Reducing the costs of battery technology has been an active area of research. Sodium-ion batteries have been attracting increasing attention and are considered to be a low-cost complement or an alternative to lithium-ion batteries due to the natural abundance and low cost of sodium compounds and their precursors. Application of sodium in primary batteries has been limited due to the lack of materials that can effectively and reversibly intercalate sodium ions with minimal degradation.
Thus, there is a need for improved primary batteries incorporating desodiated sodium transition metal oxides with controllable energy storage properties.
We have developed primary batteries incorporating a desodiated sodium transition metal oxide into a positive electrode. The primary batteries disclosed herein are advantageous as the desodiated sodium transition metal oxides provide comparable electrical performance to current Li ion technology at lower cost due to the high abundance of the precursor materials.
In one aspect, the invention features a primary battery including a negative electrode, a positive electrode including a desodiated sodium transition metal oxide of the formula NaxMO2, and an electrolyte. In the desodiated sodium transition metal oxide, 0<x<1.5, and M is one or more transition metal atoms.
In some embodiments, the one or more transition metal atoms are selected from the group consisting of Ni, Co, Fe, Mn, Rh, Pt, Cu, Mo, W, Ti, and a combination thereof, e.g., Ni, Co, Fe, Mn, Rh, Pt, Cu, Mo, W, and a combination thereof. In particular embodiments, the one or more transition metal atoms are selected from the group consisting of Ni, Co, Fe, Mn, and a combination thereof. In particular embodiments, the Fe content is 0.2-0.4, e.g., 0.2-0.3. In further embodiments, the desodiated sodium transition metal oxide include an alkali metal or alkaline earth metal atom, e.g., Li or Mg.
In some embodiments, the negative electrode includes elemental zinc. In further embodiments, the negative electrode includes zinc oxide. In some embodiments, the electrolyte includes 1 M to 9M hydroxide. In further embodiments, the electrolyte includes zinc oxide.
In some embodiments, the desodiated sodium transition metal oxide is desodiated from NaNiO2, NaCoO2, NaFeO2, NaMnO2, Na0.67MnO2, NaFe0.24Ni0.76O2, NaFe0.35Ni0.65O2, NaFe0.5Ni0.5O2, NaFe0.5Co0.5O2, Na0.67Fe0.5Mn0.5O2, NaFe0.4Mn0.2Ni0.2O2, NaFeyMn1-yO2 (0.05≤y≤0.5), Na0.67Ni1/3Mn2/3O2, NaFe1/3Ni1/3Mn1/3O2, Na0.67Mg0.23Mn0.72O2, Na0.67Mg0.205Fe0.05Ni0.1Mn0.645O2, Na0.67Mg0.23Ni0.05Mn0.72O2, Na0.67Mg0.23Ni0.05Mn0.67O2, Na0.67Mg0.205Ni0.125Mn0.67O2, Na0.67Mg0.205Fe0.05Mn0.745O2, Na0.67Mg0.23Fe0.1Mn0.62O2, Na0.67Mg0.24Fe0.13Mn0.5O2, Na0.67Mg0.205Fe0.05Co0.05Mn0.645O2, Na0.7Ni1.1O2, Na0.55Ni1.15O2, Na0.75Li0.1Ni0.15(Fe0.35Ni0.65)0.9O2, Na0.6Li0.1Ni0.2(Fe0.35Ni0.65)0.9O2, NaxFe0.35Ni0.75O2 (0.6≤x≤0.9), or NaxFeyNizO2, (0.5≤x≤1, 0≤y≤0.5, 1≤z≤1.3). In some embodiments, the desodiated sodium transition metal oxide is one or more of compositions 1-26, 29-53, 56, and 57 of Table 1 as described herein. In certain embodiments, the desodiated sodium transition metal oxide is one or more of compositions 2, 16, 17, 26, 37, 38, 44, and 45 of Table 1 as described herein.
In some embodiments the desodiated sodium transition metal oxide is Na0.24H0.76Fe0.35Ni0.65O2.
In some embodiments, the desodiated sodium transition metal oxide has stoichiometric ratio of intercalated protons to transition metal of about 0.5 to 1.67 H per M, e.g., 0.75 to 1 H per M.
In another aspect, the invention features a method of synthesizing a sodium transition metal oxide of the formula NaxMO2. The method includes mixing together a sodium source and a transition metal oxide, where the sodium source contains at least two sodium atoms, heating the mixture to form a sodium transition metal oxide, and de-intercalating sodium from the sodium transition metal oxide such that 0<x<1.5. M in the formula NaxMO2 is one or more transition metal atoms.
