This disclosure relates to radio frequency filters using acoustic wave resonators, and specifically to filters for use in communications equipment.
A radio frequency (RF) filter is a two-port device configured to pass some frequencies and to stop other frequencies, where “pass” means transmit with relatively low signal loss and “stop” means block or substantially attenuate. The range of frequencies passed by a filter is referred to as the “pass-band” of the filter. The range of frequencies stopped by such a filter is referred to as the “stop-band” of the filter. A typical RF filter has at least one pass-band and at least one stop-band. Specific requirements on a pass-band or stop-band depend on the application. For example, a “pass-band” may be defined as a frequency range where the insertion loss of a filter is better than a defined value such as 1 dB, 2 dB, or 3 dB. A “stop-band” may be defined as a frequency range where the rejection of a filter is greater than a defined value such as 20 dB, 30 dB, 40 dB, or greater depending on application.
RF filters are used in communications systems where information is transmitted over wireless links. For example, RF filters may be found in the RF front-ends of cellular base stations, mobile telephone and computing devices, satellite transceivers and ground stations, IoT (Internet of Things) devices, laptop computers and tablets, fixed point radio links, and other communications systems. RF filters are also used in radar and electronic and information warfare systems.
RF filters typically require many design trade-offs to achieve, for each specific application, the best compromise between performance parameters such as insertion loss, rejection, isolation, power handling, linearity, size and cost. Specific design and manufacturing methods and enhancements can benefit simultaneously one or several of these requirements.
Performance enhancements to the RF filters in a wireless system can have broad impact to system performance. Improvements in RF filters can be leveraged to provide system performance improvements such as larger cell size, longer battery life, higher data rates, greater network capacity, lower cost, enhanced security, higher reliability, etc. These improvements can be realized at many levels of the wireless system both separately and in combination, for example at the RF module, RF transceiver, mobile or fixed sub-system, or network levels.
High performance RF filters for present communication systems commonly incorporate acoustic wave resonators including surface acoustic wave (SAW) resonators, bulk acoustic wave (BAW) resonators, film bulk acoustic wave resonators (FBAR), and other types of acoustic resonators. However, these existing technologies are not well-suited for use at the higher frequencies and bandwidths proposed for future communications networks.
The desire for wider communication channel bandwidths will inevitably lead to the use of higher frequency communications bands. Radio access technology for mobile telephone networks has been standardized by the 3GPP (3rd Generation Partnership Project). Radio access technology for 5th generation (5G) mobile networks is defined in the 5G NR (new radio) standard. The 5G NR standard defines several new communications bands. Two of these new communications bands are n77, which uses the frequency range from 3300 MHz to 4200 MHz, and n79, which uses the frequency range from 4400 MHz to 5000 MHz. Both band n77 and band n79 use time-division duplexing (TDD), such that a communications device operating in band n77 and/or band n79 use the same frequencies for both uplink and downlink transmissions. Bandpass filters for bands n77 and n79 must be capable of handling the transmit power of the communications device. WiFi bands at 5 GHz and 6 GHz also require high frequency and wide bandwidth. The 5G NR standard also defines millimeter wave communication bands with frequencies between 24.25 GHz and 40 GHz.
The Transversely-Excited Film Bulk Acoustic Resonator (XBAR) is an acoustic resonator structure for use in microwave filters. The XBAR is described in U.S. Pat. No. 10,491,291, titled TRANSVERSELY EXCITED FILM BULK ACOUSTIC RESONATOR. An XBAR resonator comprises an interdigital transducer (IDT) formed on a thin floating layer, or diaphragm, of a single-crystal piezoelectric material. The IDT includes a first set of parallel fingers, extending from a first busbar and a second set of parallel fingers extending from a second busbar. The first and second sets of parallel fingers are interleaved. A microwave signal applied to the IDT excites a shear primary acoustic wave in the piezoelectric diaphragm. XBAR resonators provide very high electromechanical coupling and high frequency capability. XBAR resonators may be used in a variety of RF filters including band-reject filters, band-pass filters, duplexers, and multiplexers. XBARs are well suited for use in filters for communications bands with frequencies above 3 GHz.
