Dielectric ceramic compositions

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to dielectric ceramic compositions, and particularly to dielectric ceramic compositions used as materials of a ceramic laminated capacitor and the like.
2. Description of the Prior Art
Conventionally, as dielectric ceramic compositions having a small voltage dependency, a high ceramic strength and a flat dielectric temperature characteristic, those composed of, for example, BaTiO.sub.3 as a main component, to which bismuth compounds such as Bi.sub.2 O.sub.3 -TiO.sub.2 -SnO.sub.2, Bi.sub.2 O.sub.3 -ZrO.sub.2 and rare earth elements are added as by-components, are widely known.
While, separate from the dielectric ceramic compositions having the above-mentioned composition, those composed of BaTiO.sub.3 as a main component, to which Nb.sub.2 O.sub.5, rare earth oxides and transition metal oxides of Cr, Mn, Fe, Co, Ni are added as by-components, have been proposed as the dielectric ceramic composition which has a flat dielectric temperature characteristic, irrespective of its high dielectric constant of 3000 or more.
Temperature characteristics of these dielectric ceramic compositions is that, X7R characteristics of the EIA standards is satisfied, or a capacitive change factor based on an electrostatic capacity at +25.degree. C. in a temperature range of -55.degree. C. to +125.degree. C. is within .+-.15%.
In recent years, ceramic laminated capacitors are used in ECC modules (electronic control devices of an engine) installed in an engine soon of an automobile. Since the device is designed for stable control of the engine, viewing from the temperature stability of circuitries, it is desirable to satisfy the R characteristics (capacitive change factor within .+-.15%) as the temperature characteristics of the capacitors being used.
While, in winter in cold districts, temperature goes down to around -20.degree. C. in the engine room of the automobile, and in summer, the temperature rises to around +130.degree. C. when the engine is started. Particularly, when the engine is over heated, the temperature easily goes up to around 150.degree. C. Thus, the conventional dielectric ceramic compositions which satisfy the X7R characteristics can not cope with the high engine room temperature any longer.
Since the laminated capacitors are for use in the automobile, when it breaks, while being mounted on the circuit board, the ECC modules can not function sufficiently, and in the worst case, there is the possibility of causing an accident, which must be avoided by all means. Furthermore, since vibration and stress are always exerted while the automobile is running, in order to avoid damages due to such vibration and stress, the ceramics must be sufficiently strong.
When the voltage dependency of the dielectric ceramic composition is large, the dielectric can not be processed into a thin film, thus the small-sized and large capacity ceramic laminated capacitor can not be manufactured, besides, it is also not preferable from a viewpoint of circuit stability.
Now, in some cases, the dielectric ceramic composition composed of BaTiO.sub.3 as a main component, to which Nb.sub.2 O.sub.5, rare earth compounds and transition metal oxides of Cr, Mn, Fe, Co and Ni are added as by-components, was problematic in that, it is apt to break at the time of mounting to the circuit board because the ceramic strength is weak.
Since the voltage dependency of the dielectric ceramic composition having a large dielectric constant is large, it can not meet with the recent thin-film technique, thus the small-sized and large capacity ceramic laminated capacitor could not be manufactured.
Meanwhile, as stated above, though the dielectric ceramic compositions composed of BaTiO.sub.3 as the main component, to which bismuth compounds are added as the by-components, have a small voltage dependency and a high ceramic strength, when the dielectric constant is raised, a temperature change factor of the dielectric constant becomes larger. Also, in the case of ceramic laminated capacitor, when a baking temperature is raised to 1160.degree. C. of higher , an internal electrode must contain Pb by 30 wt. % or more. Hence, Pb and Bi.sub.2 O.sub.3 in the internal electrode apt to react one another, furthermore, a cost of the internal electrode increases.
SUMMARY OF THE INVENTION
It is, therefore, a primary object of the present invention to provide dielectric ceramic compositions, which can be baked at temperature of 1160.degree. C. or less and satisfies X8R characteristics irrespective of its high dielectric constant of 1000 or more, that is, when based on an electrostatic capacity at +25.degree. C., the temperature change factor (hereinafter, referred to as "TC") of the electrostatic capacity is flat within JL 15% in a wide temperature range of -55.degree. C. to +150.degree. C., and a mechanical strength of the ceramics is high, furthermore, when the thickness of a dielectric ceramic layer is processed into a thin film of 10 .mu.m to 15 .mu.m, and a d.c. voltage of 25V (50% of the rated voltage of 50V) is applied in accordance with the RB characteristics standard of JIS C6429, the temperature change factor of the electrostatic capacity (hereinafter, referred to as "bias TC") is within +15% to 40%.
A first invention is directed to the dielectric ceramic composition composed of, 97.5 to 99.5 wt. % of main component represented by a general formula {100-(a+b+c+d)}(Ba.sub.100-x Pbx)TiO.sub.3 +aZnO+bBi.sub.2 O.sub.3 +cNb.sub.2 O.sub.5 +dRe.sub.2 O.sub.3 (where, Re is at least one kind selected from La, Pr, Nd, Sm, Dy and Er, a, b, c, d and x designate mol %, 0.5.ltoreq.a.ltoreq.4.5, 0.5.ltoreq.b.ltoreq.4.5, 0.5.ltoreq.c.ltoreq.4.5, 0.5.ltoreq.d.ltoreq.5.5 and 0<x.ltoreq.6.0) , and 0.05 to 2.5 wt. % of first by-component consisting of glass whose main component is SiO.sub.2.
A second invention is directed to the dielectric ceramic composition composed of, 97.0 to 99.94 wt. % of main component represented by a general formula (100-(a+b+c +d)} (Ba.sub.100-x Pb.sub.x)TiO.sub.3 +aZnO+bBi.sub.2 O.sub.3 +cNb.sub.2 O.sub.5 +dRe.sub.2 O.sub.3 (where, Re is at least one kind selected from La, Pr, Nd, Sm, Dy and Er, a, b, c, d and x designate mol. %, 0.5.ltoreq.a<4.5, 0.5.ltoreq.b.ltoreq.4.5, 0.5.ltoreq.c.ltoreq.4.5, 0.5.ltoreq.d.ltoreq.5.5 and 0<x.ltoreq.6.0 ), 0.05 to 2.5 wt. % of first by-component consisting of glass whose main component is SiO.sub.2, and 0.01 to 0.5 wt. % of second by-component consisting of at least one kind selected from oxides of Cr, Mn, Fe, Co and Ni.
