Patent Application
20200057117
The present invention relates to a magnetic sensor including diamond. The present application claims priority to Japanese Patent Application No. 2017-029689 filed on Feb. 21, 2017, the entire contents of which are incorporated by reference.
A Hall element has widely been used as a magnetic sensor which measures intensity of magnetic field. SQUID making use of superconduction has been known for measurement of small magnetic field. A sensor capable of highly sensitive detection of magnetic field in a small region by making use of a nitrogen-vacancy complex (NV− center) formed in diamond has recently been proposed as a new sensor (NPL 1). Such a sensor detects red light produced as fluorescence from an NV− center when it emits green light as excitation light to NV− centers while it emits microwaves at a frequency of approximately 2.8 GHz to diamond containing NV− centers. Intensity of magnetic field is detected based on variation dependent on magnetic field intensity, in lowering point of fluorescence intensity in sweeping the frequency of emitted microwaves (PTL 1). Studies about diamond suitable for such a sensor have been conducted (PTL 2).
PTL 1: WO2015/107907A1
PTL 2: Japanese Patent Laying-Open No. 2012-121748
NPL 1: J. R. Maze et al., “Nanoscale magnetic sensing with an individual electronic spin in diamond,” Nature, Vol. 455, p. 644 (2008)
A sensor making use of NV− centers is capable of measuring variation in very weak magnetic field intensity. A method of measuring variation in fluorescence intensity with a frequency of emitted microwaves being fixed has been restricted in that a range of detectable magnetic field intensity is narrow. In general, there is ambient magnetic field larger than small magnetic field to be detected. Therefore, a large-scale shielded room for cutting off ambient magnetic field should be provided. Even in such a case, it is difficult to completely cut off ambient magnetic field such as magnetic field originating from an electric circuit such as a sensor, and such difficulty has imposed great restrictions on practical use. An object of the present invention is to obtain a diamond magnetic sensor which achieves a broadened range of detectable magnetism intensity and is suitable for practical use with a scheme for eliminating ambient magnetic field.
A diamond magnetic sensor according to one manner of the present invention includes diamond containing at least one NV− center, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the NV− center of the diamond, and a fluorescence sensor which receives fluorescence produced from the NV− center of the diamond, and the diamond magnetic sensor includes a pattern measurement apparatus which measures a temporal change pattern of magnetism intensity based on variation in fluorescence intensity sensed by the fluorescence sensor.
According to another manner, a diamond magnetic sensor includes diamond in a form of a plate containing a plurality of NV− center regions in a plan view, a magnetic array arranged in correspondence with the NV− center regions, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the diamond, and a fluorescence sensor array which individually receives fluorescence produced from the plurality of NV− center regions.
According to the above, a diamond magnetic sensor which achieves a broadened range of detectable magnetism intensity and is suitable for practical use by eliminating ambient magnetic field can be obtained.
[Embodiments of the Present Invention]
Suitable embodiments of the present invention will be listed.
One of embodiments is directed to a diamond magnetic sensor including diamond containing at least one NV− center, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the NV− center of the diamond, and a fluorescence sensor which receives fluorescence produced from the NV− center of the diamond, the diamond magnetic sensor including a pattern measurement apparatus which measures a temporal change pattern of magnetic field intensity based on variation in fluorescence intensity sensed by the fluorescence sensor.
The pattern measurement apparatus desirably performs a function to control sweep of a frequency of the microwaves, a function to specify a frequency of the microwaves at which a relative minimum value of the fluorescence intensity is produced, and a function to detect magnetic field intensity based on the specified frequency, and the pattern measurement apparatus measures the temporal change pattern of the magnetic field intensity by repeating detection of the magnetic field intensity by repeating sweep of the frequency.
A data analysis apparatus which separates intensity of magnetic field originating from a measurement environment and intensity of magnetic field originating from an object to be measured from each other based on the temporal change pattern is desirably further provided.
The data analysis apparatus is desirably the diamond magnetic sensor which separates the intensity of the magnetic field by filtering based on a frequency in the temporal change pattern.
Another embodiment is directed to a diamond magnetic sensor including diamond in a form of a plate containing a plurality of NV− center regions in a plan view, a magnetic array arranged in correspondence with the NV− center regions, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the diamond, and a fluorescence sensor array which individually receives fluorescence produced from the plurality of NV− center regions.
In each manner described above, a cancellation coil which lowers ambient magnetic field applied to the diamond by producing prescribed magnetic field is desirably further provided.
The diamond magnetic sensor is desirably configured to have the diamond, the microwave generator, the excitation light generator, and the fluorescence sensor or a fluorescence sensor array mounted on a single circuit board directly or with another member being interposed. Improvement in performance and reliability as a magnetic sensor, such as a smaller and more compact size of a configuration of the entire sensor, a stabilized optical axis, higher efficiency in emission of excitation light and emission of microwaves, and increase in accuracy and stability of an emission position, is thus achieved.
A configuration can also further include a magnetic shield which cuts off ambient magnetic field applied to the diamond and an antenna which introduces an external signal including an object to be sensed into the inside of the magnetic shield.
In the diamond magnetic sensor above, the pattern measurement apparatus can also be implemented by an apparatus which measures a spatial direction pattern of magnetic field intensity or measures a temporal change pattern for each spatial direction, instead of measurement of the temporal change pattern of magnetic field intensity.
In this case, the data analysis apparatus is desirably implemented by an apparatus which separates intensity of magnetic field originating from a measurement environment and intensity of magnetic field originating from an object to be measured from each other based on the spatial direction pattern or on both of the spatial direction pattern and the temporal change pattern.
Yet another embodiment is directed to a diamond magnetic sensor including diamond in a form of a plate containing a plurality of NV− center regions in a plan view, a magnetic array arranged in correspondence with the NV− center regions, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the diamond, and a fluorescence sensor which receives fluorescence produced from the plurality of NV− centers, magnitude of a relative minimum value of intensity of fluorescence produced from the plurality of NV− center regions being weighted differently for each NV− center region in accordance with a frequency of the emitted microwaves and magnetic field applied by the magnetic array.
A configuration including diamond in a form of a plate containing a plurality of NV− center regions in a plan view and a magnetic array arranged in correspondence with the NV− center regions, the diamond and the magnetic array being in contact with each other, is desirably employed as a unit of the diamond magnetic sensor. Fixed magnetic field can thus effectively be applied to each NV− center region.
Desirably, the diamond and an electronic circuit portion including the fluorescence sensor are distant from each other by at least 1 cm, and no member which electrically connects the diamond and the electronic circuit portion to each other is interposed between the diamond and the electronic circuit portion. In order to eliminate as much as possible, weak magnetic field generated from diamond serving as a sensing portion and the electronic circuit portion (an electronic circuit which generates excitation light, an electronic circuit as a fluorescence reception portion, and an electronic circuit which produces microwaves) in the diamond magnetic sensor, an apparatus with a structure in which the diamond and an electronic circuit are physically and spatially distant from each other is desirable. Thus, unnecessary influence by magnetic field onto the diamond magnetic sensor can be eliminated.
In the diamond magnetic sensor, the electronic circuit portion including the fluorescence sensor is spaced apart from the diamond by a solid through which visible light or infrared light passes, and can be used in at least one environment of a temperature environment different from a standard state, a pressure environment different from the standard state, and a gas atmosphere other than air.
