The invention concerns a device for supporting a horizontal guided, continuous glass strand.
The Danner-Technique and the Vello-Technique are used for the industrial production of glass rods and glass tubes up to diameters of approximately 100 mm. With the Danner-Technique the glass flows from a nozzle on top of a rotating tilted pipe, through which, in the case of producing tubes, a glass is blown and a glass strand is pulled off continuously from the tip. With the Vello-Technique a ring nozzle, through whose center the glass is blown for the tubing production, creates the glass strand.
Tube drawing techniques have become known for example from DE 100 54 804 A1.
With the usual techniques for the production of glass rods or glass tubes, the hot and ductile glass strand is directed into the horizontal level, cooled down over the length of the drawing bench and finally separated into sections of the desired length. The glass strand, which is still hot, is supported along the drawing path. This takes place usually by means of rollers or supports from a material, which leaves fewest possible traces on the surface of the glass strand.
Wood and graphite are the materials usually used for these rollers. V-shaped blocks made from the same materials are used instead of the rollers if extremely quiet running of the glass strand is demanded within the drawing path; the recess of the V-shaped blocks guides the glass strand.
Good lateral guide properties are achieved while accepting that the strand slides on the support and that there is the danger of developing scratches.
The small supporting surface, which the rollers offer to the glass strand, causes the glass strand (especially in its hot area) to be deformed during transport over the rollers, which in return causes an impairment of its dimensional accuracy and especially problems with ovalness. Furthermore, heat is removed from the glass strand along the contact line to the rollers. The nonuniform heat distribution over the circumference of the glass strand leads with further cooling to distortion and bending of the glass strand. In addition, the contact to the rollers transfers dust and dirt on the glass strand.
The guide rollers and guide blocks are especially in the hot area subjected to distinct wear by abrasion. This abrasion creates contaminations on the glass strand surface. During the progressive wear the occurrence of the scratches created by the supporting device increases, until the rollers and blocks must be exchanged after some time.
DE 31 25 521 A1 describes a device for conveying and supporting a hot, continuous glass tube. The supporting device exhibits a V-shaped recess, which forms a supporting area for the glass tube. The supporting area exhibits drilled holes in the vertex of the V, which are connected to compressed air. Compressed air is to lift the glass tube off the supporting area. However, in the range of the legs of the V-shaped supporting area approximation of the glass tube to the walls of the legs takes place and therefore also contact.
This leads to a mutual impairment. On the one hand scratches can develop on the exterior of the glass tube, on the other hand material wear of the supporting device takes place, especially if a soft material such as graphite is used for it.
A prior art design variation is known in which the glass tube strand is guided between two walls bent against each other, which are usually made of sheet metal, and is carried on air, which discharges from the gap between the walls. Usually these devices are present only in the first few meters; rollers do the further transport of the glass strand. In such devices one tries to stabilize the glass strand centered on a gas cushion by means of suitably guiding the gas that is emerging from a gap under the glass strand. However, lateral contact of the glass strand with the walls cannot always be prevented, so that in these cases the surface of the glass strand is damaged or contaminated.
A freely floating guide of the freshly formed glass strand on compressed air nozzles would be possible. In this case no contact can occur between glass strand and firm materials. However, the necessary airflow for supporting the glass strand would be so large, that the nozzles would cause an inadmissibly high noise level. Furthermore there is the risk that the gases impacting the glass strand surface with high speeds deform the glass strand especially in its hot area. Besides, this principle is not economical due to the high costs of compressed air.
The invention is based on the task to design a device of the initially described kind in such a manner that a glass strand—solid or hollow—originating from a continuous casting unit, is horizontally guided and supported, without having contact with a firm environment, so that damage of the glass strand and/or wear of the supporting blocks are avoided, with good dimensional accuracy of the glass strand as well as with low capital investment cost and low operating cost.
The device according to invention thus creates a gas cushion for the support of the glass strand. The gas cushion is created by means of a fine-porous, gas-permeable diaphragm body, from which gas emerges in very fine distribution. This way a gas cushion can be formed, which can be created on the one hand with gas throughput, and which impinges on the blown on areas of the glass strand as symmetrically as possible.
Thus the difficulties connected with rollers or firm supports, like the local extraction of heat at support points and the risk of deformation, are eliminated. Contrary to the rollers or firm supports the carrying force will transfer over a substantially larger area to the tubing strand, which prevents the risk of deformation. Moreover, the heat dissipation from the glass strand is homogenized, since no local contact between the glass strand and the supporting device takes place. The heat dissipated by the supporting gas is removed from the glass strand over a large surface area.
An interesting variation of the invention consists of providing the diaphragm bodies with channels for passing the compressed gas and to locate the channels at a certain distance to the gas emerging area—called from now on “supporting area”—generally parallel to the supporting area. Thereby it is possible to use diaphragm bodies made from a material with relatively low strength and to design the diaphragm bodies relatively thick-walled, so that on the one hand there is no risk of fracture, and that however on the other hand the compressed gas has to cover only a short distance from the channel to the supporting area, so that the pressure of the compressed gas can be relatively low.
