Patent Application
20120060983
I. Field of the Invention
This invention relates to delay compositions used in detonators for explosives (sometimes referred to as blasting caps) and other devices (e.g. inline detonation delay devices), and to detonation delay elements and devices containing such compositions. More particularly, the invention relates to delay compositions having slow-burning (long delay) times for use with both non-electric and electric detonators, inline delay devices, and the like.
II. Background Art
Delay compositions are materials that burn away rapidly, but not instantly, when ignited, thus create a timing delay, in the nature of a fuse, when shaped and compacted in the form of an elongated body or column and ignited at one end. Such compositions may therefore be used to create a delay between the instant at which a detonator or similar device receives a firing signal (which commences ignition of the column of delay composition), and the instant at which an associated explosive charge is set off (by heat when the combustion reaches the remote end of the burning column), or a further firing signal is generated.
Delay detonators and similar delay devices, both non-electric and electric, are widely employed in mining, quarrying and other blasting operations in order to permit sequential initiation of explosive charges distributed in a predetermined pattern of bore holes or shot holes. The provision of a delay between sequential initiation of adjacent bore or shot holes is effective in controlling the fragmentation and throw of the rock being blasted and, in addition, provides a reduction in ground vibration and in air blast noise.
Modern commercial delay detonators, whether non-electric or electric, normally comprise a metallic shell, closed at one end, which contains in sequence from the closed end: a base charge of a detonating high explosive, such as for example pentaerythritoltetranitrate (PETN), and an adjacent primer charge of a heat-sensitive detonable material, such as for example lead azide. Adjacent to the heat-sensitive material is a consolidated, e.g. compressed, column of delay composition of sufficient length and quantity to provide a desired delay time as described above. The column of the delay composition is normally confined within a hollow tubular confinement element made of metal. The confinement element and delay composition contained therein, together with sealers and primer charges, if any, form a delay element that is normally fabricated separately and assembled into a detonator or the like as a single item. Next to the delay element is an ignition (starter) charge adapted to be ignited by an electrically heated bridge wire or, alternatively, by the heat and flame of a low energy detonating cord or shock wave conductor retained in the open end of the metallic shell. Such a delay detonator may serve as an in-line delay as when coupled at both ends to a detonating cord or shock wave conductor. However, a delay device need not also be capable of serving as a detonator in order, for example, to initiate a shock wave conductor. An ignition charge in close proximity to the end of the shock wave conductor, instead of a base charge of detonating high explosive, will suffice.
The containment of the delay composition within a confinement element facilitates the handling of the composition and its introduction into a detonator or the like. The metal also protects other components (e.g. the outer shell of a detonator) from the heat and by-products of combustion as the delay composition is consumed and, for reasons of economy, minimizes the amount of the delay composition that is required. In the past, lead has often been used as the metal for the confinement elements. Lead is soft and malleable and can be loaded with a burning core, drawn to a desired diameter and cut to required lengths (different lengths produce different delay times). Lead also has a low thermal conductivity and heat capacity, and therefore diverts only a minimum amount of heat from the composition as it burns, thus reducing the risk that the combustion may be quenched or extinguished prior to complete consumption of the delay composition.
A trend has recently developed of replacing confinement elements made of lead with elements made of rigid metals, such as zinc, aluminum, steel or brass. Zinc is currently the preferred metal of choice for this purpose. The term “rigid metal” refers to those metals that, when used to form confinement elements, are not easily drawn to a desired diameter or shaped using the equipment currently available for lead. With such metals, the confinement elements are first cast to the desired diameter and length, and then the delay composition is loaded into the interior of the element and compressed. This change to rigid metal confinement elements has come about in part because the use of lead is receiving criticism from some quarters for being environmentally hazardous, even though the quantity of lead is small. Moreover, the use of rigid metal confinement elements can facilitate fabrication of delay units and their integration into detonators and delay devices, etc. However, zinc and other suitable rigid metals have higher thermal conductivities and heat capacities than lead, and thus extract more heat from the delay composition as it burns. This can increase the failure rate of detonators and delay devices because there may be insufficient heat remaining in the delay composition to maintain the combustion temperature until complete consumption of the composition has taken place, especially when such devices are used in low temperature environments. Particularly at risk of failure are delay units intended to provide long delays, e.g. more than one second, often used in underground applications.
