Patent Application
20170036269
This disclosure relates to a multi-layered shot sleeve for a die casting machine.
A typical die casting machine includes a shot sleeve having a pour opening that receives molten metal. A plunger moves axially within a cavity provided by the shot sleeve to force the molten metal into a die providing a component shape.
During die casting, one of the more problematic issues is the control of the gap between the shot sleeve and the piston. Distortion of the shot sleeve during the die casting process is a strong factor that modulates the gap and causes interference to occur between sleeve and piston. Too large of a gap causes metal blow-by and jamming of solidified metal between sleeve and piston. Too small of a gap causes interference when a sleeve distorts. Many methods have been used throughout the die cast industry to try to control this gap, such as using a water-cooled piston, heater/oil routed shot sleeves, cooling jackets, etc. One or more of these approaches may increase tool life for the casting foundry.
One type of distortion is sometimes referred to as the “banana effect” of shot sleeves, or cantilevering of shot sleeve about a constrained end. This undesired banana effect can be avoided by achieving uniform temperature throughout the length of the shot sleeve, but this is almost impossible to achieve. During casting, the shot sleeve is typically no more than 50% filled before the piston has started moving. Even with the piston traveling inside the shot sleeve, only a segment of the shot sleeve sees the full molten melt temperature. This problem is only exacerbated in very high temperature die casting processes. The distortion may be only about 0.004 inch (0.01 mm), but this slight distortion can cause interference between shot sleeve and piston, which wears the sleeve/piston interface as the piston retracts and drags along the length of the shot sleeve. A long tube simply worsens the effect.
A multi-layered shot sleeve has been proposed in an attempt to maintain sufficiently high casting temperatures between molten shots. A consolidated, unsintered layer of ceramic is provided between inner and outer metal layers. The ceramic layer provides improved insulating properties to the shot sleeve. Loose ceramic is provided between the inner and outer layers and packed using a hot isostatic pressing (HIP) process to a relatively low density. The inner and/or outer layers are then machined to desired dimensions. This process attempts to ensure that the ceramic does not bond to the inner metal layer or transfer any significant load between the inner and outer metal layers so that the ceramic is not cracked due to thermal shock during casting.
In one exemplary embodiment, a method of manufacturing a shot sleeve for a die casting machine includes engaging an intermediate sleeve layer with one of an outer sleeve layer and an inner sleeve layer, and shrink fitting the other of the outer sleeve layer and an inner sleeve layer into engagement with the intermediate sleeve layer.
In a further embodiment of the above, the engaging step includes shrink fitting the outer sleeve layer onto the intermediate sleeve layer. The other shrink fitting step includes shrink fitting an inner sleeve layer into the intermediate sleeve layer.
In a further embodiment of any of the above, the inner sleeve layer shrink fitting step is performed after the outer sleeve layer shrink fitting step.
In a further embodiment of any of the above, the inner sleeve layer shrink fitting step generates a first radial compressive force on the intermediate sleeve layer. The outer sleeve layer shrink fitting step generates a second radial compressive force on the intermediate sleeve layer.
In a further embodiment of any of the above, the first and second radial compressive forces generate a compressive stress of 35-45 MPa on the intermediate sleeve layer.
In a further embodiment of any of the above, the intermediate sleeve layer is ceramic.
In a further embodiment of any of the above, the intermediate sleeve layer is provided by ring segments.
In a further embodiment of any of the above, the inner sleeve layer is metal.
In a further embodiment of any of the above, the outer sleeve layer is metal.
In a further embodiment of any of the above, the shot sleeve consists of three layers provided by the outer, intermediate and inner sleeve layers.
In a further embodiment of any of the above, the outer sleeve layer shrink fitting step is performed by providing the outer sleeve layer at a higher temperature than the intermediate sleeve layer. The intermediate sleeve layer is inserted into the outer sleeve layer.
In a further embodiment of any of the above, the inner sleeve layer shrink fitting step is performed by providing the inner sleeve layer at a lower temperature than the intermediate sleeve layer. The inner sleeve layer is inserted into the intermediate sleeve layer.
In a further embodiment of any of the above, the method includes the step of replacing a worn inner sleeve layer by heating the outer -sleeve layer and removing the intermediate and inner sleeve layers from the outer sleeve layer.
In a further embodiment of any of the above, the engaging includes spraying the intermediate sleeve layer onto the one of an outer sleeve layer and an inner sleeve layer.
In a further embodiment of any of the above, the intermediate sleeve layer is ceramic.
In a further embodiment of any of the above, the shrink fitting step generates a compressive stress of 0.0024 inch on the intermediate sleeve layer.
In a further embodiment of any of the above, the method includes the step of machining the inner sleeve surface to provide a plunger surface that is configured to receive a plunger.
In a further embodiment of any of the above, the method includes the step of replacing a worn inner sleeve layer by heating the outer sleeve layer and removing the intermediate and inner sleeve layers from the outer sleeve layer.
In a further embodiment of any of the above, the shrink fitting step provides an interference fit in the amount of 0.0024 inch.
