Decarbonization process for carbothermically produced aluminum

Information

  • Patent Grant
  • 9068246
  • Patent Number
    9,068,246
  • Date Filed
    Monday, December 15, 2008
    16 years ago
  • Date Issued
    Tuesday, June 30, 2015
    9 years ago
Abstract
A method of recovering aluminum is provided. An alloy melt having Al4C3 and aluminum is provided. This mixture is cooled and then a sufficient amount of a finely dispersed gas is added to the alloy melt at a temperature of about 700° C. to about 900° C. The aluminum recovered is a decarbonized carbothermically produced aluminum where the step of adding a sufficient amount of the finely dispersed gas effects separation of the aluminum from the Al4C3 precipitates by flotation, resulting in two phases with the Al4C3 precipitates being the upper layer and the decarbonized aluminum being the lower layer. The aluminum is then recovered from the Al4C3 precipitates through decanting.
Description
BACKGROUND OF THE INVENTION

The present invention relates to a method of recovering commercial grade aluminum from carbothermically produced Al—C alloy. More particularly, the invention relates to a method for separating and recovering the aluminum from the alloy that contains aluminum and aluminum carbide (A4C3) particles, that is, decarbonizing the aluminum.


Generally, the overall reaction of direct carbothermic reduction of alumina to produce aluminum is Al2O3+3C=2Al+3CO. The carbothermic reduction of alumina may take place in several steps: (1) 2Al2O3+9C=Al4C3+6CO and (2) Al4C3+Al2O3=6Al+3CO.


The present invention relates to the decarbonization process after the carbothermic reduction of alumina to produce aluminum.


SUMMARY OF THE INVENTION

In one embodiment, the present invention provides a method of recovering commercial grade aluminum. In another embodiment, a method of recovering aluminum from an alloy melt that comprises Al4C3 precipitates and aluminum, by cooling the alloy melt; then adding a sufficient amount of a finely dispersed gas to the alloy melt at a temperature of about 700° C. to about 900° C. to separate the aluminum from the Al4C3 precipitates. The aluminum recovered is a decarbonized carbothermically produced aluminum where the step of adding a sufficient amount of the finely dispersed gas effects flotation of the Al4C3 precipitates.


In one embodiment, the final step of separating the aluminum from the Al4C3 precipitates is by decanting, sub-surface or vacuum tapping the decarbonized aluminum to a receiver.


In a further embodiment, the finely dispersed gas used is an inert gas. In another embodiment, the inert gas used is either argon or carbon dioxide.


In yet another embodiment, the finely dispersed gas used is a mixed gas. In another embodiment, the mixed gas is a mixture of inert gas with a reactive gas. In a further embodiment, the inert gas used is argon and the reactive gas is chlorine.


In a further embodiment, the gas is introduced to the alloy melt by a rotating disperser, a bubbler tube, or a porous diffuser.


In yet another embodiment, the gas is introduced to the alloy melt when the alloy melt is at a temperature of about 700° C. to about 900° C.


Accordingly, it is one embodiment of the invention to provide a method of producing aluminum with a very low carbon content.


It is another embodiment of the invention to provide a method of recovering decarbonized carbothermically produced aluminum as claimed herein.


These and other further embodiments of the invention will become more apparent through the following description and drawing.





BRIEF DESCRIPTION OF THE DRAWINGS

For a fuller understanding of the invention, reference is made to the following description taken in connection with the accompanying drawing(s), in which:



FIG. 1 is a flow chart showing one embodiment of the method of producing aluminum in accordance with the present invention.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The followings are the definitions of the terms used in this application. As used herein, the term “alloy melt” means a melt of at least an aluminum alloy and Al4C3 particles. Note that the alloy melt may include or contain other materials such as Al2O3, C, oxycarbides, etc.


As used herein, the term “sufficient amount” means an amount that facilitates the separation of aluminum and aluminum carbide in order to recover greater than 90 weight % of the available aluminum.


The present invention provides a method of decarbonizing aluminum.


In one embodiment, the present invention discloses a method of recovering aluminum from a carbothermically produced alloy melt that comprises aluminum carbide, such as Al4C3 and aluminum. The alloy melt is cooled and a sufficient amount of a finely dispersed gas is added to the alloy melt at a temperature of about 700° C. to about 900° C., separating the aluminum from the Al4C3 precipitates.


In one embodiment, FIG. 1 shows a flow chart outlining the principal steps of the present invention. Here, an alloy melt is provided in the first step 10. In the second step 20, the alloy melt is cooled. In the third step 30, a finely dispersed gas is added to the alloy melt to assist in transporting the solid precipitates away from the aluminum, forming two phases with the solids being the upper layer. The aluminum is then removed and recovered in the fourth step 40 by means of decanting or tapping.