A large number of delay compositions are known in the art. These generally comprise mixtures of fuels and oxidizers of various kinds. Many are substantially gasless compositions, which are generally preferred; that is, they burn without evolving large amounts of gaseous by-products which could interfere with the functioning of a delay detonator or other device. In addition to an essential gasless requirement, delay compositions are also required to be safe to handle, from both an explosive and health viewpoint, they must be resistant to moisture and not deteriorate over long periods of storage and hence change in burning characteristics, they must operate reliably over a wide range of temperatures, and they must be adaptable of use in a wide range of delay units within the limitations of space available inside a standard detonator shell or similar device. The numerous delay composition of the prior art have met with varying degrees of success in use and application.
One such prior class of delay compositions intended for use in confinement elements made of lead is that described in U.S. Pat. No. 4,419,154 to Davitt et al. (assigned to CXA Ltd/CXA LTEE) which issued on Dec. 6, 1983. This patent discloses a composition comprising silicon and barium sulfate and optionally including a proportion of particulate red lead (lead tetroxide, Pb3O4) in the amount of 25 to 75% by weight of the composition. The compositions of Davitt which include red lead can be used in confinement elements made of lead to produce intermediate to long timing delays. However, in order to achieve the long timing delays with red read, which is recognized as a strong oxidant, the Davitt compositions have to be prepared with coarse silicon. Such slow burning compositions are difficult to ignite due to the use of such coarse silicon that goes against traditional pyrotechnic principles as taught by Professor Conkling, who stated, in Chemistry of Pyrotechnics, John A. Conkling, Marcel Dekker Inc., 1985, pp 88-89:
Furthermore the slow burning compositions of Davitt et al. with red lead were prepared with a very small ratio of the fuel component (i.e. silicon) which was significantly below the stoichiometric ratio, with the consequence of reducing the energy output of the combustion process. Such formulations would not be robust in various conditions, such as when used in rigid elements as herein described where the thermal conductivity of such confinement materials is significantly higher than lead. Furthermore, when Davitt et al. attempted to use finer silicon with red lead, which would have had the consequence of improving the pyrotechnic performance, significantly faster timing results were obtained (Column 8 of the patent). The only slow burning compositions of Davitt et al. that can be prepared with fine silicon are those without red lead. Thus, according to Davitt et al., compositions with red lead are not ideal for producing long timing delays. For long delay periods, there is therefore a need to find alternative delay compositions.
U.S. Pat. No. 5,147,476 to Beck et al. (assigned to Imperial Chemical Industries PLC), which issued on Sep. 15, 1992, addresses the problem of increasing the robustness of combustion of delay compositions intended for use in rigid metal confining elements to reduce the likelihood of quenching of the combustion. The concept of Beck et al. was to facilitate the combustion of a mixture of silicon and barium sulfate (or other oxidant) by adding small amounts of dispersed metal compounds to serve as reaction-facilitating fluxes (i.e. materials that lower the fusion temperature of the composition, but are otherwise inert). The illustrated metal compounds are salts of alkali metals, oxides of antimony and oxides of vanadium. Beck et al. found that for reliable burning of such a composition, the heat sink effect of the confinement metal element should not be such as to risk quenching of the exothermic reaction (i.e. burning) of the delay composition. However, the delay compositions of the kind disclosed by Beck et al. do not work as well as might be desired, particularly when used for producing long delays. Moreover, the oxides used in these compositions as fluxes are expensive. Beck et al. suggested that additions of red lead oxide or other reactive ingredients that cause a faster rate of burning may be incorporated into the composition, but noted that large loadings of such reactive ingredients may obviate the facilitating role of the flux. Beck et al. therefore recommended that the compositions omit such additional reactive ingredients.
There is therefore a continuing need for a delay composition that can be used reliably when confined in rigid metal confinement elements and yet may be used to produce long delays without unacceptably increasing the lengths of delay units.
An object of the present invention is to provide a delay composition that may be confined within a rigid delay element and yet still undergo reliable ignition and burning capable of producing long timing delays.
Another object of the invention is to provide a delay composition of the stated kind that can be produced easily and inexpensively.
