The present invention relates to a decorative asphaltic membrane, more specifically a decorative asphaltic membrane with different chromatic patterns of designs, yet more specifically: a decorative asphaltic membrane with different chromatic patterns to be applied either on horizontal or vertical surfaces.
During a long time, asphaltic membranes of the prior art have not had into account any decorative aspect. The natural color of same was that of the upper substrates: natural aluminium, grey, black, dark brown. Over time, asphaltic membranes started to be painted. Special epoxy paints were used and the simulation of asphaltic membranes as to the environment was achieved, but always with an only color, preferable white, red brick or similar ones.
Various documents mention “aesthetic” or “decorative” aspects (U.S. Pat. Nos. 4,469,731; 4,610,902) but they make reference to roughness, bending aspects, etc., and not to color aspects of the asphaltic membrane.
Argentine patent application P2017 01 01948 of Megaflex, filed on Jul. 13, 2017, reveals an asphaltic membrane with multi-layer, trafficable, colored coating. Novelty lies on the fact that one of its layers is made of a synthetic polymer, that apart from being resistant to UV rays, includes pigments that work as a dye for the upper layer. That is: a layer is pigmented, with an only color. There are no possibilities of offering different patterns of drawings and colors.
Argentine patent AR 050464 of Megaflex, filed on Aug. 19, 2005 and granted on Oct. 19, 2009, reveals a multi-layer asphaltic lamination for waterproofing. It also reveals, in a subordinated claim, the application of a surface cleaning treatment, of color priming, of printings, of drawings and/or a combination therefrom. This patent reveals the application of colors over the surface of the asphaltic membrane, not inside same.
The first object of the present invention is to provide an asphaltic membrane with different chromatic patterns, resistant to bleaching.
Another object of the present invention is to provide an asphaltic membrane wherein chromatic patterns imitate, not exclusively, bricks, tiles, lawn, wood, stone, sports logotypes or those belonging to institutions/enterprises, texts, etc.
Another object of the present invention is to provide an asphaltic membrane that, given its decorative features, is appropriate to be applied onto vertical structures such as walls, columns, etc.
Another object of the present invention is to provide an asphaltic membrane that offers protection against UV rays.
In the manufacturing of an asphaltic membrane, a printing is applied to one of the polyethilene sheets so that said printing remains at sight once the asphaltic membrane is placed.
The printing may provide different patterns, either of designs as well as of colors. Preferably, patterns such as bricks, tiles, lawn, wood, stone, sports logos and those belonging to institutions/enterprises, texts, etc., are used.
Asphaltic Membrane
In the present description, it will be understood that the polyethilene material may be a low density polyethilene (PEBD, Spanish acronym), a high density polyethilene (PEAD, Spanish acronym) or mixtures of same.
The asphaltic membrane of the present invention is made up by 3 layers: a first lower non-stick layer, an second intermediate layer that grants waterproof features and a third upper layer that grants protection to the intermediate layer and, in our case, provides the desired design pattern.
The lower layer is a non-stick sheet. Its function is to protect the lower part of the intermediate layer during the stowage until its application. A high density polyethilene sheet is preferred. The polyethilene sheet has a thickness that ranges between 7μ and 30μ, preferably 15μ. This lower layer may also be made with non-stick asphalt to allow its cold application.
The second layer, the intermediate one, and also known as support, provides at least three components: a polyethilene layer, preferably of high density. The polyethilene sheet has a thickness ranging between 7μ to 120μ. The bitumen is modified with inert mineral loads, such as ashes, calcareous fillers and in percentages of up to 70% of the total asphaltic product.
In certain embodiments, the intermediate layer may also include an additional polyethilene layer and an asphaltic layer of modified bitumen.
The third layer, the upper one, is made of 3 sheets. Its display, from the outside to the inside, is: a polyethilene sheet, preferably of high density, a polyester sheet and a support. The polyester sheet has a thickness ranging between 7μ to 20μ, preferably 12μ. The support may be a metallic sheet, preferably aluminium, a non woven geotextile fabric or aluminized polyethilene. The metallic sheet preferably has a thickness that ranges between 7μ and 30μ. The geotextile fabric may have a weight that ranges between 50 and 180 g/cm2. The polyethilene sheet has a thickness that ranges between 7μ and 150μ, preferably 60μ, and is added with components for the protection against UV rays. Before its lamination with the other two sheets to form the upper layer of the asphaltic membrane, a printing is applied to the polyester sheet on its lower side. Said printing shall be in contact with the support and be protected from the outside by the polyethilene sheet itself.
The decorative asphaltic membrane of the present invention may provide designs which are away from the common grey, so that its application on walls or vertical surfaces is attractive.
The printing is made through a flexographic process or by means of a hollow engraving process. The digital photopolymer is prepared with the desired design. Inks shall be compatible with the lamination process. Inks are preferably based on solvents, water or UV inks. They are not viscous to attain a quick drying. They must be translucent since colors are added and not hidden.
Manufacturing Process:
As in any process known in the art related to the manufacturing of asphaltic membranes, same are laminated through a rolling mill with the required speeds and temperatures to obtain the final product. In the present invention, an additional printing process is added onto one of the layers, before using the rolling mill. The printing process may be temporally or physically independent of the lamination process of the asphaltic membrane.
The printing of the lower side of a polyester sheet is made with techniques known in the prior art. The ink is dried and this printed polyester sheet shall enter a first rolling mill to form the upper layer; a support, preferably aluminium, the printed polyester sheet and the polyethilene sheet.
Then, a second rolling mill will laminate the three layers: the upper one (already printed), the intermediate one (already made up by a polyethilene between two layers of asphalt) and the lower one to form the decorative asphaltic membrane.