In some embodiments, the sodium source is Na2O2 or Na2CO3. In some embodiments, the de-intercalating of the sodium from the sodium transition metal oxide occurs electrochemically. In other embodiments, the de-intercalating of the sodium from the sodium transition metal oxide occurs chemically.
In some embodiments, the one or more transition metal atoms are selected from the group consisting of Ni, Co, Fe, Mn, Rh, Pt, Cu, Mo, W, and a combination thereof. In particular embodiments, the one or more transition metal atoms are selected from the group consisting of Ni, Co, Fe, Mn, and a combination thereof.
In some embodiments, the sodium transition metal oxide is NaNiO2, NaCoO2, NaFeO2, NaMnO2, Na0.67MnO2, NaFe0.24Ni0.76O2, NaFe0.35Ni0.65O2, NaFe0.5Ni0.5O2, NaFe0.5Co0.5O2, Na0.67Fe0.5Mn0.5O2, NaFe0.4Mn0.2Ni0.2O2, NaFeyMn1-yO2 (0.05≤y≤0.5), Na0.67Ni1/3Mn2/3O2, NaFe1/3Ni1/3Mn1/3O2, Na0.67Mg0.23Mn0.72O2, Na0.67Mg0.205Fe0.05Ni0.1 Mn0.645O2, Na0.67Mg0.23Ni0.05Mn0.72O2, Na0.67Mg0.23Ni0.05Mn0.67O2, Na0.67Mg0.205Ni0.125Mn0.67O2, Na0.67Mg0.205Fe0.05Mn0.745O2, Na0.67Mg0.23Fe0.1 Mn0.62O2, Na0.67Mg0.24Fe0.13Mn0.55O2, Na0.67Mg0.205Fe0.05Co0.05Mn0.645O2, Na0.7Ni1.1O2, Na0.55Ni1.15O2, Na0.75Li0.1Ni0.15(Fe0.35Ni0.65)0.9O2, Na0.6Li0.1Ni0.2(Fe0.35Ni0.65)0.9O2, NaxFe0.35Ni0.75O2 (0.6≤x≤0.9), or NaxFeyNizO2, (0.5≤x≤1, 0≤y≤0.5, 1≤z≤1.3).
As used herein, the term “about” refers to +/−10% of a recited value.
The invention provides primary batteries that incorporate a desodiated sodium transition metal oxide into the positive electrode (a cathode). Batteries of the invention using a desodiated sodium transition metal oxide in the cathode exhibit discharge voltages, battery capacities, and energy densities higher than a traditional Zn—MnO2 dry cell battery, such as a commercially available AA battery. These batteries are also advantageous over comparable lithium ion batteries due to the high abundance and low cost of sodium precursor materials with similar electrical performance.
Desodiated Sodium Transition Metal Oxides
A desodiated sodium transition metal oxide of the invention has the general formula NaxMO2, where 0<x≤1.5. For example, the relative atomic amount of sodium in the desodiated sodium transition metal oxides of the invention may be from greater than 0 to about 1.5, e.g., about 0.05 to about 0.67, about 0.33 to about 1, or about 0.75 to 1.5, e.g., about 0.05, about 0.1, about 0.15, about 0.2, about 0.25, about 0.3, about 0.35, about 0.4, about 0.45, about 0.5, about 0.55, about 0.6, about 0.65, about 0.7, about 0.75, about 0.8, about 0.85, about 0.9, about 0.95, about 1.0, about 1.05, about 1.1, about 1.15, about 1.2, about 1.25, about 1.3, about 1.35, about 1.4, about 1.45, or about 1.5.
In the present invention, M is one or more transition metal atoms. Transition metals useful for the desodiated sodium transition metal oxides include, but are not limited to, Ni, Co, Fe, Mn, Rh, Pt, Cu, Mo, W, and combinations thereof. Exemplary transition metals include Ni, Co, Fe, Mn, and combinations thereof. In particular, Fe and Mn are noteworthy due to their higher abundance and substantially lower costs relative to other transition metals. The relative atomic amount of any transition metal in the desodiated sodium transition metal oxides of the invention may be from greater than 0 to about 1, e.g., about 0.01 to about 0.5, about 0.25 to about 0.75, or about 0.5 to 1, e.g., about 0.01, about 0.05, about 0.1, about 0.15, about 0.2, about 0.25, about 0.3, about 0.35, about 0.4, about 0.45, about 0.5, about 0.55, about 0.6, about 0.65, about 0.7, about 0.75, about 0.8, about 0.85, about 0.9, about 0.95, or about 1.0.
