The present invention in general relates to coatings and in particular to a wind blade finishing system.
Wind turbines are used to generate electricity from the kinetic power of the wind. Large blades at the front of the turbine assembly have a special curved shape, similar to the airfoil wings on a plane. When wind blows past a turbine's blades, the wind spins the blades around, and the rotational movement of the blades drives a generator that converts the kinetic energy to electrical power.
Wind turbine blades are generally made of composite materials. However, the surfaces of composite materials (for example composite materials made of glass fiber fabric or nonwoven and epoxy resin/vinyl ester resin) typically have a poor appearance and are not resistant to ultra violet light (UV) and weathering. Therefore, a surface coating is applied to the composite surfaces of the blades. Before the surface coating of epoxy resin/vinyl ester resin composite materials, composite materials must be polished and filled (leveled out), since erection of fibers often occurs during direct surface coating of the composite material. A gel coat is a resin system which can be applied onto molded parts of a composite structure for the production of smooth building component surfaces and at the same time also results in an attractive surface. However, over time, ultraviolet radiation from the sun, weather, pollution, and other environmental factors can wear away the exterior surface of the wind blades of a turbine. Existing processes for production of wind turbine blades are characterized by pore generation, multiple coating steps, and long process times including sanding.
Thus, there exists a need for a wind turbine blade finishing system that is robust and reduces process time by minimizing the number of components and application steps.
A finishing system for surfaces of a wind turbine blade includes having a gel coat, a putty, and a top coat. A simplified application and superior performance are obtained relative to the prior art systems.
A process for finishing a surface of a wind turbine blade includes the application of a gel coat to a mold substrate, laying up of fabrics, resin infusion and curing process. After demolding, putty is applied to the outer surface of the shell in order to smooth irregular surfaces. The cured putty surface is sanded to yield a smooth finished surface. A top coat is applied to the blade surface for installation and long-term performance.
The present invention is further detailed with respect to the following drawings. These figures are not intended to limit the scope of the present invention but rather illustrate certain attributes thereof.
The present invention has utility as a wind blade finishing system that is robust, cost effective, and is low in volatile organic compounds (VOC), while also reducing overall process time. Embodiments of the inventive differentiated wind blade finishing system combine a gel coat, putty and top coat and have excellent weather resistant properties, and takes the place of processes for producing turbine wind blades covered by gel coat, contouring putty, pore filler, top coat, and leading-edge coating. Embodiments of the inventive differentiated finishing system, minimize the need of sanding before applying the top coat, and in turn up to 11 hours of time associated with the sanding process, as well as preventing pin holes from showing through the surface of the wind blade without the need of a secondary product/operation thus eliminating pore filler, associated surface preparation and rework. Embodiments of the inventive differentiated finishing system reduce overall system cure time and process residence time, currently averaging 12 hours, and also reduces the number of products/steps needed to a minimum number. Overall, embodiments of the inventive differentiated wind blade finishing system reduce overall process times by over 25% by reducing the number of processing steps to applying the gel coat to a mold substrate, the laying up and infusing the resin with woven fiber cloth to form a shell with an outer surface defining a wind turbine blade. The putty is then applied to the outer uneven surfaces to form an even surface. The cured putty is then sanded to yield a smooth finished sanded surface. Finally, a top coat is applied to the blade surface. The process is particularly well suited for use with a wind turbine blade is at least 23 meters in length. The aforementioned steps can be completed in less than 25 hours for such a wind turbine blade with approximately 11 hours of surface preparation and 12 hours of curing time; this in contrast to a conventional process that typically takes about 33 hours for such a blade.
As used herein, the term “substantially free” with respect to pin holes, is defined as less than 0.1 total surface area percent and in some instances less than 0.05 total area percent, as measured with a telecentric laser scanning system operating in a bright field rastering mode.
