Patent Application
20140017805
This invention relates to collection of chemicals for separations and analysis. More specifically, this invention relates to a solid phase microextraction (SPME) device(s) having better capability for chemical collection and analysis. This includes better physical stability, capacity for chemical collection, flexible surface chemistry and high affinity for target analyte(s).
Solid phase microextraction (SPME) is a demonstrated and attractive method for sampling and preconcentrating trace level analytes, since it is a flexible, rapid, solvent-free extraction technique that is applicable to liquid and/or gas sampling environments. Further, SPME can be directly interfaced with wide range of analytical instrumentation for analyte detection such as gas chromatography (GC), gas chromatography mass spectroscopy (GC-MS), high-performance liquid chromatography (HPLC), liquid cromotography mass spectroscopy (LC-MS), and desorption electrospray ionization mass spectroscopy (DESI-MS), making it amenable to automation and a convenient technique. Due to its broad applicability and sensitivity SPME has been widely utilized in a variety of fields.
SPME was first successfully developed as a polymer coating on silica fibers in the early 1990s and, presently, various polymer phases are available commercially. Many types of polymers and composites with different chemical characteristics are available for the extraction of a variety of analytes of interest. Since polymer phases can be blended, different surface properties of polymers can simply be coated and tailored onto a single fiber. This leads to a certain extend application of polymer coated fibers in many fields.
However, a number of drawbacks of polymer SPME sometimes limit their applications. They are unstable with some solvents, have insufficient mechanical strength and tend to degrade at high operating temperatures. Additionally, the coatings are occasionally stripped, and they suffer from contaminations and unstable coatings on new fibers.
The demand for better chemical capacity, sensitivity, selectivity, as well as thermal, chemical, and mechanical stability has pushed continued research in the SPME field. Since the fiber coating is one of the most significant factors impacting SPME function, many different approaches have been explored to improve performance. For example, the sol-gel technology physically incorporated with polydimethysiloxane (PDMS) has been shown to enhance the thermal stability and sensitivity higher than normal PDMS. The planar geometry substrate was first applied for PDMS coating in order to increase the surface area and volume of the polymer phase, which subsequently enhances the capacity of SPME.
Certain coating polymers and polymer composites (i.e. BSP3 polymer, acrylate/silicone co-polymer, polyrrole, poly (phthalazine ether sulfone ketone)) and different preparation techniques (i.e. electrochemical, molecular imprinting, physical deposition) have also been employed to SPME for improved performance of the polymer coating.
SPME with nonpolymer coatings has been explored to overcome some of weakness of polymer coatings, specifically the limited capacity, selectivity, and chemical and thermal stability. Inorganic porous sorbents with high surface area such as, carbon nanotubes, activated charcoal, and porous silica coated SPME have been explored and reported to be effective materials for improvement in the extraction of analytes for some conditions. Metals and metal oxides such as, La (III), Al, and Nb2O5 have been investigated and developed for enhanced capturing and releasing of target analytes.
Among alternative nonpolymeric SPME materials, silica and silica composites are among the most promising coating materials. Some nanoporous silica materials can have a very high surface area per unit volume, sometimes over 1000 m2/g, while retaining hydrothermal stability. Further, they are amenable to the installation of a wide range of surface chemistries. However, integrating the silica materials into a functioning SPME device is not a trivial task. Challenges include the fragile nature of fused silica support fibers (which need extra care during SPME manufacture and application), the brittleness of ceramic coatings, and the challenge of creating a uniform thin film on the silica support fiber. It is important to maintain the available surface area of nanoporous silica material during the attachment process of coating to the support. The retention of a large relative surface area offers installation of selective silane functional groups (able to obtain high density of binding sites), resulting in high sorption capacity and sensitivity to analytes of interest. Effectively attaching nanoporous material onto the SPME fibers depends upon the attachment method. A glue method utilizing epoxy has been reported for attaching functionalized/unfunctionalized mesoporous silica and other porous silica particles onto SPME supports.