In some cases, the desodiated sodium transition metal oxides include additional atoms, such as alkali metals, e.g., Li or K, and/or alkaline earth metals, e.g., Mg, Ca, Ba, or Sr. The relative atomic amount of any alkali metal or alkaline earth metal atom in the desodiated sodium transition metal oxides of the invention may be from greater than 0 to about 1, e.g., about 0.01 to about 0.5, about 0.25 to about 0.75, or about 0.5 to 1, e.g., about 0, about 0.05, about 0.1, about 0.15, about 0.2, about 0.25, about 0.3, about 0.35, about 0.4, about 0.45, about 0.5, about 0.55, about 0.6, about 0.65, about 0.7, about 0.75, about 0.8, about 0.85, about 0.9, about 0.95, or about 1.0.
The desodiated sodium transition metal oxides are typically layered in structure. In the present invention, transition metals may be located in the sodium layer as well as the MO2 layer. Furthermore, additional atoms, such as alkali metals, e.g., Li, or alkaline earth metals, e.g., Mg, may be in the sodium or MO2 layer or both. The electrical performance of desodiated sodium transition metal oxides of the invention that contain approximately 30% Fe, such as NaFe0.24Ni0.76O2 and NaFe0.3Ni0.65O2, may be related to the high voltage rippling phase as described by Chen et al. (Adv. Funct. Mat., 2018, 28(39), 1803896). As described in Chen et al., the rippling phase, where the metal oxide layer is not flat but has a rippled surface, is caused by the collective electronic behavior of the FeO6 octahedra. In contrast, a composition with a 30% Fe content is near the percolation threshold for the Na+ or H+ ions, and these ions always “see” the Fe ions on either side of the sodium layer.
Batteries
Desodiated sodium transition metal oxides of the present invention may be used to form an electrode, e.g., a cathode, of a primary battery.
An exemplary primary battery of the invention includes a positive terminal, cathode, separator, electrolyte, anode, and negative terminal. A positive terminal is in electrical contact with the cathode, and a negative terminal is in electrical contact with the anode. Contact between a negative terminal and anode may be direct; alternatively, the contact between the negative terminal and the anode may occur through an intervening conductor, such as a pickup conductor. The separator is between the cathode and the anode. Exemplary materials for separators are nonwoven fibers (cotton, nylon, polyesters, glass), polymer films (polyethylene, polypropylene, poly (tetrafluoroethylene), polyvinyl chloride), ceramics, and naturally occurring substances (rubber, asbestos, cellulose). The primary battery of the invention may further include an outer housing to contain all of the necessary components of the cell. In particular examples, the primary battery of the invention may take the physical form of a commercial alkaline battery, e.g., AAA, AA, C, D, or 9V. Other suitable physical forms of primary batteries are known in the art.
Electrode Materials
The desodiated sodium transition metal oxides may be a solid piece of the material, or alternatively, may be deposited onto or mixed with an appropriate substrate, e.g., a fluoropolymer or carbon. For example, dry polytetrafluoroethylene (PTFE) and wet polyvinylidene fluoride (PVDF) have been used as binders when making electrode materials for incorporation into an electrochemical cell. Other binders are known in the art. Materials for use as anodes in a primary battery of the present invention include metals, e.g., Zn. The metal may be in any suitable form, such as a powder or paste to be deposited onto or mixed with a substrate, a foil, or a mesh. For either positive or negative electrodes, the electrode material can be used without any additives. Alternatively, the electrode material may have additives to enhance its physical and/or ion/electron conducting properties. For example, cathodes may have an additive (such as carbon) that modifies the surface area exposed to the electrolyte. As another example, anodes may have an additive that enhances electron conductivity, such as an oxide, e.g., ZnO. Other additives are known in the art.
In one embodiment of a primary battery of the invention, the cathode includes a desodiated sodium transition metal oxide, PTFE, and carbon black, and the anode includes Zn and ZnO.
