Dielectric ceramic composition and monolithic ceramic capacitor using the composition

Abstract

Disclosed is a dielectric ceramic composition containing an essential component represented by the formula, xBaO-yTiO.sub.2 -zRe.sub.2 O.sub.3, wherein x, y and z are in mol %; x+y+z=100; and (x, y, z) falls within a polygonal region defined by four points of A (39.5, 59.5, 1), B (1, 59.5, 39.5), C (1, 85, 14) and D (14, 85, 1), and further containing V, Cu and Mn as side components in an amount of about 0.1 wt. % to 15 wt. % in terms of V.sub.2 O.sub.5, in an amount not greater than 10 wt. % in terms of CuO, and in an amount not greater than 1 wt. % in terms of MnO, respectively, relative to 100 wt. % of the essential component.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to dielectric ceramic compositions, and particularly to dielectric ceramic compositions for use in monolithic ceramic capacitors having inner electrodes made essentially of silver-palladium (Ag-Pd).

2. Description of the Related Art

Ceramic capacitors for temperature compensation use have been used widely in tuning circuits, resonance circuits, etc. Since small-sized ceramic capacitors having a small dielectric loss and stable dielectric characteristics are preferred, dielectric ceramics for such capacitor applications desirably have a high specific inductive capacity and a small dielectric loss, i.e., a large Q value.

Monolithic ceramic capacitors using dielectric ceramic compositions having the above-mentioned characteristics have been put into practical use. However, since the firing temperature of dielectric ceramics is as high as 1300.degree. C. to 1400.degree. C., palladium, platinum or a like material having a high melting point must be used as a material for inner electrodes. One problem with these electrode materials is their high prices.

Ag-Pd is an electrode material less expensive than Pd and Pt. The melting point of Ag is 961.degree. C. As the Ag content of an electrode material increases, the electrode material cost reduces; however, the firing temperature of a dielectric ceramic must be lowered accordingly. Specifically, there is demand for a dielectric ceramic composition that can be fired at a firing temperature up to about 1250.degree. C.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a dielectric ceramic composition having a high specific inductive capacity, er, and a large Q value and which is capable of being sintered at low temperatures.

To achieve the above object, according to a first aspect of the present invention, there is provided a dielectric ceramic composition containing an essential component represented by the following formula:

xBaO-yTiO.sub.2 -zRe.sub.2 O.sub.3 where x, y, and z are in mol %; x+y+z=100; (x, y, z) falls within a polygonal region defined by four points of A(39.5, 59.5, 1), B(1, 59.5, 39.5), C(1, 85, 14) and D(14, 85, 1); and Re is at least one rare earth element selected from the group consisting of Tb, Dy, Ho, Er and Yb, and further containing V as a side component in an amount, .alpha., of about 0.1 wt. % to 15 wt. % in terms of V.sub.2 O.sub.5 relative to 100 wt. % of the essential component.

The dielectric ceramic composition according to the first aspect of the invention exhibits a specific inductive capacity, .epsilon.r, of not lower than about 30 at room temperature, and a Q value of not lower than about 1000 at 1 MHz, and can be fired at a temperature of up to about 1250.degree. C.

According to a second aspect of the present invention, there is provided a dielectric ceramic composition containing an essential component represented by the following formula:

xBaO-yTiO.sub.2 -z(ReI.sub.a ReII.sub.(1-a)).sub.2 O.sub.3 where x, y, and z are in mol %; x+y+z=100; (x, y, z) falls within a polygonal region defined by four points of A(39.5, 59.5, 1), B(1, 59.5, 39.5), C(1, 85, 14) and D(14, 85, 1); 0.2<a<1.0; ReI is at least one rare earth element selected from the group consisting of Tb, Dy, Ho, Er and Yb; and ReII is at least one rare earth element selected from the group consisting of La, Pr, Nd and Sm and further containing V as a side component in an amount, .alpha., of about 0.1 wt. % to 15 wt. % in terms of V.sub.2 O.sub.5 relative to 100 wt. % of the essential component.