The diamond magnetic sensor can be implemented by an apparatus with such a structure that the diamond serving as the sensing portion and the electronic circuit portion are spaced apart from each other by a plate transparent to a visible light region or an infrared region and are placed in environments different from each other. Thus, magnetic field in an environment against which an electronic circuit is not resistant but diamond is resistant can be measured.
[Description of Embodiments of the Present Invention]
An embodiment of the present invention will be described below with reference to the drawings. The drawings are schematic for the sake of clarity of description, unless otherwise specified. Therefore, a size and positional relation of members may be exaggerated or shown at a scale facilitating viewing. Elements having the same references allotted in a plurality of drawings represent identical portions or members. Though terms expressing positional relation such as up, down, left, and right directions are used as necessary for the sake of convenience of reference to the drawings or description, those terms are used for facilitating understanding of the invention and the technical scope of the present invention is not restricted by the meaning of those terms.
Basically, magnetism is used to mean a source of generation of magnetic field in a space (including a source with the N pole and the S pole and a quantum mechanical spin), whereas magnetic field is used to mean a field of magnetic force formed by magnetism in a space surrounding the same. A magnetic sensor herein refers to a sensor which measures magnetic field at a location where the sensor is located, which means, however, also measurement of magnetism. Therefore, the term “magnetism” is used. When it is not necessary to strictly distinguish between magnetism and magnetic field, clearly distinctive description is not provided.
An expression magnetic field intensity or magnetism intensity is used to mean that what is measured is intensity of magnetic field or magnetism,. An expression a magnetic field direction or a magnetism direction is used to mean that what is measured is a direction of magnetic field or magnetism.
For facilitating understanding, what is expressed by magnetic field (magnetism) is a segment representing one moment of a temporal change pattern of magnetic field (magnetism). Even though magnetic field (magnetism) to be sensed cannot be distinguished from magnetic field (magnetism) other than that simply by a value of magnetic field (magnetism) itself at one moment, they can be distinguished from each other when they are observed from a point of view of a temporal change pattern of magnetic field (magnetism) intensity or a magnetic field (magnetism) direction. This is because characteristics of variation in intensity or direction thereof are different by paying attention to time or a frequency.
They can further be distinguished from each other by paying attention also to a spatial direction pattern representing a spatial distribution of magnetism. The temporal change pattern refers to overall variation over time in magnetic field (magnetism) intensity or a direction thereof. The spatial direction pattern refers to a distribution of magnetic field (magnetism) directions observed at positions of sensing. Therefore, a vector pattern of magnetic field can be obtained by combining the temporal change pattern and the spatial direction pattern with each other.
<First Embodiment>
(Basic Operations by Diamond Magnetic Sensor)
Fluorescence produced from NV− centers of diamond is different in intensity between excitation from a ground state (a state that a magnetic quantum number of spins m, is 0) and excitation from a level at which electrons are resonated and excited by microwaves (a state that a magnetic quantum number of spins ms is −1 or +1). In the former example, fluorescence intensity is high, and in the latter example, fluorescence intensity is low. In excitation from the state that the magnetic quantum number of spins ms is ±1, fluorescence intensity is low because the electrons return to the ground state owing to non-light-emitting transition in which no fluorescence is emitted. At the level where electrons are excited, the number of electrons in the ground state which contribute to fluorescence by being excited by irradiation with microwaves at a specific frequency corresponding to a level difference decreases.
Therefore, fluorescence intensity is lowered by irradiation with microwaves at this specific frequency. When there is magnetic field, an excited state is split in terms of energy (Zeeman effect). Therefore, there are at least two relative minimum values of fluorescence intensity. Since a difference in microwave frequency (difference in energy) between two levels which have been equal to each other before splitting by magnetic field is in proportion to magnetic field intensity, magnetic field intensity can be calculated based on the difference in microwave frequency.
When there is a single NV− center, there is only one pair of relative minimum values in a graph showing fluorescence intensity in which the abscissa represents a microwave frequency. When directions (orientations) of bonds between N and V are different in an example where there are a plurality of NV− centers, with a difference in magnetic field intensity for each direction, a graph of fluorescence intensity exhibits a plurality of relative minimum values. In a single piece of single-crystal diamond, there are four directions of bonds between N and V at the maximum. Therefore, the number of relative minimum values in a graph of fluorescence intensity does not exceed eight. Even though there are a plurality of relative minimum values, a pair of relative minimum values on which calculation of a difference in microwave frequency is based is produced by the same magnetic field intensity, and hence it can be distinguished from other pairs. Since each pair is centered around a frequency at the time when zero magnetic field is established (since the pair of relative minimum values has as its center, a frequency at the time when zero magnetic field is established), each pair can be distinguished from other pairs.
An example in which a frequency of microwaves emitted from microwave generation source 10 is swept by a frequency sweep apparatus 11 in
A diamond magnetic sensor of this type which has conventionally been under study captures, for example, variation in small magnetic field with a microwave frequency in
Fluorescence intensity I1 is detected. It is assumed that magnetic field slightly varies and the relative minimum value of fluorescence intensity is displaced to a microwave frequency f2. In this state, what is detected is fluorescence intensity at fixed microwave frequency f1 and hence fluorescence intensity attains to I2. By thus measuring fluorescence intensity while microwaves at a constant frequency are emitted, variation in small magnetic field can be measured as variation in fluorescence intensity.
(Diamond Magnetic Sensor)
A diamond magnetic sensor according to the first embodiment of the invention of the present application will be described with reference to
Though an example which uses a frequency difference between two relative minimum values is described above, an approach capable of measuring comparable variation should only be applicable. For example, with a median frequency between two relative minimum values having already been known, any one relative minimum value alone can also be detected and a difference from the already known median frequency can also be detected as ΔF/2. In this case, a span of sweep of a frequency can be narrower. A median value refers to a point where magnetism is zero, and when it is evaluated in advance, it can be calibrated later.
The diamond magnetic sensor in the embodiment of the present application can thus find a temporal change pattern of magnetism intensity based on a frequency at which a relative minimum value of detected fluorescence intensity is exhibited, by repeating sweep of a frequency of microwaves. In order to obtain a clearer temporal change pattern of magnetism intensity, a rate of sweep of a frequency of microwaves (time required for one sweep) is preferably shorter than 1 msec., more preferably shorter than 10 μsec., and further preferably not shorter than 1 μsec. This is because, as the rate of sweep of a frequency is higher, a waveform shorter in cycle or more complicated can be reproduced. A range of sweep of a frequency of microwaves (a frequency range) and an interval between frequencies (an interval between frequencies set in one sweep) are set to a range and an interval in which two relative minimum values of fluorescence intensity can be observed and preferably a range and an interval in which at least one relative minimum value can be observed, in order to clearly reproduce a relative minimum value. What is sensed is variation in frequency of microwaves. Therefore, even though a frequency is greatly shifted, sensitivity to magnetism is calculated as a frequency difference/a frequency and is not greatly varied.
Small magnetic field can be sensed over a wider range of magnetic field than in an example where variation in intensity is given as a signal. Namely, high resolution sensitivity to magnetism intensity can be maintained. Resolution sensitivity to magnetism intensity depends on resolution of a frequency.
A magnetism measurement method presented here includes a procedure of sweeping a microwave frequency, a procedure of specifying the microwave frequency at which intensity of fluorescence measured during sweep exhibits a relative minimum value, a procedure of detecting magnetism intensity based on the specified frequency, and a procedure of measuring a temporal change pattern of magnetism intensity by repeating detection of magnetism intensity by repeating sweep of the frequency, with the use of a diamond magnetic sensor including diamond containing at least one NV− center, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the NV− center of the diamond, and a fluorescence sensor which receives fluorescence radiated from the NV− center of the diamond and including a pattern measurement apparatus which measures a temporal change pattern of magnetism intensity based on variation in fluorescence intensity.
