Dielectric ceramic composition

Abstract

A dielectric ceramic composition consists essentially of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3, PbTiO.sub.3, Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 and M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 (wherein M represents at least one element selected from the group consisting of Ba, Sr and Ca), the mole percentages of said four components being as follows:______________________________________Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 45 to 75 mole %PbTiO.sub.3 20 to 40 mole %Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 0.5 to 15 mole %M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 1.0 to 10 mole %______________________________________The dielectric ceramic composition may further contain, as an additive, manganese in an amount of not more than 0.5 mole % in terms of MnO.sub.2. The composition possesses a high dielectric constant of not less than 8000 and a low sintering temperature of 900.degree. to 1000.degree. C.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a dielectric ceramic composition and, more particularly, an improved dielectric ceramic composition with a high dielectric constant of not less than 8000 and a low sintering temperature of 900.degree. to 1000.degree. C.

2. Description of the Prior Art

Recently, electronic appliances for industrial and consumer uses are required to have a design so that they are small, light-weight and functions at high frequencies. For this reason, there is an increasing demand for monolithic ceramic capacitors because of their large capacitance-to-volume ratio, high mass producibility and excellent electrical and physical characteristics including high frequency characteristics and heat resistance.

The monolithic ceramic capacitors are generally built up of an arrangement of alternating two layers of a dielectric layer, composed of a dielectric ceramic composition of a barium titanate system, and an internal electrode. The dielectric ceramic composition of the prior art has a high sintering temperature of 1300.degree. to 1400.degree. C., so that it has been required to use a noble metal such as Au, Pt and Pd as a material for internal electrodes. However, the noble metals are expensive to use and occupies the greater part of the manufacturing cost of the monolithic ceramic capacitors. Thus, the use of the noble metal sets a limit to lower the manufacturing cost of the monolithic ceramic capacitors.

To solve this problem, it has been proposed to incorporate a glass component comprising oxides of boron, bismuth and lead into the above modified barium titanate composition. The addition of the glass component lowers the sintering temperature to 1100.degree. to 1150.degree. C., thus making it possible to use a relatively inexpensive silver-paradium alloy as a material for internal electrodes. However, the incorporation of the glass component causes lowering of the dielectric constant, and thus the monolithic ceramic capacitors increase in size for a given capacitance. This results in increase in an amount of the electrode material to be used, thus making it difficult to reduce the manufacturing cost of the monolithic ceramic capacitors.

It is an object of the present invention to provide a dielectric ceramic composition with a high dielectric constant of not less than 8000 and a low sintering temperature of 900.degree. to 1000.degree. C.

Another object of the present invention is to provide a dielectric ceramic composition capable of being used as a dielectric material for monolithic ceramic capacitors comprising internal electrodes of a relatively inexpensive silver-paradium alloy.

SUMMARY OF THE INVENTION

According to the present invention there is provided a dielectric ceramic composition consisting essentially of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3, PbTiO.sub.3, Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 and M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 (where M represents at least one element selected from the group consisting of Ba, Sr and Ca), the mole percentages of said four components being as follows:

______________________________________Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 45 to 75 mole %PbTiO.sub.3 20 to 40 mole %Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 0.5 to 15 mole %M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 1.0 to 10 mole %______________________________________

The dielectric ceramic composition of the above four component system may further contain, as an additive, manganese in an amount of not more than 0.5 mole % in terms of MnO.sub.2 with respect to one mole of its basic composition consisting essentially of 45 to 75 mole % of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3, 20 to 40 mole % of PbTiO.sub.3, 0.5 to 15 mole % of Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3, and 1.0 to 10 mole % of M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 where M represents at least one element selected from the group consisting of Ba, Sr and Ca.

These and other objects, features and advantages of the present invention will be more apparent from the following description with reference to the preferred embodiments thereof.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The dielectric ceramic composition of the present invention was produced in the following manner.

As starting raw materials there were used highly purified oxides (purity: not less than 99.9%) PbO, NiO, Nb.sub.2 O.sub.5, TiO.sub.2, ZnO, WO.sub.3, CuO, SrCO.sub.3, BaCO.sub.3, CaCO.sub.3 and MnO.sub.2. These raw materials were weighed to prepare a mixture so that the each product has a composition with the compositional proportions shown in Table 1. Each of the resultant mixture (100 g) was wet milled in a polyethylene mill with agate balls for 10 hours. The resultant slurry was dried, placed in an alumina saggar, calcined at 650.degree. to 800.degree. C. for 2 hours, and then crushed to prepare powder of the primary reactant (calcined powder). The calcined powder was wet milled together with 3% by weight of polyvinyl alcohol incorporated therein as a binder, dried and then passed through a 50 mesh sieve screen. The thus obtained granulated powder was pressed into discs having a diameter of 12 mm and a thickness of 1.2 mm under a pressure of 2000 kg/cm.sup.2 with an oil press. The discs were placed in a zirconia saggar and then fired at 900.degree. to 1100.degree. C. for 2 hours with an electric furnace in a lead-containing atmosphere.