The dielectric ceramic composition according to the second aspect exhibits a specific inductive capacity, .epsilon.r, of not lower than about 40 at room temperature, and a Q value of not lower than about 1000 at 1 MHz, and can be fired at a temperature of up to about 1250.degree. C.

Preferably, in the dielectric ceramic compositions according to the first and/or second aspects of the invention, Cu is contained as a side component in an amount, .beta., of not greater than about 10 wt. % in terms of CuO relative to 100 wt. % of the essential component, so as to further lower the firing temperature.

Preferably, in the dielectric ceramic compositions according to the first and/or second aspects of the present invention, Mn is contained as a side component in an amount, .gamma., of not greater than about 1 wt. % in terms of MnO relative to 100 wt. % of the essential component, so as to further increase the Q value.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a ternary compositional diagram showing the compositional range of an essential component of a dielectric ceramic composition according to the present invention;

FIG. 2 is a sectional view showing a monolithic ceramic capacitor using a dielectric ceramic composition of the invention;

FIG. 3 is a plan view showing a laminate of a ceramic layer and an electrode paste layer formed on the ceramic layer for use in manufacture of the monolithic ceramic capacitor of FIG. 2; and

FIG. 4 is a perspective view showing a plurality of the laminates of FIG. 3 for use in manufacture of the monolithic ceramic capacitor of FIG. 2.

PREFERRED MODES FOR CARRYING OUT THE INVENTION

Embodiments of the present invention will now be described by way of example.

EXAMPLE 1

Barium carbonate (BaCO.sub.3), titanium oxide (TiO.sub.2), rare earth oxide (Re.sub.2 O.sub.3) vanadium oxide (V.sub.2 O.sub.5), copper oxide (CuO) and manganese carbonate (MnCO.sub.3) were weighed so as to prepare dielectric ceramic compositions as shown in Table 1. Each composition was wet-milled with ethanol in a ball mill for 16 hours. The resultant mixture was dried and pulverized, followed by preliminary firing at 1000.degree. C. to obtain a preliminary fired powder. An appropriate amount of polyvinyl alcohol solution was added to the powder and mixed. The mixture was sheeted through doctor blading to obtain a ceramic green sheet having a thickness of 50 .mu.m. Thirteen thus-obtained ceramic green sheets were arranged in layers and hot-pressed to obtain a laminate. A disc having a diameter of 14 mm and a thickness of 0.5 mm was punched out from the laminate. The disc was treated at a temperature of 300.degree. C. so as to burn out binder and was then fired at firing temperature shown in Table 1, obtaining a dielectric sample.

The thus-obtained dielectric sample was coated over the entire upper and lower surfaces thereof with indium-gallium (In-Ga) serving as an electrode to obtain a disc capacitor, which served as a sample for evaluation. The sample was measured for electrostatic capacity (Cap) and Q value at a frequency of 1 MHz and an input voltage of 1 Vrms. The sample was also measured for diameter (D) and thickness (T), and the specific inductive capacity of the sample was calculated based on the measured D and T values. The results are shown in Table 1.