Throughout this description, elements appearing in figures are assigned three-digit or four-digit reference designators, where the two least significant digits are specific to the element and the one or two most significant digit is the figure number where the element is first introduced. An element that is not described in conjunction with a figure may be presumed to have the same characteristics and function as a previously-described element having the same reference designator.
Description of Apparatus
The XBAR 100 is made up of a thin film conductor pattern formed on a surface of a piezoelectric plate 110 having parallel front and back surfaces 112, 114, respectively. The piezoelectric plate is a thin single-crystal layer of a piezoelectric material such as lithium niobate, lithium tantalate, lanthanum gallium silicate, gallium nitride, or aluminum nitride. The piezoelectric plate is cut such that the orientation of the X, Y, and Z crystalline axes with respect to the front and back surfaces is known and consistent. The piezoelectric plate may be Z-cut, which is to say the Z axis is normal to the front and back surfaces 112, 114. The piezoelectric plate may be rotated Z-cut or rotated YX-cut. XBARs may be fabricated on piezoelectric plates with other crystallographic orientations.
The back surface 114 of the piezoelectric plate 110 is attached to a surface of a substrate 120 except for a portion of the piezoelectric plate 110 that forms a diaphragm 115 spanning a cavity 140 formed in the substrate. The portion of the piezoelectric plate that spans the cavity is referred to herein as the “diaphragm” 115 due to its physical resemblance to the diaphragm of a microphone. As shown in
The substrate 120 provides mechanical support to the piezoelectric plate 110. The substrate 120 may be, for example, silicon, sapphire, quartz, or some other material or combination of materials. The back surface 114 of the piezoelectric plate 110 may be attached to the substrate 120 using a wafer bonding process. Alternatively, the piezoelectric plate 110 may be grown on the substrate 120 or attached to the substrate in some other manner. The piezoelectric plate 110 may be attached directly to the substrate or may be attached to the substrate 120 via one or more intermediate material layers (not shown in
“Cavity” has its conventional meaning of “an empty space within a solid body.” The cavity 140 may be a hole completely through the substrate 120 (as shown in Section A-A and Section B-B) or a recess in the substrate 120 under the diaphragm 115. The cavity 140 may be formed, for example, by selective etching of the substrate 120 before or after the piezoelectric plate 110 and the substrate 120 are attached.
The conductor pattern of the XBAR 100 includes an interdigital transducer (IDT) 130. The IDT 130 includes a first plurality of parallel fingers, such as finger 136, extending from a first busbar 132 and a second plurality of fingers extending from a second busbar 134. The term “busbar” means a conductor from which the fingers of an IDT extend. The first and second pluralities of parallel fingers are interleaved. The interleaved fingers overlap for a distance AP, commonly referred to as the “aperture” of the IDT. The center-to-center distance L between the outermost fingers of the IDT 130 is the “length” of the IDT.
The first and second busbars 132, 134 serve as the terminals of the XBAR 100. A radio frequency or microwave signal applied between the two busbars 132, 134 of the IDT 130 excites a primary acoustic mode within the piezoelectric plate 110. The primary acoustic mode is a bulk shear mode where acoustic energy propagates along a direction substantially orthogonal to the surface of the piezoelectric plate 110, which is also normal, or transverse, to the direction of the electric field created by the IDT fingers. Thus, the XBAR is considered a transversely-excited film bulk wave resonator.
The IDT 130 is positioned on the piezoelectric plate 110 such that at least the fingers of the IDT 130 are disposed on the diaphragm 115 that spans, or is suspended over, the cavity 140. As shown in
For ease of presentation in
Referring now to the detailed schematic cross-sectional view (Detail C), a front-side dielectric layer 150 may optionally be formed on the front side of the piezoelectric plate 110. The “front side” of the XBAR is, by definition, the surface facing away from the substrate. The front-side dielectric layer 150 may be formed only between the IDT fingers (e.g. IDT finger 138b) or may be deposited as a blanket layer such that the dielectric layer is formed both between and over the IDT fingers (e.g. IDT finger 138a). The front-side dielectric layer 150 may be a non-piezoelectric dielectric material, such as silicon dioxide, alumina, or silicon nitride. A thickness of the front side dielectric layer 150 is typically less than about one-third of the thickness tp of the piezoelectric plate 110. The front-side dielectric layer 150 may be formed of multiple layers of two or more materials. In some applications, a back-side dielectric layer (not shown) may be formed on the back side of the piezoelectric plate 110.
