DENTAL PROSTHESIS COMPONENT AND METHOD FOR PRODUCING DENTAL PROSTHESIS COMPONENT

Information

  • Patent Application
  • 20140147813
  • Publication Number
    20140147813
  • Date Filed
    September 24, 2013
    11 years ago
  • Date Published
    May 29, 2014
    10 years ago
Abstract
Provided is a dental prosthesis component which is a member to configure a dental prosthesis provided with an artificial tooth root, which have high strength and a good esthetic property. The dental prosthesis component (12),(13) to configure a dental prosthesis (10) provided with an artificial tooth root (12), which are made of Zr-14Nb alloy, wherein a surface layer containing ZrO2 and having a thickness of less than 80 μm as a main ingredient is formed on the components, and the surface has a brightness of Gly 8.0 or more of the color sheets according to Practical Color Co-ordinate System 201.
Description
TECHNICAL FIELD

The present invention relates to a dental prosthesis component such as an artificial tooth root (implant, fixture) or an abutment to be used for a dental prosthesis to repair defective sites in a tooth row by the artificial tooth root, and a method for producing the dental prosthesis component.


BACKGROUND ART

A dental prosthesis provided with an artificial tooth root comprises: an artificial tooth root whose one end is to be embedded in a jawbone; an abutment to be disposed in a manner that one end thereof is fixated to the artificial tooth root and the other end is projected into an oral cavity; and an artificial tooth crown disposed in a manner to cap a projected end portion of the other end of the abutment to function as an artificial tooth.


Herein, since the abutment holds the artificial tooth root and the artificial crown by connecting them, it is considered that the abutment needs to have certain degrees and more of strength, durability, and compatibility to a biological body. From such a viewpoint, titanium alloy is often used as a material to make the abutment. However, since titanium alloy has a color similar to black, when the end portion of the abutment is capped by the artificial tooth crown, black color of the abutment is seen through the artificial tooth crown and thereby sometimes the appearance is not favorable.


With respect to this, Patent Document 1 (Japanese Patent Application Laid-Open (JP-A) No. 2010-046153) for example discloses a technique using a ceramic such as zirconia as a material to make an abutment. According to this, it is considered that defects in appearance as mentioned above can be resolved by using a white ceramic.


SUMMARY OF THE INVENTION
Problems to be Solved by the Invention

However, the abutment made of a ceramic as mentioned above has problems that the abutment has low toughness by its nature and thus is easy to be broken. Also, with regard to color, esthetic improvement is desired by making the color of the abutment even closer to the color of a natural tooth. Further, not only the abutment but also the artificial tooth root has same problems since a part of the artificial tooth root is sometimes observed by appearance.


Accordingly, an object of the present invention is to provide a dental prosthesis component which is a member to configure a dental prosthesis provided with an artificial tooth root with high strength and a good esthetic property.


Means for Solving the Problems

The present invention will be described below. In order to make the present invention easy to understand, reference numerals given in the accompanying drawings are shown here in parentheses. However, the present invention is not limited to this.


The present invention solves the above problems by a dental prosthesis component (12), (13) to configure a dental prosthesis (10) comprising an artificial tooth root (12), the dental prosthesis component are made of Zr-14Nb alloy, wherein a surface layer containing ZrO2 as a main ingredient and having a thickness of less than 80 μm is formed on the dental prosthesis component, and the surface of the surface layer has a brightness of Gly 8.0 or more of the color sheets according to Practical Color Co-ordinate System 201. Herein, in respect to brightness, “Practical Color Co-ordinate System 201” corresponds to the Munsell color system with the same basis.


A thickness of the surface layer of the dental prosthesis component is preferably 20μm or more to less than 80 μm.


Also, in a method, for producing the dental prosthesis component (12),(13) described above to configure a dental prosthesis (10) comprising an artificial tooth root (12), it is preferable to include a step of oxidation treatment carried out to a member to be a dental prosthesis component made of Zr-14Nb alloy. In the step, the oxidation treatment is preferably carried out in an atmosphere of 4% or more to 20% or less of the oxygen density and in any one of following conditions of (1) to (3).


(1) 700° C. or more to less than 800° C., for 10 hours


(2) 800° C. or more to less than 850° C., for 1 hour or more to less than 2 hours


(3) 850° C. or more to less than 900° C., for 0.5 hours or more to less than 2 hours


Effects of the Invention

According to the present invention, it is possible to provide a dental prosthesis component which is a member to configure a dental prosthesis provided with an artificial tooth root with high strength and a good esthetic property.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a view illustrating a configuration of the dental prosthesis 10.