A third invention is directed to the dielectric ceramic composition composed of, 97.5 to 99.95 wt. % of main component represented by a general formula (100-(a+b+c+d+e)}BaTiO.sub.3 +aZnO+bBi.sub.2 O.sub.3 +cMeO.sub.2 +dNb.sub.2 O.sub.5 +eRe.sub.2 O.sub.3 (where, Me is at least one kind selected from Ti, Zr and Sn, Re is at least one kind selected from La, Pr, Nd, Sm, Dy and Er, a, b, c, d and e designate mol. %, 0.5.ltoreq.a.ltoreq.4.5, 2.0.ltoreq.b.ltoreq.6.0, 0.5.ltoreq.c.ltoreq.6.5, 0.5.ltoreq.d.ltoreq.4.5 and 0.5.ltoreq.e.ltoreq.5.5), and 0.05 to 2.5 wt. % of first by-component consisting of glass whose main component is SiO.sub.2.
A fourth invention is directed to the dielectric ceramic composition composed of, 97.0 to 99.94 wt. % of main component represented by a general formula {100-(a+b+c d+e)} BaTiO.sub.3 +aZnO+bBi.sub.2 O.sub.3 +cMeO.sub.2 +dNb.sub.2 O.sub.5 +eRe.sub.2 O.sub.3 (where, Me is at least one kind selected from Ti, Zr and Sn, Re is at least one kind selected from La, Pr, Nd, Sm, Dy and Er, a, b, c, d and e designate mol. %, 0.5.ltoreq.a.ltoreq.4.5, 2.0.ltoreq.b .ltoreq.6.0, 0.5.ltoreq.c.ltoreq.6.5, 0.5.ltoreq.d.ltoreq.4.5and0.5.ltoreq.e.ltoreq.5.5),0.05 to 2.5 wt. % of first by-component consisting of glass whose main component is SiO2, and 0.01 to 0.5 wt. % of second by-component consisting of at least one kind from oxides of Cr, Mn, Fe, Co and Ni.
A fifth invention is directed to a dielectric ceramic composition composed of, 97.5 to 99.95 wt. % of main component represented by a general formula (100-(a+b+c+d+e+ f) BaTiO.sub.3 +aZnO+bBi.sub.2 O.sub.3 +cNb.sub.2 O.sub.5 +dMaO+eMbO.sub.2 +fRe.sub.2 O.sub.3 (where, Ma is at least one kind selected from Pb and Ca, Mb is at least one kind selected from Ti, Zr and Sn, Re is at least one kind selected from La, Pr, Nd, Sm, Dy and Er, a, b, c, d, e and f designate mol. %, 0.5.ltoreq.a.ltoreq.4.5, 2.0.ltoreq.b.ltoreq.6.0, 0.5.ltoreq.c.ltoreq.4.5, 0<d.ltoreq.4.0, 6.5.ltoreq.e.ltoreq.10.0 and 0.5.ltoreq.f .ltoreq.5.5), and 0.05 to 2.5 wt. % of first by-component consisting of glass whose main component is SiO.sub.2.
A sixth invention is directed to a dielectric ceramic composition composed of, 97.0 to 99.94 wt. % of main component represented by a general formula (100-(a+b+c+d+e+f) BaTiO.sub.3 +aZnO+bBi.sub.2 O.sub.3 +cNb.sub.2 O.sub.5 +dMaO+eMbO.sub.2 +fRe.sub.2 O.sub.3 (where, Ma is at least one kind selected from Pb and Ca, Mb is at least one kind selected from Ti, Zr and Sn, Re is at least one kind selected from La, Pr, Nd, Sm, Dy and Er, a, b, c, d, e and f designate mol. %, 0.5.ltoreq.a.ltoreq.4.5, 2.0.ltoreq.b.ltoreq.6.0, 0.5.ltoreq.c.ltoreq.4.5, 0<d.ltoreq.4.0, 6.5.ltoreq.e.ltoreq.10.0 and 0.5.ltoreq.f .ltoreq.5.5), and 0.05 to 2.5 wt. % of first by-component consisting of glass whose main component is SiO.sub.2, and 0.01 to 0.5 wt. % of second by-component consisting of at least one kind selected from oxides of Cr, Mn, Fe, Co and Ni.
Hereupon, as the glass which is the by-component consisting of SiO.sub.2 as the main component, there is, for example, BaO--SrO--CaO--Li.sub.2 O--SiO.sub.2. This glass is a sintering assistant which brings the baking temperature to 1160.degree. C. or lower, but it is not limited thereto, oxide glass containing boron such as BaO--Li.sub.2 O--B.sub.2 O.sub.3 --SiO.sub.3 may also be used. The non-oxide glass such as SiO.sub.2 --B.sub.4 C may also be used. The SiO.sub.2 --B.sub.4 C glass is particularly useful when a molding binder of ceramic materials is a water binder.
The dielectric ceramic compositions according to the present invention can be baked at 1160.degree. C. or lower, and in a wide temperature range of -55.degree. C. to +150.degree. C., its TC satisfies the R characteristic and its temperature characteristic is flat. Thus, a ceramic laminated capacitor using these dielectric ceramic compositions can be used in all kinds of electrical equipments which are installed in locations, where the temperature change is large under various conditions.
Since the mechanical strength of the ceramics is high, when used as the ceramic laminated capacitor, destructions such as cracks and, flaws at mounting to the circuit board are eliminated. And hence, accidents caused by improper short-circuit and exoergical damages can be prevented.
Furthermore, since the bias TC is small, the dielectric ceramic layer can be processed into a thin film of 10 .mu.m to 15 .mu.m thick, thus the small-sized and large capacity ceramic laminated capacitor can be realized.
The above and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description made with reference to the drawings.

DESCRIPTION OF THE PREFERRED EMBODIMENTS
(Embodiment 1)
First, a method of preparing a main component of a dielectric ceramic composition is described. As starting materials, the industrial materials such as BaTiO.sub.3, PbO, TiO.sub.2, ZnO, Bi.sub.2 O.sub.3, Nb.sub.2 O.sub.5 and Re.sub.2 O.sub.3 (Re is one of La, Pr, Nd, Sm, Dy and Er) were prepared. The starting materials were weighed to have composition ratios as shown in Table 1, then evaporated and dried after mixing and grinding for 16 hours in a wet ball mill to obtain a powdered mixture. The resulting powdered mixture introduced into a zirconia box was calcined at 1000.degree. C. for 2 hour in a natural atmosphere, then roughly ground so as to pass through a sieve of 200 meshes to obtain the material powder for main component of the dielectric ceramic composition.
Next, a method of preparing a first by-component of the dielectric ceramic composition is described. In this embodiment, as the first by-component which brings the baking temperature to 1160.degree. C. or lower, oxide glass whose composition is represented by 8 BaO--6 SrO--6 CaO--30 Li.sub.2 O--50SiO.sub.2 (mol. %) was used. As starting materials, the industrial materials such as BaCO.sub.3, SrCO.sub.3, CaCO.sub.3, Li.sub.2 O and SiO.sub.2 were prepared. The starting materials were weighed to have the above-mentioned composition, then evaporated and dried after mixing and grinding for 16 hours in a wet ball mill to obtain a powdered mixture. The resulting powdered mixture was introduced into a crucible made of alumina and shelved for 1 hour at 1300.degree. C., then quenched for vitrification. The glassy product was ground so as to pass through a sieve of 200 meshes to obtain the material powder for first by-component of the dielectric ceramic composition.