Each of the resultant ceramic disc was provided on its both sides with silver electrodes by applying silver paste containing borosilicate glass frit and then baking the same at 750.degree. C. for 10 minutes to prepare specimens for measurements of electrical properties.

The measurements were made on capacitance (C), dielectric loss (tan .delta.) and the insulation resistance (IR). The capacitance (C) and dielectric loss (tan .delta.) were measured at 1 KHz and 1 Vrms with an LCR meter, Model 4274 made by YOKOGAWA HEWLETT PACKARD CO. The insulation resistance (IR) was measured after applying a DC voltage of 500 V for 2 minutes with a megohom meter, Model TR 8601 made by TAKEDA RIKEN KOGYO CO. A thickness of the ceramic disc and a diameter of the opposed electrodes were measured to determine the dielectric constant (.epsilon.) and the specific resistance (.rho.). Results are shown in Table 2. The sintering temperatures for each specimen are also shown in Table 2.

In Tables 1 and 2, specimens with an asterisk (*) are those having a composition beyond the scope of the present invention, while other specimens are those included in the scope of the present invention.

TABLE 1__________________________________________________________________________Specimen Basic composition (mole %) AdditiveNo. Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 PbTiO.sub.3 Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 MnO.sub.2 (mole %)__________________________________________________________________________ 1* 74 24 0 M = Sr 2.0 0.0 2 73.5 24 0.5 " 2.0 0.0 3 65 26 7 " 2.0 0.0 4 55 28 15 " 2.0 0.0 5* 50 28 20 " 2.0 0.0 6* 58 35 7 " 0 0.0 7 61 28 10 " 1.0 0.0 8 59 26 10 M = Sr 5.0 0.0 9 56 24 10 " 10.0 0.0 10* 53 24 10 " 13.0 0.011 65 26 7 M = Ba 2.0 0.012 59 26 10 " 5.0 0.013 65 26 7 M = Ca 2.0 0.014 59 26 10 " 5.0 0.0 15* 78 15 5 M = Ba 2.0 0.0 16* 40 45 10 " 5.0 0.017 64.9 26 7 M = Sr 2.0 0.118 64.7 26 7 " 2.0 0.319 64.5 26 7 " 2.0 0.5 20* 64.0 26 7 " 2.0 1.021 64.7 26 7 M = Ca 2.0 0.322 64.7 26 7 M = Ba 2.0 0.3__________________________________________________________________________ TABLE 2______________________________________Specimen Sintering tan .delta. .rho.(.OMEGA.-cm)No. temp (.degree.C.) .epsilon. (%) At 25.degree. C. At 85.degree. C.______________________________________ 1* 1050 6400 0.12 3.12 .times. 10.sup.13 2.48 .times. 10.sup.12 2 1000 9300 0.21 2.52 .times. 10.sup.12 3.18 .times. 10.sup.11 3 950 16600 0.35 1.12 .times. 10.sup.12 5.08 .times. 10.sup.11 4 900 14700 0.30 8.01 .times. 10.sup.11 6.33 .times. 10.sup.10 5* 900 7100 1.50 7.94 .times. 10.sup.8 1.39 .times. 10.sup.7 6* 1060 19000 1.25 3.82 .times. 10.sup.11 4.94 .times. 10.sup.10 7 950 17700 0.91 2.55 .times. 10.sup.11 9.96 .times. 10.sup.10 8 900 13200 0.71 1.09 .times. 10.sup.12 1.22 .times. 10.sup.11 9 900 9400 0.32 5.01 .times. 10.sup.11 1.01 .times. 10.sup.10 10* 900 6800 0.19 3.16 .times. 10.sup. 9 1.15 .times. 10.sup.711 950 15900 0.55 4.98 .times. 10.sup.11 3.99 .times. 10.sup.912 900 11400 0.44 7.99 .times. 10.sup.11 6.28 .times. 10.sup.1013 950 12000 0.15 3.21 .times. 10.sup.11 2.50 .times. 10.sup.1014 900 9700 0.12 2.57 .times. 10.sup.11 1.31 .times. 10.sup.10 15* 1100 4100 0.11 1.00 .times. 10.sup.13 4.92 .times. 10.sup.11 16* 900 5400 5.70 1.26 .times. 10.sup.11 1.41 .times. 10.sup.1017 950 15700 0.34 5.06 .times. 10.sup.12 9.97 .times. 10.sup.1118 950 15100 0.27 1.59 .times. 10.sup.13 1.69 .times. 10.sup.1219 950 14300 0.30 3.19 .times. 10.sup.13 2.46 .times. 10.sup.12 20* 950 6900 0.98 2.53 .times. 10.sup.10 1.05 .times. 10.sup.821 950 12100 0.20 3.98 .times. 10.sup.13 1.71 .times. 10.sup.1222 950 14400 0.33 2.59 .times. 10.sup.13 1.02 .times. 10.sup.12______________________________________