Yet another object of the invention is to provide delay devices that are reliable in that they ignite and burn continuously with a high degree of reliability, even at low temperatures, and provide a reliable long delay period.
Another object of the invention is to provide delay elements and detonators or similar devices capable of providing long delay times while making use of rigid confinement elements for delay compositions.
According to one aspect of the present invention, there is provided a delay composition comprising mixed particles of silicon, barium sulfate and red lead, the red lead being present in an amount of about 3 to 15% by weight, preferably 6 to 12%, and more preferably 9 to 12% by weight, of the composition.
The barium sulfate and silicon components are preferably present in amounts of 40 to 65% by weight and 50 to 25% by weight, respectively, of the total weight of the composition.
The composition preferably also contains a binder causing collections of the particles to bind together in the form of free-flowing granules. The binder is preferably present in amounts of 0.2 to 0.6% by weight of the composition. Suitable binders include solvent-soluble polymers, silica and swelling clays, preferably water-soluble derivatives of cellulose, e.g. carboxymethyl cellulose.
According to another aspect of the invention, there is provided a delay element for a detonator or delay device, comprising an elongated hollow metal tube containing a delay composition comprising mixed particles of silicon, barium sulfate and red lead, the red lead being present in an amount of about 3 to 15% by weight of the composition. The tube is preferably open at both ends, and is preferably made of a rigid metal, most preferably zinc. The delay composition is preferably compressed to a density in the range of 1.8 to 2.2 g/cc, more preferably 1.95 to 2.15 g/cc.
The delay element preferably includes a sealer at one end thereof (the end subject to combustion first). This is may be a type of pyrotechnic composition that forms a slag of material which seals the open end of the delay element. This is desirable as the burn rate of the delay composition may be pressure-dependent and uniform delay times can be achieved when the sealer regulates the pressure within the delay element.
The delay element may also have a starter composition at the same end. The purpose of the starter composition is to generate enough heat to reliably initiate the slow burning delay composition having a high ignition temperature. A single composition may server both the function of a starter composition and of a sealer composition.
According to yet another aspect of the invention, there is provided a delay device, such as a detonator or inline delay device, comprising a detonation signal input, a charge to be detonated by the detonation signal input, and delay element separating said detonation signal input and said charge, the delay element being an element of the type described above.
The detonator 10 has a metallic tubular detonator shell 11 closed at its bottom end and containing a base charge 12 of explosive (e.g. PETN) pressed or cast therein. Immediately above the base charge 12 is a confinement element 14 made of a rigid metal such as zinc, aluminum, steel or brass (preferably zinc). The confinement element 14 contains an initiating charge 15 (e.g. of lead azide) at the lower end of the element, and a delay composition 16 within the delay element above the initiating charge 15. The confinement element and its contents, particularly the delay composition, together form a delay element 14a that is fabricated prior to the assembly of the detonator. A starter element 17, which preferably also acts as a sealer, is located above the delay element. A lower end of a bore in the starter element contains a starter charge 18. An anti-static cup 19 is positioned above the starter element and is designed to receive a lower end of a shock tube 20, which carries the firing signal. A bushing 21 surrounds the lower end of the shock tube 20 where it enters the detonator 10, and the upper end of the detonator shell 11 is crimped to hold the bushing and shock tube in place.
As already noted, the delay compositions of the invention are particularly suitable for creating long delay periods, e.g. more than one second; preferably 1 to 12 seconds, more preferably 1 to 9 seconds, and most preferably 2 to 9 seconds. In order to produce delay elements, detonators, delay devices, and the like, of acceptable length (normally no longer than about 1.5 inches), this means that the compositions should preferably have a burn rate (burn duration) in the range of at least 1500 milliseconds per linear inch, more preferably 2,000 to 7000 milliseconds per linear inch, and most preferably about 4,000 to 6,000 milliseconds per linear inch, and ideally 5,000 to 6,000 milliseconds per linear inch. In contrast, in the experience of the inventor of the present invention, the burn rates of those compositions of U.S. Pat. No. 4,419,154 that contain red lead fall in the range of about 300 to 1500 milliseconds per linear inch when they contain similar amounts of silicon of similar particle size to those of the present invention.