TABLE 1__________________________________________________________________________ V.sub.2 O.sub.5 CuO MnO Firing Sample BaO TiO.sub.2 Re.sub.2 O.sub.3 Re (mol %) .alpha. .beta. .gamma. Temperature QNo. x y z Tb Dy Ho Er Yb wt % wt % wt % (.degree. C.) .epsilon.r (at 1 MHZ)__________________________________________________________________________*1 39.5 59.5 1 0 0 0 80 20 0 0 0 1300 32 500 *2 1 59.5 39.5 0 0 0 80 20 0 0 0 1350 30 800 *3 1 85 14 0 0 0 80 20 0 0 0 1300 33 1000 *4 14 85 1 0 0 0 80 20 0 0 0 1300 35 2000 *5 30 65 5 5 10 10 75 0 0 0 0 1300 43 500*6 30 65 5 5 10 10 75 0 0 0 0 1150 Not sintered*7 3 65 32 5 10 10 75 0 0 0 0 1350 41 2000*8 3 65 32 5 10 10 75 0 0 0 0 1190 Not sintered*9 15 80 5 5 10 10 75 0 0 0 0 1300 53 2000*10 15 80 5 5 10 10 75 0 0 0 0 1150 Not sintered*11 20 70 10 0 0 0 100 0 0 0 0 1300 69 10000 or more*12 20 70 10 0 0 0 100 0 0 0 0 1150 Not sintered*13 10 70 20 0 0 0 100 0 0 0 0 1300 58 10000 or more*14 10 70 20 0 0 0 100 0 0 0 0 1150 Not sintered*15 20 58 22 20 50 0 30 0 3 0 0 1150 23 500 *16 0.5 74.5 25 20 50 0 30 0 3 0 0 1150 26 800 *17 5 90 5 20 50 0 30 0 3 0 0 1150 20 700 *18 35 64.5 0.5 20 50 0 30 0 3 0 0 1150 28 300 19 39.5 59.5 1 0 0 0 80 20 2 0 0 1150 35 1000 20 1 59.5 39.5 0 0 0 80 20 5 0 0 1190 31 1000 21 1 85 14 0 0 0 80 20 2 0 0 1150 33 2000 22 14 85 1 0 0 0 80 20 2 0 0 1150 36 3000 23 30 65 5 5 10 10 75 0 2 0 0.05 1150 44 2000 24 3 65 32 5 10 10 75 0 5 0 0.05 1190 43 3000 25 15 80 5 5 10 10 75 0 2 0 0.05 1150 55 3000 26 20 70 10 0 0 0 100 0 2 0 0 1150 63 10000 or more 27 10 70 20 0 0 0 100 0 2 0 0 1150 58 10000 or more 28 10 70 20 0 0 0 100 0 0.1 2 0 1250 58 1000 29 10 70 20 0 0 0 100 0 0.5 2 0 1250 58 2000 30 10 70 20 0 0 0 100 0 1 2 0 1200 57 4000 31 10 70 20 0 0 0 100 0 1 2 0.1 1190 57 4000 32 10 70 20 0 0 0 100 0 1 2 1 1170 56 5000 *33 10 70 20 0 0 0 100 0 1 2 2 1170 50 2000 34 10 70 20 0 0 0 100 0 5 2 0.05 1130 57 7000 35 10 70 20 0 0 0 100 0 10 0 0.05 1100 58 8000 36 10 70 20 0 0 0 100 0 15 0 0.05 1100 51 8000 *37 10 70 20 0 0 0 100 0 20 0 0.05 1100 49 2000 38 10 70 20 0 0 0 100 0 2 0.5 0.05 1120 58 10000 or more 39 10 70 20 0 0 0 100 0 2 5 0.05 1080 54 9000 40 10 70 20 0 0 0 100 0 2 10 0.05 1050 50 8000 *41 10 70 20 0 0 0 100 0 2 15 0.05 1050 49 2000 42 10 70 20 0 80 0 20 0 3 2 0.05 1100 54 10000 or more 43 10 70 20 0 80 20 0 0 3 2 0.05 1100 57 10000 or more 44 10 70 20 0 0 0 50 50 2 2 0.05 1100 51 10000 or more 45 10 70 20 70 0 15 15 0 3 2 0.05 1100 58 10000 or more 46 10 70 20 0 20 60 20 0 2 2 0.05 1100 53 10000 or more 47 10 70 20 0 80 20 0 0 3 3 0.05 1080 52 10000 or more 48 10 70 20 0 80 20 0 0 4 4 0.05 1070 51 10000 or more 49 10 70 20 0 5 5 90 0 2 2 0.05 1100 50 10000 or more 50 10 70 20 0 50 0 50 0 2 2 0.05 1100 55 10000 or more__________________________________________________________________________ Sample Nos. marked with * indicate comparative examples which fall outsid the scope of the invention.

FIG. 1 is a ternary composition diagram showing the compositional range of the essential component of the dielectric ceramic composition according to the first aspect of the present invention. The compositional range is limited to the polygonal region as defined by the points A, B, C and D. The reason for this limitation will be described below with reference to FIG. 1 and Table 1.

