Abstract
A dielectric ceramic composition exhibiting a high dielectric constant, capable of sintering in a short time, at a sintering temperature of 800.degree. to 1000.degree. C., in the atmosphere, a neutral atmosphere or a reducing atmosphere.The dielectric ceramic composition comprises a main ceramic component represented by the formula PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, wherein x+y+z=1, and subsidiary components of PbO is added in an amount of 1.0 to 25.0 mol % and NiO or WO.sub.3 in an amount of 1.0 to 15.0 mol %. The subsidiary components are added to the calcined powder of the main component.Also provided is a dielectric ceramic composition comprising a main ceramic component represented by the formula PbZr.sub.x (Ni.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, wherein x+y+z=1, and subsidiary components of PbO in an amount of 1.0 to 25.0 mol % and NiO in an amount of 1.0 to 15.0 mol %. The subsidiary components are added to the calcined powder of the main component.The dielectric ceramic compositions are useful in preparing laminate ceramic capacitors and thick film capacitors.
Description

BACKGROUND OF THE INVENTION
The present invention relates to a dielectric ceramic composition exhibiting a high dielectric constant, capable of sintering in a short time, at a sintering temperature of 800.degree. to 1000.degree. C., in the atmosphere, a neutral atmosphere or a reducing atmosphere.
As materials exhibiting a high dielectric constant suitable for use in ceramic capacitors which are progressively reduced in size and enlarged in capacity, materials mainly composed of barium titanate have been hitherto employed. However, it is necessary to sinter these materials in the atmosphere at a high temperature of about 1300.degree. C. Therefore, when fabricating laminate ceramic capacitors, expensive noble metals such as platinum and palladium are indispensable as the electrode materials, and in particular along with the trend for increasing capacity, the cost of the internal electrode material has pushed up the material cost.
Recently, it has been attempted to lower the cost of laminate ceramic capacitors by, inter alia, the following two methods. One method involves making barium titanate material resistive to reduction, and sintering it in an atmosphere of a low oxygen partial pressure, thus making it possible to use an inexpensive base metal as the electrode material. The other method involves sintering at a low temperature of about 1000.degree. C. a silver-palladium alloy electrode material and a lead dielectric material and inexpensive silver.
On the other hand, in electronic appliances where reduction in size and enhancement of reliability are demanded, the hybrid IC of a high packaging density is promoted, and the demand for a thick film capacitor is mounting to replace the conventional chip capacitor. To fabricate this thick film capacitor, a dielectric material capable of sintering at a low temperature and in a short time is required, and the lead dielectric is used mainly as this material. Therefore, as the material applicable to both increasing the capacity of a laminate chip capacitor and providing a thick film capacitor, the lead dielectric is being developed intensively.
A PbTiO.sub.3 - Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3 - Pb(Ni.sub.1/2 W.sub.1/2)O.sub.3 solid solution and a PbZrO.sub.3 - Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 - Pb(Ni.sub.1/2 Wi1/2)O.sub.3 solid solution are compositions exhibiting a high dielectric constant which can be sintered in the atmosphere at 1100.degree. C. or a lower temperature, as disclosed in Japanese Patent Laid-Open Nos. 61-155249 and No. 61-155248, but it is necessary to maintain the sintering temperature for several hours in order to heighten the dielectric constant and to obtain sintered material having a sufficient density. On the other hand, when fabricating a thick film capacitor for a hybrid IC, a low temperature and a short sintering time is indispensable, and these dielectric materials are not sintered completely under such conditions, and therefore the desired characteristics are not obtained. Still worse, due to the effects of heat in a neutral or reducing atmosphere over a long period of time, oxygen defects are likely to occur in the dielectric ceramics, which lead to practical problems such as lowering of the dielectric constant and reduction of insulation resistance.
SUMMARY OF THE INVENTION
In light of the above-discussed problems, it is a primary object of the present invention to provide a dielectric ceramic composition exhibiting a high dielectric constant, and a ceramic capacitor or thick film capacitor using the same, capable of sintering at 800.degree. to 1000.degree. C. in a short time in the atmosphere, a neutral atmosphere or a reducing atmosphere, without detrimentally affecting the high dielectric constant of a PbTiO.sub.3 - Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3 - Pb(Ni.sub.1/2 W.sub.1/2)O.sub.3 solid solution and a PbZrO.sub.3 - Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 - Pb(Ni.sub.1/2 Wi.sub.1/2)O.sub.3 solid solution.
