This invention relates to prosthodontics devices in the form of dental frameworks, in particular to methods of making and repairing dental frameworks such as dentures including tooth prostheses, in particular by means of ultrasonic welding. The invention also relates to methods and apparatus for forming dental prosthetic items such as dental frameworks, repair portions for dental frameworks, tooth prostheses and the like. In particular, aspects of the invention relate to methods and apparatus for compressive moulding of PAEK (polyaryletherketone) to form prosthodontic items such as repair portions.
Prosthodontics is concerned with treatments to address missing or deficient teeth in patients. A type of prosthodontic device is arranged to a replace a patient's missing teeth and contiguous tissue with a prosthesis which is designed to be removed by a wearer, for example nightly. Such removable prostheses, also referred to as dentures herein, may comprise removable partial or whole prosthodontic devices which cooperate with a patient's gums and palate, and with natural remaining teeth (or with other implants) to define partial or complete prosthetic dentition.
Such dentures also may also include teeth prostheses which are located in the dental framework in order to form a denture which may be removably worn by a patent with hard wearing prosthetic teeth having a natural appearance.
There are many different types of prosthodontic devices and methods of making such devices. For example, removable prosthodontic devices may comprise a metal framework (e.g. of cobalt/chrome) in combination with cast or moulded plastics parts. However, disadvantageously, such devices may be heavy, difficult to manufacture to produce an accurate mouth-fit, and have high stiffness and poor load distribution, leading to patient discomfort. Additionally, use of metal may result in relatively high levels of metal ions being introduced into patients' bodies over time. Furthermore, some patients are allergic to metals used in the devices. In addition, manufacture of existing prosthodontic devices, or those which include a combination of metal and plastics, can be time-consuming; and such devices may be aesthetically unattractive.
A problem with tooth prostheses is to provide a tooth prosthesis which is natural in appearance, is hard wearing, is easily formed into a desired shape and yet which is also light and easily attached to either a dental framework or directly to the jaw of a patient. Typically, tooth prostheses have been made from a core of metal or ceramic material, or from a cast resin material such as acrylic resin, prepared from in-situ reaction of monomers upon moulding, with a dental veneer bonded to the outer face of the core in order to form a crown. It is important that the dental veneer is strongly bonded to the underlying core and remains strongly bonded even after prolonged immersion in the fluids found in the mouth.
The presence of metals, or of trace amounts of reactive monomers, in the mouth of a patient are undesirable. It is also desirable to have cores for tooth prostheses which are easily shaped in-situ in a dental surgery, yet which may be strongly bonded to a dental veneer in order to form a crown. It is also desirable to have tooth prostheses which are easily bonded to a dental framework in order to make a removable denture. It is also desirable to have tooth prostheses which are not so excessively rigid that they cause risk of damage to opposing teeth of a patient in use. It is also desirable to have tooth prostheses which are of low weight.
It has been found that PAEK polymer, also including PEEK (polyetheretherketone) polymer, is useful for the formation of both dental frameworks and tooth prostheses. Prosthodontic devices formed from PAEK polymers are the subject of a number of co-pending applications. Typically, the preparation of prosthodontic items from PAEK may require the use of computer-aided machining to prepare the item by shaping a block of polymeric PAEK, for instance by means of computer-aided milling.
For rapid repair and formation of prosthodontic items, for instance to provide temporary and/or rapid repair to a patients dental features, it is desirable to be able to provide methods and apparatus that may enable a dentist to rapidly prepare prosthodontic items, either with or without need for recourse to complex computer-aided milling apparatus, for instance whilst a patient is waiting, on site, for a repair to be effected. The use of reactive monomers to provide a flowable resin which can be moulded into the shape of a dental prosthesis, and subsequently solidified by polymerisation of the monomers, is undesirable as it has the disadvantage that it entails the handling of reactive monomers and there is the risk of unreacted monomer remaining after solidification of the dental prosthetic item.
It is one aim of the present invention, amongst others, to provide tooth prostheses, dentures and methods which address, obviate or at least partially mitigate at least some of the problems or disadvantages in the prior art, whether identified herein or elsewhere. In particular, it is one aim of the invention, amongst others, to provide a method of joining portions of a dental framework to form an integrated dental framework. It is an aim of the present invention, amongst others, to provide methods and apparatus for forming easily, safely and rapidly forming prosthodontic items which address, obviate or at least partially mitigate at least some of the problems or disadvantages in the prior art, whether identified herein or elsewhere. For instance, it is an aim of exemplary embodiments of the invention to provide methods and apparatus for forming shaped prosthodontic items in situ in a dental workshop or consulting room. Another aim of the invention is to provide apparatus and methods for forming dental prosthodontic items in situ which are be compatible with, and easily joined to, existing dental prosthodontic items comprising PAEK but perhaps formed by other means, such as by milling from a block of PAEK-comprising composition or by moulding.