The material powder of first by-component of the dielectric ceramic composition obtained in a manner mentioned above was added to the material powder for main component of the dielectric ceramic composition to obtain weight per-cents as shown in Table 1.
For second by-component, the industrial materials such as Cr.sub.2 O.sub.3, MnO.sub.2, Fe.sub.2 O.sub.3, Co.sub.2 O.sub.3 and NiO were prepared. The second by-component was added to the main component whose composition is 93.0 (Ba.sub.97 Pb.sub.3) TiO.sub.3 --1.5 ZnO--1.5 Bi .sub.2 O.sub.3 2.0 Nb.sub.2 O.sub.5 --2.0 Nd.sub.2 O.sub.3 (mol. %), to which 1.0 wt. % of the above-mentioned first by-component is added, to obtain composition ratios as shown in Table 2.
To these additives, a polyvinyl butyral binder and an organic solvent such as toluene, ethyl alcohol and the like were added, and mixed in a wet ball mill for 16 hours, then molded into a sheet by a doctor blade method to obtain a green sheet. A thickness of the green sheet was 19 m. After printing an internal electrode pattern on the green sheet with a paste of Ag/Pd=70/30 (wt. %), 6 layers of green sheets are laminated and pressed together with dummy sheets to obtain a laminate. Molded pieces of 5.5 mm length .times.4.5 mm width .times.1 mm thickness were cut out from the laminate. Thereafter, the molded pieces were baked at baking temperatures shown in Table 3 and Table 4 for 2 hours to obtain a sinter. A thickness of the sintered dielectric was 13 .mu.m.
Then, a silver electrode was baked onto an end face of the resulting sinter to obtain a subject (a laminated capacitor), whose dielectric constant (.epsilon.), dielectric loss (tan .delta.), TC and bias TC were measured.
In this case, the dielectric constant (.epsilon.) and dielectric loss (tan .delta.) were measured at the condition of 25.degree. C., 1 KHz and 1 Vrms. As the TC, a maximum value of temperature change factor, or a maximum change factor (.DELTA.C max), between -55.degree. C. and +150.degree. C. was obtained, based on an electrostatic capacity at 25.degree. C. For the bias TC, as same as the TC, a maximum change factor (.DELTA.C.sub.maxB) was obtained, based on an electrostatic capacity at 25.degree. C. and applied voltage of 0.degree. C., by measuring the electrostatic capacity as superposing the d.c. voltage 25V on the subject within the above-mentioned temperature range.
A deflective strength of the ceramic was measured by a 3-point bending method. The material sheets having the composition shown in Table 1 and Table 2 were pressed and molded to obtain a laminate, and mold pieces of 35 mm length .times.7 mm width .times.1.2 mm thickness were cut out from the laminate. Thereafter, the mold pieces were baked at the baking temperatures shown in Table 3 and Table 4 for 2 hours to obtain rectangular-shape ceramics. In such a manner, the deflective strength was measured on 20 samples for respective compositions to obtain the mean deflective strength of the ceramics of respective compositions.
Experiment results of the compositions in Table 1 as shown in Tale 3, and those of the compositions in Table 2 are shown in Table 4.
The reason for restricting ranges of the main component quantity, first by-component quantity and second by-component quantity in the present invention, is described.
First, the reason for restricting the main component composition is described.
The reason why a value of a or ZnO is 0.5 to 4.5 mol. % is that, as Sample No. 9, if it is below 0.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max), and also the defective strength becomes 1500 kg/cm.sup.2 or less. Also, as Sample No. 10, if it exceeds 4.5 mol. %, the TC exceeds - 15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%.
The reason why a value of b or Bi.sub.2 O.sub.3 is 0.5 to 4.5 mol. % is that, as Sample No. 11, if it is below 0.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the deflective strength becomes 1500 Kg/cm.sup.2 or less. Also, as Sample No. 12, if it exceeds 4.5 mol. %, a dielectric constant (.epsilon.) becomes less than 1000.
The reason why a value of c or Nb.sub.2 0.sub.5 is 0.5 to 4.5 mol. % is that, as Sample No. 13, if it is below 0.5 mol. %, or as Sample No. 14, if it exceeds 4.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%.
The reason why a value d or Re.sub.2 O.sub.3 is 0.5 to 5.5 mol. % is that, as Sample No. 15, if it is below 0.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%. Also, as Sample No. 16, if it exceeds 5.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max).
As to a value of x or PbTiO.sub.3, as Sample No. 17, if it exceeds 6.0 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%.
Next, the reason for restricting the first by-component quantity is described.
The reason why the first by-component quantity is 0.05 to 2.5 wt. % is that, as Sample No. 18, if it is below 0.05 wt. %, the baking temperature exceeds 1160.degree. C. Also, as Sample No. 21, if it exceeds 2.5 wt. %, the dielectric constant (.epsilon.) becomes less than 1000.
Next, the reason for restricting the second by-component quantity is described.
The second by-component is for preventing reduction of the dielectric ceramic, and the reason why its quantity is restricted to 0.01 to 0.5 wt. % is that, if it is below 0.01 wt. %, the reduction preventing effect is spoiled, and as Sample No. 31, if it exceeds 0.5 wt. %, a dielectric loss (tan .delta.) exceeds 2.5%.
(Embodiment 2)
First, a method of preparing a main component of a dielectric ceramic composition is described. As starting materials, the industrial materials such as BaTiO.sub.3, ZnO, Bi.sub.2 O.sub.3, MeO.sub.2 (Me is one of Ti, Zr and Sn), Nb.sub.2 O.sub.5, Re.sub.2 O.sub.3 (Re is one of La, Pr, Nd, Sm, Dy and Er) were prepared. The starting materials were weighed to have composition ratios as shown in Table 5, then evaporated and dried after mixing and grinding for 16 hours in a wet ball mill to obtain a powdered mixture. The resulting powdered mixture introduced into a zirconia box was calcined at 1000.degree. C. for 2 hours in a natural atmosphere, then roughly ground so as to pass through a sieve of 200 meshes to obtain the material powder for main component of the dielectric ceramic composition.
Next, a method of preparing a first by-component of the dielectric ceramic composition is described. In this embodiment, as the first by-component which brings the baking temperature to 1160.degree. C. or lower, oxide glass whose composition is represented by 8 BaO--6 SrO--6 CaO--30 Li.sub.2 O--50 SiO.sub.2 (mol. %) was used. As starting materials, the industrial materials such as BaCO.sub.3, SrCO.sub.3, CaCO.sub.3, Li.sub.2 O and SiO.sub.2 were prepared. The starting materials were weighed to have the above-mentioned composition, then evaporated and dried after mixing and grinding for 16 hours in a wet ball mill to obtain a powdered mixture. The resulting powdered mixture was introduced into a crucible made of alumina and shelved for 1 hour at 1300.degree. C., then quenched for vitrification. The glassy product was ground so as to pass through a sieve of 200 meshes to obtain the material powder for first by-component of the ceramic composition.