As noted above, the delay compositions of the present invention contain about 3 to 15% by weight of particulate red lead in addition to particles of silicon and barium sulfate. More preferably, the amount of red lead is 6 to 12% by weight, and most preferably it is 9 to 12% by weight. If the percentage of red lead is increased much beyond about 15% by weight, the burn rate becomes excessively fast for long delays, whereas if the percentage is less than 3%, there are no benefits in terms of robustness of combustion and reliability. Although the amount of red lead is much less than previously employed in compositions of this kind (e.g. as disclosed in U.S. Pat. No. 4,419,154), it has been surprisingly found that the amount is sufficient to impart suitable robustness and reliability of combustion to the composition when used in rigid metal confinement elements, without increasing the burn rate unacceptably for long delay uses.
The red lead used in the compositions of the present invention does not act as a flux. Without wishing to be bound by any particular theory of operation, the red lead appears to react with silicon at a low ignition temperature (about 500° C.) and generates heat which facilitates the barium sulfate/silicon combustion reaction whose ignition temperature is high (about 1200° C.).
In the compositions of the invention, the relative proportions of the silicon and barium sulfate are preferably 40 to 65% by weight barium sulfate and 25 to 50% by weight silicon (this corresponds to 45 to 70% by weight of barium sulfate to 30 to 55% by weight of silicon before the addition of the red lead). Preferably, except possibly for a binder (described below), no other materials are present in the composition. While the presence of fluxes can be tolerated, there is no particular advantage to their use in the present invention and their use merely adds cost.
The compositions of the present invention may be prepared simply by dry mixing particles of the essential ingredients in the indicated proportions. In the case of the barium sulfate, the particulate starting material preferably has a specific surface area of typically about 0.8 m2/g (e.g. about 0.75 to 0.85 m2/g). The silicon powder preferably has a specific surface area of about 6 to 8 m2/g. The red lead preferably has a particle size of about 1 to 3 microns.
Although dry mixing of the ingredients is possible, wet mixing is preferred in order to achieve greater homogeneity and because wet mixing allows for the addition of a binder whose function is to agglomerate collections of individual particles into larger free-flowing granules. Suitable binders include solvent-soluble polymers, fine silica and finely ground swelling clays. While polyvinylchloride may be used as a binder, it is more preferable to use a water-soluble form of cellulose, e.g. nitrocellulose or, most preferably, sodium carboxymethyl cellulose (e.g. as manufactured by a European subsidiary of Hoechst and sold under the trademarks TYLOSE and TYLOSE C-600). This material is a sugar-like powder that is dissolved in water and then used for the wet mixing step. Standard methods of wet mixing, granulation and drying may be employed. As noted, the presence of a binder makes it possible to produce the composition in the form of free-flowing granules made up of collections of particles of silicon, barium sulfate, red lead and binder. Free-flowing granules have the ability to flow freely (i.e. without clumping in the nature of dry sand) when poured from one container to another. This ability is highly preferred given that the composition must be introduced into the interior of a rigid confinement element of narrow interior diameter (e.g. typically about 3.35 mm) and then compacted. It is also an advantage that the agglomerated granules each tend to contain particles (of all of the main constituents) with a range of particle sizes. The homogeneity of the resulting composition is therefore very high and there tends to be little separation of large and small particles when the composition is subjected to storage or use over a long period of time. The binder, when present, is preferably contained in the resulting composition (when dry) in an amount in the range of 0.2 to 0.6% by weight, more preferably 0.3 to 0.5% by weight, of the total composition. With amounts more than 0.6% by weight, the granulation process becomes difficult. When the amount is less than about 0.2% by weight, the binding effect may become inadequate.
After formation and drying, the composition is introduced into a rigid metal confinement element, as noted, and is compacted therein, usually by introducing a metal rod into one end of the confinement element and pressing while preventing the composition from escaping from the opposite end of the tubular confinement element. Pressing from both ends may, of course, also take place. The resulting composition in the confinement element preferably has a density falling within the range of 1.90 to 2.20 g/cc, most preferably 1.95 to 2.15 g/cc. Compaction to a suitable density is important to ensure reliable propagation of combustion, although the desired density may vary somewhat from composition to composition.
The presence of red lead in the delay composition in the indicated amounts does not alter the essential character of the Si/BaSO4 mixture as a slow delay composition (i.e. it does not substantially speed up or slow down the burning rate) but its presence does impart to the composition resistance to quenching caused by the heat-sink effect of the tubular metal confinement element, so that the composition is effective in rigid elements such as zinc elements.