The IDT fingers 138a, 138b may be one or more layers of aluminum, an aluminum alloy, copper, a copper alloy, beryllium, gold, tungsten, molybdenum, chromium, titanium or some other conductive material. The IDT fingers are considered to be “substantially aluminum” if they are formed from aluminum or an alloy comprising at least 50% aluminum. The IDT fingers are considered to be “substantially copper” if they are formed from copper or an alloy comprising at least 50% copper. Thin (relative to the total thickness of the conductors) layers of metals such as chromium or titanium may be formed under and/or over and/or as layers within the fingers to improve adhesion between the fingers and the piezoelectric plate 110 and/or to passivate or encapsulate the fingers and/or to improve power handling. The busbars (132, 134 in
Dimension p is the center-to-center spacing or “pitch” of the IDT fingers, which may be referred to as the pitch of the IDT and/or the pitch of the XBAR. Dimension m is the width or “mark” of the IDT fingers. The geometry of the IDT of an XBAR differs substantially from the IDTs used in surface acoustic wave (SAW) resonators. In a SAW resonator, the pitch of the IDT is one-half of the acoustic wavelength at the resonance frequency. Additionally, the mark-to-pitch ratio of a SAW resonator IDT is typically close to 0.5 (i.e. the mark or finger width is about one-fourth of the acoustic wavelength at resonance). In an XBAR, the pitch p of the IDT may be 2 to 20 times the width m of the fingers. The pitch p is typically 3.3 to 5 times the width m of the fingers. In addition, the pitch p of the IDT may be 2 to 20 times the thickness of the piezoelectric plate 210. The pitch p of the IDT is typically 5 to 12.5 times the thickness of the piezoelectric plate 210. The width m of the IDT fingers in an XBAR is not constrained to be near one-fourth of the acoustic wavelength at resonance. For example, the width of XBAR IDT fingers may be 500 nm or greater, such that the IDT can be readily fabricated using optical lithography. The thickness of the IDT fingers may be from 100 nm to about equal to the width m. The thickness of the busbars (132, 134) of the IDT may be the same as, or greater than, the thickness of the IDT fingers.
In the exemplary filter 200, the three series resonators 210A, B, C and the two shunt resonators 220A, B of the filter 200 are formed on a single plate 230 of piezoelectric material bonded to a silicon substrate (not visible). In some filters, the series resonators and shunt resonators may be formed on different plates of piezoelectric material. Each resonator includes a respective IDT (not shown), with at least the fingers of the IDT disposed over a cavity in the substrate. In this and similar contexts, the term “respective” means “relating things each to each”, which is to say with a one-to-one correspondence. In
Each of the resonators 210A, 210B, 210C, 220A, 220B in the filter 200 has resonance where the admittance of the resonator is very high and an anti-resonance where the admittance of the resonator is very low. The resonance and anti-resonance occur at a resonance frequency and an anti-resonance frequency, respectively, which may be the same or different for the various resonators in the filter 200. In over-simplified terms, each resonator can be considered a short-circuit at its resonance frequency and an open circuit at its anti-resonance frequency. The input-output transfer function will be near zero at the resonance frequencies of the shunt resonators and at the anti-resonance frequencies of the series resonators. In a typical filter, the resonance frequencies of the shunt resonators are positioned below the lower edge of the filter's passband and the anti-resonance frequencies of the series resonators are positioned above the upper edge of the passband. In some filters, a front-side dielectric layer (also called a “frequency setting layer”), represented by the dot-dash rectangle 270, may be formed on the shunt resonators to set the resonance frequencies of the shunt resonators lower relative to the resonance frequencies of the series resonators. In other filters, the diaphragms of series resonators may be thinner than the diaphragms of shunt resonators. In some filters, the series resonators and the shunt resonators may be fabricated on separate chips having different piezoelectric plate thicknesses.