FIG. 2 (a) is a graph showing an analysis of X-ray diffraction of the surface layers, and FIG. 2 (b) is another graph showing an analysis of X-ray diffraction of the surface layers.



FIG. 3 (a) is a graph showing measurements of thicknesses of the surface layers, and FIG. 3(b) is another graph showing measurements of thicknesses of the surface layers.



FIG. 4 (a) is a photograph of the surface of the surface layer of No. 3, FIG. 4(b) is a photograph of the surface of the surface layer of No. 5, and FIG. 4 (c) is a photograph of the surface of the surface layer of No. 12.



FIG. 5 (a) is a cross-sectional photograph of the surface layer of No. 5, FIG. 5(b) is a cross-sectional photograph of the surface layer of No. 6, FIG. 5(c) is a cross-sectional photograph of the surface layer of No. 7, and FIG. 5(d) is a cross-sectional photograph of the surface layer of No. 8.



FIG. 6 (a) is a cross-sectional photograph of the surface layer of No. 1, FIG. 6(b) is a cross-sectional photograph of the surface layer of No. 5, FIG. 6(c) is a cross-sectional photograph of the surface layer of No. 12, and FIG. 6(d) is a cross-sectional photograph of the surface layer of No. 14.



FIG. 7 is a view showing surface color of sample made under each condition.





MODES FOR CARRYING OUT THE INVENTION

The functions and benefits of the present invention described above will be apparent from the following aspects for carrying out the invention. Hereinafter, the present invention will be described based on the aspects shown in the drawings. However, the invention is not limited to these aspects.



FIG. 1 is an exploded view schematically showing a configuration of the dental prosthesis 10 illustrating one aspect. The dental prosthesis 10 has an artificial tooth crown 11, an artificial tooth root 12, and an abutment 13.


The artificial tooth crown 11 is a portion which actually compensates for a defective site in a tooth row. Accordingly, the artificial tooth crown 11 is in a shape modeled after a natural tooth in appearance, thus reproducing a shape and texture of the natural tooth. The artificial tooth crown 11 is formed in a container shape and configured in a manner to insert the abutment 13 described below thereinside and connect with the abutment at a receiving portion 11a. As the artificial tooth crown, a known artificial tooth crown may be applied.


The artificial tooth root 12 is the dental prosthesis component of the present invention, also called an implant or a fixture, and is a member to be embedded in an alveolar bone so as to adequately fixate the dental prosthesis 10 in an oral cavity. A known form of an artificial tooth root may be applied to as the artificial tooth root 12.


The abutment 13 is also the dental prosthesis component of the present invention, a member to be disposed between the artificial tooth crown 11 and the artificial tooth root 12 and connect these to hold the artificial tooth crown 11. More specifically, one end of the abutment 13 is fixated in a manner to be inserted into a hole 12a formed in the artificial tooth root 12, and the other end of the abutment 13 is fixated in a manner to be inserted into the artificial tooth crown 11 and be fitted in the receiving portion 11a. A known form of an abutment may be applied to as the abutment 13.


Various configurations for a connecting structure of an artificial tooth root and an abutment have been suggested. For example, there is a configuration in which a male screw is formed on an abutment and a female screw is formed in a hole of an artificial tooth root to fixate the abutment and the artificial tooth root by screwing the screws together, or a configuration in which an abutment and an artificial tooth root are fixated by different screws. The configurations mentioned above may be applied to the present invention without particular limitations.


The artificial tooth root 12 and/or the abutment 13 as the dental prosthesis component are formed of Zr-14Nb alloy, and has a surface layer containing ZrO2 as a main ingredient and having a thickness of less than 80 μm on the surface. Herein, the “main ingredient” refers to the ingredient accounting for 50% or more of the total ingredients composing of this layer. Measurement of the thickness of the layer may be carried out by a known method without particular limitations. Since the thickness of the surface layer is substantially even, the thickness of the surface layer may be measured by taking photographs of some part of the surface layer by SEM and the like for example. According to this, cracking in the surface layer can be prevented. Herein, “no cracking” refers that it can be observed there is no cracking occurred in the SEM image at 1000 fold magnification of the cross section of the surface layer. Also, the thickness of the surface layer is preferably 20 μm or more. This makes it possible to adequately secure the thickness of the surface layer thereby prevents even certainly the surface of the dental prosthesis component from becoming parti-colored.