The material powder for first by-component of the dielectric ceramic composition obtained in a manner mentioned above was added to the material powder for main component of the dielectric ceramic composition to obtain weight per-cents as shown in Table 5.
For second by-component, the industrial materials such as Cr.sub.2 O.sub.3, MnO.sub.2, Fe.sub.2 O.sub.3, Co.sub.2 O.sub.3 and NiO were prepared. The second by-component was added to the main component, whose composition is 90.5 BaTiO.sub.3 --1.5 ZnO--3.0 Bi.sub.2 O.sub.3 --1.0 TiO.sub.2 --0.5 ZrO.sub.2 --1.5 Nb.sub.2 O.sub.5 --1.5 Nd.sub.2 O.sub.3 --0.5 Dy.sub.2 O.sub.3 (mol. %) to which 1.0 wt. % of the above-mentioned first by-component is added, to obtain composition ratios as shown in Table 6.
To these additives, a polyvinyl butyral binder and an organic solvent such as toluene, ethyl alcohol and the like were added and mixed in a wet ball mill for 16 hours, then molded into a sheet by a doctor blade method to obtain a green sheet. A thickness of the green sheet was 19 .mu.m. After printing an internal electrode pattern on the green sheet with a paste of Ag/Pd=70/30 (wt. %), 6 layers of green sheets were laminated and pressed together with dummy sheets to obtain a laminate. Mold pieces of 5.5 mm length .times.4.5 mm width .times.1 mm thickness were cut out from the laminate. Thereafter, the molds pieces were baked at baking temperatures shown in Table 7 and Table 8 for 2 hours to obtain a sinter. A thickness of the sintered dielectric was 13 .mu.m.
Then, a silver electrode was baked onto an end face of the resulting sinter to obtain a subject (a laminated capacitor), whose dielectric constant (.epsilon.), dielectric loss (tan .delta.), TC and bias TC were measured.
In this case, the dielectric constant (.epsilon.) and dielectric loss (tan .delta.) were measured at the condition of 25.degree. C., 1 KHz and 1 Vrms. As the TC, a maximum value of temperature change factor, or a maximum change factor (.DELTA.C.sub.max), between -55.degree. C. and +150.degree. C. was obtained, based on an electrostatic capacity at 25.degree. C. For the bias TC, as same as the TC, a maximum change factor (.DELTA.C.sub.maxB) was obtained, based on an electrostatic capacity at 25.degree. C. and applied voltage of 0V, by measuring the electrostatic capacity as superposing the d.c. voltage of 25V on the subject within the above-mentioned temperature range.
A deflective strength of the ceramic was measured by a 3-point bending method. First, the material sheets having the compositions shown in Table 5 and Table 6 were pressed and molded to obtain a laminate, and mold pieces of 35 mm length .times.7 mm width .times.1.2 mm thickness were cut out from the laminate. Thereafter, the mold pieces were baked at the baking temperature shown in Table 7 and Table 8 for 2 hours to obtain rectangular-shape ceramics. In such a manner, the deflective strength was measured on 20 samples for respective compositions to obtain the mean deflection strength of the ceramics of respective compositions.
Experiment results of the compositions in Table 5 are shown in Table 7, and those of the compositions in Table 6 are shown in Table 8.
The reason for restricting ranges of the main component quantity, first by-component quantity and second by-component quantity in the present invention, is described.
First, the reason for restricting the main component composition is described.
The reason why a value of a or ZnO is 0.5 to 4.5 mol. % is that, as Sample No. 109, if it is below 0.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the deflective strength becomes 1500 kg/cm.sup.2 or less. Also, as Sample No. 110, if it exceeds 4.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%.
The reason why a value of b or Bi.sub.2 O.sub.3 is 2.0 to 6.0 mol. % is that, as Sample No. 111, if it is below 2.0 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max), and also the deflective strength becomes 1500 kg/cm.sup.2 or less. also, as Sample No. 112, if it exceeds 6.0 mol. %, the dielectric constant (.epsilon.) becomes less than 1000.
The reason why a value of c or MeO.sub.2 is 0.5 to 6.5 mol. % is that, as Sample No. 113, if it is below 0.5 mol. % or as Sample No. 114, if it exceeds 6.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max).
The reason why a value of d or Nb.sub.2 O.sub.5 is 0.5 to 4.5 mol. % is that, as Sample NO. 115, if it is below 0.5 mol. % or also as Sample No. 116, if it exceeds 4.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%.
The reason why a value of e or Re.sub.2 O.sub.3 is 0.5 to 5.5 mol. % is that, as Sample No. 117, if it is below 0.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max), and also the bias TC exceeds -40%. Also, as Sample No. 118, if it exceeds 5.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max).
Next, the reason for restricting the first by-component quantity is described.
The reason why the first by-component quantity is restricted to 0.05 to 2.5 wt. % is that, as Sample No. 119 shown in Table 5, if it is below 0.05 wt. %, the baking temperature exceeds 1160.degree. C. While, as Sample No. 122, if it exceeds 2.5 wt. %, the dielectric constant (.epsilon.) becomes less than 1000.
Next, the reason for restricting the second by-component quantity is described.
The second by-component is for preventing reduction of the dielectric ceramics, and the reason why its range is restricted to 0.01 to 0.5 wt. % is that, if it is below 0.01 wt. %, the reduction preventing effect is spoiled, and as Sample No. 132 shown in Table 6, if it exceeds 0.5 wt. %, the dielectric loss (tan .delta.) exceeds 2.5%.
(Embodiment 3 )
First, a method of preparing a main component of a dielectric ceramic composition is described. As starting materials, the industrial materials such as BaTiO.sub.3, ZnO, Bi.sub.2 O.sub.3, Nb.sub.2 O.sub.5, MaO (Ma is one of Pb and Ca), MeO.sub.2 (Me is one of Ti, Zr and Sn), Re.sub.2 O.sub.3 (Re is one of La, Pr, Nd, Sm, Dy and Er) were prepared. The starting materials were weighed to have composition ratios as shown in Table 9, then evaporated and dried after mixing and grinding for 16 hours in a wet ball mill to obtain a powdered mixture. The resulting powdered mixture introduced into a zirconia box was calcined at 1000.degree. C. for 2 hours in a natural atmosphere, then roughly ground so as to pass through a sieve of 200 meshes to obtain the material powder for main component of the dielectric ceramic composition.