To achieve the above object, the present invention provides a dielectric ceramic composition comprising main ceramic components represented by the formula PbTi .sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, wherein x+y+z=1, and subsidiary components of PbO is added in an amount of 1.0 to 25.0 mol % and NiO or WO.sub.3 in an amount of 1.0 to 15.0 mol %. The subsidiary components are added to the calcined powder of the main components represented by the formula PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni1/2 W.sub.1/2).sub.z O.sub.3. In FIG. 1, the polygon ABCDE shows a range of composition of the ceramic composition of the present invention, and the compositions A, B, C, D, E at the vertices of the polygon are expressed by the following numerical values: ##EQU1##
Also, the present invention provides a dielectric ceramic composition comprising main ceramic components represented by the formula PbZr.sub.x (Ni.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, wherein x+y+z=1, and subsidiary components of PbO in an amount of 1.0 to 25.0 mol % and NiO in an amount of 1.0 to 15.0 mol %. The subsidiary components are added to the calcined powder of the main components represented by the formula PbZr.sub.x Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3. In FIG. 2, the polygon ABCD shows a range of composition of the ceramic composition of the present invention, and the compositions A, B, C, and D at the vertices of the polygon are expressed by the following numerical values: ##EQU2##
In other words, in the dielectric ceramic composition of the invention, by adding PbO and NiO or Wo.sub.3 to the calcined powder of PbTiO.sub.3 - Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3 -Pb(Ni.sub.1/2 W.sub.1/2)O.sub.3 system and PbZrO.sub.3 - Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 -Pb(Ni.sub.1/2 W.sub.1/2)O.sub.3 system having the perovskite structure, a liquid phase is generated at low temperature by making use of the eutectic composition of PbO and NiO, or PbO and WO.sub.3, and when these additives are simultaneously solubilized at site A and site B, diffusion into the dielectric is smooth, and formation of a grain boundary layer due to additives is suppressed. Therefore, by preventing a lowering of the dielectric constant, it is possible to obtain a laminate ceramic capacitor or a thick film capacitor of a large capacity capable of being sintered to a sufficient density in a short time at a low baking temperature of not more than 1000.degree. C.
The invention will be better understood, along with other objects and features thereof, from the following detailed description in conjunction with the drawings.





BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a ternary system composition diagram mainly composed of PbTiO.sub.3, Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3 and Pb(Ni.sub.1/2 W.sub.1/2)O.sub.3 showing the composition range of one of the embodiments of the invention, and
FIG. 2 is a ternary system composition diagram mainly composed of PbZrO.sub.3, Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 and PB(Ni.sub.1/2 W.sub.1/2)O.sub.3 showing the composition range of the other embodiment of the invention.





DETAILED DESCRIPTION OF THE INVENTION
Some of the preferred embodiments of the invention are described in detail below.
Example 1
As the starting materials, PbO, MgO, Nb.sub.2 O.sub.5, TiO.sub.2, NiO, and WO.sub.3 of chemically high purity were used. After correcting their purity, specified amounts were weighed, and purified water was added, and then mixed in a ball mill for 17 hours using agate balls. After separating the majority of water content by suction filtration, the residue was dried, sufficiently crushed by an automatic agate mortar, and 5 wt. % of the powder of purified water was added, and the powder was formed into a columnar shape of 60 mm in diameter and about 50 mm in height at a forming pressure of 500 kg/cm.sup.2. It was then put in an aluminum crucible, covered with a lid of the same material, and calcined at 750.degree. to 1000.degree. C. for 2 hours. This calcined material was coarsely crushed by an alumina mortar, then further crushed by a ball mill for 17 hours, and dried after suction filtration. This process of calcination, crushing and drying was repeated several times. The resultant powder was analyzed by X-ray analysis, and the perovskite phase was recognized.
To this dielectric powder, PbO and NiO or WO.sub.3 were added as subsidiary components, and mixed by the automatic agate mortar, then a 6 wt. % aqueous solution of polyvinyl alcohol was added in an amount of 6 wt. % of the powder, subsequently granulated through a 32-mesh sieve, and formed into a disk of 13 mm in diameter and about 5 mm in height at a forming pressure of 1000 kg/cm.sup.2. Next this formed disk was kept in a 600.degree. C. atmosphere for 1 hour to get rid of the binder, then put into a magnesia ceramic container and covered with a lid of the same material, and heated to a specified temperature at a rate of 2400.degree. C./hr in the atmosphere, a neutral atmosphere or a reducing atmosphere, and after holding at the maximum temperature for 5 to 30 minutes, it was cooled at a rate of 2400.degree. C./hr.
The thus obtained sintered piece was processed into a disk of 1 mm in thickness, and Cr-Au was evaporated on both sides to form the electrodes, and the dielectric constant and tan .delta. were measured in an electric field of 1 kHz, 1 V/mm. Table 1 shows the material composition of the invention and the dielectric characteristics of the specimens sintered in the atmosphere. The results were of 900.degree. C. sintered in the sintering atmosphere of a neutral atmosphere of nitrogen, and in a nitrogen-hydrogen mixed gas with an oxygen partial pressure of 10.sup.-8 atm or more are shown in Tables 2 and 3, respectively.