A phase sweep apparatus instead of the frequency sweep apparatus can be employed in an alternative embodiment. Instead of the procedure of sweeping a frequency, a magnetism measurement method including a procedure of sweeping a phase can be implemented. A method of emitting combined waves of a microwave having a desired frequency width and a microwave resulting from phase shift thereof and sweeping the phase is applicable. In this case, magnetism intensity can be known by obtaining a spectrum as variation in fluorescence intensity with respect to a frequency by using Fourier transform of an amount of change in fluorescence intensity with an amount of phase shift.
Though the conventional approach described with reference to
A conventional approach to sensing of variation in fluorescence intensity can also obtain a temporal change pattern of magnetism intensity by digitizing outputs from a fluorescence intensity sensor. In this case, time response is determined by a response speed of the fluorescence intensity sensor and a time interval of sampling, and very high-speed response can be expected. The approach described with reference to
Therefore, an interval of data sampling (a time from one sweep to next sweep in a plurality of times of sweep) is dependent on a rate of sweep of a microwave frequency. A preferred sweep rate or the like is as described previously. A pattern of variation in magnetism intensity as a background or an environment is preferably not higher than 100 Hz or 1000 Hz, and a pattern of variation in magnetism intensity to be captured in that range is preferably higher than 1 kHz, more preferably higher than 100 kHz, and further preferably higher than 1 MHz. It is not the case, however, if magnetism intensity to be captured in ambient magnetism intensity is successfully separated from the ambient magnetism intensity by analysis. In analyzing a temporal change pattern, it is effective to leave only magnetism intensity to be captured by subtracting ambient magnetism intensity, and preferably a frequency lower than 70 Hz, more preferably a frequency lower than 1 kHz, or further preferably a frequency lower than 10 kHz is cut off.
In a manner of use of phase shift described above, magnetism intensity is obtained each time an amount of phase shift is swept. Therefore, an interval of data sampling is dependent on a rate of sweep of an amount of phase shift of a microwave.
<Second Embodiment>
(Diamond Magnetic Sensor)
A magnetic array 3 as a magnetic field generator is arranged in correspondence with the plurality of NV− center regions. Magnetic array 3 is arranged on a main surface or a rear surface of diamond 2. In magnetic array 3, a plurality of magnetism generation members are arranged at positions corresponding to locations of the plurality of NV− center regions in diamond 2. Therefore, it is easier to prepare (arrange in correspondence) regular arrangement than random arrangement. In general, the magnetism generation member is made of a magnetic material (a ferromagnet) and should only have already known magnetism and be small enough for arrangement. A magnetic material may be patterned, or a sheet of a magnetic material with a magnetic pattern can also be employed. Intensity of magnetic field formed in an individual NV− center region by the magnetic material can be controlled based on a volume (an amount) of the magnetic material, and intensity can be known by measuring in advance a spatial distribution in an environment free from magnetic field.
Ultimately a single NV− may implement the NV− center region described previously, and a magnetism generation source may ultimately be nuclear magnetism of 13C or 15N representing an isotope in diamond. Different magnetic field intensity to be applied to NV− is automatically and randomly generated by a difference in shortest distance between 13C or 15N and NV−. When the NV− center can individually be observed with a microscope, each one corresponds to each of a plurality of randomly arranged NV− center regions.
The greatest feature of the present embodiment, that is, a form that a different magnetic array and an array of NV− center regions are arranged in single piece of diamond 2, is to allow NV− centers which have experienced various types of Zeeman splitting to spatially separately be known. The ability to separately know NV− centers means instantaneously knowing a state that different microwave frequencies have been changed, which represents one form of assistance in sweep of a microwave frequency. Relation between magnetism intensity and a microwave frequency is preferably the same for all NV− center regions. Even though the relation is different, however, no problem arises if the NV− center region is initially individually calibrated.
Referring to
In order to control a frequency of microwaves and to measure intensity of received fluorescence to obtain a temporal change pattern, a pattern measurement apparatus 40 is provided.
Description here shows an example in which a plurality of NV− centers are located in a single diamond substrate. A plurality of NV− centers may be located in a plurality of diamond substrates and the plurality of diamond substrates may be combined. A single piece of diamond is preferred because the sensor is compact as a whole and measurement in an identical magnetic field environment is facilitated. For example, an already known method of forming a vacancy by electron beam irradiation in diamond containing nitrogen in its crystal lattices and thereafter forming an N-V defect by annealing can be employed as a method of forming an NV− center in diamond.
Relation of an NV− center region in diamond 2 with magnetic array 3 and fluorescence sensor array 31 will further be described with reference to
In the magnetic array, a magnetic material which produces already known magnetism is arranged at a location corresponding to each of regions a to e in diamond 2 in a plan view.
A filter which cuts off excitation light can be arranged as appropriate between an NV− center and a light reception element. A part of the NV− center can be magnified to condense light therefrom by a lens, and the light can be guided to the light reception element as appropriate. A scheme for confining excitation light such that the excitation light is less likely to exit to the outside can also be provided as appropriate between the excitation light generator and the diamond including NV− centers.
A signal detected by such a sensor will be described below.
A frequency difference between relative minimum values of intensity of fluorescence produced in correspondence with magnetic field applied to region a is denoted by ΔFa, a frequency difference between relative minimum values of intensity of fluorescence produced in correspondence with magnetic field applied to region b is denoted by ΔFb, a frequency difference between relative minimum values of intensity of fluorescence produced in correspondence with magnetic field applied to region c is denoted by ΔFc, a frequency difference between relative minimum values of intensity of fluorescence produced in correspondence with magnetic field applied to region d is denoted by ΔFd, and a frequency difference between relative minimum values of intensity of fluorescence produced in correspondence with magnetic field applied to region e is denoted by ΔFe. In this case,
Specifically, relation of 2×ΔF1=ΔFb-ΔFa=ΔFc-ΔFb=ΔFd-ΔFc=ΔFe-ΔFd is established.
When magnetic field to be detected is applied to the sensor with such setting being made, magnetic field to be detected is added to magnetic field originally applied by the magnetic array in each NV− center region. Therefore, an interval between relative minimum values of fluorescence intensity from each region with respect to a microwave frequency is uniformly varied by an amount of magnetic field added from the initial state. With variation being denoted as Fx, frequency differences corresponding to region a to region e are varied to ΔFa+Fx, ΔFb+Fx, ΔFc+Fx, ΔFd+Fx, and ΔFe+Fx, respectively.