Rigid elements containing the compositions of the invention have shown themselves in tests to be effective as reliable, reproducible delay elements within the confines of standard detonator shell dimensions used in the art while providing delays of more than one second, e.g. from about 2 seconds to optimally 9 seconds or even higher. The rigid elements tested were in fact zinc elements, being the presently preferred metal for rigid confinement elements, but may of course have been made of another suitable material, e.g. aluminum, steel or brass.
In the most preferred forms, the delay compositions of the invention consists only of silicon, barium sulfate, red lead and optionally a binder in the indicated amounts, i.e. there are no other materials such as oxidants and fluxes, except for incidental or adventitious minor impurities or ingredients.
The invention will now be further described by way of the following Examples which are illustrative of delay compositions according to the invention, and of detonators and delay devices, also according to the invention. The Examples should, not be taken as limiting the broad scope of the invention as defined by the accompanying claims.
Small quantities (10 g samples) of dry mixed BaSO4/Silicon compositions were prepared containing 3%, 5%, 7%, and 9% by weight of Pb3O4.
Rigid zinc tubular confinement elements having bore diameters of 3.35 mm were loaded with each of the compositions, as well as a control containing no Pb3O4. The loaded rigid confinement elements were assembled into detonators for testing. It was found necessary to use a Pb3O4/Si starter composition on top of the BaSO4/Silicon/Pb3O4 mixture for reliable ignition. A pyrotechnic sealer element was placed on top of the starter element. These detonators were assembled as shocktube (non-electric) detonators and tested for average delay timing and coefficient of variation (CV). The results of the tests are shown in Table 1 below. The 5% and the 7% Pb3O4 samples showed a noticeable improvement in timing accuracy compared to the control containing no Pb3O4.
The robustness of propagation of the composition was measured by testing composition ignition at −40° C. Rigid confinement elements of the above kind were prepared containing BaSO4/Silicon and 6% Pb3O4. As before, these elements were assembled into non-electric detonators. Testing of the detonators after exposure to a temperature of −40° C. for 48 hours showed reliable functioning with timing accuracy as good as a control sample tested at room temperature, while ⅘ detonators made with BaSO4/Silicon failed to propagate through the delay column. During the course of ambient temperature testing of rigid elements containing BaSO4/Silicon and no Pb3O4, a number of failures (⅖) were recorded where the BaSO4/Silicon column failed to propagate. These failures serve to show that the addition of a small amount of Pb3O4 does indeed impart a significant improvement to this composition without substantially increasing the combustion propagation rate.
It has thus been demonstrated that the addition of a small amount of Pb3O4 to a BaSO4/Silicon pyrotechnic mixture results in a new improved composition which show improved performance in rigid elements.
production mix sample of standard barium sulfate/silicon composition containing 45% by weight of silicon and 55% by weight of barium sulfate (referred to as Y composition) was first divided in 5 small mixes of 10 g each in a small Velostat™ (electrically conductive polymer) container. The first sample was left intact as a reference control sample while an addition of 3%, 5%, 7%, and 9% of red lead was made in the subsequent mixes. Conductive rubber balls were added to the mixes to help the ingredients to mix together during tumbling of the Velostat™ containers.
A 1 Kg batch of a modified standard barium sulfate/silicon composition (Y composition) having 6% red lead in it was prepared. The respective mass ratios for the ingredients were 51.7% of BaSO4 (0.8 m2/g surface area), 42.3% Silicon (milled for 12 hours) and 6% of Pb3O4. Although the red lead was added to the medium from the start to ensure a good dispersion of particles, a regular wet mixing process for standard barium sulfate/silicon composition was followed.
The compositions (both of the dry mix and the wet mix) were tested for ignition by friction. None of the compositions containing red lead showed signs of ignition when tested for friction sensitivity using a 1.33 kg steel torpedo sliding with 30° angle from 30 inch height.
The differential thermal analysis (DTA) of a composition containing no red lead and a composition containing 5% red lead showed that the presence of red lead in the standard barium sulfate/silicon composition reduced the ignition point of the composition, which facilitated ignition of the powder.