TABLE 1__________________________________________________________________________Principal dielectriccomposition Pb(Mg.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Baking Dielectric tan .delta. PbTiO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 temperature constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (.degree.C.) (20.degree. C.) [%]__________________________________________________________________________ 1* 20.0 70.0 10.0 0 0 0 900 1920 4.5 2* 20.0 70.0 10.0 0.5 0.5 0 900 3280 3.3 3 20.0 70.0 10.0 1.0 1.0 0 900 8950 3.9 4 20.0 70.0 10.0 10.0 5.0 0 900 13500 4.8 5 20.0 70.0 10.0 25.0 15.0 0 900 9680 3.9 6* 20.0 70.0 10.0 30.0 25.0 0 900 4810 3.5 7 2.5 95.0 2.5 10.0 5.0 0 900 8520 4.3 8 12.5 85.0 2.5 10.0 5.0 0 900 10500 3.8 9 60.0 10.0 30.0 10.0 5.0 0 900 6360 4.110 40.0 10.0 50.0 10.0 5.0 0 900 6880 1.511 2.5 90.0 7.5 10.0 5.0 0 900 7130 1.2 12* 20.0 70.0 10.0 0.5 0 0.5 900 3300 5.013 20.0 70.0 10.0 1.0 0 1.0 900 8720 4.014 20.0 70.0 10.0 10.0 0 5.0 900 8550 3.515 20.0 70.0 10.0 25.0 0 15.0 900 7640 3.0 16* 20.0 70.0 10.0 30.0 0 25.0 900 4360 3.917 2.5 95.0 2.5 10.0 0 5.0 900 7670 2.618 12.5 85.0 2.5 10.0 0 5.0 900 10260 2.919 60.0 10.0 30.0 10.0 0 5.0 900 6810 2.620 40.0 10.0 50.0 10.0 0 5.0 900 7280 1.821 2.5 90.0 7.5 10.0 0 5.0 900 6950 2.0 22* 20.0 70.0 10.0 10.0 5.0 0 750 3650 8.523 20.0 70.0 10.0 10.0 5.0 0 800 6280 7.624 20.0 70.0 10.0 10.0 5.0 0 850 7300 5.325 20.0 70.0 10.0 10.0 5.0 0 950 12030 4.326 20.0 70.0 10.0 10.0 5.0 0 1000 7600 6.0 27* 20.0 70.0 10.0 10.0 5.0 0 1050 4530 7.8 28* 20.0 70.0 10.0 10.0 0 5.0 750 2860 9.329 20.0 70.0 10.0 10.0 0 5.0 800 5620 8.630 20.0 70.0 10.0 10.0 0 5.0 850 6030 5.531 20.0 70.0 10.0 10.0 0 5.0 950 9780 4.832 20.0 70.0 10.0 10.0 0 5.0 1000 6830 3.9 33* 20.0 70.0 10.0 10.0 0 5.0 1050 4320 5.9__________________________________________________________________________ *The asterisked specimens are reference examples.
TABLE 2__________________________________________________________________________Principal dielectriccomposition Pb(Mg.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Dielectric tan .delta. PbTiO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (20.degree. C.) [%]__________________________________________________________________________ 1* 20.0 70.0 10.0 0 0 0 1720 6.5 2* 20.0 70.0 10.0 0.5 0.5 0 3070 5.3 3 20.0 70.0 10.0 1.0 1.0 0 9020 6.2 4 20.0 70.0 10.0 10.0 5.0 0 12250 6.9 5 20.0 70.0 10.0 25.0 15.0 0 8860 5.0 6* 20.0 70.0 10.0 30.0 25.0 0 3520 5.3 7 2.5 95.0 2.5 10.0 5.0 0 8790 6.8 8 12.5 85.0 2.5 10.0 5.0 0 11220 6.0 9 60.0 10.0 30.0 10.0 5.0 0 6000 5.210 40.0 10.0 50.0 10.0 5.0 0 6380 3.511 2.5 90.0 7.5 10.0 5.0 0 6820 2.3 12* 20.0 70.0 10.0 0.5 0 0.5 2650 5.013 20.0 70.0 10.0 1.0 0 1.0 9010 4.514 20.0 70.0 10.0 10.0 0 5.0 10660 6.215 20.0 70.0 10.0 25.0 0 15.0 7650 6.3 16* 20.0 70.0 10.0 30.0 0 25.0 3960 8.217 2.5 95.0 2.5 10.0 0 5.0 7570 3.618 12.5 85.0 2.5 10.0 0 5.0 10580 3.819 60.0 10.0 30.0 10.0 0 5.0 6660 3.920 40.0 10.0 50.0 10.0 0 5.0 7080 1.821 2.5 90.0 7.5 10.0 0 5.0 7060 2.0__________________________________________________________________________ *The asterisked specimens are reference examples.
