This application is based on and claims priority under 35 USC 119 from Japanese Patent Application No. 2012-242656 filed Nov. 2, 2012.
(i) Technical Field
The present invention relates to developers, image-forming apparatuses, and methods for forming images.
(ii) Related Art
Image-forming apparatuses, such as printers, copiers, and fax machines, that form an image with a developer may have the following intermediate transfer system.
Specifically, a type of image-forming apparatus is available that includes an intermediate transfer belt including a surface layer in which fluoropolymer resin particles are dispersed for improved toner releasability and a cleaning device including a blade-shaped member. The intermediate transfer belt is rotated so as to transport an image developed with a developer containing a toner coated with an external additive and transferred to the outer surface of the intermediate transfer belt to a second transfer section that retransfers the toner image to a recording medium such as recording paper. The blade-shaped member is disposed in contact with the outer surface of the intermediate transfer belt that has passed through the second transfer section to remove residual toner therefrom.
According to an aspect of the invention, there is provided a developer containing a toner having an external additive deposited thereon. The developer is used with an image-forming apparatus including an image carrier including a surface layer in which fluoropolymer resin particles are dispersed and a cleaning member disposed in contact with an outer surface of the image carrier. The external additive is a nonspherical external additive whose volume average particle size is smaller than the average particle size of exposed portions of the fluoropolymer resin particles in the surface layer of the image carrier.
Exemplary embodiments of the present invention will be described in detail based on the following figures, wherein:
Exemplary embodiments of the present invention will now be described with reference to the drawings.
First Exemplary Embodiment
An image-forming apparatus 1 according to the first exemplary embodiment is configured as, for example, a color printer. As shown in
The image-forming devices 10 include an image-forming device 10Y that forms a yellow (Y) toner image, an image-forming device 10M that forms a magenta (M) toner image, an image-forming device 10C that forms a cyan (C) toner image, and an image-forming device 10K that forms a black (K) toner image. These four image-forming devices 10 (10Y, 10M, 10C, and 10K) are arranged in series in the housing 2. The image-forming devices 10 (10Y, 10M, 10C, and 10K) are composed of similar components, as described below.
As shown in
The photoreceptor drum 11 includes a grounded solid or hollow cylindrical substrate and a photoconductive layer (photosensitive layer) disposed thereon. The photoconductive layer is formed of a photosensitive material and forms the image-bearing surface of the photoreceptor drum 11. The photoreceptor drum 11 rotates in the direction indicated by arrow A as it is driven by a rotational drive device (not shown). The charging device 12 is a noncontact charging device including a charging wire disposed at a predetermined distance from the image-bearing surface of the photoreceptor drum 11. The charging device 12 applies a charging current to the charging wire to charge the image-bearing surface of the photoreceptor drum 11 by corona discharge. Alternatively, the charging device 12 may be a contact charging device including a contact member such as a charging roller. The contact member is disposed in contact with the image-bearing surface of the photoreceptor drum 11 and is supplied with a charging bias. If the developing device 14 is configured for reversal development, the charging bias is a voltage or current of the same polarity as the toner supplied by the developing device 14.
The exposure device 13 irradiates the charged image-bearing surface of the photoreceptor drum 11 with light based on image information input to the image-forming apparatus 1 to form an electrostatic latent image. The exposure device 13 may be, for example, a nonscanning exposure device including a light-emitting diode and optical components or a scanning exposure device including a semiconductor laser and optical components such as a polygon mirror. An image processor (not shown) processes the image information input to the image-forming apparatus 1 to generate an image signal for each color component and transmits the image signal to the exposure device 13.
The developing device 14 (14Y, 14M, 14C, or 14K) uses a two-component developer 8 containing a toner and a carrier. As shown in
The drum-cleaning device 16 includes a container-like housing 16a, a rotating brush 16b, a cleaning blade 16c, a flicker 16d, and a collecting transport member 16e. The rotating brush 16b rotates with its brush member in contact with the circumferential surface of the photoreceptor drum 11 after first transfer. The cleaning blade 16c is disposed downstream of the rotating brush 16b in the rotational direction in contact with the circumferential surface of the photoreceptor drum 11 under a predetermined pressure to scrape off deposits such as residual toner. The flicker 16d flicks the deposits off the rotating brush 16b. The collecting transport member 16e, such as a screw auger, collects and transports the deposits flicked off the brush member of the rotating brush 16b to a collection system (not shown). The cleaning blade 16c is a blade-shaped or substantially blade-shaped member formed of, for example, a flexible rubber or resin.