Measurement of a temporal change pattern of magnetism intensity by this sensor will now be described. It is assumed that, after the initial state in
An extent of detectable magnetic field can be broadened by increasing the number of NV− center regions and further increasing the number of magnetic fields applied in the initial state, which means that a measurement range can be broadened to an order-of-magnitude wider range of magnetic field without sweeping a microwave frequency even in measurement with a frequency being fixed. Therefore, a temporal change pattern of relatively high magnetism can be measured without being restricted by a time interval At between sweeps of a microwave frequency as in data shown in
The magnetism measurement method presented here includes a procedure of measuring fluorescence intensity for each NV− center region and a procedure of measuring a temporal change pattern of magnetism intensity based on a position of variation in individual fluorescence (lowering from an example where magnetic field is zero) and variation in fluorescence intensity with the use of a diamond magnetic sensor including diamond in a form of a plate containing a plurality of NV center regions in a plan view, a magnetic array arranged in correspondence with the NV− center regions, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the diamond, and a fluorescence sensor array which individually receives fluorescence produced from the plurality of NV− center regions. As in the first embodiment, a pattern of variation in magnetism intensity as a background or an environment is again preferably not higher than 100 Hz or 1000 Hz, and a pattern of variation in magnetism intensity to be captured is preferably higher than 1 kHz, more preferably higher than 100 kHz, and further preferably higher than 1 MHz. It is not the case, however, if magnetism intensity to be captured in ambient magnetism intensity is successfully separated from the ambient magnetism intensity by analysis. In analyzing a temporal change pattern, it is effective to leave only magnetism intensity to be captured by subtracting ambient magnetism intensity, and preferably a frequency lower than 70 Hz, more preferably a frequency lower than 1 kHz, or further preferably a frequency lower than 10 kHz is cut off.
<Third Embodiment>
(Diamond Magnetic Sensor)
As described previously, it has been stated in the second embodiment that measurement over a wide range can be conducted without sweeping a microwave frequency, by measuring fluorescence detected in each NV− center region as being spatially separated with the use of a diamond magnetic sensor including a plurality of NV− center regions, a magnetic array, and a fluorescence sensor array. Measurement can also be conducted together with sweep of a microwave frequency. These features can further be developed. Specifically, a diamond magnetic sensor according to a third embodiment does not require sweeping of a microwave frequency, and in addition, measures a temporal change pattern of magnetism intensity based on variation in overall fluorescence intensity detected in each NV− center region without knowing individual fluorescence from a spatially separated NV− center.
A magnetism measurement method presented here includes a procedure of measuring intensity of overall fluorescence and a procedure of measuring a temporal change pattern of magnetism intensity based on variation in overall fluorescence intensity without using a fluorescence sensor array which individually receives fluorescence produced from a plurality of NV− center regions in a diamond magnetic sensor.
In the present embodiment, a diamond magnetic sensor including diamond in a form of a plate containing a plurality of NV− center regions in a plan view, a magnetic array arranged in correspondence with the NV− center regions, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the diamond, and a fluorescence sensor which receives fluorescence produced from the NV− center regions of the diamond, magnitude of a relative minimum value of intensity of fluorescence produced from the plurality of NV− center regions being weighted differently for each NV− center region in accordance with a frequency of the emitted microwaves and magnetic field applied by the magnetic array, is employed.
As will be described later, variation from a maximum value to a relative minimum value of fluorescence intensity with respect to a microwave frequency draws a gentle curve by simultaneously superimposing on each other, valleys including relative minimum values of weighted intensity of fluorescence produced from the plurality of NV− center regions. Therefore, even though a frequency varies over a wide range, change over time in fluorescence intensity at a specific frequency can be converted to change over time in microwave frequency by conducing measurement with a frequency being fixed to a specific frequency without sweeping a frequency. Namely, change over time in fluorescence intensity can be converted to a temporal change pattern of magnetism intensity. Furthermore, when at least a part is within a measurable range even though a part goes beyond the measurable range, effective data can be obtained.
By way of example, a magnetic array including ten NV− center regions as in region a in
A result of simulation as to the above is shown with reference to
Therefore, a numeric value of a microwave frequency can be determined based on a numeric value of a total of all fluorescence intensities. When a half-value width of the valley in each NV− center region is smaller than an interval between relative minimum values in each NV− center region (see
It can be estimated from the result of simulation above that a large valley over a width of ΔFe shown in
Though a method of simultaneous collective measurement of a plurality of NV− center regions is thus lower in sensitivity to magnetic field than measurement only of an individual NV− center region, a range of measurement (range) of magnitude of magnetic field can be broadened. Therefore, it is effective in terms of measurement of variation in large magnetic field. An object to be measured includes preferably at least one thousand NV− center regions, more preferably at least ten thousand NV− center regions, and further preferably at least one hundred and sixty thousand NV− center regions. As the number of regions is larger, the entire curve is smoother. Since an effect thereof is in proportion to a square root of the number, sensitivity is improved by orders of magnitude. As in the present method, in a test sample prepared to allow collective measurement, two relative minimum values of a profile representing a result of collective measurement (a graph of fluorescence intensity representing frequency dependency of microwaves) are preferably observed owing also to an effect of its own set magnetic field. When there is a single relative minimum value, with application of external magnetic field, the relative minimum value is consequently split into two values, which reflect different states between the initial state and a state of application of external magnetic field, and analysis becomes complicated. Therefore, a relative minimum value of fluorescence intensity is preferably initially split into two values while there is no external magnetic field being applied.
(Mechanism for Eliminating Ambient Magnetic Field)
Though the first to third embodiments are described above, in actual measurement of magnetism, various magnetic fields are present other than magnetic field to be detected, which interfere detection of weak magnetism. Such magnetic field originates from magnetism of the earth, magnetism originating from a current or the like of an apparatus, and spatial field such as radio waves, and these magnetic fields other than magnetic field of interest of measurement are collectively called ambient magnetic field. In using the diamond magnetic sensor according to the first to third embodiments, elimination of ambient magnetic field is demanded in order to measure only magnetic field to be detected. In order to eliminate ambient magnetic field, shield against ambient magnetic field and cancellation of ambient magnetic field are possible.
In order to cut off ambient magnetic field, a magnetic shield is effective. Magnetism is preferably prevented from entering a position of the sensor, for example, by arranging a soft magnetic material high in permeability such as Permalloy around the diamond magnetic sensor as a method of eliminating all ambient magnetic fields. It is possible to provide a sealed space by using a member with such a shielding effect or to eliminate magnetic field by using the Meissner effect of a superconducting material.
Only magnetic field to be a signal to be detected is guided to a sensor while all ambient magnetic fields are thus eliminated. When magnetic field to be detected is fluctuating magnetic field high in frequency, an antenna can be arranged in the inside of the magnetic shield so that fluctuation in current can be introduced into the inside of the magnetic shield through the antenna.
A cancellation coil is also preferably used as a method of canceling ambient magnetic field. The cancellation coil serves to set ambient magnetic field ideally to zero by generating magnetic field reverse in orientation to the ambient magnetic field in the sensor (which is also referred to as cancellation magnetic field below). It is difficult to cancel all ambient magnetic fields with cancellation magnetic field. Cancellation to some extent can be achieved, however, by reversing a specific magnetism pattern assumed in advance or a magnetism pattern separately detected in the vicinity of the sensor to generate cancelation magnetic field. For example, it is relatively easy to cancel only alternating-current (AC) magnetic field having a specific frequency. It is also possible to cancel a magnetic field pattern at a frequency equal to or lower than a frequency including a main magnetic field pattern in an environment and not to cancel a magnetic field pattern at a higher frequency including a magnetic field pattern to be sensed. A method of generating magnetic field by forming double coils of a cancelation coil and an introduction coil, canceling all magnetic field patterns with the cancellation coil, and introducing only a frequency of a magnetic field pattern around a frequency including a sensing signal through the introduction coil as an antenna can also be selected.
A direction of magnetic field can be detected by using a plurality of NV− centers in diamond different in direction. With this function, ambient magnetic field may be canceled. Magnetic field to be measured is often different also in orientation from ambient magnetic field. Since NV− centers in diamond can be designed to have a sensor for detecting magnetic fields in four orientations, an orientation and magnitude of magnetic field can be sensed. By outputting magnitude and an orientation of magnetic field perpendicular to ambient magnetic field, information on cancellation of ambient magnetic field can be obtained.
