The present invention relates to electrochemical cells utilizing a solid alkali ion conductive electrolyte membrane and to methods of protecting such membranes from degradation by dissolution. More particularly, the present invention discloses systems and methods for operating an electrochemical cell comprising a solid alkali ion conductive electrolyte membrane and an aqueous catholyte (or positive electrode) solution. Generally, the described systems and methods act to protect the membrane from degradation by dissolution.
Electrochemical cells comprising solid alkali ion conductive electrolyte membrane that selectively transport alkali ions are known in the art. By having an alkali ion-selective membrane in the electrochemical cell, alkali ions are allowed to pass between the cell's anolyte compartment (or negative electrode compartment) and catholyte compartment (or positive electrode compartment) while other chemicals are maintained in their original compartments. Thus, through the use of an alkali ion-specific membrane, an electrochemical cell can be engineered to be more efficient and to produce different chemical reactions than would otherwise occur without the membrane.
Solid alkali ion conductive electrolyte membranes are used in electrochemical cells for various reasons, including, but not limited to, being ion conductive, ion selective, water impermeable, chemically stable, electronic insulator, and so forth. By way of example, NaSICON (Na Super Ion CONducting) membranes selectively transport sodium cations, while LiSICON (Li Super Ion CONducting) and KSICON (K Super Ion CONducting) membranes selectively transport lithium and potassium cations, respectively. Other examples of solid alkali ion conductive electrolyte membranes include beta alumina, sodium-conductive glasses, etc.
Electrochemical cells comprising solid alkali ion conductive membranes are used to produce a variety of different chemicals and to perform various chemical processes. In some cases, such electrochemical cells convert alkali salts into their corresponding acids. In other cases, such electrochemical cells may also be used to separate alkali metals from mixed alkali salts.
One example of a conventional electrochemical cell 10 is illustrated in
The above-mentioned electrochemical cell may be modified for use with other alkali metals and acids corresponding to the alkali salts used in the anolyte solution. Moreover, it will be appreciated that other electrochemical reactions may occur which result in hydroxyl formation and a corresponding rise of pH within the positive electrode compartment 114. High pH catholyte solutions in such electrochemical cells have shortcomings. In one example, at a higher pH, such as a pH greater than about 10, certain alkali ion-conductive ceramic membranes, such as NaSICON membranes, begin to structurally degrade by dissolution. Accordingly, as the electrochemical cell 110 operates and base is produced in the positive electrode compartment 114, the cell 110 becomes less efficient or even inoperable. In another example, base produced in the positive electrode compartment 114 can actually damage the alkali ion conductive membrane, such as a NaSICON membrane, and thereby shorten its useful lifespan.
Batteries are a class of electrochemical cells that are used to store and release electrical energy for a variety of uses. In order to produce electrical energy, batteries typically convert chemical energy directly into electrical energy. Generally, a single battery includes one or more galvanic cells, wherein each of the cells is made of two half-cells that are electrically isolated except through an external circuit. During discharge, electrochemical reduction occurs at the cell's positive electrode, while electrochemical oxidation occurs at the cell's negative electrode. While the positive electrode and the negative electrode in the cell do not physically touch each other, they are generally chemically connected by at least one (or more) ionically conductive and electrically insulative electrolyte(s), which can either be in a solid or a liquid state, or in combination. When an external circuit, or a load, is connected to a terminal that is connected to the negative electrode and to a terminal that is connected to the positive electrode, the battery drives electrons through the external circuit, while ions migrate through the electrolyte.
Batteries can be classified in a variety of manners. For example, batteries that are completely discharged only once are often referred to as primary batteries or primary cells. In contrast, batteries that can be discharged and recharged more than once are often referred to as secondary batteries or secondary cells. The ability of a cell or battery to be charged and discharged multiple times depends on the Faradaic efficiency of each charge and discharge cycle.
Rechargeable batteries based on sodium and lithium can employ a solid primary electrolyte separator, such as a solid alkali ion conductive electrolyte membrane. The principal advantage of using a solid ion conductive electrolyte membrane is that the Faradaic efficiency of the resulting cell approaches 100%. Indeed, in almost all other cell designs, the electrode solutions in the cell are able to intermix over time and, thereby, cause a drop in Faradaic efficiency and loss of battery capacity.