Electrolytes
Suitable electrolytes for primary batteries include aqueous solutions of alkali hydroxides, e.g., KOH, LiOH or NaOH, any may be a combination of one or more alkali hydroxides. The concentration of the alkali hydroxides in the electrolyte may be from about 1 M to about 9M, e.g., from about 1 M to about 4M, from about 2M to about 5M, from about 3M to about 6M, from about 4M to about 7M, from about 5M to about 8M, or from about 6M to about 9M, e.g., about 1 M, about 2M, about 3M, about 4M, about 5M, about 6M, about 7M, about 8M, or about 9M. Electrolytes may be used without any additives. Alternatively, the electrolytes may have additives. Electrolyte additives may be included to stabilize electrode-electrolyte interfaces and/or increase the voltage stability windows of the electrolyte. For example, electrolytes may include alkali salts, e.g., K2CO3, KF, other alkaline hydroxides, e.g., LiOH, or transition metal compounds, e.g., ZnO. Other additives are known in the art.
Batteries of the invention may be employed in methods of providing power to an electrical device. The battery (or a series of batteries) is electrically connected to the electrical device in an electrical circuit, which may include an on/off switch or other controller to interrupt or complete the circuit as desired.
Methods of Synthesis
The invention features methods of synthesizing a desodiated sodium transition metal oxide of the formula NaxMO2. The method involves mixing together a sodium source and a transition metal oxide, with the sodium source containing at least two sodium atoms. This mixture is then heated via a furnace to produce a sodium transition metal oxide. The resulting sodium transition metal oxide is then de-intercalated to remove sodium such that 0<x≤1.5. The M of the general formula NaxMO2 may include one or more transition metal atoms, such as Ni, Co, Fe, Mn, Rh, Pt, Cu, Mo, W, or a combination thereof. Exemplary transition metals include Ni, Co, Fe, Mn, or a combination thereof. The transition metal oxide may further include additional metal atoms, such as alkali metals, e.g., Li, or alkaline earth metals, e.g., Mg.
Suitable sodium sources of the desodiated sodium transition metal oxides include any precursor that includes at least two sodium atoms in its chemical formula. Exemplary sodium sources include sodium salts, e.g., Na2CO3, or sodium bases, e.g., Na2O2.
When present, useful alkali metals include Li and K, and useful alkaline earth metals include Mg, Ca, Ba, or Sr. The precursor of the alkali or alkaline earth metal atoms generally include salts of any counterion (e.g., Cl−, NO3−, or SO42−). For example, precursors for the incorporation of Mg into sodium transition metal oxides include, but are not limited to, MgO, Mg(OH)2, MgCl2, Mg(NO3)2, MgSO4, and MgCO3.
To form the sodium transition metal oxides from the mixture, the mixture is heated using methods known in the art. The temperatures used to form the solid state electrolyte may be from about 650° C. to about
950° C. (e.g., about 650° C. to about 750° C., about 700° C. to about 800° C., about 750° C. to about 850° C., about 800° C. to about 850° C., or about 850° C. to about 950° C., e.g., about 650° C., about 660° C., about 670° C., about 680° C., about 690° C., about 700° C., about 710° C., about 720° C., about 730° C., about 740° C., about 750° C., about 760° C., about 770° C., about 780° C., about 790° C., about 800° C., about 810° C., about 820° C., about 830° C., about 840° C., about 850° C., about 860° C., about 870° C., about 880° C., about 890° C., about 900° C., about 910° C., about 920° C., about 930° C., about 940° C., or about 950° C.). The heating process can be done in the presence of air, a reactive gas (e.g., 02), or under vacuum. The resulting sodium transition metal oxide is then cooled back to room temperature or quenched using methods known in the art.
De-intercalation of sodium in desodiated sodium transition metal oxides of the present invention may be achieved by electrochemical treatment or chemical treatment. In an electrochemical treatment, a synthesized sodium transition metal oxide may be used as a cathode material in an electrochemical cell with an alkali metal, e.g., sodium metal, as the anode and a sodium salt, e.g., NaPF6 or NaClO4, dissolved in an appropriate solvent, e.g., ethylene carbonate, diethyl carbonate, or fluoroethylene carbonate, or a mixture thereof, as the electrolyte. In a chemical treatment for de-intercalation, the synthesized sodium transition metal oxides may be simultaneously oxidized and de-intercalated by being contacted with a solution of a halogen, e.g., Cl2, Br2, or I2, dissolved in an appropriate solvent, e.g., a polar aprotic solvent, e.g., acetonitrile, ethyl acetate, or dimethylformamide. Heat treatment of the solution above room temperature, such as heating to 40° C., 50° C., or 60° C., can speed up the chemical de-intercalation process.
One method of electrochemical preparation of the desodiated transition metal oxides in the present invention involves charging sodium transition metal oxide to between 3.90V and 4.50V in a Na half cell, e.g., between about 3.90V and about 4.40V, between about 3.90V and about 4.30V, between about 3.90V and about 4.20V, between about 3.90V and about 4.10V, or between about 3.95V and about 4.05V, e.g., about 4.04V. The cathode is then then washed with water to obtain the product.
