1. Field of the Invention
The present invention relates to diaphragms for speakers and manufacturing methods therefor.
This application claims priority on Japanese Patent Application No. 2006-185712, the content of which is incorporated herein by reference.
2. Description of the Related Art
According to the conventionally-known manufacturing methods, thin wooden boards are subjected to press working or molding so as to produce diaphragms for use in speakers. Japanese Unexamined Patent Application Publication No. H06-178386 teaches that a single sheet of a thin wooden board is subjected to press working so as to produce a diaphragm, or plural sheets of thin wooden boards are laminated together and are then subjected to press working so as to produce a diaphragm. It also teaches that a thin wooden board is formed in a cone shape in advance and is then subjected to press working so as to produce a diaphragm.
Japanese Unexamined Patent Application Publication No. 2004-254013 teaches that a thin wooden board having a V-shaped cutout is prepared in advance; the thin wooden board is softened by way of the addition of water thereto; opposite sides along the V-shaped cutout are adhered together by way of primary pressing; the thin wooden board after the primary pressing is impregnated with a thermosetting resin; then, the thin wooden board impregnated with the thermosetting resin is subjected to secondary pressing so as to produce a diaphragm.
In general, thin wooden boards are easily broken or split along the grains thereof during press working or molding. For this reason, in the manufacturing method taught in Japanese Unexamined Patent Application Publication No. H06-178386, the thin wooden board is subjected to steaming prior to molding, or it is subjected to boiling using an alkali solution prior to molding, thus making the thin wooden board have flexibility, whereby it is possible to control the occurrence of cracks during the molding. It is necessary that the diaphragm formed by way of press working be subjected to treatment in order to improve the durability thereof. Therefore, a coat of urethane varnish is applied to the thin wooden board after press working. However, the aforementioned manufacturing method is complex because it needs various processes before or after the press working.
The manufacturing method taught in Japanese Unexamined Patent Application Publication No. 2004-254013 is also complex because it performs press working twice. Since the opposite sides of the V-shaped cutout of the thin wooden board are adhered together, directions of the grains greatly change at the boundary of the adhered portion. This causes irregularity in terms of directions of the grains in the diaphragm, which in turn degrades the acoustic characteristics of the diaphragm or which in turn causes cracks in the diaphragm along specific directions. In addition, the adhered portion is slightly increased in thickness compared with the thickness of the other portion of the diaphragm. That is, the diaphragm suffers from irregularity in terms of the thickness, which in turn degrades the acoustic characteristics thereof.
It is an object of the present invention to provide a diaphragm for use in a speaker, which is produced by way of a simple manufacturing method without causing defects during press working.
It is another object of the present invention to provide a diaphragm for use in a speaker, which is improved in strength and acoustic characteristics.
In a first aspect of the present invention, a diaphragm for use in a speaker includes a wooden vibrator that is formed using a plurality of thin wooden boards, which are impregnated with a resin and are integrally laminated together in a laminated structure having a curved shape, and a plurality of high density portions that are elongated in a radial direction from the center to the periphery of the wooden vibrator, wherein the wooden vibrator has a uniformly distributed thickness. Herein, the high density portion in a plan view is formed in a band-like shape, a wedge-like shape, or a sectorial shape; and the width of the high density portion in a plan view is gradually increased in the direction from the center to the periphery of the wooden vibrator.
In the above, the resin is selected from among an epoxy resin, urethane resin, polyester resin, and acrylic resin. The resin content of the wooden vibrator ranges from 10 weight-percent to 70 weight-percent. In addition, coloring such as dye or pigment is applied to the wooden vibrator as necessary. Furthermore, the thickness of the wooden vibrator ranges from 0.2 mm to 0.7 mm.
The wooden fiber directions of the thin wooden boards integrally laminated together mutually cross with prescribed angles therebetween. For example, the wooden fiber directions of three or more thin wooden boards respectively cross with the same angle therebetween. When N thin wooden boards (where “N” is an integer not less than two) are laminated together, the wooden fiber directions thereof respectively cross with an angle of 360/2N degrees therebetween.
As described above, since the wooden vibrator forming the diaphragm has the uniformly distributed thickness irrespective of the formation of the high density portions, it is possible to improve the acoustic characteristics. The wooden vibrator is reinforced by means of the high density portions and is thus increased in the mechanical strength thereof; hence, it is possible to increase the degree of freedom in design. Since the rigidity of the wooden vibrator is increased by means of the high density portions, it is possible to improve the durability of the diaphragm against high input signals. Since the thin wooden boards forming the wooden vibrator are impregnated with a resin, it is possible to increase the strength of the wooden vibrator and to avoid the degradation due to aging. Since the wooden fiber directions mutually cross with prescribed angles therebetween, it is possible to further increase the strength of the wooden vibrator.