Thus, while molten sodium-based rechargeable batteries are available, these batteries must be operated at temperatures above about 100° C. At such temperatures, the solid alkali ion conductive electrolyte membrane may be exposed to catholyte solutions that are chemically reactive to the alkali ion conductive electrolyte membrane making it susceptible to degradation by dissolution.
In still other conventional batteries, the electrochemical cells may be operated using molten salts which may be chemically reactive to the alkali ion conductive electrolyte membrane.
Thus, while electrochemical cells comprising a positive electrode compartment and an negative electrode compartment that are separated by a solid alkali ion-conductive membrane are known, challenges still exist, including those mentioned above. Accordingly, it would be an improvement in the art to protect the solid alkali ion conductive electrolyte membrane from undesired chemical reactions, including degradation by dissolution, and thereby maintain its structural stability and alkali ion conductivity.
The present invention provides systems and methods for protecting a solid alkali ion-conductive electrolyte material from degradation by dissolution. The disclosed invention may advantageously be implemented in electrochemical cells containing the alkali ion conductive electrolyte membrane having conditions that would attack, degrade, dissolve, corrode, reduce the efficiency of, or otherwise adversely affect the proper function of the alkali ion conductive electrolyte membrane material. More particularly, the present invention discloses systems and methods for operating an electrochemical cell comprising a solid alkali ion conductive electrolyte membrane and an aqueous catholyte solution.
In one non-limiting embodiment, an electrochemical cell includes an negative electrode compartment comprising an anode and a positive electrode compartment comprising a cathode. The positive electrode compartment holds an aqueous catholyte solution in contact with the catholyte solution. The catholyte solution comprises concentrated halide ions or polyhalide ions pseudohalide ions or sulfide ions or polysulfide ions. A solid alkali ion conductive electrolyte membrane is positioned between the negative electrode compartment and the positive electrode compartment. The presence of concentrated halide ions polyhalide ions or pseudohalide ions or sulfide ions or polysulfide ions has been observed to substantially reduce degradation by dissolution of the solid alkali ion conductive electrolyte membrane.
In some non-limiting embodiments the halide ion or polyhalide ions or pseudohalide ions or sulfide ions or polysulfide ions concentration is greater than 1.5M. In other non-limiting embodiments, the halide ions or polyhalide ions or pseudohalide ions or sulfide ions or polysulfide ions concentration is greater than 6M. In other non-limiting embodiments, the halide ions or polyhalide ions or pseudohalide ions or sulfide ions or polysulfide ions concentration is between 3M and a saturation concentration for the halide ions or polyhalide ions or pseudohalide ions or sulfide ions or polysulfide ions at an operating temperature of the positive electrode compartment. In yet other non-limiting embodiments the halide ions or polyhalide ions or pseudohalide ions or sulfide ions or polysulfide ions concentration is between 6M and 10M.
As used herein the halide ion is selected from chloride, bromide, and iodide. The polyhalides are X−n+1 (where, X=I, Br, Cl; n=2, 4, 6, . . . ). As used here in the polysulfide ions have the general formula S2−n+1. As used herein the pseudohalide ion is selected from azide, thiocyanate, and cyanide. Other known pseudohalide ions may also be used herein.
The solid alkali ion conductive electrolyte membrane material may include, but is not limited to, an alkali Metal Super Ion Conductive (MeSICON) material, where “Me” represents an alkali metal. Non-limiting examples of MeSICON materials include ceramic NaSICON, NaSICON-type materials, LiSICON, LiSICON-type materials, KSICON, and KSICON-type materials.
In some non-limiting embodiments, the electrochemical cell is a molten sodium rechargeable cell, wherein the anode comprises molten sodium metal in contact with the alkali ion conductive electrolyte membrane as the cell operates. In such cases, the alkali ion conductive membrane may include a NaSICON or NaSICON-type sodium ion conductive membrane. In some non-limiting embodiments, the molten sodium rechargeable cell may function at an operating temperature between about 100° C. and about 150° C. In other non-limiting embodiments, the cell functions at an operating temperature between about 110° C. and about 130° C. In some non-limiting embodiments of a molten sodium rechargeable cell, the cathode comprises nickel oxyhydroxide (NiOOH) and nickel hydroxide (Ni(OH)2). In other non-limiting embodiments, the positive electrode comprises copper and copper iodide and the catholyte solution comprises sodium iodide.