Next, a method of preparing a first by-component of the dielectric ceramic composition is described. In this embodiment, as the first by-component which brings the baking temperature to 1160.degree. C. or lower, oxide glass whose main component is represented by 8 BaO--6 SrO--6 CaO--30 Li.sub.2 O -50SiO.sub.2 (mol. %) was used. As starting materials, the industrial materials such as BaCO.sub.3, SrCO.sub.3, CaCO.sub.3, Li.sub.2 O and SiO.sub.2 were prepared. These starting materials were weighed to have the above-mentioned composition, then evaporated and dried after mixing and grinding in a wet ball mill for 16 hours to obtain a powdered mixture. The resulting powdered mixture was introduced into a crucible made of alumina and shelved for 1 hour at 1300.degree. C., then quenched for vitrification. The glassy product was ground so as to pass through a sieve of 200 meshes to obtain the material powder for first by-component of the ceramic composition.
The material powder for first by-component of the dielectric ceramic competition obtained in a manner mentioned above was added to the material powder for main component of the dielectric ceramic compositions to obtain weight per-cents as shown in Table 9.
For second by-component, the industrial materials such Cr.sub.2 O.sub.3, MnO.sub.2, Fe.sub.2 O.sub.3, Co.sub.2 O.sub.3 and NiO were prepared. The second by-component was added to the main component-whose composition is 88.5 BatiO.sub.3 --1.5 ZnO--3.0 Bi.sub.2 O.sub.3 --1.0 Nb.sub.2 O.sub.5 --2.0 PbO--1.0 TiO.sub.2 --0.5 SnO.sub.2--0.5 ZrO.sub.2 --2.0 Nd.sub.2 O.sub.3 (mol. %), to which 1.0 wt. % of the above-mentioned first by-component is added, to obtain the composition ratios as shown in Table 10.
To these additives, a polyvinyl bytyral binder and an organic solvent such as toluene, ethyl alcohol and the like were added and mixed in a wet ball mill for 16 hours, then molded into a sheet by a doctor blade method to obtain a green sheet. A thickness of the green sheet was 19 .mu.m. After printing an internal electrode pattern on the green sheet with a paste of Ag/Pd=70/30 (wt. %), 6 layers of green sheets were laminated and pressed together with dummy sheets to obtain a laminate, and mold pieces of 5.5 mm length .times.4.5 mm width .times.1 mm thickness were cut out from the laminate. Thereafter, the mold pieces were baked at the baking temperatures shown in Table 11 and Table 12 for 2 hours to obtain a sinter. A thickness of the sintered dielectric was 13 .mu.m.
Then, a silver electrode was baked onto an end face of the resulting sinter to obtain a subject (a laminated capacitor), whose dielectric constant (.epsilon.), dielectric loss (tan .delta.), TC and bias TC were measured.
In this case, the dielectric constant (.epsilon.) and dielectric loss (tan .delta.) were measured at the condition of 25.degree. C., 1 KHz and 1Vrms. As the TC, a maximum value of temperature change factor, or a maximum change factor (.DELTA.C.sub.max), between -55.degree. C. and +150.degree. C. was obtained, based on an electrostatic capacity at 25.degree. C. For the bias TC, as same as the TC, a maximum change factor (.DELTA.C.sub.maxB) was obtained, based on an electrostatic capacity at 25.degree. C. and applied voltage of 0V, by measuring the electrostatic capacity as superposing the d.c. voltage of 25V on the subject within the above-mentioned temperature range.
A deflective strength of the ceramic was measured by a 3-point bending method. First, the material sheets having the compositions shown in Table 9 and Table 10 were pressed and molded to obtain a laminate, from which mold pieces of 35 mm length .times.7 mm width .times.1.2 mm thickness were cut out. Thereafter, the mold pieces were baked at the baking temperatures shown in Table 11 and Table 12 for 2 hours to obtain rectangular-shape ceramics. In such a manner, the deflective strength was measured on 20 samples for respective compositions to obtain the mean deflective strength of the ceramics of the respective compositions.
Experiment results of the compositions in Table 9 are shown in Table 11, land those of the compositions in Table 10 are shown in Table 12.
The reason for restricting ranges of the main component quantity, first by-component quantity and second by-component quantity in the present invention is described.
First, the reason for restricting the main component composition is described.
The reason why a value of a or ZnO is 0.5 to 4.5 mol. % is that, as Sample No. 209, if it is below 0.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max), and also the deflective strength becomes 1500 kg/cm.sup.2 or less. Also, as Sample No. 210, if it exceeds 4.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%.
The reason why a value of b or Bi.sub.2 O.sub.3 is 2.0 to 6.0 mol. % is that, as Sample No. 211, if it is below 2.0 wt. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max), and also the deflective strength becomes 1500kg/cm.sup.2 or less. Also, as Sample No. 212, if it exceeds 6.0 mol. %, the dielectric constant (.epsilon.) becomes less than 1000.
The reason why a value of C or Nb.sub.2 O.sub.3 is 0.5 to 4.5 mol. % is that, as Sample No. 213, if it is below 0.5 mol. % or as Sample No. 214, if it exceeds 4.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%.
The reason why a value of d or MaO is 4.0 mol. % or less is that, as Sample No. 215, if it exceeds 4.0 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max).
The reason why a value of e or MbO.sub.2 is 6.5 to 10.0 mol. % is that, as Sample No. 216, if it is below 6.5 mol. % or as Sample No. 217, if it exceeds 10.0 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max).
The reason why a value of f or Re.sub.2 O.sub.3 is 0.5 to 5.5 mol. % is that, as Sample No. 218, if it is below 0.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max) and also the bias TC exceeds -40%. Also, as Sample No. 219, if it exceeds 5.5 mol. %, the TC exceeds -15% at the maximum change factor (.DELTA.C.sub.max).
Next, the reason for restricting the first by-component quantity is described.
The reason why the first by-component quantity is 0.05 to 2.5 wt. % is that, as Sample No. 220 shown in Table 9, if it is below 0.05 wt. %, the baking temperature exceeds 1160.degree. C. While, as Sample No. 222, if it is exceeds 2.5 wt. %, the dielectric constant (.epsilon.) becomes less than 1000.
Next, the reason for restricting the second by-component quantity is described.
The second by-component is for preventing reduction of the dielectric ceramics, and the reason why the second by-component quantity is restricted to 0.01 to 0.5 wt. % is that, if it is below 0.01 wt. %, the reduction preventing effect is spoiled, and as Sample No. 232 shown in Table 10, if it exceeds 0.5 wt. %, the dielectric loss (tan .delta.) exceeds 2.5%.
In the above-mentioned embodiments, the by-components, which are prepared into a predetermined composition ratio beforehand, and ground for vitrification after heating and melting at high temperature, were added to and blended with the main components of the ceramic compositions.