In a second aspect of the present invention, a diaphragm for use in a speaker is manufactured by way of impregnating a plurality of thin wooden boards having flat rectangular shapes with a resin, forming a plurality of cutouts, which are elongated in directions along or crossing wooden fiber directions, in each of the thin wooden boards, integrally laminating the thin wooden boards together in such a way that the wooden fiber directions thereof cross each other, and performing thermal pressing on the thin wooden boards integrally laminated together so as to form a wooden vibrator serving as the diaphragm. Herein, the cutouts are each elongated in a direction from the periphery to the center of the thin wooden board. In addition, the thin wooden boards are subjected to thermal pressing after the opposite sides of the cutouts thereof are respectively connected together. Instead of the cutouts, it is possible to form a plurality of folded portions, which are elongated in directions along or crossing wooden fiber directions, in each of the thin wooden boards. Herein, the folded portions are each elongated in a direction from the periphery to the center of the thin wooden board. Furthermore, the thin wooden boards are integrally laminated together in such a way that the wooden fiber directions thereof lie along or mutually cross each other. Incidentally, the process for forming the cutouts or folded portions can be performed before the process for impregnating the thin wooden board with a resin solution.
According to the aforementioned manufacturing method, the thin wooden boards are impregnated with a resin in advance and are then subjected to thermal pressing. This causes the thin wooden boards to slip on each other during the thermal pressing; hence, it is possible to improve the formability of the wooden vibrator. Since the opposite sides of the cutouts are connected together during the thermal pressing, it is possible to easily form the high density portions, and it is possible to reduce the difference of thickness between the high density portions and the other portions; that is, it is possible to realize the diaphragm having a uniformly distributed thickness. When the cutouts are formed along the wooden fiber directions, it is possible to improve the strength of the diaphragm because the wooden fibers of the thin wooden boards are not broken by the cutouts. When the cutouts are formed in directions crossing the wooden fiber directions, the wooden fibers are partially broken so that the wooden fiber lengths are shortened, thus increasing the flexibility of the thin wooden boards. That is, it is possible to further improve the formability of the diaphragm. Since the thin wooden boards are increased in flexibility, it is possible to easily produce any types of diaphragms each having a relatively small radius of curvature. Since the cutouts are each formed in the direction from the periphery to the center of the thin wooden board, it is possible to form the high density portions elongated from the center of the wooden vibrator in a radial manner.
In addition, since the thermal pressing is performed after the opposite sides of the cutouts are connected together, it is possible to reliably form the high density portions. By connecting together the opposite sides of the cutouts, the thin wooden boards are each formed in a curved shape having a certain curvature. This greatly reduces the amount of deformation of the thin wooden boards during the thermal pressing; hence, it is possible to avoid the occurrence of cracks. Since the thin wooden boards are laminated together in such a way that the wooden fiber directions thereof cross each other, it is possible to further increase the strength of the diaphragm.
When, instead of the cutouts, the folded portions are formed in the thin wooden boards, it is possible to easily form the high density portions by way of thermal pressing. Since the folded portions are each formed in the direction from the periphery to the center of the thin wooden board, it is possible to form the high density portions elongated from the center of the wooden vibrator in a radial manner.
These and other objects, aspects, and embodiments of the present invention will be described in more detail with reference to the following drawings, in which:
The present invention will be described in further detail by way of examples with reference to the accompanying drawings, which are diagrammatically illustrated with sizes and dimensions not necessarily matching actual sizes and dimensions of products.
1. Diaphragm for Speaker
The speaker shown in
The diaphragm 1 is composed of a wooden vibrator having a cone shape, which is enlarged in diameter externally, wherein the voice coil 4 is attached to a small-diameter end of the diaphragm 1, and a large-diameter periphery of the diaphragm 1 joins the frame 6 via the collar 5.
The center cap 2 is composed of a wooden vibrator having a semi-spherical shape that projects outwardly so as to cover the cylindrical portion (or a center pole) of the magnet 7 inserted into the voice coil 4 in a non-contact manner. The center cap 2 is attached to the small-diameter end of the diaphragm 1.
A damper (not shown) is additionally arranged between the small-diameter end of the diaphragm 1 and the frame 6 so as to prevent lateral vibration. A wiring of the voice coil 4 is extended toward a terminal (not shown) formed at the small-diameter end of the diaphragm 1; hence, the wiring of the voice coil 4 is extracted onto the frame 6 via the terminal.
