight of 190 grams per square meter. .sup.2 IM7 carbon fiber having an areal weight of 145 grams per square meter. .sup.3 Microns.
The procedures of this Example were repeated except that the epoxy resin composition was made according to the procedures of Example 1. The average particle was determined from the neat epoxy resin composition using the procedures of Example 5. Table 9B sets forth the results.
TABLE 9B______________________________________Prepreg Spool Areal Weight Particle PICRun No. No. (gm/m.sup.2) Size.sup.3 (ksi)______________________________________X3995-4 2X 190 33 51.4X3987-4 2A 190 35 49.6X3995-4 7A 145 33 48.3X4048-4 3B 145 36 48.6X3997-4 2B 135 34 48.1X3997-4 18B 135 31 43.8______________________________________
Table 9B illustrates that the particle size of the neat resin is generally associated with high toughness levels.
EXAMPLE 8
An epoxy resin composition like that described in Example 1 is prepared using a different reactive aromatic oligomer. This different reactive aromatic oligomer is made by replacing an amount of the bisphenol A used in manufacture of the oligomer with sodium sulfide to yield an amine functional polyarylene polyethersulfone polythioethersulfone (see formula I in the Specification). The level of the ingredients in the epoxy resin composition was the same as in Table 1 and the mixing procedure of Example 1 followed.
Photomicrographs of the cured epoxy resin composition are taken and copies thereof are shown in FIG. 6. The large, darker circles are the infusible particles of rubber polymer. (A portion of certain of the infusible particles has been cut away during sample preparation.) The other portions of the crosslinked epoxy resin matrix exhibit phase separation yielding glassy crosslinked phases.
EXAMPLE 9
In this example, an epoxy resin composition made using the procedures of Example 1 was made into a prepreg using IM-7 carbon fibers of Hercules Incorporated. The prepreg was layed up and cured into composite test samples. The samples were tested to determine various mechanical properties as compared to composites made using the thermoplastic resin APC-2 and AS-4 carbon fibers available from Hercules Incorporated (Column B). The results are reported in Table 10 below, the data in Table 10 being normalized to 57% fiber volume.
TABLE 10______________________________________MECHANICAL DATA SUMMARY A B IM7 AS4Property X* X*______________________________________RT Tensile Strength (ksi) 390 309RT Tensile Modulus (Msi) 22.3 19.40.degree. Compression Strength (ksi)RT 235 160180.degree. F. 200180.degree. F.-Wet 180200.degree. F. 185200.degree. F.-Wet 180Short Beam Shear (ksi)RT 15.3 15.2180.degree. F. 11.5180.degree. F.-Wet 10.0250.degree. F. 9.9250.degree. F.-Wet 7.5Compression ILS (ksi)RT 11.7180.degree. F. 9.0180.degree. F.-Wet 9.0Open Hole Tensile (ksi)RT 65 62180.degree. F. 69Open Hole Compression (ksi)RT 42 44180.degree. F. 37 39180.degree. F.-Wet 35______________________________________ *Average value
Table 11, set forth below, shows exemplary properties of a composite of this invention (column A), a composite made from a standard commercially available epoxy resin (column B) and a composite made using the thermoplastic APC-2 (column C). The data in column A of Table 11 represents values obtained from the composites of this invention where the epoxy resin composition is made using procedures generally described in Example 1.
TABLE 11______________________________________ A B C______________________________________Processing 350.degree. F. Cure 350.degree. F. Cure 720.degree. F. MoldingT.DELTA.G'(.degree.C.) Wet/Dry 120/163 130/187GIC in-lb/in.sup.2 2.6 1.12 13.7(composite)Gel Times (minutes 8-15 6-12 --at 350.degree. F.)Minimum Viscosity 15 (139.degree. C.) 6-10 (114.degree. C.) --(poise).sup.1Dynamic Gel 340 (171.degree. C.) 347 (175.degree. C.) --Temperature (.degree.F.)*Post Impact 53.sup.2 22 45Compression (ksi)at 1500 in-lb/inthicknessesAbsorbed Moisture 1.3 1.3 0.2(%)______________________________________ .sup.1 Varies upon heating rate (these tested at 2.degree. F./min.). .sup.2 IM7 carbon fiber.
It is especially interesting to note that the interlaminer fracture G.sub.IC energy is much higher for the thermoplastic resin as compared to the cured neat resin of this invention but that the damage tolerance of the composites of this invention are at least comparable to (if not higher than) the damage tolerance of the thermoplastic composite.

Number	Name	Date
3837904	Hill	Sep 1974
3926903	Scola	Dec 1975
3926904	Scola	Dec 1975
4187347	Brook	Feb 1980
4195113	Brook	Mar 1980
4220686	Brook	Sep 1980
4222918	Zentner et al.	Sep 1980
4264655	Brook	Apr 1981
4539253	Hirschbuehler et al.	Sep 1985
4588778	Nir et al.	May 1986
4656207	Jabloner et al.	Apr 1987
4668736	Robins et al.	May 1987

Damage tolerant composites containing infusible particles

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Parent Case Info

US Referenced Citations (12)

Foreign Referenced Citations (1)

Non-Patent Literature Citations (8)

Divisions (1)

Entry
"Elastomer-Modified Epoxy Resins for Structural Applications", by R. Drake and A. Siebert, SAMPE Quarterly (July 1975), pp. 11-21.
"What Failure Mechanisms Tell About Toughened Epoxy Resins", by E. H. Rowe and C. K. Riew, Plastics Engineering 31, Mar. 1975, pp. 45-47.
"The Fracture Behavior of an Epoxy Polymer Having a Bimodal Distribution of Elastomeric Inclusions", by W. D. Bascom, R. J. Moulton, E. H. Rowe and A. R. Siebert, Organic Coatings and Plastic Preprints, 39 (1978), pp. 164-171.
"Microstructure of Two-Phase Polymers", by J. N. Sultan, R. C. Laible and F. J. McGarry, Applied Polymer Symposium No. 16 (1971), pp. 127-136.
"The Fracture of Epoxy-and Elastomer-Modified Epoxy Polymers in Bulk and as Adhesives", by W. D. Bascom, R. L. Cottington, R. L. Jones and P. Peyser, Journal of Applied Polymer Science, vol. 19, pp. 2545-2562 (1975).
"Development of Resins for Damage Tolerant Composites--A Systematic Approach", 29th National Sampe Symposium, Apr. 3-5, 1984, pp. 422-436.
"Building Design With Fibre Reinforced Materials", by F. J. McGarry, Royal Soc. Lond. A., 319, 59-68 (1970).
"Phase Separation Behavior of Rubber-Modified Epoxies", by T. T. Wang and H. M. Zupko, Journal of Applied Polymer Science, vol. 26, pp. 2391-2401 (1981).