In the initial step, an alloy melt is provided. In one embodiment, the alloy melt is tapped into a crucible or ladle at very high temperature with the carbon in solution in the form of Al4C3. In one embodiment, the temperature of the alloy melt is at least about 2,000° C.


In the second step, alloy melt is cooled. As the alloy melt cools, the Al4C3 solidifies and precipitates. In one embodiment, the alloy melt is cooled to a temperature of about 700° C. to about 900° C. In one embodiment, the alloy mixture is cooled by the addition of solid and/or liquid aluminum. In one embodiment, the cooling aluminum is solid and/or liquid scrap of acceptable composition.


In the third step, a finely dispersed gas is added to the alloy melt. In one embodiment, the gas is distributed through the alloy melt by a bubbler tube or a rotating disperser or a porous diffuser at a temperature of about 700° C. to about 900° C. In another embodiment, the action of the gas provides a flotation effect in transporting the solid particles away from the aluminum, with the solid particles rising to the surface. In one embodiment, the rotating disperser is a straight bladed turbine with multiple blades and with an overall diameter of 40 to 60% of the treatment crucible or ladle. In another embodiment, the disperser is rotated at 100 to 250 revolutions per minute. In another embodiment, the flotation gas is injected through a rotary seal down the hollow shaft of the disperser, exiting underneath the bottom surface of the turbine.


Suitable types of gases that may be used in the present invention include, but are not limited to, inert gases, such as argon, carbon dioxide or nitrogen or a mixture of inert gases with a reactive gas, such as Cl2. In one embodiment, argon is mixed with about 2 to about 10 volume % of Cl2. In one embodiment, argon is mixed with 5 volume % of Cl2 gas. In one embodiment of the invention, an effective flow rate of gas needed to separate aluminum from the Al4C3 precipitates is about 5 cm3/min per cm2 of crucible cross sectional area. In one embodiment, the gas dispersion time is about 20 to 30 minutes. In another embodiment, the amount of gas changes depending on the amount of alloy melt quantity.


In the fourth step, decarbonized aluminum is then recovered from the treatment crucible or ladle. In one embodiment, the aluminum is decanted to a receiver, such as a mold.


Optionally, the solids that remain in the treatment vessel are then removed and stored for future recycle to the carbothermic furnace.


Table 1 below shows the amount of aluminum recovery for five examples in which the aluminum recoveries range from 62% to 96%. The aluminum product contained less that 600 ppm of carbon. The gas composition used in Table 1 is 95% argon and 5% Cl2 by volume.















TABLE 1









Ex-





Example 1
Example 2
ample 3
Example 4
Example 5





















Initial charge,
1.0-1.5
10-16
50.9
50.9
50.9


kgs.


Initial carbon,
1.3-3.2
1.1-4.2


weight %


Melt
750
750-800
774  
774  
774  


temperature,


° C.


Aluminum
 96
95
92.6
90.6
62.0


product
by rotor
by rotor
by rotor
by rotor
by rotor


recovered,


weight %


Carbon
less
less
11.6
26.3
22.0


content in the
than 100
than 600


aluminum


product


recovered,


ppm









EXAMPLE 1

In Example 1, the melts were approximately 1 kg in weight. The aluminum carbon alloy compositions contained about 1.3 to about 3.2% of carbon. The compositions were cooled and then gas mixtures of 95% argon and 5% Cl2 were fmely dispersed into the alloy compositions by a rotor at a temperature of 750° C. Here, the aluminum recovery was 96% or higher and the aluminum product contained less than 100 ppm of carbon and less than 100 ppm of chlorides.


EXAMPLE 2

In Example 2, the melts were approximately 10-16 kg in weight. The aluminum carbon alloy compositions contained about 1.1 to about 4.2% of carbon. The compositions were cooled and then gas mixtures of 95% argon and 5% Cl2 were finely dispersed into the alloy compositions by a rotor at temperatures of 750-800° C. Here, the aluminum recoveries were 95% or higher and the aluminum product contained less than 600 ppm of carbon.


It should be noted that the aluminum recovery is a function of the initial carbon content of the alloy melt. Recovery decreases as carbon content increases. Based on experimental results, recovery decreases by about 4 to 5% for every one % carbon content increase.