TABLE 3__________________________________________________________________________Principal dielectriccomposition Pb(Mg.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Dielectric tan .delta. PbTiO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (20.degree. C.) [%]__________________________________________________________________________ 1* 20.0 70.0 10.0 0 0 0 1520 8.0 2* 20.0 70.0 10.0 0.5 0.5 0 3060 7.8 3 20.0 70.0 10.0 1.0 1.0 0 7950 5.9 4 20.0 70.0 10.0 10.0 5.0 0 9860 5.1 5 20.0 70.0 10.0 25.0 15.0 0 8680 5.3 6* 20.0 70.0 10.0 30.0 25.0 0 3950 5.9 7 2.5 95.0 2.5 10.0 5.0 0 7960 6.0 8 12.5 85.0 2.5 10.0 5.0 0 9890 6.3 9 60.0 10.0 30.0 10.0 5.0 0 6420 8.610 40.0 10.0 50.0 10.0 5.0 0 6350 3.511 2.5 90.0 7.5 10.0 5.0 0 7090 2.9 12* 20.0 70.0 10.0 0.5 0 0.5 3070 5.213 20.0 70.0 10.0 1.0 0 1.0 8360 4.814 20.0 70.0 10.0 10.0 0 5.0 8500 4.315 20.0 70.0 10.0 25.0 0 15.0 7840 4.9 16* 20.0 70.0 10.0 30.0 0 25.0 3960 5.617 2.5 95.0 2.5 10.0 0 5.0 6670 4.318 12.5 85.0 2.5 10.0 0 5.0 10020 4.619 60.0 10.0 30.0 10.0 0 5.0 6320 2.620 40.0 10.0 50.0 10.0 0 5.0 6940 2.321 2.5 90.0 7.5 10.0 0 5.0 6720 1.9__________________________________________________________________________ *The asterisked specimens are reference examples.
As shown in Tables 1 to 3, in the material composition of the invention, in spite of a short sintering time at 900.degree. C., and in various atmospheres, densely sintered bodies of a high dielectric constant were obtained.
In FIG. 1 the composition range of the principal components of the invention are shown in the ternary system composition diagram mainly composed of PbTiO.sub.3, Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3 and Pb(Ni.sub.1/2 W.sub.1/2)O.sub.3.
Here, the reason of specifically defining the claimed ceramic composition as:
a dielectric ceramic composition comprising main ceramic components represented by the formula PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, wherein x+y+z=1, and subsidiary components of PbO is added in an amount of 1.0 to 25.0 mol % and NiO or WO.sub.3 in an amount of 1.0 to 15.0 mol %. The subsidiary components are added to the calcined powder of the main components represented by the formula PbTi.sub.x (Mg.sub.1/3 Nb2/3).sub.y (Ni.sub.178 W.sub.1/2).sub.z O.sub.3. In FIG. 1, the polygon ABCDE shows a range of composition of the ceramic composition of the present invention, and the compositions A, B, C, D, E at the vertices of the polygon are expressed by the following numerical values: ##EQU3##
is that the sintering is insufficient in a composition outside the specified range, as indicated by the reference examples shown in Tables 1 to 3, since the dielectric constant of the sintered materials at a sintering temperature of 900.degree. C. is less than 5000. Furthermore, at a sintering temperature of 800.degree. C. or less, the sintering is insufficient, and at 1000.degree. C. or higher, the dielectric constant is lowered, and desired characteristics may not be obtained.
Example 2
Similar to Example 1, to the calcined, crushed and dried dielectric power, PbO and NiO or WO.sub.3 were added as subsidiary components, mixed in a wet process by a ball mill, the mixture was dried, a vehicle having a resin mainly made of ethyl cellulose dissolved in solvent was added, the compound was kneaded in three-stage rolls, and a dielectric paste was prepared. On the other hand, in order to form a thick film capacity of 2.times.2 mm.sup.2 on an alumina substrate of 96% purity, a copper electrode was printed and dried as the lower electrode, the obtained dielectric paste was printed and dried in a thickness of 50 to 60 .mu.m as the dielectric layer in two steps, a copper electrode similar to the lower electrode was printed and dried as the upper electrode, thereby forming a three-layer printed thick film consisting of an electrode, dielectric and electrode, and it was sintered in a nitrogen atmosphere at a maximum temperature of 800.degree. to 1000.degree. C., for 5 to 30 minutes, in a belt furnace. The dielectric constant and tan .delta. of the thus obtained thick film capacitor were measured in an electric field of 1 kHz, 1 V/mm. The material composition of the invention and the dielectric characteristics of the specimens sintered at 900.degree. C. in nitrogen are shown in Table 4.