In the speaker of
More specifically, as shown in
It is possible to list various wooden materials for use in the formation of the thin wooden boards forming the wooden vibrator 11, such as birch, linden, beech, oak, cherry, spruce, maple, walnut, cedar, hinoki, red cedar, agatized wood, horse chestnut, elm, zelkova, and sapele. It is possible to list various resin materials impregnated into the thin wooden boards, such as an epoxy resin, urethane resin, polyester resin, and acrylic resin. Due to the resin impregnation, it is possible to improve the formability during the press working, and it is possible to avoid the degradation of the wooden vibrator 11.
It is preferable that the resin content of the wooden vibrator 11 range from 10 weight-percent to 70 weight-percent. When the resin content is above 10 weight-percent, it is possible to improve the formability and to avoid the degradation of the wooden vibrator 11. When the resin content is below 70 weight-percent, it is possible to improve the acoustic characteristics without causing a reduction of the content of the wooden material in the wooden vibrator 11.
A through-hole 11a is formed at the center of the wooden vibrator 11. The center cap 2 (see
It is preferable that the high density portion 12 in a plan view be formed in a band-like shape, a wedge-like shape, or a sectorial shape, for example. It is preferable that the width of the high density portion 12 in a plan view be gradually increased in a direction from the center to the periphery of the wooden vibrator 11. All of the high density portions 12 in a plan view can be formed in the same size; alternatively, the high density portions 12 can be formed in different sizes.
In
The high density portions 12 can be easily and visually distinguished from the other portions in plan view by horizontally viewing the wooden vibrator 11 that has deep-colored portions and light-colored portions; that is, the deep-colored portions of the wooden vibrator 11 can be visually recognized as the high density portions 12.
When the wooden vibrator 11 having the high density portions 12 is exposed to visible rays of light, it is possible to recognize the distinction between the prescribed portions having a relatively low light transmission ratio and the other portions having a relatively high light transmission ratio. That is, it is possible to recognize the prescribed portions having a relatively low light transmission ratio as the high density portions 12.
The wooden vibrator 11 having the high density portions 12 has a uniformly distributed thickness. In other words, the thickness of the high density portions 12 is substantially identical to the thickness of the other portions in the wooden vibrator 11. It is preferable that the thickness of the wooden vibrator 11 range from 0.2 mm to 0.7 mm. When the thickness is above 0.2 mm, it is unlikely to cause a reduction of the strength and rigidity of the wooden vibrator 11. When the thickness is below 0.7 mm, the rigidity is not increased so much; hence, it is possible to prevent the degradation of the acoustic characteristics.
It is possible for the wooden vibrator 11 to include coloring in addition to the resin. It is possible to use dye or pigment as the coloring.
It is preferable that the fiber directions of plural thin wooden boards laminated together be crossed with each other. For example, the fiber directions can be crossed with the same angle therebetween. Suppose that N thin wooden boards (where “N” is an integer not less than two) are laminated together. In this case, the fiber directions of the adjacently joined thin wooden boards are crossed with an angle of 360/2N degrees.
Due to the lamination of the thin wooden boards whose fiber directions cross each other, it is possible to improve the uniformity of vibration in the wooden vibrator 11; hence, it is possible to improve the acoustic characteristics. In addition, due to the mutually crossed fiber directions of the thin wooden boards, it is possible to further improve the mechanical strength of the wooden vibrator 11.
Due to the formation of the high density portions 12 in the wooden vibrator 11 adapted to the diaphragm 1, it is possible to realize fragmentarily different wooden densities in the wooden vibrator 11, which in turn realizes the distribution of natural resonance. Due to the distribution of natural resonance, it is unlikely to cause peaks in high-frequency ranges due to natural resonance; hence, it is possible to improve the acoustic characteristics.
In addition, the high density portions 12 reinforce the wooden vibrator 11, the mechanical strength of which is thus increased. Hence, it is possible to increase the degree of freedom in designing the diaphragm 1. Since the rigidity of the wooden vibrator 11 is increased by means of the high density portions 12, it is possible to reduce partial vibration, thus realizing relatively low distortion in sound. In addition, it is possible to improve the durability of the wooden vibrator 11 against high input signals.
Furthermore, since the wooden vibrator 11 has the uniformly distributed thickness irrespective of the formation of the high density portions 12, it is possible to design the speaker without consideration of detrimental effects regarding a limit to audio frequencies in the reproduction of high tone pitches.
Since the wooden vibrator 11 is composed of the thin wooden boards impregnated with the resin, it is possible to further increase the strength of the wooden vibrator 11 and to avoid degradation due to aging.