Rapid detection of organic chemicals is important for a range of areas including biomedical, agricultural, industrial, environmental, forensic and a range of health and safety related areas. The threat of terrorism has heightened the significance of rapid fieldable detection of trace level organics for security concerns. SPME is an ideal approach for improving methods for sampling and analysis of the forensic signatures, chemical weapons and explosives.
What is needed is a device and method of making with improved capacity for trace analyte capture, enhanced affinity and selectivity of target analytes.
In one embodiment of the present invention, a device for enhanced collection of target analytes is disclosed. The device comprises a support surface and a thin film containing a plurality of nanopores bound to the support surface. The surface of the nanopores may include a chemistry installed therein for enhanced capture of target analyte(s).
In one embodiment, the nanopores are silica nanopores or some other porous ceramic.
The support surface may be a substrate. The substrate is, but not limited to, one of the following: a fiber, a metal wire, a planar support, and a tubular structure.
In one embodiment, the support surface is porous.
In one embodiment, the support surface is coated by the thin film containing micro and the nanopores. The porous thin film may be coated on the outside of the support surface. Alternatively, the nanoporous thin film may be coated on the inside of the support surface.
In one embodiment, the device further comprises a binder to increase the stability and uniformity of the thin film.
The surface chemistry may be, but not limited to, an organo-silane. The surface chemistry may comprise of multiple components to provide polyfunctional sorbent chemistry. The polyfunctional surface chemistry is, but not limited to, at least one of the following: organics, organometallics, metals, nanoparticle complex molecules, covalently bound molecules or combinations thereof.
The target analyte may be a gas-phase or liquid-phase. The gas or liquid-phase analyte is at least one of the following: explosives, explosive variants, chemical weapons agents, pesticides, and volatile organic compounds (VOCs).
In another embodiment of the present invention, a method of selective and specific capturing of target analytes is disclosed. The method comprises providing a support surface. The method further comprises coating the support surface with a thin film containing a plurality of nanopores. The nanoporous thin film can be coated on the inside or the outside of the support surface. A coating inside of a tubular support can be sued directly in commercial thermal desorption analytical systems such as GC, GC-MS or other. The method may also comprise of installing selective chemistry on the surface of the nanopores.
In one embodiment, the thin film is deposited on to the support surface by dip coating, molding or spray-on. The thin film may be subsequently sintered to solidify the structure and film adhesion to the support surface. A binder may be applied to increase the stability and uniformity of the thin film.
In another embodiment of the present invention, a device for enhanced capture of target analytes is disclosed. The device comprises a tubular support having open internal space. A nanoporous thin film is coated inside the tubular support. A surface of the nanopores may include a surface chemistry installed therein for improved affinity and selectivity of target analytes.
In one embodiment, the device further comprises equipment to collect separate and analyze the captured analytes.
In another embodiment of the present invention, a method of selective binding of target analytes at higher preconcentration factors is disclosed. The method comprises providing a tubular support having an empty space. The method further comprises coating the inside of the tubular support with a thin film containing a plurality of nanopores. The method also comprises installing surface chemistry on the nanopores. The method also comprises drawing a target analyte into the empty space for specific capture of the analyte with the nanopores containing the chemistry.
In one embodiment, the method further comprises collecting, separating and analyzing the captured analytes.
The present invention is directed to methods and devices that have high capacity and affinity for the selective capture of targeted analytes, which include explosives, explosive variants (precursors), chemical weapon agents, pesticides and other volatile organic compounds (VOC's). These devices can exceed capacity and affinity compared to existing commercially devices by over a factor of 10 thereby allowing for improved trace level sampling and detection. Further an enormous range of surface chemistries can easily be installed providing flexibility in the breadth of analytes and applications.
In one embodiment of the present invention, novel solid phase microextraction (SPME) coatings are disclosed. The supports for the coatings may include a metal wire, flexible silica coated wire, or equivalent, to provide a rigid yet somewhat flexible support for selective thin film sorbent materials of the present invention.