TABLE 4__________________________________________________________________________Principal dielectriccomposition Pb(Mg.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Dielectric tan .delta. PbTiO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (20.degree. C.) [%]__________________________________________________________________________ 1* 20.0 70.0 10.0 0 0 0 1530 8.9 2* 20.0 70.0 10.0 0.5 0.5 0 2980 6.8 3 20.0 70.0 10.0 1.0 1.0 0 7620 5.8 4 20.0 70.0 10.0 10.0 5.0 0 8320 4.8 5 20.0 70.0 10.0 25.0 15.0 0 6250 4.2 6* 20.0 70.0 10.0 30.0 25.0 0 3500 6.2 7 2.5 95.0 2.5 10.0 5.0 0 6360 5.3 8 12.5 85.0 2.5 10.0 5.0 0 6950 4.9 9 60.0 10.0 30.0 10.0 5.0 0 5260 4.910 40.0 10.0 50.0 10.0 5.0 0 5100 3.911 2.5 90.0 7.5 10.0 5.0 0 5120 2.9 12* 20.0 70.0 10.0 0.5 0 0.5 2970 5.613 20.0 70.0 10.0 1.0 0 1.0 6980 5.814 20.0 70.0 10.0 10.0 0 5.0 7930 4.915 20.0 70.0 10.0 25.0 0 15.0 6240 3.7 16* 20.0 70.0 10.0 30.0 0 25.0 2360 7.917 2.5 95.0 2.5 10.0 0 5.0 6670 3.818 12.5 85.0 2.5 10.0 0 5.0 7680 3.319 60.0 10.0 30.0 10.0 0 5.0 5390 2.820 40.0 10.0 50.0 10.0 0 5.0 6020 2.621 2.5 90.0 7.5 10.0 0 5.0 5020 9.0__________________________________________________________________________ *The asterisked specimens are reference examples.
As shown in Table 4, by using the sintered materials of the material composition of the invention, thick film capacitors exhibiting a high dielectric constant having a high density were obtained in spite of a short time and low-temperature sintering.
As demonstrated in Example 1, the dielectric constant of the sinters are less than 5000 at a sintering temperature of 800.degree. to 1000.degree. C., and the sintering is insufficient, in compositions other than those in the defined range of the present invention as indicated by the reference examples in Table 4.
In this embodiment, it is shown that sintering is possible in nitrogen, but it may be easily inferred that sintering is also possible in a neutral atmosphere of argon, helium or the like.
Meanwhile, as the electrodes used in the invention, any electrodes that can be sintered at 800 to 1000.degree. C. in the atmosphere, a neutral atmosphere or a reducing atmosphere may be properly selected and used.
Example 3
As the starting materials, PbO, ZrO.sub.2, Nb.sub.2 O.sub.5, NiO and WO.sub.3 of chemically high purity were used. They were processed in the same manner as in Example 1, and a dielectric powder was prepared.
To this dielectric powder, PbO and NiO or WO.sub.3 were added as subsidiary components, mixed by an automatic agate mortar, a 6 wt. % aqueous solution of polyvinyl alcohol was added in an amount of 6 wt. % of the powder, the mixture was granulated through a 32-mesh sieve, and formed into a disk of 13 mm in a diameter and about 5 mm in height at a forming pressure of 1000 kg/cm.sup.2. This formed disk was held in a 600.degree. C. atmosphere for 1 hour to get rid of the binder, then put in a magnesia ceramic container and covered with a lid of the same material, and heated to a specified temperature in the atmosphere, a neutral atmosphere or a reducing atmosphere at a rate of 2400.degree. C./hr, and after holding at the maximum temperature for 5 to 30 minutes, it was cooled at a rate of 2400.degree. C./hr.
The thus obtained sintered piece was processed into a disk of 1 mm in thickness, C-Au was evaporated on both sides as the electrodes, and the dielectric constant and tan .delta. were measured in an electric field of 1 kHz, 1 V/mm. Table 5 shows the material composition of the invention and the dielectric characteristics of the specimens sintered in the atmosphere. The results of 900.degree. C. sintering in the sintering atmosphere of a neutral atmosphere of nitrogen, and in a nitrogen-hydrogen mixed gas with the oxygen particle pressure of 10.sup.-8 atm or more are shown in Tables 6 and 7, respectively.