According to the present invention there are provided apparatus, dental frameworks and methods as set forth in the appended claims. Other features of the invention will be apparent from the dependent claims, and the description which follows.
Throughout this specification, the term “comprising” or “comprises” means including the component(s) specified but not to the exclusion of the presence of other components. The term “consisting essentially of” or “consists essentially of” means including the components specified but excluding other components except for materials present as impurities, unavoidable materials present as a result of processes used to provide the components, and components added for a purpose other than achieving the technical effect of the invention. Typically, when referring to compositions, a composition consisting essentially of a set of components will comprise less than 5% by weight, typically less than 3% by weight, more typically less than 1% by weight of non-specified components.
The term “consisting of” or “consists of” means including the components specified but excluding other components.
Whenever appropriate, depending upon the context, the use of the term “comprises” or “comprising” may also be taken to include the meaning “consists essentially of” or “consisting essentially of”, and also may also be taken to include the meaning “consists of” or “consisting of”.
References herein such as “in the range x to y” are meant to include the interpretation “from x to y” and so include the values x and y.
The optional features set out herein may be used either individually or in combination with each other where appropriate and particularly in the combinations as set out in the accompanying claims. The optional features for each aspect or exemplary embodiment of the invention, as set out herein, are also applicable to any other aspects or exemplary embodiments of the invention, where appropriate. In other words, the skilled person reading this specification should consider the optional features for each exemplary embodiment of the invention as interchangeable and combinable between different aspects or exemplary embodiments.
A first aspect of the invention provides a method of joining first and second portions of a dental framework to form an integrated dental framework,
wherein the first and second portions of dental framework are each independently formed of a composition comprising a polymeric material,
wherein the polymeric material comprises a repeat unit of formula (I):
wherein t1 and w1 independently represent 0 or 1 and v1 represents 0, 1 or 2;
the method comprising:
providing a male member on a first joint surface of the first portion and a female member on a second joint surface of the second portion, wherein the male and female members are arranged to mate together to hold the first and second portions together with the first and second joint surfaces mutually inter-engaged in the integrated dental framework; bringing the first and second joint surfaces into inter-engagement with the male and female members mated together; and
welding the first and second joint surfaces together by ultrasonic welding.
The composition, may consist or consist essentially of the polymeric material, or may include, for instance from 60 to 100%, say from 75 to 100% of the polymeric material, with from 0 to 40%, say from 0 to 25% of other materials. The composition may include, for example colourants (e.g. pigments, ceramics, metal oxides (e.g. titanium dioxide)) or fillers (for example reinforcing or wear enhancing fillers or fibres, bioactive fillers such as bioglasses, soluble glasses, zeolites containing antibacterial agents such as silver ions, nanosilver, ceramics such as hydroxyapatite (HA) or substituted HA or treatment agents such as antibiotic doped HA or compounds favourable to the gingiva, diagnostic agents such as radiopaque fillers such as barium sulphate, aesthetic fillers such as reflective agents and light refracting agents, fillers conveying some taste or flavour altering or enhancing effect or breath freshening effect). The composition may include, for instance, 0-10 wt %, suitably 0-6 wt % of colourants. Colourants may be selected so the composition is white. Colourants may be employed so that the colour is graduated. In one embodiment, the composition includes no colourant. When a filler is included in the composition, it may suitably be included to improve the mechanical properties and/or bonding characteristics and/or biological acceptability of the composition. However, it has been found that cores for tooth prostheses with excellent mechanical properties can be made without requiring addition of filler. Preferably, the composition comprises at least 80 wt %, at least 90 wt % or at least 94 wt % of the polymeric material. The polymeric material may be the same polymeric material for each of the first and second portions, or may be a different polymeric material. Preferably, the same polymeric material such as PEEK homopolymer is used as polymeric material in each of the first and second portions.
The polymeric material preferably consists essentially of a repeat unit of formula I. Preferred polymeric materials comprise (or consist essentially of) a repeat unit wherein t1=1, v1=0 and w1=0; t1=0, v1=0 and w1=0; t1=0, w1=1, v1=2; or t1=0, v1=1 and w1=0. More preferred polymeric materials comprise (or consist essentially of) a repeat unit wherein t1=1, v1=0 and w1=0; or t1=0, v1=0 and w1=0. The most preferred polymeric material comprises (or consists essentially of) a repeat unit wherein t1=1, v1=0 and w1=0: in other words a homopolymeric polyetheretherketone.
In preferred embodiments, the polymeric material is selected from polyetheretherketone, polyetherketone, polyetherketoneetherketoneketone and polyetherketoneketone. In a more preferred embodiment, the polymeric material is selected from polyetherketone and polyetheretherketone. In another preferred embodiment, the polymeric material is polyetheretherketone such as a homopolymer polyetheretherketone.