As shown in
As shown in
The intermediate transfer belt 21 is fabricated by, for example, forming a surface layer 212 in which the fluoropolymer resin particles 5 are dispersed on the outer surface of the belt substrate 210. The surface layer 212 is formed by, for example, preparing a polyamic acid solution in which the fluoropolymer resin particles 5 and additives such as carbon black are dispersed as a layer-forming material, applying the layer-forming material to the outer surface of the belt substrate 210, and drying the coating. The polyamic acid solution used as the layer-forming material may be, for example, a mixture of a polyamic acid solution in which carbon black is dispersed and a polyamic acid solution in which the fluoropolymer resin particles 5 are dispersed, which is imidized to prepare a polyimide resin. Alternatively, the intermediate transfer belt 21 may be fabricated by, for example, adding a fluoropolymer resin to the material for forming the belt substrate 210 and molding the material. This type of intermediate transfer belt 21 has some fluoropolymer resin particles 5 segregated in the surface layer portion of the belt substrate 210.
The fluoropolymer resin particles 5 are formed of a fluoropolymer resin such as polytetrafluoroethylene (PTFE). The fluoropolymer resin particles 5 are relatively fine particles with an average particle size of 100 to 300 nm so that they are uniformly dispersed in the intermediate transfer belt 21. The amount of fluoropolymer resin particles 5 added to the belt substrate 210 is preferably 0.2% to 30%, more preferably 1% to 15%. If the amount of fluoropolymer resin particles 5 added is less than 0.2%, the intermediate transfer belt 21 exhibits increased adhesion to a toner image and thus has decreased transfer efficiency. If the amount of fluoropolymer resin particles 5 added is more than 30%, the intermediate transfer belt 21 might warp and deform due to thermal contraction when cooled during the manufacturing process. For improved efficiency of transfer of a toner image from the intermediate transfer belt 21 to the recording paper 9, the outer surface 21a of the intermediate transfer belt 21 may have a surface roughness (10-point average roughness, Ra) of less than 0.5 and a static friction coefficient of less than 1.0.
The second transfer device 25 includes an endless second transfer belt 25a, a drive roller 25b, and at least one driven roller 25c. The second transfer belt 25a is entrained about the drive roller 25b and the driven roller 25c and is arranged to rotate in a predetermined direction. The drive roller 25b rotates in contact with the outer surface 21a (image-bearing surface) of the intermediate transfer belt 21 at the position supported by the second transfer support roller 22d under a predetermined pressure. The driven roller 25c (or the second transfer belt 25a) is supplied with a second transfer bias from a power supply for transfer (not shown). The second transfer bias is, for example, a direct-current voltage of the same (or opposite) polarity as the developer 8. The second transfer belt 25a is formed of, for example, a synthetic resin such as a polyimide or polyamide resin.
As shown in
The paper feed device 30 is disposed under the intermediate transfer system 20. The paper feed device 30 includes at least one paper feed container 31 that contains a stack of recording paper 9 of a predetermined size and type and a feeder 32 that feeds the recording paper 9 from the paper feed container 31 sheet by sheet. The fixing device 40 includes a housing 41 accommodating a heating rotor 42 and a pressing rotor 43. The heating rotor 42 rotates in the direction indicated by the arrow and is heated by a heater so that the surface thereof is maintained at a predetermined temperature. The pressing rotor 43 is rotated in contact with the heating rotor 42 substantially along the axis thereof under a predetermined pressure.
Also provided in the housing 2 of the image-forming apparatus 1 is a feed transport path formed between the paper feed device 30 and the second transfer position (where the intermediate transfer belt 21 is disposed in contact with the second transfer device 25) of the intermediate transfer system 20 by pairs of paper transport rollers 33a, 33b, 33c, . . . and transport guide members. A paper transport device 34, such as a belt transport device, is disposed between the second transfer device 25 and the fixing device 40 to transport the recording paper 9 to the fixing device 40 after second transfer. A discharge transport path is formed on the discharge side of the fixing device 40 by pairs of transport rollers 45a and 45b and transport guide members. A paper output container (not shown) for containing the recording paper 9 discharged from the discharge transport path after image formation is disposed, for example, outside the housing 2.
As described above, the two-component developer 8 for use with the image-forming apparatus 1 (in practice, the developing devices 14) contains a toner and a carrier. The two-component developer 8 is used as a mixture of the toner and the carrier in a predetermined ratio.