TABLE 5__________________________________________________________________________Principal dielectriccomposition Pb(Ni.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Baking Dielectric tan .delta. PbZrO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 temperature constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (.degree.C.) (20.degree. C.) [%]__________________________________________________________________________ 1* 55.0 30.0 15.0 0 0 0 900 1280 8.9 2* 55.0 30.0 15.0 0.5 0.5 0 900 2400 7.2 3 55.0 30.0 15.0 1.0 1.0 0 900 4750 6.3 4 55.0 30.0 15.0 10.0 5.0 0 900 8200 6.6 5 55.0 30.0 15.0 25.0 15.0 0 900 5020 5.9 6* 55.0 30.0 15.0 30.0 25.0 0 900 2900 5.7 7 35.0 60.0 5.0 10.0 5.0 0 900 8420 3.2 8 55.0 40.0 5.0 10.0 5.0 0 900 6130 5.8 9 65.0 20.0 15.0 10.0 5.0 0 900 6030 5.010 52.0 20.0 27.0 10.0 5.0 0 900 5840 2.2 11* 55.0 30.0 15.0 0.5 0 0.5 900 1780 6.312 55.0 30.0 15.0 1.0 0 1.0 900 4020 5.813 55.0 30.0 15.0 10.0 0 5.0 900 7280 5.514 55.0 30.0 15.0 25.0 0 15.0 900 4050 4.8 15* 55.0 30.0 15.0 30.0 0 25.0 900 2530 5.016 35.0 60.0 5.0 10.0 0 5.0 900 7540 2.717 55.0 40.0 5.0 10.0 0 5.0 900 5900 4.818 65.0 20.0 15.0 10.0 0 5.0 900 5750 5.019 52.5 20.0 27.5 10.0 0 5.0 900 5020 1.8 20* 55.0 30.0 15.0 10.0 5.0 0 750 2900 12.321 55.0 30.0 15.0 10.0 5.0 0 800 4430 8.222 55.0 30.0 15.0 10.0 5.0 0 850 7090 7.223 55.0 30.0 15.0 10.0 5.0 0 950 8070 6.524 55.0 30.0 15.0 10.0 5.0 0 1000 5710 6.8 25* 55.0 30.0 15.0 10.0 5.0 0 1050 2240 8.8 26* 55.0 30.0 15.0 10.0 0 5.0 750 1940 14.827 55.0 30.0 15.0 10.0 0 5.0 800 4860 8.828 55.0 30.0 15.0 10.0 0 5.0 850 6400 5.929 55.0 30.0 15.0 10.0 0 5.0 950 7240 5.230 55.0 30.0 15.0 10.0 0 5.0 1000 5200 6.3 31* 55.0 30.0 15.0 10.0 0 5.0 1050 1080 8.8__________________________________________________________________________ *The asterisked specimens are reference examples.
TABLE 6__________________________________________________________________________Principal dielectriccomposition Pb(Ni.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Dielectric tan .delta. PbZrO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (20.degree. C.) [%]__________________________________________________________________________ 1* 55.0 30.0 15.0 0 0 0 1380 8.5 2* 55.0 30.0 15.0 0.5 0.5 0 2320 8.2 3 55.0 30.0 15.0 1.0 1.0 0 4540 7.2 4 55.0 30.0 15.0 10.0 5.0 0 7960 6.8 5 55.0 30.0 15.0 25.0 15.0 0 5080 5.8 6* 55.0 30.0 15.0 30.0 25.0 0 3890 5.9 7 35.0 60.0 5.0 10.0 5.0 0 8000 3.5 8 55.0 40.0 5.0 10.0 5.0 0 6300 5.5 9 65.0 20.0 15.0 10.0 5.0 0 5580 4.910 52.5 20.0 27.5 10.0 5.0 0 5800 1.9 11* 55.0 30.0 15.0 0.5 0 0.5 1520 7.212 55.0 30.0 15.0 1.0 0 1.0 4350 6.613 55.0 30.0 15.0 10.0 0 5.0 7030 5.814 55.0 30.0 15.0 25.0 0 15.0 4850 5.0 15* 55.0 30.0 15.0 30.0 0 25.0 3100 5.016 35.0 60.0 5.0 10.0 0 5.0 6920 3.017 55.0 40.0 5.0 10.0 0 5.0 6070 4.818 65.0 20.0 15.0 10.0 0 5.0 5550 5.219 52.5 20.0 27.5 10.0 0 5.0 4910 2.0__________________________________________________________________________ *The asterisked specimens are reference examples.
TABLE 7__________________________________________________________________________Principal dielectriccomposition Pb(Ni.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Dielectric tan .delta. PbZrO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (20.degree. C.) [%]__________________________________________________________________________ 1 55.0 30.0 15.0 0 0 0 1080 9.2 2 55.0 30.0 15.0 0.5 0.5 0 2520 10.3 3 55.0 30.0 15.0 1.0 1.0 0 4320 8.2 4 55.0 30.0 15.0 10.0 5.0 0 7530 8.3 5 55.0 30.0 15.0 25.0 15.0 0 5130 6.2 6* 55.0 30.0 15.0 30.0 25.0 0 3900 6.3 7 35.0 60.0 5.0 10.0 5.0 0 7830 4.0 8 55.0 40.0 5.0 10.0 5.0 0 6210 5.2 9 65.0 20.0 15.0 10.0 5.0 0 6400 4.910 52.5 20.0 27.5 10.0 5.0 0 5130 1.8 11* 55.0 30.0 15.0 0.5 0 0.5 1330 8.412 55.0 30.0 15.0 1.0 0 1.0 4430 8.013 55.0 30.0 15.0 10.0 0 5.0 7170 7.714 55.0 30.0 15.0 25.0 0 15.0 4380 8.5 15* 55.0 30.0 15.0 30.0 0 25.0 3100 6.816 35.0 60.0 5.0 10.0 0 5.0 6740 4.217 55.0 40.0 5.0 10.0 0 5.0 5890 4.918 65.0 20.0 15.0 10.0 0 5.0 5500 4.919 52.5 20.0 27.5 10.0 0 5.0 5410 2.2__________________________________________________________________________ *The asterisked specimens are reference examples.