Since the fiber directions of the thin wooden boards forming the wooden vibrator 11 cross each other with prescribed angles therebetween, it is possible to further increase the strength of the wooden vibrator 11 adapted to the diaphragm 1.
2. First Manufacturing Method of Diaphragm
Next, a first manufacturing method of the diaphragm 1 will be described with reference to
As shown in
Next, the thin wooden board 21 having the through-hole 21a is impregnated with a resin. For example, a resin is dissolved into a solvent so as to produce a resin solution, into which the thin wooden board 21 is soaked. Alternatively, the resin solution is sprayed or applied to the thin wooden board 21.
As the resin material, it is possible to list an epoxy resin, urethane resin, polyester resin, and acrylic resin. It is preferable that the resin content of the thin wooden board 21 range from 10 weight-percent to 70 weight-percent.
Next, as shown in
Incidentally, the cutouts 22 can be formed in the thin wooden board 21 after the thin wooden board 21 is impregnated with the resin solution.
Next, as shown in
There are provided three sheets of the thin wooden boards 21, each of which is produced by way of the steps shown in
Next, as shown in
By way of the thermal pressing, the three sheets of the thin wooden boards 21 are integrally laminated together so as to form a laminated structure. Then, the outer periphery of the laminated structure is partially cut out along the dashed lines in
According to the first manufacturing method of the diaphragm 1, the thin wooden boards 21 are impregnated with the resin in advance and are then laminated together and subjected to thermal pressing. This makes it possible for the prescribed portions of the thin wooden boards 21 laminated together to easily slip on each other; hence, it is possible to easily perform shaping of the thin wooden boards 21, which are tightly held between the upper mold 31 and the lower mold 32, without causing wrinkles or unwanted lines. That is, the first manufacturing method reliably improves the formability of the wooden vibrator 11.
The connected portions 22b of the thin wooden boards 11 laminated together correspond to the high density portions 12; hence, it is possible to form the high density portions 12 in a regular pattern.
Since the thin wooden boards 21 are easily subjected to shaping without forming wrinkles or lines, it is not possible to cause an irregular pattern of the high density portions 12, which may be caused due to the unwanted formation of wrinkles or lines. This makes it possible to produce the diaphragm 1 having superior acoustic characteristics.
Since the thin wooden boards 21 are subjected to thermal pressing after the opposite sides 22a of the cutouts 22 thereof are connected together, it is possible to reliably and precisely form the high density portions 12. Since the opposite sides 22a of the cutouts 22 are connected together, it is possible to form the thin wooden boards 21 having curved shapes, which in turn reduces the amount of deformation applied to the thin wooden boards 21 during the thermal pressing and which in turn prevents the occurrence of cracks.
Since the thin wooden boards 21 are subjected to thermal pressing after the opposite sides 22a of the cutouts 22 are connected together, it is possible to reduce the difference of thickness between the connected portions 22b (corresponding to the high density portions 12), at which the opposite sides 22a of the cutouts 22 of the thin wooden boards 21 are connected together, and the other portions; hence, it is possible to produce the diaphragm 1 having the uniformly distributed thickness.
Due to the formation of the plural cutouts 22 along the wooden fiber directions, it is possible to prevent the wooden fibers of the thin wooden boards 21 from being divided via the cutouts 22; hence, it is possible to improve the strength of the diaphragm 1.
Since the cutouts 22 are formed in directions from the center to the periphery of the thin wooden boards 21, it is possible to easily form the high density portions 12 extended in a radial direction.
Since the thin wooden boards 21 are laminated together in such a way that the wooden fiber directions thereof cross each other, it is possible to further improve the strength of the diaphragm 1.
In the first manufacturing method, the opposite sides 22a of the cutouts 22 are connected together; the cutouts 22 are fixed using the resin or stapler so as to form the connected portions 22b; then, the thin wooden boards 21 laminated together are subjected to thermal pressing. However, it is possible to perform thermal pressing without connecting the cutouts 22 of the thin wooden boards 21. In this case, when the thin wooden boards 21 laminated together are held between the upper mold 31 and the lower mold 32, the opposite sides 22a of the cutouts 22 are automatically connected together so as to appropriately and easily shape them without causing wrinkles or lines; hence, it is possible to form the laminated structure in which the thin wooden boards 21 are laminated together and in which the high density portions 12 are appropriately formed.