However, as a method of adding the first by-component, alternatively, the starting materials, which are modified by preparing into a predetermined ratio beforehand and heating to temperature just before the melting point may be added, or composition elements of the first by-component may be individually added to the main component at any state such as metal alkoxide so as to melt and react during baking for vitrification.
In the above-mentioned embodiments, also in the case of second by-component, though it is added in the form of oxides from the beginning, as the starting materials at the time of preparing the materials, carbonates of the elements which turn into oxides during calcining and baking may also be used.
While the present invention has been particularly described, it is to be understood that such description is used merely as an example rather than limitation, and the spirit and scope of the present invention is determined solely by the terms of the appended claims.
TABLE 1__________________________________________________________________________main component compositon (mol %){100 - (a + b + c + d)} (Ba.sub.100-x Pb.sub.x)TiO.sub.3 + aZnO +bBi.sub.2 O.sub.3 + cNb.sub.2 O.sub.5 + dRe.sub.2 O.sub.3 main first by-Sample d component componentNo. 100 - (a + b + c + d) a b c La.sub.2 O.sub.3 Pr.sub.2 O.sub.3 Nd.sub.2 O.sub.3 Sm.sub.2 O.sub.3 Dy.sub.2 O.sub.3 Er.sub.2 O.sub.3 x (wt %) (wt__________________________________________________________________________ %) 1 93 1.5 2.5 2 0 0 1 0 0 0 1 99 1 2 89 2 4 3 0.5 1 0 0 0.5 0 1.5 98 2 3 87.5 1 4.5 4 0 0 2.5 0 0.5 0 1 99.5 0.5 4 91 4 2 1 0.5 0 0 0.5 0 1 5 99 1 5 93 1.5 3 1.5 0 0.5 0 0 0 0.5 4 98.5 1.5 6 86.5 2.5 3 3 2.5 0 2.5 0 0 0 2 99.5 0.5 7 88.5 4.5 2.5 2 0 1 0 0 1.5 0 3 98 2 8 86.5 1.5 3 4.5 0 0 2.5 1.5 0 0.5 1.5 98 2 *9 93.7 0.3 2.5 2 0.5 0 0.5 0 0.5 0 2 99 1*10 86.8 4.7 4 3 0 0 1.5 0 0 0 1.5 99.5 0.5*11 93.2 1.5 0.3 2.5 0 0 0 2 0 0.5 0.5 98 2*12 85.8 2 4.7 4.5 0 0 3 0 0 0 1.0 99.5 0.5*13 92.7 1 4 0.3 0 2 0 0 0 0 1.0 99 1*14 88.8 1.5 2.5 4.7 0 0 0 2.5 0 0 1.5 99 1*15 93.7 1.5 2.5 2 0.3 0 0 0 0 0 2 99 1*16 87.8 1.5 3 2 0 0.7 2.5 2.5 0 0 2.5 99.5 0.5*17 87.5 1 4.5 4 0 0 2.5 0 0.5 0 6.2 99.5 0.5*18 93 1.5 2.5 2 0 0 1 0 0 0 1.0 100 0 19 91.5 4 2 1 0 0 1.5 0 0 0 1.0 99.95 0.05 20 92 1.5 2.5 2 0 0 2 0 0 0 2.5 97.5 2.5*21 91 4 2 1 0 0 2 0 0 0 0.5 97.3 2.7__________________________________________________________________________ *indicates out of the scope of the invention
TABLE 2______________________________________ main first by-Sample component component second by-component (wt %)No. (wt %) (wt %) Cr Mn Fe Co Ni______________________________________22 98.99 1.0 0 0.01 0 0 023 98.85 1.0 0.05 0.05 0.05 0 024 98.95 1.0 0 0 0 0.05 025 98.9 1.0 0.05 0 0 0 0.0526 98.85 1.0 0 0.1 0 0 0.0527 98.65 1.0 0.05 0.2 0.05 0.05 028 98.6 1.0 0 0.3 0 0 0.129 98.55 1.0 0 0.3 0 0.1 0.0530 98.5 1.0 0.1 0.3 0 0.1 0*31 98.45 1.0 0 0.35 0.05 0.1 0.05______________________________________ *indicates out of the scope of the invention
TABLE 3__________________________________________________________________________baking electronic property mechanical propertySample temperature TC (%) bias TC (%) deflective strengthNo. (.degree.C.) .epsilon. tan .delta. (%) .DELTA.C.sub.max .DELTA.C.sub.maxB (kg/cm.sup.2)__________________________________________________________________________ 1 1140 2020 1.6 -12.8 -33.0 2070 2 1100 1810 1.5 -13.9 -30.0 2400 3 1100 1690 1.6 -14.0 -30.3 2180 4 1160 2020 1.7 10.0 -34.0 1910 5 1120 1770 1.7 11.0 -31.0 2210 6 1080 1360 1.8 -14.0 -28.5 2310 7 1100 1690 1.5 10.2 -33.2 2100 8 1140 1630 1.6 11.8 -31.5 2130 *9 1160 1680 2.2 -17.5 -33.5 1450*10 1080 2130 1.5 -22.0 -41.5 2060*11 1080 1620 1.7 -23.0 -36.0 1480*12 1080 980 1.8 -14.5 -26.5 2310*13 1080 1790 1.9 -22.5 -41.0 2270*14 1100 1420 1.9 -16.0 -40.8 2010*15 1140 1450 1.7 -21.0 -41.1 1970*16 1120 1500 1.1 -18.2 -35.1 1820*17 1080 1910 2.3 18.0 -42.0 2220*18 1160.degree. C. (not sintered) 19 1160 1680 2.0 13.0 -36.0 1870 20 1080 1290 1.9 14.0 -33.5 2130*21 1080 930 2.1 14.1 -34.5 2100__________________________________________________________________________ *indicates out of the scope of the invention
TABLE 4__________________________________________________________________________baking electronic property mechanical propertySample temperature TC (%) bias TC (%) deflective strengthNo. (.degree.C.) .epsilon. tan .delta. (%) .DELTA.C.sub.max .DELTA.C.sub.maxB (kg/cm.sup.2)__________________________________________________________________________22 1100 2000 1.7 -11.8 -31.0 206023 1100 1910 1.7 -12.0 -31.5 201024 1100 1970 1.8 -11.8 -31.0 197025 1100 1940 1.8 -11.5 -30.8 207026 1100 1970 1.5 -11.5 -31.0 206027 1100 1850 2.1 -12.0 -31.7 197028 1100 1900 2.1 -11.5 -31.1 195029 1100 1960 2.2 -11.8 -32.0 196030 1100 1920 2.3 -11.6 -31.3 1970*31 1100 1920 2.8 -11.4 -31.1 2010__________________________________________________________________________ *indicates out of the scope of the invention