Also, the dental prosthesis component is made to have the same or similar color as that of the artificial tooth crown by forming the surface layer. That is, white or a color similar to white. Preferably, the color of the surface of the surface layer is white which has a brightness of Gly 8.0 or more of the color sheets according to Practical Color Co-ordinate System 201.


According to the dental prosthesis component as described above, the toughness (that is, strength) becomes excelled, and the color becomes closer to the color of a natural tooth. This makes it possible to provide dental prosthesis component having excellent durability with a good esthetic property, which can endure a long-time usage.


Next, a method for producing the dental prosthesis component according to one aspect will be described. The method for producing the dental prosthesis component includes: a preparing step of a button-shaped ingot made of Zr-14Nb alloy; a molding-cutting step; a processing step; and an oxidation treatment step.


The preparing step of the button-shaped ingot made of Zr-14Nb alloy (hereinafter, sometimes referred to as “step S1”) is a step to melt a high-purity Zr (purity of 99.6% by mass for example) and a high-purity Nb (purity of 99.9% by mass for example) in a proportion which can form Zr-14Nb and solidifying the resultant. A known method may be applied to this step, and the melting and solidification may be repeated more than once in order to improve the homogeneity.


The molding-cutting step (hereinafter sometimes referred to as “step S2”) is a step to melt the ingot obtained in the step S1, then obtain Zr-14Nb in the shape of a rod by molding, and cut the rod in a predetermined size. The predetermined size is a size as a starting material which can be applied to a cutting machine in the processing step described below.


The processing step (hereinafter sometimes referred to as “step S3”) is a step of disposing the starting material obtained in the step S2 to a processing machine and cutting it to form a shape of the dental prosthesis component. A NC machine tool based on a dental CAD/CAM system can be applied for cutting the material as an example. Also, polishing may be carried out after the cutting.


The oxidation treatment step (hereinafter sometimes referred to as “step S4”) is a step to form the surface layer described above containing ZrO2 as a main ingredient by carrying out oxidation treatment to the member having the shape of the dental prosthesis component obtained by the step S3. Conditions to form the surface layer are as below. Under the air atmosphere (that is, the oxygen density is about 20%), the material is exposed to a condition satisfying anyone of the following conditions of (1) to (3), setting treatment temperature and treatment time:


(1) 700° C. or more to less than 800° C., for 10 hours


(2) 800° C. or more to less than 850° C., for 1 hour or more to less than 2 hours


(3) 850° C. or more to less than 900° C., for 30 minutes or more to less than 2 hours


By the above, the surface layer as described above can be obtained. The oxygen density does not necessarily need to be 20%, but preferably 4% to 20%, and the oxidation treatment may be carried out in an atmosphere with such an oxygen density.


Examples

In examples, the treatment temperature and the treatment time in the oxidation treatment step described above were changed, and the ZrO2 layer formed in each case was examined. The treatments were carried out under the air atmosphere. Therefore, the oxidation density was approximately 20%. Samples used were disk-shaped Zr-14Nb of 10 mm in diameter. The conditions and the results are shown in Table 1. Here, “time (h)” is a holding time after reaching the treatment temperature (aimed temperature).


In the results, “Thickness” was measured by the cross-sectional photographs by SEM, and “◯” was given if the thickness of the surface layer was less than 80 μm, and “X” was given if the thickness of the surface layer was 80 μm or more. This is because, as described below, when the surface layer has a thickness of 80 μm or more, cracks increase in the surface layer, which increases a possibility of raising a problem in strength.


“Crack” was the results of evaluation according to degrees of the cracks in the surface layer. In the image of 1000 fold magnification of the surface layer by SEM, “◯” was given if a crack was not found, and “X” was given if a crack was found.


“Color” was the evaluation of the surface colors of the samples, and “◯” was given if the color had a brightness of Gly 8.0 or more of the color sheets according to Practical Color Co-ordinate System 201, and “X” was given if the color had a brightness below Gly 8.0 of the same.












TABLE 1









Conditions
Results (ZrO2layer)












No
Temperature (° C.)
Time (h)
Thickness
Crack
Color















1
600
0.5


X


2
600
10


X


3
700
0.5


X


4
700
10





5
800
0.5


X


6
800
1





7
800
2
X
X



8
800
3
X
X



9
850
0.5





10
850
1





11
850
2
X
X



12
900
0.5
X
X



13
900
1
X
X



14
1000
0.5
X
X










As shown in Table 1, in each of No. 1 to No. 6, No. 9, and No. 10, the thickness of the surface layer (ZrO2 layer) was less than 80 μm and a crack was not created. Further, in each of No. 4, No. 6, No. 9, and No. 10, it is possible to obtain a dental prosthesis component comprising a surface layer which is especially excelled in strength and has a good esthetic property with a desirable color.