The polymeric material may have a Notched Izod Impact Strength (specimen 80 mm×10 mm×4 mm with a cut 0.25 mm notch (Type A), tested at 23° C., in accordance with ISO180) of at least 4 KJm−2, preferably at least 5 KJm−2, more preferably at least 6 KJm−2. The Notched Izod Impact Strength may be less than 10 KJm−2, suitably less than 8 KJm−2. The Notched Izod Impact Strength may be at least 3 KJm−2, suitably at least 4 KJm−2, preferably at least 5 KJm−2. The impact strength may be less than 50 KJm−2, suitably less than 30 KJm−2.
The polymeric material suitably has a melt viscosity (MV) of at least 0.06 kNsm−2, preferably has a MV of at least 0.09 kNsm−2, more preferably at least 0.12 kNsm−2, or at least 0.15 kNsm−2. Advantageously, the MV may be at least 0.35 kNsm−2 and/or at least 0.40 kNsm−2. An MV of 0.45 kNsm−2 has been found to be particularly advantageous in the manufacture of accurate, strong dental prosthetics.
The polymeric material may have a MV in the range 0.09 to 0.5 kNsm−2, preferably in the range 0.14 to 0.5 kNsm−2, more preferably in the range 0.4 to 0.5 kNsm−2.
The polymeric material may have a tensile strength, measured in accordance with ISO527 (specimen type 1b) tested at 23° C. at a rate of 50 mm/minute of at least 20 MPa, preferably at least 60 MPa, more preferably at least 80 MPa. The tensile strength is preferably in the range 80-110 MPa, more preferably in the range 80-100 MPa.
The polymeric material may have a flexural strength, measured in accordance with ISO178 (80 mm×10 mm×4 mm specimen, tested in three-point-bend at 23° C. at a rate of 2 mm/minute) of at least 50 MPa, preferably at least 100 MPa, more preferably at least 145 MPa. The flexural strength is preferably in the range 145-180 MPa, more preferably in the range 145-164 MPa.
The polymeric material may have a flexural modulus, measured in accordance with ISO178 (80 mm×10 mm×4 mm specimen, tested in three-point-bend at 23° C. at a rate of 2 mm/minute) of at least 1 GPa, suitably at least 2 GPa, preferably at least 3 GPa, more preferably at least 3.5 GPa. The flexural modulus is preferably in the range 3.5-4.5 GPa, more preferably in the range 3.5-4.1 GPa.
The polymeric material may be amorphous or semi-crystalline. It is preferably crystallisable. It is preferably semi-crystalline. The level and extent of crystallinity in a polymer is preferably measured by wide angle X-ray diffraction (also referred to as Wide Angle X-ray Scattering or WAXS), for example as described by Blundell and Osborn (Polymer 24, 953, 1983). Alternatively, crystallinity may be assessed by Differential Scanning calorimetry (DSC).
The level of crystallinity of the polymeric material may be at least 1%, suitably at least 3%, preferably at least 5% and more preferably at least 10%. In or preferred embodiments, the crystallinity may be greater than 25%. It may be less than 50% or less than 40%. Preferably the prosthodontic device includes a framework having the aforementioned levels of crystallinity.
The main peak of the melting endotherm (Tm) of the polymeric material (if crystalline) may be at least 300° C.
For the polymeric material, it is preferred that t1=1, v1=0 and w1=0.
For the method of the first aspect of the invention, the welding the first and second joint surfaces together by ultrasonic welding may comprise welding the male and female members together by ultrasonic welding.
The polymeric material in the composition of the first portion may be the same polymeric material as the polymeric material in the composition of the second portion, or, alternatively, the polymeric material in the composition of the first portion may be a different polymeric material to the polymeric material in the composition of the second portion. However, it is to be understood that even when the polymeric materials of the different portions are different polymeric materials, they are still each individually polymeric materials according to formula (I) as set out hereinbefore.
Preferably, t1=1, v1=0 and w1=0 for the polymeric material in the composition of the first portion, or the second portion, or for both portions (i.e. homopolymeric polyetheretherketone).
The first and second joint surfaces may be arranged to hinder rotation of the second portion about the male member of the first portion when the first and second joint surfaces are inter-engaged.
For instance, one way of achieving this may be for two or more male members to be provided on the first joint surface and two or more female member to be provided on the second joint surface of the second portion, wherein the male and female members may be arranged to mate together to hold the first and second portions together with the first and second joint surfaces mutually inter-engaged in the integrated dental framework.
The first portion may be a replacement portion for repair of a broken dental framework and the second portion may be a remnant portion of the broken dental framework. In other words, the method of the first aspect of the invention may be used for repair of a pre-used dental framework which has already been fitted to a patient's mouth and worn by the patient, when the dental framework has broken in use. A major remnant portion of the broken dental framework may be re-used and welded to a replacement portion, using the method of the first aspect of the invention, in order to provide a repaired dental framework.