TABLE 5__________________________________________________________________________main component composition (mol %){100 - (a + b + c + d + e)} BaTiO.sub.3 + aZnO + bBi.sub.2 O.sub.3 +cMeO.sub.2 + dNb.sub.2 O.sub.5 + eRe.sub.2 O.sub.3100 - (a + main first by-Sample b + c + c e component componentNo. d + e) a b TiO.sub.2 ZrO.sub.2 SnO.sub.2 d La.sub.2 O.sub.3 Pr.sub.2 O.sub.3 Nd.sub.2 O.sub.3 Sm.sub.2 O.sub.3 Dy.sub.2 O.sub.3 Er.sub.2 O.sub.3 (wt %) (wt__________________________________________________________________________ %) 101 92 1.5 2.5 2 0 0 1 0 0 1 0 0 0 99 1 102 89 1 4 1.5 1.5 0 1.5 0.5 1 0 0 0 0 98 2 103 84 0.5 5.5 1.5 2 1.5 2 0 0 2.5 0 0.5 0 99.5 0.5 104 87 4 2 0.5 0 0.5 4 0.5 0 0 0.5 0 1 99 1 105 90 1.5 3 0 0 0.5 4.5 0 0.5 0 0 0 0 98.5 1.5 106 79.5 2.5 6 0 5.5 1 0.5 2.5 0 2.5 0 0 0 99.5 0.5 107 87 4.5 2.5 2 0 0 1.5 0 1 0 0 1.5 0 98 2 108 86 1.5 3 0.5 1.5 0 2 0 0 2.5 1.5 0 1.5 98 2*109 92.7 0.3 2.5 0 0.5 1.5 1 0.5 0 0.5 0 0.5 0 99 1*110 86.3 4.7 4 0 0.5 0 3 0 0 1.5 0 0 0 99.5 0.5*111 90.2 1.5 1.8 1.5 0.5 0.5 1.5 0 0 0 2 0 0.5 98 2*112 81.3 2 6.2 2 2 2 1.5 0 0 3 0 0 0 99.5 0.5*113 88.7 2 4 0.3 0 0 3 0 2 0 0 0 0 99 1*114 84.3 1.5 5 3 2 1.7 2.5 0 0 0 2.5 0 0 99 1*115 91.2 2 2.5 0.5 0.5 1 0.3 0 0 0 0 2 0 99 1*116 82.8 2.5 4.5 1 2 1 4.7 0 0 0 0 0 1.5 99.5 0.5*117 92.7 1.5 2.5 0.5 1.5 0 1 0.3 0 0 0 0 0 99 1*118 85.8 1.5 3 0.5 0.5 1 2 0 0.7 2.5 2.5 0 0 99.5 0.5*119 92 1.5 2.5 0 0 2 1 0 0 1 0 0 0 100 0 120 87.5 4 2 0.5 0.5 0 4 0 0 1.5 0 0 0 99.95 0.05 121 91 1.5 2.5 1 0 1 1 0 0 2 0 0 0 97.5 2.5*122 87 4 2 0 0.5 0.5 4 0 0 2 0 0 0 97.3 2.7__________________________________________________________________________ *indicates out of the scope of the invention
TABLE 6______________________________________ main first by-Sample component component second by-component (wt %)No. (wt %) (wt %) Cr Mn Fe Co Ni______________________________________123 98.99 1.0 0 0.01 0 0 0124 98.85 1.0 0.05 0.05 0.05 0 0125 98.95 1.0 0 0 0 0.05 0126 98.9 1.0 0.05 0 0 0 0.05127 98.85 1.0 0 0.1 0 0 0.05128 98.65 1.0 0.05 0.2 0.05 0.05 0129 98.6 1.0 0 0.3 0 0 0.1130 98.55 1.0 0 0.3 0 0.1 0.05131 98.5 1.0 0.1 0.3 0 0.1 0*132 98.45 1.0 0 0.35 0.05 0.1 0.05______________________________________ *indicates out of the scope of the invention
TABLE 7__________________________________________________________________________baking electronic property mechanical propertySample temperature TC (%) bias TC (%) deflective strengthNo. (.degree.C.) .epsilon. tan .delta. (%) .DELTA.C.sub.max .DELTA.C.sub.maxB (kg/cm.sup.2)__________________________________________________________________________ 101 1140 2010 1.5 -12.1 -33.5 2060 120 1100 1790 1.5 -13.3 -30.0 2290 103 1100 1800 1.6 -14.2 -30.5 2170 104 1160 2010 1.7 -11.8 -32.0 1770 105 1120 1760 1.7 -10.6 -33.0 2210 106 1080 1370 1.2 -14.2 -28.5 2200 107 1100 1620 1.2 -14.5 -33.0 2080 108 1100 1640 1.6 12.1 -31.5 2150*109 1160 1690 2.1 -17.5 -33.8 1480*110 1120 2220 1.3 -21.4 -43.5 2020*111 1120 1740 1.8 -23.3 -37.0 1470*112 1100 980 1.3 -14.7 -28.0 2260*113 1100 1820 1.6 -23.5 -31.0 2300*114 1140 1510 1.0 -17.0 -31.5 2010*115 1140 1940 1.1 -22.5 -41.7 1980*116 1120 1620 1.7 -18.0 -44.8 2100*117 1160 1540 1.9 -29.5 -43.0 2050*118 1160 1910 1.2 -24.5 -35.2 1810*119 1160.degree. C. (not sintered) 120 1160 1700 1.3 13.0 -35.0 1620 121 1080 1390 1.2 13.5 -33.4 2150*122 1080 950 1.1 14.1 -34.4 2120__________________________________________________________________________ *indicates out of the scope of the invention
TABLE 8__________________________________________________________________________baking electronic property mechanical propertySample temperature TC (%) bias TC (%) deflective strengthNo. (.degree.C.) .epsilon. tan .delta. (%) .DELTA.C.sub.max .DELTA.C.sub.maxB (kg/cm.sup.2)__________________________________________________________________________123 1120 2000 1.5 -12.1 -33.0 2040124 1120 1920 1.7 -12.0 -33.3 2020125 1120 2010 1.5 -12.5 -34.2 1980126 1120 1970 1.6 -12.5 -33.0 2060127 1120 2060 1.6 -13.0 -34.0 2050128 1120 1890 2.0 -12.1 -33.0 1970129 1120 1920 2.1 -12.0 -32.8 1960130 1120 1950 2.1 -12.5 -35.5 1970131 1120 1920 2.2 -12.7 -33.5 1980*132 1120 1820 2.8 -11.8 -32.2 1990__________________________________________________________________________ *indicates out of the scope of the inveniton