A zinc confinement element was weighed, placed in a holder and a delay composition of the invention was poured into its cavity and pressed at the desired pressure in many small increments until full. The element was weighed again and the powder content recorded. The reliability (standard deviation SD) of powder content in elements was found good for both element lengths evaluated, as shown in Table 2 below.
Delay Timing “vs” Red Lead Content in Barium Sulfate/Silicon Compositions.
The graph of
The delay timings were determined in ORICA® 2.9 inch detonator shell having a 9.3 mm (0.362″) zinc confinement element as main and a regular starter and sealer from drawn lead tube.
Deviation in Delay Times “vs” Red Lead Content in Barium Sulfate/Silicon Compositions.
From previous timing results, the graph of
It can be seen that any barium sulfate/silicon mix that had the presence of red lead in it produced a better timing accuracy than the control sample containing no red lead.
The sample size for the above results was only 5 detonators per mix, so, in order to confirm the validity of the delay timing obtained, the mix with 5% Red Lead was further loaded in 30 zinc confinement elements and in two different element lengths. They were tested for timing accuracy in ORICA® detonator shells and results compared with those obtained by others for this specific lot of the standard barium sulfate/Si composition. The results are shown in Table 3 below (in which SD stands for standard deviation).
In lead elements, the following provided the following timing results for this lot of the standard composition:
In order to define the proper range for powder loading in rigid zinc confinement elements, the 5% red lead content mix was loaded in the 9.30 mm zinc confinement elements, pressed at different pressure and fired. Although all detonators made with elements loaded at 28 Kpsi failed to ignite, the results illustrated in the graphs of
Powder Density “vs” Loading Pressure
The density of the delay composition loaded in zinc confinement elements and at different pressure was measured for both 5% and 7% red lead mixes that showed the best timing performances. The results are shown in the graph of
An evaluation was made to measure the timing shift between +20° C. and −40° C. on various detonator designs in order to demonstrate the advantage of adding some red lead in barium sulfate/Si composition with either the drawn lead or rigid zinc confinement element technology. The results are shown in the graph of
Note: All main elements (lead or zinc) were prepared to be in the same order of delay timing, between 2800 ms and 3000 ms.
In the graph of FIG. 8:—
Although the ORICA® detonator design showed a better timing stability, no failure to ignite was observed on more than 100 detonators fired at −40° C. and having a main element made of zinc.
In this Example, the maximum quantity of red lead that can be added to the barium sulfate/Si composition for a long delay period detonator is identified and the resistance to shock stop (failure of a detonator due to the shock from an adjacent explosion) of such systems is characterized for both, drawn lead and rigid confinement element technology.
All mixes used for the delay timing evaluation are from small dry mixes where red lead was added in various quantities in barium sulfate/Si. The ingredients were put together and tumbled in small Velostat pots with conductive rubber balls.
The mixes used for the shock resistance evaluation were made wet mix in batch of 700 g.
Friction Sensitivity
A steel torpedo of 1.33 Kg weight slides on a sample of powder from 30 inch height and 30° angle.
No ignition observed in ten trials when the 12% red lead content mix was tested for friction sensitivity.
Other powder samples containing less than 9% of red lead were also tested for friction sensitivity and did not show any signs of ignition either.
In order to avoid sympathetic detonations during shock stop testing, the lead azide charge (110 mg) was pressed inside the zinc element cavity. The rest of the cavity was filled with the delay powder. A regular starter (red lead+silicon 75:25 by weight) and sealer (sealer with a small bore element filled with red lead+silicon 63:37 by weight) was pressed on top of the rigid element and a sealer crimp applied.
A low entropy plastic disc (LE disc) was put on top of the lead azide charge for those detonators made with the main delay elements from a drawn lead rod.
Delay Timing
The graphs of
A drum test was performed on composition Y and modified comp. Y containing 6% and 12% of Red Lead. The LP detonators from DNES (7000 ms) were also tested for shock resistance.
The shock pressure test was performed at 14000 psi (Position #11 in template).
Test 1 Main Delay Composition in Rigid Zinc Elements
Test 2 Main Delay Composition in Drawn Lead Elements
This Example relates to the use of a binder (carboxymethyl cellulose) in the preparation of the delay compositions of the invention.