In an area outside the polygonal region as defined by the points A, B, C and D, the specific inductive capacity Er becomes lower than 30 and the Q value becomes smaller than 1000 at 1 MHz, which are unfavorable conditions in actual use.

If the V content is less than about 0.1 wt. % relative to 100 wt. % of the essential component, the dielectric ceramic composition fails to be sintered at a temperature of up to 1250.degree. C., which is unfavorable. If the V content is in excess of about 15 wt. % relative to 100 wt. % of the essential component, the Q value decreases, which is unfavorable.

If the Cu content is in excess of about 10 wt. % relative to 100 wt. % of the essential component, the Q value decreases, which is unfavorable.

If the Mn content is in excess of about 1 wt. % relative to 100 wt. % of the essential component, the Q value decreases, which is unfavorable.

Sample Nos. 42 to 50 exhibit. Specifically, a Q value of 10000 or more, .di-elect cons.r of 50 or more, and a firing temperature of 1100.degree. C. or lower. Accordingly, preferably, (x, y, z) is (ca. 10, ca. 70, ca. 20), Re is at least one of Ho and Er, .alpha. is between about 2 and about 4, .beta. is between about 2 and about 4, and .gamma. is not greater than about 0.05.

EXAMPLE 2

BaCO.sub.3, TiO.sub.2, Re.sub.2 O.sub.3, V.sub.2 O.sub.5, CuO and MnCO.sub.3 were weighed so as to prepare dielectric ceramic compositions as shown in Table 2. The compositions were sheeted in a manner similar to that of Example 1. Dielectric samples were obtained through sintering at corresponding sintering temperatures as shown in Table 2.

In a manner similar to that of Example 1, the dielectric samples were coated with In-Ga serving as electrodes, to thereby obtain samples. The samples were measured for electrostatic capacity (Cap) and Q value at a frequency of 1 MHz and an input voltage of 1 Vrms. The samples were also measured for diameter (D) and thickness (T), and the specific inductive capacities of the samples were calculated based on the measured D and T values. The results are shown in Table 2.