Lithium niobate (LN) is a preferred piezoelectric material for use in XBARs. LN has very high electromechanical coupling and is available as thin plates attached to non-piezoelectric substrates. While a wide variety of crystal orientations can be used in an XBAR, two orientations that have been used are Z-cut (Euler angles 0°, 0°, 90°) and rotated Y-cut (Euler angles 0°, β, 0° where 0°<β≤70°). Rotated Y-cut LN with 30°≤β≤38° has higher electromechanical coupling than Z-cut LN. Further, while both Z cut and rotated Y-cut LN XBARs are susceptible to leakage of acoustic energy in the transverse direction (the direction parallel to the IDT fingers), comparatively simple structures can be used to minimize such losses in a rotated Y-cut LN XBAR. Minimizing acoustic losses in a Z-cut LN XBAR requires a more complex structure that necessitates additional fabrication steps. XBARs using rotated Y-cut LN may have fewer and smaller spurious modes than Z-cut LN XBARs.
The large difference between the resonance and anti-resonance frequencies of rotated Y-cut LN XBARs enables the design of filters with very wide bandwidth. However, the difference between the resonance and anti-resonance frequencies can be too high for some filter applications. For example, 5G NR band N79 spans a frequency range from 4400 MHz to 5000 MHz. A band N79 bandpass filter cannot be implemented with conventional rotated Y-cut LN XBARs. As previously described, the resonance frequencies of shunt resonators in a ladder filter circuit are typically just below the lower edge of the filter passband and the anti-resonance frequencies of shunt resonators are within the passband. Conversely, the anti-resonance frequencies of series resonators are typically just above the upper edge of the filter passband and the resonance frequencies of series resonators are within the passband. To achieve these two requirements, the difference between the resonance and anti-resonance frequencies of the resonators needs to be less than or equal to the filter bandwidth. The difference between the resonance and anti-resonance frequencies of a rotated Y-cut LN XBAR is 790 MHz, which is greater than the 600 MHz bandwidth of band N79.
The difference between the decoupled XBAR 400 and the XBAR 100 shown in Detail C of
The decoupling dielectric layer 450 may be made of, for example, silicon dioxide, silicon nitride, aluminum oxide, or some other suitable dielectric material. In some applications, a preferred material for the decoupling dielectric layer 450 may be silicon dioxide, which provides an important secondary benefit of lowering the temperature coefficient of frequency (TCF) of the XBAR 400 compared to the XBAR 100 of
Although not shown in
Increasing the thickness of the decoupling dielectric layer increases the overall thickness of the XBAR diaphragm which results in a corresponding reduction in resonance frequency. Increasing the thickness of the decoupling dielectric layer lowers the electromechanical coupling which reduces the difference between the resonance and anti-resonance frequencies. The values of k2eff for the three XBARs are 21%, 20%, and 19%. The k2eff of the XBAR with tdd=80 nm (dashed curve 520) is approximately the same as an XBAR using a Z-cut piezoelectric plate.
The effect of a decoupling dielectric layer will scale with the thickness of the piezoelectric plate.
The ratio tdd/tp will typically be greater than or equal to 0.05 to obtain a useful reduction in k2eff. The ratio tdd/tp will generally not be greater than 0.5.
The frequency of an XBAR or DXBAR is primarily determined by the thickness of its diaphragm, including the piezoelectric plate and any dielectric layers. The mark and pitch of the IDT of an XBAR are selected to minimize the effects of spurious modes and, in particular, to locate spurious modes at frequencies removed from the passband of a filter. The length and aperture of an XBAR or DXBAR is determined by a combination of the capacitance required to match desired filter input and output impedances and the anticipate power dissipation in the device.