In a particular embodiment of the method above, the sodium transition metal oxide to be desodiated is NaFe0.35Ni0.65O2. In some embodiments the resulting desodiated sodium transition metal oxide is Na0.24H0.76Fe0.35Ni0.65O2.
Sodium transition metal oxides of the present invention were synthesized using solid state reaction methods by mixing either Na2O2 or Na2CO3 with the transition metal oxides. The mixed precursor materials were pressed into a pellet. The pellet was then heated in a tube furnace between 650-950° C. for approximately 10-12 hours in an air or oxygen atmosphere. The choice to use air or oxygen for the heating process was based on the specific compound desired. The heated pellets were quenched or slowly cooled down after the heating process.
For the electrochemical de-intercalation method, the cathode film of the electrochemical cell was made by mixing powdered as-synthesized sodium transition metal oxides, Super P carbon black, and dry PTFE. A Swagelok battery was assembled using glass fiber as a separator, sodium metal as the anode, and 1 M NaPF6 or NaClO4 in EC/DEC/FEC as the electrolyte. The charging process was applied with the high cutoff voltage ranging from 3.9 V to 4.5 V according to the specific sodium composition (x) needed to be left in NaxMO2.
For the chemical de-intercalation method, an iodine (I2)-acetonitrile solution was used to oxidize a pristine powder of the as-synthesized sodium transition metal oxides and extract sodium simultaneously. For sodium transition metal oxides that have higher sodium atomic content, and thus correspond to a low voltage during electrochemical charging, one sodium ion can be extracted by ½ I2. For sodium transition metal oxides that have lower sodium atomic content, and thus correspond to a higher voltage during electrochemical charging, more than ½ I2 is needed to extract 1 Na+ due to reaction equilibrium limitation.
Proton intercalation was performed in a Swagelok battery connected to a Landt battery test station. For electrical testing, the discharge performance of all synthesized materials was measured at a rate of 1/30 C with a cut-off voltage of 0.2 V.
The cathode active material was the NaxMO2 material after de-intercalation of Na as described in Example 2. The cathode film had a mass ratio of 80:15:5 for active cathode material, carbon black and PTFE. The anode was a strip of Zn foil 0.25 mm thick. For most of the synthesized compounds studied, the electrolyte was an aqueous solution of 9 M KOH with 0.6 M ZnO. For the particular compound Na0.24Fe0.3Ni0.65O2, the electrolyte was an aqueous solution of 3.2 M LiOH with 0.8 M KOH. Glass fiber was used as separator.
Table 1 provides a list of exemplary desodiated sodium transition metal oxides of the present invention and their electrochemical characterization with comparisons to commercially available conventional MnO2 and AA-sized alkaline batteries.
As is seen in Table 1, battery tests using the desodiated sodium transition metal oxides of the present invention in battery setups described herein display battery discharge voltages above 1.6 V and battery capacities above 300 mAh/g. These values are much higher than commercially available MnO2-based AA batteries which typically have discharge voltages around 1.2 to 1.3 V and less than 180 mAh/g capacity (as shown in the bottom of Table 1). In our testing, many of the synthesized desodiated sodium transition metal oxides have energy densities ranging from 257 Wh/kg to 333 Wh/kg, while the commercially available MnO2-based AA batteries have capacities ranging from 137 Wh/kg to 216 Wh/kg. Changes to the testing conditions, such as changes to the electrolyte composition, e.g., adding additives, or the anode material may result in battery capacities and/or energy densities that are up to 2× larger, e.g., 1.2×, 1.6×, or 2× larger, than those specified in Table 1.
NaFe0.35Ni0.65O2 (Fe35) was first charged to 4.04V in a Na half cell. The cathode was then washed by water to obtain the Fe35(4.04V) product (
The phase and valence evolution of Fe35(4.04V) during proton intercalation or discharge was investigated by X-ray diffraction (XRD) (
Changing the Fe composition in NaFexNi1-xO2 (
These results show that the water splitting induced irreversible oxygen redox may be prevented to preserve the accessible TM redox. Cu and Ti doping is also a very promising solution to prevent the water intercalation on the intrinsic material level. Suitable coating of the NaFexNi1-xO2 particle may also obstruct the water intercalation for a higher capacity.
Other embodiments are in the claims.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2020/026827 | 4/6/2020 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62829278 | Apr 2019 | US |