As shown in Tables 5 to 7, using the material composition of the invention, in spite of the short sintering time at 900.degree. C., and in various atmospheres, densely sintered bodies exhibiting a high dielectric constant were obtained.
In FIG. 2, the composition range of the principal components of the invention is shown in the ternary system composition diagram mainly composed of PbZrO.sub.3, Pb(Ni.sub.1/3 Nb.sub.2/3)O.sub.3 and Pb(Ni.sub.1/2 W.sub.1/2)O.sub.3.
Here, the reason of specifically defining the claimed ceramic composition as:
a dielectric ceramic composition comprising main ceramic components represented by the formula PbZr.sub.x (Ni.sub.1/3 Nb.sub.2/3).sub.y (W.sub.1/2).sub.z O.sub.3, wherein x+y+z=1, and subsidiary components of PbO in an amount of 1.0 to 25.0 mol % and NiO in an amount of 1.0 to 15.0 mol %. The subsidiary components are added to the calcined powder of the main components represented by the formula PbZr.sub.x (Ni.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3. In FIG. 2, the polygon ABCD shows a range of composition of the ceramic composition of the present invention, and the compositions A, B, C, and D at the vertices of the polygon are expressed by the following numerical values: ##EQU4## is that the sintering is insufficient and the dielectric constant of the sinters which are sintered at a sintering temperature of 900.degree. C. is less than 5000 in a composition outside the specified range as indicated by reference examples shown in Tables 5 to 7. Furthermore, at sintering temperature of 800.degree. C. or less, the sintering is insufficient, and at 1000.degree. C. or higher, the dielectric constant is lowered, and desired characteristics may not be obtained.
Example 4
Similar to Example 3, to the calcined, crushed and dried dielectric powder, PbO and NiO or WO.sub.3 were added as subsidiary components, mixed in a wet process by a ball mill, the mixture was dried, a vehicle having a resin mainly made of ethyl cellulose dissolved in solvent was added, and the compound was kneaded in three-stage rolls, and a dielectric paste was prepared. On the other hand, in order to form a thick film capacity of 2 .times. 2 mm.sup.2 on an alumina substrate of 96% purity, a copper electrode was printed and dried as the lower electrode, the obtained dielectric paste was printed and dried in a thickness of 50 to 60 .mu.m as the dielectric layer in two steps, and a copper electrode similar to the lower electrode was printed and dried as the upper electrode, thereby forming a three-layer printed thick film consisting of an electrode, dielectric and electrode, this was sintered in a nitrogen atmosphere at a maximum temperature of 800.degree. to 1000.degree. C., for 5 to 30 minutes, in a belt furnace. The dielectric constant and tan .delta. of the thus obtained thick film capacitor were measured in an electric field of 1 kHz, 1 V/mm. The material composition of the invention and the dielectric characteristics of the specimens is sintered at 900.degree. C. in nitrogen are shown in Table 8.
TABLE 8__________________________________________________________________________Principal dielectriccomposition Pb(Ni.sub.1/3 Pb(Ni.sub.1/2 Subsidiary component Dielectric tan .delta. PbZrO.sub.3 Nb.sub.2/3)O.sub.3 W.sub.1/2)O.sub.3 PbO NiO WO.sub.3 constant (20.degree. C.)No. (mol %) (mol %) (mol %) (mol %) (mol %) (mol %) (20.degree. C.) [%]__________________________________________________________________________ 1* 55.0 30.0 15.0 0 0 0 1200 12.3 2* 55.0 30.0 15.0 0.5 0.5 0 2620 10.7 3 55.0 30.0 15.0 1.0 1.0 0 3940 7.9 4 55.0 30.0 15.0 10.0 5.0 0 6840 5.8 5 55.0 30.0 15.0 25.0 15.0 0 4480 5.8 6* 55.0 30.0 15.0 30.0 25.0 0 3780 6.0 7 35.0 60.0 5.0 10.0 5.0 0 6800 4.2 8 55.0 40.0 5.0 10.0 5.0 0 4850 5.7 9 65.0 20.0 15.0 10.0 5.0 0 4770 5.010 52.5 20.0 27.5 10.0 5.0 0 4900 2.4 11* 55.0 30.0 15.0 0.5 0 0.5 1630 8.412 55.0 30.0 15.0 1.0 0 1.0 4020 5.913 55.0 30.0 15.0 10.0 0 5.0 6000 4.814 55.0 30.0 15.0 25.0 0 15.0 4750 4.9 15* 55.0 30.0 15.0 30.0 0 25.0 3230 4.516 35.0 60.0 5.0 10.0 0 5.0 5940 3.517 55.0 40.0 5.0 10.0 0 5.0 5590 4.718 65.0 20.0 15.0 10.0 0 5.0 5020 5.719 52.5 20.0 27.5 10.0 0 5.0 4550 1.8__________________________________________________________________________ *The asterisked specimens are reference examples.