On the other hand, in each of No. 1 to No. 3 and No. 5, there was a problem of color. The thickness of the surface layer was less than 20 μm respectively.


In each of No. 11 to No. 14, although the color was desirable, the thickness was 80 μm or more, as a result cracks were created in the surface layer and there was a problem of toughness (strength).


The above results will be described with examples below.


<Ingredients of the Surface Layer>

The ingredients of each of the surface layers were examined. The results is shown in FIG. 2(a) and FIG. 2(b). In both of FIG. 2(a) and FIG. 2(b), the horizontal axis represents 2θ, and the vertical axis represents strength. Treatment temperature and treatment time are respectively shown to each line.


As seen from FIG. 2(a) and FIG. 2(b), it is considered that ZrO2 monoclinic is contained in majority in each case. And a slight amount of ZrO2 in other crystal structure was also contained. On the other hand, NbO and Nbo2 were hardly detected.


<Thickness of the Surface Layer>

The thickness of the surface layers was examined based on the cross-sectional photographs of the surface layers by SEM. FIG. 3(a) is a graph of the examples with the treatment temperature of 800° C., and with each treatment time being changed. FIG. 3(b) is a graph of the examples with the treatment time of 0.5 h, and with each treatment temperature being changed. The horizontal axis of each graph represents conditions and the numbers corresponding to Table 1, and the vertical axis represents the thickness of the surface layers.


As seen from FIG. 3(a) and FIG. 3 (b), there is a tendency that the higher temperature and the longer treatment time make the thicker surface layers, and No. 7, No. 8, No. 12, and No. 14 have thicknesses of 80 μm or more.


<Cracks in the Surface Layers>

The cracks created in the surface layers were observed by SEM. FIG. 4(a), FIG. 4(b), and FIG. 4(c) show images of the surface layers by SEM taken from the surface (at 1000 fold magnification). Treatment conditions and numbers corresponding to Table 1 are shown to each figure. As seen from the figures, no cracks were created in No. 3 and No. 5, but cracks were created in the surface layer of example No. 12.


Also, in FIG. 5 and FIG. 6, the images of the cross-sectional surfaces of the surface layers taken by SEM were shown. FIG. 5(a) to FIG. 5(d) are examples in which the treatment temperature was 800° C. and each treatment time was changed respectively. FIG. 6(a) to FIG. 6(d) are examples in which the treatment time was 0.5 h and each treatment temperature was changed respectively. Each of the treatment conditions and the numbers corresponding to Table 1 were shown in each figure.


As seen from these figures, cracks were created if the thickness of the surface layer was 80 μm or more (No. 7, No. 8, No. 12 and No. 14).


<Color>

In FIG. 7, examples were shown in which the surface colors of the samples were compared. Each of the treatment conditions and the numbers corresponding to Table 1 were shown with each example. As seen from FIG. 7, in view of the treatment time and the treatment temperature, it is found that if the surface layer becomes thin, a mottling shows up on the surface. Therefore, the mottling is sometimes noticeable depending on the conditions such as size, shape and the like of the samples.


DESCRIPTION OF THE REFERENCE NUMERALS




  • 10 dental prosthesis


  • 11 artificial tooth crown


  • 12 artificial tooth root (dental prosthesis component)


  • 13 abutment (dental prosthesis component)


Claims
  • 1. A dental prosthesis component to configure a dental prosthesis provided with an artificial tooth root, the dental prosthesis component is made of Zr-14Nb alloy, wherein a surface layer containing ZrO2 as a main ingredient and having a thickness of less than 80 μm is formed on the dental prosthesis component, and the surface of the surface layer has a brightness of Gly 8.0 or more of the color sheets according to Practical Color Co-ordinate System 201.
  • 2. The dental prosthesis component according to claim 1, wherein said surface layer has a thickness of 20 μm or more to less than 80 μm.
  • 3. A method for producing a dental prosthesis component to configure a dental prosthesis provided with an artificial tooth root, the method includes a step of oxidation treatment carried out to a member to be the dental prosthesis component made of Zr-14Nb alloy, wherein the oxidation treatment is carried out in an atmosphere of 4% or more to 20% or less of the oxygen density and in any one of following conditions of (1) to (3). (1) 700° C. or more to less than 800° C., for 10 hours(2) 800° C. or more to less than 850° C., for 1 hour or more to less than 2 hours(3) 850° C. or more to less than 900° C., for 0.5 hours or more to less than 2 hours