TABLE 9__________________________________________________________________________main component composition (mol %){100 - (a + b + c + d + e + f)} BaTiO.sub.3 + aZnO + bBi.sub.2 O.sub.3 +cNb.sub.2 O.sub.5 + dMaO + eMbO.sub.2 + fRe.sub.2 O.sub.3 first first 100 - main by-Sam- (a + b + compo- compo-ple c + d + d e f nent nentNo. e + f) a b c PbO CaO TiO.sub.2 ZrO.sub.2 SnO.sub.2 La.sub.2 O.sub.3 Pr.sub.2 O.sub.3 Nd.sub.2 O.sub.3 Sm.sub.2 O.sub.3 Dy.sub.2 O.sub.3 Er.sub.2 O.sub.3 (wt (wt__________________________________________________________________________ %) 201 85.5 1.5 2.5 1 0.5 0 4 2 2 0 0 1 0 0 0 99 1 202 82.5 1 4 1.5 0 0.5 5 3 1 0.5 1 0 0 0 0 98 2 203 80.5 0.5 5.5 2 2 0 2 4 0.5 0 0 2.5 0 0.5 0 99.5 0.5 204 78.5 4 2 4 0 1.5 4 0 4 0.5 0 0 0.5 0 1 99 1 205 78.5 1.5 3 4.5 2 2 4 4 0 0 0.5 0 0 0 0 98.5 1.5 206 75 2.5 6 0.5 4 0 0 4 3 2.5 0 2.5 0 0 0 99.5 0.5 207 79 4.5 2.5 1.5 0 3 4 2 1 0 1 0 0 1.5 0 98 2 208 77.5 1.5 3 2 1.5 2 3 2 2 0 0 2.5 1.5 0 1.5 98 2*209 85.2 0.3 2.5 1 2 0 4.5 1 2 0.5 0 0.5 0 0.5 0 99 1*210 77.8 4.7 4 3 2 0 5 1.5 0.5 0 0 1.5 0 0 0 99.5 0.5*211 84.2 1.5 1.8 1.5 1.5 0.5 1.5 3 2 0 0 0 2 0 0.5 98 2*212 76.8 2 6.2 1.5 0.5 3 4 1.5 1.5 0 0 3 0 0 0 99.5 0.5*213 82.7 2 4 0.3 1 0 3.5 2 2.5 0 2 0 0 0 0 99 1*214 79.8 1.5 2.5 4.7 0 1 4 2 2 0 0 0 2.5 0 0 99 1*215 78.8 2 2.5 2 2.2 2 5 2 1.5 0 0 0 0 2 0 99 1*216 80.7 2.5 4.5 1.5 1 2 3 2 1.3 0 0 0 0 0 1.5 99.5 0.5*217 79.3 1.5 2.5 1 0 1.5 4 2.2 4 0 0 0 4 0 0 99 1*218 85.2 1.5 3 2 1 0 6 1 0 0.3 0 0 0 0 0 99.5 0.5*219 76.3 1.5 2.5 1 3 1 5 0 4 0 0.7 2.5 2.5 0 0 99 1*220 77.5 4 2 4 3 1 3 3 1 0 0 1.5 0 0 0 100 0 221 83.5 1.5 2.5 1 2 0 3.5 1 3 0 0 2 0 0 0 97.5 2.5*222 78 4 2 4 1 0 5 2 2 0 0 2 0 0 0 97.3 2.7__________________________________________________________________________ *indicates out of the scope of the invention
TABLE 10______________________________________ main first by-Sample component component second by-component (wt %)No. (wt %) (wt %) Cr Mn Fe Co Ni______________________________________223 98.99 1.0 0 0.01 0 0 0224 98.85 1.0 0.05 0.05 0.05 0 0225 98.95 1.0 0 0 0 0.05 0226 98.9 1.0 0.05 0 0 0 0.05227 98.85 1.0 0 0.1 0 0 0.05228 98.65 1.0 0.05 0.2 0.05 0.05 0229 98.6 1.0 0 0.3 0 0 0.1230 98.55 1.0 0 0.3 0 0.1 0.05231 98.5 1.0 0.1 0.3 0 0.1 0*232 98.45 1.0 0 0.35 0.05 0.1 0.05______________________________________ *indicates out of the scope of the invention
TABLE 11__________________________________________________________________________baking electronic property mechanical propertySample temperature TC (%) bias TC (%) deflective strengthNo. (.degree.C.) .epsilon. tan .delta. (%) .DELTA.C.sub.max .DELTA.C.sub.maxB (kg/cm.sup.2)__________________________________________________________________________ 201 1140 2020 1.4 -12.0 -32.5 2050 202 1100 1870 1.5 -13.3 -32.0 2280 203 1100 1650 1.7 -14.2 -32.5 2170 204 1160 1700 1.3 -11.8 -31.0 1780 205 1120 1570 1.2 10.6 -33.0 2210 206 1080 1810 1.2 -14.2 -32.5 2200 207 1100 2090 1.7 -14.5 -34.0 2090 208 1100 1850 1.6 12.1 -33.5 2150*209 1160 1910 2.0 -17.5 -32.8 1470*210 1120 1800 1.3 -21.4 -40.5 2020*211 1120 1780 1.7 -23.3 -33.0 1450*212 1100 970 1.2 -14.7 -29.0 2260*213 1100 2070 1.7 -23.5 -40.6 2310*214 1140 1500 1.1 -17.0 -41.0 2010*215 1140 2000 1.3 -18.5 -31.7 1980*216 1120 1990 1.4 -18.0 -32.8 2120*217 1160 1750 1.7 -19.5 -31.5 2050*218 1160 1800 1.3 17.5 -40.2 1830*219 1160 2150 1.8 20.0 -33.5 2110*220 1160.degree. C. (not sintered) 221 1080 1400 1.2 13.5 -31.4 2150*222 1080 960 1.1 14.1 -30.4 2140__________________________________________________________________________ indicates out of the scope of the invention
TABLE 12__________________________________________________________________________baking electronic property mechanical propertySample temperature TC (%) bias TC (%) deflective strengthNo. (.degree.C.) .epsilon. tan .delta. (%) .DELTA.C.sub.max .DELTA.C.sub.maxB (kg/cm.sup.2)__________________________________________________________________________223 1120 2010 1.5 -12.3 -33.0 2050224 1120 1920 1.6 -12.0 -33.3 2020225 1120 2010 1.5 -12.7 -33.2 1990226 1120 1980 1.6 -12.5 -33.0 2060227 1120 2060 1.7 -13.1 -33.0 2050228 1120 1880 2.0 -12.1 -33.0 1980229 1120 1920 2.0 -12.3 -33.8 1960230 1120 1940 2.1 -12.5 -33.5 1950231 1120 1920 2.1 -12.9 -33.5 1980*232 1120 1830 2.8 -11.8 -32.2 1990__________________________________________________________________________ *indicates out of the scope of the invention

Number	Date	Country
5-204625	Jul 1993	JPX
5-204627	Jul 1993	JPX
5-217519	Sep 1993	JPX

Dielectric ceramic compositions

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (3)

US Referenced Citations (1)

Foreign Referenced Citations (1)