It is difficult to thus reduce ambient magnetic field completely to zero. By minimizing ambient magnetic field, however, an effect of elimination of ambient magnetic field by a method which will be described later can be enhanced.
(Diamond Magnetic Sensor Module)
The diamond magnetic sensor according to the first to third embodiments is preferably configured as a diamond magnetic sensor module in which components are arranged on a single circuit board directly or with another member being interposed. Diamond, a microwave generator, an excitation light generator, and a fluorescence sensor or a fluorescence sensor array are mounted on a single circuit board, and power supply and signal wiring are implemented by a wiring pattern on the circuit board.
A cancellation coil 70 is provided at a location corresponding to diamond 1 on a rear surface of circuit board 60. Though cancellation coil 70 is not essential, cancellation coil 70 can cancel desired magnetic field. Cancellation coil 70 can be formed as a printed wire on circuit board 60, and formation as such obviates the need for a separate coil component and space efficiency is preferably good.
The entire circuit board on which components are thus mounted is covered with magnetic shield member 80. Though magnetic shield member 80 is not essential, ambient magnetic field can be cut off by magnetic shield member 80. Measurement can be conducted by providing an opening in a part of magnetic shield member 80 and bringing magnetism to be measured closer or guiding magnetic field to the opening. Alternatively, if an object to be measured itself can be placed in the inside of magnetic shield member 80 without providing an opening, such a form of arrangement is desirable. Magnetic field can also be introduced as a current by providing an antenna (not shown) in the inside of magnetic shield member 80, without providing an opening.
Cancellation coil 70 and magnetic shield member 80 are the same as in
A drive circuit for each component and an auxiliary circuit in connection with a power supply and additionally a processor for signal processing can also be arranged on the same circuit board. A mounted electric circuit, however, may be a source of magnetic noise. Therefore, extra electric circuits and wires are preferably as few as possible. If possible, the entire module or only a portion around diamond serving as a sensor portion is preferably covered with a magnetic shield or configured such that ambient magnetic field is eliminated therefrom by a cancellation coil. A configuration of a diamond magnetic sensor as a module on a single circuit board as such is preferred in terms of elimination of ambient magnetic field or a compact size and ease in arrangement thereof in close proximity to an object to be detected such as a living body.
The configuration of the sensor as a whole is thus compact. Improvement in reliability of the sensor such as a stabilized optical axis, improved efficiency in irradiation with excitation light and irradiation with microwaves, and enhanced stability of a position of irradiation is achieved.
(Sensor Portion Detachable Diamond Magnetic Sensor Module)
It is effective to space diamond 1 (
It is also important to facilitate emission of microwaves. Use of a parabolic antenna is effective and use of an oval spherical antenna is more effective. Efficiency is significantly higher by setting a portion for oscillating microwaves at a focus of the antenna and setting diamond to be irradiated therewith at another focus. A distance between the sensing portion of diamond and a closest portion such as an electronic circuit portion other than that or an antenna portion of a microwave oscillator is preferably not shorter than 10 cm, more preferably not shorter than 20 cm, and further preferably not shorter than 50 cm. When a high voltage is generated around a diamond portion and the closest portion is located nearby, a person who is conducting measurement and a measurement instrument are affected by discharging from a high voltage portion to an immeasurable extent. An opening in each antenna has a diameter preferably not smaller than 15 cm, more preferably not smaller than 20 cm, and further preferably not smaller than 30 cm. This is because it becomes difficult to converge microwaves at one focus when a size of the opening is greater than a wavelength of microwaves.
The diamond magnetic sensor can be implemented as a module or an apparatus structured such that diamond serving as the sensing portion and other electronic circuit portions are spaced apart from each other by a plate (glass or quartz) transparent to a visible light region or an infrared region and arranged in environments different from each other. Thus, magnetism in an environment where diamond is placed can be measured by using highly resistant diamond even in an environment against which an electronic circuit is not resistant (an acid environment, an alkali resistant environment, a corrosion resistant environment, a pressure environment, a high-temperature environment, and a high-humidity environment). The environment refers to an environment in a gas atmosphere or in a strong liquid such as water, acid, and alkali. It is very difficult for other sensing materials to obtain high reliability in such an environment.
Noise caused by the electronic circuit portion is significantly lowered at a distance by at least 1 cm from the electronic circuit portion. Therefore, diamond and the electronic circuit portion are preferably spaced apart from each other by at least 1 cm. A distance therebetween is more preferably not shorter than 2 cm and further preferably not shorter than 5 cm.
(Resolved Analysis of Ambient Magnetic Field)
Since the diamond magnetic sensor according to the first to third embodiments is able to measure a temporal change pattern of magnetism intensity, it can detect based on the temporal change pattern, small magnetic field with influence by ambient magnetic field being excluded. For example, when a pattern including a plurality of AC magnetic fields is present as ambient magnetic field, magnetic field less than 1/10 of largest magnetic field in the magnetic field pattern having largest magnetic field among them can be sensed as being separated and extracted.
A temporal pattern (i) of ambient magnetic field is obtained by measurement in the absence of an object to be measured. A frequency component of ambient magnetic field is found by frequency analysis of data measured in advance. The found frequency is denoted as f0. Though description about a single frequency is given in the present example, a plurality of frequency components are desirably found when a plurality of components are superimposed on one another.
One method of separating and extracting the signal (ii) from the measured temporal change pattern (iii) is filtering. When a signal is analog, a high-pass filter which filters out a signal not higher than frequency f0 can be employed. The signal (ii) can be obtained by filtering the signal (iii). The temporal change pattern is generally obtained as a data string of digitally processed discrete values in an actual apparatus. In this example as well, the signal (ii) can be obtained by implementing an arbitrary filter by using an already known digital filtering technique.
Effective filtering in an example where a plurality of frequencies are present as being mixed is achieved by using Fourier analysis. By subjecting the measured temporal change pattern (iii) to digital Fourier transform, the temporal change pattern can be separated into frequency components, and a frequency component specified in advance as ambient magnetic field or an assumed frequency component among the frequency components should only be excluded. By converting the excluded signal back to the temporal change pattern with a reverse Fourier transform approach, the signal (ii) can be obtained. Other signal processing means such as a method of making use of an auto-correlation function of the signal may be employed.
Though description is given above with AC magnetic field being assumed as ambient magnetic field, much noise can also be understood as superimposition of AC magnetic fields. Ambient magnetic field containing broad frequency components such as white noise can also be separated. A signal to be measured can be taken out by analyzing a frequency component included in a measured temporal change pattern and extracting and separating a signal component different from a noise component investigated and analyzed in advance. Thus, according to the diamond magnetic sensor in the present application, a temporal change pattern of magnetism intensity can be obtained and weak magnetic field can efficiently be measured with ambient magnetic field being eliminated.
(Analysis of Temporal Change Pattern by Using Intermittent Data)
Continuous measurement of a temporal change pattern of magnetic field is effective for analyzing data. Even though actual variation in magnetic field goes beyond a measurable range to lead to failure in obtaining continuous data and success in obtaining only intermittent data, a temporal change pattern within the measurable range can help estimation outside the measurable range. If a temporal change pattern is predicted or has already been known, general outlines can be obtained based on values obtained within the measurable range in consideration of the temporal change pattern also inclusive of the outside of the measurable range. Specifically, if the temporal change pattern has been known to consist of sine waves, cosine waves, or triangular waves, a phase and a maximum value can be calculated based on values of some of them. This is also applicable to each of the first to third embodiments.