TABLE 2__________________________________________________________________________ V.sub.2 O.sub.3 CuO MnO Firing Sample BaO TiO.sub.2 Re.sub.2 O.sub.3 Re I (mol %) Re II (mol %) .alpha. .beta. .gamma. Temperatu re QNo. x y z a Tb Dy Ho Er Yb La Pr Nd Sm wt % wt % wt % (.degree. C.) .epsilon.r (at 1 MHZ)__________________________________________________________________________*51 39.5 59.5 1 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1320 39 800 *52 1 59.5 39.5 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1320 37 500 *53 1 85 14 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1320 41 1000 *54 14 85 1 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1320 42 1000*55 39.5 59.5 1 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1250 Not sintered. *56 1 59.5 39.5 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1250 Not sintered. *57 1 85 14 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1250 Not sintered. *58 14 85 1 0.5 0 0 20 70 10 20 20 60 0 0 0 0 1250 Not sintered.59 39.5 59.5 1 0.5 0 0 20 80 0 20 20 60 0 2 0 0 1180 41 1000 60 1 59.5 39.5 0.5 0 0 20 80 0 20 20 60 0 2 0 0 1180 43 1000 61 1 85 14 0.5 0 0 20 80 0 20 20 60 0 2 0 0 1180 40 2000 62 14 85 1 0.5 0 0 20 80 0 20 20 60 0 2 0 0 1180 44 2000 63 30 65 5 0.5 10 50 20 20 0 0 20 50 30 2 2 0.1 1130 52 2000 64 3 65 32 0.5 10 50 20 20 0 0 20 50 30 2 2 0.1 1130 50 3000 65 3 80 17 0.5 10 50 20 20 0 0 20 50 30 2 2 0.1 1130 53 2000 66 15 80 5 0.5 10 50 20 20 0 0 20 50 30 2 2 0.1 1130 59 2000 *67 3 80 17 0.2 0 80 0 20 0 20 30 30 20 3 0 0 1160 53 700 68 3 80 17 0.21 0 80 0 20 0 20 30 30 20 3 0 0 1160 51 1000 69 3 80 17 0.5 0 80 0 20 0 20 30 30 20 3 0 0 1160 50 2000 70 3 80 17 0.9 0 80 0 20 0 20 30 30 20 3 0 0 1160 42 5000 *71 3 80 17 1 0 80 0 20 0 0 0 0 0 3 0 0 1160 37 9000*72 10 70 20 0.6 0 20 0 50 30 0 30 60 10 0 0 0 1250 not sintered.73 10 70 20 0.6 0 20 0 50 30 0 30 60 10 0.1 0 0 1250 64 3000 74 10 70 20 0.6 0 20 0 50 30 0 30 60 10 0.5 0 0 1250 65 4000 75 10 70 20 0.6 0 20 0 50 30 0 30 60 10 1 0 0 1200 67 5000 76 10 70 20 0.6 0 20 0 50 30 0 30 60 10 5 0 0 1170 68 6000 *77 10 70 20 0.6 0 20 0 50 30 0 30 60 10 15 0 0 1130 64 5000 *78 10 70 20 0.5 0 20 0 50 30 0 30 60 10 20 0 0 1130 59 900 79 20 70 10 0.3 20 0 0 80 0 40 0 0 60 2 0 0.05 1170 74 6000 80 20 70 10 0.3 20 0 0 80 0 40 0 0 60 2 2 0.05 1130 75 8000 81 20 70 10 0.3 20 0 0 80 0 40 0 0 60 2 5 0.05 1090 73 5000 82 20 70 10 0.3 20 0 0 80 0 40 0 0 60 2 10 0.05 1060 72 4000 *83 20 70 10 0.3 20 0 0 80 0 40 0 0 60 2 13 0.05 1060 72 700 84 10 70 20 0.7 0 60 10 30 0 30 0 70 0 3 2 0.1 1140 56 10000 85 10 70 20 0.7 0 60 10 30 0 30 0 70 0 3 2 0.5 1140 55 6000 86 10 70 20 0.7 0 60 10 30 0 30 0 70 0 3 2 1 1140 54 2000 *87 10 70 20 0.7 0 60 10 30 0 30 0 70 0 3 2 2 1140 53 500 88 10 70 20 0.4 20 20 0 60 0 10 10 80 0 2 0.5 0.1 1160 64 5000 89 10 70 20 0.4 20 20 0 60 0 10 10 40 40 2 0.5 0.1 1160 71 3000 90 20 70 10 0.3 0 0 0 100 0 0 0 100 0 2 2 0.5 1120 76 2000 91 20 70 10 0.3 0 0 0 100 0 0 0 0 100 2 2 0.5 1120 87 2000__________________________________________________________________________ Sample Nos. marked with * indicate comparative examples which fall outsid the scope of the present invention.

The compositional range of the essential component of the dielectric ceramic composition according to the second aspect of the present invention can also be represented by the ternary diagram of FIG. 1. The compositional range is limited to the polygonal region as defined by the points A, B, C and D. The reason for this limitation will be described below with reference to FIG. 1 and Table 2.

In an area outside the polygonal region as defined by the points A, B, C and D, the specific inductive capacity .di-elect cons.r becomes lower than 40, or the Q value becomes smaller than 1000 at 1 MHz, which are unfavorable conditions in actual use.

If a is about 0.2 or about 1.0, the specific inductive capacity .di-elect cons.r becomes lower than 40, or the Q value becomes smaller than 1000 at 1 MHz, which are unfavorable conditions in actual use.

If the V content is less than about 0.1 wt. % relative to 100 wt. % of the essential component, the dielectric ceramic composition fails to be sintered at a temperature up to 1250.degree. C., which is unfavorable. If the V content is in excess of about 15 wt. % relative to 100 wt. % of the essential component, the Q value decreases, which is unfavorable.

If the Cu content is in excess of about 10 wt. % relative to 100 wt. % of the essential component, the Q value decreases, which is unfavorable.