The composition for a thin film coating the support can comprise at least one of several materials. The materials used in the thin film coatings may include, but are not nanoparticle and limited to, nanoporous silica, nanoporous alumina, a mixture of nanoporous material plus a binder agent (for adhesion), other micro and nano porous supports, or even the creation of porosity in a metal wire support itself
The thin film coatings can be applied in multiple layers to increase thickness (surface area) as well as for adhesion enhancement. The thin film material can be applied in several ways, such as dip coating, molding, spray-on, or other.
The use of a binder agent in the thin film composition of the present invention may be included to film improve stability and adhesion as well as to promote mass flow for better sampling. As one example, during the assembly of SPME coatings, the thin film material is thermally cycled in a sintering process to stabilize the nanoporous silica plus binder, or other material, as well as remove the excess binder creating a high surface area thin film that is well affixed to the support wire. The addition of a binder agent not only imporoves the adhesion to the support surface, but also improves the overall film structure by increasing film porosity. In addition to creating a more uniform thin film, the use of a binder can stabilize normally unstable materials that are desired to be used for their high capacity properties.
Upon application of the nanoporous thin film onto the support surface, which can be a wire support surface, the thin film may be functionalized with specific chemistries to increase the selectivity and affinity for target analytes. The surface chemistries applied to the thin film include, but are not limited to silanes, organics, organometallics, metals, and complex molecules. The present invention encompasses the selection of chemistries as well as how the chemistries are applied to the thin film; covalent or non-covalent installation bonding to the base support.
The surface chemistries selected may have attributes of selectivity, thermal stability and high affinity to various target analytes of interest depending on the application. The surface chemistries used in the present invention may differ greatly compared to the commercially available SPME coatings such as polydimethysiloxane-divinylbenzene (PDMS-DVB). Unlike the polymer or waxlike coatings used is SPME the preferred chemistries are grafted to the surface in very thin layers, typically covalently bound high density monolayers. Silanes and phophoic acid are a preferred type of molecule enabling strong bonding to the surfaces. Aromatic silanes such as phenyl silanes are of particular interest since they have good thermal stability form good high density monolayers and have affinity for a range of analytes of interest. Surface chemistries with nonpolar (i.e. phenyl or alkane groups) and polar sites (i.e. metal or organometallic) are of interest since they provide a “mixed mode” of a fraction for some target analytes. Additional surface chemistries include the use of phosphine oxides or simple physisorbed low vapor pressure organics. Many analytes of interest contain polar and nonpolar molecules, some are semivolatile organics. A “mixed mode” surface provides improved affinity to all components of the semipolar and semivolatile compounds - many of which are of interest such as nitroaromatic explosives, nerve agents, pesticides, etc. Surface chemistries can be applied with complimentary characteristics for liquid or gas phase techniques.
In one embodiment, the present invention utilizes a nanoporous thin film bound to a support surface comprised of porous silica or other high surface area materials that can be applied to a variety of substrates such as a thin metal wire. This structure provides improved rigidity and capacity resulting in better durability and enhanced analyte capture in a SPME device. The SPME device can be fully integrated with an existing commercial SPME form factor for both analyte sampling and analytical analysis instrumentation.
The following examples serve to illustrate exemplary embodiments and aspects of the present invention and not to be construed as limiting the scope thereof.
The nanoporous silica (MCM-41 powder for example) was attached to a metal fiber substrate using a sintered thin film method. Synthetic methods are mentioned herein or referenced as appropriate. Comparisons of these materials to other approaches in literature are included in the results and discussion.