<Preferred Manner of the Present Invention>
Another preferred manner of the present invention is additionally described below.
(Additional Aspect 1)
A diamond magnetic sensor including diamond containing at least two NV− centers different in direction of N-V bond, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the NV− centers of the diamond, a fluorescence sensor which individually receives fluorescence produced from the respective NV− centers of the diamond different in direction of N-V bond, and a pattern measurement apparatus which measures a pattern of variation in magnetic field intensity and azimuth of magnetic field based on variation in intensity of individual fluorescence.
(Additional Aspect 2)
The diamond magnetic sensor described in additional aspect 1, in which the pattern measurement apparatus measures a spatial direction pattern of the magnetic field intensity based on a spatial distribution of fluorescence intensity corresponding to a spatial distribution of each NV− center.
(Additional Aspect 3)
The diamond magnetic sensor described in additional aspect 1, in which the pattern measurement apparatus measures a spatial direction pattern of the magnetic field intensity based on a spatial distribution of fluorescence intensity corresponding to a spatial distribution of each NV− center and a temporal change pattern of the magnetic field intensity based on fluorescence intensity of each NV− center.
(Additional Aspect 4)
The diamond magnetic sensor described in any one of additional aspects 1 to 3, in which the pattern measurement apparatus performs a function to control sweep of a frequency of the microwaves, a function to specify the frequency of the microwaves at which a relative minimum value of the fluorescence intensity is produced, and a function to detect magnetic field intensity based on the specified frequency, and measures a temporal change pattern of magnetism intensity corresponding to each NV− center by repeating detection of the magnetic field intensity by repeating sweep of the frequency.
(Additional Aspect 5)
The diamond magnetic sensor described in any one of additional aspects 1 to 4, the diamond magnetic sensor further including a data analysis apparatus which separates intensity of magnetic field originating from a measurement environment and intensity of magnetic field originating from an object to be measured from each other based on the spatial direction pattern.
(Additional Aspect 6)
A diamond magnetic sensor including diamond containing at least one NV− center, a microwave generator which emits microwaves to the diamond, an excitation light generator which emits excitation light to the NV− center of the diamond, a fluorescence sensor which receives fluorescence produced from the NV− center of the diamond, and a pattern measurement apparatus which measures a temporal change pattern of magnetic field intensity based on variation in fluorescence intensity sensed by the fluorescence sensor, the microwave generator generating a combined wave of a microwave having a desired frequency width and a microwave resulting from phase shift of the microwaves, the pattern measurement apparatus measuring a temporal change pattern of the magnetic field intensity with a function to control sweep of an amount of phase shift of the combined wave, by repeating detection of the magnetic field intensity by repeating sweep of the amount of phase shift.
Results of experiments are shown below.
(Preparation of Sample for Sensor)
Samples A to D of single-crystal diamond as below were initially prepared.
(1) Sample A
Sample A was prepared by manufacturing single-crystal diamond containing at most 0.1 ppm of substitutional nitrogen by a high-temperature and high-pressure method. In manufacturing, a sample containing a small amount of nitrogen was obtained by adding a metal serving as a nitrogen getter to a solvent.
(2) Sample B
Sample B was prepared by manufacturing single-crystal diamond controlled to contain 60 ppm of substitutional nitrogen by a high-temperature and high-pressure method. In manufacturing, a uniform sample of which uniformity of impurities was within ±25% was obtained by controlling a concentration of nitrogen by a method of eliminating nitrogen naturally introduced into a solvent and adding a nitride (for example, FeN) to the solvent.
(3) Sample C
Sample C was prepared by manufacturing CVD single-crystal diamond containing at most 20 ppb of nitrogen and at most 1 ppb of substitutional nitrogen by employing sample A of single-crystal diamond in (1) as a seed substrate and epitaxially growing diamond with CVD. In manufacturing, for reducing a nitrogen impurity and other impurities, not only a high-purity seed substrate was employed but also such schemes as addition of an appropriate amount of oxygen atoms and paving of an area extending by +30 mm around a holder with a high-purity diamond plate material were adopted.
(4) Samples D1 and D2
Samples A, B, and C were made of diamond containing isotopic carbon at a natural abundance ratio. On the other hand, samples D1 and D2 were prepared by manufacturing by a high-temperature and high-pressure method, single-crystal diamond containing 50 ppm and 100 ppm of substitutional nitrogen, respectively, and containing 13C at an abundance ratio of 5%. The samples were uniform, with uniformity of impurities being within ±25%.
As a result of evaluation of a concentration of nitrogen contained in samples A, B, C, D1, and D2 of single-crystal diamond with SIMS analysis, the concentration of substitutional nitrogen substantially matched with contained nitrogen. The concentration of substitutional nitrogen in sample C made of single-crystal diamond was substituted with a total of a density of NV− light emission centers and a density of NV0 light emission centers. Since the concentration of nitrogen was low and vacancies were sufficiently introduced, it could be estimated that there was no difference by orders of magnitude. Each of samples A, B, and C is a concentration in a measured portion. Vacancies (V) were introduced by electron beam irradiation (irradiation conditions including energy of 4 MeV and a radiation dose of 20 MGy), and bonded to substitutional nitrogen in subsequent annealing (three hours at 1600° C.). Formation of NV− centers was confirmed based on photoluminescence. In samples A and C, an NV− center as being isolated alone could be observed. In samples B, D1, and D2, innumerable aggregates of NV− centers could be observed.
Samples E and F as below were manufactured.
(5) Samples E1 and E2
A sample which contained NV− centers substantially comparable to those in sample B was initially manufactured, and a rear surface thereof was polished to 100 μm and further etched by reactive ion etching to a final thickness of 70 μm. An array of dots having diameters of approximately 5, 8, 13, 20, and 30 μm was formed in lattices at an interval of 200 μm by vapor depositing Fe on the rear surface to a thickness of 2 μm. The Fe dots were prepared at a number ratio of approximately 10:8:6:4:2.
Then, an A1 mask of 20 μm ϕ was made in lattices at an interval of 200 μm on a front surface side with photolithography and diamond including NV− centers was etched (a depth of etching being set to 40 μm). The sample including the etched portion as it was adopted as a member for manufacturing sample E1. The sample in which the etched portion was again buried by epitaxial growth was manufactured, and adopted as a member for manufacturing sample E2. Since a position of the A1 mask was substantially accurately matched with a position where Fe dot array was formed on the rear surface, a member for manufacturing sample E1 in which small columnar diamond including NV− centers was located on the Fe dot array and a member for manufacturing sample E2 in which portions including NV centers were scattered over the Fe dot array could be manufactured. Finally, sample E1 including NV− centers different in magnetic field environment was manufactured by magnetizing Fe in the member for manufacturing sample E1. Sample E2 including NV− centers different in magnetic field environment was manufactured by magnetizing Fe in the member for manufacturing sample E2. Present samples E1 and E2 were each made into the diamond magnetic sensor including a magnetic array (a diamond substrate for a magnetic sensor).
(6) Sample F
A sample F was made by manufacturing an array including NV− centers partially in lattices by a method substantially the same as that for sample E. Specifically, an array of NV− centers was manufactured by drilling holes of 40 μm ϕ in lattices at an interval of 200 μm in a lead plate of 0.5 mm and introducing defects in lattices by emitting electron beams with the plate being adopted as a mask, instead of making NV− centers all over in a step of preparing a sample similar to sample B. Other features such as a method of forming a magnetic array (Fe array) on the rear surface are the same as in manufacturing sample E.