Typically, the toner is a nonmagnetic toner. The nonmagnetic toner is composed of toner particles and an external additive deposited on the surface thereof to provide the desired function. The toner particles contain a known binder resin, a colorant, and optionally other additives such as a release agent. The binder resin is, for example, a polyester or acrylic resin. Examples of other additives include release agents, magnetic materials, charge control agents, and inorganic powders. The external additive may be inorganic or organic fine particles. Examples of inorganic fine particles include silica, titania, alumina, cerium oxide, strontium titanate, calcium carbonate, magnesium carbonate, and calcium phosphate. Examples of organic fine particles include fluorine-containing resin fine particles, silica-containing resin fine particles, and nitrogen-containing resin fine particles. The external additive may be surface-treated with a hydrophobing agent such as a silane compound, a silane coupling agent, or silicone oil. Other properties of the external additive will be described later. The method for manufacturing the toner particles may be, for example, but not limited to, a known emulsification polymerization aggregation process. The nonmagnetic toner is manufactured by mixing the toner particles and the external additive in, for example, a Henschel mixer or a V-blender. The nonmagnetic toner may have a volume average particle size of 3 to 6 μm.
The magnetic carrier may be, for example, a carrier formed of a magnetic material, a coated carrier prepared by coating cores formed of a magnetic powder with a coating resin, a magnetic-powder-dispersed carrier prepared by dispersing a magnetic powder in a matrix resin, or a resin-impregnated carrier prepared by impregnating a porous magnetic powder with a resin. Examples of magnetic powders include magnetic metals such as iron, nickel, and cobalt and magnetic oxides such as ferrite and magnetite. Examples of coating resins and matrix resins include polyethylene, polypropylene, and polystyrene. The carrier may have a volume average particle size of, for example, 20 to 40 μm.
Next, the basic image-forming operation of the image-forming apparatus 1 will be described. Described herein is an image-forming operation pattern (full-color mode) in which a full-color image composed of toner images of the four colors (Y, M, C, and K) is formed using all the four image-forming devices 10 (10Y, 10M, 10C, and 10K).
When the image-forming apparatus 1 receives a request for image-forming operation (printing), the photoreceptor drum 11 of each of the four image-forming devices 10 (10Y, 10M, 10C, and 10K) rotates in the direction indicated by arrow A, and the charging device 12 charges the image-bearing surface of the photoreceptor drum 11 to a predetermined polarity and potential. The exposure device 13 then irradiates the charged image-bearing surface of the photoreceptor drum 11 with light emitted based on image data separated for different color components (Y, M, C, and K), which is received from the image processor, to form an electrostatic latent image with a predetermined potential difference for the corresponding color component. The developing device 14 (14Y, 14M, 14C, or 14K) then supplies the two-component developer 8 of the corresponding color (Y, M, C, or K), which is charged to a predetermined polarity, to the electrostatic latent image formed on the photoreceptor drum 11 to cause the toner to be electrostatically attracted to the electrostatic latent image. Thus, each image-forming device 10 forms a toner image of any of the four colors (Y, M, C, and K) on the image-bearing surface of the photoreceptor drum 11.
The first transfer device 15 then transfers the toner image formed on the photoreceptor drum 11 by the image-forming device 10 (10Y, 10M, 10C, or 10K) to the outer surface 21a of the intermediate transfer belt 21, which rotates in the direction indicated by arrow B, in the intermediate transfer system 20 such that the toner images of the four colors are sequentially combined with each other. After the first transfer is completed, the image-bearing surface of each photoreceptor drum 11 is cleaned by the drum-cleaning device 16 to prepare for the next image-forming operation.
The intermediate transfer system 20 carries the toner images on the intermediate transfer belt 21 and transports the toner images to the second transfer position. The second transfer device 25 then simultaneously transfers the toner images from the intermediate transfer belt 21 to the recording paper 9 transported from the paper feed device 30 to the second transfer position through the feed transport path. After the second transfer is completed, the outer surface 21a of the intermediate transfer belt 21 is cleaned by the belt-cleaning device 26 to prepare for the next image-forming operation.
Finally, the recording paper 9 to which the toner images are transferred is released from the intermediate transfer belt 21 and is transported to the fixing device 40 by the paper transport device 34. The fixing device 40 fixes the toner images by fixing treatment (heating and pressing). For single-sided image-forming operation, the recording paper 9 to which the toner images are fixed is discharged outside the housing 2 through the discharge transport path and is stored in the paper output container.
By the operation described above, the image-forming apparatus 1 outputs recording paper 9 on which a full-color image composed of toner images of the four colors is formed.