In the sintered thin film method, nano structured SiO2 particle was used as a binder. The adhesion slurry and coating slurry were separately prepared. The attaching agent was prepared by mixing 3 g of Ludox SM, 30% SiO2 nano particles with 6 g of H2O and 0.5 g of surfactant Legpal C0-720. The coating slurry was prepared from the ball milled MCM-41 of 0.5 μm mixed with Ferro B-75717 binder, IPA, and C18EO10 surfactant. The weight concentration of coating slurry was: 11.7% MCM-41, 52.7% Ferro B-75717, 33% IPA and 2.6% C18EO10. The cleaned fibers which were washed with 2-propanol were first dip coated with attaching slurry with 5 cm/minute lift rate. Then they were calcined at 350° C. for 1 hour. The coated fibers were finally dip coated with coating slurry with the lift rate of 2-20 cm/minute, then dried at 80° C. for 10 minutes. The dip coating and drying process were repeated 1-5 times to achieve desired the thickness. The coatings were heat treated in air at 3° C./minute, 550° C. for 4 hours.
Functionalization of thin film. A 5 mm NMR tube containing fibers with modified end pointing up and several drops of the desired silane were added and 1-3 mL of toluene was also added. The tube was capped, mixed twice, then heated in a stirred water bath at 70-80° C. for 4 hours. The solvent was carefully drained, followed by two tube rinses of methanol rinse. The samples were air-dried.
The ability to increase the sensitivity with SPME pivots on the capacity of the sorbent layer which in turn scales with the available surface area of the sorbent material. The selectivity of the SPME is dependent upon the surface chemistry of sorbent material. Nanoporous silica (or other nanoporous ceramic) provide very high surface areas, desirable chemical and thermally stability as well as the ability to install a wide range surface chemistry. The general concept with graphical illustrations and actual images of the hierarchical assembly of the device is shown in
The challenge of coating the nanoporous materials on a support surface, such as a metal wire, is the effective installation and functionalization of the nanoporous material into a SPME format that is stable and retains the advantageous properties. A number of methods to bind the nanoporous particles to the supporting SPME core fiber were explored here. Adhesive binding or “glue method” using epoxy as a binder is a method we found produced inferior results. Adhesive binding resulted in poor uniformity, blocked porosity, and limited capacity. Direct application of template Sol-gel coating formed thin films are also not uniform, had porosity that was often blocked, and had a propensity to flake off the support structure. Further processing conditions and techniques are required to obtain consistent and uniform desired structures as related to porosity, pore uniformity, flexibility etc. The sintered thin film application technique was a successful method for installation of nanoporous material onto a support structure. This method provided effective binding as well and ease of manufacture. The sintering thin film utilizes a two-step mechanism of silica formation. The first mechanism appears to involve the formation of Fe—O—Si and Al—O—Si between the surface of the steel wire and nano SiO2 particle during the first calcination. The calcination removed organic binder, at the same time it allowed the silica particles in the thin film to adhere to each other and bind to the surface of the substrate. The calcination temperature needs to be carefully chosen since the low temperature did not support the formation of the strong Fe—O—Si bonding. On the other hand, the high temperature may affect the organic binder quickly removed before the Fe—O—Si or Al—O—Si is completely formed. The nano SiO2 coated steel wire was then coated with nanoporous silica and calcinations again. The second silica formation occurred, after nanoporous silica was coated on nano SiO2-steel wire, during the second calcination. Again, the proper calcination and sintered temperature is needed for the complete organic removal and for silica particles sintering. This sintering allows the formation of Si—O—Si between nanoporous silica and nano SiO2 to occur while still retaining the high surface and porosity of the material. The calcination temperature was studied as a function of length shrinkage and surface are. Shrinkage data indicated that sintering was being started at 550° C. Meanwhile, the lower surface area was observed at the higher calcination temperature (≧650° C.), which is due to the collapsing of the pore structure. Therefore, the sintering was done at 550° C. for 4 hours to assure good binding of the nanoporous silica since Si—O—Si is a slow formation and probably takes a longer time than Fe—O—Si formation 40, and with minimal loss of structure/porosity. Thin film nanoporous silica coating calcined at 550° C. for 4 hours still retains their ordered pore structure and high surface area.