If the Mn content is in excess of about 1 wt. % relative to 100 wt. % of the essential component, the Q value decreases, which is unfavorable.

In Examples 1 and 2, the barium component, the titanium component, the rare earth component, the vanadium component, the copper component and the manganese component were all mixed and fired preliminarily. However, alternatively, the barium component, the titanium component and the rare earth component may be mixed and fired preliminarily, followed by addition of the vanadium component, the copper component and the manganese component thereto. Even in this case, the effects are similar to those in the case of Examples 1 and 2.

Also, the barium, titanium, rare earth, vanadium, copper and manganese components used in Examples 1 and 2 were BaCO.sub.3, TiO.sub.2, Re.sub.2 O.sub.3, V.sub.2 O.sub.5, CuO and MnCO.sub.3, respectively, but are not limited thereto. Other compounds, oxalates, hydroxides, alkoxides, and the like may be used.

EXAMPLE 3

A monolithic ceramic capacitor 10 shown in FIG. 2 was manufactured according to the following procedure.

Barium carbonate (BaCO.sub.3), titanium oxide (TiO.sub.2) rare earth oxide (Re.sub.2 O.sub.3), vanadium oxide (V.sub.2 O.sub.5), copper oxide (CuO) and manganese carbonate (MnCO.sub.3) were weighed so as to prepare dielectric ceramic compositions as shown in Table 1. Each composition was wet-milled with ethanol in a ball mill for 16 hours. The resultant mixture was dried and pulverized, followed by preliminary firing at a temperature of 1000.degree. C. to obtain a preliminary fired powder. An appropriate amount of polyvinyl alcohol solution was added to the powder and mixed. The mixture was sheeted through doctor blading to obtain a ceramic green sheet 14a having a thickness of 50 .mu.m.

Next, an electroconductive paste consisting essentially of Pd-Ag was printed on the ceramic green sheet 14a to form thereon an electroconductive paste layer 16, which serves as an inner electrode. See FIG. 3. As shown in FIG. 4, a plurality of the ceramic green sheets 14a each having the electroconductive paste layer 16 formed thereon were laminated in such a manner that the side of one sheet 14a having the electroconductive paste layer 16 exposed was alternated with that of another sheet 14a having the electroconductive paste layer 16 unexposed. Thus was obtained a laminate as shown in FIG. 2. This laminate was heated at 300.degree. C. in air, whereby the binder was burnt out, and was then fired for 2 hours. Then, external electrodes 18 were applied to the corresponding sides of the laminate to thereby connect the exposed inner electrodes 16.

Also, through use of a dielectric ceramic composition of Example 2, a monolithic ceramic capacitor can be manufactured in a manner similar to that described above.

As described hereinabove, the present invention provides a dielectric ceramic composition having a high specific inductive capacity, .di-elect cons.r, of not lower than 30 or not lower than 40, and a large Q value of not smaller than 1000 at 1 MHz, and which is capable of being fired at a low temperature of up to 1250.degree. C., i.e., capable of being applied to monolithic ceramic capacitors having inner electrodes made of Ag-Pd.

Claims

1. A dielectric ceramic composition containing an essential component represented by the following formula:

xBaO-yTiO.sub.2 -z(ReI.sub.a ReII.sub.(1-a)).sub.2 O.sub.3

where x, y and z are in mol %; x+y+z=100; (x, y, z) falls within a polygonal region defined by four points of A(39.5, 59.5, 1), B(1, 59.5, 39.5), C(1, 85, 14) and D(14, 85, 1); 0.2<a.ltoreq.1.0; ReI is at least one rare earth element selected from the group consisting of Tb, Dy, Ho, Er and Yb; and ReII is at least one rare earth element selected from the group consisting of La, Pr, Nd and Sm, and further containing V as a side component in an amount, .alpha., of about 0.1 wt. % to 15 wt. % in terms of V.sub.2 O.sub.5 relative to 100 wt. % of the essential component.