In order to achieve this, the female member may formed by forming a hole in the remnant portion prior to bringing the first and second joint surfaces into inter-engagement with the male and female members mated together. The male member may be formed as a unitary part of the first joint surface. The second joint surface may comprises fracture surface of the remnant portion and the first joint surface may shaped to engage with the fracture surface when the first and second joint faces are inter-engaged. In other words, the first joint surface may be made to match the fracture surface on the remnant portion of the broken dental framework. This may be achieved through computer-aided mapping of the fracture surface and subsequent computer-aided machining of the first joint surface of the repair portion. In another embodiment, the fracture surface may be moulded, and the first joint surface prepared by moulding. The polymeric material of formula (I) is particularly suitable for moulding as set out hereinafter.
In the event that the fracture surface is not a suitable shape for use as a second joint surface, for instance because it contains sharp features or because the resulting joint would be prone to further fracture, then the fracture surface may be machined, for instance using milling such as computer-aided milling, in order to provide the remnant portion with a suitable second joint surface including a female member suitable for use in the method of the first aspect of the invention.
The repair portion may be prepared by machining from a block or blank of a composition comprising or consisting essentially of the polymeric material according to formula (I), or may be moulded therefrom, or a combination of moulding and machining may be used, for instance with the repair portion moulded to fit the patient's mouth features, but with the first joint surface formed by machining, such as computer-aided machining or milling, in order to provide an accurate fit to the second joint surface of the remnant portion (which may be a fracture surface or a modified fracture provided with a female member). However, in a preferred embodiment, the repair portion may be formed, at least in part using the method and/or apparatus of the fourth and sixth aspects of the invention as set out hereinafter.
The method of the first aspect of the invention may comprise forming the first and second portions from first and second moulds prepared from impressions from a patient's mouth. The first and second moulds are prepared from separate first and second impressions taken from the patient's mouth. This gives the advantage of enabling the preparation of a complex dental framework from partial moulds, so that a large mould, leading to potential for choking or a high level of discomfort for the patient during moulding, is not required in the patient's mouth. Instead, separate, smaller moulds may be used for different portions of the dental framework, then the method of the invention may be used to form an integrated dental framework without putting the patient through an uncomfortable moulding process.
In the method according to the first aspect of the invention, the integrated dental framework may comprise at least one further portion of dental framework which is independently formed of a composition comprising a polymeric material, wherein the polymeric material comprises a repeat unit of formula (I):
wherein t1 and w1 independently represent 0 or 1 and v1 represents 0, 1 or 2; with the method comprising: providing at least one further joint surface on each further portion which is arranged to inter-engage with a respective further complementary joint surface on the first, second or another portion of the integrated dental framework, providing a further male member on one of the further joint surface and the respective further complementary joint surface and a further female member on the other of the further joint surface and the further complementary joint surface; wherein the further male and female members are each arranged to mate together to hold each further joint surface and the respective further complementary joint surface together, mutually inter-engaged in the integrated dental framework; bringing each further joint surface and respective further complementary joint surface into inter-engagement with their male and female members mated together; and welding the further joint surface and its respective further complementary joint surface together by ultrasonic welding.
In other words, the method of the first aspect of the invention may be applied to a plurality (two or more, such as three, or more or four or more) of portions of dental framework being ultrasonically welded together in order to provide an integrated dental framework.
The polymeric material in the composition of each further portion may be the same polymeric material as the polymeric material in the composition of the first and second portions, or may be a different polymeric material, but it should be understood that each portion is to be of a composition comprising a polymeric material according to formula (I).
For the method of the first aspect of the invention, the, or each, male member may be cylindrical or frustoconical in shape. Typically, the diameter or maximum width measured through a central long axis of the male member will be 1 to 7 mm, say from 2 to 6 mm.
The male member may comprise a proximal platform arranged to abut an outer portion of its respective female member when the male and female members are mated together. By “proximal” is meant adjacent or nearest to the first joint surface of which the males member forms a part. By “outer portion” is meant the portion of the female member directed from the second joint surface towards the first joint surface when the male and female members are mated together.
Suitably, walls forming the joint surfaces or the male or female members should have a thickness of at least 1 mm of the composition comprising or consisting essentially of the polymeric material of formula (I).
The ultrasonic welding may be suitably carried out using a sonotrode under manual or computer control. The sonotrode preferably has a terminal welding surface which is circular or substantially equilaterally polygonal in shape. The terminal welding surface may be planar or curved and may be flat (i.e. smooth) or roughened.
The sonotrode may comprise a terminal welding surface having a maximum width of 6 mm or less. The maximum width is measured through the centroid of the terminal welding surface.
The preferred or optional features set out in relation to the first aspect of the invention are applicable, where appropriate, to the other aspects of the invention set out below, and should be considered as additionally disclosed in relation to these aspects in order to avoid repetition.
A second aspect of the invention provides an integrated dental framework obtained or obtainable by the method of the first aspect of the invention.