The present invention provides methods for protecting a solid alkali ion-conductive electrolyte material from degradation by dissolution. In one non-limiting embodiment, the method comprises obtaining and operating an electrochemical cell as described above, wherein the presence of halide ions or complex halide ions or pseudohalide ions or sulfide ions or polysulfide ions protects the solid alkali ion conductive electrolyte membrane from degradation.
These features and advantages of the present invention will become more fully apparent from the following description and appended claims, or may be learned by the practice of the invention as set forth hereinafter.
In order that the manner in which the above-recited and other features and advantages of the invention are obtained and will be readily understood, a more particular description of the invention briefly described above will be rendered by reference to specific embodiments thereof that are illustrated in the appended drawings. Understanding that the drawings are not made to scale, depict only some representative embodiments of the invention, and are not therefore to be considered to be limiting of its scope, the invention will be described and explained with additional specificity and detail through the use of the accompanying drawings in which:
Reference throughout this specification to “one embodiment,” “an embodiment,” or similar language means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the present invention. Thus, appearances of the phrases “in one embodiment,” “in an embodiment,” and similar language throughout this specification may, but do not necessarily, all refer to the same embodiment. Additionally, while the following description refers to several embodiments and examples of the various components and aspects of the described invention, all of the described embodiments and examples are to be considered, in all respects, as illustrative only and not as being limiting in any manner.
Furthermore, the described features, structures, or characteristics of the invention may be combined in any suitable manner in one or more embodiments. In the following description, numerous specific details are given, such as examples of suitable electrochemical cells and their features, halide or pseudohalide ions, etc., to provide a thorough understanding of embodiments of the invention. One having ordinary skill in the relevant art will recognize, however, that the invention may be practiced without one or more of the specific details, or with other methods, components, materials, and so forth. In other instances, well-known structures, materials, or operations are not shown or described in detail to avoid obscuring aspects of the invention.
As understood by persons skilled in the art, secondary cells can be discharged and recharged and this specification describes cell arrangements and methods for both states. Although the term “recharging” in its various forms implies a second charging, one of skill in the art will understand that discussions regarding recharging would be valid for, and applicable to, the first or initial charge, and vice versa. Thus, for the purposes of this specification, the terms “recharge,” “recharged” and “rechargeable” shall be interchangeable with the terms “charge,” “charged” and “chargeable” respectively.
The disclosed invention provides systems and methods for protecting a solid alkali ion-conductive electrolyte material from degradation by dissolution. It has been discovered that solid alkali ion conductive electrolyte membrane materials experience minimal corrosion or dissolution when exposed to solutions containing concentrated halide ions or pseudohalide ions, especially at elevated temperatures. As used herein, elevated temperatures means a temperature greater than room temperature. In some non-limiting embodiments, an elevated temperature includes a temperature greater than 40° C. In other non-limiting embodiments, an elevated temperature includes a temperature greater than 60° C. In still other non-limiting embodiments, an elevated temperature includes a temperature greater than 80° C. In yet other non-limiting embodiments, an elevated temperature includes a temperature greater than 100° C.
As used herein the halide ion is selected from chloride, bromide, and iodide. As used herein the pseudohalide ion is selected from azide, thiocyanate, and cyanide. Other known pseudohalide ions may also be used herein.
In some non-limiting embodiments the halide ion or pseudohalide ion concentration is greater than 3M. In other non-limiting embodiments, the halide ion or pseudohalide ion concentration is greater than 6M. In other non-limiting embodiments, the halide ion or pseudohalide ion concentration is between 3M and a saturation concentration for the halide ion or pseudohalide ion at an operating temperature of the positive electrode compartment. In yet other non-limiting embodiments the halide ion or pseudohalide ion concentration is between 6M and 10M.
The solid alkali ion conductive electrolyte membrane material may include, but is not limited to, an alkali Metal Super Ion Conductive (MeSICON) material, where “Me” represents an alkali metal. Non-limiting examples of MeSICON materials include ceramic NaSICON, NaSICON-type materials, LiSICON, LiSICON-type materials, KSICON, and KSICON-type materials.