The invention is described in more detail with the help of the drawings.
The device represented in
The molten glass mass 4 flows through the annular gap between needle 3 and ring 2 and expands over the conical pinhead. From the edge of the pinhead, the tear-off edge, it flows downwards and forms into a bulb. The created hollow strand 5 is bent in the horizontal direction before solidifying while hanging freely and pulled off over supporting blocks 10 according to the invention with a drawing machine.
The gas pressure of the gas atmosphere 7 can be regulated, so that in connection with different drawing rates of the glass amount to be processed a broad dimensional spectrum can be manufactured.
The supporting block 10 represented more accurately in
Furthermore a pressure housing 10.3 is provided. It exhibits two inlets 10.4, 10.5 for compressed gas. Between the inlets 10.4, 10.5 is a further gas inlet 10.6, which can be used for passing in gas of relative low excess pressure.
The compressed gas passed into the inlets 10.4 and 10.5 passes through the pores of the diaphragm bodies 10.1, 10.2 and arrives at the supporting areas 10.1.1, 10.2.1 of the diaphragm bodies 10.1, 10.2, where it emerges. It forms a gas cushion, on which the glass strand 5 so to speak swims.
It is necessary in each case that the material of the diaphragm bodies 10.1, 10.2 is an open-porous material, so that gas from the interior of the pressure housing 10.3 can pass through to the supporting areas 10.1.1 and 10.2.1. An open-porous carbon material is preferred. It exhibits very good emergency running properties in case of the failure of the gas supply and also leaves no disturbing traces on the glass strand surface with brief contact. Beside carbon also open-porous sinter metals or metal fabrics are applicable for these parts of the device. They are used preferably in applications, in which with carbon no sufficient long time creep strength can be achieved with high temperatures.
In temperature ranges over 900° C., where even regular metals are pushed to their load limits, the use of porous ceramics such as SiC or Cordient or of porous precious metals is possible.
The angle α that the two diaphragm bodies 10.1, 10.2 form with one another, depends on the outside diameter of the glass strand 5. The arrangement can be done in such a manner that the angle α is adjustable. For glass strands with large diameter flatter angles are favorable, for thin glass strands pointed angles. Some combinations of strand diameter and angle can be taken from the following table:
Interrelationship between glass strand diameters and support angles
Inlet 10.6 for gas with low excess pressure is designed in such a manner that the gas flow divides and strokes preferably along the supporting areas 10.1.1 and 10.2.1. This division of the gas flow can take place by means of bent drilled holes, recesses misaligned against each other, recesses or other things built in the gap.
Air is the first choice for gas. In addition, other gases can be used. Gas can exercise besides its supporting function a temperature equalization function, thus that it exhibits a certain temperature.
The whole device is preferably separated into individual segments. These can be arranged directly one behind another to permit a constant support of the glass strand especially in its hot area. With increasing cooling of the glass strand however it becomes more mechanically stable, so that the segments with increasing distance of the hot area can be arranged in larger distance. Thus the operating cost can be reduced compared to a continuous device.
The reason for this design variation is the following:
A very brittle material with comparatively low strength can be used as diaphragm material, because the diaphragm bodies can be made very thick, so that the strength is acceptable. Nevertheless is the distance, which the compressed gas must cover through the diaphragm material until it arrives at the supporting areas, relatively short. The channels 10.1.3, 10.2.3 can be located relatively close to the supporting areas 10.1.1, 10.2/1.
As an alternative to the design variation in accordance with
| Number | Date | Country | Kind |
|---|---|---|---|
| 101 13 344 | Mar 2001 | DE | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 1638593 | Mulholland | Aug 1927 | A |
| 2678237 | Allander et al. | May 1954 | A |
| 2805898 | Willis, Jr. | Sep 1957 | A |
| 3254981 | Havens | Jun 1966 | A |
| 3961927 | Alderson et al. | Jun 1976 | A |
| 4312659 | Panarello et al. | Jan 1982 | A |
| 4546811 | Potard | Oct 1985 | A |
| 4636239 | Wilson et al. | Jan 1987 | A |
| 5688300 | Ashley et al. | Nov 1997 | A |
| 5766298 | Ashley et al. | Jun 1998 | A |
| 20020092326 | Langsdorf et al. | Jul 2002 | A1 |
| 20030037573 | Langsdorf et al. | Feb 2003 | A1 |
| Number | Date | Country |
|---|---|---|
| 28 03 455 | Aug 1979 | DE |
| 28 52 406 | Jul 1980 | DE |
| 31 25 521 | Mar 1982 | DE |
| 196 43 108 | Apr 1998 | DE |
| 63-236718 | Oct 1988 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20020184922 A1 | Dec 2002 | US |