A third aspect of the invention provides an integrated dental framework comprising at least two interconnected portions of dental framework, wherein each portion of dental framework is independently formed of a composition comprising a polymeric material, wherein the polymeric material comprises a repeat unit of formula (I):
wherein t1 and w1 independently represent 0 or 1 and v1 represents 0, 1 or 2; and
wherein each portion is connected to at least one other portion at a joint;
wherein each joint comprises a male member on a first joint surface of one portion and a female member on a second joint surface of an adjacent portion;
wherein the respective male and female members at the joint are arranged to mate together to hold the first and second portions together with the first and second joint surfaces mutually inter-engaged at the joint; and
wherein the first and second joint surfaces are at least partly fused together at the joint.
A fourth aspect of the invention provides a method for forming a dental prosthetic item, the method comprising:
wherein t1 and w1 independently represent 0 or 1 and v1 represents 0, 1 or 2;
The composition, may consist or consist essentially of the polymeric material, or may include, for instance from 60 to 100%, say from 75 to 100% of the polymeric material, with from 0 to 40%, say from 0 to 25% of other materials. The composition may include, for example colourants (e.g. pigments, ceramics, metal oxides—such as titanium dioxide) or fillers (for example reinforcing or wear enhancing fillers or fibres, bioactive fillers such as bioglasses, soluble glasses, zeolites containing antibacterial agents such as silver ions, nanosilver, ceramics such as hydroxyapatite (HA) or substituted HA or treatment agents such as antibiotic doped HA or compounds favourable to the gingiva, diagnostic agents such as radiopaque fillers such as barium sulphate, aesthetic fillers such as reflective agents and light refracting agents, fillers conveying some taste or flavour altering or enhancing effect or breath freshening effect). The composition may include, for instance, 0-10 wt %, suitably 0-6 wt % of colourants. Colourants may be selected so the composition is white. Colourants may be employed so that the colour is graduated. In one embodiment, the composition includes no colourant. When a filler is included in the composition, it may suitably be included to improve the mechanical properties and/or bonding characteristics and/or biological acceptability of the composition. However, it has been found that cores for tooth prostheses with excellent mechanical properties can be made without requiring addition of filler. Preferably, the composition comprises at least 80 weight %, at least 90 weight % or at least 94 weight % of the polymeric material.
The polymeric material preferably consists essentially of a repeat unit of formula I. Preferred polymeric materials comprise (or consist essentially of) a repeat unit wherein t1=1, v1=0 and w1=0; t1=0, v1=0 and w1=0; t1=0, w1=1, v1=2; or t1=0, v1=1 and w1=0. More preferred polymeric materials comprise (or consist essentially of) a repeat unit wherein t1=1, v1=0 and w1=0; or t1=0, v1=0 and w1=0. The most preferred polymeric material comprises (or consists essentially of) a repeat unit of Formula (I) wherein t1=1, v1=0 and w1=0: in other words homopolymeric polyetheretherketone.
In preferred embodiments, the polymeric material is selected from polyetheretherketone, polyetherketone, polyetherketoneetherketoneketone and polyetherketoneketone. In a more preferred embodiment, the polymeric material is selected from polyetherketone and polyetheretherketone. In another preferred embodiment, the polymeric material is polyetheretherketone such as homopolymeric polyetheretherketone. As used herein, the term PAEK may refer to any of these materials.
The preferred or optional parameters or characteristics set out in relation to the polymeric material, set out herein, are applicable to the material either before or after it has been moulded in accordance with the method of the invention, as part of, or all of the thermoplastic composition.
The polymeric material may have a Notched Izod Impact Strength (specimen 80 mm×10 mm×4 mm with a cut 0.25 mm notch (Type A), tested at 23° C., in accordance with ISO180) of at least 4 KJm−2, preferably at least 5 KJm−2, more preferably at least 6 KJm−2. The Notched Izod Impact Strength may be less than 10 KJm−2, suitably less than 8 KJm−2. The Notched Izod Impact
Strength may be at least 3 KJm−2, suitably at least 4 KJm−2, preferably at least 5 KJm−2. The impact strength may be less than 50 KJm−2, suitably less than 30 KJm−2.
The polymeric material suitably has a melt viscosity (MV) of at least 0.06 kNsm−2, preferably has a MV of at least 0.09 kNsm−2, more preferably at least 0.12 kNsm−2, or at least 0.15 kNsm−2. Advantageously, the MV may be at least 0.35 kNsm−2 and/or at least 0.40 kNsm−2. An MV of 0.45 kNsm−2 has been found to be particularly advantageous in the manufacture of strong prosthodontics. MV is suitably measured using capillary rheometry operating at 400° C. at a shear rate of 1000 s−1 using a tungsten carbide die, 0.5 mm×3.175 mm, as described hereinbefore.
The polymeric material may have a MV of less than 1.00 kNsm−2, preferably less than 0.5 kNsm−2.