In another exemplary embodiment, a shot sleeve for a die casting machine includes an intermediate sleeve layer that is in engagement with and arranged radially between inner and outer sleeve layers. A pour opening is provided through the intermediate, inner and outer sleeve layers. The intermediate layer is ceramic and subjected to a compressive stress of 35-45 MPa from the inner and outer sleeve layers.
The disclosure can be further understood by reference to the following detailed description when considered in connection with the accompanying drawings wherein:
The embodiments, examples and alternatives of the preceding paragraphs, the claims, or the following description and drawings, including any of their various aspects or respective individual features, may be taken independently or in any combination. Features described in connection with one embodiment are applicable to all embodiments, unless such features are incompatible.
A die casting machine 10 is schematically illustrated in
A shot sleeve 18 is in fluid communication with the die 12 to force molten metal into the die 12 during the die casting process. The shot sleeve 18 includes a pour opening 20 that receives molten material M. A plunger 22 is retracted by an actuator 26 via a rod 24 such that molten metal may be received in an area in the shot sleeve 18 immediately beneath the pour opening 20 and left of the retracted plunger 22. The plunger 22 is moved axially along a plunger axis R to the position illustrated in
An arrangement of nested sleeves is used to provide the shot sleeve 18, as shown in
With reference to
The outer sleeve layer 32 includes inner and outer diameter surfaces 36, 38. The intermediate sleeve layer 30 includes inner and outer diameter surfaces 40, 42. The inner sleeve layer 28 includes inner and outer diameter surfaces 44, 46. The inner diameter surface 44 corresponds to a plunger surface that cooperates with the plunger 22 during the casting process.
The inner and outer diameter surfaces 40, 42 are respectively in engagement with the inner and outer diameter surfaces 36, 46 in an assembled condition. The pour opening 20 may be provided in each of the inner, intermediate and outer sleeve layers 28, 30, 32 prior to assembly, if desired. A refractory-weldable pour liner can be incorporated if desired, which will eliminate washout effects from the hot impingement molten metal being dumped from a height into the shot tube.
In one example, the intermediate sleeve layer 30 is provided by a ceramic. Ceramic materials have unique properties of high compressive strength and low thermal expansion. The choice of ceramics can be but not limited to alumina, mullite, silicon nitrides and or their oxide/nitride derivatives. Ceramics have extremely high compressive strength with typical values of above 2100 MPa for alumina and 3800 MPa for silicon nitride. Ceramics also have a low linear coefficient of thermal expansion (CTE), for example, alumina has a CTE value of ˜7.7 to 8×10−6/°C. in the temperature range of 400-800° C., and silicon nitride has a CTE value of ˜3.2×10−6/° C. in the temperature range 400-800° C.
The inner and outer sleeve layers 28, 32 are provided by a metal. A typical H13 metal at a temperature range 400-800° C. has a CTE of 12.4×10−6/° C. Thus, by having a heat insulating, low thermal expansion ceramic interlayer, coupled with its very high compressive strength because there is simply no room for bending movement in a sandwiched construction.
In one example, the outer sleeve layer 32 is made of a H13 material. Since this layer does not contact molten metal, a non-premium grade of H13 can be used to reduce cost. This inner sleeve layer can be non-H13 steel grades or other materials, for example. A high wear resistant grade of steel in high speed steels can be used for inner sleeve to reduce frictional wear between the plunger and the shot sleeve.
A shot sleeve 18 is manufactured, as indicated at 48 in
Alternatively, the intermediate sleeve layer 30 may be sprayed onto one of the inner and outer sleeve layers 28, 32 and the other of the inner and outer sleeve layers 28, 32 is shrink-fit relative to the intermediate sleeve layer 30.
Since the compressive forces applied to the intermediate sleeve layer 30 may distort or alter the dimensions of the inner diameter surface 44, the inner sleeve layer 28 may be machined to provide the desired dimension for the cavity 34, if necessary, as shown at block 56.
If the inner sleeve layer 28 becomes worn, the inner sleeve layer 28 may be removed by heating the outer sleeve layer and removing the intermediate inner sleeve layers 30, 28 from the outer sleeve layer 32.
The disclosed multilayer construction in which the interlayer is sufficiently compressed and effectively mechanically joined to the inner and outer sleeves will control the distortion seen in shot sleeves and effectively maintain the gap tolerance during the die cast process.
It should also be understood that although a particular component arrangement is disclosed in the illustrated embodiment, other arrangements will benefit herefrom. Although particular step sequences are shown, described, and claimed, it should be understood that steps may be performed in any order, separated or combined unless otherwise indicated and will still benefit from the present invention.
Although the different examples have specific components shown in the illustrations, embodiments of this invention are not limited to those particular combinations. It is possible to use some of the components or features from one of the examples in combination with features or components from another one of the examples.
Although an example embodiment has been disclosed, a worker of ordinary skill in this art would recognize that certain modifications would come within the scope of the claims. For that reason, the following claims should be studied to determine their true scope and content.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201309056-8 | Dec 2013 | SG | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/SG2014/000561 | 11/27/2014 | WO | 00 |