For a given IDT pitch and mark, the capacitance per unit IDT area of a DXBAR will be less than the capacitance per unit area of an XBAR. The reduction in capacitance is due to the presence of the decoupling dielectric layer, which has a significantly lower dielectric constant than the piezoelectric plate. However, the mark/pitch design space (for low spurious modes) for DXBARs tends to favor smaller pitch values. Smaller pitch results in larger capacitance per unit area, which offsets the reduced capacitance due to the presence of the decoupling dielectric layer. Thus, filters using DXBARs need not be larger, and may in some cases be smaller, than filters using XBARs.
A secondary, but important benefit of using a silicon dioxide decoupling dielectric layer is an improvement in the temperature coefficient of frequency (TCF). A DXBAR with a decoupling dielectric layer thickness about 22% of the thickness of the piezoelectric plate has a TCF of 65 at the resonance frequency and 62 at the anti-resonance frequency. A comparable XBAR using Z-cut lithium niobate has a TCF of 105 at the resonance frequency and 83 at the anti-resonance frequency.
The use of a decoupling dielectric layer to reduce the electromechanical coupling of an XBAR provides the filter designer with an additional degree of freedom. The filter designer may tailor the electromechanical coupling to the requirements of a particular filter without requiring a unique cut angle for the piezoelectric plate.
Description of Methods
While
The flow chart of
The piezoelectric plate may typically be rotated Y-cut lithium niobate. The piezoelectric plate may be some other material and/or some other cut. The device substrate may preferably be silicon. The device substrate may be some other material that allows formation of deep cavities by etching or other processing.
In one variation of the process 800, one or more cavities are formed in the device substrate at 810A, before the piezoelectric plate is bonded to the substrate at 815. A separate cavity may be formed for each resonator in a filter device. The one or more cavities may be formed using conventional photolithographic and etching techniques. Typically, the cavities formed at 810A will not penetrate through the device substrate.
At 815, the piezoelectric plate is bonded to the device substrate. The piezoelectric plate and the device substrate may be bonded by a wafer bonding process. Typically, the mating surfaces of the device substrate and the piezoelectric plate are highly polished. One or more layers of intermediate materials, such as an oxide or metal, may be formed or deposited on the mating surface of one or both of the piezoelectric plate and the device substrate. One or both mating surfaces may be activated using, for example, a plasma process. The mating surfaces may then be pressed together with considerable force to establish molecular bonds between the piezoelectric plate and the device substrate or intermediate material layers.
At 820, the sacrificial substrate may be removed. For example, the piezoelectric plate and the sacrificial substrate may be a wafer of piezoelectric material that has been ion implanted to create defects in the crystal structure along a plane that defines a boundary between what will become the piezoelectric plate and the sacrificial substrate. At 820, the wafer may be split along the defect plane, for example by thermal shock, detaching the sacrificial substrate and leaving the piezoelectric plate bonded to the device substrate. The exposed surface of the piezoelectric plate may be polished or processed in some manner after the sacrificial substrate is detached.
Thin plates of single-crystal piezoelectric materials laminated to a non-piezoelectric substrate are commercially available. At the time of this application, both lithium niobate and lithium tantalate plates are available bonded to various substrates including silicon, quartz, and fused silica. Thin plates of other piezoelectric materials may be available now or in the future. The thickness of the piezoelectric plate may be between 300 nm and 1000 nm. When the substrate is silicon, a layer of SiO2 may be disposed between the piezoelectric plate and the substrate. When a commercially available piezoelectric plate/device substrate laminate is used, steps 810A, 815, and 820 of the process 800 are not performed.
At 825, a decoupling dielectric layer is formed by depositing a dielectric material on the front surface of the piezoelectric plate. The decoupling dielectric layer may typically be silicon dioxide but may be another dielectric material such as silicon nitride or aluminum oxide. The decoupling dielectric layer may be a composite of two or more dielectric materials or layers of two or more dielectric materials. The decoupling dielectric layer may be patterned such that the decoupling dielectric layer is present on some portions of the piezoelectric plate and not present on other portions of the piezoelectric plate. The decoupling dielectric layer may be formed as two or more separately-patterned layers such that different thicknesses of decoupling dielectric layer are present on different portions of the piezoelectric plate.