The polymeric material may have a MV in the range 0.09 to 0.5 kNsm−2, preferably in the range 0.14 to 0.5 kNsm−2, more preferably in the range 0.4 to 0.5 kNsm−2.
The polymeric material may have a tensile strength, measured in accordance with ISO527 (specimen type 1b) tested at 23° C. at a rate of 50 mm/minute of at least 20 MPa, preferably at least 60 MPa, more preferably at least 80 MPa. The tensile strength is preferably in the range 80-110 MPa, more preferably in the range 80-100 MPa.
The polymeric material may have a flexural strength, measured in accordance with ISO178 (80 mm×10 mm×4 mm specimen, tested in three-point-bend at 23° C. at a rate of 2 mm/minute) of at least 50 MPa, preferably at least 100 MPa, more preferably at least 145 MPa. The flexural strength is preferably in the range 145-180 MPa, more preferably in the range 145-164 MPa.
The polymeric material may have a flexural modulus, measured in accordance with ISO178 (80 mm×10 mm×4 mm specimen, tested in three-point-bend at 23° C. at a rate of 2 mm/minute) of at least 1 GPa, suitably at least 2 GPa, preferably at least 3 GPa, more preferably at least 3.5 GPa. The flexural modulus is preferably in the range 3.5-4.5 GPa, more preferably in the range 3.5-4.1 GPa.
The polymeric material may be amorphous or semi-crystalline. It is preferably crystallisable. It is preferably semi-crystalline. The level and extent of crystallinity in a polymer is preferably measured by wide angle X-ray diffraction (also referred to as Wide Angle X-ray Scattering or WAXS), for example as described by Blundell and Osborn (Polymer 24, 953, 1983). Alternatively, crystallinity may be assessed by Differential Scanning calorimetry (DSC).
The level of crystallinity of the polymeric material may be at least 1%, suitably at least 3%, preferably at least 5% and more preferably at least 10%. In or preferred embodiments, the crystallinity may be greater than 25%. It may be less than 50% or less than 40%. Preferably the dental prosthetic item as formed has the aforementioned levels of crystallinity.
The main peak of the melting endotherm (Tm) of the polymeric material may be at least 300° C., such as from 300 to 400° C., for instance 300 to 350° C.
By the term “flowable” as used herein, referring to a composition, it is meant that the composition is substantially flowable when pressure is applied to it, such that at least 100 ml of the composition may be flowed through a 0.5 cm diameter orifice in a 1 mm thick wall when subject to a pressure difference of 1 bar over a period of 1 minute. Preferably, the thermoplastic composition may be molten, by which it is meant that when placed in a vessel, in a molten state, the composition will self-level to form a horizontal surface within +/−0.5 cm over a period of 30 minutes. Typically, this means that the temperature will be in excess of the main peak of the melting endotherm (Tm) of the polymeric material.
The mould may suitably be prepared from an impression from a patient's mouth.
The thermoplastic composition may suitably be provided in the form of granules. For instance, at least 90% by weight of the granules may have a particle size from 0.5 to 8 mm as measured by sieving.
The method of the fourth aspect of the invention may further comprise drying the granules of thermoplastic material to a moisture content of 0.1% or less. The moisture content may be measured by weight loss at 200° C. for 30 minutes, using a small sample of granules (say 10 grams) in a thermostatically controlled oven in a dry atmosphere. This arrangement reduces the risk of voids formed from water vapour being present in the resulting dental prosthetic item.
The thermoplastic composition may be brought into a flowable state in the cavity of the pre-moulding chamber prior to injection into the mould.
In a preferred exemplary embodiment of the invention. the thermoplastic composition may be heated to a temperature less than, but within 50° C. of, the main peak of the melting endotherm, Tm, of the thermoplastic composition, prior to providing the thermoplastic composition in the cavity of the pre-moulding chamber.
Suitably, the thermoplastic composition should be retained in the cavity of the pre-moulding chamber for 30 minutes or less. For instance, the composition may be retained for 20 minutes or less, such as for 15 minutes or less. This arrangement reduces the risk of thermal decomposition of the polymeric material of the thermoplastic composition.
The thermoplastic composition may brought to a temperature from 350 to 420° C., preferably from 380 to 400° C., immediately prior to injection into the mould. This is in order to ensure that the thermoplastic composition is in a flowable state.
Preferably, the thermoplastic composition comprises 60% or more by weight of the polymeric material, such as 70% or more for instance 80% or more. In one preferred exemplary embodiment of the invention, the thermoplastic composition may consist or consist essentially of the polymeric material, preferably with homopolymeric polyetheretherketone as the polymeric material.
The thermoplastic composition may be maintained under pressure, following injection into the mould cavity, until the thermoplastic composition has solidified.
By “solidified” it is meant that the thermoplastic composition is no longer flowable.
The solidification of the thermoplastic composition may be controlled, for instance by reducing the cooling rate by means of thermal shielding or by use of a thermal controller for the mould, to give a crystallinity of 5% or more, preferably 15% or more, for the polymeric material after moulding into the dental prosthetic item. Crystallinity may be measured as set out hereinbefore.