The binder agents and coating process play a role for effective coating of nanoporous silica on metal wires. Nanoporous silica was coated on steel wire for 1 cm length using sintering and adhesive methods. A uniform and smooth coating of nanoporous silica was obtained by using the sintering method. The presence of nanopartilces SiO2 (calcined at 350° C. for 1 hour) improves the adhesion between coating and the substrate. The attached nanoporous silica with the binder displayed a uniform coating and smooth surface.
The thickness of new coating material is one of the more important parameters to be investigated and optimized for the development of a SPME sampling device. The thicker coating typically provides the higher volume results in higher capacity for the capture of analytes. However, it affects the equilibrium time, resulting in requiring a longer collection time. In this work, nanoporous silica coated steel wires with various coating thickness (˜2.5-55 μm) were exposed to DNT vapor for 7 days and subsequently analyzed with GC as the results shown in
Chemically functionalizing the nanoporous thin films for enhance SPME can be done with a variety of different chemistries. By modifying the surface functionality of the thin film, the affinity for the analytes of interest can be increased and tuned. The surface functionality must be stable to the analysis conditions. Using silanes to covalently attach the surface functionalities to the nanoporous thin film (NPTF), the result is a stable surface modification.
In order to increase selectivity and affinity of functionalized nanoporous thin film (FNTF) toward explosive vapors, a variety of different silanes were used to modify the surface of the nanoporous thin film. These included phenyl, thiophenyl, 2,4-dintrophenyl, and thenyl trifluro acetone (TTA). The TTA modified nanoporous thin films were treated europium. It is well known that each analyte binds differently through chemical bonding (i.e. physical adsorption, hydrogen bond, covalent) to different surface chemistries. For recovering an analyte from a SPME for subsequent analysis is typically accomplished by heating until the organic compound volatizes off of the sorbent into the instrument. Therefore, the thermal stability of the sorbent and surface chemistry is important. Further, the surface chemistry must be stable to ensure repeatability with time and reversible to allow for recovery of analyte. A range surface chemistry has been explored for improved collection of explosive signatures for air and surfaces. The organics and organometallic modified nanoporous materials have a high thermal stability - the decomposition temperature in the range of 300-400° C.—as shown in Table 1.
The surface chemistry installed on the thin film is one of the important factors that plays a major role in capture capacity, sensitivity, affinity and selectivity in analytes of interests.
The commercial SPME, the nanoporous silica thin film, and the variety of functional groups installed on the nanoporous thin films were exposed to DNT vapors for an equal period of time and tested on a GC-MS for performance comparison. The sensitivity of SPMEs were reported in the term of “response normalized volume” which were calculated from the obtained response per volume of coating thin film of SPME normalized to response per volume of coating thin film of the commercial SPME. The nanoporous silica coated metal wire exhibits the higher sensitivity (˜1.8 times) than the commercial SPME. The organic and/or metal functionalized nanoporous silicas (FNTFs) also show significant improvement in sensitivity of SPME. Especially, organometallic coating FNTF shows the highest sorption capacity of DNT, ˜8.5 times higher as compared to commercial SPME. The organometallic surface chemistry is a covalently bound beta diketone lanthanide complex. Other organometallic complexes such as Cu-thiol propyl silane are also effective. The very high affinity of DNT for FNTF suggests that sensitivity for collection of analyte of interests could be improved by selective surface chemistries. It also implies that surface chemistry has more impact for enhancing the affinity of SPME toward analytes than the surface area of fiber coating. However, again, the large surface area of fiber coating is necessary for providing the chemical or functional group installing.
The present invention has been described in terms of specific embodiments incorporating details to facilitate the understanding of the principles of construction and operation of the invention. As such, references herein to specific embodiments and details thereof are not intended to limit the scope of the claims appended hereto. It will be apparent to those skilled in the art that modifications can be made in the embodiments chosen for illustration without departing from the spirit and scope of the invention.
The invention was made with Government support under Contract DE-AC05-76RLO1830, awarded by the U.S. Department of Energy. The Government has certain rights in the invention.