While specific embodiments of the invention have been illustrated and described herein, it is realized that modifications and changes will occur to those skilled in the art. It is therefore to be understood that the appended claims are intended to cover all modification and changes which fall within the true spirit and scope of the invention.
Claims
  • 1. A dielectric ceramic composition consisting essentially of a principal component represented by the formula
  • PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3
  • wherein X+y+z=1, and substantially components of PbO in an amount of 1.0 to 25.0 mol % and NiO or WO.sub.3 in an amount of 1.0 to 15.0 mol %, wherein said subsidiary components are added to a calcined powder of said principal component, and wherein the values of x, y and z fall within ranges represented by a polygon ABCDE of a ternary system composition diagram of PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, such that the vertices of the polygon corresponding to compositions A, B, C, D, E are represented by the following numerical values: ##EQU5##
  • 2. A dielectric ceramic composition of claim 11, wherein PbO is added in an amount of 1.0 to 25.0 mol % and WO.sub.3 is added in an amount of 1.0 to 15.0 mol % to the calcined powder of said principal component.
  • 3. A ceramic capacitor composed of:
  • a dielectric ceramic composition consisting essentially of a principal component represented by the formula
  • PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3
  • wherein x+y+z=1, and subsidiary components of PbO in an amount of 1.0 to 25.0 mol % and NiO or WO.sub.3 in an amount of 1.0 to 15.0 mol %, wherein said subsidiary components are added to a calcined powder of said principal component, and wherein the values of x, y and z fall within ranges represented by a polygon ABCDE of a ternary system composition diagram of PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, such that the vertices of the polygon corresponding to compositions A, B, C, D, E are represented by the following numerical values ##EQU6## and electrodes that can be sintered at 800.degree. to 1000.degree. C. in the atmosphere.
  • 4. A ceramic capacitor composed of:
  • a dielectric ceramic composition consisting essentially of a principal component represented by the formula
  • PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3
  • wherein x+y+z=1, and subsidiary components of PbO in an amount of 1.0 to 25.0 mol % and NiO or WO.sub.3 in an amount of 1.0 to 15.0 mol %, wherein said subsidiary components are added to a calcined powder of said principal component, and wherein the values of x, y and z fall within ranges represented by a polygon ABCDE of a ternary system composition diagram of PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, such that the vertices of the polygon corresponding to compositions A, B, C, D, E are represented by the following numerical values ##EQU7## and electrodes that can be sintered at 800.degree. to 1000.degree. C. in a neutral atmosphere or a reducing atmosphere.
  • 5. A thick film capacitor composed by disposing a dielectric layer made of a dielectric ceramic composition and electrodes that can be sintered at 800.degree. to 1000.degree. C. on a ceramic substrate,
  • said dielectric ceramic composition consisting essentially of a principal component represented by the formula
  • PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3
  • wherein x+y+z=1, and subsidiary components of PbO in an amount of 1.0 to 25.0 mol % and NiO or WO.sub.3 in an amount of 1.0 to 15.0 mol %, wherein said subsidiary components are added to a calcined powder of said principal component, and wherein the values of x, y and z fall within ranges represented by a polygon ABCDE of a ternary system composition diagram of PbTi.sub.x (Mg.sub.1/3 Nb.sub.2/3).sub.y (Ni.sub.1/2 W.sub.1/2).sub.z O.sub.3, such that the vertices of the polygon corresponding to compositions A, B, C, D, E are represented by the following numerical values ##EQU8##
Priority Claims (2)
Number Date Country Kind
63-280812 Nov 1988 JPX
1-29088 Feb 1989 JPX
US Referenced Citations (1)
Number Name Date Kind
4711862 Yokotani et al. Dec 1987
Non-Patent Literature Citations (1)
Entry
Guha et al., Effect of Excess PbO on the Sintering Characteristics and Dielectric Properties of Pb(Mg.sub.1/3 Nb.sub.2/3)O.sub.3 PbTiO.sub.3 -Based Ceramics, J. Am. Ceramic Society, Mar. 1988.