In the image-forming apparatus 1, as shown in
As illustrated in
As a result, some of the fluoropolymer resin particles 5b exposed in the outer surface 21a of the intermediate transfer belt 21 are lost, and there are accordingly fewer fluoropolymer resin particles 5 for improving the toner releasability (i.e., reducing the adhesion to the toner) on the outer surface 21a of the intermediate transfer belt 21. This decreases the efficiency (second transfer efficiency) with which the toner images are transferred from the intermediate transfer belt 21 to the recording paper 9 at the second transfer position (see the dotted curve in
Accordingly, the image-forming apparatus 1 according to the first exemplary embodiment uses as the two-component developer 8 a developer containing a toner having an external additive 85 deposited thereon. The external additive 85 is a nonspherical external additive whose volume average particle size AD is smaller than the average particle size AE of the exposed portions of the fluoropolymer resin particles 5b in the surface layer 212 of the intermediate transfer belt 21 (AD<AE).
As illustrated in
The exposed portions of the fluoropolymer resin particles 5b may have an average particle size AE of 200 to 300 nm or about 200 to about 300 nm. If the exposed portions of the fluoropolymer resin particles 5b have an average particle size AE of less than 200 nm, they are less effective in reducing the adhesion to the toner after they are abraded by the cleaning blade 27. If the exposed portions of the fluoropolymer resin particles 5b have an average particle size AE of more than 300 nm, they are easily abraded by the cleaning blade 27 and come off the outer surface 21a of the intermediate transfer belt 21. An intermediate transfer belt 21 in which the exposed portions of the fluoropolymer resin particles 5b have an average particle size AE within the above range is manufactured by, for example, a molding process in which an intermediate-transfer-belt forming material containing fluoropolymer resin particles is applied to the circumferential surface of a cylindrical mold. As described above, the fluoropolymer resin particles 5 dispersed in the intermediate transfer belt 21 have an average particle size of 100 to 300 nm.
If the exposed portions of the fluoropolymer resin particles 5b in the surface layer 212 of the intermediate transfer belt 21 have an average particle size AE of 200 to 300 nm or about 200 to about 300 nm, the nonspherical external additive 85 deposited on the toner in the two-component developer 8 preferably have a volume average particle size AD of 90 to 180 nm or about 90 to about 180 nm, more preferably 140 to 160 nm or about 140 to about 160 nm, and an average circularity AR of 0.7 to 0.8 or about 0.7 to about 0.8, more preferably 0.77 to 0.8 or about 0.77 to about 0.8.
The volume average particle size AD of the nonspherical external additive 85 is the sphere-equivalent diameter at a cumulative frequency of 50% (D50v) in the distribution of the sphere-equivalent diameters of 100 primary particles of the nonspherical external additive 85 deposited (dispersed) on the toner particles. The sphere-equivalent diameters of the primary particles are determined by capturing images of the primary particles at 40,000× magnification using an SEM, measuring the largest and smallest particle sizes of each primary particle using image analysis, and calculating the sphere-equivalent diameter from the intermediate value (between the largest and smallest particle sizes). If the nonspherical external additive 85 has a volume average particle size AD of 90 to 180 nm or about 90 to about 180 nm, the volume average particle size AD is smaller than the average particle size AE of the exposed portions of the fluoropolymer resin particles 5b in the surface layer 212 of the intermediate transfer belt 21 (200 to 300 nm or about 200 to about 300 nm).
If the external additive 85 has a volume average particle size AD of less than 90 nm, it is easily embedded (buried) in the toner particles. If the external additive 85 has a volume average particle size AD of more than 180 nm, it easily comes off the toner particles.
The circularity R of the nonspherical external additive 85 is determined by capturing images of primary particles of the nonspherical external additive 85 deposited (dispersed) on the toner particles under an SEM and calculating the circularity R using image analysis as 100/SF2 by the following equation:
Circularity R=100/SF2=4π×(A/2L)
(where A is the projected area (nm2) of the primary particles of the external additive 85, L is the perimeter (nm) of the primary particles of the external additive 85 in the images, and SF2 is the secondary shape factor).
The average circularity AR of the nonspherical external additive 85 is determined as the circularity at a cumulative frequency of 50% in the distribution of the circularities of 100 primary particles determined using the above image analysis.
If the nonspherical external additive 85 has an average circularity AR of 0.7 to 0.8 or about 0.7 to about 0.8, its shape is nonspherical.