Batches (500 g each) of delay compositions were made from barium sulfate (Type N, having a specific surface area of 0.8 m2/g), silicon (2.6 microns in size, from SKW powder company, ground for 12 hours), red lead and sodium carboxymethyl cellulose (TYLOSE® C-600) using a Waring blender. The batches were formed by dissolving a powder of the carboxymethyl cellulose in 200 ml water in a mixing vessel over two minutes for complete dissolution, adding the red lead and mixing for about one minute, adding half of the quantity of barium sulfate and silicon and mixing for two minutes, then adding the remainder of the silicon and barium sulfate and mixing for a further 2 minutes. The ratio of water to dry ingredients was 40%. The batches contained 6%, 9% or 12% red lead and amounts of TYLOSE from 0.3 to 0.6% by weight. The ratio of barium sulfate to silicon (discounting other ingredients) was about 55:45 by weight). The mixtures were then dried for a few hours and manually granulated behind a shield through a 20 Tyler mesh sieve. The resulting granules were found to flow very well (i.e. freely), e.g. when poured from one container to another.
The granulated mixtures were loaded into rigid zinc confinement elements by placing the zinc elements in a holder and scooping the composition and pouring it into the element cavity and pressing at the required pressure for proper density. This was done in increments until the element was full. In all cases, the incremental loading was 5.0 mm (pressed). This corresponded to a volume of 90 mg powder for each increment. A subsequent test with incremental loading of 3.0 mm (50 mg of powder) produced an even better coefficient of variation (CV) for delay timing indicating that the procedure benefits by having many small loading increments for better reliability. It is to be noted that the loading pressure has to be reduced in order to keep the same powder loading density with smaller increments. The results are shown in Table 4 below.
Detonators were constructed with the rigid zinc confinement elements. These detonators contained a starter comprising a mixture of red lead and fine silicon (so-called E starter) and a sealer (so-called H sealer) prepared with a small bore element made from drawn lead rod containing a mixture of red lead and very fine silicon. All the results were obtained using ORICA® detonator shells.
Wet mixes with 6%, 9% and 12% red lead and 0.5% TYLOSE® in Composition Y were made and assessed in 30 mm zinc elements for detonator timing.
The 6% red lead mix showed 20% detonator failures at room temperature. The 9% red lead mix did not show detonator failure at room temperature, but 50% detonators failed when fired at low temperature (−40° C.). The 12% red lead mix showed no failures at −40° C. and was selected for the following extended characterization.
Delay Time vs. Length of Element
The burn rate of the composition in zinc elements was found to be very linear, even at low temperatures (−40° C.). The graph of
Delay Time vs. Loading Pressure
The graph of
Delay Time vs. TYLOSE Content
The graph of
A stress test was widely used in this evaluation in which the detonator was frozen in ice for 16 to 24 hours and fired within one minute. In order to give confidence to this test
The powder loading density is an important factor for the composition. This was found to be particularly true when detonators were fired at low temperature.
The graph of
The graph of
The graph of
long period detonators.
The graph of
The pressed density of composition BaSO4/Si/Pb3O4 in 44 mm length zinc elements versus TYLOSE C-600 content is shown in
The pressed density of composition BaSO4/Si/Pb3O4/Tylose in zinc elements of 44 mm length is shown in
A drum test was performed on the following detonator samples:
ORICA® LP 19
DNES® 7000 ms
The donor detonator was an ORICA® LP 10 (3500 ms delay) for all tests.
The shock pressure test was performed in “cooking mode” meaning that both detonators, the donor and the target, were fired simultaneously. The results are shown in Table 5 below:
The above results show that at least a preferred composition made of barium sulfate/silicon/red lead (12 hours ground)/TYLOSE® C-600 with respective mass ratios of 48/39.7/12/0.3% loaded into rigid zinc elements at a density of 2.08 g/cc±0.05 g/cc was found to have equal, if not superior, detonator performance compared to regular long delay detonators using lead confinement elements.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2,340,523 | Mar 2001 | CA | national |
This application is a division of applicant's copending U.S. patent application Ser. No. 09/895,334, filed Jul. 2, 2001.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11977921 | Oct 2007 | US |
| Child | 13302186 | US | |
| Parent | 09895334 | Jul 2001 | US |
| Child | 11977921 | US |