1. Field of the Invention
The present invention relates to a die casting device, specifically to a die casting technique, in which the cavity of a die is decompressed to conduct casting.
2. Description of Related Art
In conventional die casting, the following techniques are used, namely: feeding a predetermined amount of molten metal into an injection sleeve having a feeding orifice; after the feeding, moving an injection tip by drive means at a predetermined timing; and injecting the molten metal from the injection sleeve into the cavity of a die at high pressure (For example, refer to Japanese Patent Application Publication No. 2003-245768 (JP 2003-245768 A), Japanese Patent Application Publication No. 4-258357 (JP 4-258357 A), Japanese Patent Application Publication No. 2002-239708 (JP 2002-239708 A), and Japanese Patent Application Publication No. 2004-167499 (JP 2004-167499 A)).
In the die casting device disclosed in JP 2003-245768 A, molten metal is taken out of a molten-metal holding furnace by a ladle, and it is fed into the feeding orifice of an injection sleeve by the ladle.
However, in the configuration disclosed in JP 2003-245768 A, as it is difficult to adjust the amount of ladled molten metal, it is difficult to improve the feeding accuracy. In addition, as molten metal touches the atmosphere at the time of feeding from the ladle into the sleeve, there are problems that the temperature of the molten metal decreases, and/or the product quality deteriorates due to gas such as dissolved hydrogen and an oxidized film produced in the molten metal.
On the other hand, the die casting devices disclosed in the above mentioned JP 4-258357 A and JP 2002-239708 A are configured in a manner that a feeding pipe and a feeding orifice of the injection sleeve are directly joined together, and molten metal is fed through the feeding pipe in order to avoid the molten metal from touching the atmosphere.
However, because the injection sleeve is fed with molten metal of high temperature, deformation is incurred in the injection sleeve due to the heat of the molten metal, which tends to cause vibrations at the time of injection. In the configurations disclosed in JP 4-258357 A and JP 2002-239708 A, there are problems that the feeding pipe directly joined to the injection sleeve, and/or its junction are damaged due to abrasion and/or vibration at the time of injection.
In addition, the die cast device disclosed in JP 2004-167499 A is configured in a manner that a cover is provided between a feeding pipe and a feeding orifice of the injection sleeve so as to avoid molten metal from touching the atmosphere at the time of molten-metal feeding.
However, according to the technique disclosed in JP 2004-167499 A, the feeding pipe is not directly joined to the injection sleeve, and thus a separate structure for supporting the feeding pipe is required. In addition, there is a possibility that the strength of the cover is insufficient with respect to the heat of the molten metal at the time of molten-metal feeding and/or the pressure at the time of decompressing a cavity, and that the cover is damaged.
The present invention provides a die casting device that can maintain, with a simple configuration, the quality of casting products, the accuracy of molten-metal feeding into the injection sleeve, and the durability of the die casting device, and also reduce the effect of abrasion and vibration at the time of injection.
An embodiment of the present invention is a die casting device including: a die that includes a cavity; an injection sleeve that includes a feeding orifice and communicates with the cavity; a support shaft; an injection tip that is provided at the distal end of a support shaft. The injection tip is configured to be slidable in an axial direction within the injection sleeve by inserting the support shaft into the injection sleeve. Further, the die casting device includes a decompression device that communicates with the cavity; a molten-metal holding furnace that includes a space to store molten metal; a pump that pumps up the molten metal from the molten-metal holding furnace; and a feeding pipe that includes a first end connected to the pump and a second end that communicates with the feeding orifice. The feeding pipe is joined to the injection sleeve through a relay pipe that includes a vibration absorption portion. The molten metal is fed into the injection sleeve from the molten-metal holding furnace through the feeding pipe by the pump. The fed molten metal is pushed out of the injection sleeve by the injection tip so that the molten metal is injected into the cavity decompressed by the decompression device, thereby casting is conducted.
The first end of the relay pipe may be joined to an intermediate portion of the feeding pipe, and the second end of the feeding pipe may be positioned in or near the feeding orifice.