If the nonspherical external additive 85 has an average circularity AR of less than 0.7, it might chip due to concentrated stress when locally exposed to a mechanical load. If the nonspherical external additive 85 has an average circularity AR of more than 0.8, it is easily embedded in the toner particles.
The nonspherical external additive 85 may be the inorganic or organic fine particles as described above. For example, the nonspherical external additive 85 may be silica particles or titanium oxide particles, which are hard and chemically stable. The amount of nonspherical external additive 85 added to the toner may be, for example, 2% to 3%.
Thus, the image-forming apparatus 1, which uses as the two-component developer 8 a developer containing the nonspherical external additive 85 having the properties described above, may maintain the efficiency of second transfer of toner images from the intermediate transfer belt 21 to the recording paper 9 after the exposed fluoropolymer resin particles 5b come off the intermediate transfer belt 21. The image-forming apparatus 1 may therefore form a high-quality image without image defects due to a decrease in second transfer efficiency.
The mechanism by which the image-forming apparatus 1 may maintain the second transfer efficiency is believed to be as follows.
As illustrated in
Performance Test
Next, a performance test performed on the image-forming apparatus 1 to evaluate the second transfer efficiency will be described.
In this test, image formation for testing is continuously performed on a predetermined number of sheets of plain paper 9 by transferring and fixing a test image (25 mm×25 mm rectangular patch image with an image area fraction of 240%) developed with the two-component developer 8 described below. The second transfer efficiency is calculated by measuring the mass of the toner that forms the toner image on the intermediate transfer belt 21 before second transfer and the mass of the toner that remains without being transferred after second transfer using a suction device for extremely small amounts of toner. The second transfer efficiency is examined for each image obtained after completion of image formation on a predetermined number of sheets. For the 10% PTFE intermediate transfer belt 21, the image formation is continued to 600,000 runs (=600 kPV). For the 10% PTFE intermediate transfer belt 21, the image formation is continued to 200,000 runs (=200 kPV). This test is performed at a temperature of 25° C. and a humidity of 85% RH (laboratory environment).
The intermediate transfer belts 21 used in the test are two types of intermediate transfer belts 21 fabricated by dispersing 10% or 30% of PTFE particles 5 (average particle size: 100 to 300 nm) in a polyimide endless belt substrate 210 (belt thickness: 0.1 mm). The average particle size AE of the exposed portions of the fluoropolymer resin particles 5 in the outer surface 21a of the 10% PTFE intermediate transfer belt 21 before use is 100 to 300 nm. The average particle size AE of the exposed portions of the fluoropolymer resin particles 5 in the outer surface 21a of the 30% PTFE intermediate transfer belt 21 before use is 100 to 300 nm.
The belt-cleaning device 26 used in the test includes a polyurethane cleaning blade (thickness: 1.9 mm) set so as to apply a contact load of 30 to 35 N/m to the outer surface 21a of the intermediate transfer belt 21. The intermediate transfer belt 21 is rotated at 309 mm/sec in the direction indicated by arrow B.
The two-component developer 8 used in the test contains nonmagnetic toner particles formed of a polyester resin (average particle size: 3.8 μm) and magnetic carrier particles formed of a resin containing a magnetic material such as ferrite or iron powder (average particle size: 35 μm). The two-component developer 8 is prepared with a toner content of 5%. The nonspherical external additive 85 used for the toner is an external additive composed of medium-sized nonspherical silica particles with a volume average particle size AD of 160 μm and an average circularity AR of 0.775, which is deposited on the toner particles.
The results in
Material Property Test 1
Next, the fluorine and silica coverages of the outer surfaces 21a of the two types of intermediate transfer belts 21 used in the Performance Test are measured at several numbers of runs (numbers of images formed). The measurements (
The fluorine coverage refers to the coverage of the outer surface 21a of the intermediate transfer belt 21 with PTFE particles 5 (exposed in the outer surface 21a). The silica coverage refers to the coverage of the outer surface 21a of the intermediate transfer belt 21 with a nonspherical external additive 85 composed of silica particles (present in the recesses 21c). These coverages are measured at an X-ray acceleration voltage of 10 kV/10 mA using an X-ray photoelectron spectroscope (XPS) (JPS-9010 MX, available from JEOL Ltd.). The fluorine coverage is based on the fluorine content of the fluoropolymer resin (fluorine content: 100%) measured using the XPS.