One non-limiting application of the disclosed invention is in a molten sodium secondary cell that functions at an operating temperature between about 100° C. and about 150° C. While the described cell can comprise any suitable component,
Turning now to the manner in which the molten sodium secondary cell 210 functions, the cell can function in virtually any suitable manner. In one example,
In a contrasting example,
Referring now to the various components of the cell 210, the cell, as mentioned above, can comprise a negative electrode compartment 215 and a positive electrode compartment 225. In this regard, the two compartments can be any suitable shape and have any other suitable characteristic that allows the cell 210 to function as intended. By way of example, the negative electrode and the positive electrode compartments can be tubular, rectangular, or be any other suitable shape. Furthermore, the two compartments can have any suitable spatial relationship with respect to each other. For instance, while
With respect to the negative electrode 220, the cell 210 can comprise any suitable sodium negative electrode 220 that allows the cell 210 to function (e.g., be discharged and recharged) as intended. Some examples of suitable sodium negative electrode materials include, but are not limited to, a sodium sample that is substantially pure and a sodium alloy comprising any other suitable sodium-containing negative electrode material. In certain embodiments, however, the negative electrode comprises or consists of an amount of sodium that is substantially pure. In such embodiments, because the melting point of pure sodium is around 98° C., the sodium negative electrode will become molten above that temperature.
With respect to the positive electrode 230, the cell 210 can comprise any suitable positive electrode that allows the cell to be charged and discharged as intended. For instance, the positive electrode can comprise virtually any positive electrode material that has been successfully used in a sodium-based rechargeable battery system. In some embodiments, the positive electrode comprises a wire, felt, plate, tube, mesh, foam, and/or other suitable positive electrode configuration. In one non-limiting embodiment, the positive electrode comprises a nickel foam, nickel hydroxide (Ni(OH)2), nickel oxyhydroxide (NiOOH), sulfur composites, sulfur halides, including sulfuric chloride, and/or another suitable material. Furthermore, these materials may coexist or exist in combinations. In another non-limiting embodiment, the positive electrode comprises copper and copper iodide and the catholyte solution comprises sodium iodide.
For example a suitable positive electrode material may be nickel oxyhydroxide (NiOOH) (e.g., when the cell is at least partially charged) and nickel hydroxide (Ni(OH)2) (e.g., when the cell is at least partially discharged). In certain embodiments, however, the positive electrode comprises a nickel oxyhydroxide (NiOOH) electrode. It is understood that a nickel oxyhydroxide electrode, even when fully charged, will contain some amount of nickel hydroxide. In another non-limiting embodiment, the positive electrode comprises copper and copper iodide and the catholyte solution comprises sodium iodide.
In some non-limiting embodiments where the positive electrode 230 comprises a nickel oxyhydroxide (NiOOH) electrode, the negative electrode 220 comprises sodium, and the positive electrode solution 235 (as discussed below) comprises an aqueous solution, the reactions that occur at the negative electrode and at the positive electrode and the overall reaction as the cell 210 is discharged may occur as illustrated below:
Negative electrode Na→Na++e− (−2.71V)
Positive electrode NiOOH+H2O→Ni(OH)2+OH− (0.52V)
Overall Na+NiOOH+H2O→Ni(OH)2+NaOH (3.23V)
Accordingly, the above embodiment of the describe cell 210, at least theoretically, are capable of producing about 3.2V±0.5V at standard temperature and pressure.
Moreover, some examples of overall reactions that may occur during the discharging and charging of a cell in which the positive electrode 230 comprises a nickel oxyhydroxide (NiOOH) electrode, the negative electrode 220 comprises sodium, and the positive electrode solution 235 (as discussed below) comprises an aqueous solution, are shown below:
(Discharge) NiOOH+H2O+Na+→Ni(OH)2+NaOH
(Charge) Ni(OH)2+NaOH→NiOOH+H2O+Na
In another non-limiting embodiment, the positive electrode comprises and the catholyte solution comprises sodium iodide.
In some non-limiting embodiments where the positive electrode 230 comprises copper and copper iodide, the negative electrode 220 comprises sodium, and the positive electrode solution 235 comprises sodium iodide, the reactions that occur at the negative electrode and at the positive electrode and the overall reaction as the cell 210 is discharged may occur as illustrated below:
Negative electrode Na→Na++e− (−2.71V)
Positive electrode e−+CuI2−→Cu+2I− (−0.19V)
Overall Na+CuI2−→Cu+NaI+I− (2.51V)
Accordingly, the above embodiment of the describe cell 210, at least theoretically, are capable of producing about 2.5 V±0.5V at standard temperature and pressure.