2. A dielectric ceramic composition as claimed in claim 1, wherein a is 1.

3. The dielectric ceramic composition as claimed in claim 2, which contains Cu as a side component in an amount, .beta., of not greater than about 10 wt. % in terms of CuO relative to 100 wt. % of the essential component.

4. The dielectric ceramic composition as claimed in claim 2, which contains Mn as a side component in an amount, .gamma., of not greater than about 1 wt. % in terms of MnO relative to 100 wt. % of the essential component.

5. The dielectric ceramic composition as claimed in claim 4, which contains Cu as a side component in an amount, .beta., of not greater than about 10 wt. % in terms of CuO relative to 100 wt. % of the essential component.

6. The dielectric ceramic composition as claimed in claim 5, wherein .alpha. is between about 2 and about 4, .beta. is between about 2 and about 4, and .gamma. is not greater than about 0.05.

7. The dielectric ceramic composition as claimed in claim 6, wherein (x, y, z) is about (10, 70, 20) and ReI is at least one of Ho and Er.

8. A dielectric ceramic composition as claimed in claim 1, wherein a is less than 1.

9. The dielectric ceramic composition as claimed in claim 8, which contains Cu as a side component in an amount, .beta., of not greater than about 10 wt. % in terms of CuO relative to 100 wt. % of the essential component.

10. The dielectric ceramic composition as claimed in claim 8, which contains Mn as a side component in an amount, .gamma., of not greater than about 1 wt. % in terms of MnO relative to 100 wt. % of the essential component.

11. The dielectric ceramic composition as claimed in claim 10, which contains Cu as a side component in an amount, .beta., of not greater than about 10 wt. % in terms of CuO relative to 100 wt. % of the essential component.

12. The dielectric ceramic composition as claimed in claim 11, wherein .alpha. is between about 2 and about 4, .beta. is between about 2 and about 4, and .gamma. is not greater than about 0.05.

13. A monolithic ceramic capacitor comprising:

a ceramic layer;

a plurality of inner electrodes which are embedded inside the ceramic layer, each of the electrodes being disposed so as to be apart from one another in the ceramic layer; and

outer electrodes on outer surfaces of the ceramic layer electrically conducted to the inner electrodes;

wherein

the ceramic layer is of a dielectric ceramic composition according to claim 1.

14. The monolithic ceramic capacitor as claimed in claim 13, wherein the inner electrodes are Pd-Ag.

15. A monolithic ceramic capacitor comprising:

a ceramic layer;

a plurality of inner electrodes which are embedded inside the ceramic layer, each of the electrodes being disposed so as to be apart from one another in the ceramic layer; and

outer electrodes on outer surfaces of the ceramic layer electrically conducted to the inner electrodes;

wherein

the ceramic layer is of a dielectric ceramic composition according to claim 2.

16. The monolithic ceramic capacitor as claimed in claim 15, wherein the inner electrodes are Pd-Ag.

17. A monolithic ceramic capacitor comprising:

a ceramic layer;

a plurality of inner electrodes which are embedded inside the ceramic layer, each of the electrodes being disposed so as to be apart from one another in the ceramic layer; and

outer electrodes on outer surfaces of the ceramic layer electrically conducted to the inner electrodes;

wherein

the ceramic layer is of a dielectric ceramic composition according to claim 6.

18. A monolithic ceramic capacitor comprising:

a ceramic layer;

a plurality of inner electrodes which are embedded inside the ceramic layer, each of the electrodes being disposed so as to be apart from one another in the ceramic layer; and

outer electrodes on outer surfaces of the ceramic layer electrically conducted to the inner electrodes;

wherein

the ceramic layer is of a dielectric ceramic composition according to claim 8.

19. The monolithic ceramic capacitor as claimed in claim 18, wherein the inner electrodes are Pd-Ag.

20. A monolithic ceramic capacitor comprising:

a ceramic layer;

a plurality of inner electrodes which are embedded inside the ceramic layer, each of the electrodes being disposed so as to be apart from one another in the ceramic layer; and

outer electrodes on outer surfaces of the ceramic layer electrically conducted to the inner electrodes;

wherein

the ceramic layer is of a dielectric ceramic composition according to claim 11.