EXAMPLE 3

In Example 3, 50.9 kg of impure carbothermic alloy was added to 50.9 kg of molten aluminum contained in a 15.5 inch dia.×23.25 inch deep clay-graphite crucible at 774° C. The carbothermic alloy was mechanically submerged using steel tools. A graphite rotor having a 6″ diameter rotor with 9 teeth evenly spread around the circumference was immersed into the molten mixture. This rotor was attached to a 3 inch diameter graphite tube. A gas mixture of Ar-5% Cl2 was supplied through the shaft and dispersed into the molten mixture by rotating the shaft/rotor assembly at 350 rpm. During a 30 minute treatment time with this gas mixture, solid materials on the surface of the molten alloy mixture were continually pushed below the surface by mechanical tamping. After the treatment was completed, the rotor was removed from the metal and the thick dross layer that collected on the surface was removed. It should be noted that this dross contained Al4C3 particles, aluminum oxide, aluminum oxycarbides and some entrained aluminum metal. The resulting product metal was then manually removed from the crucible with a steel ladle. A total of 77.3 kg of metal was removed from this operation. The dross that was removed was subsequently processed in a separate step by immersing it into a molten salt bath (50% NaCl-50% KCl) to recover the residual metal in the dross. A total of 2.1 kg of metal was removed from the dross during this step. The overall metal recovery for the fluxing operation was calculated to be [(77.3−50.9)/(77.3−50.9+2.1)]*100=92.6%. The carbon content of the aluminum removed from the process was analyzed to be 11.6 ppm.


EXAMPLE 4

In Example 4, 50.9 kg of impure carbothermic alloy was added to 50.9 kg of molten aluminum at 774° C. The molten mixture was treated using the same method as Example 3, except the treatment gas was pure argon. No chlorine was used in this example. A total of 74.0 kg of aluminum was removed from the process. An additional 2.4 kg of aluminum was recovered from the dross, giving an overall metal recovery of 90.6%. The carbon content of the aluminum recovered from the process was 26.3 ppm.


EXAMPLE 5

In Example 5, 50.9 kg of impure carbothermic alloy was added to 50.9 kg of molten aluminum at 774° C. The molten mixture was treated using the same method as Example 4, except the materials floating on the surface were not mechanically submerged by tamping throughout the process. There was no tamping conducted during this example. A total of 64.0 kg of aluminum was removed from this process. An additional 8.0 kg of aluminum was removed from the dross, giving an overall metal recovery of 62.0%. The carbon content of the aluminum removed from this process was 22.0 ppm.


Examples 3, 4 and 5 show that the impure carbothermic alloy containing approximately 3.5% carbon can be purified using the fluxing method to produce a commercially acceptable alloy with a carbon content of less than 30 ppm. A comparison of Examples 3 and 4 shows that the fluxing process can be used either with or without chlorine in the fluxing gas. A comparison of Example 5 to Examples 3 and 4 show that tamping during the fluxing process considerably improves the recovery. Without tamping the recovery was 62%; when tamping was used the recovery was greater than 90%.


While specific embodiments of the invention have been described in detail, it will be appreciated by those skilled in the art that various modifications and alternatives to those details could be developed in light of the overall teachings of the disclosure. Accordingly, the particular arrangements disclosed are meant to be illustrative only and not limiting as to the scope of the invention which is to be given the full breadth of the appended claims and any and all equivalents thereof.

Claims
  • 1. A method comprising: (a) carbothermically preparing an aluminum alloy melt comprising Al4C3 precipitates and aluminum metal;(b) separating the aluminum metal from the Al4C3 precipitates, wherein the separating step comprises: introducing a gas into the aluminum alloy melt with a rotating disperser while the aluminum alloy melt is at a temperature of 700° C. to 900° C.;tamping the Al4C3 precipitates on the surface of the aluminum alloy melt to push the Al4Cl3 precipitates below the surface, into the aluminum alloy melt; and(c) recovering the aluminum metal from the melt.
  • 2. The method of claim 1, wherein recovering step (c) comprises: decanting, sub-surface or vacuum tapping the aluminum to a receiver.
  • 3. The method of claim 1, wherein the gas is an inert gas.
  • 4. The method of claim 3, wherein the inert gas used is either argon or carbon dioxide.
  • 5. The method of claim 3, wherein the inert gas used is nitrogen.
  • 6. The method of claim 1, wherein the carbothermically preparing step (a) comprises: cooling the aluminum alloy melt.
  • 7. The method of claim 6, wherein the cooling step comprises: cooling the aluminum alloy melt to a temperature of 700° C. to 900° C.
  • 8. The method of claim 6, wherein the cooling step comprises: adding solid or liquid aluminum to the aluminum alloy melt.
  • 9. The method of claim 1, wherein the introducing step comprises: transporting the Al4C3 precipitates towards a surface of the aluminum alloy melt.
  • 10. The method of claim 1, wherein, concomitant to the carbothermically preparing step (a), the temperature of the alloy melt is at least 2000° C.
  • 11. The method of claim 1, wherein the introducing step comprises: flowing the gas at a rate of 5 cm3 per min per cm2 of crucible cross-sectional area.
  • 12. The method of claim 1, wherein the introducing step comprises: rotating the rotating dispenser at 100 to 250 revolutions per minute.
GOVERNMENT FUNDING STATEMENT

This invention was made with government support under Contract No. DE-FC36-001D13900, awarded by the U.S. Department of Energy. The government has certain rights in the invention.