Embodiments of the inventive finishing system have only three primary components gel coat, putty, and a top coat as opposed to conventional finishing systems that also have a pore filler and a leading-edge coating. The tackiness of the inventive gel coat even after more than 1 hours helps to hold fabrics while laying up the wind blade structure, which eases the fabrication process. Furthermore, embodiments of the transparent and flexible gel coat increase the durability of the applied coating under dynamic load and stress during service conditions of wind blades produced with the inventive finishing system. In addition, sanding/surface preparation is may not require on gel coat applied areas prior to the topcoat application. Embodiments of the inventive rapid curing putty, which can be sanded after 30 minutes without clogging reduces process time significantly. The “Quick dry to touch” property and long pot life of the inventive top coat also provides for a reduction in process time. The superior abrasion resistance of embodiments of the top coat also serve as a leading-edge coating for the turbine blades.
The reduced number of coating components (gel coat, putty, and top coat) in embodiments of the inventive differentiated wind blade finishing system versus currently available coating systems that have five or more coating components (gel coat, putty, pore filler, leading edge coat, base coat, etc.) result in reduced processing steps associated surface preparations required before and after the application of additional components including gel coat, pore filler, leading edge coat, etc. In fact, market segment focus (MSF) findings have revealed that, almost 34% of total process time consumed by surface preparation of wind turbine blades occurred during the coating process, which includes putty application followed by sanding, surface preparation prior to the coating, sanding after pore filler application etc. Elimination of just the sanding process saves almost 11 hours of process time per blade. The elimination of the sanding step in the present invention is made possible using a transparent gel coat as one of the components and eliminating pore filler component from present invention. Removing pore filler from the present invention will be managed by addressing pin holes with a low viscous top coat. Furthermore, proper adhesion of coating components may be achieved without any surface preparation.
A primary concern during turbine wind blade manufacturing is the generation of pinholes during the coating process. Currently, blade manufacturers eliminate these pin holes using pore fillers as a finishing component which requires an additional sanding process for a better result, but this process is sometimes inefficient to cover the pinholes and introduces additional cost to their process. Embodiments of the present invention eliminate pore filler which results in the elimination of additional sanding time and in turn over all processing time. The features of pore filler have been incorporated into the topcoat of the inventive differentiated wind blade finishing system. The inventive topcoat covers pin holes and eliminates the sanding process and the associated additional process time.
Embodiments of the inventive gel coat provide improved flexibility and mechanical properties as compared to existing gel coats. Turbine wind blades are generally manufactured out of fiber reinforced epoxy/unsaturated polymer matrices; glass fiber reinforced plastics (GFRP) that are expected to last at least 20 years in a challenging service environment. Generally, the length of the blade is around 60 meters long and to enhance the efficiency and energy yield of wind turbines, the length of the blades is being increased to 80-90 meters. The longer blades experience more deflection across the length of the blade hence increasing dynamic load and stress throughout the blade length. This adversely affects the durability of coating components and hence the protection of blades will be damaged. In order to enhance the life of coating components, flexibility of coating components especially the gel coat component has been improved in embodiments of the inventive differentiated wind blade finishing system.
Certain embodiments of the inventive putty have rapid curing characteristics under room temperature conditions. The rapid curing putty can be sanded after 30 minutes without clogging which reduces process time significantly as against the competitor, which can be sanded only after 120 minutes.
Embodiments of the inventive top coat provide excellent UV stability under QUV-B conditions and reduce maintenance costs associated with wind turbine blades having the inventive top coat.
It is to be understood that in instances where a range of values are provided that the range is intended to encompass not only the end point values of the range but also intermediate values of the range as explicitly being included within the range and varying by the last significant figure of the range. By way of example, a recited range of from 1 to 4 is intended to include 1-2, 1-3, 2-4, 3-4, and 1-4.
A specific embodiment of the inventive differentiated wind blade finishing system has three components a gel coat, putty, and a top coat. The properties of these finishing components are depicted in tables 2A, 2B, and 2C below.
Patent documents and publications mentioned in the specification are indicative of the levels of those skilled in the art to which the invention pertains. These documents and publications are incorporated herein by reference to the same extent as if each individual document or publication was specifically and individually incorporated herein by reference.
This application claims priority benefit of U.S. Provisional Application Ser. No. 62/448,500 filed Jan. 20, 2017; the contents of which are hereby incorporated by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2018/014149 | 1/18/2018 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62448500 | Jan 2017 | US |