The dental prosthetic item prepared by the method of the fourth aspect of the invention may be a denture, crown, bridge, abutment or implant, or a portion thereof, such as a repair portion.
The preferred or optional features set out in relation to the fourth aspect of the invention are applicable, where appropriate, to the fifth to seventh aspects of the invention set out below, and should be considered as additionally disclosed in relation to these aspects in order to avoid repetition.
A fifth aspect of the invention provides a dental prosthetic item, such as a repair portion, obtained or obtainable by the method of the fourth aspect of the invention.
A sixth aspect of the invention provides an apparatus for forming a dental prosthetic item, the apparatus comprising:
The mould and the pre-injection chamber may be of unitary construction (i.e. formed as a single structure), or may be separate items arranged for mutual, removable interconnection such that there is a fluid connection between the respective cavities.
The mould may include exit tubes of a small diameter (say 0.5 mm or less) so that air can be expelled from the mould cavity as the thermoplastic composition is injected into the mould in its flowable state. This means that no vacuum needs to be applied in order to achieve a fully-filled mould.
The apparatus of the sixth aspect of the invention may comprise a first temperature controller arranged to control the temperature of the pre-injection chamber. For instance this may be a heating element under control of a thermostatic control means arranged to hold the pre-injection chamber at a desired preset temperature.
The apparatus may comprise a second temperature controller arranged to control the temperature of the mould. For instance this may be a heating and/or cooling element under control of a thermal control means arranged to control the cooling of the mould after injection whereby the solidified thermoplastic composition is cooled at a slow rate in order to provide a desired level of crystallinity for the polymeric material in the thermoplastic composition.
The press may be a mechanical press comprising a plunger arranged for driving the flowable thermoplastic polymer from the cavity of the pre-injection chamber into the mould cavity under pressure.
The mechanical press may comprise a brake for retaining the plunger in place prior to injection and a mechanism for applying a driving force to the plunger whilst retained by the brake, which driving force is applied by the plunger to the flowable thermoplastic polymer after release of the brake. The mechanism for applying the driving force may be, for instance, a resilient means such as a spring, which is compressed to a desired degree against the plunger in order to provide the driving force.
A seventh aspect of the invention provides use of a method according to the fourth aspect of the invention, or of an apparatus according to the sixth aspect of the invention, wherein the method or apparatus is used to prepare a dental prosthetic item for a patient in a dental laboratory or surgery, following a consultation with the patient, whereby the dental prosthetic item is made available to the patient within 24 hours of the consultation. That is, the dental prosthetic item is made available the patient within 24 hours of the end of the consultation, preferably even sooner such as on the same day as the consultation, for instance within 2 hours of the consultation. The invention allows for a dental prosthesis to be rapidly prepared in-situ at a dental surgery, and fitted in order to minimise inconvenience to a patient, without the requirement for complex apparatus or handling of potentially toxic monomers.
For a better understanding of the invention, and to show how exemplary embodiments of the same may be carried into effect, reference will be made, by way of example only, to the accompanying diagrammatic Figures, in which:
For each of the embodiments set out below, the composition of the dental frameworks and/or portions of dental framework consists of: PEEK-OPTIMA (Trade Mark) LT1-polyetheretherketone (PEEK) of melt viscosity (MV) 0.45 kNsm−2, simply referred to hereinafter a PEEK. Alternatively other variants of PEEK-OPTIMA® (Trade Mark) LT2 or LT3 of melt viscosity (MV) in the range between 0.45 and 0.15 could also have been used.
Turning to
In accordance with the method of the first aspect of the invention, the first portion 1 is pushed into the second portion 2 in order to mate the male members 5 with the female members 6, and the male members 5′ with the female members 6′, so that the first joint surface 3 s also brought into contact with second joint surface 4 and first joint surface 3′ is brought into contact with second joint surface 4′. The joint surfaces are then welded together ultrasonically by contacting the adjoining surfaces of the portions with the terminal welding surface of a hand-held sonotrode having ultrasonic power supplied thereto (70 KHz at 100 W). In particular, the edges of the female members 6, 6′ are welded to the male members 5, 5′ where these protrude through the female members. The protruding male members, following ultrasonic welding, may be covered by a crown in order to mask their appearance or to provide a further tooth prosthesis.
Turning to
A repair portion 1 has been formed using the original mould details from the broken dental framework, but with a first joint surface 3 formed by computer-aided machining in order to include unitarily formed male members 5, and with the first joint surface 3 and the male members 5 shaped to respectively mate with the female members 6 and complement the second joint surface 4.