Change in Fluorine Coverage
The fluorine coverage of the 30% PTFE intermediate transfer belt 21 will be discussed first. The measurements of the fluorine coverage at the early stage in the upper right graph in
Next, the fluorine coverage of the 10% PTFE intermediate transfer belt 21 at 600 kPV in
Assuming that the above findings apply to the measurements of the fluorine coverage of the 10% PTFE intermediate transfer belt 21 in
Change in Silica Coverage
The silica coverage of the 30% PTFE intermediate transfer belt 21 will be discussed first. The measurements of the silica coverage at the early stage in the lower right graph in
Next, the silica coverage of the 10% PTFE intermediate transfer belt 21 at 600 kPV in
Assuming that the above findings apply to the measurements of the silica coverage of the 10% PTFE intermediate transfer belt 21 in
Estimated Changes in Fluorine Coverage and Silica Coverage
Based on the above findings, the estimated change in the fluorine coverage of the 10% PTFE intermediate transfer belt 21 in the range from 0 to 600 kPV is added to the measurements of the fluorine coverage of the 10% PTFE intermediate transfer belt 21 in
Also, the estimated change in the silica coverage of the 10% PTFE intermediate transfer belt 21 in the range from 0 to 600 kPV is added to the measurements of the silica coverage of the 10% PTFE intermediate transfer belt 21 in
Discussion
The estimated change in fluorine coverage in
Thus, as more fluoropolymer resin particles 5 are lost, their effect of improving the toner releasability of the intermediate transfer belt 21 decreases, and the second transfer efficiency decreases accordingly.
The estimated change in silica coverage in
Thus, a certain amount of nonspherical external additive 85 may be present on the intermediate transfer belt 21 at a relatively early stage and remain thereafter. This may provide the effect of improving the toner releasability (instead of the lost fluoropolymer resin particles 5b), thus maintaining the second transfer efficiency irrespective of the decrease in fluorine coverage at a relatively early stage (see
Material Property Test 2
Next, intermediate transfer belts for testing are fabricated by applying predetermined amounts of the following three types of silica external additives to single-layer intermediate transfer belts (belt substrates 210 in which no fluoropolymer resin particles 5 are dispersed) composed only of a polyimide endless belt substrate (belt thickness: 0.1 mm). The silica coverage and second transfer efficiency of each intermediate transfer belt are then measured, and the relationship therebetween is examined. The silica coverage and the second transfer efficiency are measured by the same measurement procedures as in the Performance Test and Material Property Test 1 described above. In Test 2, the silica coverage and second transfer efficiency of an uncoated single-layer intermediate transfer belt are also measured. The second transfer efficiency is measured immediately after the toner is coated with an external additive. The results of Test 2 are shown in
(1) Small-sized spherical silica (volume average particle size: 140 nm, average circularity: 0.937)
(2) Large-sized nonspherical silica (volume average particle size: 200 nm, average circularity: 0.808)
(3) Medium-sized nonspherical silica (volume average particle size; 160 nm, average circularity: 0.775)
The results in
The second transfer efficiency of the single-layer intermediate transfer belt at the early stage of use is 89.3%, whereas the second transfer efficiency of the 10% PTFE intermediate transfer belt 21 at the early stage of use is 98%. The fluorine coverage of the 10% PTFE intermediate transfer belt 21 decreases considerably at 100 kPV (see FIG. 9A).
Based on the findings on the improvement in second transfer efficiency at a silica coverage of about 2%, the change in the second transfer efficiency of the 10% PTFE intermediate transfer belt 21 in the case where a toner (two-component developer 8) having a spherical silica external additive deposited thereon is estimated and is added to
Considering the estimated change in second transfer efficiency for the spherical silica external additive also shows that the second transfer efficiency for the nonspherical silica external additive decreases less than that for the spherical silica external additive.
In the results in
For reference,
The foregoing description of the exemplary embodiments of the present invention has been provided for the purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise forms disclosed. Obviously, many modifications and variations will be apparent to practitioners skilled in the art. The embodiments were chosen and described in order to best explain the principles of the invention and its practical applications, thereby enabling others skilled in the art to understand the invention for various embodiments and with the various modifications as are suited to the particular use contemplated. It is intended that the scope of the invention be defined by the following claims and their equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-242656 | Nov 2012 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20050130050 | Takada et al. | Jun 2005 | A1 |
| 20100209149 | Hara et al. | Aug 2010 | A1 |
| 20100261113 | Aruga et al. | Oct 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| A-2005-172968 | Jun 2005 | JP |
| A-2010-002748 | Jan 2010 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20140126927 A1 | May 2014 | US |