A first conductor pattern, including IDTs and reflector elements of each XBAR, is formed at 845 by depositing and patterning one or more conductor layers on the front side of the piezoelectric plate. All or portions of the first conductor pattern may be over the decoupling dielectric layer formed at 825. The conductor layer may be, for example, aluminum, an aluminum alloy, copper, a copper alloy, or some other conductive metal. Optionally, one or more layers of other materials may be disposed below (i.e. between the conductor layer and the piezoelectric plate) and/or on top of the conductor layer. For example, a thin film of titanium, chrome, or other metal may be used to improve the adhesion between the conductor layer and the piezoelectric plate. A second conductor pattern of gold, aluminum, copper or other higher conductivity metal may be formed over portions of the first conductor pattern (for example the IDT bus bars and interconnections between the IDTs).
Each conductor pattern may be formed at 845 by depositing the conductor layer and, optionally, one or more other metal layers in sequence over the surface of the piezoelectric plate. The excess metal may then be removed by etching through patterned photoresist. The conductor layer can be etched, for example, by plasma etching, reactive ion etching, wet chemical etching, or other etching techniques.
Alternatively, each conductor pattern may be formed at 845 using a lift-off process. Photoresist may be deposited over the piezoelectric plate. and patterned to define the conductor pattern. The conductor layer and, optionally, one or more other layers may be deposited in sequence over the surface of the piezoelectric plate. The photoresist may then be removed, which removes the excess material, leaving the conductor pattern.
At 850, one or more frequency setting dielectric layer(s) may be formed by depositing one or more layers of dielectric material on the front side of the piezoelectric plate. For example, a dielectric layer may be formed over the shunt resonators to lower the frequencies of the shunt resonators relative to the frequencies of the series resonators. The one or more dielectric layers may be deposited using a conventional deposition technique such as physical vapor deposition, atomic layer deposition, chemical vapor deposition, or some other method. One or more lithography processes (using photomasks) may be used to limit the deposition of the dielectric layers to selected areas of the piezoelectric plate. For example, a mask may be used to limit a dielectric layer to cover only the shunt resonators.
At 855, a passivation/tuning dielectric layer is deposited over the piezoelectric plate and conductor patterns. The passivation/tuning dielectric layer may cover the entire surface of the filter except for pads for electrical connections to circuitry external to the filter. In some instantiations of the process 800, the passivation/tuning dielectric layer may be formed after the cavities in the device substrate are etched at either 810B or 810C.
In a second variation of the process 800, one or more cavities are formed in the back side of the device substrate at 810B. A separate cavity may be formed for each resonator in a filter device. The one or more cavities may be formed using an anisotropic or orientation-dependent dry or wet etch to open holes through the back side of the device substrate to the piezoelectric plate. In this case, the resulting resonator devices will have a cross-section as shown in
In a third variation of the process 800, one or more cavities in the form of recesses in the device substrate may be formed at 810C by etching the substrate using an etchant introduced through openings in the piezoelectric plate. A separate cavity may be formed for each resonator in a filter device. The one or more cavities formed at 810C will not penetrate through the device substrate.
Ideally, after the cavities are formed at 810B or 810C, most or all of the filter devices on a wafer will meet a set of performance requirements. However, normal process tolerances will result in variations in parameters such as the thicknesses of dielectric layer formed at 850 and 855, variations in the thickness and line widths of conductors and IDT fingers formed at 845, and variations in the thickness of the piezoelectric plate. These variations contribute to deviations of the filter device performance from the set of performance requirements.
To improve the yield of filter devices meeting the performance requirements, frequency tuning may be performed by selectively adjusting the thickness of the passivation/tuning layer deposited over the resonators at 855. The frequency of a filter device passband can be lowered by adding material to the passivation/tuning layer, and the frequency of the filter device passband can be increased by removing material to the passivation/tuning layer. Typically, the process 800 is biased to produce filter devices with passbands that are initially lower than a required frequency range but can be tuned to the desired frequency range by removing material from the surface of the passivation/tuning layer.