The second end of the feeding pipe may be bent in an injection direction of the molten metal.
The relay pipe may be connected to the injection sleeve through a thermal insulation member.
The molten-metal holding furnace may store the molten metal in a state that the molten metal is insolated from the atmosphere.
The die casting device of the present invention can maintain, with a simple configuration, the quality of casting products, the accuracy of molten-metal feeding into the injection sleeve, and the durability of the die casting device, and also reduce the effect of abrasion and vibration at the time of injection.
Features, advantages, and technical and industrial significance of exemplary embodiments of the invention will be described below with reference to the accompanying drawings, in which like numerals denote like elements, and wherein:
It should be noted that the scope of the invention is not limited to the following embodiment but broadly contains the whole technical idea that is described in this specification and the drawings.
The die casting device 30 according to one embodiment of the present invention will be described with reference to
As shown in
The injection sleeve 2 has a feeding orifice 6, through which molten metal 5 is fed into the injection sleeve 2 through the feeding pipe 41, 42, which will be described later. The support shaft 9 is inserted into the injection sleeve 2 and controlled by an actuator (not shown) composed of an air cylinder, hydraulic cylinder or the like, to move forward and backward. The injection tip 3 provided at the distal end of the support shaft 9 slides within the injection sleeve 2 in the axial direction.
The die 1 is provided with a suction port 16 for suctioning air from the cavity 4. In addition, a shut valve 17 is provided in a passage connecting between the cavity 4 and the suction port 16. By connecting the suction port 16 to a decompression device (a decompression tank 21 and a vacuum pump 22 in this embodiment), the decompression device communicates with the inside of the cavity 4. A valve 23 is provided in the passage between the decompression tank 21 and the suction port 16 to open and close the passage. Decompression of the cavity 4 is started by opening the valve 23 of the passage in conjunction with injection control.
The die casting device 30 includes: an molten-metal holding furnace 50, which stores molten metal 5 therein; and an electromagnetic pump 40, of which one end is inserted into the molten metal 5 in the molten-metal holding furnace 50 at an angle of about 45 degrees, to pump up the molten metal 5 from the molten-metal holding furnace 50. The inner surface of the electromagnetic pump 40 is made of ceramic, and the electromagnetic pump 40 pumps up the molten metal 5 by an electromagnetic force by applying a voltage to a built-in coil in conjunction with injection control. In this embodiment, although the electromagnetic pump 40 is used as a pump, other pumps such as a positive displacement pump and a turbopump using a rotor may be used. In addition, in this embodiment, the molten-metal holding furnace 50 stores the molten metal 5 in a state that the molten metal 5 is isolated from the atmosphere.
In addition, the die casting device 30 includes the feeding pipe 41, 42 made of ceramic. The feeding pipe 41, 42 have an upper end connected to the electromagnetic pump 40 and a lower end communicating with the feeding orifice 6. More specifically, the feeding pipe 41, 42 is configured by jointing the upper feeding pipe 41 and the lower feeding pipe 42 (hereinafter, the upper feeding pipe 41 and the lower feeding pipe 42 are collectively referred to as feeding pipe 41, 42) together. The upper feeding pipe 41 is arranged such that its upper end is connected to the upper end of the electromagnetic pump 40, and inclined toward the injection sleeve 2. Furthermore, the upper end of the lower feeding pipe 42 is arranged so as to be connected to the lower end of the upper feeding pipe 41, and the lower end of the lower feeding pipe 42 is arranged so as to be perpendicular to the feeding orifice 6.
The feeding pipe 41, 42 are joined to an injection sleeve 2 through a relay pipe 61 having a bellows 61c of a bellows structure, which is a vibration absorption portion. Specifically, the injection sleeve 2 is connected to a thermal insulation member 71 made of metal or ceramic, and formed in a tubular shape communicating with the feeding orifice 6. That is, the relay pipe 61 is connected to the injection sleeve 2 through the thermal insulation member 71.