The repair is achieved to form a repaired dental framework by pushing together the opposing joint surfaces 3, 4 so that the male members 5 mate with the female members 6 and contacting the adjoining surfaces of the portions with the terminal welding surface of a hand-held sonotrode having ultrasonic power supplied thereto. For this example, the sonotrode has a square, flat terminal welding surface having 4 mm square sides. In particular, the edges of the female members 6 are welded to the male members 5 where these protrude through the female members (through the back surface of the remnant portion 2, not shown in the Figure).
Turning to
In this embodiment, there is a thermal shield 30 surrounding the mould and pre-injection chamber. It will be understood that this shield 30 acts to reduce the cooling rate of the thermoplastic composition following moulding for this exemplary embodiment.
The mechanical press 23 has a cylindrical tubular wall 31 in which a piston 32 is constrained to travel, driven by a screw 33 turned by handle 34. A spring 35 is located between the piston 32 and a circular plate 36 which is also constrained to travel within the tubular wall 31. A plunger 38 in the form of a rod adapted to be snugly slidable into the pre-injection cavity 28 is rigidly attached to the plate 36. The plate 36 is shown held fixed in the tubular wall 31 by a brake 37 in a locked configuration. The piston 32 is shown compressing the spring 35 against the plate 36 to provide a driving force acting on the plunger 38 through the plate 36 when the brake 37 is released. A pointer 39 arranged to move with the piston 32 indicates the driving force on the scale 40 on the support structure 22.
In use, the plate 36 is locked in place by the brake 37 and the spring 35 compressed by the piston 32, against the plate 16 by turning the handle 34 so that the screw 33 drives the piston 32 (which is connected to the screw 33 by a tapped hole (not shown) down towards the plate 36. When a desired driving force is reached, as indicated by the pointer 39 on scale 40, granules of PEEK, which have been pre-melted in an oven, are poured into the pre-injection cavity 28 which is then aligned under the piston 38. The brake 37 is released so that the plunger 38 is driven into the pre-injection cavity, forcing the PEEK in its molten, flowable state into the mould cavity 29. The pressure from the mechanical press remains in place as the mould cools (with cooling slowed by the thermal barrier 30 to provide crystallinity in the PEEK of the resulting moulded item). When the PEEK has solidified, the pressure is released by turning back the handle 34 and the moulded dental prosthetic item removed from the mould cavity 29. A timer 41 is provided in the support structure 22 and may be used to estimate when the moulded item has solidified. The mould cavity in this embodiment is composed of a plurality of inter-engageable parts (at least two parts—not shown—held together by retainers—not shown) to facilitate removal of the moulded item from the mould cavity.
Although a few exemplary embodiments have been shown and described, it will be appreciated by those skilled in the art that various changes and modifications might be made without departing from the scope of the invention, as defined in the appended claims. For example, a different frequency or power of ultrasonics, other than as set out in the embodiments described, may be used for ultrasonic welding. As a further example, the pre-injection chamber 25 in
In summary, a method for forming an integrated or repaired dental framework is disclosed. Portions of dental framework formed of a composition comprising a polymeric material:
wherein t1 and w1 independently represent 0 or 1 and v1 represents 0, 1 or 2;
are provided with a male member on a joint surface of one portion and a female member on a joint surfaces of second portion, with the male and female members arranged to mate together to hold the portions together at the joint surfaces and then welded together by ultrasonic welding. Integrated dental frameworks formed by the method are also disclosed.
Large dental frameworks may thus be formed from the easily machinable, biocompatible polymeric material by moulding portions of a patient's mouth sequentially and forming an integrated framework from the moulds. Similarly, broken dental frameworks may be easily and conveniently repaired.
The invention provides methods for forming a dental prosthetic item, such as a repair portion, involving injecting a flowable thermoplastic composition from into a mould under pressure and cooling the mould to solidify the thermoplastic composition. The thermoplastic composition comprises a polymeric material with a repeat unit of formula (I):
wherein t1 and w1 independently represent 0 or 1 and v1 represents 0, 1 or 2.
Apparatus for putting the methods into effect and dental prosthetic items made using the method are disclosed, as is the use of the methods and apparatus for rapid preparation of prostheses following a consultation.
The invention allows for easy and rapid formation of durable and non-toxic dental prosthetic items in a dental laboratory or surgery without the need for complex apparatus or handling of toxic monomers.
Attention is directed to all papers and documents which are filed concurrently with or previous to this specification in connection with this application and which are open to public inspection with this specification, and the contents of all such papers and documents are incorporated herein by reference.
All of the features disclosed in this specification (including any accompanying claims and drawings), and/or all of the steps of any method or process so disclosed, may be combined in any combination, except combinations where at least some of such features and/or steps are mutually exclusive.
Each feature disclosed in this specification (including any accompanying claims and drawings) may be replaced by alternative features serving the same, equivalent or similar purpose, unless expressly stated otherwise. Thus, unless expressly stated otherwise, each feature disclosed is one example only of a generic series of equivalent or similar features.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1322508.1 | Dec 2013 | GB | national |
| 1400129.1 | Jan 2014 | GB | national |