From the results shown in Table 2, it is apparent that the dielectric ceramic composition according to the present invention has a high dielectric constant of not less than 8000 and a low sintering temperature ranging from 900.degree. to 1000.degree. C.

In the present invention, the mole percentages of the four components, Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3, PbTiO.sub.3, Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 and M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 are limited to the ranges as defined above for the following reasons.

Firstly, if the content of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 is less than 45 mole %, the dielectric constant decreases to less than 8000 and the dielectric loss (tan .delta.) increases to more than 2.5%. If the content of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 is greater than 75 mole %, the dielectric constant decreases to less than 8000.

Secondary, if the content of PbTiO.sub.3 is less than 20 mole %, the dielectric constant decreases to less than 8000. If the content of PbTiO.sub.3 is greater than 40 mole %, the dielectric constant decreases to less than 8000 and the dielectric loss tangent increases to more than 2.5%.

Thirdly, if the content of Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 is less than 0.5 mole %, the sintering temperature rises to a temperature higher than 1000.degree. C. and the dielectric constant decreases to less than 8000.degree.. If the content of Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 is greater than 15 mole %, the sintering temperature lowers to a temperature of less than 900.degree. C., but the dielectric constant decreases to less than 8000 and the specific resistance decreases to less than 10.sup.11 .OMEGA.-cm at room temperature.

If the content of M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 is less than 1.0 mole %, the sintering temperature rises to a temperature higher than 1000.degree. C. If the content of M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 is greater than 10 mole %, the dielectric constant decreases to less than 8000 and the specific resistance decreases to less than 10.sup.11 .OMEGA.-cm.

The added amount of manganese is limited to the range of not more than 0.5 mole % in terms of MnO.sub.2 with respective one mole of the basic composition of the four components for the following reasons. If the added amount of Mn is greater than 0.5 mole %, the specific resistance lowers to less than 10.sup.11 .OMEGA.-cm.

The dielectric ceramic composition of the present invention has excellent electrical and physical properties. They include,

(1) a high dielectric constant (.epsilon.) of not less than 8000

(2) a low dielectric loss (tan .delta.) of not more than 2.5%

(3) a high specific resistance of not less than 10.sup.11 .OMEGA.-cm at room temperature.

(4) a low sintering temperature of 900.degree. to 1000.degree. C.

(5) the specific resistance at room temperature and an elevated temperature (85.degree. C.) may be further increased by incorporation of a specific amount of Mn, and the specific resistance of not less than 10.sup.12 .OMEGA.-cm can be obtained at room temperature.

Accordingly, the dielectric ceramic composition of the present invention can be used as a dielectric material not only for fixed ceramic capacitors but also for monolithic ceramic capacitors. The dielectric ceramic composition of the present invention has a low sintering temperature, thus making it possible to use a relatively inexpensive silver-paradium alloy as a material for internal electrodes of monolithic ceramic capacitors. Accordingly, it is possible to manufacture monolithic ceramic capacitors with a large capacitance-to-volume ratio at a low cost.

Claims

1. A dielectric ceramic composition consisting essentially of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3, PbTiO.sub.3, Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 and M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 (wherein M represents at least one element selected from the group consisting of Ba, Sr and Ca), the mole percentages of said four components being as follows:

______________________________________Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 45 to 75 mole %PbTiO.sub.3 20 to 40 mole %Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3 0.5 to 15 mole %M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3 1.0 to 10 mole %______________________________________

2. The dielectric ceramic composition according to claim 1 containing, as an additive, manganese in an amount of not more than 0.5 mole % in terms of MnO.sub.2 with respect to one mole of its basic composition consisting essentially of 45 to 75 mole % of Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3, 20 to 40 mole % of PbTiO.sub.3, 0.5 to 15 mole % of Pb(Zn.sub.1/2 W.sub.1/2)O.sub.3, and 1.0 to 10 mole % of M(Cu.sub.1/3 Nb.sub.2/3)O.sub.3.

3. The dielectric ceramic composition according to claim 1 wherein said composition possesses a high dielectric constant of not less than 8000 and a low sintering temperature of 900.degree. to 1000.degree. C.