Examples of overall reactions that may occur during the charging of a cell in which the positive electrode 230 comprises a copper and copper iodide electrode, the negative electrode 220 comprises sodium, and the positive electrode solution 235 comprises sodium iodide, are shown below:
Negative electrode Na++e−→Na
Positive electrode Cu→Cu++e−
Cu++I−→CuI
CuI+I−→CuI2−
Overall Cu+NaI+I−→Na+CuI2−
With reference now to the terminals 245 and 250, the cell 210 can comprise any suitable terminals that are capable of electrically connecting the cell with an external circuit, including without limitation, to one or more cells. In this regard, the terminals can comprise any suitable material and any suitable shape of any suitable size.
In addition to the aforementioned components, the cell 210 can optionally comprise any other suitable component. By way of non-limiting illustration
The described cell 210 may function at any suitable operating temperature. In other words, as the cell is discharged and/or recharged, the sodium negative electrode may have any suitable temperature. Indeed, in some embodiments, the cell functions at an operating temperature that is as high as a temperature selected from about 120° C., about 130° C., and about 150° C. Moreover, in such embodiments, as the cell functions, the temperature of the negative electrode can be as low as a temperature selected from about 120° C., about 115° C., about 110° C., and about 100° C. Indeed, in some embodiments, as the cell functions, the temperature of the negative electrode between about 100° and about 150° C. In other embodiments, the cell functions at a temperature between about 100° and about 130° C. In yet other embodiments, however, as the cell functions, the temperature of the negative electrode is about 120° C.±about 10° C.
The following examples are given to illustrate various embodiments within, and aspects of, the scope of the present invention. These are given by way of example only, and it is understood that the following examples are not comprehensive or exhaustive of the many types of embodiments of the present invention that can be prepared in accordance with the present invention.
Thirteen different NaSICON and NaSICON-type materials manufactured by Ceramatec, Inc., Salt Lake City, Utah, were placed in 50 wt. % NaOH at 100° C. The samples were removed and weighed to measure weight loss due to dissolution. The samples all experienced weight loss ranging from about 6.5 wt. % to great than 50 wt. %. The results are shown in
Four different formulations of a NaSICON material were placed in 50 wt. % NaOH at 100° C. for a period of nine weeks to measure weight loss due to dissolution. Three samples of each formulation were weighed each week.
For each different formulation, three samples were pre-weighed on a 4-place analytical balance and the weight was recorded. Then the samples were placed into a plastic container with a screw sealed lid containing 50 wt. % NaOH solution. The container with the solution and samples was placed in an oven set to 100° C. and allowed to sit for one week. After a week the samples were removed from the solution and thoroughly rinsed with water. The samples were then sonicated in a sonic bath of DI water, and then dried for 1 hour at 100° C. Once dried, the samples were then weighed again using the same calibrated balance. The new weight for each sample was recorded. The weight loss from week to week was measured as a percent loss. Each of the three samples per formulation were averaged together to get the data shown in
Three different formulations of a NaSICON material were placed in different sodium halide solutions at 100° C. (6 M NaI, 53 wt. % NaBr, 25 wt. % NaCl) for a period of nine weeks to measure weight loss due to dissolution. Three samples of each formulation were weighed each week.
For each different formulation, three samples were pre-weighed on a 4-place analytical balance and the weight was recorded. Then the samples were placed into a plastic container with a screw sealed lid containing the respective sodium halide solution. The container with the solution and samples was placed in an oven set to 100° C. and allowed to sit for one week. After a week the samples were removed from the solution and thoroughly rinsed with water. The samples were then sonicated in a sonic bath of DI water, and then dried for 1 hour at 100° C. Once dried, the samples were then weighed again using the same calibrated balance. The new weight for each sample was recorded. The weight loss from week to week was measured as a percent loss. Each of the three samples per formulation were averaged together to get the data shown in
Four different formulations of a NaSICON material were placed in different sodium iodide solutions at 120° C. (10M Nat 6M NaI and 3M iodine, 6M NaI, 6M NaI and 20 wt. % borax) for a period of nine weeks to measure weight loss due to dissolution. The 6M NaI and 3M iodine was made by dissolving sodium iodide salt into DI water and then adding 3M iodine crystals to the solution to try and increase the iodine content of the salt solution. Three samples of each formulation were weighed each week.