3. Second Manufacturing Method of Diaphragm
Next, a second manufacturing method of the diaphragm 1 will be described with reference to
As shown in
Next, as shown in
Next, as shown in
There are provided three sheets of the thin wooden boards 41, each of which is produced by way of the aforementioned steps shown in
Thereafter, similar to the first manufacturing method, there are provided upper and lower molds having Nichrome wires (not shown), between which the three sheets of the thin wooden boards 41 laminated together are tightly held and are then subjected to thermal pressing. By way of the thermal pressing, the three sheets of the thin wooden boards 41 are integrally laminated together to form a laminated structure. Then, the outer periphery of the laminated structure is partially cut out, thus forming the diaphragm 1 as shown in
According to the second manufacturing method of the diaphragm 1, it is possible to demonstrate the foregoing effects demonstrated by the first manufacturing method.
Specifically, due to the formation of the cutouts 42 along the directions crossing the wooden fiber directions of the thin wooden board 41, wooden fibers are partially broken by way of the cutouts 42 so that the wooden fiber length of the thin wooden board 41 is shortened so as to increase the flexibility of the thin wooden board 41. This makes it possible for the thin wooden board 41, which is tightly held between the upper and lower molds, to be easily shaped without forming wrinkles or lines during the thermal pressing. Due to the increased flexibility of the thin wooden board 41, it is possible to easily form the diaphragm 1 having a relatively small radius of curvature. Incidentally, the cutouts 42 can be formed in any directions crossing the wooden fiber directions of the thin wooden board 41. For example, as shown in
4. Third Manufacturing Method of Diaphragm
Next, a third manufacturing method of the diaphragm 1 will be described with reference to
Similar to the first and second manufacturing methods, there is provided a thin wooden board 51 having a flat rectangular shape in plan view, in which a circular through-hole 51a is formed at the center thereof. The thin wooden board 51 has grains aligned in directions indicated by dashed lines in
Next, as shown in
Next, there are provided three sheets of the thin wooden boards 51, each of which is produced by way of the aforementioned steps shown in
Thereafter, similar to the first and second manufacturing methods, there are provided upper and lower molds having Nichrome wires, between which the three sheets of the thin wooden boards 51 laminated together are tightly held and are subjected to thermal pressing. By way of the thermal pressing, the three sheets of the thin wooden boards 51 are integrally laminated together so as to form a laminated structure. Then, the outer periphery of the laminated structure is partially cut out so as to produce the diaphragm 1 as shown in
According to the third manufacturing method, it is possible to demonstrate the foregoing effects demonstrated by the first and second manufacturing methods. In addition, the third manufacturing method demonstrates the following effect.
That is, the third manufacturing method is characterized in that, instead of the cutouts, the folded portions 52b are formed in the thin wooden boards 51, which are then subjected to thermal pressing; hence, it is possible to easily form the high density portions 12. Since no cutout is formed in the thin wooden boards 51, the wooden fibers are not broken; hence, it is possible to further increase the strength of the diaphragm 1.
Incidentally, it is not necessary to form the two folded portions 52b elongated along the wooden fiber directions as shown in
Moreover, the number of thin wooden boards, which are laminated together and are subjected to thermal pressing, is not necessarily limited to three; that is, it is possible to use two thin wooden boards or to use four or more thin wooden boards. Herein, through-holes (e.g., through-holes 21a, 41a, and 51a) are not necessarily formed before the impregnation of the resin and can be formed after the thermal pressing.
Lastly, the present invention is not necessarily limited to the aforementioned embodiment and the aforementioned manufacturing methods; hence, it is possible to realize variations within the scope of the invention defined by the appended claims.
Number | Date | Country | Kind |
---|---|---|---|
2006-185712 | Jul 2006 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
1917013 | Bostwick | Jul 1933 | A |
4100992 | Rehde et al. | Jul 1978 | A |
4674592 | Aoki et al. | Jun 1987 | A |
4699242 | Ono | Oct 1987 | A |
5256837 | Pak | Oct 1993 | A |
5274199 | Uryu et al. | Dec 1993 | A |
5329072 | Kageyama et al. | Jul 1994 | A |
5903658 | Okazaki et al. | May 1999 | A |
20040129492 | Bertagni et al. | Jul 2004 | A1 |
20040168851 | Imamura et al. | Sep 2004 | A1 |
20090038878 | Imamura et al. | Feb 2009 | A1 |
Number | Date | Country |
---|---|---|
01082896 | Mar 1989 | JP |
05083791 | Apr 1993 | JP |
05083792 | Apr 1993 | JP |
06-178386 | Jun 1994 | JP |
2004-254013 | Sep 2004 | JP |
Number | Date | Country | |
---|---|---|---|
20080006475 A1 | Jan 2008 | US |