US Referenced Citations (52)
Number Name Date Kind
1219797 Barnett et al. Mar 1917 A
1222593 Barnett et al. Apr 1917 A
2090451 Kruh Aug 1937 A
2255549 Kruh Sep 1941 A
2755178 Rasmussen Jul 1956 A
2776884 Grunert Jan 1957 A
2829961 Miller et al. Apr 1958 A
2974032 Grunert et al. Mar 1961 A
3068092 Menegoz Dec 1962 A
3169854 Rapson Feb 1965 A
3198625 Stroup Aug 1965 A
3211547 Jarrett et al. Oct 1965 A
3230072 Johnson Jan 1966 A
3607221 Kibby Sep 1971 A
3715200 Archibald et al. Feb 1973 A
3721546 Shiba et al. Mar 1973 A
3767382 Bruno et al. Oct 1973 A
3839019 Bruno et al. Oct 1974 A
3846122 Valdo Nov 1974 A
3849119 Bruno et al. Nov 1974 A
3958979 Valdo May 1976 A
3971653 Cochran Jul 1976 A
3975187 Kibby Aug 1976 A
4177060 Tylko Dec 1979 A
4216010 Kibby Aug 1980 A
4221590 Dawless et al. Sep 1980 A
4222830 Dawless et al. Sep 1980 A
4239606 Dawless et al. Dec 1980 A
4246249 Dawless Jan 1981 A
4256717 Dawless Mar 1981 A
4273627 Dawless et al. Jun 1981 A
4294612 Dawless et al. Oct 1981 A
4299619 Cochran et al. Nov 1981 A
4312846 Dawless Jan 1982 A
4312847 Dawless Jan 1982 A
4312848 Dawless Jan 1982 A
4312849 Kramer Jan 1982 A
4409021 Moore Oct 1983 A
5342429 Yu et al. Aug 1994 A
5453110 Yu et al. Sep 1995 A
6440193 Johansen et al. Aug 2002 B1
6475260 LaCamera Nov 2002 B2
6530970 Lindstad Mar 2003 B2
6805723 Aune et al. Oct 2004 B2
6849101 Fruehan et al. Feb 2005 B1
6980580 Aune et al. Dec 2005 B2
7169207 Vegge et al. Jan 2007 B2
20060042413 Fruehan Mar 2006 A1
20080016984 Christini Jan 2008 A1
20080196545 Fruehan Aug 2008 A1
20090013823 Fruehan et al. Jan 2009 A1
20100107815 Fruehan et al. May 2010 A1
Foreign Referenced Citations (2)
Number Date Country
95122501 Mar 1996 RU
2007111945 Mar 2006 RU
Non-Patent Literature Citations (6)
Entry
Bruno, M.J., Aluminium Carbothermic Technology, Retrieved from the Internet: URL:http://www.osti.gov/bridge/purl.cover.jsp;jsessionid=F631E937A8806276EA77088DA10D11COA?purl=/838679-h1h8sh/> [retrieved on Feb. 15, 2010] pp. 31-32, Dec. 31, 2004.
Johansen Kai, et al, Aluminum carbothermic technology alcoa-elkem advanced reactor process, TMS Light Metals: Light Metals, Proceedings of the Technical Sessions, Technical TMS Annual Meeting, No. 132, p. 404, Mar. 2, 2003.
International Search Report and Written Opinion, dated Feb. 25, 2010, from related International Application No. PCT/US2009/064897.
Johansen et al., Carbothermic Aluminum, Proceedings 6th Conference on Molten Slags, Fluxes and Salts, Stockholm, Sweden-Helsinki, Finland (Jun. 12-17, 2002).
Morel et al., Alternative Process for Aluminum Production, pp. 1-44, (2007).
Saavedra et al., Investigating the Viability of Carbothermic Alumina Reduction, Journal of Metals, pp. 32-36 (Nov. 1988).
Related Publications (1)
Number Date Country
20100147113 A1 Jun 2010 US