Furthermore, the relay pipe 61 is connected to the upper side of the thermal insulation member 71, and this relay pipe 61 supports the junction of the upper feeding pipe 41 and the lower feeding pipe 42. That is, the upper end of the relay pipe 61 is joined to the junction of the upper feeding pipe 41 and the lower feeding pipe 42 (which is an intermediate portion of the feeding pipe 41, 42), and the lower end of the lower feeding pipe 42 is positioned in or near the feeding orifice 6.
The support structure of the feeding pipe 41, 42 by the relay pipe 61 will be described in more detail using
The relay pipe 61 includes: a bellows 61c, which is a tubular bellows structure; an upper flange portion 61a formed outwardly at the upper end thereof; and a lower flange portion 61b formed outwardly at the lower end thereof. The bellows 61c is extendable and bendable, and absorbs deformation and vibration at the upper end or lower end of the relay pipe 61.
The relay pipe 61 and the thermal insulation member 71 are joined by connecting the lower flange portion 61b to the flange portion 71a of the thermal insulation member 71. In this embodiment, the lower flange portion 61b and the flange portion 71a of the thermal insulation member 71 are fastened by a bolt and nut. However, such connection method is not restrictive, but other connection means may be used for the connection. In addition, it is possible not to employ the thermal insulation member 71, by forming the lower end of the relay pipe 61 from a material of high thermal insulation properties.
On the other hand, the upper feeding pipe 41 has a connection flange portion 41a formed at the lower end thereof and protruding outward. The lower feeding pipe 42 has a connection flange portion 42a formed at the upper end thereof and protruding outward. The junction of the upper feeding pipe 41 and the lower feeding pipe 42 is supported by the relay pipe 61 by connecting the connection flange portion 41a and the connection flange portion 42a to the upper flange portion 61a of the relay pipe 61 with connection members such as a bolt and nut in a state that the connection flange portion 41 a and the connection flange portion 42a face and abut each other. In this embodiment, the lower end 42b of the lower feeding pipe 42, which is the other end of the feeding pipe 41, 42, is bent in the right side direction, which is the injection direction of the molten metal 5.
In addition, in this embodiment, in order to secure sealability for each part, gaskets 81, 82, 83, and 84a and 84b made of a graphite material are inserted between the connection flange portion 41a and the connection flange portion 42a, between the connection flange portion 42a and the upper flange portion 61a, between the lower flange portion 61b and the flange portion 71a, and between the inner circumference surface of the tubular portion 71b and the outer circumference surface of the injection sleeve 2, respectively.
The die casting device 30 according to this embodiment is configured in the above manner. The die casting device 30 conducts casting by conducting an injection action by feeding molten metal 5 into the injection sleeve 2 from the molten-metal holding furnace 50 through the feeding pipe 41, 42 by the electromagnetic pump 40, and pushing out the molten metal 5 in the right side direction by the injection tip 3 to inject the molten metal 5 into the cavity 4 in a state that the inside of the cavity 4 is decompressed by a decompression device.
[Vacuum-Casting Process by Die Casting Device 30]
Next, a vacuum-casting process by the die casting device 30 is described with reference to
Next, as shown in
Then, as shown in
In this manner, in a state that air in the cavity 4 is suctioned by the decompression device during the decompression step, the molten metal 5 is injected into the cavity 4 as the injection step. Then, after the injection tip 3 completely moved to the injection side, the valve 23 is closed and it will be in a state that the decompression has been completed. Furthermore, when a product within the cavity 4 has been solidified, the die is opened and the product is taken out.
In addition, after the completion of the injection, the injection tip 3 is retracted to the state shown in
In this manner, by the retraction action of the injection tip 3, the inner circumference surface of the injection sleeve 2 can be made into a clean state. Also, by removing rubbish and the like, it is possible to restrain mixing of impurities in a next injection, and eventually to improve the quality.
In the die casting device 30 according to this embodiment, as the feeding amount of molten metal 5 is controlled by the electromagnetic pump 40, it becomes possible to improve the accuracy of feeding molten metal. Specifically, as compared with the configuration that the amount of molten metal to be pumped up is adjusted by a ladle, this embodiment can improve the error rate of molten-metal feeding amount by 2%.