For each different formulation, three samples were pre-weighed on a 4-place analytical balance and the weight was recorded. Then the samples were placed into a plastic container with a screw sealed lid containing the respective sodium iodide solution. The container with the solution and samples was placed in an oven set to 120° C. and allowed to sit for one week. After a week the samples were removed from the solution and thoroughly rinsed with water. The samples were then sonicated in a sonic bath of DI water, and then dried for 1 hour at 120° C. Once dried, the samples were then weighed again using the same calibrated balance. The new weight for each sample was recorded. The weight loss from week to week was measured as a percent loss. Each of the three samples per sodium iodide solution were averaged together to get the data shown in
A molten sodium secondary cell (battery) was prepared and operated. The negative electrode (anode) was molten sodium and the positive electrode (cathode) was copper wire and copper iodide. A 1.4 cm2 disk comprising NaSICON sodium ion conductive electrolyte membrane was disposed between the negative and positive electrodes. The positive electrode (or catholyte) solution contained 3 mL of 2M CuI in 10M NaI. The cell underwent 43 charge/discharge cycles over about 330 hours. It was operated at a temperature of 120° C. The discharge voltage was about 2.15 V.
While specific embodiments and examples of the present invention have been illustrated and described, numerous modifications come to mind without significantly departing from the spirit of the invention, and the scope of protection is only limited by the scope of the accompanying claims.
This application claims the benefit of U.S. Provisional Patent Application No. 61/723,122 filed Nov. 6, 2012, entitled “Degradation Protection of Solid Alkali Ion Conductive Electrolyte Membrane.” This prior application is expressly incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
4041215 | Kormanyos et al. | Aug 1977 | A |
4162351 | Putt et al. | Jul 1979 | A |
4244986 | Paruso et al. | Jan 1981 | A |
4307164 | Church et al. | Dec 1981 | A |
4375501 | Peled et al. | Mar 1983 | A |
4427747 | Bennett et al. | Jan 1984 | A |
4546055 | Coetzer et al. | Oct 1985 | A |
4579796 | Muramatsu | Apr 1986 | A |
4753858 | Jow | Jun 1988 | A |
5139897 | Wedlake | Aug 1992 | A |
5264298 | Townsend | Nov 1993 | A |
5290405 | Joshi et al. | Mar 1994 | A |
5422197 | Zito | Jun 1995 | A |
5525442 | Shuster | Jun 1996 | A |
5552244 | Griffin et al. | Sep 1996 | A |
5563006 | Von Benda et al. | Oct 1996 | A |
5686201 | Chu | Nov 1997 | A |
6030720 | Chu et al. | Feb 2000 | A |
6033343 | Licht | Mar 2000 | A |
6376123 | Chu | Apr 2002 | B1 |
6410181 | Spillman et al. | Jun 2002 | B1 |
6852450 | Hwang et al. | Feb 2005 | B2 |
6881234 | Towsley | Apr 2005 | B2 |
8012621 | Joshi et al. | Sep 2011 | B2 |
8883339 | Choi | Nov 2014 | B2 |
8968902 | Coors | Mar 2015 | B2 |
20020150818 | Amatucci et al. | Oct 2002 | A1 |
20020172871 | Shucker | Nov 2002 | A1 |
20040065543 | Kovarsky | Apr 2004 | A1 |
20050109617 | Ono et al. | May 2005 | A1 |
20050260460 | Kishi et al. | Nov 2005 | A1 |
20060141346 | Gordon et al. | Jun 2006 | A1 |
20060177732 | Visco et al. | Aug 2006 | A1 |
20060226022 | Balagopal et al. | Oct 2006 | A1 |
20060257734 | Obata et al. | Nov 2006 | A1 |
20070048610 | Tsang et al. | Mar 2007 | A1 |
20070154762 | Schucker | Jul 2007 | A1 |
20070221265 | Affinito et al. | Sep 2007 | A1 |