An experimental apparatus configured as shown in
Samples A and C were searched for a single fluorescent point by magnifying an image of a surface of each sample with the lens. What was closest to the sample (diamond 100) was an objective lens and a distance therebetween was approximately 1 mm.
Then, an apparatus which generated a simulated magnetic waveform was prepared. A copper wire X 116 of 0.8 mm ϕ was prepared, and an AC current to be fed to copper wire X 116 by an AC current source 122 was controlled. AC was set to 60 Hz and a current value was set as appropriate. A copper wire Y 118 of 0.1 mm was arranged in proximity to and in parallel to copper wire X 116 so that a pulsed current could be fed from a pulsed power supply 124. The pulsed current was set to have a pulse interval of 60 Hz and a pulse width of 1 msec. Copper wire X 116 and copper wire Y 118 were arranged at a closest distance of 0.5 cm from samples A and C of diamond configured to perform sensing. AC current source 122 and pulsed power supply 124 implemented a simulation circuit for generating a simulating signal to be sensed.
An experiment as below was conducted as preparatory measurement. When samples A and C of diamond were irradiated with semiconductor laser beams having a wavelength of 520 nm while they were irradiated with microwaves with a constant direct-current (DC) current being fed to copper wire X 116, red fluorescence having a wavelength of approximately 638 nm was detected. When a frequency of microwaves was swept around 2.87 GHz, fluorescence exhibited two relative minimum values (valleys) at different frequencies (see
Then, main measurement was conducted. An AC current of 60 Hz (a highest current of 1.2 A) was fed to copper wire X 116. A current through copper wire Y 118 was zero. The experiment was conducted in a box free from influence by magnetism of the earth. The diamond was excited by the semiconductor laser and irradiated with microwaves, and a frequency of the microwaves was swept while intensity of red fluorescence at a wavelength of approximately 638 nm was measured. A relative minimum value was detected based on the obtained waveform of fluorescence intensity by sweeping the microwave frequency for a short period of time (a sweep period being not longer than 1 msec.), and a frequency corresponding thereto was stored. Thus, a temporal change pattern of the frequency corresponding to the relative minimum value was obtained. This temporal change pattern could be converted to a magnetism temporal change pattern. This part was performed by an apparatus which could obtain data on temporal change in microwave frequency corresponding to the relative minimum value and convert the data to a magnetism temporal change pattern.
A pulsed current (having a maximum current value of 10 msec.) was fed to copper wire Y 118 while the AC current was fed to copper wire X 116.
Based on comparison between
Since the conventional diamond magnetic sensor mainly aimed to be high in sensitivity (to sense very small magnetic field), it suffered from overrange before measurement and at a time point when there was a little base magnetic field, and it was unable to know a waveform of a current which produced magnetic field, by sensing a temporal change pattern. According to one manner of the present invention, a rate of sweep of a frequency was raised and data was interpreted as a temporal change pattern. Therefore, a measurable range of magnetic field was significantly larger and even minor variation in magnetic field therein could be observed.
According to the present method, when a pulsed current higher in frequency component was to be detected, a frequency should be swept faster and finer. When a range of frequencies to be swept was broader, however, it was found efficient to trace only a valley as a single relative minimum value and to sweep a frequency around a relative minimum value expected based on time.
An experimental apparatus configured as shown in
For each of samples B, D1, and D2, semiconductor laser beams were emitted to a sample central portion without going through such an optical system as a lens, and red fluorescence radiated from the sample central portion was detected by a light reception element by using a panopticon at a magnification of 50× (a long lens 126). In order to prevent laser beams from entering the light reception element, a filter which cut off green light was employed. A microwave antenna distant by approximately 1 cm was closest to the sample (a diamond source material).
Then, an apparatus which generated a simulated magnetic waveform (AC current source 122 and pulsed power supply 124) was prepared as in Example 1. Copper wire X 116 and copper wire Y 118 were arranged at a closest distance of 0.5 cm from the sample of diamond configured to perform sensing.
Preliminary measurement as below was initially conducted. When the sample of diamond was irradiated with semiconductor laser beams having a wavelength of 520 nm while it was irradiated with microwaves, red fluorescence around a wavelength of 638 nm was detected. When a microwave frequency was swept around 2.87 GHz, fluorescence exhibited two relative minimum values (valleys) at different frequencies. Unlike Example 1, the valleys were wide and two valleys overlapped with each other.
It could be confirmed, however, that there were two relative minimum values. This is because of presence of NV− centers in various states (atoms having nuclear magnetism, such as 13C and 14N, being arranged around NV− centers) in samples B, D1, and D2. When a concentration of the NV− centers was high, a distribution width was larger and greater. By emitting microwaves at a frequency greatly distant from the frequency at the relative minimum value, fluorescence intensity exhibited the maximum value. Even when the microwave was fixed to a single frequency included in the valley at the relative minimum value and emission of the microwaves was stopped (output of microwaves was set to zero), fluorescence exhibited the maximum value.
Then, main measurement was conducted as below. A DC current was fed to copper wire X 116 by a constant current power supply, and it was confirmed that a frequency interval between two relative minimum values was varied in the sample of diamond nearby when the current was flowing. Samples B, D1, and D2 used in the present experiment were relatively gradual in variation in fluorescence intensity with respect to variation in magnetism, and a wide magnetic range could be confirmed based on fluorescence intensity.
Then, measurement as below was conducted: The sample was irradiated with pulsed beams as laser beams having a duty of 50% (a pulse width being half a cycle) in each of cycles of 10 msec. (100 Hz) and 0.1 msec. (10 kHz), and red fluorescence was observed. Consequently, emission in each cycle of 100 Hz and 10 kHz was confirmed while laser beams were emitted.
Supply of a constant current (1 A) to copper wire X 116 was turned on (power feed) or off (non-power feed) while a pulse interval (a cycle) of laser beams was set to 10 msec. (100 Hz), microwaves at a frequency corresponding to one of the two relative minimum values of fluorescence intensity were emitted, and fluorescence intensity attained to the relative minimum value.
Then, while a current of 1 A was fed to copper wire X 116 with a pulse interval (cycle) of laser beams being set to 0.1 msec. (10 kHz) and while fluorescence intensity was at the relative minimum value by emitting microwaves at a frequency corresponding to one of the two relative minimum values of fluorescence intensity, an AC current having a frequency of 60 Hz and a maximum value of 1.2 A was fed to copper wire X 116.
With copper wire X 116 and copper wire Y 118 being set, an AC current at 60 Hz having a maximum value of 1.05 A was fed to copper wire X 116 and a pulsed current having a pulse interval (cycle) of 60 Hz, a pulse width of 1 msec., and a maximum current value of 1 mA was fed to copper wire Y 118.
An experimental apparatus configured as shown in
Similarly to measurement with the use of measurement system 132, of intensity of radiated fluorescence by irradiating diamond 100 in proximity to copper wire X 116 with laser beams and microwaves while a current was supplied from AC current source 122 to copper wire X 116 and copper wire Z 120, intensity of radiated fluorescence was measured with the use of measurement system 134, by irradiating diamond 136 in proximity to copper wire Z 120 with laser beams and microwaves. A phase difference by 90° could be sensed by analyzing obtained results as above.