At 860, a probe card or other means may be used to make electrical connections with the filter to allow radio frequency (RF) tests and measurements of filter characteristics such as input-output transfer function. Typically, RF measurements are made on all, or a large portion, of the filter devices fabricated simultaneously on a common piezoelectric plate and substrate.
At 865, global frequency tuning may be performed by removing material from the surface of the passivation/tuning layer using a selective material removal tool such as, for example, a scanning ion mill as previously described. “Global” tuning is performed with a spatial resolution equal to or larger than an individual filter device. The objective of global tuning is to move the passband of each filter device towards a desired frequency range. The test results from 860 may be processed to generate a global contour map indicating the amount of material to be removed as a function of two-dimensional position on the wafer. The material is then removed in accordance with the contour map using the selective material removal tool.
At 870, local frequency tuning may be performed in addition to, or instead of, the global frequency tuning performed at 865. “Local” frequency tuning is performed with a spatial resolution smaller than an individual filter device. The test results from 860 may be processed to generate a map indicating the amount of material to be removed at each filter device. Local frequency tuning may require the use of a mask to restrict the size of the areas from which material is removed. For example, a first mask may be used to restrict tuning to only shunt resonators, and a second mask may be subsequently used to restrict tuning to only series resonators (or vice versa). This would allow independent tuning of the lower band edge (by tuning shunt resonators) and upper band edge (by tuning series resonators) of the filter devices.
After frequency tuning at 865 and/or 870, the filter device is completed at 875. Actions that may occur at 875 include forming bonding pads or solder bumps or other means for making connection between the device and external circuitry (if such pads were not formed at 845); excising individual filter devices from a wafer containing multiple filter devices; other packaging steps; and additional testing. After each filter device is completed, the process ends at 895.
Closing Comments
Throughout this description, the embodiments and examples shown should be considered as exemplars, rather than limitations on the apparatus and procedures disclosed or claimed. Although many of the examples presented herein involve specific combinations of method acts or system elements, it should be understood that those acts and those elements may be combined in other ways to accomplish the same objectives. With regard to flowcharts, additional and fewer steps may be taken, and the steps as shown may be combined or further refined to achieve the methods described herein. Acts, elements and features discussed only in connection with one embodiment are not intended to be excluded from a similar role in other embodiments.
As used herein, “plurality” means two or more. As used herein, a “set” of items may include one or more of such items. As used herein, whether in the written description or the claims, the terms “comprising”, “including”, “carrying”, “having”, “containing”, “involving”, and the like are to be understood to be open-ended, i.e., to mean including but not limited to. Only the transitional phrases “consisting of” and “consisting essentially of”, respectively, are closed or semi-closed transitional phrases with respect to claims. Use of ordinal terms such as “first”, “second”, “third”, etc., in the claims to modify a claim element does not by itself connote any priority, precedence, or order of one claim element over another or the temporal order in which acts of a method are performed, but are used merely as labels to distinguish one claim element having a certain name from another element having a same name (but for use of the ordinal term) to distinguish the claim elements. As used herein, “and/or” means that the listed items are alternatives, but the alternatives also include any combination of the listed items.
This patent application is a continuation of U.S. patent application Ser. No. 17/547,113, filed Dec. 9, 2021, which is a continuation of U.S. patent application Ser. No. 17/408,120, filed Aug. 20, 2021, issued as U.S. Pat. No. 11,239,816, which claims priority to U.S. Provisional Patent Application No. 63/137,736, filed Jan. 15, 2021, entitled XBAR WITH INSULATING LAYER BETWEEN ELECTRODE AND PIEZOELECTRIC MEMBRANE TO REDUCE ACOUSTIC COUPLING, the entire contents of each application are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 63137736 | Jan 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17547113 | Dec 2021 | US |
| Child | 18477307 | US | |
| Parent | 17408120 | Aug 2021 | US |
| Child | 17547113 | US |