20080268327 | Gordon et al. | Oct 2008 | A1 |
20090061288 | Gordon et al. | Mar 2009 | A1 |
20090134040 | Gordon et al. | May 2009 | A1 |
20090134842 | Joshi et al. | May 2009 | A1 |
20090136830 | Gordon | May 2009 | A1 |
20090189567 | Joshi et al. | Jul 2009 | A1 |
20090212743 | Hagiwara et al. | Aug 2009 | A1 |
20100089762 | Gordon | Apr 2010 | A1 |
20100239893 | Gordon et al. | Sep 2010 | A1 |
20100261051 | Okada et al. | Oct 2010 | A1 |
20100285372 | Lee et al. | Nov 2010 | A1 |
20110104526 | Boxley et al. | May 2011 | A1 |
20120021273 | Ohmori et al. | Jan 2012 | A1 |
20120045695 | Sheem et al. | Feb 2012 | A1 |
20120126752 | Joshi et al. | May 2012 | A1 |
20120141856 | Gordon et al. | Jun 2012 | A1 |
20120214043 | Olschimke et al. | Aug 2012 | A1 |
20120219833 | Coors et al. | Aug 2012 | A1 |
20120219843 | Bogdan et al. | Aug 2012 | A1 |
Number | Date | Country |
---|---|---|
62186470 | Aug 1987 | JP |
2008293678 | Dec 2008 | JP |
100651246 | Aug 2005 | KR |
WO 2005091946 | Oct 2005 | WO |
WO 2011057135 | Aug 2011 | WO |
WO 2012061823 | Jul 2012 | WO |
Entry |
---|
Young, Lee W., “International Search Report”, PCT Search Report for App. No. PCT/US 08/10435, (Nov. 25, 2008),1-2. |
Young, Lee W., “Written Opinion of the International Searching Authority”, PCT Written Opinion for App. No. PCT/US 08/10435, (Nov. 25, 2008),1-4. |
Salminen, Justin et al., “Ionic liquids for rechargeable lithium batteries”, Lawrence Berkeley National Laboratory, (Sep. 21),1-19. |
Cullen, Sean P., “Office Action for U.S. Appl. No. 12/205,759”, (Sep. 16, 2010),1-22. |
Cullen, Sean P., “Office Action for U.S. Appl. No. 12/205,759”, (Apr. 13, 2011),1-15. |
Lee, Kang Young “International Search Report”, International App. No. PCT/US2010/055718, (Jun. 21, 2011),1-3. |
Lee, Kang Young “Written Opinion”, International App. No. PCT/US2010/055718, (Jun. 21, 2011),1-3. |
Suzuki, et al., “Bibliographical Data and Abstract (English Language)”, Japanese Patent application JP62-186470, (Aug. 14, 1987),1-2. |
Yun, Cho K., “Internationial Search Report”, PCT App. No. PCT/US2012/036959 (corresponding to U.S. Appl. No. 13/466,844), (Nov. 23, 2012),1-3. |
Yun, Cho K., “Written Opinion of the International Searching Authority”, PCT. App. No. PCT/US2012/036959 (corresponding to U.S. Appl. No. 13/466,844), (Nov. 23, 2012),1-5. |
Cullen, Sean P., “Non Final Office Action”, U.S. Appl. No. 12/205,759, (Apr. 5, 2013),1-17. |
Lee, Dong W., “International Serach Report”, PCT Application No. PCT/US13/68552 (Corresponding to U.S. Appl. No. 14/072,468), (Jan. 24, 2014),1-3. |
Lee, Dong W., “Written Opinion of the International Searching Authority”, PCT Application No. PCT/US2013/68552 (Corresponding to U.S. Appl. No. 14/072,468), (Jan. 24, 2014),1-5. |
Lee, Dong W., “International Search Report”, PCT Application No. PCT/US13/62386 (Corresponding to U.S. Appl. No. 14/040,241), (Dec. 23, 2013),1-3. |
Lee, Dong W., “Written Opinion of the International Search Authority”, PCT Application No. PCT/US2013/62386 (Corresponding to U.S. Appl. No. 14/040,241), (Dec. 23, 2014),1-5. |
Lee, Dong W., “International Search Report”, PCT Application No. PCT/US2013/058403 (Corresponding to U.S. Appl. No. 14/019,651), (Dec. 2, 2013),1-3. |
Lee, Dong W., “Written Opinion of the International Searching Authority”, PCT Application No. PCT/US2013/058403 (Corresponding to U.S. Appl. No. 14/019,651), (Dec. 2, 2013),1-6. |
Parsons, Thomas H., “Non Final Office Action”, U.S. Appl. No. 13/466,844, (Feb. 26, 2015),1-22. |