In addition, in the die casting device 30 according to this embodiment, molten metal 5 is fed into the injection sleeve 2 from the molten-metal holding furnace 50 through the electromagnetic pump 40 and the feeding pipe 41, 42 so as to prevent molten metal 5 from exposing to atmosphere at the time of molten-metal feeding. For this reason, this embodiment can prevent temperature reduction of molten metal 5, and deterioration of the product quality due to gas such as dissolved hydrogen and an oxidized film produced in the molten metal 5. Specifically, this embodiment can reduce the difference between the temperature in molten metal 5 in the molten-metal holding furnace 50 and the temperature in molten metal 5 in the feeding orifice 6. In addition, this embodiment can reduce the amount of gas (hydrogen gas and nitrogen gas) within the casted product by several times as compared with a product made by a general die casting device.
Furthermore, in the die casting device 30 according to this embodiment, the feeding pipe 41, 42 is joined to the injection sleeve 2 through the relay pipe 61 having the bellows 61c, which is a vibration absorption portion formed to be extendable and bendable. Thereby, it is configured to absorb deformation and vibration in the injection sleeve 2 by the bellows 61c.
As described above, even if deformation has been made on the injection sleeve 2 due to heat during use, or vibration is produced by this deformation at the time of injection, this embodiment can absorb deformation and vibration in the injection sleeve 2 by the bellows 61c. That is, this embodiment can prevent the feeding pipe 41, 42 and its junction from being damaged by abrasion and vibration at the time of injection.
Furthermore, in the die casting device 30 according to this embodiment, because the feeding pipe 41, 42 is directly joined to the injection sleeve 2, no separate structure for supporting the feeding pipe 41, 42 is required. In addition, because the relay pipe 61 having the bellows 61c has a sufficient strength against the heat of molten metal 5 at the time of molten-metal feeding and against pressure at the time of decompression of the cavity 4, the die casting device 30 is not damaged by them.
That is, the die casting device 30 of this embodiment can maintain, with a simple configuration, product quality, the accuracy of molten-metal feeding into the injection sleeve 2, and durability, and it can also reduce the effect of abrasion and vibration at the time of injection.
In addition, in this embodiment, the upper end of the relay pipe 61 is joined to the junction of the upper feeding pipe 41 and the lower feeding pipe 42, which is an intermediate portion of the feeding pipe 41, 42, and the lower end 42b of the lower feeding pipe 42, which is the lower end of the feeding pipe 41, 42 is positioned in or near the feeding orifice 6.
In this manner, because the lower end of the feeding pipe 41, 42 extends in or near the feeding orifice 6 of the injection sleeve 2, this embodiment can prevent molten metal 5 from scattering at the time of feeding into the injection sleeve 2. In addition, because the relay pipe 61 does not directly contact molten metal 5, the relay pipe 61 can be protected from the high heat of the molten metal 5.
In addition, in this embodiment, the lower end 42b of the lower feeding pipe 42, which is the lower end of the feeding pipe 41, 42, is bent in the right side direction, that is, the injection direction of molten metal 5. Thereby, this embodiment can feed molten metal 5 into the injection sleeve 2 in the same direction as the injection direction (the right side in
In addition, in this embodiment, the relay pipe 61 is connected to the injection sleeve 2 through the thermal insulation member 71. Thereby, the present invention can prevent the relay pipe 61 from being exposed to the high heat of the injection sleeve 2, and improve the durability of the relay pipe 61.
In addition, in this embodiment, the molten-metal holding furnace 50 stores molten metal 5 in a state that the molten metal 5 is isolated from the atmosphere. Thereby, the die casting device 30 as a whole prevents the molten metal 5 from being exposed to the atmosphere and can prevent the deterioration in quality of casting products.
Number | Date | Country | Kind |
---|---|---|---|
2011-205377 | Sep 2011 | JP | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/IB2012/001712 | 9/6/2012 | WO | 00 | 3/20/2014 |