Since the conventional diamond magnetic sensor mainly aimed to be high in sensitivity (to sense very small magnetic field), it suffered from overrange if a measurement site was slightly displaced, and it was unable to know a waveform of a current which produced magnetic field by sensing a temporal change pattern. According to one manner of the present invention, single-crystal diamond in which various types of background magnetism were arranged around NV− centers was manufactured and sensitivity was maintained without allowing two relative minimum values of fluorescence intensity to disappear. Thus, a sufficient difference in fluorescence intensity (a difference between the relative minimum value and the maximum value being at least 2%) and a wide magnetic field range (not lower than 10 nT) could be ensured so that a temporal change pattern could be obtained. When a concentration of NV− centers was higher than 200 ppm, two relative minimum values could no longer be observed and a sufficient difference in fluorescence intensity could not be obtained. A sample X in which a concentration of 13C was 28% was prototyped separately to the sample above and subjected to measurement. Consequently, when a concentration of 13C was higher than 20% in spite of a concentration of NV< centers being 1 ppm, two relative minimum values could no longer be observed and a sufficient difference in fluorescence intensity could not be obtained. Furthermore, an experiment similar to the above was conducted with a pulse interval of laser beams being set to 1 μsec. Then, a similar phase difference could accurately been sensed. A pulsed current fed to copper wire Y 118 could also be sensed exactly in the same manner as in Example 1.
An experiment was conducted by using each of samples A, C, E1, E2, and F of diamond. When the experiment was initially conducted with a method the same as in Example 1 by using each of samples A and C (see
Then, an experiment for identifying fluorescence of dots aligned in lattices by magnifying samples E1 and E2 with a long lens set in a stage preceding a light reception element was conducted in the experiment system the same as in Example 2 (see
An experiment was conducted similarly to the above by using sample F. Consequently, though NV− center regions of sample F had a size of 40 μm ϕ, it could be confirmed that a function substantially the same as that of samples E1 and E2 (sensing of magnetism produced by an AC current and sensing of magnetism produced by a pulsed current in the AC current) could be performed.
As set forth above, individual slight variation in magnetism could be measured over a large magnetic field range by both of a method of making observation such that NV− centers served as at least one thousand luminous points (an individual one could be defined as an NV− center region) at a high magnification in each of samples A and C and addressing each of them and a method of forming different background magnetism by designing an array (NV− center regions) in lattices including a plurality of NV− centers at a low magnification in each of samples E1, E2, and F and combining the array with a magnetic array. Namely, small magnetic field in large magnetic field could be measured. A cause of magnetic field (for example, a current) could be specified by measuring such a temporal change pattern.
Though fluorescence intensity of an individual array was observed by using samples E1, E2, and F above, the entire sample was irradiated with excitation light in the present Example and intensity of fluorescence radiated from the entire sample was collectively observed. There were a plurality of dots analogous in characteristics (points in lattices), and a different number of dots were set for each different characteristic. Namely, the dots were weighted for each different characteristic. An analogous characteristic means NV− centers resonant at the same microwave frequency. The different characteristic means a different resonant microwave frequency. Therefore, a microwave frequency is known based on fluorescence intensity which exhibits a relative minimum value. Superimposition of all obtained fluorescence intensities provides one great variation in fluorescence intensity. Therefore, fluorescence intensity substantially determines a microwave frequency. As a resonant frequency is lower, the number of dots should be larger, and as a resonant frequency is higher, the number of dots should be smaller. By doing so, a graph of fluorescence intensity having a wide and large valley with respect to a microwave frequency can be formed. Relation between fluorescence intensity and a microwave frequency, that is, relation between fluorescence intensity and magnetism, was determined by performance of diamond and performance of design, and could be stored as a database in advance so that data on magnetism could be calculated based on fluorescence intensity. In addition, since arbitrary design could be made, relation between fluorescence intensity and magnetism could loosely be set and measurement over a wide range of magnetism could be conducted. Similarly, a temporal change pattern could also be obtained. When a current was fed to copper wire X 116 as in
An experimental apparatus configured as shown in
Arrangement of each of samples E1, E2, and F of diamond serving as the sensor portion remotely from a measurement electronic element (excitation semiconductor laser and a semiconductor light reception element) is the same as in Example 5. The sample of diamond serving as the sensing portion was set in an environment in vacuum (0.01 atmosphere), in water at a high pressure (10 atmospheres), and in oil at a high temperature (200° C.), laser beams and microwaves were emitted remotely through a window of quartz glass, and fluorescence was detected. A configuration, arrangement, and measurement conditions were otherwise the same as in Example 5. Though the environment around the sensing portion (the sample of diamond) was significantly different from the standard state (for example, one atmosphere (101325 Pa) 0° C.), measurement basically the same as above could be conducted.
The sample and the measurement system the same as in Example 1 were adopted, and a coil for generating magnetic field was arranged to cover the sample of diamond serving as the sensing portion. Magnetic field was generated such that AC magnetic field generated by an AC current through copper wire X 116 at a position where the sample of diamond was arranged was canceled by the coil for generating magnetic field. Since combined magnetic field formed by copper wire X 116 and the coil for generating magnetic field was not uniform on diamond, it could not cancel magnetic field in a strict sense. When a portion to be observed was small and AC magnetic field was expected, however, the magnetic field was substantially canceled. In this state, variation in magnetic field could be sensed at all phases of sinusoidal magnetic field which remained without being canceled and could be sensed as a temporal change pattern, and pulsed magnetic field in the AC magnetic field could be sensed as shown in
The sample and the measurement system the same as in Example 2 were adopted, and the sample of diamond serving as the sensing portion and a sensing circuit portion including an excitation semiconductor element for sensing and a light reception element were manufactured on the same circuit board so that magnetism and a temporal change pattern of magnetism could be sensed. By sensing AC magnetic field as shown in
An experiment was conducted by adopting the sample and the measurement system the same as in Example 7 and arranging also a coil for generating magnetic field as in Example 7. Magnetic field was generated such that the coil for generating magnetic field canceled AC magnetic field generated by an AC current through copper wire X 116 at a position where the sample of diamond was arranged, and magnetic field generated by a pulsed current through copper wire Y 118 was increased by another coil. The AC magnetic field caused by copper wire X 116 could be canceled as in Example 7, and magnetic field generated by copper wire Y 118 could be applied to the diamond as being amplified and could be sensed as a temporal change pattern of magnetism. Pulsed magnetic field in the AC magnetic field shown in
Though the present invention has been described above by describing embodiments, the embodiments are illustrative and the present invention is not restricted only to the embodiments. The scope of the present invention is defined by each claim in the scope of claims with reference to the description in detailed description of the invention and includes any modifications within the scope and meaning equivalent to the terms of the claims.
1, 2 diamond; 3 magnetic array; 3a, 3b magnetic material; 10 microwave generator; 11 frequency sweep apparatus; 12 microwave; 20 excitation light generator; 21 excitation light; 22 fluorescence; 30 fluorescence sensor; 31 fluorescence sensor array; 32a, 32b light reception element; 40 pattern measurement apparatus; 60 circuit board; 70 cancellation coil; 80 magnetic shield member; a, b, c, d, e, R1, R2, R3, R4 region; Cl cross-section; 100, 136 diamond (sample); 102 laser light source; 104 semiconductor light reception element; 106 optical lens system; 108 microscope lens; 110 triangular prism; 112 reflector; 114 microwave coil; 116 copper wire X; 118 copper wire Y; 120 copper wire Z; 122 AC current source; 124 pulsed power supply; 126 long lens; 128 capacitor; 130 resistor; 132, 134 measurement system; 138 oval spherical mirror
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017-029689 | Feb 2017 | JP | national |