Marks, Jacob B., “Non Final Office Action”, U.S. Appl. No. 14/469,865, (Apr. 7, 2015),1-6. |
Shin, Ju C., “International Search Report”, PCT Application No. PCT/US2014/059954 (Corresponding with U.S. Appl. No. 14/511,031) (Jan. 20, 2015),1-3. |
Shin, Ju C., “Written Opinion of the International Searching Authority”, PCT Application No. PCT/US2014/059954 (Corresponding with U.S. Appl. No. 14/511,031, (Jan. 20, 2015),1-4. |
Jarvi, Tommi “Supplementary European Search Report”, European Patent Application No. 12783042.0, (Oct. 14, 2014),1-7. |
Armand, Michel et al., “ionic-liquid materials for the electrochemical challenges of the future”, Nature Materials, (Jul. 24, 2009),621-629. |
Doyle, Kevin P., et al., “Dentrite-Free Electrochemical Deposition of Li—Na Alloys from an Ionic Liquid Electrolyte”, Journal of The Electrochemical Society, (May 2006),A1353-A1357. |
Kim, K et al., “Electrochemical Investigation of Quaternary Ammonium/Aluminum Chloride Ionic Liquids”, Journal of The Electrochemical Society, (Jun. 2004),A1168-A1172. |
Kim, Ketack et al., “The Role of Additives in the Electroreduction of Sodium Ions in Chloroaluminate-Based Ionic Liquids”, Journal of The Electrochemical Society, (Dec. 2004),E9-E13. |
Lang, Christopher M., et al., “Cation Electrochemical Stability in Chloroaluminate Ionic Liquids”, J. Phys. Chem., (2005),19454-19462. |
Cullen, Sean P., “Non-Final Office Action”, U.S. Appl. No. 12/725,319, (Jan. 6, 2012),1-10. |
Cullen, Sean P., “Final Office Action”, U.S. Appl. No. 12/725,319, (Apr. 27, 2012),1-12. |
Cho, Jun B., “International Search Report”, PCT App. No. US2010/027535 (Corresponding to U.S. Appl. No. 12/725,319), (Oct. 20, 2010),1-4. |
Cho, Jun B., “Written Opinion of the International Searching Authority”, PCT App. No. US2010/027535 (Corresponding to U.S. Appl. No. 12/725,319), (Oct. 20, 2010),1-5. |
Ryu, et al., “Bibliographical Data and Abstract (English Language)”, Application Publication for US2007154814, Corresponding to KR10-0651246, (Aug. 22, 2005),1. |
Wiedemann, Eric “Supplementary European Search Report”, European Patent Application No. 10754004.9 (Corresponding to U.S. Appl. No. 12/725,319, (May 16, 2012),1-6. |
Sonoda, et al., “Bibliographical Data and Abstract (English Translation)”, Japanese Patent Application JP-59-75985, (Apr. 28, 1984),1-2. |
Takeguchi, Yasuhiro “Final Rejection Action”, Japanese Patent Application No. 2012-537241, (Jun. 17, 2014),1-6. |
“Notice of Allowance”, Japanese Patent Application 2012-537241, (May 11, 2015),1-6. |
Parsons, Thomas H., “Final Office Action”, U.S. Appl. No. 13/466,844, (Aug. 11, 2015),1-13. |
Masatsugu, Morimitsu “English Lanuage Abstract”, JP2008293678, (Dec. 4, 2008),1. |
Peramunage, et al., “A Solid Sulfur Cathode for Aqueous Batteries”, Science, vol. 261, (Aug. 20, 1993),1029-1032. |
Marks, Jacob B., “Non-Final Office Action”, U.S. Appl. No. 12/940,864, (Jun. 18, 2013),1-30. |
Marks, Jacob B., “Final Office Action”, U.S. Appl. No. 12/940,864, (Jan. 29, 2014),1-11. |
Marks, Jacob B., “Notice of Allowance”, U.S. Appl. No. 12/940,864, (Jun. 20, 2014),1-7. |
Cain, Edward J., “Non Final Office Action”, U.S. Appl. No. 14/072,468, (Oct. 5, 2015),1-6. |
Quraishi, Kiran “Non-Final Office Action”, U.S. Appl. No. 14/040,241, (Oct. 28, 2015),1-12. |
Colucci, Rios J., “Non-Final Office Action”, U.S. Appl. No. 14/019,651, (Aug. 17, 2015),1-26. |
Number | Date | Country | |
---|---|---|---|
20140170443 A1 | Jun 2014 | US |
Number | Date | Country | |
---|---|---|---|
61723122 | Dec 2012 | US |